More complex and bigger structures have increased the applicability of low alloy high strength steels due to weight and cost reductions in these projects. One of the requirements for the use of these materials is the preservation of performance after welding. Meanwhile, the norms on which the Welding Procedures Specifications (WPS) are based have not yet considered the development of modern steel and its new production process, resulting in unnecessary welding costs that diminish the profits of the application of this type of steel. This thesis aimed to develop and evaluate an experimental methodology to guide the creation and control of welding procedures for structural steel through a microstructural atlas of the heat affected zone (HAZ) in a thermomechanical control process (TMCP), 65 ksi steel (ASTM A572 Grade 65). This steel was used in the project of an industrial building for CBMM in Araxá, Minas Gerais, Brazil. It is proposed that through a microstructural atlas of a given steel, it is possible to determine the range of cooling rates that the steel may suffer during welding without affecting mechanical properties and without risking cold cracks. When comparing the microstructure of steel welds performed in field conditions, it is possible to determine the heat input range for a given process in the preparation of a WPS. The selected case study is from a high strength low alloy class 65 ksi steel (ASTM A572 Grade 65) that was used in the structure of an industrial building. The steel was produced using TMCP. The atlas was created via the construction of a continuous cooling transformation diagram using physical simulation (dilatometer and Gleeble) of the coarse grain HAZ (GCHAZ). The characterization of the simulated region was performed by metallography and mechanical tests. The microstructure of real welds made by a qualified WPS were compared to the atlas in order to certify the correct use of parameters and to validate the method. The methodology was also qualified and the potential economic benefits were quantified (based only on the reduction of consumables used and the increased availability of the welding process machine) for the selected industrial project. The mapped microstructures varied from martensite (at high cooling rates) to pearlite/ferrite with large grain size (at low cooling rates). There was remarkable prevalence of bainitic microstructure in a wide range of cooling rates, consistent with the chemical composition of the steel studied. Comparisons with real weld microstructures showed the atlas is compatible with them, and that it can more accurately describe the effective thermal cycle xi that occurs in the coarse grain region of the HAZ (other regions were not included). The application of this methodology in the development of new WPS would allow greater flexibility in the welding procedures, including welding without preheating. In this respect alone, it was possible to forecast savings of approximately R$200,000.00, 1,000 hours of processing and 172 tonnes of carbon equivalent emissions. / Estruturas cada vez mais complexas e de maiores dimensões vêm aumentando a aplicabilidade de aços de baixa liga e alta resistência, devido à redução de peso e custo dessas estruturas. Um dos requisitos para o uso desses materiais é a manutenção do desempenho após soldagem. Entretanto, as normas em que se baseiam as Especificações de Procedimentos de Soldagem (EPS) ainda não consideram aços mais modernos em termos de rota de fabricação, o que pode fazer com que custos desnecessários de soldagem minimizem os ganhos da aplicação desses aços. Este trabalho teve como objetivo o desenvolvimento e avaliação de uma metodologia para, experimentalmente, orientar a elaboração e o controle da aplicação de procedimentos de soldagem para aços estruturais, através de atlas microestrutural de regiões da zona afetada pelo calor (ZAC). Propõe-se que, através de um atlas microestrutural de um dado aço, seja possível determinar a faixa otimizada de energia de soldagem para um dado processo na elaboração e aplicação da EPS e, consequentemente, as velocidades de resfriamento que o aço possa sofrer durante a soldagem, sem perder as propriedades mecânicas e sem colocálo em risco quanto a trincas a frio. Tomou-se como estudo de caso o aço produzido por laminação controlada de classe de resistência de 65 ksi (ASTM A572 Grau 65), utilizado em um projeto de um prédio industrial na empresa CBMM. Trata-se de um aço fabricado pelo processo TMCP com resfriamento acelerado. A elaboração do Atlas se deu através da construção de um diagrama CCT, por simulação física (dilatômetro e Gleeble), da região de grãos grosseiros da zona afetada pelo calor (ZAC GG). Foram feitas caracterizações metalográficas e mecânicas das regiões simuladas. Microestruturas de soldas realizadas com EPS qualificadas foram comparadas com as do Atlas para se certificar da adequabilidade dos parâmetros utilizados e validação da abordagem. Foram realizadas ainda a qualificação e quantificação de potenciais benefícios econômicos no citado projeto industrial, obtidos pelo uso desta metodologia. As microestruturas apresentadas no mapa variavam de martensíta, para altas taxas de resfriamento, até perlita/ferrita de tamanho de grão elevado, para baixas taxas de resfriamento. Observou-se notável predominância da microestrutura bainítica em uma larga faixa de taxas de resfriamento, compatível com as propriedades e composição do aço estudado (alta soldabilidade). As comparações com as microestruturas de soldas reais mostraram que o Atlas pode descrever de forma precisa o ciclo térmico efetivamente imposto ix na ZAC GG. Concluiu-se que a aplicação desta metodologia na elaboração de novas EPS permitiria uma maior flexibilidade nos procedimentos de soldagem, admitindo inclusive soldagem sem pré-aquecimento. Em relação a não necessidade de pré-aquecimento, podese prever uma economia significante de custos e redução de emissão de gases que provocam efeito estufa. / Mestre em Engenharia Mecânica

Made available in DSpace on 2016-03-15T19:36:54Z (GMT). No. of bitstreams: 1 Maria Claudia Lopes Guerra.pdf: 9968717 bytes, checksum: 7d0e4986884ffa382a835b641ed76573 (MD5) Previous issue date: 2015-06-12 / Fundo Mackenzie de Pesquisa / The ECAP (Equal Channel Angular Pressing) is a mechanical process of Severe Plastic Deformation (SPD) where a sample is subjected to a shearing force when passing through the region of intersection of two channels. The main goal of this method is Severe Plastic Deformation achieve a microstructure with ultrafine grains, which have much higher than the equivalent coarse grain materials physical properties, such as an increase in strength and toughness simultaneously. What makes this increasingly interesting technique is that as there is no reduction cross section is possible to obtain plastic strain accumulation and therefore gain in grain order of nanometer scale. The great advantage of ECAP is to achieve a much higher degree of strain hardening than obtained by conventional methods of plastic deformation, and consequently a grain refining much higher as well. The importance of the study of severe plastic deformation process is on improving the mechanical performance of the materials and the possibility of a better understanding of the mechanisms of strain hardening, which may indicate a new path for producing high-strength materials, possibly scaled industrial. In this work are presented the microstructural, mechanical and electrical analysis of the aluminum alloy AA 1050 samples, commonly used for electrical purposes, with ultrafine grains (typical grain size below a micron) resulting from processing by ECAP, based on the method of SPD. / A PCE (Prensagem em Canais Equiangulares) consiste num processo mecânico de Deformação Plástica Intensa (DPI) onde um corpo de prova é sujeito a um esforço de cisalhamento ao passar pela região de intersecção de dois canais. Os principais objetivos desse método de Deformação Plástica Intensa é alcançar uma microestrutura com grãos ultrafinos, os quais possuem propriedades físicas muito superiores aos equivalentes materiais de grãos grosseiros, como um aumento em resistência mecânica e tenacidade simultâneas. O que torna esta técnica cada vez mais interessante é que como não há redução da seção transversal é possível obter acumulo de deformação plástica e com isso obter grãos na ordem de escala nanométrica. A grande vantagem do PCE é alcançar um grau de encruamento muito superior do que obtido por métodos convencionais de deformação plástica, e consequentemente, um refino de grão muito superior também. A importância do estudo do processo de deformação plástica intensa está na melhoria do desempenho mecânico dos materiais e na possibilidade de uma melhor compreensão dos mecanismos de encruamento, fato que pode indicar um novo caminho para a produção de materiais de alta resistência mecânica, possivelmente em escala industrial. Nesse trabalho são apresentadas as análises microestruturais, mecânicas e elétricas de amostras de ligas de alumínio AA 1050, comumente utilizadas para fins elétricos, com estrutura de grãos ultrafinos (tamanho de grão típico abaixo de um micrometro) resultantes do processamento por PCE, baseada no método de DPI.

The aim of this thesis is to analyze a media campaign called Responsible Together, which is focused on decrease of violence against women. Campaign Responsible Together is created by non-profit organizations that are part of civil society. This thesis brings a description of the creative process of the campaign, it's target group, and communication mix. One part of this thesis also introduces the specifics of marketing in the non-profit field. A case study was selected as a research design because it allows combining more than one method of collecting data. These methods were document analysis, analysis of graphics, and participatory observation.

The goal of this dissertation is to describe an evolution of visions of the Slovak future, as they were introduced during the Great War (1914-1918) by groups of Slovaks living mainly abroad. It strives to decide, which of these visions had a chance to become real and which were only fantasies without real political importance. To reach this goal it tries to describe Slovak relations to other relevant nations in pre-war years and also the position of Slovaks in their fatherland or abroad including the ideologies by which they were influenced. One of most decisive goals of this dissertation should be answering the question if the Czecho-Slovak orientation was the only alternative to the idea of Hungarian state for Slovak politicians, or if the victory of this conception in 1918 was just a result of unpredictable processes, and whether other conceptions had their chance to influence the Slovak future, too.