This thesis studies the magnetoelastic, transport and magnetic properties of single crystals of yttrium and scandium dopped with rare earth magnetic impurities. From our measurements of magnetostriction on dilute alloys we derive the magnetoelastic coefficients of the interaction between isolated ions and lattice strains. Our magnetoresistance measurements give the exchange and quadrupole coefficients of the interaction of isolated ions with the conduction electrons. The aim of our magnetic measurements is mainly to study the spin glass properties at low temperatures. The yttrium-rare earth and scandiumorare earth dilute alloys are interesting systems to probe the typical properties predicted by mean field theory for spin glasses with uniaxial crystal field.

Made available in DSpace on 2014-06-11T19:31:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-08Bitstream added on 2014-06-13T20:21:37Z : No. of bitstreams: 1 bellucci_fs_dr_bauru.pdf: 8154488 bytes, checksum: 544941f3ad193b46924bac291e662b7f (MD5) / Nanocompósitos são materiais multifásicos em que pelo menos uma das fases constituintes tem dimensão inferior a 100 nm. Tais materiais têm despertado interesse científico e tecnológico devido ao seu caráter multifuncional e potencial para realizar únicas combinações de propriedades inatingíveis com materiais tradicionais. Este trabalho teve como objetivo desenvolver uma metodologia para a preparação de nanocompósitos funcionais e multifuncionais a base de borracha natural vulcanizada com diversas concentrações de nanopartículas cerâmicas ferroelétricas de niobato de potássio estrôncio KSr2Nb5O15(KSN) e paramagnéticas de ferrita de níquel-zinco Ni0,5Zn0,5Fe2O4 (NZF). As nanopartículas foram sintetizadas pela rota química denominada Método Poliol Modificado obtendo-se partículas com geometria aproximadamente esférica e tamanho igual a 15 nm para a fase niobato e 10 nm para a fase ferrita. Foram produzidos nanocompósitos vulcanizados utilizando um sistema de vulcanização a base de enxofre e um processo de prensagem a quente, hot pressing, com pressing, com parâmetros determinados vai ensaios de reometria. Ensaios mecânicos de tensão/deformação e tensão/compressão foram realizados e efeitos de reticulação combinados com efeitos de superfície das nanopartículas ocasionaram propriedades mecânicas 20% superiores frente as da borracha natural vulcanizada. Foi iniciado o desenvolvimento de quatro potenciais aplicações para os compósitos e nanocompósitos a base de borracha natural vulcanizada e os resultados preliminares são encorajadores. A saber: (i) Modulação das propriedades mecânicas dos compósitos utilizando campo magnético; (ii) Utilização dos nanocompósitos ferruelétricos e paramagnéticos como agentes de modulação do desenvolvimento de colônias de Leishmaniose brasiliense; (iii) Emprego de uma nova metodologia... / Nanocomposites are multiphase materials in which at least one of the constituent phases is made up of nanoparticles with size less than 100 nm. These materials have attracted scientific and technological interest because its multifunctionaity and the possibility of unique combinations of properties not attainable with traditional materials. This present work is intended to develop a methodology for preparation of functional and multifunctional nanocomposites of vulcanized natural rubber with different concentration... (Completo abstract click electronic access below)

Orientador: Marian Rosaly Davolos / Banca: José Clayston Melo Pereira / Banca: Sergio Antonio Marques de Lima / Banca: Yara Galvão Gobato / Banca: Andrea Simone Stucchi de Camargo Alvarez Bernardez / Resumo: Neste trabalho, foram obtidos e caracterizados complexos luminescentes com íons Ln3+ (Ln = Eu, Gd, Tb, Dy) homo e/ou heterobilantanídicos com o ligante ácido tiofeno-2- carboxílico, que atua eficientemente como antena, absorvendo energia e transferindo-a para o íon emissor. A presença do anel tiofênico nos ligantes confere características interessantes, como por exemplo, maior polarizabilidade por conter em sua estrutura um átomo de enxofre. Os complexos foram caracterizados por análise elementar, análise de Ln3+ por análise titulométrica com uso de edta, análise térmica, espectroscopia vibracional na região do infravermelho e DRX, que permitiram propor as estequiometrias [Ln(α-tpc)3(α-Htpc)2]n e [Ln(α-tpc)3(α-Htpc)] e que a coordenação se dá pelo modo bidentado. Pelas espectroscopias eletrônica UV-vis, fotoluminescência e de excitação por raios X, foram observadas as transições características dos íons Ln3+ envolvidos neste trabalho. São propostos mecanismos de transferência de energia em compostos puros e nos complexos heterobilantanídicos, à partir da elaboração de diagramas de energia, baseados nos resultados de fotoluminescência. Os complexos também tiveram suas propriedades magnéticas investigadas, em alguns casos, pela utilização da técnica de EPR, PPMS e VSM, sendo observado um comportamento predominantemente paramagnético para os complexos. Os complexos foram expostos à radiação ionizante por um tempo prolongado, a fim de verificar o comportamento e estabilidade química desses complexos homo e heterolantanídicos sob radiação ionizante e os resultados mostraram que os complexos são estáveis frente à excitação com raios-X. / Abstract: Monometallic and/or heterobimetallic Ln3+ (Ln = Eu, Gd, Tb, Dy) luminescent complex with thiophen-2-carboxylic acid was investigated. The ligand employed in this work, acts efficiently as antenna, absorbing and transfer energy to the emitter ion. The thiophen ring provides interesting features to the system, like higher polarizability due the sulphur atom. The complex were characterized by elemental analysis, complexometric titrimetry with edta, in order to quantify Ln3+, thermal analysis, FTIR and XRD which allowed propose two different stoichiometries [Ln(α-tpc)3(α-Htpc)2]n and [Ln(α-tpc)3(α-Htpc)] and the coordination of the ligand to the Ln3+ occurs through the bidentate coordination mode. By the UV-vis, photoluminescence and X rays spectroscopies, were observed the Ln3+ transitions. Energy transfer mechanism were proposed in monometallic and heterobimetallic complexes, from the drafting of the energy diagram, based on results of fotoluminescence. The complex also have the magnetic properties investigated, by the EPR, PPMS and VSM techniques and the results shows a predominantly paramagnetic behavior to the complexes. The complexes were exposure to ionizing radiation during a extended time, in order to verify the chemical stability of the homo and hetero-lanthanide complex forward to ionizing radiation and is observed high stability over X-ray excitation. / Doutor

Orientador: Aldo Eloizo Job / Coorientador: José Antonio de Saja-Sáez / Coorientador: Miguel Ángel Rodríguez Pérez / Banca: Paulo Noronha Lisboa Filho / Banca: Silvio Rainho Teixeira / Banca: Eduardo Ribeiro de Azevedo / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, tem carater institucional e integra as atividades de pesquisa em materiais de diversos campi da Unesp / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, apresenta convênio acadêmico internacional visando a preparação de teses e dissertações e a duplla titulação / Resumo: Nanocompósitos são materiais multifásicos em que pelo menos uma das fases constituintes tem dimensão inferior a 100 nm. Tais materiais têm despertado interesse científico e tecnológico devido ao seu caráter multifuncional e potencial para realizar únicas combinações de propriedades inatingíveis com materiais tradicionais. Este trabalho teve como objetivo desenvolver uma metodologia para a preparação de nanocompósitos funcionais e multifuncionais a base de borracha natural vulcanizada com diversas concentrações de nanopartículas cerâmicas ferroelétricas de niobato de potássio estrôncio KSr2Nb5O15(KSN) e paramagnéticas de ferrita de níquel-zinco Ni0,5Zn0,5Fe2O4 (NZF). As nanopartículas foram sintetizadas pela rota química denominada Método Poliol Modificado obtendo-se partículas com geometria aproximadamente esférica e tamanho igual a 15 nm para a fase niobato e 10 nm para a fase ferrita. Foram produzidos nanocompósitos vulcanizados utilizando um sistema de vulcanização a base de enxofre e um processo de prensagem a quente, hot pressing, com pressing, com parâmetros determinados vai ensaios de reometria. Ensaios mecânicos de tensão/deformação e tensão/compressão foram realizados e efeitos de reticulação combinados com efeitos de superfície das nanopartículas ocasionaram propriedades mecânicas 20% superiores frente as da borracha natural vulcanizada. Foi iniciado o desenvolvimento de quatro potenciais aplicações para os compósitos e nanocompósitos a base de borracha natural vulcanizada e os resultados preliminares são encorajadores. A saber: (i) Modulação das propriedades mecânicas dos compósitos utilizando campo magnético; (ii) Utilização dos nanocompósitos ferruelétricos e paramagnéticos como agentes de modulação do desenvolvimento de colônias de Leishmaniose brasiliense; (iii) Emprego de uma nova metodologia... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Nanocomposites are multiphase materials in which at least one of the constituent phases is made up of nanoparticles with size less than 100 nm. These materials have attracted scientific and technological interest because its multifunctionaity and the possibility of unique combinations of properties not attainable with traditional materials. This present work is intended to develop a methodology for preparation of functional and multifunctional nanocomposites of vulcanized natural rubber with different concentration... (Completo abstract click electronic access below) / Doutor

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-24T13:49:11Z No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_ConfiguracoesMagneticasColineares.pdf: 2444399 bytes, checksum: 17ab382cbcb9c29bb4b87b155e274e6d (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-11T14:02:08Z (GMT) No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_ConfiguracoesMagneticasColineares.pdf: 2444399 bytes, checksum: 17ab382cbcb9c29bb4b87b155e274e6d (MD5) / Made available in DSpace on 2014-06-11T14:02:08Z (GMT). No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_ConfiguracoesMagneticasColineares.pdf: 2444399 bytes, checksum: 17ab382cbcb9c29bb4b87b155e274e6d (MD5) Previous issue date: 2010 / Neste trabalho investigamos as propriedades magnéticas de currais de Fe, Cr e Mn adsorvidos sobre a superfície de Pt(111) utilizando o método RS-LMTO-ASA (Real Space Linear Muffin Tin Orbital - Atomic Sphere Approximation), o qual é um método de primeiros princípios baseado na Teoria do Funcional da Densidade (DFT-Density Functional Theory), que permite o cálculo de estruturas magnéticas não-colineares. Obtivemos que os átomos de Fe apresentam momentos magnéticos elevados, da ordem de 3.5µB /átomo, e têm uma interação de troca entre primeiros vizinhos forte e ferro-magnética. Isto leva a um arranjo magnético colinear no curral. Para os currais de Mn e Cr encontramos que estes possuem elevado momento magnético, da ordem de 4.51µB /átomo e 4.15µB /átomo, respectivamente, e interações de troca entre primeiros vizinhos antiferro-magnéticas. Isto conduz a arranjos magnéticos colineares em currais simples, assim como interessantes ordenamentos não-colineares, tais como estruturas tipo vértice (skyrmions), para os currais com uma geometria particular onde o antiferromagnetismo se apresenta frustado. / In this study, we investigated the magnetic properties of Fe, Cr and Mn corrals adsorbed on a Pt (111) surface using the first principle RS-LMTO-ASA (Real Space Linear Muffin Tin Orbital – Atomic Sphere Approximation) method, which is based on the Density Functional Theory (DFT), which allows for non-collinear magnetic ordering. We obtained that the Fe atoms posses a large magnetic moment, of the order of 3.5µB / atom, and have a strong ferromagnetic exchange interaction between nearest neighbors. This leads to collinear magnetic arrangements in the corral. For Mn and Cr corrals on Pt (111) we find that the Mn and Cr present large magnetic moments, of the order of 4.51µB / atom and 4.15µB / atom respectively, and have antiferromagnetic interatomic exchange interactions between first neighbor. This leads to collinear magnetic arragements in simple corrals, as well as novel non-collinear ordering, as vortex-like structures (skyrmions), for the case of corrals with particular geometry where antiferromagnetism becomes frustrated.

This thesis studies the magnetoelastic, transport and magnetic properties of single crystals of yttrium and scandium dopped with rare earth magnetic impurities. From our measurements of magnetostriction on dilute alloys we derive the magnetoelastic coefficients of the interaction between isolated ions and lattice strains. Our magnetoresistance measurements give the exchange and quadrupole coefficients of the interaction of isolated ions with the conduction electrons. The aim of our magnetic measurements is mainly to study the spin glass properties at low temperatures. The yttrium-rare earth and scandiumorare earth dilute alloys are interesting systems to probe the typical properties predicted by mean field theory for spin glasses with uniaxial crystal field.

This thesis studies the magnetoelastic, transport and magnetic properties of single crystals of yttrium and scandium dopped with rare earth magnetic impurities. From our measurements of magnetostriction on dilute alloys we derive the magnetoelastic coefficients of the interaction between isolated ions and lattice strains. Our magnetoresistance measurements give the exchange and quadrupole coefficients of the interaction of isolated ions with the conduction electrons. The aim of our magnetic measurements is mainly to study the spin glass properties at low temperatures. The yttrium-rare earth and scandiumorare earth dilute alloys are interesting systems to probe the typical properties predicted by mean field theory for spin glasses with uniaxial crystal field.

Made available in DSpace on 2016-12-23T14:20:01Z (GMT). No. of bitstreams: 1 EMC_Heusler- parte 1.pdf: 1976712 bytes, checksum: 54cbe3c62f71ef7121b79c6f4e1efaa0 (MD5) Previous issue date: 2008-03-28 / Conselho Nacional de Desenvolvimento Científico e Tecnológico / In this work, magnetic entropy change of nonstoichiometric Ni54[Mn(1-x)Fex]19Ga27 Heusler alloys was experimentally verified by partial substitution (up to 50%) of the Mn atoms by magnetic Fe atoms. Such study was mainly concentrated in the magneto-structural transformation region, at low temperatures. The analysis of X-ray diffraction patterns indicate that the partial substitution of Mn atoms by Fe atoms causes predominance of the L21 -phase, however accompanied by spurious phases. The magnetization measurements as a function of the temperature in the low magnetic field reveals that, in all concentration range (0 x 0.5), the system presents a magnetic transition (Ferromagnetic Paramagnetic) at a temperature, TC, near the room temperature, when the material lay in the austenitic phase. Moreover, as many others Heusler alloys, the material undergoes a martensitic structural transition at low temperatures, TM. As the Fe concentration increases, the Curie temperature, TC, undergoes a little variation, increasing around 5%, while TM decreases slowly and monotonically. The magnetic entropy change, for a field of 5T, presents a maximum SM = - 9,3 J/kg.K, for x = 0.1, at a temperature of 250K, and than decreases for x 0.3, changing linearly with the maximum applied field. / Neste trabalho, verificou-se experimentalmente a variação da entropia magnética nas ligas Heusler não-estequiométricas Ni54[Mn(1-x)Fex]19Ga27, substituindo-se parcialmente (até 50%) os átomos de Mn por átomos de Fe. Tal estudo focalizou-se principalmente na região de transformação magneto-estrutural a baixas temperaturas. A análise dos difratogramas de raios-X indica que a substituição parcial de Mn por Fe nessa faixa de concentração, ocasiona uma predominância da fase- L21, porém acompanhada de outras fases espúrias. As medidas de magnetização em função da temperatura realizadas a campos baixos revelam que, em toda a faixa de concentração estudada (0 x 0,5), o sistema apresenta uma transição magnética (Ferromagnético Paramagnético) ao atingir a temperatura de Curie, TC, um pouco acima da temperatura ambiente, quando o material se encontra na fase austenítica. E, assim como muitas outras ligas Heusler, o material sofre uma transição estrutural ao ser resfriado a temperaturas inferiores à temperatura de transição martensítica, TM. À medida que se aumenta a concentração de Fe, a temperatura de Curie, TC, sofre uma pequena variação, aumentando em torno de 5%, enquanto que TM diminui lenta e monotonicamente. A variação da entropia, para um campo de 5T, apresenta um máximo SM = - 9,3 J/kg.K para x = 0,1, a uma temperatura T = 250K e, então, diminui para x 0,3, variando linearmente com o campo aplicado.

Made available in DSpace on 2016-12-23T14:20:02Z (GMT). No. of bitstreams: 1 andre luiz alves pre-textual.pdf: 117556 bytes, checksum: 76d3afbdf37ad33e26738ca777741be3 (MD5) Previous issue date: 2010-10-30 / We have studied the stabilization of NaZn13 phase in the intermetallic compound of generic composition LaFe11,4sp1,6 (sp = Si, Al). This stabilization was investigated through the partial substitution of Fe by atoms of Al and Si, and trough the substitution of La by Y or Gd, which are rare earths elements with no orbital contribution to the magnetic moments. We have chosen to study the compounds with stoichiometry LaFe11,4sp1,6 (sp = Al, Si), with y = 0,88, for which compounds are metamagnetic. We firstly studied NaZn13 phase formation in some mixed compounds of composition LaFe11,4(AlxSi1-x)1,6 (0 less or equals x less or equals 1), prepared using an electric arc furnace. The compounds were characterized by Mössbauer Spectroscopy, X Rays Diffraction and Energy Dispersive X Ray Spectroscopy. Some compositions have a predominant NaZn13 phase, while in other regions the fraction of the NaZn13 phase is relative small due to the presence of other phases formed by segregation. We have also investigated the partial substitution of La atoms by atoms of Y and Gd, in the following compounds La1-x(RE)xFe11,4Si1,6 (RE = Gd or Y), with x= 5%. This substitution doesn t modify significantly the stabilization of the NaZn13 phase compared to the non-substituted compound and the fraction of the segregated a-Fe phase is maintained around 50%. We have used a new procedure using the mechanical alloying to prepare LaFe11,4Si1,6 compounds. It consists in submitting the melted sample to a 0.5 to 1 hour long high energy ball milling process and then in annealing the sample. The process induced a significant reduction of the rich-Fe phase formation compared to a conventional process. Therefore, the process allows to obtain samples with a higher fraction of the desired NaZn13 phase. Therefore, the process allows obtaining samples with a higher fraction of the desired NaZn13 phase. / Neste trabalho foi estudada a estabilização da fase tipo NaZn13 no composto intermetálico LaFe11,4sp1,6 (sp = Si, Al). Essa estabilização foi investigada através da substituição parcial de átomos de Fe por átomos de Al e Si, além da substituição parcial de La por Y ou Gd, que são terras-raras com contribuição orbital nula para o momento magnético. Particularmente, foram escolhidos os compostos com fórmula estequiométrica La[Feysp1-y]13 , com y = 0,88, devido seu caráter metamagnético. Foi inicialmente estudada a formação da fase tipo NaZn13, nos compostos mistos LaFe11,4(AlxSi1-x)1,6 (0 menor ou igual x menor ou igual 1), através da fusão em arco voltaico. Esses compostos foram caracterizados pelas técnicas experimentais de: espectroscopia Mössbauer, difração de raios X e espectroscopia por dispersão de energia. Em algumas regiões de composição, os compostos mistos apresentam a fase NaZn13 majoritária. Em outras regiões de composição, a quantidade da fase tipo NaZn13 é relativamente pequena, se comparado com as demais fases formadas nos processos de segregação. Em seguida, foi investigada a substituição parcial de La por átomos de Y e Gd, ou seja, foram estudados os compostos La1-x(RE)xFe11,4Si1,6 (RE = Y ou Gd) com x = 5%. Os resultados sugerem que esta substituição não provoca mudança significativa na estabilização da fase tipo NaZn13 nos compostos a base de Si, ou seja, independentemente do dopante a fração das fases segregadas ricas em Fe é de aproximadamente 50%. Finalmente, foi usada a técnica de mecanossíntese (ou moagem em altas energias) para propiciar a estabilização de uma maior fração da fase tipo NaZn13, nos compostos a base de Si, já que estes apresentam maiores segregações de Fe e possuem grande potencial para aplicação tecnológica em refrigeradores que usam o efeito magnetocalórico. Assim, as amostras foram fundidas e submetidas à mecanossíntese por 0,5 - 1 hora em um moinho da marca SPEX8000 e depois tratada termicamente. Os resultados estão mostrando significativa redução da fase bcc-Fe segregada, conseqüentemente um aumento da fração da fase tipo NaZn13.

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-25T15:47:50Z No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PropriedadesMagneticasNanoestruturas.pdf: 20228142 bytes, checksum: 9976e2317ce08c4aebbd71bd44297386 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-17T12:29:49Z (GMT) No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PropriedadesMagneticasNanoestruturas.pdf: 20228142 bytes, checksum: 9976e2317ce08c4aebbd71bd44297386 (MD5) / Made available in DSpace on 2014-06-17T12:29:49Z (GMT). No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_PropriedadesMagneticasNanoestruturas.pdf: 20228142 bytes, checksum: 9976e2317ce08c4aebbd71bd44297386 (MD5) Previous issue date: 2012 / CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Motivados por estudos experimentais acerca de monocamadas de metais de transição 3d sobre superfícies de Pd, nesta dissertação investigamos o complexo magnetismo de nanoestruturas, embebidas ou adsorvidas, em superfícies metálicas através de cálculos de primeiros princípios. Utilizamos o método RS-LMTO-ASA (Real Space - Linear MuffinTin Orbital - Atomic Sphere Approximation), o qual é baseado na teoria do funcional da densidade (DFT - Density Functional Theory) e implementado para o cálculo de estruturas magnéticas não colineares. Com este propósito, investigamos nanoestruturas embebidas e ligas (2 x 2) de metais 3d (Cr, Mn, Fe, Co e Ni) na superfície Pd (110), além de nanoestruturas de Cr adsorvidas sobre a superfície de Pd (111). Primeiro, para as nanoestruturas embebidas na superfície Pd (110), analisamos a variação do momento magnético de spin orbital com relação ao número de vizinhos e de valência dos metais 3d. Também mostramos que estas estruturas têm ordenamento magnético colinear, exceto as de Cr e Mn, que apresentam magnetismo não colinear associado à frustração geométrica. Para o caso de nanofios de Cr adsorvidos sobre a superfície de Pd (111), verificamos uma configuração colinear antiferromagnética para cadeias com até 9 átomos. Para o nanofio com 10 átomos obtivemos uma configuração tipo antiferromagnética inclinada (canted). No caso de nanoestruturas de Cr bidimensionais, verificamos complexas configurações magnéticas não colineares com diferentes quiralidades. / Motivated by experimental studies of 3d transitional metal monolayers on Pd surfaces, we studied the complex magnetism of nanostructures, intermixed or adsorbed, on metallic surfaces, via ab initio calculations. We used the RS-LMTO-ASA method (Real Space - Linear Muffin-Tin Orbitals - Atomic Sphere Approximation), which is based on the Density Functional Theory and has been implemented to calculate non-collinear magnetic structures. With this purpose, we investigated intermixed metallic (Cr, Mn, Fe, Co and Ni) nanostructures and alloys (2 x 2) in Pd (110) surface and also adsorbed nanostructures on Pd (111). For intermixed nanostructures in Pd (110), we analyzed the behavior of the spin and orbital magnetic moments as function of the number of first neighbors and the valence number of the 3d metals. We verified a collinear magnetism for most of the cases, except for the Cr and Mn geometrically frustrated structures, which present noncollinear magnetic configurations. For Cr nanowires adsorbed on Pd (111), we obtained a collinear antiferromagnetic configuration for chains with up to 9 atoms. For the nanowire with 10 atoms of Cr, the magnetic ordering is antiferromagnetic canted. For two dimensional Cr nanostructures adsorbed on Pd (111), we obtained complex noncollinear magnetic structures, with different chiralities.