Orientador: Julio Roberto Bartoli / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-14T01:31:00Z (GMT). No. of bitstreams: 1
Faria_TatianeDiasMarques_M.pdf: 2955450 bytes, checksum: 63c9a4b195b9577f64bd709603a63795 (MD5)
Previous issue date: 2008 / Resumo: Adesivos preparados com borracha termoplástica são de grande importância na indústria de adesivos sensíveis à pressão devido à sua grande versatilidade de processamento. Porém, geralmente estes adesivos apresentam desvantagens em ensaios em que temperaturas na faixa de 90º C são requeridas. Neste trabalho, foram preparados adesivos de borracha termoplástica com nanoargilas do tipo montmorilonita com duas organofilicidades diferentes, a fim de se estudar o desempenho das propriedades adesivas de peel, tack, shear e SAFT (Shear Adhesion Failure Temperature), além das propriedades de flamabilidade. Primeiramente, foram preparados masterbatches de resina hidrocarbônica e nanoargilas Cloisite® 20A e 25A (sendo a 20A mais organofílica) pelo processo de intercalação do fundido, através de extrusora dupla-rosca. Análises de difração de raios X e microscopia eletrônica de transmissão sugerem uma esfoliação da Cloisite® 20A na resina e uma intercalação da Closite® 25A. Depois, os masterbatches foram utilizados na preparação de compostos adesivos nas concentrações de 5 e 10 phr de nanoargilas, também em extrusora dupla-rosca. Ensaios de difração de raios X sugereriram a esfoliação das nanoargilas em todos os compostos adesivos, porém, pelas análises de microscopia eletrônica de transmissão, a amostra preparada com a Cloisite® 20A, na concentração de 10 phr, apresentou uma esfoliação relativamente maior. Ensaios dinâmico-mecânicos apresentaram significativo deslocamento da temperatura de transição vítrea (pico de tan d) para os adesivos preparados com a Cloisite® 20A, sugerindo a formação de nanocompósitos. Os módulos de armazenamento, na faixa de 70 a 93º C, obtidos com estes compostos adesivos, apresentaram também valores inferiores aos demais adesivos, sendo que a uma concentração de 10 phr o módulo foi o menor obtido e a uma concentração de 5 phr o módulo apresentou um valor intermediário. Os ensaios nas fitas adesivas demonstraram um maior equilíbrio de propriedades adesivas para o adesivo preparado com a Closite® 20A numa concentração de 5phr, apresentando este, módulo ótimo na faixa de temperatura de 70 a 93º C. Este adesivo manteve as propriedades de peel e tack próximas às do adesivo referência, melhorando significativamente as propriedades de shear a 70 e 93º C e SAFT. O ensaio de flamabilidade não foi conclusivo pois as amostras foram consideradas inflamáveis e houve muita variabilidade nos resultados obtidos para os tempos de queima. / Abstract: Adhesives prepared with thermoplastic rubber are very important for the pressure sensitive adhesives industry due to its easy processability. However, these adhesives are usually not indicated for applications in which temperature resistance around 90o C is required. In this study, thermoplastic rubber adhesives with nanoclays were prepared, in order to evaluate its adhesion performance: peel, tack, shear and SAFT. Moreover, the flammability properties are also going to be studied. Firstly, masterbatches of nanoclays Cloisite® 20A and 25A (being 20A more organophilic) and hydrocarbon resin were prepared through melt intercalation process, using a twin-screw extruder. Analysis through X ray difraction and transmission electronic microscopy suggests the exfoliation of Cloisite® 20A in the resin and the intercalation of Cloisite® 25A. After that, the masterbatches were used in the hot melt adhesives preparation, giving the nanoclays concentration of 5 and 10 phr. This process was also made in the twin-screw extruder. Analysis through X ray difraction showed again the exfoliation of the nanoclays in the adhesive, however, transmission electronic microscopy suggests that the sample prepared with Cloisite® 20A and concentration of 10phr presented the higher level of exfoliation. Dynamic-mechanical analysis showed a glass transition temperature shift (tan d peak) for the adhesives prepared with Cloisite® 20A, suggesting the formation of nanocomposites. The storage modulus of these adhesives, in the range from 70 to 93oC, showed values lower than the reference and other adhesives, being the adhesive with 20A and 10 phr the lowest modulus and the adhesive with 20A and 5 phr the intermediate value for the modulus. The testing done with the adhesive tapes, showed more balanced properties for the adhesive prepared with Cloisite® 20A and 5 phr, suggesting an optimal value for the modulus. This adhesive kept peel and tack properties close to the reference and showed improvements in properties like: 70 and 93oC shear and SAFT. Flammability testing was not conclusive because all samples were considered flammable and lots of variability was oberved in the burning times obtained. / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267172 |
Date | 14 August 2018 |
Creators | Faria, Tatiane Dias Marques |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Bartoli, Julio Roberto, 1954-, Ito, Edson Noriyuki, Peres, Leila |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 138 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds