Previous issue date: 2013-02-26 / Este trabalho teve como objetivos avaliar as características anatômicas e físicas do bambu in natura , analisar os efeitos da termorretificação nas propriedades tecnológicas do bambu laminado colado termorretificado (BLCTR) e na sua durabilidade natural. Foram coletados quatro colmos em idade adulta e cortados a cada 2,0 m, divididos em quatro secções no sentido longitudinal sendo imersas em água durante 10 dias e secas ao ar. As secções foram transformadas em taliscas com dimensões de 0,5 x 3,5 x 45 cm (espessura x largura x comprimento) e tratadas termicamente a 100, 140, 160, 180 e 200°C, durante uma hora para cada temperatura. Os adesivos utilizados foram o Cascophen RS-216-M , à base de resorcinol - formaldeído, Cascamite PL-2030 , à base de uréia - formaldeído, ambos termofixos e um termoplástico à base de acetato de polivinila, Cascorez 2500 . As taliscas termorretificadas foram dimensionadas conforme cada ensaio realizado. Observou-se que os colmos de bambu possuem uma frequência de vasos de 0 a 4 vasos.mm-2 com média de 2 vasos.mm-², fibras longas e estreitas com comprimento médio de 2,72 mm. A massa específica básica de 0,66 g.cm-3 e a retratibilidade volumétrica de 15,41%. Os teores de extrativos e lignina total aumentaram, conforme o incremento da temperatura, e o teor de holocelulose foi reduzido. A partir da temperatura de 160 °C ocorreu um ganho na durabilidade natural do bambu e na estabilidade dimensional do BLCTR aderido com RF, porém houve uma queda nos valores da massa específica básica e na resistência mecânica do material / This work aimed to evaluate the physical and anatomical characteristics of bamboo "in natura", analysing the effects of thermal treatment on the technological properties of glued laminated bamboo thermo-modified (GLBT) and in your natural durability. A total of four culms were collected in age adulthood and cut every to 2.0 m and divided into four lengthwise sections that were immersed in water for 10 days and air-dried. The sections were transformed into flights with dimensions of 0.5 x 3,5 x 45 cm (thickness x width x length) and thermal treated to 100, 140, 160, 180 and 200 °C for one hour for each temperature. T he adhesives used were Cascophen RS-216-M , based resorcinol formaldehyde, Cascamite PL-2030 , based on urea - formaldehyde, both thermoset and thermoplastic based on one polyvinylacetate, Cascorez 2500 . The flights thermal treated were scaled according to each proposed test. It was observed that the bamboo culms have a frequency of 0 to 4 vessels.mm-2, whith mean of vessels.mm-2, with long and narrow fibres with length average of 2.72 mm. The basic specific gravity was of 0.66 g.cm-3 and volumetric shrinkage of 15.41%. The total extractives and lignin contents increased as the temperature increase, and holocellulose content has been reduced. Since the temperature of 160 °C was a gain in durability natural bamboo and the dimensional stability of GLBT adhered to RF, but there was a decrease in the values of specific gravity and mechanicalproperties of the material
| Identifer | oai:union.ndltd.org:IBICT/oai:dspace2.ufes.br:10/5775 |
| Date | 26 February 2013 |
| Creators | Brito, Flávia Maria Silva |
| Contributors | Paes, Juarez Benigno, Fantuzzi Neto, Humberto, Vidaurre, Graziela Baptista, Oliveira, José Tarcísio da Silva, Arantes, Marina Donária Chaves |
| Publisher | Universidade Federal do Espírito Santo, Programa de Pós-Graduação em Ciências Florestais, UFES, BR, Ciências Florestais |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | text |
| Source | reponame:Repositório Institucional da UFES, instname:Universidade Federal do Espírito Santo, instacron:UFES |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds