An acid rock drainage (ARD) stream emanating from the Zn-Pb XY-deposit in the Yukon Territory was examined in order to evaluate the physico-chemical and geochemical processes governing the distribution of dissolved elements from the creek. The creek showed very high concentrations of metals (300 mg/L Fe, 500 mg/L Zn, 15 000 µg/L Ni, 1300 µg/L Cu and 4500 µg/L Cd), low water temperatures (1 – 12°C) and was acidic to moderately acidic (pH 3.1 – 5.0). It was found that this stream experienced a strong seasonal evolution, with increased sulphate and metal concentrations and decreased pH over the course of the summer. The mineral precipitates that formed under low pH conditions were a mixture of schwertmannite, goethite, jarosite and barite, while those that formed under moderately acidic conditions were a mixture of jurbanite, hydrobasaluminite, gibbsite and an X-ray amorphous Al-sulphate phase. Most of the mineral precipitates were of inorganic origin, although microbes may have played a role in mineral formation and trace metal sequestration in some of the precipitates. All of the mineral precipitates contained anomalous concentrations of trace elements (up to 1.5 % wt Zn) and showed a seasonal evolution in their mineralogy, both of which were determined to be a function of the pH and prevailing geochemical conditions. The geochemistry of the ARD creek draining the XY-deposit was compared to another ARD creek in the area that was likely draining shales. The two creeks were compared in order to determine if ARD geochemical characteristics can be used as a tool for the mineral exploration industry.

The West Ansil deposit was the first Cu discovery in 25 years in the Noranda Central Camp. It has a combined indicated and inferred resource of ~1.2 Mt. Grades for the indicated resource are 3.4% Cu, 0.4% Zn, 1.4 g/t Au and 9.2 g/t Ag. The bulk of the resource is located in three massive sulphide lenses (Upper, Middle and Lower) that are entirely within the Rusty Ridge Formation above the Lewis exhalite. The mineralization in all three ore lenses consists of massive pyrrhotite + chalcopyrite + magnetite. Semi-massive sphalerite is restricted to the upper and lower parts of the Middle lens. Massive magnetite occurs at the center of the Upper and Middle lenses, where it replaces massive pyrrhotite. A striking feature of West Ansil is the presence of abundant colloform and nodular pyrite (+marcasite) in the massive sulphides. Late-stage replacement of massive pyrrhotite by colloform pyrite and marcasite, occurs mostly along the upper and lower contacts of the lenses.

This study is concerned with the Pb-isotope compositions of galena samples from Pb-Zn occurrences in southern Turkey. The purpose is to i) provide chronologic information for ore deposition, ii) investigate the likely source(s) of lead in ore deposits, and iii) examine the possible control of tectonic setting and crustal basement on Pb-isotope compositions. The data used in the study belongs to the deposits located in Taurides (Zamanti, KahramanmaraS, Malatya, Elazig, Bitlis), with additional data from Nigde Massif and Hakkari Area. The mineralizations are dominantly carbonate-hosted Pb-Zn deposits formed as fracture and karst fillings and, in some places, parralel to bedding. Ore minerals are mainly Zn-oxides and minor Zn, Pb-sulphides. The Pb-isotope compositions, as evaluated in terms of their configuration with respect to reference crustal growth curves and reference isochrons on conventional Pb-isotope diagrams, point to U/Pb ratios greater than average crustal values (and close to the Western Mediterranean Crustal Growth Curve) for all the deposits, indicating upper crustal source for Pb. However, some of the deposits (AfSin-KahramanmaraS / Oreks, D&uuml / ndarli, AgcaSar and skarn type deposits to the south of &Ccedil / adirkaya in Zamanti (Kayseri-Adana) / Keban-Elazig) appear to have magmatic inputs in their genesis. Relatively old deposits are likely Paleozoic (Cafana-Malatya and T&uuml / rksevin-KahramanmaraS), Late Paleozoic-Early Mesozoic (Kalek&ouml / y-Zamanti) and Mesozoic (Hakkari) in age. The rest of the deposits (most of the occurrences in Zamanti, Nigde, KahramanmaraS, Elazig and Bitlis) are likely of Cenozoic age. The Pb-isotope compositions are, in general, similar to those from other occurrences in the Mediterranean Belt.

Thesis (Ph. D.)--Miami University, Dept. of Chemistry and Biochemistry, 2008. / Title from second page of PDF document. Includes bibliographical references.

Made available in DSpace on 2014-06-11T19:32:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-12-07Bitstream added on 2014-06-13T20:44:20Z : No. of bitstreams: 1 schoenlein_nc_dr_rcla.pdf: 708327 bytes, checksum: 8cde8b071e32b6d7c6b3ae6e75ecacae (MD5) / O solo do pólo cerâmico de Santa Gertrudes tem sido poluído há décadas por diversos elementos, como Pb, Zn e outros. Foram realizadas quatro coletas de solo (duas durante a época chuvosa e duas na seca), em cinco locais, entre novembro de 2002 a junho de 2003; mediram-se temperaturas, pH, teores de Pb, Zn e umidade. Os fungos foram isolados através do método de Warcup, modificado, com a utilização de meios de extrato de malte agar (MEA) a 2%, adicionados com doses crescentes de nitrato de Zn e de Pb, sendo as colônias purificadas e identificadas. Foram obtidos 70 táxons de fungos anamorfos com 70% de similaridade entre as micotas obtidas com os dois metais. Foram isolados 43 taxons dos meios de cultura com Pb, havendo predominância de isolamentos nos teores mais elevados (500 a 1000 mg Pb/dm3). Foram obtidos 63 táxons nos meios com Zn, com teores de 200 a 500 mg /dm3. Predominaram espécies de Trichoderma, Penicillium e outras usualmente associadas a substratos em decomposição. Estabelecida a diversidade dos fungos, estudou-se a tolerância do Aspergillus terreus e do Paecilomyces lilacinus a nitratos de Pb e Zn. Foi usado o meio Czapek, com a adição de 250; 500; 750 e 1000 mg de Pb por dm3 e 1.000; 2.000; 3.000; 4.000; 6.000; 8.000 e 10.000 mg de Zn por dm3 .Com os dados obtidos, foi possível cálcular o teor do metal que inibe 50% e 100% do crescimento da biomassa EC 50 e/ou EC100 .Para o A. terreus foram encontrados: EC 50 Pb= 489,05 mg/dm3 ; EC 100 Pb = 1.049,08 mg/dm3 ; EC50 Zn = 81,26 mg/dm3 ; EC100 Zn= 6.360,98 mg/dm3 . Para o P. lilacinus foram encontrados: EC 50 Pb = 1.147,89 mg/dm3; EC 100 Pb = 2.389,45 mg/dm3 ; EC 50 Zn= 8.323,75 mg/dm3; EC 100 Zn= 15.995,36 mg/dm3 . Em relação à sensibilidade a Pb e a Zn, o A. terreus apresentou sensibilidades maiores do que o P. lilacinus. Constatou-se também, que a sensibilidade do A . terreus a Zn foi maior do que ao Pb. / The soil of the ceramic pole, has been polluted since decades by several elements, mainly lead and zinc. Four soil sample collections were conducted (2 during the rainy and 2 in the dry season) at 5 sites, between november 2002 and june 2003, measuring the temperature, pH and the content of Pb, Zn and moisture in the soil. The fungi were obtained by the modified Warcup's soil plate method, using malt extract agar (2%), added of increasing dosis of Zn and Pb salts.The colonies were purified and identified .Seventy anamorphs were obtained, with 70% of similarity between the mycotas isolated from the culture media added with the metals. Fourty three taxa were isolated from the culture media with Pb, with predominance of isolations in higher Pb concentrations (500 to 1000 mg Pb per dm3). 63 taxa were obtained in the media with Zn, mainly in the concentrations between 200 and 500 mg Zn per dm3. Species of Trichoderma, Penicillium and several fungi usually found in decomposing plant debris prevailed. After determining the diversity of fungi in the ceramic pole, Aspergillus terreus and Paecilomyces lilacinus were submitted to tests of tolerance to Pb and Zn. A modified medium Czapek was used amended with 250; 500; 750 and 1000 mg of Pb per dm3 and 1000; 2000; 3000; 4000; 6000; 8000 and 10000 for Paecilomyces lilacinus mg of Zn per dm3 . Afterwards it was possible to calculate the effective concentrations inhibiting growth by 50% and 100% values ( EC50 and EC100 ). Values obtained for A terreus: EC 50 Pb = 489,05 mg/dm3 ; EC 100 Pb= 1.049,08 mg/dm3 ; EC 50 Zn= 81,26 mg/dm3; EC 100 Zn= 6.360,98 mg/dm3 .Values obtained for P. lilacinus; EC 50 Pb = 1.147,89 mg/dm3 ; EC 100 Pb = 2.389,45 mg/dm3 ; EC 50 Zn = 8.323,79 mg/dm3 ; EC 100 Zn = 15.995,36 mg/dm3 . With regards to the sensitivity to lead and zinc, A. terreus showed greater sensitivity than P. lilacinus. A greater sensitivity of A. terreus for zinc than lead was recorded.

Este estudo avaliou o efeito de fontes e níveis de suplementação de selênio (Se) em dietas de aves reprodutoras pesadas sobre produção de ovo e a concentração de Se no conteúdo total do ovo. Foram utilizadas 50 reprodutoras Cobb 500 de 22 semanas, alojadas individualmente e alimentadas com dieta basal sem a suplementação de Se por três semanas. Após as aves receberam cinco tratamentos dietéticos com 10 repetições de uma ave cada, sendo compostos por selenito de sódio (inorgânico; Na2SeO3, 45% Se) e Zn-LSe- metionina (orgânico; ZnSeMet, 0,1% Se), como segue: T1- 0,15% inorgânico; T2- 0,30% inorgânico; T3- 0,15% orgânico; T4- 0,30% orgânico; T5- 0,15% inorgânico e 0,15% orgânico. Avaliações foram realizadas em dois períodos de 4 semanas. A produção de ovo e o peso do ovo foram diariamente registrados e a gravidade específica foi medida duas vezes por semana até o final do estudo. No primeiro período os animais alimentados com 0,30 ppm de Se orgânico apresentaram maior percentual de produção de ovo (P < 0,05), sendo que, no segundo período, nenhuma diferença foi observada entre os tratamentos (P > 0,05). As avaliações entre os períodos apresentaram que o peso do ovo não foi diferente (P > 0,05), sendo que a gravidade específica foi menor no segundo período (P < 0,05) e a concentração de Se no ovo aumentou com o tempo de suplementação (P < 0,05), independentemente da fonte de Se suplementada. A comparação dos tratamentos que continham apenas uma única fonte de Se demonstrou que a concentração de Se no ovo foi maior com a suplementação do maior nível de ZnSeMet (P < 0,05). Entretanto, a suplementação com a combinação das fontes (Na2SeO3 e ZnSeMet) produziu similares concentrações de Se no ovo. O aumentou da dose de selenito de sódio de 0,15 para 0,30 ppm não foi acompanhado por um aumento da deposição de Se no ovo. / This study evaluated effects of sources and levels of Se in broiler breeder diets on egg production and Se concentration in eggs. Fifty Cobb 500 hens 22 wks of age were individually placed in steel cages and fed a basal diet without Se supplementation for 3 wks. Birds were then provided five dietary treatments with 10 replicates of one individual hen, which had dietary selenium supplied from sodium selenite (inorganic; Na2SeO3, 45% Se) and/or from Zn-LSe- methionine (organic; ZnSeMet, 0.1% Se) as follow: T1- 0.15% Se from Na2SeO3; T2- 0.30% Se from Na2SeO3; T3- 0.15% Se from ZnSeMet; T4- 0.3ç0% Se from ZnSeMet; T5- 0.15% Se from Na2SeO3 + 0.15% Se from ZnSeMet. Evaluations were conducted in two periods of 4 wks each. Experimental diets were prepared through the supplementation of corn-soybean meal diets. Egg production and egg weight were recorded daily, whereas specific gravity was measured twice a wk towards the end of the study. In the first period, the hens fed 0.30 ppm of organic Se produced more eggs (P < 0.05) whereas no difference (P > 0.05) in egg production was found in the second period. Period evaluations showed that egg weight was not different (P > 0.05), whereas specific gravity decreased (P < 0.05) and Se concentration in eggs increased (P < 0.05) in the second period, regardless of Se source. The comparison between treatments with single Se sources demonstrated that the concentration of Se in eggs was greater with the highest level of ZnSeMet (P <0.05) and, the supplementation of a combination of sources (Na2SeO3 and ZnSeMet) produced similar concentrations of Se in the egg (P <0.05). However, increasing the dose of sodium selenite from 0.15 to 0.30 ppm was not accompanied by increased deposition of Se in the egg.

Submitted by Nathália Faria da Silva (nathaliafsilva.ufv@gmail.com) on 2017-06-21T12:00:53Z No. of bitstreams: 1 texto completo.pdf: 1640010 bytes, checksum: 164e79ea0d9bf2327b08bba217ccda91 (MD5) / Made available in DSpace on 2017-06-21T12:00:53Z (GMT). No. of bitstreams: 1 texto completo.pdf: 1640010 bytes, checksum: 164e79ea0d9bf2327b08bba217ccda91 (MD5) Previous issue date: 2002-08-21 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este trabalho foi desenvolvido com o objetivo de avaliar a distribuição e formas de ocorrência de Zn, Cd e Pb, tendo em vista identificar a origem de valores anômalos em amostras de solos, adjacentes às áreas mineradas da Companhia Mineira de Metais (CMM), no município de Vazante-MG. Objetivou-se, também, estabelecer valores de referência local (VRL) para estes metais nestas zonas mineralizadas, a fim de permitir uma avaliação da contaminação ambiental. Foram coletadas amostras de perfis de solo em remanescentes sobre a área mineralizada e a jusante e montante desta, nas profundidades de 0 a 2 cm, 2 a 5 cm, 5 a 10 cm, 10 a 20 cm, 20 a 50 cm, 50 a 100 cm e 100 a 150 cm. As concentrações de Zn, Cd e Pb foram obtidas para as formas: a) solúvel; b) trocável; c) associada a carbonatos; d) associada a óxidos amorfos; e) associada a óxidos cristalinos; f) associada a matéria orgânica; g) residual; e h) total. Foram determinadas, também, as concentrações desses elementos nas formas disponíveis (Mehlich-3 e DTPA). Os valores de referência local (VRL’s) foram obtidos considerando-se a média ponderada dos teores de Zn, Cd e Pb nas camadas de 0 a 20 cm dos perfis a montante. De posse desses valores calculou-se o fator de contaminação (F.C.) e o índice de geoacumulação (IGeo) para cada perfil. Verificou-se que os teores de Zn, Cd e Pb, de modo geral, são mais elevados nas áreas localizadas sobre a zona de mineralização, com solos mais jovens (Cambissolos e Neossolos), em relação àqueles perfis mais intemperizados (Latossolos e Argissolos), localizados à montante e a jusante do empreendimento. Os teores totais podem ser considerados extremamente elevados, principalmente para Zn e Cd. Mesmo considerando apenas os teores de Zn e Cd trocáveis e associados a matéria orgânica, obtêm-se valores superiores aos reportados, como teores totais encontrados naturalmente em solos. Há um padrão decrescente dos teores com a profundidade, principalmente para Zn e Cd, nos perfis localizados fora da área mineralizada (áreas a montante e jusante). Há um aumento dos teores de Zn em profundidade para o Cambissolo (perfil 2), e de Cd para os Cambissolos (perfis 2, 3, 4 e 5) localizados na zona de mineralização. Não há diferença significativa entre os teores médios de Zn, Cd e Pb das áreas à montante e à jusante, ao nível de 5% de significância, para todas as formas nas quais esses elementos encontram-se associados. Os valores de referência (VRL ́s) obtidos foram de 1.262 mg/kg para Zn; 4,75 mg/kg para Cd e 384 mg/kg para Pb. O VRL para Zn é inferior aos valores de intervenção (VI ́s) para as áreas industriais adotados no Estado de São Paulo, EUA e Canadá. Para o Cd o VRL é inferior aos VI’s adotados em São Paulo, para a área agrícola de proteção máxima e nos EUA e Canadá, para áreas residenciais. O VRL para Pb é inferior aos VI’s adotados em São Paulo, Alemanha, Canadá e EUA, para áreas residenciais. Os perfis das áreas mineralizadas apresentaram os maiores fatores de contaminação com destaque para o perfil 5 (área mineralizada em exploração). De acordo com o índice de geoacumulação (IGeo) os perfis de solo a jusante foram classificados como não poluídos a moderadamente poluídos. / This work was carried out to evaluate the distribution and forms of Zn, Cd and Pb, aiming to identify the origin of abnormal values in soils associated with mining areas of the CMM company, in Vazante (MG-Brazil). Also, it aimed to establish local reference values (LRV) for these elements based on total and available levels (Melich 3 and DTPA) and offer subsidies to environmental risk assessment. Soil profiles were samples in mined areas, at both upper and downslope at depths of 0-2, 2-5, 5-10, 10-20, 20-50, 50-100 and 100-150 cm. The Zn, Cd and Pb concentrations were obtained for the following forms: (a) soluble; (b) exchangeable; (c) carbonate-associated; (d) associated with amorphous oxides; (e) associated with crystalline oxides; (f) organically bound; (g) residual and (h) total. It was also determined the concentration of available forms of these elements (Melich-3 and DTPA). The LRV’s were obtained by the mean of Zn, Cd and Pb levels at 0-20 cm soils at upslope position. Based on the LRV, the contamination factor (C.F.) and the geo-accumulation index were calculated for xiiieach profile. Overall, the levels of Zn, Cd and Pb were higher in younger soils of the mineralized zone in relation to deeply weathered soils, at both upslope and downslope from the mine plant. The total levels are extremely high, specialy for Zn and Cd. Even when only the exchangeable and organically bound forms of Zn and Cd are considered, the values are much higher than those reported by Alloway, considering the naturally occurring levels in soils. There is a decreasing trend with depth, mostly for Zn and Cd, in soils outside the mineralized area (at both up and downslope positions). There is an increase in the Zn levels with depth in the Cambisol (P2), and also for Cd (P2, P3, P8, P9), in the mined area. There is no significant difference between mean values of Zn, Cd and Pb at upslope and downslope, at 5% significance. The LRV’s obtained were 1.662 mg/kg for Zn; 4,75 mg/kg for Cd and 384 mg/kg for Pb. The LRV for Zn is lower than the IV’s adopted in São Paulo for agricultural areas at maximum protection and lower than those adopted in the USA and in Canada for residential areas. The LRV for Pb is lower than the IV’s adopted in São Paulo, USA, Canada and Germany for residential areas. The profiles of the mineralized area, specially P9 (mining area), presented higher CF’s. Based on the geo-accumulation index (IGeo), the profiles positioned dowslope were classified as moderately contaminated to not contaminated.

Les besoins actuels en électronique de puissance concernent principalement la fiabilité et l'augmentation de la densité de puissance. Dans les deux cas, ce qu'il est convenu d'appeler l'intégration de puissance constitue une solution. Les problèmes de fiabilité peuvent être résolus par la diminution du nombre d'interconnexions et par la maitrise complète de la réalisation des convertisseurs et, ceux liés à la densité de puissance, par la réduction des dimensions et par la mutualisation d'un certain nombre de fonctions: intégration des passifs, substrats fonctionnalisés, composants de couplage... Ceci passe nécessairement par une stratégie de choix de structures de conversion permettant de répondre à ces questions. Les convertisseurs multi-niveaux, multicellulaires entrelacés sont un exemple de structure permettant de réduire la taille et le volume des composants magnétiques. Le point clé de ces structures réside dans le partage des flux magnétiques entre les différentes phases du convertisseur via un transformateur intercellulaire (ICT). Ce type de composant permet l'entrelacement de nombreuses cellules de commutation. Il consiste en un noyau magnétique de forme spécifique et souvent complexe. Les travaux réalisés dans le cadre de cette thèse concernent le développement de technologies permettant la réalisation de composants magnétiques de type ICT en vue de leur intégration. Les principales propriétés du matériau (magnétiques et diélectriques) nécessaires à la réalisation de ce type de composant nous ont conduits à choisir une ferrite de type Ni0,30Zn0,57Cu0,15Fe2O4 susceptible de s'adapter tant aux fréquences de fonctionnement qu'à la gamme de puissance envisagée. Différents procédés de mise en œuvre (et les paramètres qui leur sont associés) ont été étudiés. Il s'agit soit du formage, via l'utilisation de moules souples ou encore du pressage isostatique, et de l'usinage soit à cru soit après frittage. Concernant l'usinage, deux systèmes distincts nous ont permis la mise en forme des noyaux complexes soit en 2 D soit en 3D. Les résultats de cette démarche tant en termes d'objet que de propriétés du composant, sont présentés. L'influence des différents paramètres utilisés lors de la réalisation (température de frittage, pression,...) sur les caractéristiques finales est aussi étudiée. / Current issues in power electronics are mainly related to the reliability and the increase in the power density. In both cases, what is called power integration is proposed as the solution. Reliability issues can be solved by reducing the number of interconnections and by the full design and elaboration of converters; and those related to the power density are addressed by reducing the dimensions and the mutualization of a number of functions: integration of passive components, embedded substrates, coupling components... This necessarily involves the choice of a strategy for converting structures. Multilevel converters, interleaved multicellular converters are an example of structures that reduce the size and volume of magnetic components. The key point of these structures is the sharing of magnetic flux between the different phases of the converter via an intercellular transformer (ICT). This type of component allows interleaving many switching cells. It consists of a magnetic core of specific, often complex and shape. The work done in this thesis concerns the development of technologies for the realization of ICT magnetic components for their integration. The main material properties (magnetic and dielectric) necessary for the implementation of this type of component oriented us towards a ferrite Ni0,30Zn0,57Cu0,15Fe2O4 able to work at the proposed operating frequencies and power range. Various elaboration processes (and the parameters associated with them) were studied. It is either forming, through the use of flexible molds or by isostatic pressing, and machining either raw or after sintering. By machining, two separate systems have enabled us obtaining complex magnetic cores either in 2D or in 3D. The results of this approach in terms of object and component properties are presented. The influence of various parameters used during the production (sintering temperature, pressure,...) on the final characteristics is also investigated.

Este estudo avaliou o efeito de fontes e níveis de suplementação de selênio (Se) em dietas de aves reprodutoras pesadas sobre produção de ovo e a concentração de Se no conteúdo total do ovo. Foram utilizadas 50 reprodutoras Cobb 500 de 22 semanas, alojadas individualmente e alimentadas com dieta basal sem a suplementação de Se por três semanas. Após as aves receberam cinco tratamentos dietéticos com 10 repetições de uma ave cada, sendo compostos por selenito de sódio (inorgânico; Na2SeO3, 45% Se) e Zn-LSe- metionina (orgânico; ZnSeMet, 0,1% Se), como segue: T1- 0,15% inorgânico; T2- 0,30% inorgânico; T3- 0,15% orgânico; T4- 0,30% orgânico; T5- 0,15% inorgânico e 0,15% orgânico. Avaliações foram realizadas em dois períodos de 4 semanas. A produção de ovo e o peso do ovo foram diariamente registrados e a gravidade específica foi medida duas vezes por semana até o final do estudo. No primeiro período os animais alimentados com 0,30 ppm de Se orgânico apresentaram maior percentual de produção de ovo (P < 0,05), sendo que, no segundo período, nenhuma diferença foi observada entre os tratamentos (P > 0,05). As avaliações entre os períodos apresentaram que o peso do ovo não foi diferente (P > 0,05), sendo que a gravidade específica foi menor no segundo período (P < 0,05) e a concentração de Se no ovo aumentou com o tempo de suplementação (P < 0,05), independentemente da fonte de Se suplementada. A comparação dos tratamentos que continham apenas uma única fonte de Se demonstrou que a concentração de Se no ovo foi maior com a suplementação do maior nível de ZnSeMet (P < 0,05). Entretanto, a suplementação com a combinação das fontes (Na2SeO3 e ZnSeMet) produziu similares concentrações de Se no ovo. O aumentou da dose de selenito de sódio de 0,15 para 0,30 ppm não foi acompanhado por um aumento da deposição de Se no ovo. / This study evaluated effects of sources and levels of Se in broiler breeder diets on egg production and Se concentration in eggs. Fifty Cobb 500 hens 22 wks of age were individually placed in steel cages and fed a basal diet without Se supplementation for 3 wks. Birds were then provided five dietary treatments with 10 replicates of one individual hen, which had dietary selenium supplied from sodium selenite (inorganic; Na2SeO3, 45% Se) and/or from Zn-LSe- methionine (organic; ZnSeMet, 0.1% Se) as follow: T1- 0.15% Se from Na2SeO3; T2- 0.30% Se from Na2SeO3; T3- 0.15% Se from ZnSeMet; T4- 0.3ç0% Se from ZnSeMet; T5- 0.15% Se from Na2SeO3 + 0.15% Se from ZnSeMet. Evaluations were conducted in two periods of 4 wks each. Experimental diets were prepared through the supplementation of corn-soybean meal diets. Egg production and egg weight were recorded daily, whereas specific gravity was measured twice a wk towards the end of the study. In the first period, the hens fed 0.30 ppm of organic Se produced more eggs (P < 0.05) whereas no difference (P > 0.05) in egg production was found in the second period. Period evaluations showed that egg weight was not different (P > 0.05), whereas specific gravity decreased (P < 0.05) and Se concentration in eggs increased (P < 0.05) in the second period, regardless of Se source. The comparison between treatments with single Se sources demonstrated that the concentration of Se in eggs was greater with the highest level of ZnSeMet (P <0.05) and, the supplementation of a combination of sources (Na2SeO3 and ZnSeMet) produced similar concentrations of Se in the egg (P <0.05). However, increasing the dose of sodium selenite from 0.15 to 0.30 ppm was not accompanied by increased deposition of Se in the egg.

Submitted by Kilvya Braga (kilvyabraga@hotmail.com) on 2018-04-19T11:38:41Z No. of bitstreams: 1 MIKARLA BAÍA DE SOUSA - DISSERTAÇÃO (PPGEQ) 2015.pdf: 2853939 bytes, checksum: 73cb4a3ae1a6f5afdefa786c3032de07 (MD5) / Made available in DSpace on 2018-04-19T11:38:41Z (GMT). No. of bitstreams: 1 MIKARLA BAÍA DE SOUSA - DISSERTAÇÃO (PPGEQ) 2015.pdf: 2853939 bytes, checksum: 73cb4a3ae1a6f5afdefa786c3032de07 (MD5) Previous issue date: 2015-09-29 / CNPq / O processo de corrosão está constantemente transformando os materiais metálicos de modo que a durabilidade e o desempenho dos mesmos deixam de satisfazer os fins a que se destinam. Uma forma de se minimizar a corrosão em materiais metálicos é revesti-los com outros materiais. A eletrodeposição é um método muito utilizado na obtenção de revestimentos metálicos resistentes à corrosão e ao desgaste mecânico. Através da eletrodeposição é possível obter ligas metálicas, as quais são geralmente preparadas com o intuito de melhorar as propriedades dos seus constituintes iniciais. O estudo proposto tem como objetivo otimizar as variáveis de entrada (densidade de corrente e pH) e obter a liga CuZn-Ni resistente à corrosão, caracterizando-a quanto à morfologia, eficiência de corrente catódica, composição da liga, microdureza e resistência à corrosão. Para a otimização do processo de eletrodeposição da liga foi realizado um planejamento fatorial completo 32. Avaliou-se quantitativamente a influência das variáveis de entrada bem como suas possíveis interações com a realização mínima de experimentos. Estudou-se o processo de eletrodeposição de liga Cu-Zn-Ni sobre um cátodo, utilizando um banho contendo sulfato de cobre, sulfato de zinco, sulfato de níquel e citrato de sódio. Todos os experimentos foram realizados em temperatura ambiente e em triplicata, os valores ótimos encontrados através da polarização potenciodinâmica linear foram: densidade de corrente catódica de 30 mA/cm2 e pH 6,0; com esses parâmetros foi possível alcançar um potencial de corrosão de -0,31949 V, uma resistência à polarização de 948090 Ω e uma corrente de corrosão de 6,4265 nA. Os ensaios de impedância eletroquímica confirmaram os resultados obtidos pelos ensaios de polarização potenciodinâmica linear. A composição média deste depósito foi 56 w.t.% de Cu, 38 w.t.% de Zn e 6 w.t. % de Ni. As ligas encontradas apresentaram brilho, aderência e boa resistência à polarização e através da difração de raios-x concluiu-se que a liga obtida é cristalina. O estudo da morfologia acusou a presença de nódulos esféricos de vários tamanhos na superfície da liga. A composição química dos revestimentos parece ser o fator mais importante para a microdureza dos revestimentos, já que o experimento com maior conteúdo de zinco apresentou o valor mais elevado de microdureza, que foi de 571 HV. Estas ligas podem ter grande utilidade em várias aplicações nas indústrias químicas, petrolíferas, petroquímicas, navais, de construções civis e automobilísticas em decorrência de algumas características especiais, como alta resistência à corrosão e ao desgaste e ao baixo sobrepotencial de evolução do hidrogênio da liga Cu-Zn-Ni. / The corrosion process is constantly transforming metallic materials, so that their durability and behavior no longer satisfy their goals. One way to minimize corrosion in metallic materials is to coat them with other materials. Electrodeposition is a widely used method in obtaining metallic coatings resistant to corrosion and mechanic wear. Through electrodeposition, it is possible to obtain alloys, which are generally prepared in order to improve the characteristics of their initial constituents. The proposed study has, as a goal, to optimize the input variables (current density and pH), and obtain the Cu-Zn-Ni alloy resistant to corrosion. A 32 experimental design was used to optimize the electrodeposition process. Both the input variable influence, and their possible interactions, performing less experiments as possible, were quantitatively evaluated. The electrodeposition process of the Cu-Zn-Ni on a cathode was studied, using a bath containing copper sulfate, zinc sulfate, nickel sulfate and sodium citrate. All experiments were conducted at room temperature and in triplicate. The best reached values, through linear potentiodynamic polarization, were: cathode current density of 30 mA/cm2 and pH 6.0; with those parameters, it was possible to reach a potential of -0.31949 V, a 948090 Ω polarization resistance, and a 6.4265 nA current density. Electrochemical impedance spectroscopy confirms the linear potentiodynamic polarization results. Its chemical composition, in average, was 56 w.t. % of Cu, 38 w.t.% of Zn, and 6 w.t.% of Ni. Those found alloys showed bright, adherence and good resistance to polarization, and, through X-ray diffraction, it is concluded that the alloy is crystalline. The morphology study pointed out the presence of spherical nodules with different sizes on the alloy surface. The chemical composition of the coatings seems to be the most important factor for the coatings microhardness, since the experiment with the highest zinc content showed the highest microhardness value, which was 571 HV. Those alloys may have great utility in many applications in chemical, oil, petrochemical, naval industries, civil construction and automobile industries, because of some special characteristics, such as high resistance to corrosion and wear, and low overpotential for hydrogen evolution reaction of the Cu-Zn-Ni alloy.