Made available in DSpace on 2014-06-11T19:25:33Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-05-28Bitstream added on 2014-06-13T19:53:26Z : No. of bitstreams: 1 solano_rav_me_ilha.pdf: 1596702 bytes, checksum: 57065466a13a3d33408ee670525cd7f2 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Neste trabalho foram estudados os filmes supercondutores do sistema BPSCCO ( (2-X) X 2 2 3 10 Bi Pb Sr Ca Cu O ), depositados em dois substratos diferentes (lâmina de prata e cristal de aluminato de lantânio). Estas deposições foram feitas pelo método de Dip coating, e foram feitas 3 deposições para cada substrato em seguida foi submetido a um tratamento térmico. Os resultados da medida elétrica do filme depositado nos substratos confirmaram o estado supercondutor a uma temperatura crítica (Tc) de 80K. Para determinar a temperatura crítica Tc foram efetuadas as medidas de resistência em função da temperatura. A Junção foi montada no Laboratório de Vidros e Cerâmica do Departamento de Física e Química da UNESP. As Junções Josephson usadas neste trabalho foram: Junções SIS (supercondutor – isolante – supercondutor) e SNS (supercondutor – metal normal – supercondutor), sobre as quais se mediu a corrente (I) em função da voltagem (V) obtendo-se as curvas característica da junção. As barreiras usadas nas junções foram de dois tipos: óxido de alumínio e a prata (metal). O alumínio foi depositado utilizando-se uma evaporadora em alto vácuo e posteriormente oxidado em um forno a uma temperatura de 400ºC durante uma hora; e a prata, depositada com a técnica de Sputtering. O efeito túnel ou tunelamento é característico em Junções Josephson. No entanto, para que esse efeito ocorra é necessário que a espessura do isolante seja da ordem de 10 Å. Portanto, trabalhamos de tal forma que a deposição fosse feita para que obtivessemos isolantes com essa espessura. Os resultados obtidos com as medidas de corrente e voltagem mostraram que a curva característica de tunelamento apresentou a forma prevista pela teoria. / In this work, we have studied the superconducting thin films of the system BPSCCO ( (2-X) X 2 2 3 10 Bi Pb Sr Ca Cu O ) with critical temperature around 110 K. The films were deposited in two different substrates (thin foil of silver and lanthanum aluminate polished crystal). These depositions have been made by the method called Dip coating, and it has been made 3 depositions for each substrate after that they were submitted to a thermal treatment. Electrical measurements of the films have confirmed the superconducting state to a critical temperature (Tc) around 80K. Critical temperature has been determined by measures temperature dependence of the resistance. The Junction was mounted in the Laboratory of Glasses and Ceramics of the Department of Physics and Chemistry of the FEIS-UNESP. The proposal of this work was to study two types of Josephson Junctions: SIS (Superconducting - Isolating - Superconducting) and SNS (Superconducting - Normal metal - Superconducting). Josephson junctions Characteristic Curves were done measuring dc electrical current (I) as a function of the voltage (V). It was used two kinds of barriers: aluminum oxide and silver. Aluminum was deposited using a high vacuum evaporator after this it was oxidized by thermal process using an oven, it was applied a thermal treatment around 400ºC during one hour. Silver was deposited using Sputtering technique. The tunnel effect or tunneling is characteristic property of the Josephson Junctions, although, this effect occurs just for barriers with thickness below tenth of nm. In this way, we have tried to get insolated barriers with the same order thickness as described above. Our results have shown that it is possible to observe the characteristic tunneling curve predicted by the theory.

Orientador: Cláudio Luiz Carvalho / Banca: Hermes Adolfo de Aquino / Banca: Edson Sardella / Resumo: Neste trabalho foram estudados os filmes supercondutores do sistema BPSCCO ( (2-X) X 2 2 3 10 Bi Pb Sr Ca Cu O ), depositados em dois substratos diferentes (lâmina de prata e cristal de aluminato de lantânio). Estas deposições foram feitas pelo método de Dip coating, e foram feitas 3 deposições para cada substrato em seguida foi submetido a um tratamento térmico. Os resultados da medida elétrica do filme depositado nos substratos confirmaram o estado supercondutor a uma temperatura crítica (Tc) de 80K. Para determinar a temperatura crítica Tc foram efetuadas as medidas de resistência em função da temperatura. A Junção foi montada no Laboratório de Vidros e Cerâmica do Departamento de Física e Química da UNESP. As Junções Josephson usadas neste trabalho foram: Junções SIS (supercondutor - isolante - supercondutor) e SNS (supercondutor - metal normal - supercondutor), sobre as quais se mediu a corrente (I) em função da voltagem (V) obtendo-se as curvas característica da junção. As barreiras usadas nas junções foram de dois tipos: óxido de alumínio e a prata (metal). O alumínio foi depositado utilizando-se uma evaporadora em alto vácuo e posteriormente oxidado em um forno a uma temperatura de 400ºC durante uma hora; e a prata, depositada com a técnica de Sputtering. O efeito túnel ou tunelamento é característico em Junções Josephson. No entanto, para que esse efeito ocorra é necessário que a espessura do isolante seja da ordem de 10 Å. Portanto, trabalhamos de tal forma que a deposição fosse feita para que obtivessemos isolantes com essa espessura. Os resultados obtidos com as medidas de corrente e voltagem mostraram que a curva característica de tunelamento apresentou a forma prevista pela teoria. / Abstract: In this work, we have studied the superconducting thin films of the system BPSCCO ( (2-X) X 2 2 3 10 Bi Pb Sr Ca Cu O ) with critical temperature around 110 K. The films were deposited in two different substrates (thin foil of silver and lanthanum aluminate polished crystal). These depositions have been made by the method called Dip coating, and it has been made 3 depositions for each substrate after that they were submitted to a thermal treatment. Electrical measurements of the films have confirmed the superconducting state to a critical temperature (Tc) around 80K. Critical temperature has been determined by measures temperature dependence of the resistance. The Junction was mounted in the Laboratory of Glasses and Ceramics of the Department of Physics and Chemistry of the FEIS-UNESP. The proposal of this work was to study two types of Josephson Junctions: SIS (Superconducting - Isolating - Superconducting) and SNS (Superconducting - Normal metal - Superconducting). Josephson junctions Characteristic Curves were done measuring dc electrical current (I) as a function of the voltage (V). It was used two kinds of barriers: aluminum oxide and silver. Aluminum was deposited using a high vacuum evaporator after this it was oxidized by thermal process using an oven, it was applied a thermal treatment around 400ºC during one hour. Silver was deposited using Sputtering technique. The tunnel effect or tunneling is characteristic property of the Josephson Junctions, although, this effect occurs just for barriers with thickness below tenth of nm. In this way, we have tried to get insolated barriers with the same order thickness as described above. Our results have shown that it is possible to observe the characteristic tunneling curve predicted by the theory. / Mestre

Made available in DSpace on 2016-06-02T20:15:20Z (GMT). No. of bitstreams: 1 2679.pdf: 25013011 bytes, checksum: c8fa361775e24d238927a782402fff59 (MD5) Previous issue date: 2009-10-16 / Universidade Federal de Sao Carlos / In this thesis we studied the quantum effects in networks of Josephson junctions under the induction of vortices and as a consequence of the size of the sample itself. For this, it also was carried out all the instrumentation required to achieve that goal. The superconducting devices known as Josephson junctions offer the opportunity to study a wide variety of concepts of basic physics, especially when they are in the form of twodimensional arrays called networks. In particular, these structures allow us to study quantum phenomena such as tunneling Josephson dc / ac, proximity effect, Coulomb blockade, quantum fluctuations and others like phase transition of Berezinsky-Kosterlitz-Thouless (BKT), all present in these devices. In particular, in this thesis we study two-dimensional networks of Josephson junctions of types SNS (superconductor-normal-superconductor) and SIS (superconductor-insulatorsuperconductor) with composition Nb -CuxAlyOz-Nb. The study of these samples was performed by obtaining the characteristic curves V × I with and without applied magnetic field. The analysis of these curves was performed by the law of power scale: ��������������for the SNS network, and ������������������/�������� for the SIS networks. The fact th��at ��t��w��o types of formulas adjustment is due to the asymptotic behavior present in these samples. Moreover, the temperature of the BKT transition was determined for ��������������������3. The analysis of the experimental obtained results clearly shows the dependence of quantum effects on the size of the samples studied. / Neste trabalho de Tese foram estudados os efeitos quânticos em redes de junções Josephson decorrentes da indução de vórtices e como conseqüência do tamanho da própria amostra. Para isso, também fora desenvolvida toda a instrumentação associada necessária para alcançar esse objetivo. Os dispositivos supercondutores conhecidos como junções Josephson oferecem a oportunidade de estudar uma ampla variedade de conceitos de física básica, principalmente quando eles se encontram na forma de arranjos bidimensionais denominados de redes. Em particular, estas estruturas permitem estudar fenômenos quânticos tais como tunelamento Josephson dc/ac, efeito de proximidade, bloqueio de Coulomb, flutuações quânticas e outras como a transição de fase de Berezinsky-Kosterlitz-Thouless (BKT), todos eles presentes nestes dispositivos. Em particular, nesta Tese estudamos redes de junções Josephson bidimensionais dos tipos SNS (supercondutor-normal-supercondutor) e SIS (supercondutor-isolante-supercondutor) com composição Nb-CuxAlyOz-Nb. O estudo dessas amostras foi realizado através da obtenção das curvas características V×I com e sem campo magnético aplicado. A análise dessas curvas foi realizada mediante a lei de escalas de potencias: ������������������������ para as redes SNS, e ������������������/�������� para as redes SIS. O fato de ter dois tipos de fórmulas de ajuste é devido ao comportamento assintótico presente nessas amostras. Além disso, a temperatura de transição de BKT foi determinada para ��������������������3. A análise dos resultados experimentais obtidos mostra claramente a dependência desses efeitos quânticos com o tamanho das amostras estudadas.

Orientador: Iakov Veniaminovitch Kopelevitch / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-13T05:43:34Z (GMT). No. of bitstreams: 1 GutierrezYatacue_DiegoFernando_M.pdf: 13276293 bytes, checksum: 707c38ac7116b9830e881ac37cc37b9e (MD5) Previous issue date: 2009 / Resumo: No intuito de verificar a existência de correlações supercondutoras em grafite, estudamos a possível existência do fenômeno conhecido como efeito de proximidade gigante em amostras de grafite pirolítica altamente orientada (HOPG). Medidas de magneto-transporte realizadas em amostras de HOPG com eletrodos supercondutores de In ou In-Pb revelaram a ocorrência de efeito de proximidade em uma escala muito maior que o comprimento de coerência dos eletrodos supercondutores, o que indica que a grafite pode ser considerada um supercondutor com flutuações de fase. Além disso, nossos estudos revelaram uma supressão do efeito de proximidade para campos magnéticos da ordem de 1 kOe aplicado perpendicularmente aos planos de grafite. Adicionalmente, realizamos estudos comparativos do efeito de proximidade em bismuto metálico. Discutimos os resultados obtidos em termos de modelos teóricos propostos para este assunto. / Abstract: In order to verify the existence of superconducting correlations in graphite, in this work we studied the possibility of the so-called giant proximity effect in highly oriented pyrolytic graphite (HOPG) samples. Magnetoresistance measurements performed on various thoroughly characterized HOPG samples with attached superconducting In or Pb-In electrodes revealed the occurrence of proximity effect on a scale much bigger than a coherence length of superconducting electrodes, indicating that graphite can be considered as a phase-fluctuating superconductor, indeed. Besides, our studies revealed a suppression of the proximity effect in magnetic field H ~ 1 kOe applied perpendicularly to graphene planes. Additionally, we performed comparative studies of the proximity effect in semimetallic bismuth. We discuss the obtained results in terms of available theoretical models. / Mestrado / Física da Matéria Condensada / Mestre em Física