Made available in DSpace on 2016-12-08T17:19:19Z (GMT). No. of bitstreams: 1 Cleber P Fenili.pdf: 5079728 bytes, checksum: e3ab5832297ac591534e15390527a095 (MD5) Previous issue date: 2013-02-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This work is a study of the behavior of iron and nickel aluminides, since the high energy milling until the consolidation. Particle size and morphology of aluminides after milling and heat treatment were evaluated. A high energy milling with predetermined time and speed along with a defined stoichiometry of elemental powders were thus directed in order to obtain the intermetallic Fe3Al and Ni3Al. By obtaining the intermetallic was studied consolidation processes. The consolidation has great influence on the mechanical and microstructural properties of aluminides, motivating in recent years the study of consolidation as the density x porosity relationship. With the consolidation processes defined, which evaluates the influence of temperature, time, velocity, pressure and atmosphere. The sintering process, sintering and hot forming (S-HP) and hot pressing assisted field (FAHP) were used. The materials obtained after the consolidation processes were evaluated for density, hardness, formation of other phases and oxidation. These properties were evaluated by optical microscopy, scanning electron microscopy, vickers hardness, density, semiquantitative analysis (EDS) and X-ray diffraction. The results showed that the process FAHP is effective in consolidating the iron aluminides and nickel, for resulted in greater densification and therefore a good hardness confirming other studies using similar processes. The other cases in this study had less impressive results when compared to process FAHP, but compared to other references are considered suitable. / Neste trabalho foi realizado um estudo do comportamento dos aluminetos de ferro e níquel, desde a moagem de alta energia até a consolidação. Avaliou-se o tamanho das partículas e morfologia dos aluminetos após a moagem e tratamento térmico. A moagem de alta energia com tempo e velocidade pré determinados juntamente com uma estequiometria dos pós elementares definidos, foram assim direcionados com o intuito de obter os intermetálicos Fe3Al e Ni3Al. Com a obtenção dos intermetálicos estudou-se os processos de consolidação. A consolidação possui grande influência nas propriedades mecânicas e microestruturais dos aluminetos, motivando nos últimos anos o estudo dos processos de consolidação quanto a densidade x porosidade. Com os processos de consolidação definidos, avaliou-se a influência da temperatura, tempo, velocidade, atmosfera e pressão de compactação. Foram utilizados os processos de sinterização, sinterização e conformação a quente (S-HP) e prensagem a quente assistida por campo (FAHP). Os materiais obtidos após os processos de consolidação foram avaliados quanto a densidade, dureza, formação de outras fases e oxidação. Estas propriedades foram avaliadas através das metalografias mediante microscopia óptica, microscopia eletrônica de varredura, microdureza vickers, densidade, análise semiquantitativa (EDS) e difratometria de raios-X. Os resultados mostraram que o processo FAHP é eficaz na consolidação dos aluminetos de ferro e níquel, pois resultou em maior densificação e, por conseguinte uma boa dureza comparando com outros estudos utilizando processos parecidos. Os outros processos deste estudo obtiveram resultados menos expressivos quando comparados ao processo FAHP, porém comparados a outras referências são considerados adequados.

Made available in DSpace on 2016-12-08T17:19:32Z (GMT). No. of bitstreams: 1 1 Caderno_Zero_e_Introducao.pdf: 124923 bytes, checksum: 98c6d8b2bbb09c47a9216bc181431401 (MD5) Previous issue date: 2008-07-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The objective of this assignment is the synthesis of Ni3Al and Fe3Al, though the high energy milling. Intermetallic compounds are ordinate alloys, usually consisted of two elements characterized by the order of long reach they exhibit, that is caused by the strong connection among the different atoms when compared to the same atoms in the system. Some of the intermetallic compounds, specially those ones based on aluminum and silicium, have the attractive combinations of low density, high resistance and good resistance to corrosion and oxidation. The samples were obtained in attrition mill varying the milling time to a same relation ball/powder. The powders were submitted to thermal treatment for the final formation of the intermetallics. The structural characterization was accomplished through the diffraction of X-rays and electronic microscopy. The obtained results show the viability to obtain several systems of intermetallic compounds. / Esse trabalho tem por objetivo a síntese de sistemas intermetálicos de Ni3A1 e i, através da técnica de moagem de alta energia. Compostos intermetálicos são ligas ordenadas, normalmente consistidas de dois elementos sendo caracterizados pela ordem de o alcance que exibem, que é causada pela forte ligação entre os átomos diferentes quando comparados aos átomos iguais no sistema. Alguns dos compostos intermetálicos, especialmente aqueles baseados em alumínio e silício, têm as atrativas combinações de a densidade, alta resistência e boa resistência à corrosão e oxidação. As amostras obtidas em moinho atritor do tipo horizontal, variando o tempo de moagem para relação bolas/pó. Os pós foram submetidos a tratamento térmico para a final dos intermetálicos. A caracterização estrutural foi realizada através de de raios-X e microscopia eletrônica. Os resultados obtidos demonstram a ~ de obter diversos sistemas de compostos intermetálicos.

Made available in DSpace on 2015-03-03T15:15:26Z (GMT). No. of bitstreams: 1 BrunoFA_DISSERT.pdf: 1242758 bytes, checksum: 3fd41c76d37384c7bc0008cfd31e4a64 (MD5) Previous issue date: 2011-08-05 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / The calcium ferrite (Ca2Fe2O5) has a perovskite-type structure with oxygen deficiency and is used as a chemical catalyst. With the advent of nanoscience and nanotechnology, methods of preparation, physical and chemical characterizations, and the technological applications of nanoparticles have attracted great scientific interest. Calcium nanostructured ferrites were produced via high-energy milling, with subsequent heat treatment. The milling products were characterized by X-ray diffraction, magnetization and M?ssbauer spectroscopy. Samples of the type Ca2Fe2O5 were obtained from the CaCO3 and Fe2O3 powder precursors, which were mixed stoichiometrically and milled for 10h and thermally treated at 700?C, 900?C and 1100?C. The M?ssbauer spectra of the treated samples were adjusted three subespectros: calcium ferrite (octahedral and tetrahedral sites) and a paramagnetic component, related to very small particles of calcium ferrite, which are in a superparamagnetic state. For samples beats in an atmosphere of methyl alcohol, there is a significant increase in area associated with the paramagnetic component. Hysteresis curves obtained are characteristic of a weak ferromagnetic-like material / A ferrita de c?lcio (Ca2Fe2O5) possui uma estrutura do tipo perovskita com defici?ncia de oxig?nio e ? utilizada como catalisador qu?mico. Com o advento da nanoci?ncia e da nanotecnologia, os m?todos de prepara??o, as caracteriza??es f?sicas e qu?micas, e as aplica??es tecnol?gicas de nanopart?culas t?m despertado grande interesse cient?fico. Ferritas de c?lcio nanoestruturadas foram produzidas via moagem de alta-energia, com subsequente tratamento t?rmico. Os produtos da moagem foram caracterizados por difra??o de raios X, magnetiza??o e espectroscopia M?ssbauer. Amostras do tipo Ca2Fe2O5 foram obtidas a partir dos p?s-precursores Fe2O3 e CaCO3, os quais foram estequiometricamente misturados e mo?dos por 10h e tratados termicamente a 700 C, 900 C e 1100 C. Os espectros M?ssbauer das amostras tratadas foram ajustados com tr?s subespectros que correspondem ? ferrita de c?lcio (s?tios octaedrais e tetraedrais) e a uma componente paramagn?tica, relacionada com part?culas muito pequenas da ferrita de c?lcio, as quais est?o em estado superparamagn?tico. Para as amostras batidas em atmosfera de ?lcool met?lico, observa-se um aumento significativo da ?rea associada ? componente paramagn?tica. As curvas de histerese obtidas s?o caracter?sticas de um material antiferromagn?tico com uma fraca componente ferromagn?tica.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2015-11-18T12:11:41Z No. of bitstreams: 1 WellingtonCantanhedeDosSantos_DISSERT.pdf: 28481348 bytes, checksum: 2d5163f73607a4e015bf9536232e933b (MD5) / Approved for entry into archive by Elisangela Moura (lilaalves@gmail.com) on 2015-11-18T15:01:11Z (GMT) No. of bitstreams: 1 WellingtonCantanhedeDosSantos_DISSERT.pdf: 28481348 bytes, checksum: 2d5163f73607a4e015bf9536232e933b (MD5) / Made available in DSpace on 2015-11-18T15:01:11Z (GMT). No. of bitstreams: 1 WellingtonCantanhedeDosSantos_DISSERT.pdf: 28481348 bytes, checksum: 2d5163f73607a4e015bf9536232e933b (MD5) Previous issue date: 2014-03-14 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / No presente trabalho foram sintetizados comp?sitos, a partir da moagem de altaenergia dos precursores hidroxiapatita - HAp (Ca10(PO4)6(OH)2) e ferro met?lico (?-Fe),com o intuito de serem utilizados em hipertermia magn?tica no tratamento do c?ncer. Osprodutos da moagem foram caracterizados por difratometria de raios X (DRX),microscopia eletr?nica de varredura (MEV), espectroscopia de energia dispersiva (EDS),medidas de magnetiza??o em fun??o do campo aplicado e medidas de temperatura emfun??o do campo alternado. Os DRX das amostras batidas de HAp/Fe revelaram somente apresen?a dos precursores. O MEV mostrou aglomerados com formatos irregulares. Ascurvas de magnetiza??o obtidas apresentam casos t?picos de comportamentoferromagn?tico fraco. Para as amostras batidas e submetidas a tratamento t?rmico asseguintes fases foram identificadas: HAp (Ca10(PO4)6(OH)2) , hematita (Fe2O3) e ferrofosfato tric?lcio, FeTCP, Ca19Fe2 (PO4)14. Analisando os resultados de M x H, verificou-seuma redu??o na magnetiza??o de satura??o, tendo em vista que o Fe foi incorporado ?HAp. As curvas de histerese, obtidas a 300 K, s?o caracter?sticas de amostras que possuemmais de uma fase. Em 77 K, o comportamento da curva de histerese ? influenciado pelapresen?a da hematita que ? antiferromagn?tica. J? em T = 4,2K, ? observado umcomportamento ferromagn?tico fraco. Al?m disso, verifica-se o efeito de ?exchange bias?.Os resultados obtidos das medidas de temperatura em fun??o do campo alternado s?opromissores para aplica??es em hipertermia magn?tica e outras aplica??es biom?dicas. / In this work, composites were prepared using high energy mechanical milling from the precursors hydroxyapatite - HAp (Ca10(PO4)6(OH)2) and metallic iron ( -Fe ). The main goal here is to study composites in order to employ them in magnetic hyperthermia for cancer therapy. The produced samples were characterized by X-ray di raction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), magnetization curves as a function of applied eld (MxH), and nally measurements of magnetic hyperthermia. The XRD patterns of the milled samples HAp/Fe revealed only the presence of precursor materials. The SEM showed clusters with irregular shapes. The magnetization curves indicated typical cases of weak ferromagnetic behavior. For samples submitted to grinding and annealing, the identi ed phases were: HAp (Ca10(PO4)6(OH)2), hematite (Fe2O3) and Calcium Iron Phosphate (Ca9Fe(PO4)7). Analyzing the results of MxH, there was a reduction of the saturation magnetization, given that the Fe was incorporated into HAp. Hysteresis curves obtained at 300 K are characteristics of samples possessing over a phase. At 77 K, the behavior of the hysteresis curve is in uenced by the presence of hematite, which is antiferromagnetic. Already at T = 4.2 K, it is observed a weak ferromagnetic behavior. Furthermore, there is the e ect of exchange bias. Regarding the magnetic hyperthermia, the results of temperature measurements as a function of the alternating eld are promising for applications in magnetic hyperthermia and other biomedical applications.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-01-14T18:59:50Z No. of bitstreams: 1 TatianePotiguaraOliveira_DISSERT.pdf: 4152176 bytes, checksum: 173f9461ab0652eaed0cc9d6f2283f24 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-01-15T20:11:56Z (GMT) No. of bitstreams: 1 TatianePotiguaraOliveira_DISSERT.pdf: 4152176 bytes, checksum: 173f9461ab0652eaed0cc9d6f2283f24 (MD5) / Made available in DSpace on 2016-01-15T20:11:56Z (GMT). No. of bitstreams: 1 TatianePotiguaraOliveira_DISSERT.pdf: 4152176 bytes, checksum: 173f9461ab0652eaed0cc9d6f2283f24 (MD5) Previous issue date: 2014-08-01 / O comp?sito Al2O3-Cu alia a fase cer?mica da alumina, que ? extremamente dura e resistente, por?m muito fr?gil, ? fase met?lica do cobre de alta ductilidade e elevada tenacidade ? fratura. Tais caracter?sticas fazem desse material um forte candidato para aplica??o como ferramenta de corte. P?s comp?sitos Al2O3-Cu nanocristalinos e de alta homogeneidade podem ser produzidos por moagem de alta energia, assim como estruturas densas e de melhores propriedades mec?nicas podem ser obtidas por sinteriza??o com fase l?quida. Este trabalho investiga o efeito da moagem de alta energia na dispers?o das fases Al2O3 e Cu, bem como a influ?ncia do teor de Cu na forma??o das part?culas comp?sitas Al2O3-Cu. Um moinho planet?rio Pulverisatte 7 de alta energia foi usado para efetuar os experimentos de moagem. P?s de Al2O3 e Cu na propor??o de 5, 10 e 15% em massa de Cu foram colocados para moer em um recipiente com bolas de metal duro e ?lcool et?lico. Uma raz?o em massa de p? para bolas de 1:5 foi utilizada. Todos os p?s foram mo?dos at? 100 horas, e amostras de p?s foram coletadas ap?s 2, 10, 20, 50 e 70 horas de moagem. Compactos de p?s comp?sitos com forma cil?ndrica de 8 mm de di?metro foram prensados em matriz uniaxial e sinterizados em forno resistivo a 1200, 1300 e 1350 oC por 60 minutos e sob uma atmosfera de arg?nio e hidrog?nio. A taxa de aquecimento usada foi de 10 oC/min. Os p?s e as estruturas dos corpos sinterizados foram caracterizados por DRX, MEV e EDS. An?lises de TG, DSC e granulometria tamb?m foram usadas para caracterizar os p?s mo?dos, assim como, a dilatometria foi empregada para observar a contra??o dos corpos sinterizados. A densidade dos corpos verdes e sinterizados foi medida usando o m?todo geom?trico (massa/volume). Medidas de microdureza vickers com carga de 500 g durante 10 s foram efetuadas nas estruturas sinterizados. Os comp?sitos Al2O3?Cu com 5% de cobre alcan?aram densidade de 61% da densidade te?rica, e uma dureza de 129 HV quando sinterizados a 1300 oC por 1h. Diferentemente, menores densidades (59 e 51% da densidade te?rica) e durezas (110 e 105 HV) foram alcan?adas quando o teor de cobre aumento para 10 e 15%. / The Cu-Al2O3 composite ceramic combines the phase of alumina, which is extremely hard and durable, yet very brittle, to metallic copper phase high ductility and high fracture toughness. These characteristics make this material a strong candidate for use as a cutting tool. Al2O3-Cu composite powders nanocrystalline and high homogeneity can be produced by high energy milling, as well as dense and better mechanical structures can be obtained by liquid phase sintering. This work investigates the effect of high-energy milling the dispersion phase Al2O3, Cu, and the influence of the content of Cu in the formation of Cu-Al2O3 composite particles. A planetary mill Pulverisatte 7 high energy was used to perform the experiments grinding. Al2O3 powder and Cu in the proportion of 5, 10 and 15% by weight of Cu were placed in a container for grinding with balls of hard metal and ethyl alcohol. A mass ratio of balls to powder of 1:5 was used. All powders were milled to 100 hours, and powder samples were collected after 2, 10, 20, 50 and 70 hours of grinding. Composite powders with compact cylindrical shape of 8 mm diameter were pressed and sintered in uniaxial matrix resistive furnace to 1200, 1300 to 1350 ?C for 60 minutes under an atmosphere of argon and hydrogen. The heating rate used was 10?C/min. The powders and structures of the sintered bodies were characterized by XRD, SEM and EDS. Analysis TG, DSC and particle size were also used to characterize the milled powders, as well as dilatometry was used to observe the contraction of the sintered bodies. The density of the green and sintered bodies was measured using the geometric method (mass / volume). Vickers microhardness with a load of 500 g for 10 s were performed on sintered structures. The Cu-Al2O3 composite with 5% copper density reached 61% of theoretical density and a hardness of 129 HV when sintered at 1300 ? C for 1h. In contrast, lower densities (59 and 51% of the theoretical density) and hardness (110 HV and 105) were achieved when the copper content increases to 10 and 15%.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-03-22T00:17:59Z No. of bitstreams: 1 GilbertoMelchiors_TESE.pdf: 68131058 bytes, checksum: 5c5b863430fd078b972416d9cc3742d6 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-03-22T21:40:15Z (GMT) No. of bitstreams: 1 GilbertoMelchiors_TESE.pdf: 68131058 bytes, checksum: 5c5b863430fd078b972416d9cc3742d6 (MD5) / Made available in DSpace on 2016-03-22T21:40:15Z (GMT). No. of bitstreams: 1 GilbertoMelchiors_TESE.pdf: 68131058 bytes, checksum: 5c5b863430fd078b972416d9cc3742d6 (MD5) Previous issue date: 2015-03-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / As pseudoligas Nb-Cu apresentam-se como potenciais substitutas ?s ligas de um sistema conhecido e j? aplicado comercialmente, como as de W-Cu, usadas em aplica??es como dissipadores de calor, contatos el?tricos e bobinas para gera??o de altos campos magn?ticos. Por tratar-se de um sistema imisc?vel, onde h? insolubilidade m?tua e baixa molhabilidade do Cu l?quido na superf?cie do Nb, a rota de processamento empregada neste trabalho foi a da Metalurgia do P?. Duas composi??es de Nb foram utilizadas, com adi??es de 10% e 20% em peso de Cu, e tempos de 20, 30 e 40 horas, para a moagem de alta energia dos p?s de partida. A evolu??o da moagem dos p?s ? apresentada atrav?s de diversas t?cnicas de caracteriza??o, como a particulometria por difra??o a LASER, DRX, MEV, EDS, DSC, dilatometria, MET e an?lise qu?mica. Ap?s a moagem, partes das cargas de p?s foram submetidas ao tratamento t?rmico de recozimento. O processo empregado para a consolida??o das amostras foi a compacta??o a quente, a qual foi aplicada tanto em algumas amostras de p?s mo?dos, quanto nos p?s recozidos. Tratamentos t?rmicos posteriores foram realizados nas amostras, nas temperaturas de 1000?C (em fase s?lida) e 1100?C (em fase l?quida do Cu). Todos os conjuntos de amostras consolidadas e tamb?m os dois conjuntos das tratadas termicamente foram analisados por DRX, MEV, EDS, densidade e microdureza Vickers. Paralelamente, outras amostras de p?s de Nb com 10% e 20% em peso de Cu obtidas por simples mistura mec?nica, foram consolidadas, tratadas termicamente e caracterizadas com as mesmas t?cnicas aplicadas nas demais, e os resultados foram comparados entre eles. Apesar da dificuldade de consolida??o e densifica??o das duas pseudoligas do sistema Nb-Cu deste estudo, na rota que passa pela MAE, foram obtidas amostras com densidades em torno de 90% da densidade te?rica. E, na rota de processamento das amostras que foram apenas misturadas, os valores chegaram at? 97%. Por isso, nesse trabalho, tamb?m s?o enfatizados os processos que tornaram poss?veis os resultados encontrados. / The Nb-Cu pseudoalloys present themselves as potential substitutes for the alloys from a well known system and already commercially applied, as the W-Cu alloys, used in applications such as heat sinks, electrical contacts and coils for the generation of high magnetic fields. Because it is an immiscible system, where there is mutual insolubility and low wettability of the liquid Cu on the Nb surface, the processing route used in this work was the Powder Metallurgy. Two Nb alloys were used, with additions of 10% and 20% in weight of Cu, and times of 20, 30 and 40 hours for the high energy milling of the starting powders. The milling evolution of the powders is presented through the characterization techniques, such as the LASER diffraction for particle size, XRD, SEM, EDS, DSC, dilatometry, TEM and chemical analysis. After the milling, portions of the loads were submitted to the annealing heat treatment. The process used for the samples consolidation was the hot pressing, which has been applied both on some milled powders samples, as on the annealed powders. Subsequent heat treatments were performed in the samples at temperatures of 1000?C (solid phase) and 1100?C (in the Cu liquid phase). All sets of consolidated samples, and also the two sets of the heat treated, were analyzed by XRD, SEM, EDS, density and Vickers microhardness. Moreover, other Nb powder samples with 10% and 20% in weight of Cu obtained by simple mechanical mixing, were consolidated, thermally treated and characterized with the same techniques applied to the others, and the results were compared among themselves. Despite the difficulty of consolidation and densification of the two pseudoalloys of the Nb-Cu system of this study, on the route that passes through the HEM, samples were obtained with densities around 90% of the theoretical density. And, on the processing route of which were only mixed, the values reached up to 97%. Therefore, in this work are also emphasized the processes that made possible these results.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-07-22T14:59:52Z No. of bitstreams: 1 HeytorVitorSouzaBezerraDeAzevedo_DISSERT.pdf: 4226943 bytes, checksum: 879f905d96e12f6e15faa6de0fec4be5 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-07-26T22:08:45Z (GMT) No. of bitstreams: 1 HeytorVitorSouzaBezerraDeAzevedo_DISSERT.pdf: 4226943 bytes, checksum: 879f905d96e12f6e15faa6de0fec4be5 (MD5) / Made available in DSpace on 2016-07-26T22:08:45Z (GMT). No. of bitstreams: 1 HeytorVitorSouzaBezerraDeAzevedo_DISSERT.pdf: 4226943 bytes, checksum: 879f905d96e12f6e15faa6de0fec4be5 (MD5) Previous issue date: 2016-01-29 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Comp?sitos ? base de alumina (Al2O3), carbeto de tungst?nio (WC) e cobalto (Co) apresentam propriedades espec?ficas como baixa densidade, alta resist?ncia ? oxida??o, alto ponto de fus?o e elevada in?rcia qu?mica. Esse comp?sito revela ser um material promissor para ser aplicado em diversos campos da engenharia. Este trabalho tem como objetivo avaliar algumas propriedades mec?nicas durante a confec??o e, ap?s a sinteriza??o do comp?sito (Al2O3 - WC - Co). P?s comp?sitos com a composi??o de 80%.p de Al2O3, 18%.p de WC e 2%.p de Co foram processados pela rota de moagem de alta energia (MAE), em moinho planet?rio por 50 horas, bem como por mistura manual em um recipiente de vidro, seguindo a mesma propor??o em peso. Amostras foram coletadas (2, 10, 20, 30, 40 e 50 horas) durante o processo de moagem. Em seguida, os p?s foram prensados no formato de amostra circular com di?metro de 5 mm em uma prensa uniaxial com press?es de 200 e 400 MPa. A sinteriza??o ocorreu de duas maneiras: a primeira sinteriza??o via fase s?lida foi realizada ? 1300 ?C e ? 1126 ?C durante 1h com taxa de aquecimento de 10?C/min em forno resistivo sob atmosfera de arg?nio as press?es de compacta??o utilizadas foram de 200 e 400 MPa, a segunda sinteriza??o foi realizada em dilat?metro via fase s?lida ? 1300 ?C com press?o de compacta??o de 200 MPa, tamb?m foi realizada em dilat?metro outra sinteriza??o, desta vez por fase l?quida ? 1550 ?C com press?es de compacta??o de 200 e 400 MPa, obedecendo os mesmos par?metros utilizados no forno resistivo. As mat?rias-primas foram caracterizadas por difra??o de raios X - (DRX), fluoresc?ncia de raios X - (FRX), microscopia eletr?nica de varredura (MEV), espectroscopia por dispers?o de energia (EDS) e particulometria a laser. As amostras sinterizadas foram submetidas a ensaios de microdureza. Os resultados mostraram que a moagem de alta energia atingiu os objetivos quanto ao tamanho de part?cula e a densifica??o do comp?sito. Entretanto, a microdureza n?o alcan?ou resultados significativos, isso ? um ind?cio que o comp?sito possui baixa tenacidade ? fratura. / Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 ? WC ? Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 ?C for 1 hour with a heating rate of 10 ?C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 ?C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 ?C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X ? ray diffraction (XRD), X ? ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-01-12T14:20:00Z No. of bitstreams: 1 RodolfoAlbuquerqueBuarqueDeAssuncao_DISSERT.pdf: 3341925 bytes, checksum: 95332904ffdde1cc83db64f825ee63fe (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-01-18T14:22:16Z (GMT) No. of bitstreams: 1 RodolfoAlbuquerqueBuarqueDeAssuncao_DISSERT.pdf: 3341925 bytes, checksum: 95332904ffdde1cc83db64f825ee63fe (MD5) / Made available in DSpace on 2017-01-18T14:22:16Z (GMT). No. of bitstreams: 1 RodolfoAlbuquerqueBuarqueDeAssuncao_DISSERT.pdf: 3341925 bytes, checksum: 95332904ffdde1cc83db64f825ee63fe (MD5) Previous issue date: 2016-06-30 / O comp?sito Mo-Cu ? muito usado como material para contatos el?tricos e dissipadores de calor devido ?s excelentes propriedades do cobre de condutividade t?rmica e el?trica e boa trabalhabilidade, aliada ? alta resist?ncia a solda e eros?o por arco el?trico do molibd?nio. No primeiro caso, formas bastante simples s?o exigidas e a infiltra??o de cobre l?quido em um esqueleto de molibd?nio pr?-sinterizado ? a t?cnica de consolida??o normalmente utilizada. Diferentemente, geometrias mais complexas e densidades iguais ou pr?ximas da te?rica s?o necess?rias para aplica??o como dissipadores de calor. A metalurgia do p? atrav?s das t?cnicas de prepara??o de p?s com processamento por moagem de alta energia, compacta??o ou moldagem de p? por inje??o e sinteriza??o ? uma rota bastante vi?vel para produ??o desses componentes. Entretanto, a baixa solubilidade entre cobre e molibd?nio dificulta a obten??o de densidade igual ou pr?xima da densidade te?rica. Este trabalho investiga a obten??o do comp?sito Mo-27,82%?Cu preparado por moagem de alta energia e mistura mec?nica dos p?s de cobre e heptamolibdato de am?nio (HMA) de f?rmula qu?mica (NH4)6Mo7O24 .4H2O, decomposto e reduzido por H2, antes e durante a sinteriza??o, evidenciando duas rotas de fabrica??o diferentes para o material. A influ?ncia da press?o de compacta??o na densifica??o e microestrutura do comp?sito Mo-27,82%?Cu tamb?m foi investigada. Para isto, os p?s mo?dos por 50 horas foram prensados a 200, 400 e 600 MPa. Para se entender o efeito da temperatura na densidade e microestrutura do comp?sito Mo-27,82%?Cu, amostras foram sinterizadas a 1000, 1100 e 1200 oC. Os corpos prensados a 200 e 400 MPa e sinterizados a 1200 oC alcan?aram a maior densidade entre as amostras produzidas, no valor de 94?0,4 % da densidade te?rica. Por?m, aqueles que foram decompostos e reduzidos durante a sinteriza??o apresentaram trincas de fabrica??o. J? os corpos sinterizados a 1100 oC atingiram o maior valor de microdureza (571,70?78,82 HV), apesar de uma baixa densidade em rela??o a te?rica (79,17?1,78%). / The Mo-Cu composite is a material used for electrical contact and heat sinks due its excellent properties of thermal and electrical conductivity and cooper good workability allied to its great resistance welding and electrical arc erosion of molybdenum. In the first case, simple shapes are required and the infiltration of the pre-sintered molybdenum skeleton with liquid copper is the technique of consolidation normally used. On the second case, more complex geometries and a density near or equal the theoretical density are required for the application as heat sink. The powder metallurgy is a very viable route for the production of these components, through the techniques of powder preparation processed by mechanical alloying, compaction or casting. However, the low dissolution of one component in the other and the liquid copper high contact angle on the molybdenum phase difficult the obtainment of a density near or equal the theoretical density. This research investigates the obtainment of the Mo-27,82%?Cu composite prepared by mechanical alloying and mechanical mix of the copper powders and ammonium heptamolybdate (HMA) of chemical formula (NH4)6Mo7O24 .4H2O, decomposed and reduced by ?2 before and during the sintering, showing two different fabrication routes for the material. The compaction pressure influence at the densification and microstructure of the Mo-27,82%?Cu composite were also investigated. For this, the powder milled for 50 hours and the mixed powder were pressed at 200, 400 and 600 MPa. In order to understand the temperature effect at the density and microstructure were sintered at 1000, 1100 and 1200 ?C. The bodies pressed at 200 and 400 MPa and sintered at 1200?C reached 94?0,4 % of the theoretical density. However, those which were decomposed and reduced during sintering showed manufacturing cracks. On the other hand, the bodies sintered at 1100 ?C reached the highest microhardness value (571,70?78,82 HV), despite a low theory density (79.17 ? 1.78%).

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-07-03T13:37:23Z No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-07-06T16:06:51Z (GMT) No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) / Made available in DSpace on 2017-07-06T16:06:51Z (GMT). No. of bitstreams: 1 JoseLeonaldoDeSouza_DISSERT.pdf: 2323627 bytes, checksum: 0b82f3fcf1052c6990e64f3b99a70364 (MD5) Previous issue date: 2016-05-30 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Os materiais cer?micos, tais como a alumina (Al2O3) e o cobalto (Co), apresentam caracteristicas relevantes para aplica??o como ferramentas de corte, e dentre estas se destacam a elevada dureza e o alto ponto de fus?o. No entanto, a sua aplica??o ? limitada pela sua baixa tenacidade e baixa resist?ncia mec?nica. Desta forma, a fim de aumentar a tenacidade do material, mantendo-se as elevadas propriedades mec?nicas, alguns metais, como por exemplo, o cobalto (Co), t?m sido usados na tentativa de se produzir um material mais tenaz. Neste trabalho, estudouse o efeito da moagem de alta energia e da adi??o de (%p.) Co na densifica??o e microestrutura, assim como, nas propriedades mec?nicas do composto Al2O3-Co. Os p?s-particulados (Al2O3 e Co), com percentuais de 5 e 20%p. de cobalto, foram mo?dos em um moinho planet?rio durante 50 horas, e amostras de p?s foram coletadas nos intervalos de 2, 10, 15, 20, 30,40 e 50 horas. Os p?s mo?dos foram caracterizados por difra??o de raios-X (DRX), an?lises particulom?tricas, microscopia eletr?nica de varredura (MEV); e compactados em uma matriz cil?ndrica sob uma press?o uniaxial de 100 MPa. Posteriormente, os compactados a verde foram sinterizados em um forno resistivo nas temperaturas de 1200 a 1500 ?C, por 60 minutos, sob uma atmosfera de arg?nio com taxa de aquecimento de 10?C/min. Os corpos de prova sinterizados foram caracterizados por DRX, MEV e energia dispersiva (EDS). A densidade foi medida usando o m?todo geom?trico (massa/volume), e os melhores valores foram obtidos para as amostras sinterizadas a temperatura de 1500 ?C, sendo a densidade relativa igual a 78 %, seguido das sinterizadas a temperaturas de 1350?C e 1300?C, que apresentaram as respectivas densidades 68 %, e 62 %. / Ceramic materials, such as alumina (Al2O3) and cobalt (Co), present characteristics like high hardness and the high melting point for application as cutting tools. However, its application is limited because of its low toughness and low mechanical strength. Thus, in order to increase the toughness and maintaining the high mechanical properties, some metals such as cobalt (Co) have been used. In this work, the effect of the high energy milling and different amount of Co on densification, microstructure and mechanical properties of the Al2O3-Co compound were studied. The particulate powders (Al2O3 and Co), with 5 and 20 wt% of cobalt, were milled in a planetary milling for 50 hours, and powder mixture samples were collected at the intervals of 2, 10, 15, 20, 30, 40 and 50 hours. The milled powders were characterized by X-ray diffraction (XRD), particulometric analyzes, scanning electron microscopy (SEM); And compacted in a cylindrical matrix under a uniaxial pressure of 100 MPa. Subsequently, green compacts were sintered in a resistance furnace at 1200 to 1500 ?C with holding time of 60 minutes under an argon atmosphere with a heating rate of 10 ?C/min. The sintered samples were characterized by XRD, SEM and EDS. Density was measured using the geometric method (mass/volume), and the best values were obtained for the samples sintered at 1500 ?C with relative density of 78% compared with sample sintering at 1350 and 1300 ?C which presented relative densities of 68% and 62% respectively.

O emprego de resíduos da indústria como materiais alternativos na Engenharia vem sendo tópico recorrente em pesquisas de desenvolvimento de novos materiais, devido a uma maior consciência da opinião pública quanto ao impacto ambiental oriundo da produção industrial. Buscando colaborar com esta discussão, esta pesquisa procurou inserir dois resíduos (cinza volante e cal de carbureto), gerados na região metropolitana de Porto Alegre, como alternativa de solução em Engenharia. Analisando-se a microestrutura da cinza volante, observa-se que ela é formada por esferas ocas e plerosferas (esferas ocas preenchidas por esferas menores). Foi estudado o ganho de resistência da mistura promovido pela moagem da cinza volante em um moinho de bolas cerâmicas, visando uma potencialização da reatividade do material. A fim de possibilitar a utilização destes resíduos, é necessário um estudo do seu comportamento mecânico decorrente da cimentação proporcionada pela mistura e compactação destes materiais. A presente pesquisa busca fornecer subsídios para que seja possível determinar o seu comportamento, através do uso da relação porosidade (η)/teor volumétrico de cal (LV) obtidas a partir da identificação e quantificação das variáveis mais importantes no controle da resistência da mistura dos dois resíduos, com e sem o processo de moagem da cinza, levando a formulação de equações para previsão da resistência à compressão simples do material cimentado para cinza volante com diferentes tempos de moagem e cura acelerada. Para isso, foram realizados ensaios de compressão simples em corpos de prova com 5, 10 e 15% de cal, com peso específico aparente seco de 11, 12 e 13 kN/m3, curados por 7 dias, com umidade de 18% para os tempos de moagem 0, 2 e 6h nas temperaturas 23 e 40°C, e 0 e 6h a 60°C. Os resultados apontam que o aumento do teor de cal gerou ganhos de resistência para as maiores temperaturas de cura; a diminuição da porosidade proporcionou um ganho de resistência para todas as combinações; o aumento da temperatura foi importante no ganho de resistência entre 23oC e 40oC; a moagem da cinza por 2h promoveu ganhos significativos de resistência em relação à não moída, porém, para 6h de moagem os ganhos não foram significativos para as temperaturas de cura de 23oC e 60oC. A relação η/LV, ajustada por um expoente [η/(Lv)0,07], mostrou-se adequada na formulação de equações na previsão da resistência do material cimentado para todas as temperaturas e tempos de moagem estudados. Além disso, a existência de relações únicas e distintas no controle da resistência à compressão simples em função da porosidade, teor volumétrico de cal, temperatura de cura e tempo de moagem, mostraram-se úteis para formulações de dosagem. Os resultados foram submetidos à análise de variância que comprovou que todos os fatores controláveis escolhidos para o experimento são significativos, assim como todas suas interações. / The use of industry by-products as alternative materials in Engineering has been a recurring topic of research in development of new materials, mainly, due to a larger public conscience regarding the environmental impact of industrial production of waste. Aiming to contribute on this discussion, this research sought to introduce two by-products (fly ash and carbide lime), produced on the metropolitan area of Porto Alegre, as an alternative Engineering solution. Analyzing the microstructure of the fly ash, it is observed that it is composed by void spheres and plerospheres (void spheres filed with smaller ones). Having that in mind, it was studied the admix strength gain promoted by the grinding of de fly ash on a ceramic ball mill, aiming an enhancement of the reactivity of the material. In order to enable the use of these byproducts, it is necessary the study of its mechanical behavior due to the cementation provided by the mixture and compaction of these materials. The current research seeks to provide subsides in order to determine its behavior, through the use of the ratio porosity (η)/ volumetric lime content (LV), obtained from the identification and quantification of the most important variables on the control of the strength of the admixes of both by-products, with or without the process of fly ash grinding. This means, the formulation of equations for the simple compressive strength forecast of the cemented material for the fly ash with different grinding times and accelerated curing temperature. In order to do so, it were realized simple compression tests with 5, 10 and 15% of lime, with a specific dry unit weight of 11, 12 and 13 kN/m3, cured for 7 days, with water content of 18% for the grinding times of 0, 2 and 6h to the curing temperatures of 23 and 40oC, and 0 and 6h to 60oC. The results show that, the increase of lime content provided strength gains for the higher temperatures; the decrease of porosity generated strength gain to all the combinations; the increase in curing temperature was important on the strength gain between 23oC and 40oC; the grinding of fly ash for 2h promoted significant strength gains when compared to the not ground samples, however, for 6h of grinding the strength gain wasn’t significant for the 23oC and 60oC curing temperatures. The η/LV ratio, adjusted by an exponent [η/(LV)0,07], presented itself adequate for the formulation of the equations for the forecast of the strength gain of the cemented material to all the studied temperatures and grinding times. Besides that, the existence of unique and distinct relationships on the control of the simple compression strength depending on the porosity, volumetric lime content, curing temperature and grinding time, have been shown useful for the dosage formulation. The results were submitted to variance analysis, which demonstrated that all the factors chosen on the experiment were significant, as all their interactions.