Efeito da termorretificação nas propriedades tecnológicas do bambu / Effect of the thermal treatment in the technological properties of the bamboo

Made available in DSpace on 2016-12-23T13:51:45Z (GMT). No. of bitstreams: 1
Flavia Maria Silva Brito.pdf: 1958233 bytes, checksum: 19806ba42f2c6acb72b77967069c2d99 (MD5)
Previous issue date: 2013-02-26 / Este trabalho teve como objetivos avaliar as características anatômicas e físicas do bambu in natura , analisar os efeitos da termorretificação nas propriedades tecnológicas do bambu laminado colado termorretificado (BLCTR) e na sua durabilidade natural. Foram coletados quatro colmos em idade adulta e cortados a cada 2,0 m, divididos em quatro secções no sentido longitudinal sendo imersas em água durante 10 dias e secas ao ar. As secções foram transformadas em taliscas com dimensões de 0,5 x 3,5 x 45 cm (espessura x largura x comprimento) e tratadas termicamente a 100, 140, 160, 180 e 200°C, durante uma hora para cada temperatura. Os adesivos utilizados foram o Cascophen RS-216-M , à base de resorcinol - formaldeído, Cascamite PL-2030 , à base de uréia - formaldeído, ambos termofixos e um termoplástico à base de acetato de polivinila, Cascorez 2500 . As taliscas termorretificadas foram dimensionadas conforme cada ensaio realizado. Observou-se que os colmos de bambu possuem uma frequência de vasos de 0 a 4 vasos.mm-2 com média de 2 vasos.mm-², fibras longas e estreitas com comprimento médio de 2,72 mm. A massa específica básica de 0,66 g.cm-3 e a retratibilidade volumétrica de 15,41%. Os teores de extrativos e lignina total aumentaram, conforme o incremento da temperatura, e o teor de holocelulose foi reduzido. A partir da temperatura de 160 °C ocorreu um ganho na durabilidade natural do bambu e na estabilidade dimensional do BLCTR aderido com RF, porém houve uma queda nos valores da massa específica básica e na resistência mecânica do material / This work aimed to evaluate the physical and anatomical characteristics of bamboo "in natura", analysing the effects of thermal treatment on the technological properties of glued laminated bamboo thermo-modified (GLBT) and in your natural durability. A total of four culms were collected in age adulthood and cut every to 2.0 m and divided into four lengthwise sections that were immersed in water for 10 days and air-dried. The sections were transformed into flights with dimensions of 0.5 x 3,5 x 45 cm (thickness x width x length) and thermal treated to 100, 140, 160, 180 and 200 °C for one hour for each temperature. T he adhesives used were Cascophen RS-216-M , based resorcinol formaldehyde, Cascamite PL-2030 , based on urea - formaldehyde, both thermoset and thermoplastic based on one polyvinylacetate, Cascorez 2500 . The flights thermal treated were scaled according to each proposed test. It was observed that the bamboo culms have a frequency of 0 to 4 vessels.mm-2, whith mean of vessels.mm-2, with long and narrow fibres with length average of 2.72 mm. The basic specific gravity was of 0.66 g.cm-3 and volumetric shrinkage of 15.41%. The total extractives and lignin contents increased as the temperature increase, and holocellulose content has been reduced. Since the temperature of 160 °C was a gain in durability natural bamboo and the dimensional stability of GLBT adhered to RF, but there was a decrease in the values of specific gravity and mechanicalproperties of the material

Identiferoai:union.ndltd.org:IBICT/oai:dspace2.ufes.br:10/5775
Date26 February 2013
CreatorsBrito, Flávia Maria Silva
ContributorsPaes, Juarez Benigno, Fantuzzi Neto, Humberto, Vidaurre, Graziela Baptista, Oliveira, José Tarcísio da Silva, Arantes, Marina Donária Chaves
PublisherUniversidade Federal do Espírito Santo, Programa de Pós-Graduação em Ciências Florestais, UFES, BR, Ciências Florestais
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formattext
Sourcereponame:Repositório Institucional da UFES, instname:Universidade Federal do Espírito Santo, instacron:UFES
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0025 seconds