Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2018. / Submitted by Raquel Viana (raquelviana@bce.unb.br) on 2018-07-19T19:07:23Z No. of bitstreams: 1 2018_MarinaMansurRamagem.pdf: 2292469 bytes, checksum: cdefb233d41217103ef47eb8727b3080 (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2018-07-20T19:58:08Z (GMT) No. of bitstreams: 1 2018_MarinaMansurRamagem.pdf: 2292469 bytes, checksum: cdefb233d41217103ef47eb8727b3080 (MD5) / Made available in DSpace on 2018-07-20T19:58:08Z (GMT). No. of bitstreams: 1 2018_MarinaMansurRamagem.pdf: 2292469 bytes, checksum: cdefb233d41217103ef47eb8727b3080 (MD5) Previous issue date: 2018-07-19 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES); Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) e Fundação de Apoio a Pesquisa do Distrito Federal (FAPDF). / Restaurações em dentes vitais envolvem cuidados operatórios para preservar a integridade pulpar, uma vez que a elevação da temperatura pulpar pode resultar em danos celulares. A síntese de heat shock proteins (HSP) é umas das formas de se avaliar a severidade do trauma sofrido pela polpa dental em consequência de um estresse térmico. Esta pesquisa avaliou in vitro danos celulares produzidos pelo estresse térmico gerado sobre a cultura de células macrófagos RAW 264.7 devido ao uso de fotopolimerizadores LED – Valo Led (Ultradent Products Inc) e Bluephase G2 (Ivoclar Vivadent Ltda.) – de alta irradiância. As células foram irradiadas com os LED diretamente sobre a base da placa de cultivo celular de 24 poços sem ou com interposição de dentina e resina gerando os seguintes grupos: G1 – grupo controle; G2 – Valo; G3 – Valo e dentina; G4 – Valo e dentina e resina; G5 – Bluephase; G6 – Bluephase e dentina; G7 – Bluephase e dentina e resina. Avaliou-se o metabolismo celular - pelo ensaio de MTT-, a produção de óxido nítrico (NO), a morfologia celular pela microscopia eletrônica de varredura (MEV) e análise da expressão gênica da HSP 70 pelo teste de Polymerase Chain Reaction em tempo real (PCR) de cada grupo. Os dados de MTT e NO foram avaliados pelos testes não-paramétricos (Kruskal-Wallis e Mann-Whitney) e os de PCR por testes paramétricos (ANOVA e Tukey). Resultados: os grupos G2 e G3 resultaram nos menores valores para metabolismo celular quando comparados com o G1 (p<0.05); os grupos G4, G6 e G7 apresentaram valores de metabolismo celulares estatisticamente superiores ao G1; a produção de óxido nítrico foi baixa para todos os grupos, porém o grupo G1 e o G7 apresentaram valores estatisticamente superiores aos demais grupos (p<0.05); os grupos G2, G3 e G5 apresentaram células com menor número de prolongamentos entre elas e presença de restos/fragmentos celulares evidenciando morte celular; os grupos G2 e G5 foram os únicos que apresentaram dados estatisticamente superiores quando comparado com o grupo G1 para a expressão gênica da proteína HSP 70. Os resultados sugerem que a irradiação com os LED induz vias de sinalização para reparar o tecido celular danificado. Contudo, estudos adicionais são necessários para melhor evidenciação dos resultados obtidos, visto que este é um estudo in vitro. / Vital tooth restorations involve operative care to preserve pulp integrity, since raising the pulp temperature can result in cellular damage. The heat shock protein synthesis (HSP) is known as a way to evaluate the severity of the trauma suffered by the dental pulp as a result of thermal stress. The present study evaluated in vitro cell damage caused by thermal stress generated on RAW 264.7 cell culture due to the use of high irradiance LED - Valo Led (Ultradent Products Inc) and Bluephase G2 (Ivoclar Vivadent Ltda.). The cells were irradiated with the LED units directly on the base of the 24-well cell culture plate without or with dentin and/or resin interposition generating the following groups: G1 - control group; G2-Valo; G3 - Valo and dentin; G4 - Valo and dentin and resin; G5-Bluephase; G6 - Bluephase and dentin; G7 - Bluephase and dentin and resin. Samples from each group were used to evaluate cell metabolism by the MTT assay, nitric oxide (NO) production, cell morphology by scanning electron microscopy (SEM) and analysis of the gene expression of HSP 70 by the real time Polymerase Chain Reaction (PCR) test. MTT and NO data were evaluated by non-parametric (Kruskal-Wallis and Mann-Whitney) and RT-PCR data by parametric tests (ANOVA and Tukey). According to the results, it was possible to observe that the G2 and G3 groups resulted in the lowest values for cellular metabolism when compared to the G1 (p <0.05). The G4, G6 and G7 groups had statistically higher values of cellular metabolism than the G1. The production of nitric oxide was low for all groups, and the G1, as well as G7, presented statistically higher values than the other groups (p <0.05). In the analysis of the cell morphology, the G2, G3 and G5 groups presented cells with less number of extensions between them and presence of cell debris/fragments evidencing cell death. Analysis of the gene expression of HSP 70 demonstrated that the G2 and G5 groups were the only ones that presented statistically superior data when compared to the control group for the gene expression of the HSP 70 protein. The results suggest that the irradiation with the LED induce signaling pathways to repair damaged cell tissue. However, additional studies are needed to better demonstrate the results obtained, since this is an in vitro study.

Orientador: Alvaro Della Bona / Banca: Mário Alexandre Coelho Sinhoreti / Banca: Estevão Tomomitsu Kimpara / Resumo: O objetivo do estudo foi verificar a influência da angulação axial de preparos coronários na resistência à compressão de restaurações cerâmicas livres de metal a base de Y-TZP (YZ- Vita YZ) cobertas com uma porcelana (VM9- Vita VM9). Inicialmente foram realizadas as análises composicional e microestrutural das cerâmicas (YZ e VM9), bem como determinada a densidade (), o módulo de elasticidade (E) e a razão de Poisson (). Análise por elementos finitos (AEF) em modelos dimensionalmente iguais aos usados experimentalmente foi realizada para verificar a distribuição de tensões. Oitenta infra-estruturas (IE) de YZ foram usinadas pelo sistema CAD-CAM (Cerec inLab, Sirona) e divididas em 4 grupos, de acordo com o ângulo de convergência oclusal total (COT) do preparo coronário e o design da IE: G6 - COT de 6° e IE padrão (n=20); G12 - COT de 12° e IE padrão (n=20); G20 - COT de 20° e IE padrão (n=20); G20MOD - COT de 20° e IE modificada, compensando a inclinação do preparo (n=20). Todas as IE foram cobertas com VM9, cimentadas em modelos de resina epóxica reforçada por fibras de vidro e submetidas à carga compressiva até a fratura. Metade das restaurações de cada grupo (n=10) foi envelhecida por ciclagem mecânica (106 ciclos) antes do teste que aplicou uma carga compressiva nas restaurações. As falhas foram analisadas em estereomicroscópio e microscopia eletrônica de varredura (MEV), sendo determinada a origem da fratura. Os resultados foram avaliados estatisticamente usando análise de variância (ANOVA) e Tukey (=0,05). As análises composicionais e microestruturais e a determinação da , E e  revelaram dois materiais, mecânica e estruturalmente, distintos. A AEF mostrou maior valor de tensão máxima principal (TMP) na porcelana do G12 (4839 MPa), e na IE dos grupos... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of the study was to investigate the influence of the convergence angle of tooth preparation on the compression strength of Y-TZP-based ceramic (YZ- Vita YZ) infra-structure (IS) veneered by a feldspathic porcelain (VM9- Vita VM9). Microstructural and element analysis of the ceramics (YZ and VM9) were made, and density (), elastic modulus (E) and Poisson's ratio ( ) were obtained. Finite Element Stress Analysis (FEA) in dimensionally identical models to those used in vitro was performed to verify the stress distribution in the system. Eighty YZ specimens were fabricated by the Cerec inLab CAD-CAM system and divided into four groups according to the total occlusal convergence angle (TOC): G6 - 6° TOC and standard IS (n=20); G12 -12° TOC and standard IS (n=20); G20 -20° TOC and standard IS (n=20); G20MOD - 20° TOC and modified IS (n=20). All IS were veneered with VM9, cemented in a fiber reinforced epoxy resin die and submitted to a compressive load until fracture. Half of the specimens from each group (n=10) were cyclic fatigued (106 cycles) before testing. Failure analysis was made using stereomicroscope and scanning electron microscopy (SEM) to determine the fracture origin. Data were statistically analyzed using ANOVA and Tukey tests (=0.05). Microstructure and element analyses and the determination of , E and  revealed distinct materials. FEA showed the greatest maximum principal stress (MPS) value of 4839 MPa for the G12 in the porcelain and of 403.3 MPa (G6) and 388.8 MPa (G12) in the IS. The stress distribution in the porcelain was similar for G6 and G12 groups, whereas the stress distribution in the IS of the G20MOD group suggested a superior performance under compression load compared to other groups. The in vitro test showed the greater maximum fracture... (Complete abstract click electronic access below) / Mestre

A microinfiltração na interface dente /restauração é considerada como o fator mais crítico nos materiais estéticos, como as resinas compostas, e é afetada negativamente pela sua contração de polimerização, pelo estresse mastigatório e pelo coeficiente de expansão térmica linear, que levam ao rompimento do selamento marginal. Muitas são as técnicas para testar a propriedade de selamento marginal de restaurações “ in vivo" e “ in vitro". Entretanto as dificuldades na realização destes estudos são diversas, e uma delas, principalmente quando a pesquisa é realizada “ in vitro" , é a necessidade de se reproduzirem no laboratório as condições clínicas a que são submetidos esses materiais. Uma dessas condições está relacionada às mudanças térmicas intra-orais que ocorrem clinicamente, e produzem alterações volumétricas, permitindo a microinfiltração. O processo “ in vitro" ou laboratorial que reproduz estas mudanças é denominada ciclagem térmica, e é definida como o processo que submete a restauração e o dente à temperaturas extremas compatíveis com as que ocorrem na cavidade oral. O objetivo deste trabalho foi verificar a influência do número de ciclos no processo de termociclagem para o estudo da microinfiltração marginal de restaurações de resina composta, assim como comparar os métodos de avaliação desta microinfiltração: quantitativos (medida linear e da área) e qualitativo ( escores) dos espécimes. Para isto, cavidades circulares foram confeccionadas em 76 pré-molares, localizadas totalmente em cemento e/ou dentina e restauradas com o sistema Scotchbond Multi Purpose Plus / Z-100. Terminadas as restaurações, os dentes foram armazenados imersos em água destilada por 24 horas em uma estufa a 37oC. A seguir os dentes foram polidos e divididos em 4 grupos, que se diferenciaram apenas no número de ciclos a que foram submetidos: Grupo 1- não foi submetido a ciclagem térmica (controle); Grupo 2- submetido a 100 ciclos; Grupo 3- submetido a 200 ciclos; Grupo 4- submetido a 1000 ciclos. As temperaturas utilizadas foram de 5oC e 55oC, e os espécimes permaneceram imersos 15 segundos em cada banho. Para se evitar a penetração do corante em áreas indesejadas, todos os dentes tiveram seus forames apicais ampliados e em seu interior foi condensado amálgama e toda a superfície do dente foi coberta com 2 camadas de esmalte para unha, exceto 1mm ao redor das restaurações. Terminado o processo de termociclagem, os dentes, inclusive os do grupo controle (sem ciclagem), foram armazenados e submersos em fucsina a 0,5%, a 37oC por 24 horas. Os espécimes foram totalmente incluídos em cilindros de resina poliestirênica, adaptados à máquina de corte, e para cada espécime cerca de 4 secções foram obtidas. Estes cortes foram avaliados pelos métodos qualitativo (escore) e quantitativos (linear e área), e a seguir os resultados avaliados estatisticamente pelos testes de Kruskall-Wallis e de Correlação de Spearman. Com base nessa análise, pode-se concluir que: a termociclagem, nas condições em que foi empregada neste trabalho, não demonstrou influência estatisticamente significante na microinfiltração em restaurações de resina composta, quando comparados os grupos não ciclado e os termociclados (100, 200 ou 1000 ciclos); as metodologias de leitura qualitativa (escores) e quantitativas (linear e área), para medir a infiltração do corante se equivaleram, tanto nas avaliações dos valores médios como dos máximos de penetração do corante. / Marginal integrity is an important parameter to evaluate the longevity of a restorative material since that caries recurrence are related to the formation of a gap between teeth and restorative material. Microleakage is defined as the penetration of bacteria, fluids, molecules or ions between the cavity wall and the restorative material. Microleakage of composite resin restorations is related to the polimerization shrinkage, mastigatory stress, and the linear thermal expansion coeficient which lead the rupture of marginal sealing. There are a number of methods to test the sealing property of in vivo and in vitro restorations. However, the accomplishment of those tecniques are not easy. One of the difficulties of in vitro studies, is the reproduction of the clinical conditions to which these materials are subjected as the introral thermal changes. The laboratory process that reproduces these changes is named thermocycling, and it is defined as the in vitro process that submmits the tooth and the restoration to extreme temperatures compatible to the ones occuring in the oral cavity. The purpose of this study was to verify the influence of the cycles number on the thermocycling process for assessing the marginal microleakage of composite resin restorations as well as to compare the qualitative (scores) and quantitative (linear and area measurements) evaluation methods of the specimens. Circular cavities were prepared in 76 premolars, totally localized in cementum and/or dentine and restored with the Scothbond Multipurpose Plus / Z-100 system. The teeth were stored in distilled water at 37oC for 24 hours than polished and divided into four groups: Group 1- not submitted to thermocycling; Group 2- submitted to 100 cycles; Group 3- submitted to 200 cycles; Group 4- submitted to 1000 cycles. Thermocycling was processed between 5oC and 55oC with dwell time of 15 seconds in each bath. To avoid dye penetration in undesirable areas, the teeth were prepared with retrograde amalgams and coated with two layers of nail polish to within 1mm of the restorations margins. The teeth were stored in 0,5% fuchsin solution, 37oC for 24 hours. After this period, the specimens were totally embedded in polystirenic resin to be sectioned. Approximately 4 sections were made from each specimen. These sections were evaluated by both quantitative and qualitative methods, and then the results were statistically assessed. On the basis of this analysis it was concluded that: Thermocycling, under the conditions of this study did not influenced ststisticslly the microleakage of composite resin restorations. The qualitative (scores) and quantitatives (linear and area) reading methodologies to measure dye penetration were equivalent in the evaluations of the mean values and the maximum values of the dye penetration.

Avaliaram-se a resistência adesiva, por meio de testes de cisalhamento de porcelana aderida à dentina, e a microinfiltração marginal em incrustações de porcelana fixadas com três sistemas de fixação resinosos de dupla polimerização. Os sistemas utilizados foram o Enforce, Scotchbond Resin Cement/Scotchbond Multi-Uso Plus e Variolink Professional Set. Na primeira parte desta pesquisa, 30 molares humanos extraídos foram incluídos em cilindros de PVC e a superfície oclusal abrasionada até a exposição da dentina. Cilindros de porcelana foram confeccionados, jateados com óxido de alumínio com partículas de 50 µm e em seguida, condicionados com ácido fluorídrico a 8% por quatro minutos. Os corpos-de-prova foram divididos aleatoriamente em três grupos e fixados com os respectivos sistemas de fixação. Todos os espécimes foram armazenados em água a 37oC por 24 horas e o teste de resistência adesiva ao cisalhamento conduzido em uma máquina de testes universal Kratos. Os valores obtidos foram tabulados e submetidos à análise estatística. O modo de fratura dos espécimes também foi determinado. Na segunda parte do experimento, cavidades mesioclusodistais para incrustações de porcelana foram preparadas em 30 pré-molares humanos extraídos, mantendo-se o término cervical em esmalte. Estas cavidades foram moldadas e as incrustações de porcelana confeccionadas sobre o modelo refratário. As restaurações foram posicionadas sobre os respectivos dentes, os ajustes internos realizados e os espécimes divididos aleatoriamente em três grupos. Todas as incrustações tiveram sua superfície interna condicionada com ácido fluorídrico a 8% por quatro minutos e foram fixadas com os respectivos sistemas de fixação. Os corpos-de-prova foram armazenados em água destilada a 37oC por 24 horas, cobertos com esmalte de unha deixando livre 1mm em torno das margens da restauração e termociclados. Depois, os espécimes foram imersos em fucsina básica a 0,5% por 24 horas, lavados e seccionados no sentido mesiodistal, obtendo-se três secções de cada espécime. Os índices de infiltração marginal foram atribuídos por meio de uma lupa estereoscópica com aumento de 40X por três examinadores previamente calibrados. Foi estabelecido o critério de infiltração máxima do corante em cada corpo-de-prova de acordo com os seguintes escores: 0- nenhuma infiltração; 1- infiltração na parede gengival; 2- infiltração na parede axial; 3- infiltração na parede axial e em direção à polpa. Os dados obtidos foram analisados estatisticamente. Com base na análise dos resultados foi possível concluir que não houve diferença estatisticamente significante na resistência adesiva ao cisalhamento entre os sistemas de fixação Enforce e Scotchbond Resin Cement/Scotchbond Multi-Uso Plus, porém estas foram estatisticamente superiores ao sistema de fixação Variolink Professional Set. O modo de fratura dos corpos-de-prova submetidos à força de cisalhamento foi predominantemente mista para os sistemas de fixação Enforce e Scotchbond Resin Cement/ Scotchbond Multi-Uso Plus, enquanto o Sistema de fixação Variolink Professional Set apresentou fratura adesiva entre a dentina e o sistema de fixação em todos os espécimes. Embora nenhum dos sistemas de fixação utilizados tenha sido capaz de impedir a infiltração marginal, os sistemas Enforce e Scotchbond Resin Cement/ Scotchbond Multi-Uso Plus se comportaram de forma similar e estatisticamente superior ao sistema Variolink Professional Set. / The shear bond strength of porcelain discs bonded to dentin and the microleakage of porcelain inlays with 3 different dual resin cement systems were evaluated. The systems used were Enforce, Scotchbond Resin Cement/Scotchbond Multi-Uso Plus and Variolink Professional Set. In the first part of the experiment, 30 extracted human molars were embedded in PVC cylinders and their occlusal surfaces were abraded to expose the dentin. Porcelain cylinders were manufactured, abraded with 50µm aluminum oxide particles and etched with 8% hydrofluoric acid for 4 minutes. The specimens were divided randomly in 3 groups and bonded with one of the dual resin cements. All the specimens were stored in distilled water at 37°C for 24 hours and the shear bond strength test performed in a Kratos Universal Machine. The resulted bond strength values were recorded and submitted to a statistical analysis. The mode of fracture of the specimens was also evaluated. In the second part of the experiment, MOD cavity preparations with enamel margins were made in 30 extracted human premolars. Impressions were taken and porcelain inlays manufactured on refractory dies. The inlays were seated on the respective prepared teeth, internally adapted and then, the specimens were randomly divided in 3 groups. The internal surfaces of the inlays were etched with 8% hydrofluoric acid for 4 minutes and then bonded into the preparations with one of the dual resin cements. The specimens were stored in distilled water at 37°C for 24 hours, covered with nail varnish, leaving 1mm around the restoration margins uncovered, and finally thermocycled. Then, the specimens were immersed in 0.5% basic fuchsin for 24 hours, washed and cut in a mesio-distal direction, resulting in 3 sections for each specimen. The microleakage scores were attributed by 3 previously calibrated examiners using a stereomicroscope (40X magnification). The adopted criteria was maximum penetration of the die in each specimen, according to the following scores: 0 – no leakage; 1 – leakage at the gingival wall; 2 – leakage at the axial wall; 3 – leakage at the axial wall, toward the pulp. The data was statistically analyzed. Based on the results, it was concluded that there was no significant difference on shear bond strength between Enforce and Scotchbond Resin Cement / Scotchbond Multi-Uso Plus, but both were statistically superior than Variolink Professional Set. The mode of fracture of the specimens submitted to shear load was predominantly combined for the Enforce and Scotchbond Resin Cement / Scotchbond Multi-Uso Plus, while the Variolink Professional Set presented adhesive failures between dentin and the resin cement in all of the specimens. Although none of the dual resin cement systems had been able to prevent microleakage, Enforce and Scotchbond Resin Cement / Scotchbond Multi-Uso Plus system performed similarly and were statistically superior than the Variolink Professional Set system.

Made available in DSpace on 2014-06-11T19:28:57Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-02-03Bitstream added on 2014-06-13T20:58:49Z : No. of bitstreams: 1 corazza_ph_me_sjc.pdf: 927368 bytes, checksum: f79b2ce575ab972fcb3906a754af7d8c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo do estudo foi verificar a influência da angulação axial de preparos coronários na resistência à compressão de restaurações cerâmicas livres de metal a base de Y-TZP (YZ- Vita YZ) cobertas com uma porcelana (VM9- Vita VM9). Inicialmente foram realizadas as análises composicional e microestrutural das cerâmicas (YZ e VM9), bem como determinada a densidade (), o módulo de elasticidade (E) e a razão de Poisson (). Análise por elementos finitos (AEF) em modelos dimensionalmente iguais aos usados experimentalmente foi realizada para verificar a distribuição de tensões. Oitenta infra-estruturas (IE) de YZ foram usinadas pelo sistema CAD-CAM (Cerec inLab, Sirona) e divididas em 4 grupos, de acordo com o ângulo de convergência oclusal total (COT) do preparo coronário e o design da IE: G6 – COT de 6° e IE padrão (n=20); G12 – COT de 12° e IE padrão (n=20); G20 – COT de 20° e IE padrão (n=20); G20MOD – COT de 20° e IE modificada, compensando a inclinação do preparo (n=20). Todas as IE foram cobertas com VM9, cimentadas em modelos de resina epóxica reforçada por fibras de vidro e submetidas à carga compressiva até a fratura. Metade das restaurações de cada grupo (n=10) foi envelhecida por ciclagem mecânica (106 ciclos) antes do teste que aplicou uma carga compressiva nas restaurações. As falhas foram analisadas em estereomicroscópio e microscopia eletrônica de varredura (MEV), sendo determinada a origem da fratura. Os resultados foram avaliados estatisticamente usando análise de variância (ANOVA) e Tukey (=0,05). As análises composicionais e microestruturais e a determinação da , E e  revelaram dois materiais, mecânica e estruturalmente, distintos. A AEF mostrou maior valor de tensão máxima principal (TMP) na porcelana do G12 (4839 MPa), e na IE dos grupos... / The aim of the study was to investigate the influence of the convergence angle of tooth preparation on the compression strength of Y-TZP-based ceramic (YZ- Vita YZ) infra-structure (IS) veneered by a feldspathic porcelain (VM9- Vita VM9). Microstructural and element analysis of the ceramics (YZ and VM9) were made, and density (), elastic modulus (E) and Poisson’s ratio ( ) were obtained. Finite Element Stress Analysis (FEA) in dimensionally identical models to those used in vitro was performed to verify the stress distribution in the system. Eighty YZ specimens were fabricated by the Cerec inLab CAD-CAM system and divided into four groups according to the total occlusal convergence angle (TOC): G6 – 6° TOC and standard IS (n=20); G12 –12° TOC and standard IS (n=20); G20 –20° TOC and standard IS (n=20); G20MOD - 20° TOC and modified IS (n=20). All IS were veneered with VM9, cemented in a fiber reinforced epoxy resin die and submitted to a compressive load until fracture. Half of the specimens from each group (n=10) were cyclic fatigued (106 cycles) before testing. Failure analysis was made using stereomicroscope and scanning electron microscopy (SEM) to determine the fracture origin. Data were statistically analyzed using ANOVA and Tukey tests (=0.05). Microstructure and element analyses and the determination of , E and  revealed distinct materials. FEA showed the greatest maximum principal stress (MPS) value of 4839 MPa for the G12 in the porcelain and of 403.3 MPa (G6) and 388.8 MPa (G12) in the IS. The stress distribution in the porcelain was similar for G6 and G12 groups, whereas the stress distribution in the IS of the G20MOD group suggested a superior performance under compression load compared to other groups. The in vitro test showed the greater maximum fracture... (Complete abstract click electronic access below)

Este trabalho de conclusão pretende conhecer e analisar os procedimentos para intervenções em obras de restauração no estado do Rio Grande do Sul. Para isto utilizou pesquisa bibliográfica sobre os procedimentos recomendados nas Cartas Patrimoniais e nas recomendações dos teóricos da restauração. Estes documentos representam as tentativas de estabelecer normas e procedimentos para a conservação e restauração, assim como de definir os conceitos utilizados na área da preservação do patrimônio cultural. Também foi importante o conhecimento das intervenções realizadas, sendo analisada as obras do arquiteto Edegar Bittencourt da Luz, por ser este profissional um dos mais capacitados no Estado nesta área. Para conhecimento das intervenções ocorridas foi realizado levantamento através da técnica de entrevista com este profissional e sua equipe técnica, sobre a atuação profissional, recomendações e aspectos críticos apontados por ele. Estes aspectos críticos foram verificados se estão contidos nas Cartas Patrimoniais e nas teorias de restauração, e quais as recomendações sobre os mesmos. Também foi sugerido trabalhos futuros na área como forma de aperfeiçoar a recuperação de bens de interesse cultural. Conclui-se que os aspectos críticos apontados são recomendados na maioria das orientações internacionais para o adequado desenvolvimento das obras de restauração e que ainda não existe o verdadeiro entendimento do conceito de restauração por parte de alguns profissionais que se envolvem com este tipo de obra. Este trabalho além de contribuir para o conhecimento dos profissionais da área, também é importante para os leigos no assunto, que muitas vezes confundem o verdadeiro significado da palavra restauração, e dos diversos conceitos utilizados nesta área.

Este trabalho de conclusão pretende conhecer e analisar os procedimentos para intervenções em obras de restauração no estado do Rio Grande do Sul. Para isto utilizou pesquisa bibliográfica sobre os procedimentos recomendados nas Cartas Patrimoniais e nas recomendações dos teóricos da restauração. Estes documentos representam as tentativas de estabelecer normas e procedimentos para a conservação e restauração, assim como de definir os conceitos utilizados na área da preservação do patrimônio cultural. Também foi importante o conhecimento das intervenções realizadas, sendo analisada as obras do arquiteto Edegar Bittencourt da Luz, por ser este profissional um dos mais capacitados no Estado nesta área. Para conhecimento das intervenções ocorridas foi realizado levantamento através da técnica de entrevista com este profissional e sua equipe técnica, sobre a atuação profissional, recomendações e aspectos críticos apontados por ele. Estes aspectos críticos foram verificados se estão contidos nas Cartas Patrimoniais e nas teorias de restauração, e quais as recomendações sobre os mesmos. Também foi sugerido trabalhos futuros na área como forma de aperfeiçoar a recuperação de bens de interesse cultural. Conclui-se que os aspectos críticos apontados são recomendados na maioria das orientações internacionais para o adequado desenvolvimento das obras de restauração e que ainda não existe o verdadeiro entendimento do conceito de restauração por parte de alguns profissionais que se envolvem com este tipo de obra. Este trabalho além de contribuir para o conhecimento dos profissionais da área, também é importante para os leigos no assunto, que muitas vezes confundem o verdadeiro significado da palavra restauração, e dos diversos conceitos utilizados nesta área.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2013. / Submitted by Alaíde Gonçalves dos Santos (alaide@unb.br) on 2013-12-09T15:26:52Z No. of bitstreams: 1 2013_JulianaSaLeitaoFiuzaLima.pdf: 19697388 bytes, checksum: 11a2ac8c62a3944513fc450daa199aa7 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2013-12-10T11:24:25Z (GMT) No. of bitstreams: 1 2013_JulianaSaLeitaoFiuzaLima.pdf: 19697388 bytes, checksum: 11a2ac8c62a3944513fc450daa199aa7 (MD5) / Made available in DSpace on 2013-12-10T11:24:25Z (GMT). No. of bitstreams: 1 2013_JulianaSaLeitaoFiuzaLima.pdf: 19697388 bytes, checksum: 11a2ac8c62a3944513fc450daa199aa7 (MD5) / A estabilidade de cor é um dos parâmetros clínicos mais importantes em relação ao sucesso de restaurações estéticas. Ainda que a qualidade destes materiais tenha sido aprimorada nos últimos anos, o manchamento de resinas compostas ainda é uma das principais razões que levam à substituição de restaurações em dentes anteriores. Os objetivos deste estudo foram avaliar a estabilidade de cor de cinco resinas compostas (Filtek Z350 XT, Estelite ? Quick, Durafill VS, Opallis e Empress Direct) após a exposição a diferentes bebidas usualmente consumidas e investigar a possibilidade de remoção do manchamento ocorrido, pelo repolimento. Para isso, 20 espécimes foram confeccionados para cada resina composta e avaliados após a imersão em vinho tinto, café, Coca-Cola e água destilada (controle) por 24 horas, 7 e 30 dias. Ao final do experimento os espécimes foram repolidos com discos de óxido de alumínio (Sof-Lex, 3M ESPE). As mensurações de cor foram realizadas utilizando um espectrofotômetro (Vita EasyShade Compact) baseado no sistema de cor CIELAB. Os dados foram analisados estatisticamente pelos testes ANOVA e post hoc Tukey (p=0,05). Os resultados mostraram que todas as resinas compostas apresentaram alteração de cor após o manchamento artificial. A resina Filtek Z350 XT resultou em maior alteração de cor do que as resinas Durafill VS e Estelite ? Quick. O vinho tinto exibiu o maior potencial corante enquanto a Coca-Cola não apresentou diferenças significativas em relação ao grupo controle. Após o repolimento todos os materiais apresentaram redução significativa do manchamento provocado pelo vinho e pelo café. Foi concluído que a alteração de cor varia de acordo com a composição do material e as diferentes soluções em que são expostos. O repolimento é efetivo na redução do manchamento extrínseco e deve ser considerado antes da decisão pela substituição de restaurações estéticas por motivos relacionados à cor. _______________________________________________________________________________________ ABSTRACT / Color stability is one of the most important clinical parameters related to success of esthetic restorations. Although the quality of these materials has improved in recent years, discoloration of resin composites remains a major cause of replacement of anterior restorations. The aim of this study was to evaluate the color stability of five different composites (Filtek Z350 XT, Estelite ? Quick, Durafill VS, Opallis e Empress Direct) after exposure to commonly consumed beverages and the possibility to remove stain with repolishing. Twenty disk-shaped specimens were prepared from five different composites and evaluated after immersion in red wine, coffee, cola or distilled water (control) for 24 hours, 7 and 30 days. At the end of the experiment the specimens were repolished using alumin oxide discs (Sof-Lex, 3M ESPE). Color measurements were made using a spectrophotometer (Vita EasyShade Compact) based on the CIELAB color scale. Data were statistically analyzed by ANOVA and post hoc Tukey tests (?=0.05). The results showed that all composites presented color change after the stain challenge. Filtek Z350 XT showed a higher color change than Durafill VS and Estelite ? Quick. Red wine resulted in greatest pigmentation while cola did not show a significant difference from the control group. After repolishing all composites presented significant reduction in coffee and wine staining. Composite staining susceptibility proved to vary among composite types and staining solutions. Repolishing is an effective method to reduce extrinsic stains and must be considered before the decision to replace esthetic restorations for color reasons.

Este trabalho de conclusão pretende conhecer e analisar os procedimentos para intervenções em obras de restauração no estado do Rio Grande do Sul. Para isto utilizou pesquisa bibliográfica sobre os procedimentos recomendados nas Cartas Patrimoniais e nas recomendações dos teóricos da restauração. Estes documentos representam as tentativas de estabelecer normas e procedimentos para a conservação e restauração, assim como de definir os conceitos utilizados na área da preservação do patrimônio cultural. Também foi importante o conhecimento das intervenções realizadas, sendo analisada as obras do arquiteto Edegar Bittencourt da Luz, por ser este profissional um dos mais capacitados no Estado nesta área. Para conhecimento das intervenções ocorridas foi realizado levantamento através da técnica de entrevista com este profissional e sua equipe técnica, sobre a atuação profissional, recomendações e aspectos críticos apontados por ele. Estes aspectos críticos foram verificados se estão contidos nas Cartas Patrimoniais e nas teorias de restauração, e quais as recomendações sobre os mesmos. Também foi sugerido trabalhos futuros na área como forma de aperfeiçoar a recuperação de bens de interesse cultural. Conclui-se que os aspectos críticos apontados são recomendados na maioria das orientações internacionais para o adequado desenvolvimento das obras de restauração e que ainda não existe o verdadeiro entendimento do conceito de restauração por parte de alguns profissionais que se envolvem com este tipo de obra. Este trabalho além de contribuir para o conhecimento dos profissionais da área, também é importante para os leigos no assunto, que muitas vezes confundem o verdadeiro significado da palavra restauração, e dos diversos conceitos utilizados nesta área.

Orientador: Luiz Andre Freire Pimenta / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T12:59:51Z (GMT). No. of bitstreams: 1 Morais_PaulaMathiasRabelode_M.pdf: 2726762 bytes, checksum: b8bc543135bb81ee07f4e05d34c97e58 (MD5) Previous issue date: 1997 / Resumo: o objetivo do presente trabalho foi avaliar a penetração de corante ao redor de restaurações de amálgama, em cavidades com margens em cemento e/ou dentina, por meio de um teste quantitativo. Cavidades classe V padronizadas (2 mm de diâmetro e 1,5 mm de profundidade) foram preparadas, 3 mm abaixo da junção amelo-cementária, na superficie vestibular da raiz de 75 dentes humanos unirradiculares recém-extraídos. Os dentes foram divididos aleatoriamente em cinco grupos contendo quinze unidades experimentais cada. Antes de serem restauradas com a liga de amálgama tipo mistura Permite C, as cavidades foram forradas com: Copalite (CO); Panavia Ex (P A); Scotchbond Multi-Purpose Plus (SBMP+); Photac-Bond (PB), sendo o grupo controle (C) restaurado sem o uso de qualquer tipo de agente intermediário. As raízes restauradas foram armazenadas em umidade relativa a 37°C, por 24 horas e, após esse periodo, as restaurações foram polidas. Os conjuntos dente/restauração foram submetidos a 500 ciclos térmicos entre 5:i::2°C e 55:i::2°C, com banhos de um minuto em cada temperatura, e imersos em solução de azul de metileno a 2% por doze horas, em 37°C. A microinfiltração foi quantifiéada através da espectrofotometria e exwessa em ~g de corante. Os valores das medianas foram: C=10,610; CO=7,422; PA=:3,066; PB=1,941; SB=0,234. A análise estatística realizada, utilizando o teste Kruskal-Wallis, indicou diferença significativa entre todos os grupos avaliados. O uso do SBMP+ sob as restaurações de amálgama mostrou ser o procedimento mais efetivo na redução da microinfiltração, seguido pelo uso do PB; PA; CO e pelo grupo controle, que exibiu os piores resultados / Abstract: The purpose of tms in vitro study was to evaluate the dye penetration around amalgam restorations in dentin cavities, by a quantitative test. Standardized circular cavities (2mm wide and 1,5mm depth) were prepared on facial surface of 75 extracted human unirradicular teeth. The cavities were made 3mm below the CEJ. The teeth were randomly divided into five groups of fifteen each. Before restoring with an admixture alloy - Permite C, the cavities were lined with Copalite (CO), Panavia Ex (PA), ScotchBond Multi-Purpose Plus (SBMP+), Photac-Bond (PB), and a control group (C) with no lining agent. The restorations were stored in relative humidity at 37°C for 24 hours, after that, finished and polished. The specimens were thermocycled between 5 :i: 2°C and 55 :i: 2°C for 500 cycles with one minute dwell time, followed by immersion in a 2% methylene blue solution for twelve hours at 37°C. The quantitative microleakage was evaluated by spectrophotometry and was expressed by ~g dye. Th~ median values were: C=10.610; CO= 7.422; PA= 3.066; PB= 1.941; SB=0.234. Statistical analysis using Kruskal-Wallis test indicated significant differences among alI groups (x,2=67.653, a=O.OOOl). The results showed that the use of bonded amalgam restor~tions with SBMP+ is more effective in reducing microleakage, followed by the use of PB; P A; CO and the unlined restorations (C), that showed the worst result, under the experimental conditions / Mestrado / Dentística / Mestre em Clínica Odontológica