<div>Aluminum 6061 is extensively used in industry and welding and additive manufacturing (AM) of Al6061 offer flexibility in manufacturing. Solid-state welding and AM processes can overcome the shortcomings of fusion-based processes, such as porosity and hot cracking. In this thesis, friction stir welding and friction stir additive manufacturing, which are both based on the concepts of friction stir processing (solid-state), were studied. The welding parameters for a sound weld during friction stir welding of Al6061-T6 alloy were determined based on the experimental and numerical analysis. Formation of tunnel defects and cavity defects was also studied. A Coupled Eulerian-Lagrangian (CEL) finite element model was established to analyze the process, where the workpiece was modeled as an Eulerian body, and the tool as Lagrangian. The model was validated by conducting experiments and correlating the force measured by a three-axis dynamometer. The experimentally validated simulation model was used to find an optimum parameter set for the sound weld case.</div><div>To demonstrate the friction stir additive manufacturing process, a 40 mm × 8 mm × 8 mm (L×B×H) material was fabricated by adding five 1.6 mm thick plates. A similar coupled Eulerian-Lagrangian based finite element model was used to predict the effects of sound process parameters, such as the tool’s rotational speed and the translational speed. The temperature predicted by the model was used to predict the microhardness distribution in the sample and to further elucidate the hardness change in the weld zone, which showed a good agreement with the experimental results. The microstructure of the samples was analyzed, and the mechanical properties of the additive manufactured samples were characterized and compared with those of other AM techniques via tensile tests and tensile shear tests.</div>

The recent emphasis on magnesium alloys can be appreciated by following the research push from several agencies, universities and editorial efforts. With a density equal to two-thirds of Al and one-thirds of steel, Mg provides the best opportunity for lightweighting of metallic components. However, one key bottleneck restricting its insertion into industrial applications is low strength values. In this respect, Mg-Y-Nd alloys have been promising due to their ability to form strengthening precipitates on the prismatic plane. However, if the strength is compared to Al alloys, these alloys are not attractive. The primary reason for low structural performance in Mg is related to low alloying and microstructural efficiency. In this dissertation, these terminologies are discussed in detail. A simple calculation showed that the microstructural efficiency in Mg-4Y-3Nd alloy is 30% of its maximum potential. Guided by the definitions of alloying and microstructural efficiency, the two prime objectives of this thesis were to: (i) to use thermomechanical processing routes to tailor the microstructure and achieve high strength in an Mg-4Y-3Nd alloy, and (ii) optimize the alloy chemistry of the Mg-rare earth alloy and design a novel rare—earth free Mg alloy by Calphad approach to achieve a strength of 500 MPa. Experimental, theoretical and computational approaches have been used to establish the process-structure-property relationships in an Mg-4Y-3Nd alloy. For example, increase in strength was observed after post aging of the friction stir processed/additive manufactured microstructure. This was attributed to the dissolution of Mg2Y particles which increased the alloying and microstructural efficiency. Further quantification by numerical modeling showed that the effective diffusivity during friction stir processing and friction stir welding is 60 times faster than in the absence of concurrent deformation leading to the dissolution of thermally stable particles. In addition, the investigation on the interaction between dislocations and strengthening precipitate revealed that, specific defects like the I1 fault aid in the accelerated precipitation of the strengthening precipitate in an Mg-4Y-3Nd alloy. Also, the effect of external field (ultrasonic waves) was studied in detail and showed accelerated age hardening response in Mg-4Y-3Nd alloy by a factor of 24. As the bottleneck of low strength is addressed, the answers to the following questions are discussed in this dissertation: What are the fundamental micro-mechanisms governing second phase evolution in an Mg-4Y-3Nd alloy? What is the mechanical response of different microstructural states obtained by hot rolling, friction stir processing and friction stir additive manufacturing? Is defect engineering critical to achieve high strength Mg alloys? Can application of an external field influence the age hardening response in an Mg-4Y-3Nd alloy? Can a combination of innovative processing for tailoring microstructures and computational alloy design lead to new and effective paths for application of magnesium alloys?