Previous issue date: 2010-02-26 / This paper aims to present the feasibility of using a composite using discarded material from the cultivation of banana tree (pseudostem), which is fibrillated together with synthetic resin replacing glass fiber to be used in structural elements that do not demand large mechanical stress such as reservoirs, troughs, domes, sewage pipes etc.. For this, there were studies about the mechanical properties of a composite made with polyester resin and fiber of banana tree (Musa sp, musac), in which the
splints were removed from the pseudostem, being made fibrillation by hand, with the aid of a brush steel, followed by natural drying. After treatment for cleaning and removal of wax, the fiber was cut into pieces of approximately 60 mm to 100 mm, for, together with synthetic resin, make cards of a features fiber composite with random orientation relative to the weight of the resin. We used three different percentages of
fiber (3%, 6% and 9%), in order to make a comparative study between them and what would be the one with the best performance. Were manufactured specimens of each material and then subjected to uniaxial tensile tests, three point bending,
moisture absorption and thermal characteristics. The results show that, in general, the use of banana tree fiber is feasible simply by an improvement in the production process (machining of the procedure) and greater care in the manufacture of parts / Este trabalho tem como objetivo apresentar a viabilidade de um comp?sito utilizando material descartado da lavoura da bananeira (pseudocaule), o qual ? fibrilado juntamente com resina sint?tica em substitui??o ? fibra de vidro, a ser
utilizado em elementos estruturais que n?o demandem grandes esfor?os mec?nicos, tais como reservat?rios, calhas, domos, tubula??es de esgotamento etc. Para isso foram efetuados estudos sobre as propriedades mec?nicas de um comp?sito de
resina poli?ster e fibra de bananeira (musa s.p., mus?cea), nos quais foram retiradas as talas do pseudocaule, sendo feita a fibriliza??o de forma manual, com o aux?lio de uma escova de a?o, seguido de secagem ao natural. Ap?s tratamento para limpeza e retirada de cera, a fibra foi cortada em peda?os de aproximadamente 60 mm a 100 mm para, juntamente com a resina sint?tica, fabricar placas de um comp?sito de caracter?sticas fibrosas com orienta??o aleat?ria em rela??o ao peso da resina. Foram utilizadas tr?s percentagens distintas de fibras (3%, 6% e 9%), a fim de se efetuar um estudo comparativo entre elas e determinar qual seria aquela com o
melhor desempenho mec?nico. Foram fabricados corpos de prova de cada material, sendo ent?o submetida aos ensaios de tra??o uniaxial, flex?o em tr?s pontos, absor??o de umidade e caracter?sticas t?rmicas. Os resultados demonstram que, de
forma geral, o uso de fibra de bananeira ? vi?vel, bastando uma melhoria no seu processo de obten??o (mecaniza??o do procedimento) e um maior cuidado durante a fabrica??o das pe?as
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/15617 |
| Date | 26 February 2010 |
| Creators | Mota, Rui Carlos de Sousa |
| Contributors | CPF:13291085400, http://lattes.cnpq.br/7103009428184656, Souza, Luiz Guilherme Meira de, CPF:25094955420, http://lattes.cnpq.br/0801747108308706, Souza, Roberto Silva de, CPF:44466927472, http://lattes.cnpq.br/4012782800846844, Mendes, Jos? Ubiragi de Lima |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Engenharia Mec?nica, UFRN, BR, Tecnologia de Materiais; Projetos Mec?nicos; Termoci?ncias |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds