Made available in DSpace on 2014-06-11T19:25:34Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-01-21Bitstream added on 2014-06-13T19:32:50Z : No. of bitstreams: 1 akita_ah_me_araiq.pdf: 2521064 bytes, checksum: d6299e2b6a5a5f33b4d14c1d8463e878 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Dois sistemas foram estudados utilizando uma microcélula desenvolvida no laboratório: a) ferricianeto/ferrocianeto em KCl 0,6 mol L-1 e em H2SO4 0,1 mol L-1 e b) aços ferramentas SAE 1045 e X155CrVMo12-1 e as respectivas regiões aço/cermet/níquel-cobre-níquel/aço em solução aquosa de NaCl 0,6 mol L-1 . Na primeira parte, o sistema ferri/ferrocianeto foi estudado por voltametria cíclica (CV) e espectroscopia de impedância eletroquímica (EIS) sobre Pt e carbono vítreo com eletrodos de tamanho convencional e com a microcélula (capilares de 200 e 1200 μm de diâmetro). Os valores de separação dos picos de corrente anódica e catódica e a razão entre as correntes desses picos (ipc/ipa > 0,90) sugerem um processo de eletrodo quase-reversível sem reação química acoplada para todas as condições estudadas. Os valores das funções-corrente mostram diferenças significativas e os coeficientes de difusão diferem em ca. uma ordem de grandeza entre a microcélula e a célula convencional. Espectros de impedância eletroquímica para a microcélula foram similares aos obtidos em eletrodo convencional mostrando uma constante de tempo em alta freqüência associada à transferência de carga e perfil típico de difusão do tipo de Warburg na região de médias freqüências. Em baixas freqüências há um desvio do comportamento esperado para uma difusão do tipo de Warburg. Na segunda parte, os aços ferramenta estudados antes da solda foram SAE 1045, X155CrVMo12-1 (F521) e 90MnCrV8 (F522) usando célula convencional e os dois primeiros também com a microcélula. A microcélula foi usada para os estudos eletroquímicos das regiões aço/cermet/níquel-cobre-níquel/aço formadas pela solda do tipo difusão dinâmica, uma vez que é praticamente impossível preparar um eletrodo com composição semelhante àquela da região de solda. A superfície atacada por solução aquosa de cloreto foi observada em tempo real usando um microscópio. / Two systems were studied using a home made microcell: a) ferricyanide/ferrocyanide in 0.6 mol L-1 KCl and in 0.1 mol L-1 H2SO4, and b) the SAE 1045 and X155CrVMo12-1 tool steels and the corresponding steel/cermet/níquel- copper-nickel/steel interphases in 0.6 mol L-1 NaCl solution. In the first part, the ferri/ferrocynide system was studied by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) on Pt and glassy carbon electrodes with electrodes of conventional size and with a microcell (capillaries of 200 and 1200 µm diameter). For all conditions studied, the anodic and cathodic peak potential difference and the anodic and cathodic current peak ration values suggest a quasi-reversible charge transfer process without coupled chemical reactions. Comparing microcell and conventional cell the current function values showed some significant differences and the diffusion coefficient values are ca. one order of magnitude different each other. Electrochemical impedance spectra were similar for both microcell and conventional cell and were interpreted considering a time constant at high frequencies related to the charge transfer reaction and a typical Warburg type diffusion at middle frequencies region. At low frequencies a deviation from the expected typical Warburg type diffusion was observed. In the second part, the SAE 1045, X155CrVMo12-1 (F521) and 90MnCrV8 (F522) tool steels were studied using a conventional cell and the first two steels also with a microcell. The microcell was mainly used to investigate the steel/cermet/nickel- copper-nickel/steel regions prepared by dynamic diffusion bond, since is almost impossible to prepare an electrode with the same composition of the welding region. The attacked surface by using chloride solution was observed in real time by means of a microscope. Electrochemical and microscopic... (Complete abstract click electronic access below)

Projetos de instalações industriais com requisitos de assepsia e resistência à corrosão têm os aços inoxidáveis austeníticos como materiais de engenharia, e a liga AISI 316L é amplamente utilizada. A soldagem de chapas espessas é executada por processos MIG e a qualificação do procedimento de soldagem é realizada com base em propriedades mecânicas, avaliação insuficiente para aplicações que necessitam de uma película passiva resistente. A microestrutura da zona fundida da liga AISI 316L exerce influência sobre a resistência à corrosão, e há a necessidade de definir os mecanismos que governam a influência da fase sigma na resistência à corrosão. Inserido neste contexto, o objetivo do presente estudo foi avaliar a influência da fase sigma na resistência à corrosão em microrregiões de juntas soldadas multipasse da liga AISI 316L produzidas pelo processo MIG nos modos de transferência metálica pulsado, curto-circuito e spray. A metodologia consistiu em reproduzir amostras soldadas com parâmetros de soldagem aplicados na indústria para os modos de transferência metálica de interesse, com detalhada caracterização microestrutural da zona fundida de cada condição de soldagem. Em seguida, foram conduzidos ensaios eletroquímicos de corrosão em microrregiões da junta soldada em solução de 3,5% NaCl, e a influência da fase sigma na corrosão por pite foi avaliada por ensaio de imersão em solução de cloreto férrico (6% FeCl3). Caracterizou-se a área exposta à varredura por técnicas de microscopia ótica, microscopia eletrônica de varredura e microanálise química. A soldagem no modo pulsado resultou em uma zona fundida com microestrutura bifásica com a mais baixa fração volumétrica de ferrita delta, de refinada morfologia e isenta de fase sigma, proporcionando o mais nobre desempenho nos ensaios de corrosão, que se manifestou pelo mecanismo de corrosão localizada. A avaliação da área exposta à varredura demonstrou que, previamente a corrosão por pite, a corrosão incia-se de forma localizada, contudo, sem corrosão preferencial de uma das fases, característica que proporcionou parâmetros eletroquímicos mais nobres do que aqueles com corrosão seletiva de fases. Está característica é atribuída à ausência da fase sigma na microestrutura da zona fundida do modo pulsado. No modo curto-circuito ocorreu à decomposição eutetóide da ferrita delta formando a austenita secundária e a fase sigma, sendo está última precipitada principalmente no interior da ferrita delta. A morfologia da corrosão se dá, na fase inicial, como corrosão seletiva de fases, com degradação preferencial da austenita secundária e em direção a ferrita delta, devido à fragilização desta fase pela precipitação de fase sigma em seu interior. A degradação seletiva das fases austenita secundária e ferrita delta causam danos localizados ao filme passivo e, nestas regiões empobrecidas de cromo e molibdênio, ocorre à corrosão por pite. O modo spray com a mais elevada energia de soldagem resultou em uma ferrita delta grosseira e com estreitas bandas de austenita na microrregião de enchimento do chanfro e na raiz da solda, com alto índice de fase sigma nestas localizações. O processo corrosivo da zona fundida caracterizou-se por corrosão seletiva da fase austenita secundária e em direção à matriz austenítica, uma vez que a fase sigma revestiu a ferrita delta, tornando-a a região de comportamento catódico entre o par galvânico formado entre as fases austenita e ferrita delta. A corrosão seletiva da matriz austenítica causa a fragilização localizada do filme passivo com consequente corrosão por pite. O trabalho realizado permite concluir que o potencial de pite foi reduzido com a presença de fase sigma e fases a esta associada, e justamente o modo pulsado obteve destacada resistência à corrosão em função da ausência da fase sigma em sua microestrutura. / Industrial plant designs with asepsis and corrosion resistance requirements have austenitic stainless steels as engineering materials, and the AISI 316L alloy is widely used. The welding of thick plates is performed by MIG processes and the qualification of the welding procedure is carried out based on mechanical properties, insufficient evaluation for applications that require a resistant passive film. The microstructure of the molten zone of the AISI 316L alloy influences the corrosion resistance, and it is necessary to define the mechanisms that govern the influence of the sigma phase on corrosion resistance. In this context, the aim of the present study was to evaluate the influence of the sigma phase on the corrosion resistance in microrregions of multipass welded joints of the AISI 316L alloy produced by MIG process with metal transfer in pulsed, short circuit and spray modes. The methodology consisted in reproducing welded samples with welding parameters applied in the industry for the modes of metallic transfer of interest, with detailed microstructural characterization of the molten zone of each welding condition. Then, electrochemical corrosion tests were carried out in microrregions of the welded joint in 3.5% NaCl solution, and the influence of the sigma phase on pitting corrosion was evaluated by immersion test in ferric chloride solution (6% FeCl3). The area exposed to the scanning was characterized by optical microscopy, scanning electron microscopy and chemical microanalysis. Pulsed mode welding resulted in a molten zone with a biphasic microstructure with the lowest volume fraction of delta ferrite, refined morphology and sigma phase free, providing the noblest performance in the corrosion tests, which occurred in the form of localized corrosion. The evaluation of the area exposed to the scan showed that, prior to pitting corrosion, the corrosion started in a localized manner, however, without preferential corrosion of one of the phases, a characteristic that gave better electrochemical parameters than those with selective corrosion of phases. This characteristic is attributed to the absence of the sigma phase in the microstructure of the molten zone of the pulsed mode. In the short-circuit mode, the eutectoid decomposition of the delta ferrite formed the secondary austenite and the sigma phase, the latter being mainly precipitated inside the delta ferrite. The corrosion morphology occurs in the initial phase as selective corrosion of phases, with preferential degradation of the secondary austenite and towards the ferrite delta, due to the embrittlement of this phase by the precipitation of the sigma phase inside. The selective degradation of the secondary austenite and delta ferrite phases causes localized damage to the passive film and, in these impoverished regions of chromium and molybdenum, occurs to pitting corrosion. The spray mode with the highest welding energy resulted in a coarse delta ferrite with narrow bands of austenite in the chamfer filling microrregion and at the root of the weld, with a high sigma phase index at these locations. The corrosive process of the molten zone was characterized by selective corrosion of the secondary austenite phase and towards the austenitic matrix, since the sigma phase covered the delta ferrite, making it the region of cathodic behavior between the galvanic pair formed between the austenite and ferrite delta phases. Selective corrosion of the austenitic matrix causes localized embrittlement of the passive film with consequent pitting corrosion. The study accomplished allows concluding that the pitting potential was reduced with the presence of sigma phase and phases associated with it, and precisely the pulsed mode obtained outstanding corrosion resistance due to the absence of the sigma phase in its microstructure.

Projetos de instalações industriais com requisitos de assepsia e resistência à corrosão têm os aços inoxidáveis austeníticos como materiais de engenharia, e a liga AISI 316L é amplamente utilizada. A soldagem de chapas espessas é executada por processos MIG e a qualificação do procedimento de soldagem é realizada com base em propriedades mecânicas, avaliação insuficiente para aplicações que necessitam de uma película passiva resistente. A microestrutura da zona fundida da liga AISI 316L exerce influência sobre a resistência à corrosão, e há a necessidade de definir os mecanismos que governam a influência da fase sigma na resistência à corrosão. Inserido neste contexto, o objetivo do presente estudo foi avaliar a influência da fase sigma na resistência à corrosão em microrregiões de juntas soldadas multipasse da liga AISI 316L produzidas pelo processo MIG nos modos de transferência metálica pulsado, curto-circuito e spray. A metodologia consistiu em reproduzir amostras soldadas com parâmetros de soldagem aplicados na indústria para os modos de transferência metálica de interesse, com detalhada caracterização microestrutural da zona fundida de cada condição de soldagem. Em seguida, foram conduzidos ensaios eletroquímicos de corrosão em microrregiões da junta soldada em solução de 3,5% NaCl, e a influência da fase sigma na corrosão por pite foi avaliada por ensaio de imersão em solução de cloreto férrico (6% FeCl3). Caracterizou-se a área exposta à varredura por técnicas de microscopia ótica, microscopia eletrônica de varredura e microanálise química. A soldagem no modo pulsado resultou em uma zona fundida com microestrutura bifásica com a mais baixa fração volumétrica de ferrita delta, de refinada morfologia e isenta de fase sigma, proporcionando o mais nobre desempenho nos ensaios de corrosão, que se manifestou pelo mecanismo de corrosão localizada. A avaliação da área exposta à varredura demonstrou que, previamente a corrosão por pite, a corrosão incia-se de forma localizada, contudo, sem corrosão preferencial de uma das fases, característica que proporcionou parâmetros eletroquímicos mais nobres do que aqueles com corrosão seletiva de fases. Está característica é atribuída à ausência da fase sigma na microestrutura da zona fundida do modo pulsado. No modo curto-circuito ocorreu à decomposição eutetóide da ferrita delta formando a austenita secundária e a fase sigma, sendo está última precipitada principalmente no interior da ferrita delta. A morfologia da corrosão se dá, na fase inicial, como corrosão seletiva de fases, com degradação preferencial da austenita secundária e em direção a ferrita delta, devido à fragilização desta fase pela precipitação de fase sigma em seu interior. A degradação seletiva das fases austenita secundária e ferrita delta causam danos localizados ao filme passivo e, nestas regiões empobrecidas de cromo e molibdênio, ocorre à corrosão por pite. O modo spray com a mais elevada energia de soldagem resultou em uma ferrita delta grosseira e com estreitas bandas de austenita na microrregião de enchimento do chanfro e na raiz da solda, com alto índice de fase sigma nestas localizações. O processo corrosivo da zona fundida caracterizou-se por corrosão seletiva da fase austenita secundária e em direção à matriz austenítica, uma vez que a fase sigma revestiu a ferrita delta, tornando-a a região de comportamento catódico entre o par galvânico formado entre as fases austenita e ferrita delta. A corrosão seletiva da matriz austenítica causa a fragilização localizada do filme passivo com consequente corrosão por pite. O trabalho realizado permite concluir que o potencial de pite foi reduzido com a presença de fase sigma e fases a esta associada, e justamente o modo pulsado obteve destacada resistência à corrosão em função da ausência da fase sigma em sua microestrutura. / Industrial plant designs with asepsis and corrosion resistance requirements have austenitic stainless steels as engineering materials, and the AISI 316L alloy is widely used. The welding of thick plates is performed by MIG processes and the qualification of the welding procedure is carried out based on mechanical properties, insufficient evaluation for applications that require a resistant passive film. The microstructure of the molten zone of the AISI 316L alloy influences the corrosion resistance, and it is necessary to define the mechanisms that govern the influence of the sigma phase on corrosion resistance. In this context, the aim of the present study was to evaluate the influence of the sigma phase on the corrosion resistance in microrregions of multipass welded joints of the AISI 316L alloy produced by MIG process with metal transfer in pulsed, short circuit and spray modes. The methodology consisted in reproducing welded samples with welding parameters applied in the industry for the modes of metallic transfer of interest, with detailed microstructural characterization of the molten zone of each welding condition. Then, electrochemical corrosion tests were carried out in microrregions of the welded joint in 3.5% NaCl solution, and the influence of the sigma phase on pitting corrosion was evaluated by immersion test in ferric chloride solution (6% FeCl3). The area exposed to the scanning was characterized by optical microscopy, scanning electron microscopy and chemical microanalysis. Pulsed mode welding resulted in a molten zone with a biphasic microstructure with the lowest volume fraction of delta ferrite, refined morphology and sigma phase free, providing the noblest performance in the corrosion tests, which occurred in the form of localized corrosion. The evaluation of the area exposed to the scan showed that, prior to pitting corrosion, the corrosion started in a localized manner, however, without preferential corrosion of one of the phases, a characteristic that gave better electrochemical parameters than those with selective corrosion of phases. This characteristic is attributed to the absence of the sigma phase in the microstructure of the molten zone of the pulsed mode. In the short-circuit mode, the eutectoid decomposition of the delta ferrite formed the secondary austenite and the sigma phase, the latter being mainly precipitated inside the delta ferrite. The corrosion morphology occurs in the initial phase as selective corrosion of phases, with preferential degradation of the secondary austenite and towards the ferrite delta, due to the embrittlement of this phase by the precipitation of the sigma phase inside. The selective degradation of the secondary austenite and delta ferrite phases causes localized damage to the passive film and, in these impoverished regions of chromium and molybdenum, occurs to pitting corrosion. The spray mode with the highest welding energy resulted in a coarse delta ferrite with narrow bands of austenite in the chamfer filling microrregion and at the root of the weld, with a high sigma phase index at these locations. The corrosive process of the molten zone was characterized by selective corrosion of the secondary austenite phase and towards the austenitic matrix, since the sigma phase covered the delta ferrite, making it the region of cathodic behavior between the galvanic pair formed between the austenite and ferrite delta phases. Selective corrosion of the austenitic matrix causes localized embrittlement of the passive film with consequent pitting corrosion. The study accomplished allows concluding that the pitting potential was reduced with the presence of sigma phase and phases associated with it, and precisely the pulsed mode obtained outstanding corrosion resistance due to the absence of the sigma phase in its microstructure.