The aim of this study was to verify the behavior of five brands of NiCr alloys, indicated to porcelain fused to metal restorations, comparing the castability with the ability of reproducing the thin edges of restoration margins. The samples were divided in five groups, each one for one brand, with ten repetitions for castability test and ten for edge reproduction, in a total of 100 specimens. A carbon free phosphate bonded investment was used for all casting procedures. Optical microscopy was used to investigate the microstructure of the specimens obtained with two of the alloys, those which have shown better results. Statistical analysis stated that the commercial brand Tilite showed both better castability and edge reproduction. / O objetivo desta pesquisa foi verificar o desempenho de cinco ligas de níquel-cromo para restaurações de metalocerâmicas, comparando a fluidez com a capacidade de cópia da borda fina das restaurações. Os corpos-de-prova foram divididos em 5 grupos um para cada liga, sendo realizado dez corpos-de-prova para o teste de fluidez e dez corpos-de-prova para o teste da cópia da borda, totalizando 100 corpos-de-prova. Um revestimento de fosfato sem carbono foi usado para todas as inclusões e fundições. Em seguida foram submetidos a microscopia óptica, para se observar a microestrutura das duas ligas que obtiveram os melhores desempenhos. Os resultados, após análise estatística, demonstraram que a liga Tilite apresentou a melhor fluidez e melhor cópia da borda.

O estudo comparativo da distribuição de tensões de von Mises em dente endodonticamente tratado, com dois formatos de retentores intra-radiculares, pré-fabricado cilíndrico/escalonado e fundido cônico, foi realizado pelo método dos elementos finitos em modelos tridimensionais de caninos superiores com geometria axi-simétrica e restaurados com coroas metalocerâmicas, aplicando-se uma carga oblíqua de 100N com 45 º de inclinação em relação ao seu longo eixo. Os resultados indicaram uma discreta diferença nos dois modelos (formatos) de retentores. O pino escalonado neutralizou mais as cargas no sentido corono-apical e no pino cônico ficou evidenciado o efeito de cunha. / The aim of this study was to compare the von Mises stress distribution on a human canine teeth endodontically treated and restored with two types of post and core. The analysis was made using the three dimensional Finite Element Analysis method. For the analysis was created and axy-simetric structure of the teeth, including a porcelain fused to metal crown, a cement layer, and the periodontal structures. The model was analyzed when a 100N load was applied on the surface of the crown with 45º angulation with the long axis of the teeth. The results showed that both models exhibit little difference, the “stair shape" post system neutralized the axial loads, and the conical shape post showed a wedge effect on the apical third of the root.

O objetivo deste trabalho foi avaliar a influência de dois diferentes ambientes de sinterização (vácuo e argônio) sobre a resistência da união metaloceramica (RUMC) envolvendo diferentes ligas de metais básicos (Co-Cr e Ni-Cr) e uma porcelana odontológica, através do teste de flexão de três pontos, conforme preconizado pela ISO 9693:2012. As ligas estudadas foram Co-Cr: Remanium e Keragen e Ni-Cr: Verabond II e uma liga experimental “SR” . Foram obtidos 80 corpos de prova em forma tiras metálicas medindo 25 X 0,5 X 5 mm. Para esse ensaio, portanto, o número de corpos de prova foi o produto de 4 ligas x 2 condições de atmosfera de sinterização x 10 repetições. A parte metálica de todos os corpos de prova após a fundição foram usinados e jateados com óxido de alumínio (150μm) e a seguir tratados como preconizado pelo fabricante. O corpo cerâmico, com o auxílio de uma matriz, foi confeccionado na área central da tira, 8,0 X 3,0mm, apresentando 1,1mm de espessura, sendo 10 corpos de prova em cada ambiente de sinterização para cada tipo de liga. Os corpos de prova obtidos foram submetidos aos testes de flexão de três pontos na Máquina de Ensaios Mecânicos (EMIC) com velocidade de 1.0mm/min. para determinação da RUMC. Os valores da carga de ruptura obtidos em quilograma-força (Kgf) foram convertidos para Newton (N) e a partir disso foi calculado o valor da RUMC para cada corpo de prova, considerando o coeficiente de elasticidade de cada liga e a espessura exata de cada corpo de prova. Os dados obtidos (MPa) foram submetidos à análise estatística (ANOVA) e Bonferroni. A Análise de Variância indicou diferença estatisticamente significante para os fatores de variação ambiente (P=0,00), liga (P=0,009) e entre as interações ambiente de sinterização e liga (P=0,000). Na sinterização a vácuo as ligas Keragen, SR e Verabond II apresentaram maiores valores de RUMC do que o argônio. Para a liga Remanium, não houve diferença entre a sinterização em argônio e a sinterização a vácuo. Dentre os grupos sinterizados no argônio não houve diferença estatisticamente significante entre as ligas. Entretanto, no vácuo a liga Remanium apresentou menor valor de RUMC do que as demais ligas, que não apresentaram diferença entre si. Os corpos de prova, após os ensaios de flexão, foram submetidos a análise em microscopia optica, MEV e EDS para avaliar e registrar tipo de falha que sofreram. De acordo com a MO, houve predomínio de fraturas mistas. Os corpos de prova de Co-Cr (Remanium e Keragen), independende do ambiente de sinterização, apresentaram uma fina camada de óxido no corpo cerâmico, o que foi comprovado pelo EDS, com maior presença de íons Cr nessas regiões, já os grupos SR e Verabond II, apresentaram maior quantidade de opaco aderido em suas tiras metálicas. A MEV comprovou os achados da MO, onde foi possível encontrar grandes ilhas de material cerâmico nas ligas de Ni-Cr. A sinterização em argônio influenciou negativamente a RUMC dos pares metalocerâmicos confeccionados em Ni-Cr e na liga Keragem / The aim of this study was to evaluate the influence of two different firing atmosphere (vacuum and argon) on the metalceramic bond strength (MCBS) involving different base metal alloys (Co-Cr and Ni-Cr) and a dental porcelain through three-point bending test, as recommended by ISO 9693: 2012. Co-Cr alloys studied were: Remanium and Keragen and Ni-Cr: Verabond II and an experimental alloy \"SR\". 80 specimens were obtained in metallic form strips measuring 25X0.5 X 5.0 mm. For this test, therefore, the number of specimens was the product of 4 x 2 alloy sintering atmosphere conditions x 10 replicates. The metal portion of all specimens were machined after casting and sandblasted with aluminum oxide (100μm) and then treated as recommended by the manufacturer. By using a matrix, the ceramic body was made in the central area of the strip, 8.0 x 3.0 mm, it was made 1.1 mm thickness, 10 specimens in each sintering environment for each type of alloy. The specimens obtained were tested for three-point bending in a universal testing machine with a speed of 1.0mm / min. to determine MCBS. The values of the tensile strength obtained in kilogramforce (kgf) were converted into Newton (N) and from this the value of MCBS for each specimen was calculated, considering the coefficient of elasticity of each league and the exact thickness of each specimen. The data (MPa) were subjected to statistical analysis (ANOVA) and Bonferroni. The analysis of variance indicated statistically significant difference for the environment factors of firing atmosphere (P = 0.00) and alloy (P = 0.009). There was a statistically significant difference in the interaction factors for firing atmosphere x alloy (P = 0.000). In the vacuum Keragen, SR and Verabond II alloys showed higher MCBS than argon. To Remanium, there was no difference between the sintering in argon and vacuum. Among the groups sintered in argon there was no statistically significant difference between the alloys. However, the vacuum Remanium showed the lowest RUMC than other alloys, which showed no difference between them. The specimens after the bending tests, were subjected to analysis in optical microscopy, SEM and EDS to assess and record type of failure they suffered. According to the MO was predominantly mixed fractures. Specimens of Co-Cr (Remanium and Keragen) independende the atmosphere firing, showed a thin oxide layer on the ceramic body, which was confirmed by EDS, with greater presence of Cr in these regions, since the SR groups and Verabond II, presented more opaque stuck in their metal strips. SEM confirmed the findings of MO, where it was possible to find large islands of ceramic material in Ni-Cr alloys. The sintering in argon negatively influenced MCBS metalceramic of pairs made of Ni-Cr alloy and Keragem

O objetivo deste trabalho foi avaliar o efeito do ambiente de sinterização vácuo e argônio na resistência de união (RUMC) de cerâmicas às ligas de Ni-Cr (Fit Cast SB), Co-Cr (Star Loy C) e titânio comercialmente puro (Tritan). A partir de uma matriz de teflon, foram obtidos 60 padrões de resina/cera em forma de cilindro, com 8 mm de comprimento e 5 mm de diâmetro. Os padrões foram incluídos e os anéis foram levados ao forno e submetidos a ciclos térmicos para a expansão do revestimento. Em seguida, os anéis para fundição em Ni-Cr e Co-Cr foram levados à máquina de fundição por indução eletrônica. Os anéis referentes ao titânio foram levados à máquina de fundição por arco voltaico. Após resfriamento dos anéis, as fundições foram desincluídas e jateadas com óxido de alumínio (100 μm). Depois de recortados dos canais de alimentação, os cilindros metálicos foram preparados para aplicação da cerâmica. Em seguida, foi realizada a aplicação e sinterização da cerâmica à vácuo ou em argônio. Para as ligas alternativas, foi utilizada a cerâmica IPS Classic V e para o titânio, a Triceram. Na sequência, os cilindros compostos pelo metal e disco cerâmico (5 mm de diâmetro e 2 mm de espessura) (n=10) foram submetidos aos ensaios de RUMC por cisalhamento na máquina de ensaios universais com célula de carga de 500 Kg e velocidade do travessão móvel de 0,5 mm/min. Após os ensaios, foram realizadas análises das fraturas por meio de microscopia óptica (MO) (15X) e microscopia eletrônica de varredura (MEV). Os dados de RUMC (MPa) obtidos foram analisados estatisticamente pelos testes ANOVA e Tukey (α=0,05). Os resultados demonstraram que a sinterização à vácuo propiciou obtenção de maiores valores (MPa) de RUMC (76,58) que a sinterização em argônio (51,31). Quanto às ligas avaliadas, as de Ni-Cr e Co-Cr apresentaram maiores valores de RUMC (71,32 e 71,28, respectivamente) que o titânio cp (49,23); sendo que entre elas não houve diferença estatística. Não houve interação entre os fatores avaliados. De acordo com a MO, houve predomínio de fraturas mistas. Segundo a MEV, os espécimes de Ni-Cr e titânio sinterizados a vácuo apresentaram maior rugosidade de superfície do que os sinterizados em argônio. Para a liga de Co-Cr não houve diferença na topografia de superfície. A sinterização em argônio influenciou negativamente a RUMC dos pares metalocerâmicos analisados. / The aim of this study was to evaluate the effect of firing atmospheres: vacuum and argon on the bond strength of ceramic to Ni-Cr (Fit Cast SB), Co-Cr (Star Loy C) and commercially pure titanium (Tritan) alloys. 60 wax/acrylic resin cylinder patterns (8 mm high and 5 mm in diameter) were prepared on a plastic custom mold for metalceramic bond strength (MCBS) test. The patterns were invested in phosphated investment and manipulated on vacuum. The rings were placed in a furnace to burn out patterns and thermally expand the molds. Then, the rings of Ni-Cr and Co-Cr were placed in an electronic machine to cast. The rings related to titanium were positioned in the casting machine with a voltaic arc. After the rings have cooled, the castings were divested manually and abraded with aluminum oxide particles (100 μm). Then, the cylinders were prepared for applying of the ceramic veneering disks. The ceramic was applied and fired in vacuum and argon atmospheres. IPS-Classic ceramic was used for alternative alloys and for titanium, Triceram ceramic. Then, the cylinders composed of metal and ceramic disk (5 mm diameter and 2 mm height) (n=10) were submitted to metal-ceramic bond strength (MCBS) shear tests on an universal testing machine with load cell of 500 Kg at a crosshead speed of 0.5 mm/min. After the tests, there were made fracture analysis by optic microscopy (OM) and scanning electron microscopy (SEM). The MCBS data (MPa) were statistically analyzed by the ANOVA and Tukey test (α=0.05). The results indicated that the vacuum firing (76.58) promoted higher MCBS values than argon firing (51.31). Among the metals, Ni-Cr and Co-Cr alloys presented higher MCBS (71.32 e 71.28, respectively) than titanium (49.23); between two base alloys there was no statistical difference. There was no interaction between the evaluated factors. According to MO analysis, there was predominance of mixed fractures. According SEM, the Ni-Cr and titanium specimens submitted to vacuum presented higher surface roughness than the specimens submitted to argon. For Co-Cr, there was no difference of surface topography. The argon firing influenced negatively the MCBS of metal-ceramic evaluated pairs.

O objetivo deste trabalho foi avaliar a influência de dois diferentes ambientes de sinterização (vácuo e argônio) sobre a resistência da união metaloceramica (RUMC) envolvendo diferentes ligas de metais básicos (Co-Cr e Ni-Cr) e uma porcelana odontológica, através do teste de flexão de três pontos, conforme preconizado pela ISO 9693:2012. As ligas estudadas foram Co-Cr: Remanium e Keragen e Ni-Cr: Verabond II e uma liga experimental “SR” . Foram obtidos 80 corpos de prova em forma tiras metálicas medindo 25 X 0,5 X 5 mm. Para esse ensaio, portanto, o número de corpos de prova foi o produto de 4 ligas x 2 condições de atmosfera de sinterização x 10 repetições. A parte metálica de todos os corpos de prova após a fundição foram usinados e jateados com óxido de alumínio (150μm) e a seguir tratados como preconizado pelo fabricante. O corpo cerâmico, com o auxílio de uma matriz, foi confeccionado na área central da tira, 8,0 X 3,0mm, apresentando 1,1mm de espessura, sendo 10 corpos de prova em cada ambiente de sinterização para cada tipo de liga. Os corpos de prova obtidos foram submetidos aos testes de flexão de três pontos na Máquina de Ensaios Mecânicos (EMIC) com velocidade de 1.0mm/min. para determinação da RUMC. Os valores da carga de ruptura obtidos em quilograma-força (Kgf) foram convertidos para Newton (N) e a partir disso foi calculado o valor da RUMC para cada corpo de prova, considerando o coeficiente de elasticidade de cada liga e a espessura exata de cada corpo de prova. Os dados obtidos (MPa) foram submetidos à análise estatística (ANOVA) e Bonferroni. A Análise de Variância indicou diferença estatisticamente significante para os fatores de variação ambiente (P=0,00), liga (P=0,009) e entre as interações ambiente de sinterização e liga (P=0,000). Na sinterização a vácuo as ligas Keragen, SR e Verabond II apresentaram maiores valores de RUMC do que o argônio. Para a liga Remanium, não houve diferença entre a sinterização em argônio e a sinterização a vácuo. Dentre os grupos sinterizados no argônio não houve diferença estatisticamente significante entre as ligas. Entretanto, no vácuo a liga Remanium apresentou menor valor de RUMC do que as demais ligas, que não apresentaram diferença entre si. Os corpos de prova, após os ensaios de flexão, foram submetidos a análise em microscopia optica, MEV e EDS para avaliar e registrar tipo de falha que sofreram. De acordo com a MO, houve predomínio de fraturas mistas. Os corpos de prova de Co-Cr (Remanium e Keragen), independende do ambiente de sinterização, apresentaram uma fina camada de óxido no corpo cerâmico, o que foi comprovado pelo EDS, com maior presença de íons Cr nessas regiões, já os grupos SR e Verabond II, apresentaram maior quantidade de opaco aderido em suas tiras metálicas. A MEV comprovou os achados da MO, onde foi possível encontrar grandes ilhas de material cerâmico nas ligas de Ni-Cr. A sinterização em argônio influenciou negativamente a RUMC dos pares metalocerâmicos confeccionados em Ni-Cr e na liga Keragem / The aim of this study was to evaluate the influence of two different firing atmosphere (vacuum and argon) on the metalceramic bond strength (MCBS) involving different base metal alloys (Co-Cr and Ni-Cr) and a dental porcelain through three-point bending test, as recommended by ISO 9693: 2012. Co-Cr alloys studied were: Remanium and Keragen and Ni-Cr: Verabond II and an experimental alloy \"SR\". 80 specimens were obtained in metallic form strips measuring 25X0.5 X 5.0 mm. For this test, therefore, the number of specimens was the product of 4 x 2 alloy sintering atmosphere conditions x 10 replicates. The metal portion of all specimens were machined after casting and sandblasted with aluminum oxide (100μm) and then treated as recommended by the manufacturer. By using a matrix, the ceramic body was made in the central area of the strip, 8.0 x 3.0 mm, it was made 1.1 mm thickness, 10 specimens in each sintering environment for each type of alloy. The specimens obtained were tested for three-point bending in a universal testing machine with a speed of 1.0mm / min. to determine MCBS. The values of the tensile strength obtained in kilogramforce (kgf) were converted into Newton (N) and from this the value of MCBS for each specimen was calculated, considering the coefficient of elasticity of each league and the exact thickness of each specimen. The data (MPa) were subjected to statistical analysis (ANOVA) and Bonferroni. The analysis of variance indicated statistically significant difference for the environment factors of firing atmosphere (P = 0.00) and alloy (P = 0.009). There was a statistically significant difference in the interaction factors for firing atmosphere x alloy (P = 0.000). In the vacuum Keragen, SR and Verabond II alloys showed higher MCBS than argon. To Remanium, there was no difference between the sintering in argon and vacuum. Among the groups sintered in argon there was no statistically significant difference between the alloys. However, the vacuum Remanium showed the lowest RUMC than other alloys, which showed no difference between them. The specimens after the bending tests, were subjected to analysis in optical microscopy, SEM and EDS to assess and record type of failure they suffered. According to the MO was predominantly mixed fractures. Specimens of Co-Cr (Remanium and Keragen) independende the atmosphere firing, showed a thin oxide layer on the ceramic body, which was confirmed by EDS, with greater presence of Cr in these regions, since the SR groups and Verabond II, presented more opaque stuck in their metal strips. SEM confirmed the findings of MO, where it was possible to find large islands of ceramic material in Ni-Cr alloys. The sintering in argon negatively influenced MCBS metalceramic of pairs made of Ni-Cr alloy and Keragem

O objetivo deste trabalho foi avaliar o efeito do ambiente de sinterização vácuo e argônio na resistência de união (RUMC) de cerâmicas às ligas de Ni-Cr (Fit Cast SB), Co-Cr (Star Loy C) e titânio comercialmente puro (Tritan). A partir de uma matriz de teflon, foram obtidos 60 padrões de resina/cera em forma de cilindro, com 8 mm de comprimento e 5 mm de diâmetro. Os padrões foram incluídos e os anéis foram levados ao forno e submetidos a ciclos térmicos para a expansão do revestimento. Em seguida, os anéis para fundição em Ni-Cr e Co-Cr foram levados à máquina de fundição por indução eletrônica. Os anéis referentes ao titânio foram levados à máquina de fundição por arco voltaico. Após resfriamento dos anéis, as fundições foram desincluídas e jateadas com óxido de alumínio (100 μm). Depois de recortados dos canais de alimentação, os cilindros metálicos foram preparados para aplicação da cerâmica. Em seguida, foi realizada a aplicação e sinterização da cerâmica à vácuo ou em argônio. Para as ligas alternativas, foi utilizada a cerâmica IPS Classic V e para o titânio, a Triceram. Na sequência, os cilindros compostos pelo metal e disco cerâmico (5 mm de diâmetro e 2 mm de espessura) (n=10) foram submetidos aos ensaios de RUMC por cisalhamento na máquina de ensaios universais com célula de carga de 500 Kg e velocidade do travessão móvel de 0,5 mm/min. Após os ensaios, foram realizadas análises das fraturas por meio de microscopia óptica (MO) (15X) e microscopia eletrônica de varredura (MEV). Os dados de RUMC (MPa) obtidos foram analisados estatisticamente pelos testes ANOVA e Tukey (α=0,05). Os resultados demonstraram que a sinterização à vácuo propiciou obtenção de maiores valores (MPa) de RUMC (76,58) que a sinterização em argônio (51,31). Quanto às ligas avaliadas, as de Ni-Cr e Co-Cr apresentaram maiores valores de RUMC (71,32 e 71,28, respectivamente) que o titânio cp (49,23); sendo que entre elas não houve diferença estatística. Não houve interação entre os fatores avaliados. De acordo com a MO, houve predomínio de fraturas mistas. Segundo a MEV, os espécimes de Ni-Cr e titânio sinterizados a vácuo apresentaram maior rugosidade de superfície do que os sinterizados em argônio. Para a liga de Co-Cr não houve diferença na topografia de superfície. A sinterização em argônio influenciou negativamente a RUMC dos pares metalocerâmicos analisados. / The aim of this study was to evaluate the effect of firing atmospheres: vacuum and argon on the bond strength of ceramic to Ni-Cr (Fit Cast SB), Co-Cr (Star Loy C) and commercially pure titanium (Tritan) alloys. 60 wax/acrylic resin cylinder patterns (8 mm high and 5 mm in diameter) were prepared on a plastic custom mold for metalceramic bond strength (MCBS) test. The patterns were invested in phosphated investment and manipulated on vacuum. The rings were placed in a furnace to burn out patterns and thermally expand the molds. Then, the rings of Ni-Cr and Co-Cr were placed in an electronic machine to cast. The rings related to titanium were positioned in the casting machine with a voltaic arc. After the rings have cooled, the castings were divested manually and abraded with aluminum oxide particles (100 μm). Then, the cylinders were prepared for applying of the ceramic veneering disks. The ceramic was applied and fired in vacuum and argon atmospheres. IPS-Classic ceramic was used for alternative alloys and for titanium, Triceram ceramic. Then, the cylinders composed of metal and ceramic disk (5 mm diameter and 2 mm height) (n=10) were submitted to metal-ceramic bond strength (MCBS) shear tests on an universal testing machine with load cell of 500 Kg at a crosshead speed of 0.5 mm/min. After the tests, there were made fracture analysis by optic microscopy (OM) and scanning electron microscopy (SEM). The MCBS data (MPa) were statistically analyzed by the ANOVA and Tukey test (α=0.05). The results indicated that the vacuum firing (76.58) promoted higher MCBS values than argon firing (51.31). Among the metals, Ni-Cr and Co-Cr alloys presented higher MCBS (71.32 e 71.28, respectively) than titanium (49.23); between two base alloys there was no statistical difference. There was no interaction between the evaluated factors. According to MO analysis, there was predominance of mixed fractures. According SEM, the Ni-Cr and titanium specimens submitted to vacuum presented higher surface roughness than the specimens submitted to argon. For Co-Cr, there was no difference of surface topography. The argon firing influenced negatively the MCBS of metal-ceramic evaluated pairs.

Objetivo: comparar a qualidade do ajuste interno de três tipos de infra-estruturas cerâmicas e um tipo de infra-estrutura metálica, sistemas universalmente usados na confecção de coroas totais. Métodos: A partir de um preparo mestre de coroa total, 40 troquéis de gesso tipo IV foram obtidos e distribuídos randomicamente em quatro grupos (n = 10) a saber: Grupo In-Ceram, Grupo Procera, Grupo Empress 2 e Grupo Metal.. Após sua confecção, cada infra-estrutura foi cimentada individualmente sobre o troquél mestre, usando silicone de adição de ultra-baixa viscosidade para preencher o espaço entre a infra-estrutura e o preparo. Após a remoção das coroas, cada réplica foi pesada em balança de precisão e logo separadas nas porções correspondentes à interface parede cervical e interface parede ocluso-axial, sendo então pesadas separadamente, para posterior obtenção de seu volume. Resultados: Interface paredes do preparo/paredes da infra-estrutura: Neste computo geral, houve diferença estatística significativa (P < 0,0001) entre os grupos estudados. As principais diferenças quantitativas no volume da interface ocorreram entre o Grupo In-Ceram e os demais grupos. Interface paredes ocluso-axial do preparo/paredes ocluso-axial da infra-estrutura: Repete-se aqui, diferença estatística significativa entre os grupos estudados (P < 0,0001). Mantêm-se as principais diferenças quantitativas no volume da interface em relação ao Grupo In-Ceram. Interface parede cervical do preparo/parede cervical da infra-estrutura: Não houve diferença estatística significativa (P > 0,5) no volume da interface cervical entre os Grupos Metal (menor média) e In-Ceram, com este apresentando pequeno aumento no volume desta interface, comparado ao primeiro. Em relação ao Grupo Metal, o volume da interface cervical foi maior no Grupo Empress 2, seguido do Grupo Procera, ambos mostrando diferença estatística significativa no confronto com o Grupo Metal (P < 0,001 e P < 0,01 respectivamente). Não houve diferença estatística significativa (P > 0,05) entre os Grupos Procera e Empress 2. Conclusões: Exceto em relação à interface cervical, o Grupo In-Ceram mostou os melhores resultados, seguido do Grupo Metal, para o ajuste interno. Os Grupos Metal e In-Ceram apresentaram os melhores desempenhos no ajuste interno, para a interface cervical. Os resultados sugerem estas infra-estruturas como as mais confiáveis quanto ao ajuste interno dentre as testadas neste trabalho. / Objective: Compare the quality of the internal fit of three kinds of ceramic infrastructures and one kind of metal infrastructure, universally used systems for total crown moulding. Methods: Starting from the preparation of a total crown master, 40 dies made of gypsum plaster, kind IV, were obtained and distributed at random in four groups (n = 10) that is: In-Ceram group, Procera group, Empress 2 group and Metal group.. After moulding, each infrastructure was individually cemented on the master die, ultra-low viscosity silicon adhesive was used to fill in the space between the infrastructure and the preparation area. After crown removal each replicate was weighed on a precision scale and was then separated in parts corresponding to the cervical wall interface and the occluso-axial wall interface; they were then weighed separately to get their volume. Results: Walls interface of infrastructure preparation/walls: Within this general estimate a statistically significant difference (P < 0,0001) was found between the studied groups. The main quantitative differences on the interface volume occurred between the In-Ceram group and the other groups. Occluso-axial walls interface of the infrastructure occlusal-axial preparation/walls: Here again, a statistically significant difference between the studied groups (P < 0,0001) is present. Main quantitative differences on the interface volume remain in relation to the In-Ceram group. Cervical wall interface of the infrastructure cervical preparation/wall: No statistically significant difference was found (P > 0,5) on the cervical interface volume between the Metal groups (least average) and In-Ceram, the latter presenting a slight increase on the volume of this interface, when compared to the first one. In relation to the Metal group, the cervical interface volume was greater in the Empress 2 group, followed by the Procera group, both showing a statistically significant difference when compared to the Metal group (P < 0,001 e P < 0,01 respectively). No statistically significant difference (P > 0,05) was found between the Procera and Empress 2 groups. Conclusions: Except for the relation of the cervical interface, the In-Ceram group showed the best results, followed by the Metal group, for internal fit. The Metal and In-Ceram groups presented the best performance in the internal fit, for the cervical interface. The results obtained suggest that these infrastructures are the most reliable ones regarding the internal fit considering the ones tested in this work.

Objetivo: comparar a qualidade do ajuste interno de três tipos de infra-estruturas cerâmicas e um tipo de infra-estrutura metálica, sistemas universalmente usados na confecção de coroas totais. Métodos: A partir de um preparo mestre de coroa total, 40 troquéis de gesso tipo IV foram obtidos e distribuídos randomicamente em quatro grupos (n = 10) a saber: Grupo In-Ceram, Grupo Procera, Grupo Empress 2 e Grupo Metal.. Após sua confecção, cada infra-estrutura foi cimentada individualmente sobre o troquél mestre, usando silicone de adição de ultra-baixa viscosidade para preencher o espaço entre a infra-estrutura e o preparo. Após a remoção das coroas, cada réplica foi pesada em balança de precisão e logo separadas nas porções correspondentes à interface parede cervical e interface parede ocluso-axial, sendo então pesadas separadamente, para posterior obtenção de seu volume. Resultados: Interface paredes do preparo/paredes da infra-estrutura: Neste computo geral, houve diferença estatística significativa (P < 0,0001) entre os grupos estudados. As principais diferenças quantitativas no volume da interface ocorreram entre o Grupo In-Ceram e os demais grupos. Interface paredes ocluso-axial do preparo/paredes ocluso-axial da infra-estrutura: Repete-se aqui, diferença estatística significativa entre os grupos estudados (P < 0,0001). Mantêm-se as principais diferenças quantitativas no volume da interface em relação ao Grupo In-Ceram. Interface parede cervical do preparo/parede cervical da infra-estrutura: Não houve diferença estatística significativa (P > 0,5) no volume da interface cervical entre os Grupos Metal (menor média) e In-Ceram, com este apresentando pequeno aumento no volume desta interface, comparado ao primeiro. Em relação ao Grupo Metal, o volume da interface cervical foi maior no Grupo Empress 2, seguido do Grupo Procera, ambos mostrando diferença estatística significativa no confronto com o Grupo Metal (P < 0,001 e P < 0,01 respectivamente). Não houve diferença estatística significativa (P > 0,05) entre os Grupos Procera e Empress 2. Conclusões: Exceto em relação à interface cervical, o Grupo In-Ceram mostou os melhores resultados, seguido do Grupo Metal, para o ajuste interno. Os Grupos Metal e In-Ceram apresentaram os melhores desempenhos no ajuste interno, para a interface cervical. Os resultados sugerem estas infra-estruturas como as mais confiáveis quanto ao ajuste interno dentre as testadas neste trabalho. / Objective: Compare the quality of the internal fit of three kinds of ceramic infrastructures and one kind of metal infrastructure, universally used systems for total crown moulding. Methods: Starting from the preparation of a total crown master, 40 dies made of gypsum plaster, kind IV, were obtained and distributed at random in four groups (n = 10) that is: In-Ceram group, Procera group, Empress 2 group and Metal group.. After moulding, each infrastructure was individually cemented on the master die, ultra-low viscosity silicon adhesive was used to fill in the space between the infrastructure and the preparation area. After crown removal each replicate was weighed on a precision scale and was then separated in parts corresponding to the cervical wall interface and the occluso-axial wall interface; they were then weighed separately to get their volume. Results: Walls interface of infrastructure preparation/walls: Within this general estimate a statistically significant difference (P < 0,0001) was found between the studied groups. The main quantitative differences on the interface volume occurred between the In-Ceram group and the other groups. Occluso-axial walls interface of the infrastructure occlusal-axial preparation/walls: Here again, a statistically significant difference between the studied groups (P < 0,0001) is present. Main quantitative differences on the interface volume remain in relation to the In-Ceram group. Cervical wall interface of the infrastructure cervical preparation/wall: No statistically significant difference was found (P > 0,5) on the cervical interface volume between the Metal groups (least average) and In-Ceram, the latter presenting a slight increase on the volume of this interface, when compared to the first one. In relation to the Metal group, the cervical interface volume was greater in the Empress 2 group, followed by the Procera group, both showing a statistically significant difference when compared to the Metal group (P < 0,001 e P < 0,01 respectively). No statistically significant difference (P > 0,05) was found between the Procera and Empress 2 groups. Conclusions: Except for the relation of the cervical interface, the In-Ceram group showed the best results, followed by the Metal group, for internal fit. The Metal and In-Ceram groups presented the best performance in the internal fit, for the cervical interface. The results obtained suggest that these infrastructures are the most reliable ones regarding the internal fit considering the ones tested in this work.

O estudo comparativo da distribuição de tensões de von Mises em dente endodonticamente tratado, com dois formatos de retentores intra-radiculares, pré-fabricado cilíndrico/escalonado e fundido cônico, foi realizado pelo método dos elementos finitos em modelos tridimensionais de caninos superiores com geometria axi-simétrica e restaurados com coroas metalocerâmicas, aplicando-se uma carga oblíqua de 100N com 45 º de inclinação em relação ao seu longo eixo. Os resultados indicaram uma discreta diferença nos dois modelos (formatos) de retentores. O pino escalonado neutralizou mais as cargas no sentido corono-apical e no pino cônico ficou evidenciado o efeito de cunha. / The aim of this study was to compare the von Mises stress distribution on a human canine teeth endodontically treated and restored with two types of post and core. The analysis was made using the three dimensional Finite Element Analysis method. For the analysis was created and axy-simetric structure of the teeth, including a porcelain fused to metal crown, a cement layer, and the periodontal structures. The model was analyzed when a 100N load was applied on the surface of the crown with 45º angulation with the long axis of the teeth. The results showed that both models exhibit little difference, the “stair shape” post system neutralized the axial loads, and the conical shape post showed a wedge effect on the apical third of the root.