This thesis provides a structural and materials engineering explanation for many of the running fractures that occurred in steel structures during the destructive Kobe and Northridge earthquakes in the mid 1990s. A method is developed that allows the ductile endurance of structural steel members subjected to cyclic plastic deformation during earthquakes to be assessed and for pre-necking running fractures to be avoided. The study commenced following the 2000 World Earthquake Conference in Auckland. The conference brought together the findings of the huge research effort, in America, Japan, Europe and New Zealand, that followed the Kobe and Northridge earthquakes. The running fractures that had occurred in steel structures represented an unpredicted failure mode that structural engineers have not known how to predict or suppress through the engineering design process. A clear fundamental understanding of the causes and how to prevent the fractures did not arise from the conference. In fact apparently conflicting results were reported. Full scale cyclic tests in New Zealand on structural assemblies had not resulted in running fractures, whereas tests in American and Japan had. Structural engineers designing earthquake resistant structures rely on constructional steel to be materially homogeneous and nominally tri-linear in behaviour. Steel is expected to behave elastically under regular in-service loading, have a reliable and flat yield stress-strain characteristic, and under overload then develop predictable levels of strain-hardening in conjunction with significant plastic elongation up to its ultimate tensile strength. Steel is expected to eventually fracture after further plastic elongation and necking. Ductile design strategies and methods utilise the plastic elongation characteristics of steel to protect structures in earthquake. Plastic deformation is considered to beneficially dissipate energy generated in the structure by a severe earthquake and also dampen the structure’s response. The occurrence of running fracture without significant cyclic plastic deformation and before section necking in steelwork, therefore undermines the basis of the ductile seismic design approach. The initial part of the thesis is devoted to bringing together the fundamental aspects of materials engineering related to fracture of constructional steel. This is intended to provide a bridge of knowledge for structural engineering practitioners and researchers not fully conversant with materials engineering aspects of fracture. Fracture behaviour in steel is a broad and complex topic that developed rapidly in the twentieth century driven by the demands of technological growth. The unexpected fracture of welded liberty ships at sea in World War 2; the need for reliable long term containment for the nuclear reactors in the 1950s and 1960s; and prevention of fatigue failures in aircraft frames since the 1950s all drove engineering research into steel fracture behaviour. There are many subtle variations in definitions in the published literature on fracture that can be confusing. Therefore an attempt has been made to clarify terminology. The term brittle fracture in particular is only used in this thesis as applying to running fracture when the general or far field tensile stresses are below the yield stress of the steel. The term pre-necking or running fracture is preferred to describe the condition more broadly which may occur prior to and also after general yielding, but before section necking. Running fracture is a manifestation of pre-necking fracture in which insufficient plastic flow is available in the assembly to absorb the energy released upon fracture. The experimental studies investigated the behaviour of constructional steel commonly used in New Zealand, at various levels of plastic strain. This started with Charpy V-Notch (CVN) testing which revealed that a significant transition temperature shift and curve shape change occurs with increasing plastic strain and the associated strain-hardening. This showed that the ability of steel to avoid pre-necking or running fracture reduces as the level of plastic strain-hardening increases. Temperature controlled Crack Tip Opening Displacement (CTOD) testing was then undertaken. The setting of testing temperatures for the CTOD tests were guided by review of the CVN test results, using published CVN to fracture toughness correlation methods. However running cleavage fractures developed in the CTOD specimens at higher than predicted temperatures of 10 oC and 20 oC. These are typical service temperatures for structures in New Zealand and so are very likely to occur at the time of an earthquake. The implication from this is that there are levels of strain-hardening and conditions of material notching constraint that can lead to pre-necking and running fracture in New Zealand fabricated steel structures, under severe earthquake loading. Care was taken in the CTOD testing to monitor and maximise the capture of data electronically using a specially developed Direct Current Potential Drop method. This allowed the test results to be analysed and considered in varying ways, leading to a consistent assessment of the CTOD, crack growth, and the specific work of fracture in each test piece. While CTOD test results have sometimes been published by structural and welding engineering researchers in the wake of Kobe and Northridge, the results were typically of little use for this study as the CTOD initiation point was generally not identified effectively. The effect of remote plastic flow in the specimens was also not adequately accounted for. The CTOD test results were often simply used to help correlate other factors observed by the researchers. Side-grooving of specimens was not reported as having been used in any of the published results reviewed. When conducting CTOD test with highly ductile constructional steels it is very difficult to get useful CTOD results if the specimens are not side-grooved, as significant necking and tunnelling will otherwise occur and limit the usefulness of the results. Work by Knott and also by McRobie and Smith was seminal in terms of identifying some critical aspects of plane strain development in CTOD tests, and the links to non-metallic particle density with respect to fracture toughness and CTOD at initiation. Some of their findings with regards to the effect of pre-strain on CTOD initiation were subsequently found to confirm the experimental findings in this study. No effective methodology for prediction of pre-necking or running fracture in a structural member or assembly when subjected to gross plastic cyclic deformation was found to exist in the literature. It was concluded however that the principles of specific work of fracture, and monotonic and cyclic fracture similitude were particularly relevant. These were therefore utilised in the development of the design method proposed in this thesis. The CTOD test results were reviewed, isolating the remote plastic flow component, to determine the critical specific work of fracture property Rc of the steels tested. A meeting with Professor Kuwamura at the University of Tokyo was providential, allowing discussion of his similitude principle, and observations in person of some of the fractured specimens developed during his full scale test series’. Running fractures with cleavage were evident in the specimens, with their tell-tale chevron markings. He had predicted running fracture problems in structures in Japan ahead of the Kobe earthquake and been largely ignored. His insights were subsequently seriously considered in Japan after the earthquake. He and his colleagues developed the principle of structural similitude that relates monotonic fracture displacement ductility to cyclic fracture displacement ductility for a particular assembly. This arose from their observation that running fractures developed from ductile crack formation at blunt notches in structures. The similitude principle has echoes of the Coffin-Manson approach to ductile crack initiated low cycle fracture. The principle of similitude has a log–log relationship as does the Manson-Coffin relationship. So where notch plasticity controls the initiation of fracture in a structural assembly it is conceptually reasonable to expect that the number of cycles to initiation of fracture from a notch will have a log–log relationship to the amplitude of the cyclic strain developed in the notch. Kuwamura found that steel assemblies with lower CVN energy had reduced cyclic fracture endurance than the same assemblies made with steel with higher CVN impact energy. However no method of predicting performance of any particular assembly could be developed from his observations. The benefit of his method primarily relates to the minimising of testing necessary to assess the fracture limited cyclic displacement ductility of a structural assembly. However it doesn’t provide a means for designing a structural assembly to achieve specific levels of ductile endurance other than clearly identifying the need to use steel with good CVN characteristics. The most significant development arising from this thesis is therefore the development of a design method to assess cyclic ductile endurance. The method utilises the specific work of fracture properties obtained from CTOD specimens of the steel in conjunction with a relatively simple fracture mechanics assessment and an elasto-plastic finite element analysis (FEA). The FEA model is used to determine the displacement ductility of the assembly at the calculated onset of pre-necking fracture. The elasto-plastic stress–strain properties of the steel in various pre-strain states required for the FEA may be derived from tensile testing. Kuwamura’s similitude principle is then used to predict cyclic plastic endurance at various constant displacement ductility amplitudes. The method is extended using Miner’s rule to allow for the effects of increasing variable amplitude cyclic plastic loading. In summary the thesis explains why pre-necking and running fractures occur in steel members subjected to cyclic plastic deformation during a severe earthquake. In addition a method for consistently assessing the ability of structural steel assemblies to achieve a specified level of ductile endurance during earthquakes is proposed. The method is verified against published results for a cyclic test of a simple steel member with a crack at mid-span. / Whole document restricted, but available by request, use the feedback form to request access.

This thesis provides a structural and materials engineering explanation for many of the running fractures that occurred in steel structures during the destructive Kobe and Northridge earthquakes in the mid 1990s. A method is developed that allows the ductile endurance of structural steel members subjected to cyclic plastic deformation during earthquakes to be assessed and for pre-necking running fractures to be avoided. The study commenced following the 2000 World Earthquake Conference in Auckland. The conference brought together the findings of the huge research effort, in America, Japan, Europe and New Zealand, that followed the Kobe and Northridge earthquakes. The running fractures that had occurred in steel structures represented an unpredicted failure mode that structural engineers have not known how to predict or suppress through the engineering design process. A clear fundamental understanding of the causes and how to prevent the fractures did not arise from the conference. In fact apparently conflicting results were reported. Full scale cyclic tests in New Zealand on structural assemblies had not resulted in running fractures, whereas tests in American and Japan had. Structural engineers designing earthquake resistant structures rely on constructional steel to be materially homogeneous and nominally tri-linear in behaviour. Steel is expected to behave elastically under regular in-service loading, have a reliable and flat yield stress-strain characteristic, and under overload then develop predictable levels of strain-hardening in conjunction with significant plastic elongation up to its ultimate tensile strength. Steel is expected to eventually fracture after further plastic elongation and necking. Ductile design strategies and methods utilise the plastic elongation characteristics of steel to protect structures in earthquake. Plastic deformation is considered to beneficially dissipate energy generated in the structure by a severe earthquake and also dampen the structure’s response. The occurrence of running fracture without significant cyclic plastic deformation and before section necking in steelwork, therefore undermines the basis of the ductile seismic design approach. The initial part of the thesis is devoted to bringing together the fundamental aspects of materials engineering related to fracture of constructional steel. This is intended to provide a bridge of knowledge for structural engineering practitioners and researchers not fully conversant with materials engineering aspects of fracture. Fracture behaviour in steel is a broad and complex topic that developed rapidly in the twentieth century driven by the demands of technological growth. The unexpected fracture of welded liberty ships at sea in World War 2; the need for reliable long term containment for the nuclear reactors in the 1950s and 1960s; and prevention of fatigue failures in aircraft frames since the 1950s all drove engineering research into steel fracture behaviour. There are many subtle variations in definitions in the published literature on fracture that can be confusing. Therefore an attempt has been made to clarify terminology. The term brittle fracture in particular is only used in this thesis as applying to running fracture when the general or far field tensile stresses are below the yield stress of the steel. The term pre-necking or running fracture is preferred to describe the condition more broadly which may occur prior to and also after general yielding, but before section necking. Running fracture is a manifestation of pre-necking fracture in which insufficient plastic flow is available in the assembly to absorb the energy released upon fracture. The experimental studies investigated the behaviour of constructional steel commonly used in New Zealand, at various levels of plastic strain. This started with Charpy V-Notch (CVN) testing which revealed that a significant transition temperature shift and curve shape change occurs with increasing plastic strain and the associated strain-hardening. This showed that the ability of steel to avoid pre-necking or running fracture reduces as the level of plastic strain-hardening increases. Temperature controlled Crack Tip Opening Displacement (CTOD) testing was then undertaken. The setting of testing temperatures for the CTOD tests were guided by review of the CVN test results, using published CVN to fracture toughness correlation methods. However running cleavage fractures developed in the CTOD specimens at higher than predicted temperatures of 10 oC and 20 oC. These are typical service temperatures for structures in New Zealand and so are very likely to occur at the time of an earthquake. The implication from this is that there are levels of strain-hardening and conditions of material notching constraint that can lead to pre-necking and running fracture in New Zealand fabricated steel structures, under severe earthquake loading. Care was taken in the CTOD testing to monitor and maximise the capture of data electronically using a specially developed Direct Current Potential Drop method. This allowed the test results to be analysed and considered in varying ways, leading to a consistent assessment of the CTOD, crack growth, and the specific work of fracture in each test piece. While CTOD test results have sometimes been published by structural and welding engineering researchers in the wake of Kobe and Northridge, the results were typically of little use for this study as the CTOD initiation point was generally not identified effectively. The effect of remote plastic flow in the specimens was also not adequately accounted for. The CTOD test results were often simply used to help correlate other factors observed by the researchers. Side-grooving of specimens was not reported as having been used in any of the published results reviewed. When conducting CTOD test with highly ductile constructional steels it is very difficult to get useful CTOD results if the specimens are not side-grooved, as significant necking and tunnelling will otherwise occur and limit the usefulness of the results. Work by Knott and also by McRobie and Smith was seminal in terms of identifying some critical aspects of plane strain development in CTOD tests, and the links to non-metallic particle density with respect to fracture toughness and CTOD at initiation. Some of their findings with regards to the effect of pre-strain on CTOD initiation were subsequently found to confirm the experimental findings in this study. No effective methodology for prediction of pre-necking or running fracture in a structural member or assembly when subjected to gross plastic cyclic deformation was found to exist in the literature. It was concluded however that the principles of specific work of fracture, and monotonic and cyclic fracture similitude were particularly relevant. These were therefore utilised in the development of the design method proposed in this thesis. The CTOD test results were reviewed, isolating the remote plastic flow component, to determine the critical specific work of fracture property Rc of the steels tested. A meeting with Professor Kuwamura at the University of Tokyo was providential, allowing discussion of his similitude principle, and observations in person of some of the fractured specimens developed during his full scale test series’. Running fractures with cleavage were evident in the specimens, with their tell-tale chevron markings. He had predicted running fracture problems in structures in Japan ahead of the Kobe earthquake and been largely ignored. His insights were subsequently seriously considered in Japan after the earthquake. He and his colleagues developed the principle of structural similitude that relates monotonic fracture displacement ductility to cyclic fracture displacement ductility for a particular assembly. This arose from their observation that running fractures developed from ductile crack formation at blunt notches in structures. The similitude principle has echoes of the Coffin-Manson approach to ductile crack initiated low cycle fracture. The principle of similitude has a log–log relationship as does the Manson-Coffin relationship. So where notch plasticity controls the initiation of fracture in a structural assembly it is conceptually reasonable to expect that the number of cycles to initiation of fracture from a notch will have a log–log relationship to the amplitude of the cyclic strain developed in the notch. Kuwamura found that steel assemblies with lower CVN energy had reduced cyclic fracture endurance than the same assemblies made with steel with higher CVN impact energy. However no method of predicting performance of any particular assembly could be developed from his observations. The benefit of his method primarily relates to the minimising of testing necessary to assess the fracture limited cyclic displacement ductility of a structural assembly. However it doesn’t provide a means for designing a structural assembly to achieve specific levels of ductile endurance other than clearly identifying the need to use steel with good CVN characteristics. The most significant development arising from this thesis is therefore the development of a design method to assess cyclic ductile endurance. The method utilises the specific work of fracture properties obtained from CTOD specimens of the steel in conjunction with a relatively simple fracture mechanics assessment and an elasto-plastic finite element analysis (FEA). The FEA model is used to determine the displacement ductility of the assembly at the calculated onset of pre-necking fracture. The elasto-plastic stress–strain properties of the steel in various pre-strain states required for the FEA may be derived from tensile testing. Kuwamura’s similitude principle is then used to predict cyclic plastic endurance at various constant displacement ductility amplitudes. The method is extended using Miner’s rule to allow for the effects of increasing variable amplitude cyclic plastic loading. In summary the thesis explains why pre-necking and running fractures occur in steel members subjected to cyclic plastic deformation during a severe earthquake. In addition a method for consistently assessing the ability of structural steel assemblies to achieve a specified level of ductile endurance during earthquakes is proposed. The method is verified against published results for a cyclic test of a simple steel member with a crack at mid-span. / Whole document restricted, but available by request, use the feedback form to request access.

This thesis provides a structural and materials engineering explanation for many of the running fractures that occurred in steel structures during the destructive Kobe and Northridge earthquakes in the mid 1990s. A method is developed that allows the ductile endurance of structural steel members subjected to cyclic plastic deformation during earthquakes to be assessed and for pre-necking running fractures to be avoided. The study commenced following the 2000 World Earthquake Conference in Auckland. The conference brought together the findings of the huge research effort, in America, Japan, Europe and New Zealand, that followed the Kobe and Northridge earthquakes. The running fractures that had occurred in steel structures represented an unpredicted failure mode that structural engineers have not known how to predict or suppress through the engineering design process. A clear fundamental understanding of the causes and how to prevent the fractures did not arise from the conference. In fact apparently conflicting results were reported. Full scale cyclic tests in New Zealand on structural assemblies had not resulted in running fractures, whereas tests in American and Japan had. Structural engineers designing earthquake resistant structures rely on constructional steel to be materially homogeneous and nominally tri-linear in behaviour. Steel is expected to behave elastically under regular in-service loading, have a reliable and flat yield stress-strain characteristic, and under overload then develop predictable levels of strain-hardening in conjunction with significant plastic elongation up to its ultimate tensile strength. Steel is expected to eventually fracture after further plastic elongation and necking. Ductile design strategies and methods utilise the plastic elongation characteristics of steel to protect structures in earthquake. Plastic deformation is considered to beneficially dissipate energy generated in the structure by a severe earthquake and also dampen the structure’s response. The occurrence of running fracture without significant cyclic plastic deformation and before section necking in steelwork, therefore undermines the basis of the ductile seismic design approach. The initial part of the thesis is devoted to bringing together the fundamental aspects of materials engineering related to fracture of constructional steel. This is intended to provide a bridge of knowledge for structural engineering practitioners and researchers not fully conversant with materials engineering aspects of fracture. Fracture behaviour in steel is a broad and complex topic that developed rapidly in the twentieth century driven by the demands of technological growth. The unexpected fracture of welded liberty ships at sea in World War 2; the need for reliable long term containment for the nuclear reactors in the 1950s and 1960s; and prevention of fatigue failures in aircraft frames since the 1950s all drove engineering research into steel fracture behaviour. There are many subtle variations in definitions in the published literature on fracture that can be confusing. Therefore an attempt has been made to clarify terminology. The term brittle fracture in particular is only used in this thesis as applying to running fracture when the general or far field tensile stresses are below the yield stress of the steel. The term pre-necking or running fracture is preferred to describe the condition more broadly which may occur prior to and also after general yielding, but before section necking. Running fracture is a manifestation of pre-necking fracture in which insufficient plastic flow is available in the assembly to absorb the energy released upon fracture. The experimental studies investigated the behaviour of constructional steel commonly used in New Zealand, at various levels of plastic strain. This started with Charpy V-Notch (CVN) testing which revealed that a significant transition temperature shift and curve shape change occurs with increasing plastic strain and the associated strain-hardening. This showed that the ability of steel to avoid pre-necking or running fracture reduces as the level of plastic strain-hardening increases. Temperature controlled Crack Tip Opening Displacement (CTOD) testing was then undertaken. The setting of testing temperatures for the CTOD tests were guided by review of the CVN test results, using published CVN to fracture toughness correlation methods. However running cleavage fractures developed in the CTOD specimens at higher than predicted temperatures of 10 oC and 20 oC. These are typical service temperatures for structures in New Zealand and so are very likely to occur at the time of an earthquake. The implication from this is that there are levels of strain-hardening and conditions of material notching constraint that can lead to pre-necking and running fracture in New Zealand fabricated steel structures, under severe earthquake loading. Care was taken in the CTOD testing to monitor and maximise the capture of data electronically using a specially developed Direct Current Potential Drop method. This allowed the test results to be analysed and considered in varying ways, leading to a consistent assessment of the CTOD, crack growth, and the specific work of fracture in each test piece. While CTOD test results have sometimes been published by structural and welding engineering researchers in the wake of Kobe and Northridge, the results were typically of little use for this study as the CTOD initiation point was generally not identified effectively. The effect of remote plastic flow in the specimens was also not adequately accounted for. The CTOD test results were often simply used to help correlate other factors observed by the researchers. Side-grooving of specimens was not reported as having been used in any of the published results reviewed. When conducting CTOD test with highly ductile constructional steels it is very difficult to get useful CTOD results if the specimens are not side-grooved, as significant necking and tunnelling will otherwise occur and limit the usefulness of the results. Work by Knott and also by McRobie and Smith was seminal in terms of identifying some critical aspects of plane strain development in CTOD tests, and the links to non-metallic particle density with respect to fracture toughness and CTOD at initiation. Some of their findings with regards to the effect of pre-strain on CTOD initiation were subsequently found to confirm the experimental findings in this study. No effective methodology for prediction of pre-necking or running fracture in a structural member or assembly when subjected to gross plastic cyclic deformation was found to exist in the literature. It was concluded however that the principles of specific work of fracture, and monotonic and cyclic fracture similitude were particularly relevant. These were therefore utilised in the development of the design method proposed in this thesis. The CTOD test results were reviewed, isolating the remote plastic flow component, to determine the critical specific work of fracture property Rc of the steels tested. A meeting with Professor Kuwamura at the University of Tokyo was providential, allowing discussion of his similitude principle, and observations in person of some of the fractured specimens developed during his full scale test series’. Running fractures with cleavage were evident in the specimens, with their tell-tale chevron markings. He had predicted running fracture problems in structures in Japan ahead of the Kobe earthquake and been largely ignored. His insights were subsequently seriously considered in Japan after the earthquake. He and his colleagues developed the principle of structural similitude that relates monotonic fracture displacement ductility to cyclic fracture displacement ductility for a particular assembly. This arose from their observation that running fractures developed from ductile crack formation at blunt notches in structures. The similitude principle has echoes of the Coffin-Manson approach to ductile crack initiated low cycle fracture. The principle of similitude has a log–log relationship as does the Manson-Coffin relationship. So where notch plasticity controls the initiation of fracture in a structural assembly it is conceptually reasonable to expect that the number of cycles to initiation of fracture from a notch will have a log–log relationship to the amplitude of the cyclic strain developed in the notch. Kuwamura found that steel assemblies with lower CVN energy had reduced cyclic fracture endurance than the same assemblies made with steel with higher CVN impact energy. However no method of predicting performance of any particular assembly could be developed from his observations. The benefit of his method primarily relates to the minimising of testing necessary to assess the fracture limited cyclic displacement ductility of a structural assembly. However it doesn’t provide a means for designing a structural assembly to achieve specific levels of ductile endurance other than clearly identifying the need to use steel with good CVN characteristics. The most significant development arising from this thesis is therefore the development of a design method to assess cyclic ductile endurance. The method utilises the specific work of fracture properties obtained from CTOD specimens of the steel in conjunction with a relatively simple fracture mechanics assessment and an elasto-plastic finite element analysis (FEA). The FEA model is used to determine the displacement ductility of the assembly at the calculated onset of pre-necking fracture. The elasto-plastic stress–strain properties of the steel in various pre-strain states required for the FEA may be derived from tensile testing. Kuwamura’s similitude principle is then used to predict cyclic plastic endurance at various constant displacement ductility amplitudes. The method is extended using Miner’s rule to allow for the effects of increasing variable amplitude cyclic plastic loading. In summary the thesis explains why pre-necking and running fractures occur in steel members subjected to cyclic plastic deformation during a severe earthquake. In addition a method for consistently assessing the ability of structural steel assemblies to achieve a specified level of ductile endurance during earthquakes is proposed. The method is verified against published results for a cyclic test of a simple steel member with a crack at mid-span. / Whole document restricted, but available by request, use the feedback form to request access.

This thesis provides a structural and materials engineering explanation for many of the running fractures that occurred in steel structures during the destructive Kobe and Northridge earthquakes in the mid 1990s. A method is developed that allows the ductile endurance of structural steel members subjected to cyclic plastic deformation during earthquakes to be assessed and for pre-necking running fractures to be avoided. The study commenced following the 2000 World Earthquake Conference in Auckland. The conference brought together the findings of the huge research effort, in America, Japan, Europe and New Zealand, that followed the Kobe and Northridge earthquakes. The running fractures that had occurred in steel structures represented an unpredicted failure mode that structural engineers have not known how to predict or suppress through the engineering design process. A clear fundamental understanding of the causes and how to prevent the fractures did not arise from the conference. In fact apparently conflicting results were reported. Full scale cyclic tests in New Zealand on structural assemblies had not resulted in running fractures, whereas tests in American and Japan had. Structural engineers designing earthquake resistant structures rely on constructional steel to be materially homogeneous and nominally tri-linear in behaviour. Steel is expected to behave elastically under regular in-service loading, have a reliable and flat yield stress-strain characteristic, and under overload then develop predictable levels of strain-hardening in conjunction with significant plastic elongation up to its ultimate tensile strength. Steel is expected to eventually fracture after further plastic elongation and necking. Ductile design strategies and methods utilise the plastic elongation characteristics of steel to protect structures in earthquake. Plastic deformation is considered to beneficially dissipate energy generated in the structure by a severe earthquake and also dampen the structure’s response. The occurrence of running fracture without significant cyclic plastic deformation and before section necking in steelwork, therefore undermines the basis of the ductile seismic design approach. The initial part of the thesis is devoted to bringing together the fundamental aspects of materials engineering related to fracture of constructional steel. This is intended to provide a bridge of knowledge for structural engineering practitioners and researchers not fully conversant with materials engineering aspects of fracture. Fracture behaviour in steel is a broad and complex topic that developed rapidly in the twentieth century driven by the demands of technological growth. The unexpected fracture of welded liberty ships at sea in World War 2; the need for reliable long term containment for the nuclear reactors in the 1950s and 1960s; and prevention of fatigue failures in aircraft frames since the 1950s all drove engineering research into steel fracture behaviour. There are many subtle variations in definitions in the published literature on fracture that can be confusing. Therefore an attempt has been made to clarify terminology. The term brittle fracture in particular is only used in this thesis as applying to running fracture when the general or far field tensile stresses are below the yield stress of the steel. The term pre-necking or running fracture is preferred to describe the condition more broadly which may occur prior to and also after general yielding, but before section necking. Running fracture is a manifestation of pre-necking fracture in which insufficient plastic flow is available in the assembly to absorb the energy released upon fracture. The experimental studies investigated the behaviour of constructional steel commonly used in New Zealand, at various levels of plastic strain. This started with Charpy V-Notch (CVN) testing which revealed that a significant transition temperature shift and curve shape change occurs with increasing plastic strain and the associated strain-hardening. This showed that the ability of steel to avoid pre-necking or running fracture reduces as the level of plastic strain-hardening increases. Temperature controlled Crack Tip Opening Displacement (CTOD) testing was then undertaken. The setting of testing temperatures for the CTOD tests were guided by review of the CVN test results, using published CVN to fracture toughness correlation methods. However running cleavage fractures developed in the CTOD specimens at higher than predicted temperatures of 10 oC and 20 oC. These are typical service temperatures for structures in New Zealand and so are very likely to occur at the time of an earthquake. The implication from this is that there are levels of strain-hardening and conditions of material notching constraint that can lead to pre-necking and running fracture in New Zealand fabricated steel structures, under severe earthquake loading. Care was taken in the CTOD testing to monitor and maximise the capture of data electronically using a specially developed Direct Current Potential Drop method. This allowed the test results to be analysed and considered in varying ways, leading to a consistent assessment of the CTOD, crack growth, and the specific work of fracture in each test piece. While CTOD test results have sometimes been published by structural and welding engineering researchers in the wake of Kobe and Northridge, the results were typically of little use for this study as the CTOD initiation point was generally not identified effectively. The effect of remote plastic flow in the specimens was also not adequately accounted for. The CTOD test results were often simply used to help correlate other factors observed by the researchers. Side-grooving of specimens was not reported as having been used in any of the published results reviewed. When conducting CTOD test with highly ductile constructional steels it is very difficult to get useful CTOD results if the specimens are not side-grooved, as significant necking and tunnelling will otherwise occur and limit the usefulness of the results. Work by Knott and also by McRobie and Smith was seminal in terms of identifying some critical aspects of plane strain development in CTOD tests, and the links to non-metallic particle density with respect to fracture toughness and CTOD at initiation. Some of their findings with regards to the effect of pre-strain on CTOD initiation were subsequently found to confirm the experimental findings in this study. No effective methodology for prediction of pre-necking or running fracture in a structural member or assembly when subjected to gross plastic cyclic deformation was found to exist in the literature. It was concluded however that the principles of specific work of fracture, and monotonic and cyclic fracture similitude were particularly relevant. These were therefore utilised in the development of the design method proposed in this thesis. The CTOD test results were reviewed, isolating the remote plastic flow component, to determine the critical specific work of fracture property Rc of the steels tested. A meeting with Professor Kuwamura at the University of Tokyo was providential, allowing discussion of his similitude principle, and observations in person of some of the fractured specimens developed during his full scale test series’. Running fractures with cleavage were evident in the specimens, with their tell-tale chevron markings. He had predicted running fracture problems in structures in Japan ahead of the Kobe earthquake and been largely ignored. His insights were subsequently seriously considered in Japan after the earthquake. He and his colleagues developed the principle of structural similitude that relates monotonic fracture displacement ductility to cyclic fracture displacement ductility for a particular assembly. This arose from their observation that running fractures developed from ductile crack formation at blunt notches in structures. The similitude principle has echoes of the Coffin-Manson approach to ductile crack initiated low cycle fracture. The principle of similitude has a log–log relationship as does the Manson-Coffin relationship. So where notch plasticity controls the initiation of fracture in a structural assembly it is conceptually reasonable to expect that the number of cycles to initiation of fracture from a notch will have a log–log relationship to the amplitude of the cyclic strain developed in the notch. Kuwamura found that steel assemblies with lower CVN energy had reduced cyclic fracture endurance than the same assemblies made with steel with higher CVN impact energy. However no method of predicting performance of any particular assembly could be developed from his observations. The benefit of his method primarily relates to the minimising of testing necessary to assess the fracture limited cyclic displacement ductility of a structural assembly. However it doesn’t provide a means for designing a structural assembly to achieve specific levels of ductile endurance other than clearly identifying the need to use steel with good CVN characteristics. The most significant development arising from this thesis is therefore the development of a design method to assess cyclic ductile endurance. The method utilises the specific work of fracture properties obtained from CTOD specimens of the steel in conjunction with a relatively simple fracture mechanics assessment and an elasto-plastic finite element analysis (FEA). The FEA model is used to determine the displacement ductility of the assembly at the calculated onset of pre-necking fracture. The elasto-plastic stress–strain properties of the steel in various pre-strain states required for the FEA may be derived from tensile testing. Kuwamura’s similitude principle is then used to predict cyclic plastic endurance at various constant displacement ductility amplitudes. The method is extended using Miner’s rule to allow for the effects of increasing variable amplitude cyclic plastic loading. In summary the thesis explains why pre-necking and running fractures occur in steel members subjected to cyclic plastic deformation during a severe earthquake. In addition a method for consistently assessing the ability of structural steel assemblies to achieve a specified level of ductile endurance during earthquakes is proposed. The method is verified against published results for a cyclic test of a simple steel member with a crack at mid-span. / Whole document restricted, but available by request, use the feedback form to request access.

This thesis provides a structural and materials engineering explanation for many of the running fractures that occurred in steel structures during the destructive Kobe and Northridge earthquakes in the mid 1990s. A method is developed that allows the ductile endurance of structural steel members subjected to cyclic plastic deformation during earthquakes to be assessed and for pre-necking running fractures to be avoided. The study commenced following the 2000 World Earthquake Conference in Auckland. The conference brought together the findings of the huge research effort, in America, Japan, Europe and New Zealand, that followed the Kobe and Northridge earthquakes. The running fractures that had occurred in steel structures represented an unpredicted failure mode that structural engineers have not known how to predict or suppress through the engineering design process. A clear fundamental understanding of the causes and how to prevent the fractures did not arise from the conference. In fact apparently conflicting results were reported. Full scale cyclic tests in New Zealand on structural assemblies had not resulted in running fractures, whereas tests in American and Japan had. Structural engineers designing earthquake resistant structures rely on constructional steel to be materially homogeneous and nominally tri-linear in behaviour. Steel is expected to behave elastically under regular in-service loading, have a reliable and flat yield stress-strain characteristic, and under overload then develop predictable levels of strain-hardening in conjunction with significant plastic elongation up to its ultimate tensile strength. Steel is expected to eventually fracture after further plastic elongation and necking. Ductile design strategies and methods utilise the plastic elongation characteristics of steel to protect structures in earthquake. Plastic deformation is considered to beneficially dissipate energy generated in the structure by a severe earthquake and also dampen the structure’s response. The occurrence of running fracture without significant cyclic plastic deformation and before section necking in steelwork, therefore undermines the basis of the ductile seismic design approach. The initial part of the thesis is devoted to bringing together the fundamental aspects of materials engineering related to fracture of constructional steel. This is intended to provide a bridge of knowledge for structural engineering practitioners and researchers not fully conversant with materials engineering aspects of fracture. Fracture behaviour in steel is a broad and complex topic that developed rapidly in the twentieth century driven by the demands of technological growth. The unexpected fracture of welded liberty ships at sea in World War 2; the need for reliable long term containment for the nuclear reactors in the 1950s and 1960s; and prevention of fatigue failures in aircraft frames since the 1950s all drove engineering research into steel fracture behaviour. There are many subtle variations in definitions in the published literature on fracture that can be confusing. Therefore an attempt has been made to clarify terminology. The term brittle fracture in particular is only used in this thesis as applying to running fracture when the general or far field tensile stresses are below the yield stress of the steel. The term pre-necking or running fracture is preferred to describe the condition more broadly which may occur prior to and also after general yielding, but before section necking. Running fracture is a manifestation of pre-necking fracture in which insufficient plastic flow is available in the assembly to absorb the energy released upon fracture. The experimental studies investigated the behaviour of constructional steel commonly used in New Zealand, at various levels of plastic strain. This started with Charpy V-Notch (CVN) testing which revealed that a significant transition temperature shift and curve shape change occurs with increasing plastic strain and the associated strain-hardening. This showed that the ability of steel to avoid pre-necking or running fracture reduces as the level of plastic strain-hardening increases. Temperature controlled Crack Tip Opening Displacement (CTOD) testing was then undertaken. The setting of testing temperatures for the CTOD tests were guided by review of the CVN test results, using published CVN to fracture toughness correlation methods. However running cleavage fractures developed in the CTOD specimens at higher than predicted temperatures of 10 oC and 20 oC. These are typical service temperatures for structures in New Zealand and so are very likely to occur at the time of an earthquake. The implication from this is that there are levels of strain-hardening and conditions of material notching constraint that can lead to pre-necking and running fracture in New Zealand fabricated steel structures, under severe earthquake loading. Care was taken in the CTOD testing to monitor and maximise the capture of data electronically using a specially developed Direct Current Potential Drop method. This allowed the test results to be analysed and considered in varying ways, leading to a consistent assessment of the CTOD, crack growth, and the specific work of fracture in each test piece. While CTOD test results have sometimes been published by structural and welding engineering researchers in the wake of Kobe and Northridge, the results were typically of little use for this study as the CTOD initiation point was generally not identified effectively. The effect of remote plastic flow in the specimens was also not adequately accounted for. The CTOD test results were often simply used to help correlate other factors observed by the researchers. Side-grooving of specimens was not reported as having been used in any of the published results reviewed. When conducting CTOD test with highly ductile constructional steels it is very difficult to get useful CTOD results if the specimens are not side-grooved, as significant necking and tunnelling will otherwise occur and limit the usefulness of the results. Work by Knott and also by McRobie and Smith was seminal in terms of identifying some critical aspects of plane strain development in CTOD tests, and the links to non-metallic particle density with respect to fracture toughness and CTOD at initiation. Some of their findings with regards to the effect of pre-strain on CTOD initiation were subsequently found to confirm the experimental findings in this study. No effective methodology for prediction of pre-necking or running fracture in a structural member or assembly when subjected to gross plastic cyclic deformation was found to exist in the literature. It was concluded however that the principles of specific work of fracture, and monotonic and cyclic fracture similitude were particularly relevant. These were therefore utilised in the development of the design method proposed in this thesis. The CTOD test results were reviewed, isolating the remote plastic flow component, to determine the critical specific work of fracture property Rc of the steels tested. A meeting with Professor Kuwamura at the University of Tokyo was providential, allowing discussion of his similitude principle, and observations in person of some of the fractured specimens developed during his full scale test series’. Running fractures with cleavage were evident in the specimens, with their tell-tale chevron markings. He had predicted running fracture problems in structures in Japan ahead of the Kobe earthquake and been largely ignored. His insights were subsequently seriously considered in Japan after the earthquake. He and his colleagues developed the principle of structural similitude that relates monotonic fracture displacement ductility to cyclic fracture displacement ductility for a particular assembly. This arose from their observation that running fractures developed from ductile crack formation at blunt notches in structures. The similitude principle has echoes of the Coffin-Manson approach to ductile crack initiated low cycle fracture. The principle of similitude has a log–log relationship as does the Manson-Coffin relationship. So where notch plasticity controls the initiation of fracture in a structural assembly it is conceptually reasonable to expect that the number of cycles to initiation of fracture from a notch will have a log–log relationship to the amplitude of the cyclic strain developed in the notch. Kuwamura found that steel assemblies with lower CVN energy had reduced cyclic fracture endurance than the same assemblies made with steel with higher CVN impact energy. However no method of predicting performance of any particular assembly could be developed from his observations. The benefit of his method primarily relates to the minimising of testing necessary to assess the fracture limited cyclic displacement ductility of a structural assembly. However it doesn’t provide a means for designing a structural assembly to achieve specific levels of ductile endurance other than clearly identifying the need to use steel with good CVN characteristics. The most significant development arising from this thesis is therefore the development of a design method to assess cyclic ductile endurance. The method utilises the specific work of fracture properties obtained from CTOD specimens of the steel in conjunction with a relatively simple fracture mechanics assessment and an elasto-plastic finite element analysis (FEA). The FEA model is used to determine the displacement ductility of the assembly at the calculated onset of pre-necking fracture. The elasto-plastic stress–strain properties of the steel in various pre-strain states required for the FEA may be derived from tensile testing. Kuwamura’s similitude principle is then used to predict cyclic plastic endurance at various constant displacement ductility amplitudes. The method is extended using Miner’s rule to allow for the effects of increasing variable amplitude cyclic plastic loading. In summary the thesis explains why pre-necking and running fractures occur in steel members subjected to cyclic plastic deformation during a severe earthquake. In addition a method for consistently assessing the ability of structural steel assemblies to achieve a specified level of ductile endurance during earthquakes is proposed. The method is verified against published results for a cyclic test of a simple steel member with a crack at mid-span. / Whole document restricted, but available by request, use the feedback form to request access.

Sélectionner des traitements de surface pour l’industrie nécessite de prendre en compte : les propriétés à conférer au substrat, la nature et la géométrie de celui-ci et les caractéristiques du milieu extérieur. Certaines combinaisons de ces paramètres rendent difficile la sélection d’un traitement unique, d’où le recours à des multitraitements de surface. Dès lors, se posent les questions suivantes : - Utiliser des multitraitements de surface peut se faire en scindant les différentes requêtes en sous-ensembles, de manière à ce que chaque traitement réponde à l’un d’eux. Dans quel ordre ces requêtes doivent-elles être introduites par rapport au substrat ? - Comment sélectionner les traitements de surface répondant à chaque requête individuelle ? - Comment classer des multitraitements en termes d’adéquation au problème posé ? Dans ce travail, les première et troisième questions sont abordées, en explorant les requêtes concernant habituellement les dispositifs de moulage de l’aluminium : - Résistance aux contraintes d’origine thermique. - Résistance à la corrosion par les métaux fondus. - Résistance au frottement. L’analyse de la bibliographie relative aux traitements de surface utilisés dans ces systèmes a été analysée et des « architectures »-types ont été identifiées (chapitre 3). On prévoit, par exemple, un traitement conférant la résistance à la fatigue superficielle, ainsi qu’un revêtement étanche et résistant à l’aluminium fondu. Une barrière thermique est parfois préconisée. Pour chacune des architectures, des traitements de surface individuels peuvent être sélectionnés. Un « facteur de performance » permettant de classer les solutions par rapport au problème de la fatigue thermique a été construit (chapitre 4) et discuté dans deux situations : - Lorsqu’un revêtement est présent, et que les contraintes d’origine thermique (différence de dilatation thermique couche-substrat) menacent de le rompre lors de l’immersion dans un milieu corrosif à haute température. Des essais de corrosion dans de l’aluminium fondu ont été réalisés sur un acier revêtu par du nitrure de chrome dopé à l’aluminium, synthétisé par déposition physique en phase vapeur (chapitre 5 – collaboration : Inasmet). - Lorsque des variations thermiques rapides menacent de rompre le substrat et la (les) couches. Des essais de fatigue thermique ont été réalisés sur de l’acier à outils pour travail à chaud non traité, boruré ou recouvert d’un multitraitements (zircone yttriée / NiCrAlY / boruration / acier). Le revêtement en zircone yttriée a été obtenu par projection par plasma. L’essai de fatigue thermique a été modélisé et le facteur de performance, discuté (chapitre 6). Au chapitre 7, les architectures-types ont été introduites dans une méthodologie de sélection des multi-traitements de surface, qui a été appliquée dans deux cas : - Celui des moules de fonderie, devant résister à la fatigue thermique et à la corrosion par l’aluminium fondu. Le facteur de performance a été extrapolé à d’autres situations qu’aux chapitres 5 et 6. Les solutions habituellement proposées pour résoudre ce problème sont retrouvées. - Celui de deux pièces en acier frottant l’une contre l’autre en présence d’aluminium fondu. To select surface treatments, one must account for the required functional properties, the substrate features and the solicitations the substrate must endure. Certain combinations of these parameters make it difficult to select a single surface treatment, a reason why several successive treatments are preferred. To select them, one needs to determine: - How to divide the several requests into groups and how to stack up these groups from the substrate to the outer surface, so that each treatment deals with one specific group of requests/properties. - How to select individual layers for each group of properties. - How to rank the multi-treatments in terms of relevance for a given application. In this work, one tries to answer the first and the third questions, by studying the case of aluminium foundry, in which the industrial devices frequently face the following solicitations: - Thermal stress (thermal fatigue, thermal expansion mismatch). - Presence of corrosive molten metal. - Sliding wear. In the literature, several “standard” architectures are proposed (chapter 3), like a diffusion layer reducing superficial fatigue plus a corrosion barrier layer. A thermal barrier coating is also sometimes proposed. For each of these architectures, one can select individual treatments. To rank them, one devised a “performance index” for thermal stress (chap.4), which is discussed for two cases: - For large differences between layer and substrate thermal expansion coefficients, when both are put into contact with a high temperature corrosive medium, the layer may be damaged. One discusses this case by examining the corrosion caused by molten aluminium for a steel substrate coated by anticorrosive chromium nitride doped with aluminium. The layer is produced by physical vapour deposition (chap. 5 – cooperation: Inasmet). - Repeated fast surface temperature transients can also damage the substrate and/or the layer by thermal fatigue. One conducted thermal fatigue tests with samples of hot work tool steel, respectively untreated, simply borided and protected by a multilayer. In the last case, top coat is yttria stabilised zirconia, followed by a nickel superalloy and then a borided layer (undercoat). One synthesized the zirconia coating by plasma spray and one modelled the thermal fatigue (chap. 6). In chap. 7, architectures from chap. 2 are introduced in a multi-treatment selection routine, which is applied in two cases: - Foundry moulds for molten aluminium, withstanding both thermal fatigue and corrosion. The devised performance index is extrapolated beyond the tests of chap. 5 and 6 to treatments for this industrial application, thereby quantifying their respective merits. - A foundry device exposed to molten metal and sliding wear.

Sélectionner des traitements de surface pour l’industrie nécessite de prendre en compte :les propriétés à conférer au substrat, la nature et la géométrie de celui-ci et les caractéristiques du milieu extérieur. Certaines combinaisons de ces paramètres rendent difficile la sélection d’un traitement unique, d’où le recours à des multitraitements de surface. Dès lors, se posent les questions suivantes :<p>- Utiliser des multitraitements de surface peut se faire en scindant les différentes requêtes en sous-ensembles, de manière à ce que chaque traitement réponde à l’un d’eux. Dans quel ordre ces requêtes doivent-elles être introduites par rapport au substrat ?<p>- Comment sélectionner les traitements de surface répondant à chaque requête individuelle ?<p>- Comment classer des multitraitements en termes d’adéquation au problème posé ?<p>Dans ce travail, les première et troisième questions sont abordées, en explorant les requêtes concernant habituellement les dispositifs de moulage de l’aluminium :<p>- Résistance aux contraintes d’origine thermique.<p>- Résistance à la corrosion par les métaux fondus.<p>- Résistance au frottement.<p>L’analyse de la bibliographie relative aux traitements de surface utilisés dans ces systèmes a été analysée et des « architectures »-types ont été identifiées (chapitre 3). On prévoit, par exemple, un traitement conférant la résistance à la fatigue superficielle, ainsi qu’un revêtement étanche et résistant à l’aluminium fondu. Une barrière thermique est parfois préconisée.<p>Pour chacune des architectures, des traitements de surface individuels peuvent être sélectionnés. Un « facteur de performance » permettant de classer les solutions par rapport au problème de la fatigue thermique a été construit (chapitre 4) et discuté dans deux situations :<p>- Lorsqu’un revêtement est présent, et que les contraintes d’origine thermique (différence de dilatation thermique couche-substrat) menacent de le rompre lors de l’immersion dans un milieu corrosif à haute température. Des essais de corrosion dans de l’aluminium fondu ont été réalisés sur un acier revêtu par du nitrure de chrome dopé à l’aluminium, synthétisé par déposition physique en phase vapeur (chapitre 5 – collaboration :Inasmet).<p>- Lorsque des variations thermiques rapides menacent de rompre le substrat et la (les) couches. Des essais de fatigue thermique ont été réalisés sur de l’acier à outils pour travail à chaud non traité, boruré ou recouvert d’un multitraitements (zircone yttriée / NiCrAlY / boruration / acier). Le revêtement en zircone yttriée a été obtenu par projection par plasma. L’essai de fatigue thermique a été modélisé et le facteur de performance, discuté (chapitre 6).<p>Au chapitre 7, les architectures-types ont été introduites dans une méthodologie de sélection des multi-traitements de surface, qui a été appliquée dans deux cas :<p>- Celui des moules de fonderie, devant résister à la fatigue thermique et à la corrosion par l’aluminium fondu. Le facteur de performance a été extrapolé à d’autres situations qu’aux chapitres 5 et 6. Les solutions habituellement proposées pour résoudre ce problème sont retrouvées.<p>- Celui de deux pièces en acier frottant l’une contre l’autre en présence d’aluminium fondu.<p><p>To select surface treatments, one must account for the required functional properties, the substrate features and the solicitations the substrate must endure. Certain combinations of these parameters make it difficult to select a single surface treatment, a reason why several successive treatments are preferred. To select them, one needs to determine:<p>- How to divide the several requests into groups and how to stack up these groups from the substrate to the outer surface, so that each treatment deals with one specific group of requests/properties.<p>- How to select individual layers for each group of properties.<p>- How to rank the multi-treatments in terms of relevance for a given application.<p>In this work, one tries to answer the first and the third questions, by studying the case of aluminium foundry, in which the industrial devices frequently face the following solicitations:<p>- Thermal stress (thermal fatigue, thermal expansion mismatch).<p>- Presence of corrosive molten metal.<p>- Sliding wear.<p>In the literature, several “standard” architectures are proposed (chapter 3), like a diffusion layer reducing superficial fatigue plus a corrosion barrier layer. A thermal barrier coating is also sometimes proposed.<p>For each of these architectures, one can select individual treatments. To rank them, one devised a “performance index” for thermal stress (chap.4), which is discussed for two cases:<p>- For large differences between layer and substrate thermal expansion coefficients, when both are put into contact with a high temperature corrosive medium, the layer may be damaged. One discusses this case by examining the corrosion caused by molten aluminium for a steel substrate coated by anticorrosive chromium nitride doped with aluminium. The layer is produced by physical vapour deposition (chap. 5 – cooperation: Inasmet).<p>- Repeated fast surface temperature transients can also damage the substrate and/or the layer by thermal fatigue. One conducted thermal fatigue tests with samples of hot work tool steel, respectively untreated, simply borided and protected by a multilayer. In the last case, top coat is yttria stabilised zirconia, followed by a nickel superalloy and then a borided layer (undercoat). One synthesized the zirconia coating by plasma spray and one modelled the thermal fatigue (chap. 6).<p>In chap. 7, architectures from chap. 2 are introduced in a multi-treatment selection routine, which is applied in two cases:<p>- Foundry moulds for molten aluminium, withstanding both thermal fatigue and corrosion. The devised performance index is extrapolated beyond the tests of chap. 5 and 6 to treatments for this industrial application, thereby quantifying their respective merits.<p>- A foundry device exposed to molten metal and sliding wear.<p><p> / Doctorat en Sciences de l'ingénieur / info:eu-repo/semantics/nonPublished