Superplasticerarens påverkan och ballastskillnader på betong med krossad betong som ballast : En experimentell studie om tryckhållfasthet, konsistens och fraktionsfördelning

Detta examensarbete är baserat på experimentella studier med avsikten att studera skillnaden som uppstår vid användning av superplasticerare på betong med krossad betong samt makadam och sand som ballast, med avseende på arbetbarhet, konsistens samt tryckhållfasthet. Fraktionsfördelningen kommer även analyseras på den krossade betongen i jämförelse med makadamen och sanden. Det utformades fyra olika blandningar där första blandningen var utan superplasticerare och hade makadam som ballast, andra blandningen innehöll superplasticerare samt makadam som ballast, den tredje blandningen var utan superplasticerare och hade krossad betong som ballast, den fjärde blandningen innehöll superplasticerare och hade krossad betong som ballast. Betongens arbetbarhet uppskattades på samtliga blandningar innan konsistensen mättes. Konsistensen mättes i form av sättmått med hjälp av en sättkon. Sedan tillverkades fyra provkroppar av varje blandning där tryckhållfastheten testades. Resultaten som erhållits visade att superplasticerare var mer effektiv på blandningarna med makadam. Betongens arbetbarhet och konsistens förändrades endast marginellt, dock ökade tryckhållfastheten med 28,7 och 23,8% för blandningarna med makadam respektive krossad betong som ballast. Den krossade betongen visade på bra fraktionsfördelning men skiljde sig någorlunda från makadamen, den stora skillnaden fanns i de finare fraktionsstorlekarna. / This thesis is based on experimental studies with the intention of determine the efficiency of Superplasticizer in concrete made with recycled concrete aggregate compared with macadam in terms of workability, consistency and compressice strength. The fraction distribution will also be analysed on the recycled concrete aggregate compared to the macadam. Four different mix designs was made in which the first mix was without superplasticizer and had macadam as aggregates, the second mix contained superplasticizer and also had macadam as aggregates, the third mix was without superplasticizer and had recycled concrete aggregate, the fourth mix contained superplasticizer also had recycled concrete aggregates. The workability of was estimated on all mix designs before the consistency was measured. The slump of all mix designs was measured to determine the consistency. Then four specimens were made from each mixture on which the compressive strength was tested. The results obtained showed that superplasticizers were more effective on the mixtures with macadam as their aggregates. The workability and consistency only changed slightly, the compressive strength increased by 28.7 respectively 23.8% for mixtures with macadam and recycled concrete aggregates. The recycled concrete aggregates showed good fraction distribution but differed quite a bit from the sand and the macadam, the big difference was in the finer fractions.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hh-42973
Date January 2020
CreatorsSelander, Carl
PublisherHögskolan i Halmstad, Akademin för ekonomi, teknik och naturvetenskap
Source SetsDiVA Archive at Upsalla University
LanguageSwedish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0035 seconds