Alkyd emulsions are currently being developed for coating applications. These paints combine the technical advantages of alkyd polymers, which give coatings of a high gloss finish, with the environmental and health benefits of solvent-free systems. Nonetheless, the drying and film formation of these systems involve several steps, none of which is well understood yet. These include creaming or sedimentation, evaporation of the continuous water phase, coalescence of the alkyd droplets, a possible phase-inversion, and the oxidative cross-linking of the alkyd polymer to form a hard coating. In this thesis. Magnetic Resonance Microscopy is used to investigate the film formation of alkyd emulsion coatings. As the process is complex, studies on a different range of emulsions and related systems are performed to gain further insight into the different steps involved. A combination of Liquid State Microscopy, diffusometry and broad line imaging (Stray Field Magnetic Resonance Imaging) is employed, and it is shown that this combination provides results extremely rich in information. First, a study of the cream layer and the creaming dynamics of model bulk oil-in-water emulsions containing different concentrations of thickener is presented. The experimental data are compared to the predictions of a numerical model, and evidence is gained that the presence of the thickener induces flocculation according to a depletion mechanism. Then, the water evaporation from alkyd emulsion droplets is investigated and the water concentration across the droplet is modelled according to an original model based on lateral diffusion of water. There is no evidence from spectroscopy and diffusometry for phase-inversion during the drying of alkyd emulsion coatings. Finally the cross-linking of alkyds containing driers is found to be non-uniform across the film thickness.

Submitted by Maria Medeiros (maria.dilva1@ufcg.edu.br) on 2018-07-09T13:22:22Z No. of bitstreams: 1 NEYBER FÁDIO CAVALCANTI NASCIMENTO - DISSERTAÇÃO (PPGCEMat) 2016.pdf: 1783822 bytes, checksum: 978c857fd44cc5a5c4f6d54a35a5e8a3 (MD5) / Made available in DSpace on 2018-07-09T13:22:22Z (GMT). No. of bitstreams: 1 NEYBER FÁDIO CAVALCANTI NASCIMENTO - DISSERTAÇÃO (PPGCEMat) 2016.pdf: 1783822 bytes, checksum: 978c857fd44cc5a5c4f6d54a35a5e8a3 (MD5) Previous issue date: 2016-02-27 / Capes / Devido a suas propriedades reológicas, uma grande quantidade de bentonitas são empregadas como aditivos para tintas como agentes espessantes, estabilizadores e antisedimentantes. Este trabalho teve por objetivo avaliar os efeitos da ativação individual e conjunta por Na2CO3 e MgO nas propriedades reológicas de argilas bentoníticas policatiônicas do estado da Paraíba visando o uso das mesmas como agentes espessantes de tintas de base água.Foram utilizadas argilas bentoníticas policatiônicas do estado da Paraíba das ocorrências de Boa Vista e Cubati, denominadas de Chocolate Boa Vista (CH BV) e Chocolate Campos Novos (CH CN), respectivamente. A caracterização física, química e mineralógica das amostras foi realizada pelos seguintes métodos: análise granulométrica (AG), fluorescência de raios X (EDX), difração de raios X (DRX), capacidade de troca de cátions (CTC), área específica (AE), análise térmica diferencial (ATD) e análise termogravimétrica (ATG). Os percentuais dos aditivos Na2CO3 e MgO foram de 0,0%, 0,5%, 1,0%, 1,5%, 2,0%, 3,0% e 4,0% quando utilizados de forma individual e de 0,5%, 1,0%, 1,5% de MgOe 0,5%, 1,0%, 1,5% de Na2CO3 associados de modo que todas as combinações fossem analisadas.Os resultados obtidos foram comparados com as especificações API e ISO de bentonitas para uso em tintas base água. A ativação apenas com MgO não proporcionou maiores valores de viscosidade às suspensões bentoníticas estudadas. A ativação apenas com Na2CO3, na forma sólida, e com ambos aditivos aumentou a viscosidade das dispersões bentoníticas com argila CH BV e foram observados comportamentos reológicos do tipo pseudoplástico com tensão de escoamentoe tixotrópico. Verificou-se também que as argilasCH BV e CH CN, com ambos aditivos, apresentaram comportamentos pseudoplástico com tensão de escoamentoe tixotrópico. Conclui-se que as bentonitas CH BV e CH CN podem ser utilizadas como espessantes de tintas de base água. / Due to its rheological properties, a large amount of bentonites are used as additives for paints as thickeners, stabilizers and anti-settling. This study aimed to evaluate the effects of individual and joint activation Na2CO3 and MgO in the rheological properties of polycationic bentonite clays of the Paraíba state aimed at using them as thickeners for water-based paints. Polycationic clays were used bentonite state of Paraiba occurrences of Boa Vista and Cubati, called Chocolate Boa Vista (CH BV) and Chocolate Campos Novos (CH CN), respectively. The physical, chemical and mineralogical samples was performed by the following methods: Particle size analysis (GA), X-ray fluorescence XDE), X-ray diffraction (XRD), capacity of cation exchange (CEC), specific area (SA), differential thermal analysis (DTA) and thermal gravimetric analysis (TGA). The percentages of MgO and additives Na2CO3 were 0.0%, 0.5%, 1.0%, 1.5%, 2.0%, 3.0% and 4.0% when used individually, and 0.5%, 1.0%, 1.5% MgO and 0.5%, 1.0%, 1.5% Na2CO3 associated so that all combinations were analyzed. The results obtained were compared with API bentonite and ISO specifications for use in water based paints. Activation only with MgO did not provide higher viscosity values for bentonite suspensions studied. Activation only with Na2CO3, in solid form, and with both additives increased the viscosity of bentonite clay dispersions with CH BV and were observed rheological behavior of the pseudoplastic type with yield stress and thixotropic. It was also found that the clays CH BV and CH CN with both additives, presented pseudoplastic behavior with yield stress and thixotropic. It follows that the bentonite and CH CN CH BV can be used as thickeners in water based paints.

Made available in DSpace on 2014-10-09T12:25:36Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:46Z (GMT). No. of bitstreams: 1 06790.pdf: 5752105 bytes, checksum: 9b66a692f462ce07b2dd97fe9220e337 (MD5) / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Made available in DSpace on 2014-10-09T12:25:36Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:46Z (GMT). No. of bitstreams: 1 06790.pdf: 5752105 bytes, checksum: 9b66a692f462ce07b2dd97fe9220e337 (MD5) / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / Os primers sÃo tintas primÃrias que funcionam como fundo anticorrosivo quando aplicados sobre metais. As suas propriedades anticorrosivas devem-se os pigmentos usados na sua composiÃÃo, sendo os mais comuns o zarcÃo, o cromato de zinco, o Ãxido de ferro e o pà de zinco. As tintas à base de resina epoxÃdica sÃo bastanteutilizadas como primers, pois apÃs a cura estas tornam-se impermeÃveis e, quandosÃo associadas a pigmentos com propriedades anticorrosivas, aumentam a resistÃnciado substrato à corrosÃo. PelÃculas secas de tintas-primers formuladas com resinaepoxÃdica DGEBA (Ãter Diglicidil de Bisfenol A), reticuladas com umapoliaminoamida (Versamid 125), e com dois pigmentos anticorrosivos, um tÃxico (cromato de zinco) e outro nÃo-tÃxico (sÃlica trocadora de cÃlcio) foram estudadas atravÃs das tÃcnicas de termogravimetria (TG), infravermelho (FTIR) e microscopia eletrÃnica de varredura (MEV). AtravÃs de TG foram determinados parÃmetros cinÃticos, como a Energia de ativaÃÃo, tanto pelo mÃtodo de Ozawa-Wall-Flynn, quanto de Kissinger. Verificou-se que o mecanismo de degradaÃÃo das tintas epoxidÃcas à alterado na presenÃa dos pigmentos. A estabilidade termo-oxidativa do primer com cromato de zinco, baseada nos valores de IPDT, à menor do que a do primer com o pigmento silica cÃlcio. A imersÃo dos primers em Ãcido clorÃdrico, nas concentraÃÃes de 10-5 atà 6,0M, reduz a estabilidade tÃrmica, sendo o mais afetado aquele contendo cromato de zinco. Neste ocorre a formaÃÃo de poros, detectados pela MEV. O uso do pigmento anticorrosivo sÃlica cÃlcio apresenta, alÃm da vantagem da nÃo toxidade, maior estabilidade termo-oxidativa e maior resistÃncia a ambientes Ãcidos do que o pigmento cromato de zinco. / The primers are primary anticorrosive dyes, with anticorrosive property due to the presence of appropriate pigment. The most common used anticorrosive pigments are zarcÃo, zinc chromate, iron oxide and zinc powder. Paints based on epoxy resin are very used as primers, because their impermeability and, when associated with anticorrosive pigments, the increase in the resistance against corrosion. Films of paint-primers formulated with DGEBA epoxy resin (Diglycidyl Ether of Bisphenol A), crosslinked with polyaminoamida (Versamid 125) , and with two anticorrosive pigments, zinc chromate (toxic) and calcium silicate (not toxic), were studied by thermogravimetric analysis (TG), infrared spectroscopy (FTIR) and scanning electronic microscopy (SEM). Kinetic parameters, such as activation energy, were calculated by TG, using Ozawa-Wall-Flynn and Kissinger methods. Change in the mechanism of epoxy paint degradation was observed in the presence of the two pigments. Primer with calcium silicate was more thermally stable than that with zinc chromate, based on IPDT values. The immersion of primers films in hydrochloric acid in the concentrations range from 10-5 to 6,0 M led to a decrease in the thermal stability. The most affected primer was that with zinc chromate, in which porous was detected by SEM after the immersion in acid solution. The primer with calcium silicate has the advantage of being more thermally stable and more resistant to acid attack, in addition to its more important ecological property, the non toxicity.

Sais quaternários de amônio são amplamente usados como agentes antissépticos, desinfetantes, detergentes e preservantes. Além disso, sais quaternários de amônio são frequentemente utilizados como algicidas, sendo o cloreto de dodecil dimetil benzil amônio (Cloreto de benzalcônio) o mais efetivo contra estes microorganismos. No entanto sua aplicação como algicida de superfícies é limitada, devido a sua alta hidrofilicidade, ocasionando uma alta lixiviação deste composto quando a superfície é exposta à alta umidade e intempéries de clima tropical. Atualmente compostos como Diuron e S-Triazina são empregados como algicidas, considerados de baixa lixiviação. No entanto, altos níveis de concentração destes biocidas foram detectados em regiões costeiras evidenciando a lixiviação destes biocidas, quando utilizados em tintas para casco de navio. Assim surge a necessidade do desenvolvimento de um algicida para suprir as deficiências de lixiviação dos compostos empregados atualmente. Materiais como as argilas organofílicas são uma excelente alternativa, pois são altamente hidrofóbicas. Portanto sintetizou-se neste trabalho uma argila organofílica utilizando-se cloreto de benzalcônio, a qual foi utilizada em uma formulação de tinta imobiliária. O material foi caracterizado pelas técnicas de difração de Raios X e análise termogravimétrica. Um filme de tinta foi submetido a uma câmara de lixiviação, simulando a ação da chuva. Após a lixiviação o filme de tinta seguiu para testes microbiológicos, para verificar se a superfície ainda possui proteção microbiana. As algas testadas foram das espécies Phormidium cebenense, Trentepohlia odorata, Chlorella sp e Scenedesmus quadricauda colocadas num pool de algas. Através das análises de Difração de Raios X e termogravimétrica é possível determinar a estrutura e quantificar o teor cloreto de benzalcônio no material, respectivamente. Os testes microbiológicos e de lixiviação avaliaram a capacidade biocida assim como a resistência à intempérie do material. O novo composto sintetizado neste trabalho apresentou um alto potencial para uso como agente microbiano em tintas. / Quaternary ammonium compounds are widely used as antiseptic agents, disinfectants, detergents and preservatives. In addition, quaternary ammonium compounds are often used as algaecides, and dodecyl dimethyl benzyl ammonium chloride (benzalkonium chloride) is the most effective against these microorganisms. However benzalkonium chloride is not used as surface algaecide compound due its high hydrophilic, bring on high leaching of this compound when the surface is exposed to high humidity and severe weather from tropical climate. Currently, compounds such as diuron and s-triazine are used as microbial agent, considered low leaching. However diuron and s-triazine were detected in coastal regions in high levels concentration showing the leaching of these biocides when used in antifouling paints in ships. Considering these, it can be observed the necessity to develop a new algaecide to overcome the failings of leaching of the compounds used nowadays. Material as organoclay is an excellent alternative because they are highly hydrophobic. Therefore in this work was synthesized a new nanomaterial using benzalkonium chloride, which was applied in a house paint formulation. The material was characterized by the techniques of X-ray diffraction and thermogravimetric analysis. A film coating was placed in a leaching chamber, simulating the action of rain. After leaching the coating film was applied to microbiological tests to check if the surface still had microbial protection against the following algae species: Phormidium cebenense, Trentepohlia odorata, Chlorella sp and Scenedesmus quadricauda; placed in a pool of algae. It was possible to determine the structure and quantify the amount of benzalkonium chloride in the material through X-ray Diffraction and Thermogravimetric analysis, respectively. The biocide capabilities as well as the resistance to weathering of coating with the material were analyzed by microbiological and leaching test, respectively. The new compound developed in this study has a high potential to be used as microbial agent in paints.

O principal objetivo deste estudo foi avaliar a refletância e sua influência no comportamento térmico de tintas refletivas e tintas convencionais aplicadas em telhas de fibrocimento para cobertura de habitações brasileiras. Foram realizados ensaios em laboratório de determinação de cor e de brilho por medida instrumental e determinação da refletância por análise espectrofotométrica em películas. Para o estudo do comportamento térmico foram realizados ensaios de simulação em laboratório com corpos-de-prova expostos à radiação infravermelha emitida por lâmpadas e de exposição à radiação solar em campo através de protótipos com monitorização da temperatura durante as exposições. Os resultados dos ensaios de determinação de cor e de brilho mostraram que as pinturas refletivas e convencionais realmente apresentaram cores correspondentes. Os resultados de refletância mostraram que as pinturas refletivas apresentaram valores de refletância superiores em relação às tintas convencionais, o que foi comprovado pela temperatura medida nos ensaios de exposição à radiação infravermelha e radiação solar. A conclusão do estudo é que as tintas refletivas têm potencial para redução da temperatura superficial da telha de fibrocimento e que é necessária uma continuidade do estudo de durabilidade e do desempenho térmico de tintas refletivas coloridas. / The main purpose of this study was to investigate the effect of reflective colored paints and conventional colored paints applied on fiber cement corrugated roofing sheets, proving whether both type of paints can present different reflection characteristics in the infrared solar radiation and high thermal performance. Color and gloss were measured by instrumental methods and reflectivity (reflection coefficient) was measured using spectrophotometers equipped with integrating spheres in free paint films. In order to investigate the thermal performance of reflective and conventional paints, simulation tests were performed in laboratory by IR lamps using fiber cement specimens and in field by exposure solar radiation using prototypes with temperature monitoring. The results showed that the reflective paints present higher reflectivity and better thermal performance than the conventional paint, independently of the color. The results showed that the reflective paints present potential to reduce superficial temperature of fiber cement corrugated roofing sheets. It is necessary to continue the reflective colored paints study on durability and thermal performance by exposure tests.

O principal objetivo deste estudo foi avaliar a refletância e sua influência no comportamento térmico de tintas refletivas e tintas convencionais aplicadas em telhas de fibrocimento para cobertura de habitações brasileiras. Foram realizados ensaios em laboratório de determinação de cor e de brilho por medida instrumental e determinação da refletância por análise espectrofotométrica em películas. Para o estudo do comportamento térmico foram realizados ensaios de simulação em laboratório com corpos-de-prova expostos à radiação infravermelha emitida por lâmpadas e de exposição à radiação solar em campo através de protótipos com monitorização da temperatura durante as exposições. Os resultados dos ensaios de determinação de cor e de brilho mostraram que as pinturas refletivas e convencionais realmente apresentaram cores correspondentes. Os resultados de refletância mostraram que as pinturas refletivas apresentaram valores de refletância superiores em relação às tintas convencionais, o que foi comprovado pela temperatura medida nos ensaios de exposição à radiação infravermelha e radiação solar. A conclusão do estudo é que as tintas refletivas têm potencial para redução da temperatura superficial da telha de fibrocimento e que é necessária uma continuidade do estudo de durabilidade e do desempenho térmico de tintas refletivas coloridas. / The main purpose of this study was to investigate the effect of reflective colored paints and conventional colored paints applied on fiber cement corrugated roofing sheets, proving whether both type of paints can present different reflection characteristics in the infrared solar radiation and high thermal performance. Color and gloss were measured by instrumental methods and reflectivity (reflection coefficient) was measured using spectrophotometers equipped with integrating spheres in free paint films. In order to investigate the thermal performance of reflective and conventional paints, simulation tests were performed in laboratory by IR lamps using fiber cement specimens and in field by exposure solar radiation using prototypes with temperature monitoring. The results showed that the reflective paints present higher reflectivity and better thermal performance than the conventional paint, independently of the color. The results showed that the reflective paints present potential to reduce superficial temperature of fiber cement corrugated roofing sheets. It is necessary to continue the reflective colored paints study on durability and thermal performance by exposure tests.

Com a crescente demanda do mercado de tintas por produtos mais sustentáveis, toda a cadeia produtiva tem se movimentado para oferecer soluções neste âmbito. Para contemplar o pilar ambiental da sustentabilidade, a redução de Compostos Orgânicos Voláteis (VOC), de alquilfenol etoxilados (APEO) e a substituição de matérias-primas de origem fóssil por vegetal nas formulações de tintas são algumas das práticas em expansão neste setor. No presente estudo, os perfis de impactos ambientais de duas tintas imobiliárias base água foram comparados aplicando-se a metodologia de Avaliação do Ciclo de Vida (ACV) (ABNT NBR ISO 14040 e 14044). Primeiramente, foram desenvolvidas duas fórmulas genéricas não comerciais de tinta standard (ABNT NBR 15079): \"Tinta A\" com matérias-primas de uso convencional e \"Tinta B\" com algumas matérias-primas alternativas, que hipoteticamente contribuiriam com um melhor desempenho ambiental do produto final. Em seguida, ambas fórmulas foram reproduzidas em laboratório, as amostras das tintas foram submetidas a testes de desempenho técnico e com os dados obtidos determinou-se os fluxos de referência para cumprir a unidade funcional definida por cobrir 36 m2 de parede de alvenaria interior por um período mínimo de 4 anos (ABN NBR 15575-1). A ACV tem quatro fases: objetivo e definição do escopo, análise de inventário, avaliação do impacto ambiental e interpretação. Com os objetivos e escopo do estudo definidos, foi realizada uma abrangente coleta de dados, majoritariamente secundários, para possibilitar a Análise de Inventário (ICV). Posteriormente, o ciclo de vida das tintas foi modelado e analisado no software SimaPro 8.2 e na fase de Avaliação de Impactos do Ciclo de Vida (AICV) foi selecionado o método ReCiPe Midpoint (H) v.1.12. Para as sete categorias de impacto analisadas, a \"Tinta B\" apresentou perfil de impactos ambientais reduzido em relação a \"Tinta A\": Mudanças Climáticas (-18,6%), Formação de Oxidantes Fotoquímicos (-19%), Toxicidade Humana (-17,7%), Ecotoxicidade (-30,5%), Depleção de Recursos Fósseis (18,8%), Depleção de Recursos Minerais (-21,4%) e Depleção de Recursos Hídricos (-18,7%). Os resultados do estudo, reforçam a importância da ACV como uma ferramenta eficaz para mensurar o desempenho ambiental de tintas. No entanto, a falta de disponibilidade de dados primários dos processos de toda a cadeia produtiva de tintas dificulta a execução de estudos e compromete a precisão dos resultados. Destaca-se ainda, que a perspectiva do ciclo de vida de produtos e processos foi incluída como requisito da nova versão da norma ISO 14001, que é do interesse de toda a cadeia de valor, portanto, vale considerar a aplicação da ACV na indústria de tintas. / The demand for sustainable products in the paint market has been steadily growing and is pushing the whole production chain to offer solutions following this scenario. The reduction of Volatile Organic Compounds (VOC), alkylphenol ethoxylates (APEO) and the substitution of raw materials of fossil origin by vegetable in the formulations of paints are some of the practices increasing among this sector to meet the environmental sustainability pillar. In the present study, the environmental impact profiles of two water-based architectural paints were compared applying the Life Cycle Assessment (LCA) methodology (ABNT NBR ISO 14040 and 14044). Firstly, two generic non-commercial formulas of standard paint (ABNT NBR 15079) were developed: \"Paint-A\" with conventional raw materials and \"Paint- B\" containing some alternative raw materials, which would hypothetically contribute to a better environmental performance of the final product. Then both formulas were reproduced in the laboratory and the samples of the paints were submitted to technical performance tests. With the data obtained, the reference flows were determined to fulfill the functional unit defined by covering 36 m2 of interior masonry wall by a minimum period of 4 years (ABN NBR 15575-1). The LCA has four phases: goal and scope definition, inventory analysis, environmental impact assessment and interpretation. After goal and scope definition, a comprehensive data collection was carried to enable the Inventory Analysis (LCI). Afterwards, the life cycle of the paints was modeled and analyzed in the SimaPro 8.2 software and in the Life Cycle Impact Assessment (LCIA) phase the ReCiPe Midpoint (H) v.1.12 method was selected. Within seven impact categories analyzed, \"Paint-B\" presented a reduced environmental impact profile compared to \"Paint-A\": Climate Change (-18.6%), Photochemical Oxidants Formation (-19%), Human Toxicity (-18.5%), Ecotoxicity (-30.5%), Fossil Resources Depletion (18.8%), Mineral Resources Depletion (-21.4%) and Water Resources Depletion (-18.7%). The results of the study strengthen the importance of LCA as an effective tool for measuring the environmental performance of paints. However, the lack of availability of primary process data throughout the paint production chain makes it difficult to carry out studies and compromises the accuracy of the results. It is also relevant to highlight that the product and process lifecycle perspective was included as a requirement of the new version of the ISO 14001 standard, which is a matter of concern to the entire value chain, so it is worth considering the application of LCA in the paints industry.

O presente trabalho apresenta a caracterização química de tintas artísticas brasileiras. Diferente de outras matrizes, os materiais de arte fabricados no Brasil não apresentam informações na literatura que auxiliem em sua conservação e restauração. Amostras de tintas acrílicas e a óleo, nacionais e importadas, foram analisadas pelas técnicas espectroscópicas Raman e infravermelho por transformada de Fourier (FTIR), pirólise acoplada a cromatografia a gás e espectrometria de massas (Py-GC/MS) e microscopia eletrônica de varredura acoplada a espectrometria de fluorescência de raios X (SEM-EDS). Resultados de análise indicam que tintas acrílicas brasileiras são compostas por poliestireno (PS), diferentemente das importadas, compostas por polimetilmetacrilato (PMMA). Enquanto as tintas a óleo apresentam composição semelhante (óleo de linhaça), brasileiras e importadas. Duas pinturas do acervo da Pinacoteca do Estado de São Paulo foram selecionadas para um estudo de caso. As obras apresentam a formação de exsudatos em sua superfície, o que demanda a caracterização química como etapa anterior ao desenvolvimento de uma metodologia de restauração. A obra \"Mandala da saudade\", de Sara Goldman-Belz, é composta por tinta spray (alkyd) e a obra \"Três pessoas\", de Marina Saleme, por tinta a óleo. Os resultados de análise apresentam um primeiro passo no estabelecimento de um banco de dados de materiais artísticos fabricados no Brasil para fins de restauração e perícia criminal de obras de arte. / The current work presents the chemical characterization of Brazilian artistic paints. Differently from other matrices, art materials produced in Brazil lack for information in literature that help in their conservation and restoration. Acrylic and oil paint samples, Brazilian and imported, were analyzed by Raman and Fourier transform infrared (FTIR) spectroscopies, pyrolysis coupled with gas chromatography and mass spectrometry (Py-GC/MS) and scanning electron microscopy coupled with x-ray fluorescence spectrometry (SEM-EDS). Results indicate that Brazilian acrylic paints are composed of polystyrene (PS), differently from imported ones, composed of polymethyl methacrylate (PMMA). Whereas, oil paints present similar composition (linseed oil), Brazilian and imported. Two paintings from the collection of Pinacoteca do Estado de São Paulo were selected for a case study. Both works of art present formation of exudates on their surface, which demands chemical characterization as a previous step to the development of a restoration methodology. The painting \"Mandala da saudade\", by Sara Goldman-Belz, is composed of spray paint (alkyd) and the painting \"Três pessoas\", by Marina Saleme, is composed of oil paint. Results presented in this thesis are the first step towards the establishment of a database for artistic materials produced in Brazil for purposes of art restoration and forensic science.