This study focuses on factors that affect the structural integrity of wood-based composites. Wood-based composites exposed to fire may decompose due to the elevated temperatures, resulting in a degradation in performance. Thermal modelling can only predict the structural integrity of construction materials in fire if it is given accurate inputs. Consequently, methods for the characterization of the thermal, physical, and mechanical behaviors of wood and wood-based composites are selected, designed, and benchmarked. The relevant thermal and physical responses characterized includes porosity, permeability and thermal diffusivity. Common construction materials (white pine board, medium density fiberboard and spruce 24) are characterized from room temperature to complete decomposition. The characterization techniques and processes are based on existing literature and relevant ASTM standards. To reduce the number of experiments required for future material characterization, estimates based upon the degree of decomposition and the measured values for the virgin and charred materials are used. For porosity and thermal diffusivity, these models allow values at intermediate temperatures to be estimated with measurements at room temperature and complete decomposition and thermogravimetric analysis (TGA). We find that permeability depends heavily on the microstructure of materials and should be measured independently at the conditions of interest. An additional important aspect of the performance of wood-based composites is the fracture behavior of wood/adhesive systems. Adhesive bonding enables many engineered wood products such as furniture and structural wood joints and the adhesive fracture toughness often determines the durability. The conventional characterization method for wood/adhesive fracture resistance relies on samples with machined grain angles designed to funnel cracks to the adhesive interface. This method of sample preparation is difficult and time-consuming for certain wood species. In this work, a practical and efficient method is developed to characterize adhesive fracture energy of adhesively bonded veneer systems. In the method, auxiliary aluminum adherends are bonded to the veneers in an effort to drive the crack to the wood/adhesive interface. The method is applied to rotary-peeled veneers and saw-cut veneers produced from three species of wood bonded with three commonly used adhesives. The new tests method yields a high interfacial failure rate and successfully identifies differences in the performance of the three adhesives. SPG (one species of the rotary-peeled veneers) demonstrates a rising R-curve behavior (an increase in the fracture toughness with crack length) when bonded on the loose side. This increase in fracture toughness is observed to be a result of adhesive-substrate interaction, which is a developing process zone behind the crack tip consisting of bridged wood ligaments. / Doctor of Philosophy / Construction materials exposed to elevated temperatures from fires may reach temperatures where the material decomposes from the original material to a char. Protected and unprotected structural timber products exposed to fires may exhibit this behavior resulting in a degradation of performance. Understanding the thermal and physical responses of these materials is crucial in evaluating the materials behavior in fire. Additionally, many wood-based products (such as furniture) rely on adhesive bonds. Consequently, their usefulness is determined by the performance of those bonds. In this work, methods are developed to measure key properties impacting the behavior of wood-based systems at elevated temperatures, such as that experienced in fires and when they are subjected to forces attempting to debond one wood material from another. These techniques are demonstrated on common building materials (white pine board, medium density fiberboard and spruce 24) and wood veneers from three different species bonded with three different adhesives. Mathematical models are developed to expand the use of the data beyond the specific conditions for which it is measured.

No description available.

This dissertation is to obtain an overall understanding of the crack path selection in adhesively bonded joints. Using Dow Chemical epoxy resin DER 331® with various levels of rubber concentration as an adhesive, and aluminum 6061-T6 alloy with different surface pretreatments as the adherends, both symmetric and asymmetric double cantilever beam (DCB) specimens are prepared and tested under mixed mode fracture conditions in this study. Post-failure analyses conducted on the failure surfaces indicate that the failure tends to be more interfacial as the mode II component in the fracture increases whereas more advanced surface preparation techniques can prevent failure at the interface. Through mechanically stretching the DCB specimens uniaxially until the adherends are plastically deformed, various levels of T-stress are achieved in the specimens. Test results of the specimens with various T-stresses demonstrate that the directional stability of cracks in adhesive bonds depends on the T-stress level. Cracks tend to be directionally stable when the T-stress is compressive whereas directionally unstable when the T-stress is tensile. However, the direction of crack propagation is mostly stabilized when more than 3% mode II fracture component is present in the loading regardless of the T-stress levels in the specimens. Since the fracture sequences in adhesive bonds are closely related to the energy balance in the system, an energy balance model is developed to predict the directional stability of cracks and the results are consistent with the experimental observations. Using the finite element method, the T-stress is shown to be closely related to the specimen geometry, indicating a specimen geometry dependence of the directional stability of cracks. This prediction is verified through testing DCB specimens with various adherend and adhesives thicknesses. By testing the specimens under both quasi-static and low-speed impact conditions, and using a high-speed camera to monitor the fracture sequence, the influences of the debond rate on the locus of failure and the directional stability of cracks are investigated. Post-failure analyses suggest that the failure tends to be more interfacial when the debond rate is low and tends to be more cohesive when the debond rate is high. However, this rate dependence of the locus of failure is greatly reduced when more advanced surface preparation techniques are used in preparing the specimens. The post-failure analyses also reveal that cracks tend to be more directionally unstable as the debond rate increases. Finally, employing interface mechanics and extending the criteria for the direction of crack propagation to adhesively bonded joints, the crack trajectories for directionally unstable cracks are predicted and the results are consistent with the overall features of the crack paths observed experimentally. / Ph. D.

Structural adhesives are widely used with great success, and yet occasional failures can occur, often resulting from improper bonding procedures or joint design, overload or other detrimental service situations, or in response to a variety of environmental challenges. In these situations, cracks can start within the adhesive layer or debonds can initiate near an interface. The paths taken by propagating cracks can affect the resistance to failure and the subsequent service lives of the bonded structures. The behavior of propagating cracks in adhesive joints remains of interest, including when some critical environments, complicated loading modes, or uncertainties in material/interfacial properties are involved. From a mechanics perspective, areas of current interest include understanding the growth of damage and cracks, loading rate dependency of crack propagation, and the effect of mixed mode fracture loading scenarios on crack path selection. This dissertation involves analytical, numerical, and experimental evaluations of crack propagation in several adhesive joint configurations. The main objective is an investigation of crack path selection in adhesively bonded joints, focusing on in-plane fracture behavior (mode I, mode II, and their combination) of bonded joints with uniform bonding, and those with locally weakened interfaces. When removing cured components from molds, interfacial debonds can sometimes initiate and propagate along both mold surfaces, resulting in the molded product partially bridging between the two molds and potentially being damaged or torn. Debonds from both adherends can sometimes occur in weak adhesive bonds as well, potentially altering the apparent fracture behavior. To avoid or control these multiple interfacial debonding, more understanding of these processes is required. An analytical model of 2D parallel bridging was developed and the interactions of interfacial debonds were investigated using Euler-Bernoulli beam theory. The numerical solutions to the analytical results described the propagation processes with multiple debonds, and demonstrated some common phenomena in several different joints corresponding to double cantilever beam configurations. The analytical approach and results obtained could prove useful in extensions to understanding and controlling debonding in such situations and optimization of loading scenarios. Numerical capabilities for predicting crack propagation, confirmed by experimental results, were initially evaluated for crack behavior in monolithic materials, which is also of interest in engineering design. Several test cases were devised for modified forms of monolithic compact tension specimens (CT) were developed. An asymmetric variant of the CT configuration, in which the initial crack was shifted to two thirds of the total height, was tested experimentally and numerically simulated in ABAQUS®, with good agreement. Similar studies of elongated CT specimens with different specimen lengths also revealed good agreement, using the same material properties and cohesive zone model (CZM) parameters. The critical specimen length when the crack propagation pattern abruptly switches was experimentally measured and accurately predicted, building confidence in the subsequent studies where the numerical method was applied to bonded joints. In adhesively bonded joints, crack propagation and joint failure can potentially result from or involve interactions of a growing crack with a partially weakened interface, so numerical simulations were initiated to investigate such scenarios using ABAQUS®. Two different cohesive zone models (CZMs) are applied in these simulations: cohesive elements for strong and weak interfaces, and the extended finite element method (XFEM) for cracks propagating within the adhesive layer. When the main crack approaches a locally weakened interface, interfacial damage can occur, allowing for additional interfacial compliance and inducing shear stresses within the adhesive layer that direct the growing crack toward the weak interface. The maximum traction of the interfacial CZM appears to be the controlling parameter. Fracture energy of the weakened interface is shown to be of secondary importance, though can affect the results when particularly small (e.g. 1% that of the bulk adhesive). The length of the weakened interface also has some influence on the crack path. Under globally mixed mode loadings, the competition between the loading and the weakened interface affects the shear stress distribution and thus changes the crack path. Mixed mode loading in the opposite direction of the weakened interface is able to drive the crack away from the weakened interface, suggesting potential means to avoid failure within these regions or to design joints that fail in a particular manner. In addition to the analytical and numerical studies of crack path selection in adhesively bonded joints, experimental investigations are also performed. A dual actuator load frame (DALF) is used to test beam-like bonded joints in various mode mixity angles. Constant mode mixity angle tracking, as well as other versatile loading functions, are developed in LabVIEW® for use with a new controller system. The DALF is calibrated to minimize errors when calculating the compliance of beam-like bonded joints. After the corrections, the resulting fracture energies ( ) values are considered to be more accurate in representing the energy released in the crack propagation processes. Double cantilever beam (DCB) bonded joints consisting of 6061-T6 aluminum adherends bonded with commercial epoxy adhesives (J-B Weld, or LORD 320/322) are tested on the DALF. Profiles of the values for different constant mode mixity angles, as well as for continuously increasing mode mixity angle, are plotted to illustrate the behavior of the crack in these bonded joints. Finally, crack path selection in DCB specimens with one of the bonding surfaces weakened was studied experimentally, and rate-dependency of the crack path selection was found. Several contamination schemes are attempted, involving of graphite flakes, silicone tapes, or silane treatments on the aluminum oxide interfaces. In all these cases, tests involving more rapid crack propagation resulted in interfacial failures at the weakened areas, while slower tests showed cohesive failure throughout. One possible explanation of this phenomenon is presented using the rate-dependency of the yield stress (commonly considered to be corresponding to the maximum traction) of the epoxy adhesives. These experimental observations may have some potential applications tailoring adhesive joint configurations and interface variability to achieve or avoid particular failure modes. / Ph. D.