In the history of the concrete structures there was a time in which the mechanical resistance was the most important property for the designers. However due to amount of pathologies in the concrete structures and your respective worn-out amounts in recovery, other feature is being prioritized: the durability. And for environmental reasons as global heating, pollution and the raw materials decrease, the sustentability is prioritized. Aiming at collaborate to these factors these paper has as objective analyzes the microstructure of the covercrete with substitution in mass of 90% of cement for mineral additions. Were researched three types of concretes reference concrete (100%CPV-ARI), concrete with 70%Slag+20%FlyAsh and other similar mixture with addition of 20% of hydrated lime with the intention of partially restoring the hydroxide of calcium consumed by the pozzolanics reactions - named respectively of R, EV and EVC. Aims at, more specifically, to establish the differences microstructures of the covercrete of the prototypes(beams-70x20x15cm), through the tests of combined water, x-ray diffraction and scanning electron microscopy. For comparison effect, compressive strength test were also accomplished in molded cylinders(10x20cm) and cured in humid camera and in the cylinders(10x20cm) extracted of the cured prototypes in environmental conditions after 7 days of humid cure. Were studied three relationships a/ag: 0.40, 0.60 and 0.80 for the concrete R and 0.30, 0.40 and 0.50 for the concretes with additions, obtaining resistance between 20 and 70MPa. The tests of the microstructure were accomplished in the 91 and 300 days, with samples starting from the surface of the prototypes, in layers, in the depths of: 0-1.0cm(C1), 2.0-3.0cm(C2) and 4.5-5.5cm(C3). Evolution of the strength was accompanied in the ages of 28, 91, 182 and 300 days. Results were analyzed in equality of a/ag and compressive strength. For a/ag 0.40 and 0.50, to 28 days of age, in relation to reference concrete, the strength of the concrete EV was 54.0% on average of this, and the concrete EVC it was 68.5%. In the final age of 300 days, the percentile are of 72.5% and 76%. In both tests ages, with the increase of the depth of the layer occurs: decrease in the intruded volume total mercury, decrease in the tenor of combined water for the reference concrete and increment in the concretes with additions, decrease in the intensity of pick of the hydroxide of calcium in the three mixtures, decrease in the intensity of pick of the hydrated silicate for the reference concrete and increment in the concretes with mineral additions. Analysis on scanning electron microscopy showed refinement in the size of the grains, larger compact and uniformity in the mixtures with additions / Na história das estruturas de concreto houve período no qual a resistência mecânica foi a propriedade mais importante para os projetistas. Porém, devido ao surgimento de manifestações patológicas nas estruturas de concreto e seus respectivos montantes gastos em recuperação, outro aspecto também está sendo considerado: a durabilidade. Por motivos ambientais como aquecimento global, poluição e diminuição das matérias-primas, prioriza-se também a sustentabilidade. Visando colaborar com estes fatores o presente trabalho tem como objetivo analisar a microestrutura da camada de cobrimento de concretos com substituição em massa de 90% de cimento Portland por adições minerais. Foram pesquisadas três misturas: concreto de referência (100%CPV-ARI), concreto com 70%Escória+20%CinzaVolante e outra mistura similar com adição de 20% de cal hidratada com o intuito de repor parcialmente o hidróxido de cálcio consumido pelas reações pozolânicas as quais foram nomeadas respectivamente de R, EV e EVC. Objetiva, mais especificamente, estabelecer as diferenças microestruturais da camada de cobrimento de protótipos (vigas 70x20x15cm), através dos ensaios de porosimetria por intrusão de mercúrio, água combinada, difração de raios-X e microscopia eletrônica de varredura. Para efeito de comparação, também foram realizados ensaios de resistência à compressão em corpos-de-prova (10x20cm) moldados e curados em câmara úmida e em testemunhos (10x20cm) extraídos dos protótipos curados em condições ambientais após 7 dias de cura úmida. Foram estudadas três relações a/ag: 0.40, 0.60 e 0.80 para o concreto R e 0.30, 0.40 e 0.50 para os concretos com adições, obtendo resistências entre 20 e 70MPa. Os ensaios da microestrutura foram realizados aos 91 e 300 dias, com amostras a partir da face dos protótipos, em três camadas, nas profundidades: 0-1cm(C1), 2- 3cm(C2) e 4.5-5.5cm(C3). A evolução da resistência foi acompanhada nas idades de 28, 91, 182 e 300 dias. Os resultados foram analisados em igualdade de relação a/ag e resistência à compressão. Para as relações a/ag 0.40 e 0.50, aos 28 dias de idade, em relação ao concreto de referência, a resistência do concreto EV foi em média 54.0% deste, e o concreto EVC foi 68.5%. E na idade final de 300 dias, os percentuais são de 72.5% e 76%. Em ambas as idades de ensaio, com o aumento da profundidade da camada ocorreu: decréscimo no volume total intrudido de mercúrio, decréscimo no teor de água combinada para o concreto de referência e acréscimo nos concretos com adições, decréscimo na intensidade de pico do hidróxido de cálcio nas três misturas, decréscimo na intensidade de pico do silicato de cálcio hidratado para o concreto de referência e acréscimo nos concretos com adições minerais. A análise das micrografias mostrou refinamento no tamanho dos grãos, maior densificação e uniformidade nas misturas com adições

Made available in DSpace on 2014-10-09T12:41:24Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:39Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:27:47Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:04:53Z (GMT). No. of bitstreams: 0 / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Thesis submitted in fulfilment of requirements for the degree Magister Technologiae: Chemical Engineering In the FACULTY OF ENGINEERING At the CAPE PENINSULA UNIVERSITY OF TECHNOLOGY, 2012 / The generation of electricity from coal in South Africa results in millions of tons of fly ash being produced each year. Less than 10 % of the fly ash generated is being used constructively and the remaining unused ash is currently inducing disposal and environmental problems. Intensive research on the utilisation of fly ash has been conducted either to reduce the cost of disposal or to minimise its impact on the environment. It has been shown that South African fly ash can be used as a feedstock for zeolite synthesis due to its compositional dominance of aluminosilicate and silicate phases. Most of the studies conducted on zeolite synthesis using South African fly ash are performed on small laboratory scale. Therefore, production of zeolites on an industrial/pilot plant scale would, in addition to producing a valuable product, help abate the pollution caused by the disposal of fly ash in the country. This research focuses on the investigation of the scale-up opportunity of zeolite synthesis from South African fly ashes with the view of understanding the effects of some reactor and operational parameters on the quality of the zeolite produced. Two types of zeolites (zeolite Na-P1 and zeolite A) were synthesised via two different routes in this study: (1) a two stage hydrothermal synthesis method (zeolite Na-P1) and (2) alkaline fusion prior to hydrothermal synthesis (zeolite A). The synthesis variables evaluated in this study were; the effect of impeller design and agitation rates during the aging step (zeolite Na-P1) using three different impellers (anchor, 4-flat-blade and Archimedes screw impeller) at three agitation speeds (150, 200 and 300 rpm), the effect of fly ash composition and solvents (water sources) on the phase purity of both zeolite Na-P1 and zeolite A, and the effect of the hydrothermal reaction time during the synthesis of zeolite Na-P1 using low amorphous phase fly ash i.e. aging time (12-48 hours) and hydrothermal treatment time (12-48 hours). The raw materials (fly ashes from Arnot, Hendrina, Tutuka, Lethabo and Matla power stations) and the synthesised zeolite product were characterised chemically, mineralogically and morphologically by X-ray fluorescence spectrometry, X-ray powder diffraction and scanning electron microscopy. Other characterisation techniques used in the study were 1) Fourier transform infrared spectroscopy to provide structural information and also monitor the evolution of the zeolite crystals during synthesis and 2) inductively coupled plasma atomic emission (ICP-AES) and mass spectrometry for multi-elemental analysis of the synthesis solution and the solvents used in this study. The experimental results demonstrated that the phase purity of zeolite Na-P1 was strongly affected by agitation and the type of impeller used during the aging step of the synthesis process. A high crystalline zeolite Na-P1 was obtained with a 4-flat-blade impeller at a low agitation rate of 200 rpm. Although a pure phase of zeolite Na-P1 was obtained at low agitation rates, the variation in the mineralogy of the fly ash was found to affect the quality of the zeolite produced significantly. The results suggested that each batch of fly ash would require a separate optimisation process of the synthesis conditions. Therefore, there is a need to develop a database of the synthesis conditions for zeolite Na-P1 based on the fly ash composition. As a consequence, the scale-up synthesis of zeolite Na-P1 would require step-by-step optimisation of the synthesis conditions, since this zeolite was sensitive to the SiO2/Al2O3 ratio, agitation and the mineralogy of the fly ash. On the other hand, zeolite A synthesis had several advantages over zeolite Na-P1. The results suggested that a pure phase of zeolite A can be produced at very low reaction temperature (i.e. below 100 °C, compared to 140 °C for zeolite Na-P1), shorter reaction times (i.e. less than 8 hours compared to 4 days for zeolite Na-P1), with complete dissolution of fly ash phases and more importantly less sensitive to the SiO2/Al2O3 ratio of the raw materials. The zeolite A synthesis process was found to be more robust and as a result, it would be less rigorous to scale-up despite the energy requirements for fusion. This study showed for the first time that different impeller designs and agitation during the aging step can have a profound impact on the quality of the zeolite produced. Therefore, it is not only the hydrothermal synthesis conditions and the molar regime but also the dissolution kinetics of the feedstock that influence the outcome of the zeolite synthesis process. This study has also shown for the first time that a pure phase of zeolite A can be synthesised from various sources of South African fly ash containing different mineralogical and chemical compositions via the alkali fusion method under the same synthesis conditions. Therefore, the effective zeolitisation of fly ash on a large scale would assist to mitigate the depletion of resources and environmental problems caused by the disposal of fly ash.

O emprego de resíduos da indústria como materiais alternativos na Engenharia vem sendo tópico recorrente em pesquisas de desenvolvimento de novos materiais, devido a uma maior consciência da opinião pública quanto ao impacto ambiental oriundo da produção industrial. Buscando colaborar com esta discussão, esta pesquisa procurou inserir dois resíduos (cinza volante e cal de carbureto), gerados na região metropolitana de Porto Alegre, como alternativa de solução em Engenharia. Analisando-se a microestrutura da cinza volante, observa-se que ela é formada por esferas ocas e plerosferas (esferas ocas preenchidas por esferas menores). Foi estudado o ganho de resistência da mistura promovido pela moagem da cinza volante em um moinho de bolas cerâmicas, visando uma potencialização da reatividade do material. A fim de possibilitar a utilização destes resíduos, é necessário um estudo do seu comportamento mecânico decorrente da cimentação proporcionada pela mistura e compactação destes materiais. A presente pesquisa busca fornecer subsídios para que seja possível determinar o seu comportamento, através do uso da relação porosidade (η)/teor volumétrico de cal (LV) obtidas a partir da identificação e quantificação das variáveis mais importantes no controle da resistência da mistura dos dois resíduos, com e sem o processo de moagem da cinza, levando a formulação de equações para previsão da resistência à compressão simples do material cimentado para cinza volante com diferentes tempos de moagem e cura acelerada. Para isso, foram realizados ensaios de compressão simples em corpos de prova com 5, 10 e 15% de cal, com peso específico aparente seco de 11, 12 e 13 kN/m3, curados por 7 dias, com umidade de 18% para os tempos de moagem 0, 2 e 6h nas temperaturas 23 e 40°C, e 0 e 6h a 60°C. Os resultados apontam que o aumento do teor de cal gerou ganhos de resistência para as maiores temperaturas de cura; a diminuição da porosidade proporcionou um ganho de resistência para todas as combinações; o aumento da temperatura foi importante no ganho de resistência entre 23oC e 40oC; a moagem da cinza por 2h promoveu ganhos significativos de resistência em relação à não moída, porém, para 6h de moagem os ganhos não foram significativos para as temperaturas de cura de 23oC e 60oC. A relação η/LV, ajustada por um expoente [η/(Lv)0,07], mostrou-se adequada na formulação de equações na previsão da resistência do material cimentado para todas as temperaturas e tempos de moagem estudados. Além disso, a existência de relações únicas e distintas no controle da resistência à compressão simples em função da porosidade, teor volumétrico de cal, temperatura de cura e tempo de moagem, mostraram-se úteis para formulações de dosagem. Os resultados foram submetidos à análise de variância que comprovou que todos os fatores controláveis escolhidos para o experimento são significativos, assim como todas suas interações. / The use of industry by-products as alternative materials in Engineering has been a recurring topic of research in development of new materials, mainly, due to a larger public conscience regarding the environmental impact of industrial production of waste. Aiming to contribute on this discussion, this research sought to introduce two by-products (fly ash and carbide lime), produced on the metropolitan area of Porto Alegre, as an alternative Engineering solution. Analyzing the microstructure of the fly ash, it is observed that it is composed by void spheres and plerospheres (void spheres filed with smaller ones). Having that in mind, it was studied the admix strength gain promoted by the grinding of de fly ash on a ceramic ball mill, aiming an enhancement of the reactivity of the material. In order to enable the use of these byproducts, it is necessary the study of its mechanical behavior due to the cementation provided by the mixture and compaction of these materials. The current research seeks to provide subsides in order to determine its behavior, through the use of the ratio porosity (η)/ volumetric lime content (LV), obtained from the identification and quantification of the most important variables on the control of the strength of the admixes of both by-products, with or without the process of fly ash grinding. This means, the formulation of equations for the simple compressive strength forecast of the cemented material for the fly ash with different grinding times and accelerated curing temperature. In order to do so, it were realized simple compression tests with 5, 10 and 15% of lime, with a specific dry unit weight of 11, 12 and 13 kN/m3, cured for 7 days, with water content of 18% for the grinding times of 0, 2 and 6h to the curing temperatures of 23 and 40oC, and 0 and 6h to 60oC. The results show that, the increase of lime content provided strength gains for the higher temperatures; the decrease of porosity generated strength gain to all the combinations; the increase in curing temperature was important on the strength gain between 23oC and 40oC; the grinding of fly ash for 2h promoted significant strength gains when compared to the not ground samples, however, for 6h of grinding the strength gain wasn’t significant for the 23oC and 60oC curing temperatures. The η/LV ratio, adjusted by an exponent [η/(LV)0,07], presented itself adequate for the formulation of the equations for the forecast of the strength gain of the cemented material to all the studied temperatures and grinding times. Besides that, the existence of unique and distinct relationships on the control of the simple compression strength depending on the porosity, volumetric lime content, curing temperature and grinding time, have been shown useful for the dosage formulation. The results were submitted to variance analysis, which demonstrated that all the factors chosen on the experiment were significant, as all their interactions.

abstract: Nuclear magnetic resonance (NMR) is an important phenomenon involving nuclear magnetic moments in magnetic field, which can provide much information about a wide range of materials, including their chemical composition, chemical environments and nuclear spin interactions. The NMR spectrometer has been extensively developed and used in many areas of research. In this thesis, studies in two different areas using NMR are presented. First, a new kind of nanoparticle, Gd(DTPA) intercalated layered double hydroxide (LDH), has been successfully synthesized in the laboratory of Prof. Dey in SEMTE at ASU. In Chapter II, the NMR relaxation studies of two types of LDH (Mg, Al-LDH and Zn, Al-LDH) are presented and the results show that when they are intercalated with Gd(DTPA) they have a higher relaxivity than current commercial magnetic resonance imaging (MRI) contrast agents, such as DTPA in water solution. So this material may be useful as an MRI contrast agent. Several conditions were examined, such as nanoparticle size, pH and intercalation percentage, to determine the optimal relaxivity of this nanoparticle. Further NMR studies and simulations were conducted to provide an explanation for the high relaxivity. Second, fly ash is a kind of cementitious material, which has been of great interest because, when activated by an alkaline solution, it exhibits the capability for replacing ordinary Portland cement as a concrete binder. However, the reaction of activated fly ash is not fully understood. In chapter III, pore structure and NMR studies of activated fly ash using different activators, including NaOH and KOH (4M and 8M) and Na/K silicate, are presented. The pore structure, degree of order and proportion of different components in the reaction product were obtained, which reveal much about the reaction and makeup of the final product. / Dissertation/Thesis / Ph.D. Physics 2013

Made available in DSpace on 2014-10-09T12:41:24Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:39Z (GMT). No. of bitstreams: 0 / As cinzas resultantes da queima de carvão por usinas termelétricas tem sido uma fonte de contaminação constante devido a seu descarte sobre o solo de forma inadequada. Os elementos tóxicos presentes na cinza de carvão quando lixiviados da cinza para o solo podem ficar biodisponíveis e serem absorvidos por plantas, consumidos por animais ou ainda transportados para diversas matrizes ambientais, tais como, águas subterrâneas e águas superficiais. Ensaio de germinação e desenvolvimento das radículas de Lactuca sativa e ensaio de toxicidade aguda com Daphnia similis foram realizados para avaliar a toxicidade dos percolados de colunas de cinza de carvão e de solo com cinza de carvão. De acordo com os valores obtidos por meio dos ensaios de germinação e desenvolvimento das radículas de L. sativa foram observados efeitos tóxicos à germinação das sementes de L. sativa nos percolados da coluna de cinza de carvão. Os valores médios de CI50(120h) destes percolados variaram de 27,6 a 90,6% e os valores do índice de germinação (IG) variaram de 6,7 a 40,8. Nos ensaios de toxicidade aguda com os organismos teste D. similis também foram observados efeitos tóxicos à mobilidade e/ou sobrevivência dos organismos expostos aos percolados da coluna de cinza de carvão. Os valores obtidos para CE50(48h) nestes percolados variaram de 25,6 a 84,1%. Os percolados das colunas de solo com cinza de carvão não apresentaram toxicidade tanto à L. sativa como à D. similis. Os resultados obtidos por meio destes ensaios ecotoxicológicos para os percolados das colunas de cinza de carvão e de solo com cinza de carvão indicam que o solo das colunas retiveram as substâncias tóxicas lixiviadas da cinza de carvão, ou seja, os solos utilizados nestas colunas atuaram como filtros. / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:27:47Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:04:53Z (GMT). No. of bitstreams: 0 / Cinza leve de carvão, resíduo gerado em usina termelétrica, foi usada para sintetizar zeólita por meio de tratamento hidrotérmico com solução de NaOH. A cinza leve (CL-2) e a zeólita sintética (ZM-2) que foi predominantemente identificada como hidroxi-sodalita foram utilizadas como adsorventes dos corantes aniônicos índigo carmina (IC) e reativo laranja 16 (RL16) de soluções aquosas. Nos processos de adsorção, os efeitos de tempo de contato, concentração inicial de corantes, pH, massa de adsorventes e temperatura foram avaliados. O estudo cinético de adsorção demonstrou que os resultados apresentaram melhor ajuste ao modelo de pseudo-segunda ordem e que adsorção de superfície e difusão intrapartícula participaram no mecanismo de adsorção. Os parâmetros termodinâmicos demonstraram que a adsorção foi espontânea em todos os processos de adsorção. Os processos de adsorção foram de natureza endotérmica para todos os sistemas, com exceção do sistema IC/ZM-2, em que foi exotérmico. Os dados de entropia mostraram a ocorrência do aumento da desordem na interface sólido/solução durante a adsorção em todos os sistemas, exceto novamente no IC/ZM-2, no qual se verificou a diminuição da desordem na interface. As isotermas de adsorção ajustaram-se à equação linear de Langmuir. As capacidades máximas de adsorção foram 1,48 mg/g para o sistema IC/CL-2; 1,13 mg/g para IC/ZM-2; 0,96 mg/g para RL16/CL-2 e 1,14 mg/g para RL16/ZM-2 à temperatura ambiente. O estudo de dessorção realizado com água, com soluções aquosas ácidas e com solução aquosa básica demonstrou ser ineficiente tanto para a recuperação dos corantes quanto para a regeneração dos adsorventes. / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

As cinzas resultantes da queima de carvão por usinas termelétricas tem sido uma fonte de contaminação constante devido a seu descarte sobre o solo de forma inadequada. Os elementos tóxicos presentes na cinza de carvão quando lixiviados da cinza para o solo podem ficar biodisponíveis e serem absorvidos por plantas, consumidos por animais ou ainda transportados para diversas matrizes ambientais, tais como, águas subterrâneas e águas superficiais. Ensaio de germinação e desenvolvimento das radículas de Lactuca sativa e ensaio de toxicidade aguda com Daphnia similis foram realizados para avaliar a toxicidade dos percolados de colunas de cinza de carvão e de solo com cinza de carvão. De acordo com os valores obtidos por meio dos ensaios de germinação e desenvolvimento das radículas de L. sativa foram observados efeitos tóxicos à germinação das sementes de L. sativa nos percolados da coluna de cinza de carvão. Os valores médios de CI50(120h) destes percolados variaram de 27,6 a 90,6% e os valores do índice de germinação (IG) variaram de 6,7 a 40,8. Nos ensaios de toxicidade aguda com os organismos teste D. similis também foram observados efeitos tóxicos à mobilidade e/ou sobrevivência dos organismos expostos aos percolados da coluna de cinza de carvão. Os valores obtidos para CE50(48h) nestes percolados variaram de 25,6 a 84,1%. Os percolados das colunas de solo com cinza de carvão não apresentaram toxicidade tanto à L. sativa como à D. similis. Os resultados obtidos por meio destes ensaios ecotoxicológicos para os percolados das colunas de cinza de carvão e de solo com cinza de carvão indicam que o solo das colunas retiveram as substâncias tóxicas lixiviadas da cinza de carvão, ou seja, os solos utilizados nestas colunas atuaram como filtros. / The coal fly ash of power plants has been a constant source of contamination due to the improperly disposed on the soil. The toxic elements leached from coal fly ash when in contact with soil could become bioavailable and be absorbed by plants, consumed by animals or transported to different environmental matrices, such as groundwater and surface water. Seed germination and root elongation tests with Lactuca sativa and acute toxicity tests with Daphnia similis were done to evaluate the toxicity of the leachate from coal fly ash and soil with coal fly ash columns. According to the values obtained for the seed germination and root elongation tests were observed toxic effects to seed germination of L. sativa for the leachates from coal fly ash column. The mean values of IC50(120h) for these leachates ranged from 27.6 to 90.6% and the germination index values (IG) ranged from 6.7 to 40.8. In the acute toxicity tests with test organisms D. similis were also observed toxic effects to mobility and/or survival of organisms exposed to leachates of the coal fly ash column. The values obtained for EC50(48h) for these leachates range from 25.6 to 84.1%. The leachates of soil with coal fly ash columns not presented toxicity to both test organisms, L. sativa and D. similis. The data obtained by these ecotoxicological tests to the leachates of soil coal fly ash and soil with coal fly ash columns indicate that the soil of the columns have retained the toxic substances leached from the coal fly ash, thus the soils used in these columns have acted as filters.

A utilização de cinza volante na composição de material cimentício o torna mais sustentável, além de conferir à matriz hidratada características peculiares que melhoram o desempenho frente à ação de diferentes agentes deletérios. A principal desvantagem da utilização de pozolana no sistema cimentício é a maior susceptibilidade à carbonatação. A maior taxa de neutralização da solução aquosa dos poros é devida ao teor remanescente menor de portlandita na matriz. O conhecimento das características da cinza volante que influenciam a interação com a cal, é necessário para subsidiar medidas preventivas com relação ao consumo de portlandita. A presente pesquisa objetiva verificar a eficiência da adição de cal hidratada em concreto executado com cimento pozolânico como forma de reduzir a susceptibilidade à carbonatação. As etapas realizadas para cumprir o objetivo abrangem: a caracterização da cinza volante, com ênfase na determinação do teor de fase vítrea; a cinética de reação em sistema de cinza volante e hidróxido de cálcio; a evolução da hidratação, e a decorrente variação microestrutural. Nos sistemas cimentícios de concretos cujas composições são 100% de cimento ou 50% de cimento e 50% cinza volante, com e sem a adição de 20% de cal hidratada, foi caracterizado a microestrutura da camada de cobrimento e o seu desempenho frente à ação do anidrido carbônico, em ensaio acelerado. Na cinza volante estudada, o teor de fase vítrea foi de 57%, e o consumo máximo por atividade pozolânica, função da área específica BET, foi de 0,69 gramas de Ca(OH)2/grama de fase vítrea de cinza volante. No cimento portland pozolânico, este consumo é menor devido à estrutura formada pela hidratação do cimento. A adição de cal hidratada à pasta de cimento e cinza volante, além de aumentar o consumo de cal por atividade pozolânica, restabeleceu, parcialmente, o teor remanescente de portlandita na matriz. A interação da cinza volante com a cal hidratada não interfere no volume total de vazios da matriz hidratada, porém, refina a microestrutura, aumentando o volume de mesoporos. A carbonatação, em concretos com mesma resistência à compressão de 55 MPa, atingiu maior profundidade quando executado com cimento pozolânico. A adição de cal hidratada não foi eficiente em reduzir a susceptibilidade à carbonatação acelerada. / The use of fly ash in the composition of the cementitious material makes it more sustainable, besides conferring to the hydrated matrix peculiar characteristics which improve its performance with relation to the action of different deleterious agents. The main disadvantage of pozzolan utilization in cementious systems is its susceptibility to carbonation. The greatest neutralization rate of the aqueous solution of the cement pore is, generally, attributed to the smallest amount of portlandite remaining in the matrix. It is necessary to widen knowledge about the characteristics of the fly ash which influence the interaction with calcium hydroxide in order to promote preventive measures with regard to portlandite consumption. This current research aims at verifying the efficiency of hydrated lime addition to concrete by using pozzolanic cement as a way of reducing its susceptibility to carbonation. The steps employed to attain this objective include: fly ash characterization with an emphasis on glass content; fly ash and calcium hydroxide systems kinetics; hydration evolution; and the consequent microstructure variation. In cementious systems of concrete whose composition is either 100% cement or 50% cement and 50% fly ash _ with or without 20% addition of hydrated lime _ it was characterized the microstructure of covercrete and its performance with regard to the interaction with carbon dioxide in accelerated testing. In the studied fly ash, glass content was 57% and the maximum consumption per pozzolanic activity, which is function of BET specific surface area, was 0.69 g of Ca(OH)2/g of glass content in the fly ash. As far as pozzolanic Portland cement is concerned, this consumption is smaller due to the structure formed by the cement hydration. The addition of hydrated lime to the cement paste and fly ash, besides increasing the consumption of lime per pozzolanic activity, partially, reestablished the remaining content of portlandite in the matrix. The interaction of the fly ash with the hydrated lime does not interfere in the total volume of void spaces in the hydrated matrix; however, it refines the microstructure by increasing the volume of mesopores. Carbonation in concrete with the same compressive strength of 55 MPa reached its deepest point when performed in pozzolanic cement. The addition of hydrated lime was not efficient at reducing susceptibility to accelerated carbonation.