Heterojunction bipolar transistors (HBT) based on SiGeC havebeen investigated. Two high-frequency architectures have beendesigned, fabricated and characterized. Different collectordesigns were applied either by using selective epitaxial growthdoped with phosphorous or by non-selective epitaxial growthdoped with arsenic. Both designs have a non-selectivelydeposited SiGeC base doped with boron and a poly-crystallineemitter doped with phosphorous. Selective epitaxial growth of the collector layer has beendeveloped by using a reduced pressure chemical vapor deposition(RPCVD) technique. The incorporation of phosphorous and defectformation during selective deposition of these layers has beenstudied. A major problem of phosphorous-doping during selectiveepitaxy is segregation. Different methods, e.g. chemical orthermal oxidation, are shown to efficiently remove thesegregated dopants. Chemical-mechanical polishing (CMP) hasalso been used as an alternative to solve this problem. The CMPstep was successfully integrated in the HBT process flow. Epitaxial growth of Si1-x-yGexCy layers for base layerapplications in bipolar transistors has been investigated indetail. The optimization of the growth parameters has beenperformed in order to incorporate carbon substitutionally inthe SiGe matrix without increasing the defect density in theepitaxial layers. The thermal stability of npn SiGe-based heterojunctionstructures has been investigated. The influence of thediffusion of dopants in SiGe or in adjacent layers on thethermal stability of the structure has also been discussed. SiGeC-based transistors with both non-selectively depositedcollector and selectively grown collector have been fabricatedand electrically characterized. The fabricated transistorsexhibit electrostatic current gain values in the range of 1000-2000. The cut-off frequency and maximum oscillation frequencyvary from 40-80 GHz and 15-30 GHz, respectively, depending onthe lateral design. The leakage current was investigated usinga selectively deposited collector design and possible causesfor leakage has been discussed. Solutions for decreasing thejunction leakage are proposed. <b>Key words:</b>Silicon-Germanium-Carbon (SiGeC),Heterojunction bipolar transistor (HBT), chemical vapordeposition (CVD), selective epitaxy, non-selective epitaxy,collector design, high-frequency measurement, dopantsegregation, thermal stability.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-3674 |
Date | January 2003 |
Creators | Suvar, Erdal |
Publisher | KTH, Mikroelektronik och informationsteknik, IMIT, Kista : Mikroelektronik och informationsteknik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-EKT, 1650-8599 ; 2003:5 |