Previous issue date: 2006-02-22 / The present study aims to evaluate in vitro the flexural strength of the direct
composite resin (FiltekTM Z-250 – 3M/ESPE) and of the second generation
laboratory resin (CeseaDST II – Kuraray) either associated or not to glass fibers
(Fibrex-coronal – Angelus), varying the source of photoactivating (L.E.Demetron 1
– Kerr e Strobolux – EDG). Fifty-six samples were made inside a biparted metalic
matrix, 13.0 mm in diameter X 2.4 mm thick, divided into 8 study groups (n=7): GI
– Resin FiltekTM Z-250/ Fibreless/ LED; GII – Resin FiltekTM Z-250/ Fibreless/
Strobolux; GIII - Resin FiltekTM Z-250/ Fibrex-coronal/ LED; GIV - Resin FiltekTM
Z-250/ Fibrex-coronal/ Strobolux; GV – Resin CeseaDST II/ Fibreless / LED; GVI -
Resin CeseaDST II/ Fibreless / Strobolux; GVII - Resin CeseaDST II/ Fibrexcoronal/
LED; GVIII - Resin CeseaDST II/ Fibrex-coronal/ Strobolux. The samples
were under the test of biaxial flexural strength in the Kratos equipment, with
speed of 1 ± 0.5 mm/min and load cell of 500 Kgf. The flexural strength values
were submitted to the Tukey test (P=0,01). The rate of the results in MPa were:
GI – 187.91 ± 32.78; GII – 196.76 ± 31.15; GIII – 208.27 ± 18.79; GIV – 218.02 ±
15.76; GV – 101.72 ± 11.25; GVI – 103.05 ± 9.56; GVII – 164.76 ± 12.54 e GVIII
– 176.75 ± 47.03. The conclusion is that the analyzed composites showed
different behaviors in vitro; the direct composite FiltekTM Z-250 showed higher
values of flexural strength in all the studied groups; the type of light source did not
interfere in the flexural strength of the evaluated composites; reinforcement with
fibers increased the flexural strength both evaluated composites, however only for
the indirect composite CeseaDST II that increase was significant. / O objetivo deste estudo foi avaliar in vitro a resistência flexural da resina
composta direta (FiltekTM Z-250 – 3M/ESPE) e da resina laboratorial de segunda
geração (CeseaDST II – Kuraray) associadas ou não a fibras de vidro (Fibrexcoronal
– Angelus), variando a fonte de luz fotoativadora (L.E.Demetron 1 – Kerr
e Strobolux – EDG). Foram confeccionados 56 corpos-de-prova (CP) em uma
matriz metálica bipartida com as dimensões de 13,0 mm de diâmetro X 2,4 mm
de espessura divididos em 8 grupos (n=7) de estudo: GI - Resina FiltekTM Z-250/
Sem fibras/ LED; GII – Resina FiltekTM Z-250/ Sem fibras/ Strobolux; GIII - Resina
FiltekTM Z-250/ Fibrex-coronal/ LED; GIV - Resina FiltekTM Z-250/ Fibrex-coronal/
Strobolux; GV – Resina CeseaDST II/ Sem fibras/ LED; GVI - Resina CeseaDST II/
Sem fibras/ Strobolux; GVII - Resina CeseaDST II/ Fibrex-coronal/ LED; GVIII -
Resina CeseaDST II/ Fibrex-coronal/ Strobolux. Os CP foram submetidos ao teste
de resistência flexural biaxial no equipamento Kratos com velocidade de 1 ± 0,5
mm/min e célula de carga de 500 Kgf. Os valores de resistência flexural foram
submetidos ao teste de Tukey (P=0,01). A média dos resultados em MPa foram:
GI – 187,91 ± 32,78; GII – 196,76 ± 31,15; GIII – 208,27 ± 18,79; GIV – 218,02 ±
15,76; GV – 101,72 ± 11,25; GVI – 103,05 ± 9,56; GVII – 164,76 ± 12,54 e GVIII
– 176,75 ± 47,03. Concluiu-se que: os compósitos avaliados apresentaram
diferentes comportamentos in vitro; o compósito direto FiltekTM Z-250 apresentou
maiores valores de resistência flexural em todos os grupos estudados; o tipo de
fonte de luz não interferiu na resistência flexural dos compósitos avaliados; o
reforço com fibras aumentou a resistência flexural de ambos os compósitos
avaliados, sendo que apenas para o compósito indireto CeseaDST II esse
aumento foi significante.
Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/1774 |
Date | 22 February 2006 |
Creators | Portero, Priscila Paiva |
Contributors | Gomes, Osnara Maria Mongruel, Gomes, João Carlos |
Publisher | UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Programa de Pós-Graduação em Odontologia, UEPG, BR, Clinica Integrada, Dentística Restauradora e Periodontia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 1.266 seconds