Optically transparent carbon based nanomaterials including graphene and carbon nanotubes(CNTs) are promising candidates as transparent conductive electrodes due to their high electrical conductivity coupled with high optical transparency, can be flexed several times with minimal deterioration in their electronic properties, and do not require costly high vacuum processing conditions. CNTs are easily solution processed through the use of surfactants sodium dodecyl sulfate(SDS) and sodium cholate(SC). Allowing CNTs to be deposited onto transparent substrates through vacuum filtration, ultrasonic spray coating, dip coating, spin coating, and inkjet printing. However, surfactants are electrically insulating, limit chemical doping, and increase optical absorption thereby decreasing overall performance of electrodes. Surfactants can be removed through nitric acid treatment and annealing in an inert environment (e.g. argon). In this thesis, the impact of surfactant removal on electrode performance was investigated. Nitric acid treatment has been shown to p-dope CNTs and remove the surfactant SDS. However, nitric acid p-doping is naturally dedoped with exposure to air, does not completely remove the surfactant SC, and has been shown to damage CNTs by creating defect sites. Annealing at temperatures up to 1000°C is advantageous in that it removes insulating surfactants. However, annealing may also remove surface functional groups that dope CNTs. Therefore, there are competing effects when annealing CNT electrodes. The impacts on electrode performance were investigated through the use of conductive-tip atomic force microscopy, sheet resistance, and transmittance measurements. In this thesis, the potential of graphene CNT composite electrodes as high performing transparent electrodes was investigated. As-made and annealed graphene oxide CNT composites electrodes were studied. Finally, a chemical vapor deposition grown graphene CNT composite electrode was also studied.

Ohmic contacts are crucial components in semiconductor devices such as transistors and diodes, and lowering their contact resistance is an important factor in device performance enhancement. This is especially important for low-noise amplifiers (LNAs) where device noise temperature decreases both directly and indirectly with decreasing contact resistance. This becomes relevant in quantum computers operated at cryogenic temperatures as LNAs constitutes the 4 K quantum bit (qubit) readout signal amplification chain. The goal of this project is to investigated the superconducting element niobium (Nb) as contact material for indium phosphide (InP) high-electron-mobility transistors (HEMTs), being the active component in cryogenic high-frequency LNAs. For contact and barrier resistance determination, test structures were fabricated and utilized according to the transfer length method(TLM) and the recess TLM respectively. Measurements were performed in room temperature as well as in cryogenic temperatures below and above Nb’s bulk transition temperature of 9.25 K. The results show low-resistance Nb-based ohmic contacts for n-In0.65Ga0.35As, with the non-alloyed Nb(50 nm)/Au(100 nm) stack yielding a room temperature contact resistivity of (9.4 ± 0.5) × 10−8 Ωcm2. For all contacts the contact resistivity increased moving to cryogenic temperatures, as expected when electron occupation of high-energy states decreases. At cryogenic temperatures nosuperconducting transition was observed, attributed to the Nb layer thickness being roughly equal to its coherence length. Considering the effective barrier resistance, the Ni/Ge/Au/Nb/Au alloyed contact had the lowest room temperature resistance, reporting 143 Ω µm. In cryogenic temperatures the effective barrier resistance unexpectedly decreased in all contacts. The Nb/Au contact showed the best cryogenic performance, with a barrier resistance of 28 − 37 Ω µm. This indicates great potential for non-alloyed Nb/Au contacts in cryogenic InP HEMTs. / Alla halvledarkomponenter, som dioder och transistorer, har ohmska kontakter. Att sänka kontaktresistansen hos de ohmska kontakterna är ett sätt att höja prestandan hos en komponent. Särskilt gäller detta för lågbrusförstärkare, som har en brustemperatur som minskar både direkt och indirekt med avtagande kontaktresistans. För kvantdatorer som måste kylas till kryogena temperaturer för att fungera är detta relevant eftersom förstärkningen av utläsningssignalen från kvantbitar sker via lågbrusförstärkare vid 4 K. Målet för detta examensprojekt är att undersöka ohmska kontakter baserade på det supraledande materialet niobium (Nb) i indiumfosfidbaserade högelektronmobilitetstransistorer, som är den aktivakomponenten i kryogena högfrekvens-lågbrusförstärkare. För bestämning av kontaktoch barriärresistans producerades teststrukturer enligt Transfer Length-metoden (TLM) respektive etsad TLM. Mätningar genomfördes i rumstemperatur samt vid kryogena temperaturer både över och under niobiumets kritiska temperatur på 9.25 K. Resultatet visar låg kontaktresistans för Nb-baserade ohmska kontakter på n-In0.65Ga0.35As. Den icke-legerade Nb(50 nm)/Au(100 nm)-kontakten hade en kontaktresistivitet på (9.4 ± 0.5) × 10−8 Ωcm2 . Vid kryogena temperaturer ökade kontaktresistansen för samtliga Nb-baserade kontakter, vilket är förväntat då färre elektroner fyller högenergitillstånd. Inget supraledande tillstånd observerades vid kryogena temperaturer, vilket kan förklaras av att tjockleken på niobiumlagret var ungefär lika med dess koherenslängd. Lägst barriärresistans vid rumstemperatur hade den legerade Ni/Ge/Au/Nb/Au-kontakten, med ett värde på 143 Ω µm. Vid kryogena temperaturer skedde en oväntad minskning hos barriärsresistansen hos samtliga kontakter, där den lägst barriärsresistans uppmättes på den icke-legerade Nb/Au-kontakten, 28 − 37 Ω µm. Slutsatsen som dras är att det finns stor potential för användning av icke-legerade Nb/Au-kontakter för kryogena lågbrusförstärkare baserade på indiumfosfid.