Made available in DSpace on 2014-12-17T14:06:58Z (GMT). No. of bitstreams: 1 PollyannaTTBN_DISSERT.pdf: 3294347 bytes, checksum: 23d933599f7d6d6327054ef468580147 (MD5) Previous issue date: 2011-07-01 / The corrosive phenomenon on reinforced concrete structures is one of the most founded pathologies on the coastal area. With the objective to prevent the process development, or even, retard its beginning, it was studied the application of inorganic covering over concrete surfaces, after its cure, as well as, evaluate the efficiency of the covering applied on the concrete in reducing its porosity of concrete preventing the entrance of aggressive agents to preserve the integrity of the existing armor inside it, comparing the result obtained with the body-of-proof reference, that didn?t receive covering protection. On the concrete production it was used Portland Cement CP II 32, coarse aggregate, fine aggregate and water from the local distributive. Two types of covering were used, one resin based of silicon and solvent and other white cement based, selected sands and acrylic resin. The concrete mixture adopted was 1:1,5:2,5 (cement, fine aggregate, coarse aggregate) and 0.50 water/cement ratio. With the concrete on fresh state was made the experiment test to determinate the workability. On the hardened state was made the concrete resistance experiment, absorption of water and electrochemical experiments, through polarization curves. Also was held optical microscopy and Scanning Electron Microscopy experiments to analyze the layer of the covering applied to the concrete surface and the interface between the concrete and the layer. The obtained results shows that the covering applied to the concrete surface didn?t affect the resistance towards compression. On the absorption of water occurred a diminution of the percentage absorbed, improving the concrete development by making it more impermeable towards the entrance of aggressive agents. The electrochemical experiment results confirmed the water absorption results; the body-of-proof covered presented larger protection towards the development of corrosives process and retarded the evolution of the corrosive phenomenon / O fen?meno de corros?o em estruturas de concreto armado ? uma das patologias mais encontradas em ?reas litor?neas. Com o objetivo de impedir que o processo se desenvolva ou mesmo retardar o seu in?cio, estudou-se a aplica??o de revestimentos inorg?nicos sobre a superf?cie do concreto, ap?s sua cura, bem como, foi avaliado a efici?ncia dos revestimentos aplicados a superf?cie do concreto em reduzir a sua porosidade, impedindo a entrada dos agentes agressivos para preservar a integridade da armadura existente no seu interior, comparando o resultado obtido com corpos-de-prova refer?ncia, que n?o receberam nenhum revestimento de prote??o. Na produ??o do concreto utilizou-se o Cimento Portland CP II F 32, agregado gra?do, agregado mi?do e ?gua da concession?ria local. Como revestimentos foram utilizados dois tipos, um ? base de resina de silicone e solvente e o outro, ? base de cimento branco, areias selecionadas e resina acr?lica. O tra?o adotado para o estudo foi 1:1,5:2,5 (cimento, areia e brita) e rela??o a/c = 0,50. Com o concreto no estado fresco, realizou-se o ensaio de abatimento de tronco de cone para determina??o da trabalhabilidade. J? no estado endurecido, realizou-se o ensaio de resist?ncia ? compress?o, absor??o de ?gua e os ensaios eletroqu?micos, atrav?s de curvas de polariza??o. Tamb?m foram realizados ensaios de Microscopia ?ptica e Microscopia Eletr?nica de Varredura para an?lise da camada de revestimento aplicada ? superf?cie do concreto e a interface entre o concreto e a camada. Os resultados obtidos mostram que os revestimentos aplicados ? superf?cie do concreto n?o afetaram a resist?ncia ? compress?o. J? em rela??o ? absor??o de ?gua houve uma diminui??o do percentual absorvido, melhorando o desempenho do concreto por torn?-lo mais imperme?vel ? entrada dos agentes agressivos. Os resultados dos ensaios eletroqu?micos confirmaram o resultado do ensaio de absor??o de ?gua; os CP?s revestidos apresentaram uma maior prote??o ao desenvolvimento de processos corrosivos e retardaram a evolu??o do fen?meno de corros?o

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-06-23T20:18:47Z No. of bitstreams: 1 MarcosAndreCapitulinoDeBarrosFilho_DISSERT.pdf: 1391023 bytes, checksum: c9de84ee4fe7550a9fa173f8a04d4002 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-06-27T21:06:25Z (GMT) No. of bitstreams: 1 MarcosAndreCapitulinoDeBarrosFilho_DISSERT.pdf: 1391023 bytes, checksum: c9de84ee4fe7550a9fa173f8a04d4002 (MD5) / Made available in DSpace on 2016-06-27T21:06:25Z (GMT). No. of bitstreams: 1 MarcosAndreCapitulinoDeBarrosFilho_DISSERT.pdf: 1391023 bytes, checksum: c9de84ee4fe7550a9fa173f8a04d4002 (MD5) Previous issue date: 2015-12-14 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Apesar das in?meras vantagens advindas do uso da tecnologia de membranas filtrantes, algumas limita??es inerentes ao processo de incrusta??o tornam-se relevantes para sua aplicabilidade. O controle das condi??es operacionais consiste em importante ferramenta para mitigar o fouling e alcan?ar bons n?veis de efici?ncia. Nesse sentido, o objetivo deste trabalho foi investigar o efeito da press?o transmembrana e da vaz?o de concentrado no desempenho da ultrafiltra??o, aplicada ao p?s-tratamento de esgoto sanit?rio. O processo foi avaliado e otimizado variando-se a press?o (0,5 e 1,5 bar) e a vaz?o de concentrado (300 e 600 L/h), por meio de um planejamento fatorial 22, a fim de investigar os efeitos no fluxo permeado e na qualidade dos efluentes gerados, em cada condi??o operacional. Avaliaram-se os seguintes indicadores de qualidade para os permeados: pH, Condutividade El?trica, S?lidos Suspensos Totais, Turbidez, C?lcio e Demanda Qu?mica de Oxig?nio (DQO). Em todos os ensaios, observou-se diminui??o acentuada do fluxo permeado nos instantes iniciais, seguida de uma queda lenta que se prolongou at? atingir um patamar relativamente constante por volta dos 120 minutos de filtra??o. O aumento da press?o resultou em maior fluxo permeado inicial, por?m a queda do fluxo com o tempo foi maior para os ensaios realizados a press?o mais elevada, evidenciando um processo de incrusta??o mais pronunciado. Por outro lado, o aumento da vaz?o de concentrado resultou em queda mais lenta de fluxo permeado com o tempo de filtra??o. Com rela??o a qualidade dos permeados, a press?o transmembrana de 0,5 bar foi a que permitiu melhores resultados, sendo confirmado estatisticamente, por meio do teste da ANOVA two-way com medidas repetidas, efeito significativo da press?o sobre a turbidez do permeado. A vaz?o de concentrado, por sua vez, n?o apresentou influ?ncia significativa sobre nenhum dos par?metros de qualidade. Dessa forma, considerando que o efeito do aumento da vaz?o de concentrado no retardamento do fouling n?o resultou em melhoria significativa do fluxo permeado, conclui-se que a condi??o operacional otimizada para a gera??o de permeados com maior grau de pureza, associado a gera??o de um menor volume de res?duo, consiste naquela em que se aplica uma press?o transmembrana baixa associada a uma vaz?o menor de concentrado. / Despite the numerous advantages resulting from the use of membrane filters technology, intrinsic limitations fouling process become relevant to its applicability. The control of operating conditions is an important tool to mitigate fouling and achieve good levels of efficiency. In this sense, the objective of this study was to investigate the effect of transmembrane pressure and concentrate flow in the performance of ultrafiltration, applied to the post-treatment of domestic sewage. The process was evaluated and optimized by varying the pressure (0.5 and 1.5 bar) and the concentrate flow (300 and 600 L/h), using a 22 factorial design, in order to investigate the effects on the permeate flow and quality of effluents generated at each operating condition. We evaluated the following quality indicators for permeate: pH, electrical conductivity, total suspended solids, turbidity, calcium and Chemical Oxygen Demand (COD). In all tests, we observed marked reduction in the permeate flux at the early stages, followed by a slow decline that lasted until it reaches a relatively constant level, around 120 minutes of filtration. The increased pressure resulted in a higher initial permeate flux, but the decrease of the flow with time is greater for tests at higher pressure, indicating a more pronounced fouling process. On the other hand, increasing the concentrate flow resulted in a slower decline in permeate flux with the filtration time. Regarding the quality of permeate, the transmembrane pressure of 0,5 bar was the one that allowed better results, and was statistically confirmed through the two-way ANOVA test with repeated measures, significant effect of pressure on the turbidity of the permeate. The concentrate flow, in turn, showed no significant influence on any of the quality parameters. Thus, we conclude that, from an economic and environmental point of view, it is more interesting to operate ultrafiltration membrane system with a lower concentrate flow associated with a low transmembrane pressure, since under these conditions will produce less waste, and the permeate will present lower concentrations of the analyzed constituent, especially lower turbidity.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-08-09T22:51:25Z No. of bitstreams: 1 EmanueleDaSilvaRodriguesMontalvao_TESE.pdf: 1580309 bytes, checksum: 39bf0d8e4a7d3087d516e4317b43d692 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-08-10T23:27:44Z (GMT) No. of bitstreams: 1 EmanueleDaSilvaRodriguesMontalvao_TESE.pdf: 1580309 bytes, checksum: 39bf0d8e4a7d3087d516e4317b43d692 (MD5) / Made available in DSpace on 2016-08-10T23:27:44Z (GMT). No. of bitstreams: 1 EmanueleDaSilvaRodriguesMontalvao_TESE.pdf: 1580309 bytes, checksum: 39bf0d8e4a7d3087d516e4317b43d692 (MD5) Previous issue date: 2016-01-26 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico (CNPq) / Este trabalho tem como objetivo propor um novo modelo de metasuperf?cie com c?lula b?sica simplificada, capaz de converter sinais linearmente polarizados gerados por um arranjo de antenas planar em sinais circularmente polarizados, para a faixa de frequ?ncia ISM (2,45 GHz), apresentando uma boa largura de banda de perda de retorno e de raz?o axial. Para poder estudar o comportamento da estrutura proposta, a metasuperf?cie ? acoplada a tr?s estruturas diferentes. Primeiro s?o feitos testes iniciais com a metasuperf?cie acoplada a uma antena de microfita em sua configura??o simples. Em seguida a metasuperf?cie ? utilizada acoplada a um arranjo com dois elementos do tipo patch. E posteriormente ela ? acoplada a um arranjo otimizado, que utiliza um toco em sua alimenta??o principal, para obter um melhor casamento de imped?ncias. As estruturas s?o analisadas numericamente atrav?s do Ansoft HFSS? e para validar esses resultados, as estruturas s?o caracterizadas experimentalmente. S?o apresentadas as caracter?sticas de transmiss?o simuladas e medidas. Os resultados experimentais mostram uma boa concord?ncia com os resultados simulados. A estrutura aqui proposta apresenta a vantagem de atender as caracter?sticas desejadas, com uma geometria simples de ser constru?da e utilizando um substrato de baixo custo (FR-4). / This work aims to propose a new model of metasurface with simplified basic cell, able to convert linearly polarized signals generated by planar antenna array in circularly polarized signals, for the ISM frequency band (2.45 GHz), with good bandwidth of return loss and axial ratio. To study the behavior of the proposed structure, the metasurface is coupled to three different structures. First, initial tests are made with the metasurface coupled to a microstrip antenna in its simple configuration. Then the metasurface is coupled to an array with two elements of patch type. And later it is coupled to an optimized array, that uses a stub in its main feed, to get a better impedance matching. The structures are analyzed numerically through Ansoft HFSS?, and to validate these results, the structures are characterized experimentally. The characteristics of transmissions simulated and measures are presented. A good agreement between simulated and measured results was obtained. The structure proposed here has the advantage of meeting the desired characteristics, with a simple geometry to be built using a low-cost substrate (FR-4).

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-12-29T16:36:10Z No. of bitstreams: 1 AugustoCesarPereiraDaSilvaMontalvao_TESE.pdf: 3356285 bytes, checksum: 91694fd2667b473c4c31ff9be48f2171 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-01-02T18:07:35Z (GMT) No. of bitstreams: 1 AugustoCesarPereiraDaSilvaMontalvao_TESE.pdf: 3356285 bytes, checksum: 91694fd2667b473c4c31ff9be48f2171 (MD5) / Made available in DSpace on 2017-01-02T18:07:35Z (GMT). No. of bitstreams: 1 AugustoCesarPereiraDaSilvaMontalvao_TESE.pdf: 3356285 bytes, checksum: 91694fd2667b473c4c31ff9be48f2171 (MD5) Previous issue date: 2016-07-04 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Este trabalho tem como objetivo propor uma nova estrutura capaz de converter sinais linearmente polarizados gerados por uma antena de microfita em sinais circularmente polarizados, para duas bandas de opera??o (2,45 GHz e 5,8 GHz), para aplica??o em leitores RFID port?teis, usando duas metasuperf?cies miniaturizadas. Para poder estudar o comportamento da estrutura proposta, s?o utilizados tr?s layouts diferentes. Primeiro s?o feitos testes iniciais de simula??o, utilizando a primeira metasuperf?cie acoplada ? antena. Em seguida, a antena ? testada acoplada ? segunda metasuperf?cie. E posteriormente a antena ? acoplada ?s duas metasuperf?cies. As estruturas s?o analisadas numericamente atrav?s do Ansoft HFSS? e para validar esses resultados, as estruturas s?o caracterizadas experimentalmente. S?o apresentadas as caracter?sticas de transmiss?o simuladas e medidas. Os resultados experimentais mostram uma boa concord?ncia com os resultados simulados. A estrutura aqui proposta apresenta a vantagem de atender ?s caracter?sticas desejadas nas duas bandas de interesse, conseguindo obter excelentes valores de largura de banda de perda de retorno, bem como de raz?o axial, sendo uma estrutura simples de ser constru?da e com baixo custo. / This work aims to propose a new structure able to convert signals linearly polarized generated by a microstrip antenna for circularly polarized signals at two operating bands (2.45 GHz and 5.8 GHz), for use in portable RFID readers, using two miniaturized metasurfaces. In order to study the behavior of the proposed structure, three different layouts are used. First initial simulation tests are made, using the first metasurface coupled to the antenna. Then, the antenna is tested coupled to the second metasurface. Posteriorly the antenna is coupled to the two metasurfaces. The structures are analyzed numerically through ANSYS HFSS?, and to validate these results, the structures are characterized experimentally. The characteristics of transmissions simulated and measures are presented. A good agreement between simulated and measured results was obtained. The structure proposed here has the advantage to meet desired characteristics in two bands of interest, obtaining excellent values of return loss wideband, as well as the axial ratio, being a simple structure to be constructed and with low cost.

Made available in DSpace on 2014-12-17T15:41:49Z (GMT). No. of bitstreams: 1 DanyelleMA_DISSERT.pdf: 886887 bytes, checksum: bdfc465050e9656b4d629363ccd362a0 (MD5) Previous issue date: 2010-07-29 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Corrosion inhibitors in solution are utilized to minimize processes from corrosion in steel. Of the present dissertation was evaluated the efficiency by inhibition from the surfactant saponified coconut oil (OCS) in the carbon steel 1020 through in linear polarization electrochemistry technique, well as, studied the process from adsorption through from the isotherms from Langmuir, Frumkin and Temkin. The corrosion current was determined through in Tafel extrapolation from the curves in the polarization, and then, was calculated the efficiency in the inhibitor to each concentration and temperature. Were studied four concentrations (12,5 ppm, 25 ppm, 50 ppm, and 75 ppm) in the inhibitor OCS and one in the NaCl salt (10.000 ppm) in six temperatures (301 K, 308 K, 313 K, 318 K, 323 K, and 328 K) in triplicate. By the results obtained observed that the technique applied can evaluated with rapidity and efficiency corrosion inhibitors. In relation to the isotherms, the than best appropriated was the in Langmuir and in the concentrations studied, the that obtained the best efficiency was the concentration of 75 ppm / Inibidores de corros?o em solu??o s?o utilizados para minimizar processos de corros?o em a?o. Na presente disserta??o foi avaliada a efici?ncia de inibi??o do tensoativo ?leo de coco saponificado (OCS) no a?o carbono 1020, atrav?s da t?cnica eletroqu?mica polariza??o linear, bem como, estudado o processo de adsor??o atrav?s das isotermas de Langmuir, Frumkin e Temkin. A corrente de corros?o foi determinada atrav?s da extrapola??o de Tafel nas curvas de polariza??o e, ent?o, foi calculada a efici?ncia do inibidor para cada concentra??o e temperatura. Foram estudadas quatro concentra??es (12,5, 25,0, 50,0 e 75,0 ppm) do inibidor OCS e uma do sal NaCl (10.000 ppm) em seis temperaturas (301, 308, 313, 318, 323 e 328 K) em triplicata. Pelos resultados obtidos, observou-se que a t?cnica utilizada pode avaliar com rapidez e efici?ncia inibidores de corros?o. Em rela??o ?s isotermas, a que melhor se adequou foi a de Langmuir e dentre as concentra??es estudadas a que obteve a melhor efici?ncia foi ? concentra??o de 75 ppm

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-03-17T19:09:01Z No. of bitstreams: 1 EdwinLuizeFerreiraBarreto_TESE.pdf: 4396827 bytes, checksum: 67d20b4064513759f618b9148557fcdd (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-03-17T21:47:01Z (GMT) No. of bitstreams: 1 EdwinLuizeFerreiraBarreto_TESE.pdf: 4396827 bytes, checksum: 67d20b4064513759f618b9148557fcdd (MD5) / Made available in DSpace on 2017-03-17T21:47:01Z (GMT). No. of bitstreams: 1 EdwinLuizeFerreiraBarreto_TESE.pdf: 4396827 bytes, checksum: 67d20b4064513759f618b9148557fcdd (MD5) Previous issue date: 2016-11-18 / Este trabalho tem como objetivo principal realizar o estudo e an?lise de diferentes antenas planares de microfita, atrav?s do emprego de geometrias fractais no patch ressoador e da remo??o parcial do plano de terra com acoplamento. Recentes estudos mostram que as varia??es nas formas geom?tricas do patch da antena e do plano de terra produzem mudan?as na distribui??o da densidade de corrente da estrutura e consequentemente nos modos ressonantes e na polariza??o da antena. No desenvolvimento desta tese, apresenta-se uma nova antena fractal que utiliza a t?cnica de inser??o de fendas e aberturas de forma fractal no plano de terra e tamb?m descontinuidades no transformador ? de onda na linha de transmiss?o a fim de aumentar a largura de banda e alcan?ar comportamentos espec?ficos em aplica??es de banda de frequ?ncia. Emprega-se o substrato FR-4 com dimens?es de 85,0 x 85,0 x 1,57 mm?. Al?m disso, usam-se diferentes modos de casamento de imped?ncia na linha de alimenta??o de antena como CPW (Coplanar Wave Guide) e altera??es da largura da linha de transmiss?o, a fim de obter varia??o na distribui??o de corrente e, consequentemente, na largura de banda de resposta por imped?ncia para S11 ? -10dB para banda C (3.9 GHz - 6,2 GHz) e banda S (2,0 GHz - 4,0 GHz). Uma an?lise comparativa de desempenho para a linha de microfita e CPW foi realizada, obtendo-se para alguns casos antenas circularmente polarizadas. Boa concord?ncia foi obtida entre os resultados medidos e simulados. / This work has as main objective to carry out the study and analysis of different planar microstrip antenna, by employing fractal geometry in the resonator patch and partial removal of the ground plane with coupling. Recent studies show that variations in geometric shapes of the antenna and the ground plane generate changes in current density distribution of the planar structure and consequently the resonant modes and antenna polarization. In developing this thesis presents a new fractal antenna using the technique of insertion slots and fractal shaped defects (gaps) in the ground plane and discontinuities with ? wavelength transformer in the transmission line in order to increase the bandwidth and inserting in the feed line to reach specific behaviors in three frequency bandwidth applications. We used the FR-4 substrate with dimensions of 85.0 x 85.0 x 1.57 mm?. In addition, we used different modes of impedance matching in line antenna feed as CPW (Coplanar Wave Guide), to change the width of the transmission line in order to obtain a variation in the current distribution and hence the response bandwidth impedance to S11 ? -10dB for C band (3.9 GHz - 6.2 GHz) and S band (2.0 GHz - 4.0 GHz). A comparative analysis of cases with microstrip line and CPW was made, applications in this frequency range require preferably circularly polarized antennas. Good agreement was obtained between measured and simulated results.

Made available in DSpace on 2014-12-17T15:41:43Z (GMT). No. of bitstreams: 1 ThiagoRR.pdf: 1895833 bytes, checksum: 59d0cd6d03df2b5c8165e3ae0bf39a80 (MD5) Previous issue date: 2008-04-25 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / An interesting development in surfactants science and technology is their application as corrosion inhibitors, since they act as protective films over anodic and cathodic surfaces. This work aims to investigate the efficiency of saponified coconut oil (SCO) as corrosion inhibitor and of microemulsified system (SCO + butanol + kerosene oil + distilled water), in saline medium, using an adapted instrumented cell, via techniques involving linear polarization resistance (LPR) and mass loss coupons (MLC). For this, curves of efficiency versus SCO concentration (ranging between 0 and 75 ppm) have been constructed. According to the obtained results, the following efficiency levels were reached with OCS: 98% at a 75 ppm concentration via the LPR method and 95% at 75 ppm via the MLC method. The microemulsified system, for a concentration of 15 ppm of SCO, obtained maximum inhibition of 97% (LPR) and 93% (MLC). These data indicate that it is possible to optimize the use of SCO in similar applications. Previous works have demonstrated that maximal efficiencies below 90% are attained, typically 65% as free molecules and 77% in microemulsified medium, via the LPR method in a different type of cell. Therefore, it can be concluded that the adapted instrumented cell (in those used methods) showed to be an important tool in this kind of study and the SCO was shown effective in the inhibition of the metal / Tensoativos v?m sendo alvo de interesse como inibidores de corros?o, pois funcionam como pel?culas protetoras sobre ?reas an?dicas e cat?dicas. Este trabalho teve como objetivo avaliar a efici?ncia de inibi??o ? corros?o do tensoativo ?leo de coco saponificado (OCS) e do sistema icroemulsionado (OCS + butanol + querosene + ?gua destilada), em meio salino, utilizando-se uma c?lula instrumentada adaptada. A efic?cia do OCS foi avaliada utilizando-se os m?todos de resist?ncia de polariza??o linear (LPR) e cupons de perda de massa (CPM), tendo sido constru?das curvas de efici?ncia versus concentra??o de OCS (variando de 0 a 75 ppm). De acordo com os resultados obtidos, verificou-se que este tensoativo apresenta a seguinte ordem de efici?ncia de inibi??o ? corros?o: para uma concentra??o de 75 ppm, 98% pelo m?todo LPR e 95% pelo m?todo CPM. O sistema microemulsionado, para uma concentra??o de 15 ppm de OCS, obteve inibi??o m?xima de 97% (LPR) e 93% (CPM). Atrav?s deste trabalho foi poss?vel otimizar o uso do tensoativo OCS, que em trabalhos anteriores mostrou efic?cia m?xima inferior a 90% (63% na sua forma livre e 77% na sua forma microemulsionada, pelo m?todo LPR, em um outro tipo de c?lula). Conclusivamente, pode-se dizer que a c?lula instrumentada adaptada (nos m?todos utilizados) provou ser uma ferramenta importante neste tipo de estudo e o OCS mostrou-se efetivo na inibi??o do metal

Submitted by Sandra Pereira (srpereira@ufrrj.br) on 2017-03-21T13:39:54Z No. of bitstreams: 1 2015 - Arthur Valbon Rodrigues.pdf: 2339821 bytes, checksum: 867f44f511f5a52dfdcf023619e589a9 (MD5) / Made available in DSpace on 2017-03-21T13:39:54Z (GMT). No. of bitstreams: 1 2015 - Arthur Valbon Rodrigues.pdf: 2339821 bytes, checksum: 867f44f511f5a52dfdcf023619e589a9 (MD5) Previous issue date: 2015-08-04 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / In this work six asymmetric thyourea, derived from benzylamine and phenethylamine, were synthesized by reaction of p-substituted phenyl isothiocyanates in the presence of benzylamine and phenethylamine in toluene as solvent by irradiation in ultrasonic bath, featuring the first report in the literature of the adoption of this method for such molecules. The compounds were obtained in high purity, requiring only one recrystallization from hexane/dichloromethane. Yields were very satisfactory, ranging from 89 to 98%. The compounds were characterized by spectroscopic techniques such as 1H, 13C Nuclear Magnetic Resonance and IR. The synthesized compounds were evaluated by electrochemical potentiodynamic polarization techniques, Electrochemical Impedance Spectroscopy and Linear Polarization Resistance as inhibitors to the corrosion AISI 1020 carbon steel in 1M HCl media. Molecular modeling was used for better visualization of the thiourea structures and to correlate theoretical parameters such as the energy of the symmetrical frontier orbital, Mulliken charge on the sulfur atom and dipole moment with the experimental results for corrosion efficiency. In general, all compounds showed corrosion inhibition efficiency with characteristics of mixed inhibitors with anodic trend, however compounds with nitro substituent showed less efficiency, a fact that may be related to their electrons withdrawing potential, which consequently decreases the electron density at the possible center of chemical adsorption, the sulfur atom. However, compounds which showed no substituent and those that contain electron donating group (OCH3) stood out as inhibitors, highlighting N- (p-methoxyphenyl) -N'-phenetylthiourea, which showed 95% efficiency corrosion inhibition, from Electrochemical Impedance spectroscopy. Thus, the asymmetric thiourea benzyl and phenethyl-substituted, especially methoxy-substituted phenyl, can be considered as promising corrosion inhibitors for carbon steel in acid. / Nesse trabalho de disserta??o foram sintetizadas seis tioureias assim?tricas, derivadas da benzilamina e fenetilamina. A obten??o ocorreu atrav?s da rea??o dos isotiocianatos de fenila p-substituidos na presen?a da benzilamina e fenetilamina em tolueno como solvente atrav?s de irradia??o em banho de ultrassom, sendo o primeiro relato na literatura dessa metodologia para tais mol?culas. Os compostos foram obtidos em alto grau de pureza, sendo necess?ria apenas uma recristaliza??o em hexano/diclorometano. Os rendimentos foram muitos satisfat?rios, variando de 89 ? 98%. Os compostos foram caracterizados por t?cnicas espectrosc?picas como Resson?ncia Magn?tica Nuclear 1H,13C e Infravermelho. Os compostos sintetizados foram avaliados atrav?s das t?cnicas eletroqu?micas de Polariza??o Potenciodin?mica, Espectroscopia de Imped?ncia Eletroqu?mica e Resist?ncia a Polariza??o Linear quanto ? a??o como inibidores de corros?o frente a a?o carbono AISI 1020 em HCl 1 mol.L-1. A Modelagem Molecular foi utilizada para melhor visualiza??o das estruturas das tioureias e correlacionar os par?metros te?ricos como a energia dos orbitais de fronteiras sim?tricos, carga de Mulliken no ?tomo de enxofre e momento dipolar com os resultados experimentais da efici?ncia anticorrosiva. De forma geral, todos apresentaram efici?ncia de inibi??o ? corros?o com caracter?sticas de inibidores mistos com tend?ncia an?dica, por?m os compostos com substituinte nitro apresentaram menor efici?ncia, fato esse que pode estar relacionado ao seu poder retirador de el?trons, que consequentemente, diminui a densidade eletr?nica no poss?vel centro de adsor??o qu?mica, o enxofre. Por?m, os compostos que n?o apresentaram substituintes e os que cont?m grupo doador de el?trons (OCH3) se destacaram como inibidores, dando destaque a N-(p-metoxi-fenil)-N?-fenetiltioureia, que apresentou efici?ncia de 95% de inibi??o da corros?o, pela t?cnica de Espectroscopia de Imped?ncia Eletroqu?mica. Assim, as tioureias assim?tricas benzil e fenetil-substitu?das, especialmente met?xi-fenil substitu?das, podem ser consideradas como promissores agentes inibidores da corros?o para o a?o-carbono em meio ?cido.

Submitted by Jorge Silva (jorgelmsilva@ufrrj.br) on 2018-08-29T19:26:49Z No. of bitstreams: 1 2017 - Cristiane Frauches dos Santos.pdf: 7660831 bytes, checksum: d9f6418f111957d4be1789ee9411cc8f (MD5) / Made available in DSpace on 2018-08-29T19:26:49Z (GMT). No. of bitstreams: 1 2017 - Cristiane Frauches dos Santos.pdf: 7660831 bytes, checksum: d9f6418f111957d4be1789ee9411cc8f (MD5) Previous issue date: 2017-09-25 / CAPES / CNPq / FAPERJ / Petrobr?s / Corrosion is one of the serious problems faced in industrial processes, generating enormous financial losses. Several techniques are used to prevent or remedy corrosion in the different materials it affects. Among them, the use of organic or inorganic inhibitors has been widely used. Thus, in this thesis were synthesized 34 heterocyclic compounds, 18 chlorides of 1,3,4-thiadiazolium-2-phenylamines, (11 unpublished), and the other 16 compounds belonging to the class of mesoionic 1,3,4-triazolium -2-thiolate, (15 unpublished), with the objective of evaluating its efficiency as inhibitors of corrosion in acidic corrosion. Derivatives of the class 1,3,4-thiadiazolium-2-phenylamines were obtained with satisfactory purity and yields in the range of 42-96% and, in the class of 1,3,4-triazolium-2-thiolates in 20 -97%. All compounds were characterized by IR, 1H and 13C NMR spectroscopies. The theoretical study was conducted using the SPARTAN-PRO program in the semi-empirical method with the Hamiltonian AM1, to determine its structural and electronic properties of 1,3,4-thiadiazolium-2-phenylamines that could contribute to the efficiency of inhibition of corrosion. The compounds of 1,3,4-thiadiazolium-2-phenylamine class were tested against corrosion of AISI 1020 carbon steel in 0.5 mol L-1HCl and in 0.5 mol L-1 H2SO4. For this evaluation, the electrochemical techniques of Potenciodynamic Polarization (PP), Resistance to Linear Polarization (RPL) and Electrochemical Impedance Spectroscopy (EIS) were used. The results showed significant percentages of corrosion inhibition in both acidic solutions, reaching the rate of up to 95% efficiency for the compound 4-phenyl-5-(3'-methoxy-phenyl)-1,3,4-thiadiazolium-2-phenylamine chloride in the concentration of 3.5x10-4 mol L-1 for the HCl solution, and 99% efficiency for the 2'-chloro and 2'-fluorosubstituted compounds in the concentration of3.5x10-4 mol L-1 for the H2SO4 solution. In addition to the electrochemical techniques, the gravimetric technique was used, which presented 99% of anticorrosive efficiency for the 2'-trifluoromethyl-substituted 1,3,4-thiadiazolium-2-phenylamine derivative, showed the best inhibitory effect in HCl solution. However, the 2'-trifluoromethyl-substituted 1,3,4-triazolium-2-thiol derivative showed less corrosion efficiency than its corresponding isomer. The methodologies used to evaluate the corrosion activity (PP, RPL and EIE), including the theoretical evaluation by molecular modeling, indicated the mesoionic chloridrates as efficient mixed corrosion inhibitors. / S?ntese e avalia??o da atividade anticorrosiva de cloretos de 1,3,4-tiadiaz?lio-2-fenilaminas e 1,3,4-triaz?lio-2-tiolatos em meio ?cido. 2017. 251p Tese (Doutorado em Qu?mica, Ci?ncia exatas, s?ntese org?nica). Departamento de qu?mica, Universidade Federal Rural do Rio de Janeiro, Serop?dica, RJ, 2017. A corros?o ? um dos s?rios problemas enfrentados nos processos industriais, gerando enormes preju?zos financeiros. Diversas t?cnicas s?o utilizadas para evitar ou remediar a corros?o nos diferentes materiais que ela afeta. Dentre elas o uso de agentes inibidores org?nicos ou inorg?nicos tem sido muito utilizado. Assim, neste trabalho de tese foram sintetizados 34 compostos heteroc?clicos, sendo 18 cloretos de 1,3,4-tiadiaz?lio-2-fenilaminas (11 in?ditos) e os outros 16 compostos pertencentes ? classe dos mesoi?nicos 1,3,4-triaz?lio-2-tiolato (15 in?ditos), com o objetivo de avaliar sua efici?ncia como inibidores de corros?o em meio ?cido. Os derivados sintetizados da classe 1,3,4-tiadiaz?lio-2-fenilaminas foram obtidos com grau de pureza e rendimentos satisfat?rios na faixa de 42-96% e, da classe dos 1,3,4-triaz?lio-2-tiolatos em 20-97%. Todos os compostos foram caracterizados por espectroscopia de IV, RMN de 1H e13C. Foi realizado o estudo de modelagem molecular, utilizando o programa SPARTAN-PRO com o m?todo semi-emp?rico, hamiltoniano AM1, para determina??o das propriedades estruturais e eletr?nicas dos 1,3,4-tiadiaz?lio-2-fenilaminas que pudessem contribuir para a efici?ncia de inibi??o da corros?o. Os cloridratos mesoi?nicos da classe 1,3,4-tiadiaz?lio-2-fenilaminas foram testados frente ? corros?o de a?o carbono AISI 1020 em solu??o de HCl 0,5 mol L-1 e em H2SO4 0,5 mol L-1. Para tal avalia??o foram utilizadas as t?cnicas eletroqu?micas de Polariza??o potenciodin?mica (PP), Resist?ncia ? polariza??o linear (RPL) e Espectroscopia de imped?ncia eletroqu?mica (EIE). Os resultados mostraram percentuais significativos de inibi??o da corros?o em ambas solu??es ?cidas, alcan?ando o ?ndice de at? 95% de efici?ncia para o composto cloreto de 4-fenil-5-(3?-met?xi-fenil)-1,3,4-tiadiaz?lio-2-fenilamina na concentra??o de 3,5x10-4 mol L-1 para a solu??o de HCl e, 99% de efici?ncia para os compostos 2?-cloro e 2?-fluor-substitu?dos na concentra??o de 3,5x10-4 mol L-1 para a solu??o de H2SO4. Al?m das t?cnicas eletroqu?micas, foi utilizada a t?cnica gravim?trica que apresentou 99% de efici?ncia anticorrosiva para o derivado 2?-trifluormetil-substitu?do da classe 1,3,4-tiadiaz?lio-2-fenilamina que mostrou o melhor efeito inibidor em solu??o HCl. No entanto, o derivado 2?-trifluormetil-substitu?do da classe 1,3,4-triaz?lio-2-tiol apresentou menor efici?ncia anticorrosiva do que seu is?mero correspondente. As metodologias utilizadas para avalia??o da atividade anticorrosiva (PP, RPL e EIE), incluindo a avalia??o te?rica por modelagem molecular, indicaram os cloridratos mesoi?nicos como eficientes inibidores de corros?o mistos.

Made available in DSpace on 2014-12-17T14:07:04Z (GMT). No. of bitstreams: 1 GineideCA_DISSERT.pdf: 4064193 bytes, checksum: e2de6f4f6fcb019525ce377c5625f694 (MD5) Previous issue date: 2012-10-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / In the search for products that act as corrosion inhibitors and do not cause environmental, impact the use of plant extracts as corrosion inhibitors is becoming a promising alternative. In this work the efficiency of polar extracts (ethanol extracts) obtained from the plants Anacardium occidentale Linn (AO) and Phyllantus amarus Schum. & Thonn (PA) as corrosion inhibitors were evaluated in different concentrations. For that AO and PA extracts were solubilized in the microemulsion systems (SME) containing saponified coconut oil as surfactant (SME -OCS and SME-OCS-1) in saline (NaCl 3,5 %) solution, which was also used as electrolyte. Both SME-OCS and SME-OCS-1 were characterized by surface tension and viscosity methods showing a Newtonian fluid behavior. The SME-OCS and SME-OCS-1 systems satisfactorily solubilized the polar extracts AO and PA with measurements carried out by ultraviolet spectroscopy. The measurements of corrosion inhibition efficiencies were performed by the electrochemical linear polarization resistance (LPR) technique as well as weight loss, on the surface of AISI 1020 carbon steel. The maximum corrosion inhibition efficiencies were determined by extrapolation of Tafel plots, showing the following values: 95,6 % for the system SME-OCS-AO, 98,9 % for the system SME-OCS-AO-1 and 93,4 % for the system SME-OCS-PA / Na busca por produtos que combatam a corros?o e ao mesmo tempo n?o agridam o meio ambiente, a utiliza??o de extratos vegetais como inibidores de corros?o v?m se tornando uma alternativa promissora. Neste trabalho a efici?ncia de inibi??o ? corros?o foi avaliada em diferentes concentra??es de extratos polares (etan?licos) obtidos das plantas Anacardium occidentale Linn (AO) e Phyllantus amarus Schum. & Thonn (PA). Para tanto, os extratos AO e PA foram solubilizados no sistema microemulsionado (SME) contendo o tensoativo ?leo de coco saponificado (SME-OCS e SME-OCS-1) em solu??o salina (NaCl 3,5 %), que tamb?m foi utilizada como eletr?lito. Estes sistemas microemulsionados foram caracterizados por m?todos que avaliam a tens?o superficial e viscosidade, tendo sido evidenciado que se comportam como fluidos Newtonianos. As medidas de efici?ncia de inibi??o ? corros?o foram realizadas atrav?s da t?cnica eletroqu?mica de resist?ncia ? polariza??o linear (LPR) e perda de massa, na superf?cie de a?o carbono AISI 1020. A corrente aplicada ao eletrodo foi controlada pelo equipamento Potenciostato/Galvanostato possibilitando a medi??o da diferen?a de potencial el?trico entre o eletrodo de trabalho e o de refer?ncia. Os sistemas SME-OCS e SME-OCS-1 solubilizaram os extratos etan?licos AO e PA, com quantifica??es realizadas por espectroscopia na regi?o do ultravioleta. As efici?ncias m?ximas de inibi??o ? corros?o foram determinadas atrav?s da extrapola??o das curvas de Tafel, tendo apresentado os seguintes valores: 95,6 % para o sistema SME-OCS-AO, 98,9 % para o sistema SMEOCS- 1-AO e 93,4 % para o sistema SME-OCS-PA