Previous issue date: 2015-03-09 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Este estudo avaliou o efeito de diferentes tratamentos de superfície na resistência de união e adaptação marginal entre uma coroa de cerâmica Y-TZP e um material análogo à dentina. Foram confeccionadas 40 bases de um material resinoso análogo à dentina (NEMA grade G-10) para originar preparos padronizados. Estes foram usinados para simular um dente preparado para coroa total com término em chanfro, paredes de 6 graus de convergência e anatomia radicular. A porção radicular foi coberta com poliéter (Impregum - 3M ESPE) e incluída em poliuretano (F16 - Axson). Quarenta coroas cerâmicas IPS emax ZirCAD (Ivoclar - Vivadent) foram fabricadas pelo sistema CAD/CAM. Para o tratamento de superfície foram realizadas a silicatização, aplição de primer para zircônia e duas técnicas de vitrificação, sendo que estas representaram os grupos teste. As coroas foram aleatoriamente divididas em 4 grupos (n=10), conforme o tratamento de superfície: GS (Glaze Spray VITA AKZENT), condicionamento com ácido fluorídrico a 10% (HF) (1 min) + silanização (RelyX Ceramic Primer - 3M ESPE); GP (Glaze Pó/Líquido VITA AKZENT), condicionamento com HF a 10% (1 min) + silanização (RelyX Ceramic Primer - 3M ESPE); P: aplicação do primer (Signum Zirconia Bond - Heraeus Kulzer) e RS: jateamento com partículas de óxido de alumínio revestidas por sílica 30 μm (Rocatec Soft® 3M ESPE ) (silicatização) + silanização (RelyX Ceramic Primer - 3M ESPE). Em seguida, realizou-se a cimentação das coroas com o cimento autoadesivo Rely X U200 (3M ESPE), seguindo as recomendações do fabricante. Todas as amostras de cada grupo foram submetidas à ciclagem termomecânica (TC) (2.000.000 ciclos – 100 N, 4 Hz, 5 ºC – 55 ºC, tempo de permanência 60 s), com um pistão de aço inoxidável (Ø=4mm) no centro da superfície oclusal. Para avaliação da desadaptação marginal entre a coroa cimentada e o G-10, realizou-se a análise por estereomicroscópio (EM) (40x), fazendo-se 8 aferições para cada amostra e, por microscópio eletrônico de varredura (MEV). Para determinação da resistência a tração, foi realizado o ensaio mecânico numa máquina de ensaio universal (célula de carga de 1000 Kgf, v= 1mm/min) até o descolamento da coroa. Os dados de desadaptação marginal obtidos foram analisados estatisticamente (Teste Kruskal Wallis e de Dunn: p ˂ 0,05) e os dados de resistência de união foram analisados pelo teste Anova (um fator) e de Tukey (p ˂ 0,05). Os resultados de desadaptação marginal (média e desvio padrão) foram os seguintes GS (48,69±19,90ª μm); GP (65,48±42,57ª μm); P (156,0±113,3c μm) e RS (96,05±62,98b μm). Os resultados de resistência de união foram: GP (470,5±104,1ª μm); GS (416,8±170,2ª μm); P (342,1±109,7ab μm) e RS (208,9±110,0b μm). Através do estudo realizado concluiu-se que os grupos que tiveram menor desadaptação marginal foram GS e GP; os valores de resistência de união dos grupos GP e GS foram estatisticamente superiores aos valores de resistência de união do grupo RS e semelhante aos valores encontrados para grupo P. / This study evaluated the effect of different surface treatments on the bond strength and marginal adaptation from a Y-TZP ceramic crown and a material similar to dentin. Were made 40 bases in a similar resinous material to dentin (NEMA G-10 grade) to give standardized preparations. These were machined to simulate a tooth prepared for full crown in bevel, walls of 6 degrees of convergence and root anatomy. The root portion was covered with polyether (Impregum - 3M ESPE) and included in polyurethane (F16 - Axson). Forty crowns IPS emax ZirCAD (Ivoclar - Vivadent) were fabricated by CAD / CAM system. For the surface treatment were carried out silica coating, application of primer to zirconia and two glazing techniques, and these test groups represented. The crowns were randomly divided into 4 groups (n = 10), as the surface treatment: GS (VITA Akzent Glaze Spray), etching with hydrofluoric acid 10% (HF) (1 min) + silanization (RelyX Ceramic Primer - 3M ESPE ); GP (Glaze Powder / Liquid VITA Akzent), etching with HF 10% (1 min) + silanization (RelyX Ceramic Primer - 3M ESPE); P: primer (Signum Zirconia Bond - Heraeus Kulzer) and RS: sandblasting with aluminum oxide particles coated with silica 30 microns (Rocatec SOFT® 3M ESPE) (silica coating) + silanization (RelyX Ceramic Primer - 3M ESPE). Then was held the cementation of crowns with the self-adhesive cement Rely XU200 (3M ESPE), following the manufacturer's recommendations. All samples from each group were submitted to thermomechanical cycling (TC) (2,000,000 cycles - 100 N, 4 Hz, 5° C - 55° C, residence time 60 sec) with a stainless steel piston (= Ø 4mm) the center of the occlusal surface. Then the analysis by stereomicroscope (MS) (40x) and scanning electron microscope (SEM) to evaluate the marginal leakage between the cemented crown and the G-10 was held. To determine the tensile strength, the mechanical test was performed in a universal testing machine (load cell of 1000 kgf, v = 1 mm / min) until the detachment of the crown. Data marginal misfit obtained were analyzed statistically (Kruskal Wallis and Dunn: p ˂ 0.05) and bond strength data were analyzed by ANOVA (one factor) and Tukey (p ˂ 0.05). The results of marginal leakage (mean and standard deviation) were as follows GS (48.69 ± 19,90ª μm); GP (65.48 ± 42,57ª μm); P (156.0 ± 113,3c μm) and RS (96.05 ± 62,98b μm). The results of bond strength were: GP (470.5 ± 104,1ª μm); GS (416.8 ± 170,2ª μm); P (342.1 ± 109,7ab μm) and RS (208.9 ± 110,0b μm). Through the conducted study showed that the groups that had less marginal discrepancy were GS and GP; values of bond strength of GP and GS groups were statistically superior to the values of bond strength of the RS group and similar to values found for group P.
Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/101 |
Date | 09 March 2015 |
Creators | Antunes, Monize Carelli Felipe |
Contributors | Leite, Fabíola Pessôa Pereira, Leite, Fabíola Pessôa Pereira, Kimpara, Estevão Tomomitsu, Carvalho, Rodrigo Furtado de |
Publisher | Universidade Federal de Juiz de Fora, Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds