This thesis deals with the influence of process parameters on the contamination level of powder materials produced by mechanical alloying (MA) technology. For this purpose austenitic stainless steel 316 L and equiatomic CoCrFeNi high-entropy alloy (HEA) were prepared by high-energy ball milling. Both materials were milled in argon and nitrogen atmospheres from 5 to 30 hours. Spark plasma sintering method (SPS) was then used for consolidation of chosen powder samples. Chemical analysis of contamination within MA was carried out using combustion analysers for determination of carbon, oxygen, and nitrogen contents after different lengths of milling. Also differences in chemical composition of powder and corresponding bulk samples were measured. The microstructure analysis using scanning electron microscopy (SEM) of both powder and bulk materials was executed with focus on oxide and carbide presence and dispersion. Increasing content of carbon with increasing milling time was observed across all measured samples. This contamination is attributed to using milling vial made of tool steel AISI D2 (containing 1,55 wt. % of carbon). Increase of carbon content within consolidation using SPS was also observed. Milling of specimens using N2 as milling atmosphere caused higher contamination level in both AISI 316 L and HEA compared to milling in argon.

These diploma thesis is focused on assessment of hazardous metals in soils near the road Rudná in Ostrava. Seventeen sampling sites have been chosen along this road, samples from this sites were collected in three series. The amounts of mercury, lead, copper, cadmium, zinc, vanadium and manganese were determined. There was also assessed contamination of selected sites using contamination factor and degree of contamination.

This diploma thesis deals with a potential contamination of hazardous metals of soil and sediments. The metals cadmium, copper, lead and mercury were chosen, their specification, limited concentration and methods of determination are also described in thesis. City Jihlava and its surroundings were chosen for evaluating pollution of the soil and sediments in this area. In collected samples of the soil and sediments presence of copper, cadmium, lead and mercury were detected via atomic absorption spectrometry (F-AAS, ET-AAS, AMA 254). The metal pollution of soils and sediments by hazardous elements in Jihlava River and in Jihlava region was evaluated.

Mineralogical and geochemical characteristics of metallurgical wastes from the Cu-Co smelters situated in the Zambian Copperbelt have been investigated. A number of instrumental analytical methods (XRD, SEM/EDS, EPMA, TEM/EDS) has been used to identify primary and secondary phases in smelter slags and dusts. A set of leaching experiments (CEN/TS 14997 pH-static test, EN 12457 batch test) in combination with geochemical modelling has been performed, with the emphasis on the leaching behaviour of potential contaminants and their release as a function of the pH. The effect of sample preparation on metal leachability from slag was also evaluated, considering the grain size reduction required by the standardised leaching protocols. Environmental and health risk assessments of the dust samples have been performed. It was shown that the main carriers of metals in the studied slags were Cu sulphides (bornite, digenite, chalcocite), Co sulphides (cobaltpentlandite), Co-bearing intermetallic phases and alloys. Copper and cobalt were detected in major silicates and spinels, substituting for Fe or Mg in their structures, and in glass. The presence of secondary metal-bearing phases observed on the slag surfaces indicated the reactivity of the slags on contact with water/atmosphere. It was reported that in...

This master's thesis deals with the issue of volcanic ash as a complex and its impact on aviation, including the volcanic activity itself (conditions for its existence, for existence of eruptions and their basic products). In addition, the thesis also deals with effect of volcanic ash on aircraft and airports, possibilities of its detection or monitoring as well as mechanism of its spreading in airspace. The emphasis is laid mainly on air incidents related to volcanic ash and on danger it poses to the airspace of the Czech Republic.