Previous issue date: 2015-02-27 / CNPq / As indicações das cerâmicas odontológicas se devem as propriedades estéticas. O sistema CAD/CAM permite realizar restaurações cerâmicas, gerando uma elevada quantidade de resíduos, na forma de pó, durante o desbaste e fresa da peça cerâmica, que atualmente é descartado. Este trabalho tem por objetivo estudar o reaproveitamento dos resíduos de zircônia obtidos através do sistema CAD/CAM visando sua aplicação em prótese odontológica. Foi estudado o resíduo proveniente da fresagem de blocos comerciais de zircônia estabilizada com 3% de ítria (3Y-TZP), (sistema Zirkonzahn®), o resíduo caracterizado através da determinação da composição química, difração de raios X, determinação de tamanho de partículas e análise térmica diferencial/gravimétrica. O resíduo beneficiado seguiu duas rotas: desaglomeração em moinho de bolas e sem desaglomeração. Ambos os materiais foram utilizados para confecção de corpos de prova de zircônia queimados a 1180oC em seguida infiltrou-se o vidro de lantânio a 1140oC, os corpos para densificação e os corpos confeccionados extraídos das placas comerciais (Zirkonzahn®) foram queimados em temperaturas de 1300, 1400 e 1500oC após sinterização caracterizados com a determinação da porosidade aparente, microscopia eletrônica de varredura, resistência à flexão em três pontos e microdureza Vickers. Observou-se nos resultados que o resíduo é constituído por zircônia estabilizada com 3% de ítria (3Y-TZP) e matéria orgânica. A desaglomeração diminui o tamanho dos agregados e favoreceu o processo de sinterização, os corpos infiltrados não apresentam resistência adequada para infraestruturas, os corpos sinterizados a 1500oC apresentaram porosidade próxima da obtida pelos corpos de referência. A resistência e a microdureza dos corpos do resíduo atingiram o valor máximo de 1079 HV para os corpos com zircônia não desaglomerada (ZSD) e de 1523 HV para os corpos com zircônia desaglomerada (ZCD), após queima a 1500oC. / The use of ceramics in dental prosthesis is due to the aesthetic properties. The CAD/CAM system allows making ceramic restorations, generating a large amount of waste, in powder form, during the roughing and milling cutter of the ceramic piece, which currently is thrown away. The aim of this work is to study the reuse of the waste obtained from zirconia CAD/CAM system for its application in dental prosthesis. It was studied the residue from the milling of commercial stabilized zirconia blocks with 3% of yttria (3Y-TZP). The residue was characterized by chemical composition, X-ray diffraction, particle size and differential and gravimetric thermal analysis. The improvement residue followed two routes: deagglomeration in a ball mill and without deagglomeration. Both materials were used for preparation of specimens of zirconia. It were sintered at 1180oC then infiltrated with lanthanum glass at 1140oC. The infiltrated specimens and the specimens extracted from the commercial blocks (Zirkonzahn ®) were sintered at temperatures of 1300, 1400 and 1500oC.After sintering its were characterized by apparent porosity, scanning electron microscopy, flexural strength in three points and Vickers micro hardness. It was observed in the results that the residue consists of stabilized zirconia with 3% yttria (3Y-TZP) and organic matter. The deagglomeration decreases the size of the aggregates and favored the sintering process. The infiltrated specimens do not have adequate resistance to infrastructures, the sintered bodies to 1500oC presented close porosity obtained by the scanbodies. Resistance and micro hardness of bodies of waste reached the maximum value of 1079 HV for the bodies with no deagglomeration zirconia (ZSD) and 1523 HV for the bodies with zirconia desaglomerada (ZCD), after burning the 1500oC.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1025 |
| Date | 21 June 2018 |
| Creators | CORDEIRO, Valéria Vital. |
| Contributors | LIRA, Hélio de Lucena., MENEZES, Romualdo Rodrigues., RIBEIRO, Maria Aparecida., TEÓFILO, Edvania Trajano., BRAGA, Aluska do Nascimento Simões., SILVA, Valmir José da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds