The construction sector is responsible for 20% of Greenhouse Gas (GHG) emissions, of whichdiesel-powered construction equipment are large contributors. Currently there are many ongoing Fuel Cell (FC) powered construction equipment projects as it is seen as an attractiveoption to power the futures zero-emission heavy-duty machines. Although an attractivealternative, hydrogen FC has drawbacks such as releasing liquid water and water vapor viathe exhaust as a byproduct which in their working environment can cause a suite of issues. Agap in the literature on the water exhausted is present and therefore this degree project seeksto investigate the amount, and ratio, of liquid water and water vapor released from threetypical construction equipment drive cycles which would allow further investigation onappropriate management. The method used for this degree project was to modify a pre-mademodel in Simulink built with Simscape blocks. The model was modified to represent a FCsystem used in a test-rig by implementing experimental and measured data for design andoperating parameters. Different pressures, temperatures, and cathode inlet RelativeHumidity (RH) were investigated to find their effect on the performance and water in theexhaust. A sensitivity analysis of different unknown parameters was also conducted tounderstand their influence on the results. For the reference case, the results showed that foran articulated hauler, the water in the exhaust was 26% liquid which translates to 8.6 kg for a1-hour drive cycle. The crawler excavator and wheel loader, both had 30-minute drive cyclesand had 1.1 kg liquid water with a liquid water ratio of 7% and 0.7 kg liquid water with aliquid water ratio of 5% in the exhaust respectively. For a full 8-hour workday with twoparallel FCs connected, the articulated hauler liquid water amount is 137.6 kg, the crawlerexcavator 35.2 kg, and the wheel loader 22.4 kg. Overall, it was found the liquid water ratiocould be changed to a large extent with different operating parameters, where thetemperature had the greatest influence. The system and stack efficiencies did not changeconsiderably with different operating parameters, meaning that the total water in the exhaustremained similar for the different respective drive cycles.

Um filme polimérico utilizado na fabricação de curativos adesivos não perfurados deve ter baixo módulo de elasticidade e boa permeabilidade ao vapor d\' água. O baixo módulo de elasticidade garante sensação de maior conforto do produto em contato com a pele quando a pessoa que o está utilizando movimenta a parte do corpo sobre a qual está aplicado o curativo, principalmente a região das articulações, como joelhos e cotovelos. A importância de uma boa permeabilidade ao vapor d\' água está relacionada, principalmente em curativos não perfurados, ao fato de que a pele perde água constantemente e, se o filme polimérico não permitir a saída dessa água ao meio ambiente, ocorrerá um fenômeno denominado maceração, que é a sensibilização excessiva da pele, causada pela hiper hidratação da mesma. O presente trabalho apresenta um estudo da permeabilidade ao vapor d\' água, bem como a caracterização vibracional e térmica de um filme polimérico constituído por três polímeros diferentes, desenvolvido para substituir a poliuretana utilizada atualmente na produção de curativos adesivos não perfurados, com custo inferior. Os polímeros que constituem o filme foram caracterizados separadamente e alguns resultados obtidos, como Tm e a estrutura química dos polímeros Lotader® e Lotryl® foram comparados aos dados fornecidos pelo fabricante. Verificou-se que as propriedades de módulo de elasticidade e permeabilidade ao vapor d\' água do filme desenvolvido são inferiores às da poliuretana inviabilizando a substituição. Entretanto, o trabalho proporcionou um melhor entendimento dos fatores que influenciam o módulo de elasticidade e a permeabilidade do novo material ao vapor d\' água. / A polymeric film must have low elasticity modulus and good water vapor permeation to be used in the production of non perforated adhesive tapes. Low modulus is desirable to provide comfort sensation as the consumer moves the part of his or her body in which the tape is applied on, mainly in the articulations regions, as elbows and knees. The importance of good water vapor permeation is related, mainly in the case of non perforated adhesive tapes with the continuous loss of water by the skin. If the film does not allow the release of the water continuously lost by the skin to the environment, the skin will become very sensitiveness as a result of over hydration. This work presents a study of water permeability and a thermal and vibrational characterization of a polymeric film composed of three different polymers developed to replace the adhesive not perforated polyurethane tape providing lower cost. Besides characterization a test of Water Vapor Transmission Rate (WVTR) was performed. Each polymer present in the film composition was analyzed and the results as Tm and chemical structure of Lotader® e Lotryl® were compared with the producer data. It was verified that the properties of elasticity modulus and water vapor permeability of the new material developed are worse than polyurethane so the substitution can not be performed. However, the work provided a better understanding of the factors that influences the elasticity modulus and water vapor permeability of the new material.

Um filme polimérico utilizado na fabricação de curativos adesivos não perfurados deve ter baixo módulo de elasticidade e boa permeabilidade ao vapor d\' água. O baixo módulo de elasticidade garante sensação de maior conforto do produto em contato com a pele quando a pessoa que o está utilizando movimenta a parte do corpo sobre a qual está aplicado o curativo, principalmente a região das articulações, como joelhos e cotovelos. A importância de uma boa permeabilidade ao vapor d\' água está relacionada, principalmente em curativos não perfurados, ao fato de que a pele perde água constantemente e, se o filme polimérico não permitir a saída dessa água ao meio ambiente, ocorrerá um fenômeno denominado maceração, que é a sensibilização excessiva da pele, causada pela hiper hidratação da mesma. O presente trabalho apresenta um estudo da permeabilidade ao vapor d\' água, bem como a caracterização vibracional e térmica de um filme polimérico constituído por três polímeros diferentes, desenvolvido para substituir a poliuretana utilizada atualmente na produção de curativos adesivos não perfurados, com custo inferior. Os polímeros que constituem o filme foram caracterizados separadamente e alguns resultados obtidos, como Tm e a estrutura química dos polímeros Lotader® e Lotryl® foram comparados aos dados fornecidos pelo fabricante. Verificou-se que as propriedades de módulo de elasticidade e permeabilidade ao vapor d\' água do filme desenvolvido são inferiores às da poliuretana inviabilizando a substituição. Entretanto, o trabalho proporcionou um melhor entendimento dos fatores que influenciam o módulo de elasticidade e a permeabilidade do novo material ao vapor d\' água. / A polymeric film must have low elasticity modulus and good water vapor permeation to be used in the production of non perforated adhesive tapes. Low modulus is desirable to provide comfort sensation as the consumer moves the part of his or her body in which the tape is applied on, mainly in the articulations regions, as elbows and knees. The importance of good water vapor permeation is related, mainly in the case of non perforated adhesive tapes with the continuous loss of water by the skin. If the film does not allow the release of the water continuously lost by the skin to the environment, the skin will become very sensitiveness as a result of over hydration. This work presents a study of water permeability and a thermal and vibrational characterization of a polymeric film composed of three different polymers developed to replace the adhesive not perforated polyurethane tape providing lower cost. Besides characterization a test of Water Vapor Transmission Rate (WVTR) was performed. Each polymer present in the film composition was analyzed and the results as Tm and chemical structure of Lotader® e Lotryl® were compared with the producer data. It was verified that the properties of elasticity modulus and water vapor permeability of the new material developed are worse than polyurethane so the substitution can not be performed. However, the work provided a better understanding of the factors that influences the elasticity modulus and water vapor permeability of the new material.