Efeito magnetocalórico em filmes finos nanocompósitos sintetizados por sputtering / Magnetocaloric effect in nanocomposite thin films obtained by sputtering

Gadioli, Giovana Zanini, 1980- 24 March 2006 (has links)
Orientador: Marco Antonio Bica de Moraes / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-06T01:12:05Z (GMT). No. of bitstreams: 1 Gadioli_GiovanaZanini_M.pdf: 816711 bytes, checksum: 5d38a2c08f13049d8af5fd4659ded22e (MD5) Previous issue date: 2006 / Resumo: As propriedades de filmes obtidos por co-deposição de um material ferromagnético e um não-magnético são objetos de intensa investigação. Neste trabalho, foram investigadas as propriedades de filmes Gdx W1-x, com x variando de 0 a 1. Os filmes foram depositados por magnetron-sputtering a partir de alvos de Gd e W. Para a análises dos filmes foram usadas as técnicas EPMA (microanálise eletrônica) e difratometria de raio-x de baixo ângulo para determinar a composição atômica e a estrutura cristalina, respectivamente. O momento magnético, m , de cada filme foi medido em função da temperatura, T, e do campo magnético aplicado, H, usando um magnetômetro SQUID (superconducting quantum interference device). Os filmes são amorfos para para 0,15 < x < 0,85, mas a coercividade foi observada em todos as amostras. A partir das curvas m vs T, foi observado um forte ordenamento magnético para T < TB. Para T > T B as amostras se mostram paramagnéticas. Os valores de T B foram observados em baixa temperatura (entre 5 e 50 K). A temperatura de Curie-Weiss, deduzida a partir das curvas x -1 vs T, onde x é a suscetibilidade, aumentaram com x. O efeito magnetocalórico foi estudado a partir das isotermas de magnetização, M vs H, das quais a variação de entropia magnética, D S M, foi obtida. As curvas D SM vs T exibiram máximos que variam entre 5 K e temperatura ambiente, dependendo da proporção de Gd / Abstract: The magnetic properties of films obtained by the co-deposition of a ferromagnetic and a non-magnetic components are the subject of intense investigation. In this work, the magnetic properties of Gdx W1-x, with x ranging from 0 to 1, were investigated. The films were deposited by magnetron sputtering from Gd and W targets. EPMA (electron probe microanalysis) and low-angle XRD (x-ray diffraction) were used to determine the film atomic composition and structure, respectively. The magnetic moment, m , of the films was measured as a function of temperature, T, and applied field H, using a SQUID (superconducting quantum device) magnetometer. The films were amorphous for 0.15 < x < 0.85 but coercivity was observed in all samples. From plots of m vs T, a strong magnetic ordering was observed for T < TB. For T > T B the samples were paramagnetic. TB-values occurred at low temperatures (between 5 K and 50 K). The Curie paramagnetic temperature, deduced from the x -1 vs T plots, where x is the susceptibility, was observed to increase with increasing x. The magnetocaloric effect was investigated from the magnetization isotherms, M vs H, from which the magnetic entropy change, D SM, caused by the application and removal of a 50 kOe field, was deduced. The D SM vs T curves exhibited maxima which varied from 5 K to about room temperature, depending on the Gd concentration / Mestrado / Física da Matéria Condensada / Mestre em Física
2

Efeitos de diluição química no composto intermetálico GdIn3

Silva, Leonardo de Sousa 20 February 2013 (has links)
This work proposes the development of a technique to growth of single crystals through metallic flux technique at the Sergipe State. Besides, the system YxGd1-xIn3 (0 x 0.5 to pass of 0.10 % ) has been obtained via this technique and its structural and magnetic properties are studied. X-ray diffraction results have been performed in order to verify if the desired crystalline phase was obtained. The experimental results show that it has been grown with success. The magnetic characterization is carried out through magnetic susceptibility data as function of temperature (2 x 300 K) and magnetic field (??7 H 7T). The T-dependence of the magnetization shows a suppression of the magnetic ordering temperature with increasing of the yttrium concentration. The analyses of these experimental data show that the system presents magnetic frustration which is linked to the dilution effect introduced by the yttrium ion in the gadolinium site. The magnetization data as function of magnetic field carried out at 2 K show a usual behavior of a material with antiferromagnetic ordering. / Este trabalho propôs a implementação da técnica de crescimento de monocristais via fluxo metálico, na Universidade Federal de Sergipe (UFS) campus de itabaiana. Além disso, o sistema YxGd1-xIn3 (0 < x < 0.5 a passo de 0.10 % ) foi obtido através dessa técnica e as propriedades estruturais e magnéticas foram estudadas. Medidas de difração de raios X foram realizadas com o intuito de verificar o crescimento da fase cristalina desejada. Os dados mostraram que ela foi obtida com sucesso. A caracterização magnética foi feita através de medidas de susceptibilidades magnética em função da temperatura (2 < x < 300 K) e do campo magnético (-7 < H < 7T). As medidas de magnetização em função da temperatura mostraram uma supressão da temperatura de ordenamento magnético com o aumento da concentração de ítrio. As análises desses dados mostraram que o sistema apresenta frustração magnética que está ligado ao efeito de diluição introduzido pelo íon de ítrio no sitio do gadolínio. As medidas de magnetização em função do campo magnético realizadas a 2 K mostraram um comportamento típico de um material com ordenamento antiferromagnético.