Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-graduação em Odontologia / Made available in DSpace on 2012-10-23T08:46:23Z (GMT). No. of bitstreams: 1
247966.pdf: 14616516 bytes, checksum: 4d006e9da5f998712de0ac8cb9f9f868 (MD5) / Os objetivos deste estudo foram analisar a quantidade e a composição química do precipitado formado pelos cimentos ProRoot MTA, MTA Branco, MTA BIO e Portland branco, após imersão em tampão fosfato salino (PBS); avaliar a interface cimento-dentina e, paralelamente, analisar o pH e a liberação de íons cálcio a partir dos cimentos empregados. As coroas de 28 dentes humanos foram removidas e o terço médio das raízes cortados transversalmente para a obtenção de discos radiculares com 2 mm de espessura. Em cada secção, o espaço do canal foi ampliado a fim de obter uma cavidade padronizada com 2 mm de diâmetro. As secções foram divididas aleatoriamente em 5 grupos, sendo as cavidades preenchidas com: ProRoot MTA (Grupo 1), MTA Branco (Grupo 2), MTA BIO (Grupo 3), CP1: Cimento de Portland branco com 20% de óxido de bismuto (Grupo 4), e CP2: Cimento de Portland branco com 20% de óxido de bismuto e 10% cloreto de cálcio (Grupo 5). Em seguida, as amostras foram colocadas em recipientes plásticos contendo 15 mL de PBS e levadas à estufa (37ºC) por um período de 2 meses. A solução tampão foi substituída a cada 5 dias. A cada substituição, os precipitados foram colhidos, lavados, dessecados e pesados. Aos 5, 15, 25 e 35 dias, a solução foi coletada para medição do pH e da concentração de íons cálcio. Ao final dos 2 meses, as amostras foram processadas para avaliação, em MEV, da interface cimento-dentina. Os dados foram analisados estatisticamente em um nível de significância de 5%. Em todas as amostras foi observada a formação de precipitados de apatita carbonatada e a presença de uma intercamada na interface cimento-dentina. A partir da intercamada, foram observados prolongamentos penetrando nos túbulos dentinários. O ProRoot MTA e o MTA BIO formaram maior quantidade de precipitados, geraram os valores de pH mais altos e a maior concentração de íons cálcio em todos os períodos de avaliação. O ProRoot MTA, o MTA Branco, o MTA BIO e o cimento Portland branco têm a capacidade de dissolver alguns de seus componentes e propiciar a precipitação de apatita carbonatada, promovendo a formação de uma intercamada com prolongamentos que penetram nos túbulos dentinários.
The aim of this study was to analyze the amount and the chemical composition of the precipitate formed by ProRoot MTA, White MTA, MTA BIO and white Portland cements, after immersion in phosphate buffered saline (PBS), to evaluate the cement-dentine interface and to analyze the pH and the calcium ions release. The crowns of 28 human teeth were removed and the middle third of the roots was sectioned transversally in order to obtain 2mm-thickness sections. In each section, the space of the canal was enlarged to obtain 2mm-diameter standardized cavities. The samples were randomly divided in 5 groups, and the cavities filled with: ProRoot MTA (Group 1), White MTA (Group 2), MTA BIO (Group 3), white Portland cement with 20% of bismuth oxide (CP1) (Group 4), and white Portland cement with 20% of bismuth oxide and 10% calcium chloride (CP2) (Group 5). The samples were immediately placed in plastic vials containing 15 mL of PBS for 2 months at 37ºC. The PBS solution was collected and replaced every 5 days. After each replacement, the precipitates were collected, washed, desiccated and weighed. Calcium ions release and pH of the collected solution were monitored at 5, 15, 25 e 35 days. The samples were processed for SEM observation. Data obtained were statistically analyzed with 5% level of significance. Precipitates of carbonated apatite were observed in all the samples, along with the presence of an interfacial layer between the cement and the dentinal wall. Tags reproducing demineralized tubular dentin were observed from the interfacial layer. ProRoot MTA and MTA BIO cements produced the overall highest amount of precipitates, reached higher pH values, and released more calcium ions at all time intervals. ProRoot MTA, White MTA, MTA BIO and white Portland cements have dissolved, releasing some of their major components, promoting the precipitation of carbonated apatite and the formation of an interfacial layer with tags.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/90336 |
| Date | January 2007 |
| Creators | Carmona, Jessie Fabiola Reyes |
| Contributors | Universidade Federal de Santa Catarina, Felippe, Wilson Tadeu, Felippe, Mara Cristina Santos |
| Publisher | Florianópolis, SC |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 100 f.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds