Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015. / Made available in DSpace on 2016-02-16T03:07:09Z (GMT). No. of bitstreams: 1 337792.pdf: 125470577 bytes, checksum: a2ee7ce55e3638fa0777a1659a72e495 (MD5) Previous issue date: 2015 / O objetivo deste trabalho foi avaliar in vitro a adaptação marginal e a interna de inlays MOD confeccionadas com técnicas restauradoras semidiretas e indiretas. Para tanto, confeccionou-se um modelo metálico mestre com preparo cavitário Classe II MOD, do qual foram obtidas restaurações inlays por meio de diferentes técnicas restauradoras. Os grupos foram formados de acordo com o material e a técnica restauradora (n=10): Grupo G1 (CAD/CAM): fresagem de blocos pré-fabricados para CAD/CAM (IPS e.max CAD - Ivoclar Vivadent); Grupo G2 (Prensada): prensagem à quente de uma cerâmica vítrea à base de dissilicato de lítio (IPS e.max Press - Ivoclar Vivadent); Grupo G3 (SD Poliéter): resina composta semidireta utilizando um modelo de poliéter; Grupo G4 (SD Gesso tipo V): resina composta semidireta utilizando um modelo de gesso tipo V; Grupo G5 (SD Intraoral): resina composta semidireta confeccionada diretamente sobre o preparo dental. O ajuste interno foi realizado em todas as restaurações. Procedeu-se com a simulação da cimentação por meio da técnica do cimento-análogo. A adaptação marginal foi avaliada após a simulação da cimentação em estereomicroscópio (100x). Avaliou-se a adaptação interna pela mensuração da espessura da película de silicone no estereomicroscópio (80x). Tanto a adaptação marginal quanto a adaptação interna foram avaliadas com relação à adaptação geral e de acordo com a região do preparo. Os resultados foram submetidos ao teste de ANOVA one-way, Tukey e Games-Howell. Observou-se que houve diferença significativa na adaptação marginal geral entre as técnicas restauradoras, sendo que os menores valores foram obtidos nos grupos G1 (CAD/CAM = 87,33 µm), G3 (SD Poliéter = 89,22 µm) e G5 (SD Intra-oral = 74,31 µm). Os grupos G3 (75,61 µm) e G5 (68,38 µm) apresentaram os menores valores estatisticamente significativos de adaptação interna geral. Houve diferença entre as técnicas restauradoras na adaptação marginal e interna de acordo com a região do preparo, porém não houve diferença na adaptação marginal obtida na análise visual direta com a técnica do cimento-análogo. Diante disso, a adaptação marginal foi mais precisa nas restaurações obtidas pela técnica semidireta intraoral, porém apenas em relação à técnica semidireta (gesso tipo V) e à cerâmica prensada. Já a adaptação interna foi mais precisa nas restaurações obtidas pelas técnicas de resina composta semidireta do poliéter e intraoral.<br> / Abstract : The objective of this study was to evaluate the marginal and internal adaptation of MOD inlays fabricated with semi-direct and indirect restorative techniques. Therefore, a master metallic model was fabricated with a Class II MOD preparation, which inlays restorations were obtained from different restorative techniques. The groups were divided according to the material and the restorative technique (n = 10): G1 (CAD / CAM): Milling prefabricated blocks for CAD/CAM (IPS e.max CAD - Ivoclar Vivadent); G2 (Pressed): hot-pressed technique of a glass-ceramic-based lithium disilicate (IPS e.max Press - Ivoclar Vivadent); G3 (SD polyether): semidirect composite resin using a polyether cast; G4 (SD gypsium type V): semidirect composite resin using a gypsium type V cast; G5 (SD Intraoral): semidirect composite resin made directly on the tooth preparation. The internal adjustment was performed in all restorations. It proceeded to the cementation simulation by means of replica technique. The fit was analyzed after the simulation of cementation in stereomicroscope (100x). The analysis of internal adaptation was done by measuring the thickness of the silicon film in stereomicroscope (80x). Both the marginal adaptation and the internal adaptation were evaluated for general adaptation and the adaptation according to the restoration area. The results were analyzed by one-way ANOVA test, Tukey and Games-Howell. It was observed that the restorative techniques showed significant differences in marginal adaptation of inlays. The lowest values were obtained in G1 (CAD/CAM = 87,33 µm), G3 (SD polyether = 89,22 µm) and G5 (SD Intraoral = 74,31 µm). The G3 (75,61 µm) and G5 (68,38 µm) had the lowest internal adaptation values. There was a significant difference between the materials on the marginal and internal fit according to the restoration area. In addition, there was no difference observed when comparing the marginal adaptation obtained in the direct visual analysis and the replica technique. Therefore, the fit was more accurate in restorations obtained by semidirect intraoral technique, but only in relation to semidirect on type V cast and pressed ceramic. The internal adaptation was more accurate in restorations obtained by semidirect intraoral and polyether techniques.

Orientador: Carlos Rocha Gomes Torres / Banca: Eduardo Bresciani / Banca: Taciana Marco Ferraz Caneppele / Banca: Roberta Tarkany Basting Höfling / Banca: Sérgio Ricardo Garcia Badini / Resumo: O objetivo deste estudo foi analisar a efetividade de polimerização, a adaptação marginal e interna de resinas compostas para dentes posteriores, empregando diferentes matrizes associadas ao envelhecimento artificial. Cento e vinte incisivos bovinos foram cortados e desgastados para simular dentes posteriores, nos quais foram realizados preparados de Classe II, com o ângulo cavosuperficial gengival em dentina. As cavidades tinham 6 mm de altura (ocluso-cervical), 3 de largura (vestibulo-lingual) e 1,5 de profundidade (mesio-distal). Os espécimes foram divididos em seis grupos de acordo com o material restaurador utilizado: GrandioSO (Voco)- convencional incremental, G-aenial universal flo (GC)- fluída incremental, Xtra fil (Voco)- convencional com inserção em bloco, X-tra base (Voco)- fluída com inserção em bloco, Venus Bulk Fill (Kulzer)- fluída com inserção em bloco e SureFil SDR (Dentsply)- fluída com inserção em bloco. As resinas fluídas com inserção em bloco foram inseridas em incremento de 4 mm e receberam uma cobertura oclusal de 2 mm utilizando a resina GrandioSO, com exceção da X-tra fil que foi coberta com uma camada adicional do mesmo material. Nos demais grupos foi utilizada uma técnica incremental de 2 mm. Metade dos espécimes foi restaurada com matriz metálica e a outra metade com matriz de poliéster. O percentual de polimerização foi mensurado através da dureza Knoop e da relação dureza base/topo. A média da largura das fendas marginais presentes nas margens de cada restauração foi calculada após medição, em micrometros, no microscópio óptico (100x). Os espécimes foram submetidos à ciclagem mecânica (500,000 ciclos) e térmica (1,000 ciclos) e a fenda marginal foi avaliada novamente. Para fenda interna, os espécimes foram seccionados em uma cortadeira de precisão e o comprimento, em milímetros, da parede gengival que apresentava fenda foi mensurado no microscópio óptico... / Abstract: The aim of this study was to analyze the effectiveness of cure, marginal and internal adaptation of composite resins for posterior teeth using different matrices bands associated with artificial aging. One hundred and twenty bovine incisors were cut and flattened in order to simulate posterior teeth, and then were prepared for class II cavities with gingival cavosurface margin in dentin. Cavities had 6 mm height (occluso-cervical), 3 mm width (bucco-lingual) and 1.5 mm deep (mesio-distal). Specimens were divided into six groups according to the restorative material: GrandioSO (Voco)- conventional, G-aenial universal flo (GC)- flowable, X-tra fil (Voco)- conventional bulk, X-tra base (Voco)- flowable bulk, Venus Bulk Fill (Kulzer)- flowable bulk, and SureFil SDR (Dentsply)- flowable bulk. Bulk-fill composites were placed in single increment of 4mm and received a 2mm occlusal coverage of GrandioSO, with the exception of X-tra fil which was covered with a layer of the same material. The remmaing groups were restored in 2 mm incremental technique. Half of the specimens were restored with metallic and the other half with polyester matrix. Effectiveness of cure was measured by Knoop hardness and the bottom/top hardness ratio was evaluated. The average width of marginal gaps present in the restoration was calculated after optical microscope measuring (100x), in microns. The specimens were subjected to mechanical (500.000 cycles) and thermal cycling (1.000 cycles) and marginal gap was evaluated again. For internal adaptation, the specimens were sectioned and the gap length, in millimeters, present on the gingival wall was measured in an optical microscope. The percentage of gap length in relation to the total length of the wall was also calculated. Data were analyzed with three and two-way ANOVA and Tukey's test. Regarding effectiveness of cure, significant differences were observed for resin... / Doutor

Orientador: Carlos Augusto Pavanelli / Banca: Leonardo Buso / Banca: Marco Antonio Bottino / Resumo: Este estudo avaliou a discrepância marginal (DM) e interna (DI) de coroas totais cerâmicas fabricadas pelo sistema CAD/CAM Cerec inLab, frente a três diferentes términos cervicais. A hipótese nula foi que o tipo de término não influencia a DM e DI das coroas. A partir de três troquéis metálicos com distintos términos cervicais, foram fresadas trinta coroas cerâmicas (ProCad/Ivoclar Vivadent) (n=10): CI) chanfro inclinado; CL) chanfro largo e O) ombro arredondado. Para análise da DM, mensurou-se, em 50 pontos, a distância entre a margem externa de cada coroa à margem do término cervical do respectivo troquel metálico. Utilizando a técnica da réplica, avaliou-se a DI de cada coroa em 12 pontos igualmente distribuídos por regiões: término (T), axial (A) e oclusal (Ocl). As mensurações foram realizadas em microscópio óptico (250x). Os dados obtidos ('mü'm) foram submetidos aos testes estatísticos ANOVA e de Tukey (5%). Os resultados demonstraram que grupo O (28,24'mais ou menos'11,42'mü'm) gerou valores de DM significativamente inferiores (p=0,001) aos dos grupos CI (99,92'mais ou menos'18,32'mü'm) e CL (64,71'mais ou menos'25,64'mü'm), os quais diferiram estatisticamente entre si. A análise da DI demonstrou que o grupo CL (183,01'mais ou menos'62,82'mü"m) apresentou valores inferiores (p=0,0014) aos demais grupos: CI (216,26'mais ou menos'83,23 'mü'm) e O (219,12'mais ou menos'87,24'mü'm), os quais foram semelhantes entre si. Observou-se também que a DI variou entre as regiões mensuradas (p=0,0001). A hipótese nula foi rejeitada. Baseado nos resultados pôde-se concluir que, apesar das diferenças estatísticas observadas entre os grupos, os três términos cervicais geraram coroas com valores de DM e DI aceitáveis clinicamente. / Abstract: This study evaluated the marginal discrepancy (MD) and internal (ID) of ceramic crowns manufactured by the CAD/CAM system Cerec inLab, varying the finish line. The null hypothesis was that the preparations won't influence the MD and ID of the crowns. From three metallic dies with different finish lines, thirty ceramic crowns (ProCad/Ivoclar Vivadent) were machined (n=10): TC) tilted chamfer; LC) large chamfer and RS) rounded shoulder. For MD analysis, were measured, in 50 points, the distance between each crown extern edge to the edge of the cervical preparation on the respective metallic die. Using the replica technique, it was evaluated the ID of each crown at 12 points equally distributed between the regions: end (E), axial (A) and oclusal (Ocl). The mensurations were done in optical microscope (250x). The data obtained ('mü'm) were submitted to the statistical tests ANOVA and Tukey (5 %). The results demonstrated that the group RS (28,24 'mais ou menos'11,42'mü'm) produced MD values smaller (p=0,001) than the groups TC (99,92'mais ou menos'18,32'mü'm) and LC (64,71'mais ou menos'25,64 'mu'm), which, between them, differed statistically. The analysis of ID demonstrated that the group LC (183,01'mais ou menos'62,82 'mü'm) presented values lower (p=0,0014) than TC (216,26'mais ou menos'83,23'mü'm) and RS (219,12'mais ou menos'87,24 'mü'm), which were similar between them. It was also noticed that ID varied between the measured regions (p=0.0001). The null hypothesis was rejected. It was concluded that, in spite of the statistical differences observed between the groups, the three cervical finish lines produced crowns with MD and ID values clinically acceptance. / Mestre

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2010 / Made available in DSpace on 2012-10-25T14:16:03Z (GMT). No. of bitstreams: 1 278777.pdf: 999442 bytes, checksum: 3470ad25d31030c307e5553fb536bd39 (MD5) / O objetivo deste estudo foi avaliar in vitro a influência de três diferentes métodos de confecção de facetas cerâmicas na adaptação marginal, antes e após o ajuste, e na adaptação interna, após o ajuste. Dez incisivos centrais superiores artificiais foram preparados com espessura uniforme de 0,7 mm, término cervical e proximal em chanfro e sem redução incisal. Para cada dente preparado, foram preparadas três facetas, de acordo com o método de confecção, totalizando 30 facetas (10 por método): G1 - método de aglutinação (modelo refratário); G2 - método da cerâmica injetada (IPS Empress); G3 - método computadorizado (CEREC). A adaptação marginal foi avaliada através da medição do valor máximo da discrepância entre a margem da restauração e a margem do preparo dental e a adaptação interna através da medição da espessura de um silicone de adição (Fit Checker II, GC), utilizado para simular a cimentação. Todas as imagens foram capturadas por um microscópio óptico, e as medições realizadas pelo programa Image-Pro Plus. Não houve diferença significativa entre os grupos em relação à adaptação marginal antes (G1: 74,22 ± 13,16 µm; G2: 67,98 ± 10,69 µm; G3: 73,85 ± 9,92 µm) e após o ajuste (G1: 36,05 ± 8,28 µm; G2: 36,61 ± 3,68 µm; G3: 39,56 ± 4,46 µm). Uma redução significativa nos valores da discrepância marginal após o ajuste interno das restaurações pode ser observada em todos os grupos. Em relação à adaptação interna, enquanto na secção vestíbulo-palatal o G3 apresentou valores de espessura de película interna maiores do que os outros dois grupos, na secção mésio-distal os três grupos foram estatisticamente diferentes (G3 > G2 > G1). Em conclusão, o presente estudo demonstrou que o método de confecção não influenciou na adaptação marginal das facetas cerâmicas. O método computadorizado apresentou maiores valores de espessura interna. Entretanto, todos os valores estão dentro dos limites clinicamente aceitáveis. O ajuste interno das facetas cerâmicas reduziu de forma significativa a discrepância marginal sugerindo que as facetas cerâmicas devem ser ajustadas antes da cimentação.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2017. / Made available in DSpace on 2017-05-31T14:18:23Z (GMT). No. of bitstreams: 1 345802.pdf: 2808706 bytes, checksum: b1c922798dff25394a856877feda3b8c (MD5) Previous issue date: 2017 / Apesar do uso da zircônia em diversas aplicações técnicas e biomédicas, após 20 anos de pesquisa, a possibilidade de este material envelhecer em função, fenômeno conhecido como degradação em baixas temperaturas (DBT), continua sendo um assunto em controvérsia. O objetivo deste estudo "in vitro" foi analisar a influência do envelhecimento no grau de adaptação de coroas bilaminares feitas em Y-TZP (Z-CAD HD, Metoxit AG, Suíça) e recobertas com cerâmica (E-max, Ivoclar Vivadent, Liechtenstein) e coroas monolíticas (Z-CAD HTL, Metoxit AG, Suíça), assim como a influência do agente de cimentação (Rely X U200, 3M Espe, EUA) no grau de adaptação marginal dessas peças cerâmicas. Quarenta e oito corpos de prova foram usinados em aço inoxidável simulando um primeiro pré-molar inferior que receberia uma coroa protética. Os corpos de prova foram divididos aleatoriamente em quatro grupos com 12 espécimes cada e, após, foram confeccionadas as seguintes coroas: (1) coroas bilaminares (infraestrutura em zircônia e cerâmica de cobertura) cimentadas; (2) coroas bilaminares (infraestrutura em zircônia e cerâmica de cobertura) não cimentadas; (3) coroas monolíticas em zircônia não cimentadas; (4) coroas monolíticas em zircônia cimentadas. Em relação ao envelhecimento, todos os grupos foram submetidos a dois tempos diferentes: T1: nenhum tratamento de envelhecimento e armazenamento em ambiente seco e temperatura ambiente. T2: tratamento de envelhecimento artificial em autoclave, sob uma atmosfera úmida a 131°C e pressão de 1,7 bares durante 5 horas. A adaptação marginal foi avaliada pela medida da discrepância marginal absoluta das coroas realizadas, utilizando um microscópio eletrônico de varredura. A difração de raios X foi utilizada para calcular a fração de fase monoclínica e monitorizar a DBT. Tanto as coroas bilaminares como as monolíticas apresentaram discrepâncias marginais verticais semelhantes, entretanto, não foram observadas diferenças significativas na adaptação marginal entre os grupos testados (p= 0,41). Também não foram observadas diferenças na discrepância marginal quanto à presença ou não de agente de cimentação e quando o envelhecimento artificial foi empregado (p= 0,17). A intensidade do pico da fase monoclínica a tetragonal aumentou de 1,2 a 3% para as coroas bilaminares e de 0,8 a 1,6% para as coroas monolíticas. As coroas monolíticas e bilaminares de zircônia confeccionadas mediante tecnologia CAD/CAM apresentaram gaps marginais que estavam dentro de uma faixa aceitável de discrepância marginal. A cimentação não demonstrou ter uma influência significativa no ajuste marginal. A adaptação marginal não foi influenciada pelo envelhecimento, e este não levou a uma transformação significativa da fase tetragonal para a fase monoclínica. Estudos "in vitro" demonstraram que a tecnologia CAD / CAM pode produzir estruturas de zircônia com um ajuste marginal clinicamente aceitável. Com base na ausência de estudos científicos longitudinais, não parece claro a relação entre o ajuste marginal e a consequente degradação do envelhecimento.<br> / Abstract : Despite the use of Yttria Tetragonal Zirconia Polycrystal (3Y-TZP) in several technical and biomedical applications, after over 20 years of research, the possibility that this material can aged in function, a phenomenon known as low temperature degradation (LTD), remains a subject under discussion. The aim of this "in vitro" research was to analyze the influence of aging on the degree of adaptation of Y-TZP based crowns, either monolithic (Z-CAD HTL, Metoxit AG, Tayngen, Switzerland) or ceramic coating (Z-CAD HD, Metoxit AG, Tayngen, Switzerland; E-max, Ivoclar Vivadent) as well as the influence of cementation (Rely X U200, 3M Espe) on the fit of the restorations. Forty-eight standardized dies will be prepared from stainless steel, to receive a ceramic crown. The specimens were randomly divided into 4 groups of 12 specimens each: (1) bilayer crown (zirconium structure with ceramic coating) cemented; (2) bilayer crown (zirconium structure with ceramic coating) without cement; (3) monolithic zirconia crown without cement; (4) cemented monolithic zirconia crown. All groups will be treated as a function of aging, in 2 different times: T1: No aging treatment and stored in a dry place at room temperature; T2: Treatment of artificial aging (hydrothermally), in autoclave, under a humid atmosphere at 131 °C and pressure of 1,7 bar for 5 hours. Marginal adaptation will be evaluated by measuring the absolute marginal discrepancy of the ceramic crowns on the specimens, using a scanning electron microscope. The monoclinic-to-tetragonal (m/t) peak intensity ratio measured by x-ray diffraction was used to calculate the monoclinic phase fraction and monitor LTD. Both zirconia groups showed similar vertical marginal discrepancies, however, no significant differences (p= 0.41) in marginal adaptation were observed among the experimental groups. Moreover, no differences were observed in either group in marginal discrepancies between cementation process neither artificial aging (p= 0.17). The relative XRD peak intensity of the monoclinic to tetragonal phase increased for 1,2 to 3% for bilayer crowns and from 0,8 to 1,6% for monolithic crowns. Monolithic and bilayer CAD /CAM zirconia crowns showed marginal gaps that were within an acceptable range of marginal discrepancy. Cementation was not found to have a statistically significant influence on the marginal fit. Marginal adaptation was not influenced by aging, and this did not lead a significant transformation from tetragonal to monoclinic phase. ?In vitro? studieshave demonstrated that CAD/CAM technology can produce zirconia structures with a clinically acceptable marginal fit. Based on the lack of rigorous scientific longitudinal studies, it seems not clear the relationship between the marginal fit and the resulting degradation of aging.

Made available in DSpace on 2014-06-11T19:31:26Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-12-01Bitstream added on 2014-06-13T20:41:43Z : No. of bitstreams: 1 macedo_rp_dr_arafo.pdf: 474447 bytes, checksum: 4d9c167f257a4293018ed19aaa516902 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Neste trabalho, estudou-se a influência de quatro diferentes técnicas de inserção (Incremental, Única, Beta-quartzo e Pré-polimerizada) da resina composta fotoativada em dois tamanhos de cavidades classe II, no vedamento marginal, através de testes de infiltração de um agente corante. As cavidades foram preparadas em dentes molares humanos extraídos, com a parede cervical localizada em cemento. Os materiais (adesivo dentinário e resina composta) foram de uma mesma marca comercial. Realizadas as restaurações, os dentes foram submetidos à termociclagen (5o C e 55o C, durante 500 ciclo) e depois de adequadamente impermeabilizados, foram imersos em solução corante Rodamina a 5% por uma semana. Em seguida, os dentes foram cortados e avaliados, quanto à microinfiltração na interface parede gengival e material restaurador, por dois examinadores, segundo um critério pré-estabelecido (graus de 0 a 3). Após a análise dos resultados, foi possível concluir que: a técnica incremental em esmalte (Grupo 1B e 2B) foi a que apresentou os menores níveis de infiltração marginal, logo a que produziu o melhor vedamento marginal. A técnica incremental em cemento (Grupo 1C) apresentou resultados intermediários, não sendo estatisticamente diferente dos grupos 1B e 2B. A técnica com inserção de Beta Quartz Inserts (Grupos 1E e 2E), e técnica de inserção de pérolas pré-polimerizadas de resina (Grupos 1F e 2F) foram as menos efetivas em impedir a infiltração marginal. A confecção de um bisel chanfrado parece desempenhar importante papel na qualidade das margens das restaurações. / This study had the purpose of evaluating the influence of four different techniques of insertion of composite resin (Incremental, Single, Beta-quartz inserts nd Pre-cured) in two sizes of Class II cavities, regarding marginal sealing when submitted to leakage tests using a dying agent. Cavities were prepared in extracted human molars, presenting the cervical wall in the cementum area. Materials used (adhesive and composite resin) were from the same manufacturer. After the restorations were done, teeth were subjected to thermo cycling (5º C e 55º C, for 500 cycles), and then carefully coated with nail polish before submersed in a 5% Rodamine, for the period of one week. Teeth were then sectioned and evaluated to microleakage, at the interface gingival wall and restorative material, by two evaluators following pre-determined criteria (from 0 to 3). After analyzing the results it was possible to conclude that: incremental technique in enamel (Group 1B e 2B) presented the lowest levels of marginal leakage or the best marginal sealing. The incremental technique for the cementum group (Group 1C) presented intermediary results, not statistically different from group 1B e group 2B. The techniques using Beta Quartz Inserts (Groups 1E e 2E), and pre-cured pellets of resin (Groups 1F e 2F) were the least effectives in preventing the marginal leakage. The preparation of a chamfered bevel seemed to play an important role in the quality of the margins of the restorations.

Made available in DSpace on 2016-12-09T13:52:21Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-03-05. Added 1 bitstream(s) on 2016-12-09T13:55:26Z : No. of bitstreams: 1 000867914.pdf: 1125966 bytes, checksum: 0e913723d2a96b546859d0335ca9badf (MD5) / Este estudo objetivou analisar a precisão de diferentes métodos de união de transferentes em moldagem sobre implantes utilizando guias multifuncionais em reabilitações orais de maxilas com implantes hexágono externo. Para as técnicas de moldagem com dois tipos de guia multifuncional (com e sem patalo) foi comparado diferentes métodos de união dos transferentes: transferentes unidos com metal e resina acrílica, transferentes unidos apenas com resina acrílica e transferentes sem união. Uma barra metálica passiva fabricada sobre o modelo mestre foi parafusado nos modelos de gesso no análogo A e realizado a mensuração 3 vezes da fenda presente nos análogos C e D. Posteriormente a barra é parafusado no análogo D e realizada a mensuração 3 vezes da fenda nos análogos A e B, utilizando um programa de análise de imagens (Leica QWin) que recebeu as imagens de uma câmara de vídeo acoplada a uma lupa Leica (100X). Após verificação da distribuição e da homocedasticidade dos dados, métodos estatísticos (α=0,05) foram empregados para avaliar a influência das variáveis independentes. De maneira geral, os modelos geraram maiores desajustes marginais em relação ao modelo mestre, independentemente da técnica de união dos transferentes. Porém, só houve diferenças estatísticas quando comparado à técnica de moldagem OM=203,04µm (guia multifuncional com palato aberto e transferentes unidos com metal e resina acrílica) com às técnicas de moldagem PR=151,61µm (guia multifuncional com cobertura de palato e transferentes unidos com resina acrílica) e com o modelo Mestre (MM=142,78µm). Considerando as limitações desse estudo pode-se sugerir que a utilização da técnica de moldagem OM gera os modelos menos precisos. / This study analyze in vitro the accuracy of different union transfers methods in impressiom using multifunctional guides for prosthetic rehabilitation in a toothless jaw with external hexagon implants installed. For the impression techniques with two types of multifunctional guide (palate coverage and open palate) it was compared different methods of union of the square transfers: metal splinted transfers, acrylic resin splinted transfers and without splinted transfers. A metal structure fabricated on the master model with passive fit was screwed in the models obtained, on A analogue while measurements were made 3 times on analogs C and D and when screwed into analog D measurements were made 3 times in analogues A and B, by a image analysis software (Leica QWin) that received the images from a video camera attached to a Leica magnifier (100X). After verification of distribution and homoscedasticity data, statistical methods (α = 0.05) were used to assess the influence of the independent variables. In general, larger models generated fringe displacement in relation to the master model, irrespective of splint techniques. But only exist statistical differences when compared the impression technique OM = 203,04µm (multifunctional guide with open palate and transfers splinted with metal and acrylic resin) with impression technique PR = 151,61µm (multifunctional guide with coverage palate and transfers splinted with resin acrylic) and the master model (MM = 142,78µm). Considering the limitations of this study may suggest that the use of OM molding technique generates less accurate models.

Orientador: José Roberto Cury Saad / Banca: Adair Luís Stefanello Busato / Banca: Alcebíades Nunes Barbosa / Banca: Maria Salete Machado Cândido / Banca: Welingtom Dinelli / Resumo: Neste trabalho, estudou-se a influência de quatro diferentes técnicas de inserção (Incremental, Única, Beta-quartzo e Pré-polimerizada) da resina composta fotoativada em dois tamanhos de cavidades classe II, no vedamento marginal, através de testes de infiltração de um agente corante. As cavidades foram preparadas em dentes molares humanos extraídos, com a parede cervical localizada em cemento. Os materiais (adesivo dentinário e resina composta) foram de uma mesma marca comercial. Realizadas as restaurações, os dentes foram submetidos à termociclagen (5o C e 55o C, durante 500 ciclo) e depois de adequadamente impermeabilizados, foram imersos em solução corante Rodamina a 5% por uma semana. Em seguida, os dentes foram cortados e avaliados, quanto à microinfiltração na interface parede gengival e material restaurador, por dois examinadores, segundo um critério pré-estabelecido (graus de 0 a 3). Após a análise dos resultados, foi possível concluir que: a técnica incremental em esmalte (Grupo 1B e 2B) foi a que apresentou os menores níveis de infiltração marginal, logo a que produziu o melhor vedamento marginal. A técnica incremental em cemento (Grupo 1C) apresentou resultados intermediários, não sendo estatisticamente diferente dos grupos 1B e 2B. A técnica com inserção de Beta Quartz Inserts (Grupos 1E e 2E), e técnica de inserção de pérolas pré-polimerizadas de resina (Grupos 1F e 2F) foram as menos efetivas em impedir a infiltração marginal. A confecção de um bisel chanfrado parece desempenhar importante papel na qualidade das margens das restaurações. / Abstract: This study had the purpose of evaluating the influence of four different techniques of insertion of composite resin (Incremental, Single, Beta-quartz inserts nd Pre-cured) in two sizes of Class II cavities, regarding marginal sealing when submitted to leakage tests using a dying agent. Cavities were prepared in extracted human molars, presenting the cervical wall in the cementum area. Materials used (adhesive and composite resin) were from the same manufacturer. After the restorations were done, teeth were subjected to thermo cycling (5º C e 55º C, for 500 cycles), and then carefully coated with nail polish before submersed in a 5% Rodamine, for the period of one week. Teeth were then sectioned and evaluated to microleakage, at the interface gingival wall and restorative material, by two evaluators following pre-determined criteria (from 0 to 3). After analyzing the results it was possible to conclude that: incremental technique in enamel (Group 1B e 2B) presented the lowest levels of marginal leakage or the best marginal sealing. The incremental technique for the cementum group (Group 1C) presented intermediary results, not statistically different from group 1B e group 2B. The techniques using Beta Quartz Inserts (Groups 1E e 2E), and pre-cured pellets of resin (Groups 1F e 2F) were the least effectives in preventing the marginal leakage. The preparation of a chamfered bevel seemed to play an important role in the quality of the margins of the restorations. / Doutor

Orientador: Francisco de Assis Mollo Junior / Banca: Pedro Cesar Garcia de Oliveira / Banca: José Maurício dos Santos Nunes Reis / Resumo: Este estudo objetivou analisar a precisão de diferentes métodos de união de transferentes em moldagem sobre implantes utilizando guias multifuncionais em reabilitações orais de maxilas com implantes hexágono externo. Para as técnicas de moldagem com dois tipos de guia multifuncional (com e sem patalo) foi comparado diferentes métodos de união dos transferentes: transferentes unidos com metal e resina acrílica, transferentes unidos apenas com resina acrílica e transferentes sem união. Uma barra metálica passiva fabricada sobre o modelo mestre foi parafusado nos modelos de gesso no análogo A e realizado a mensuração 3 vezes da fenda presente nos análogos C e D. Posteriormente a barra é parafusado no análogo D e realizada a mensuração 3 vezes da fenda nos análogos A e B, utilizando um programa de análise de imagens (Leica QWin) que recebeu as imagens de uma câmara de vídeo acoplada a uma lupa Leica (100X). Após verificação da distribuição e da homocedasticidade dos dados, métodos estatísticos (α=0,05) foram empregados para avaliar a influência das variáveis independentes. De maneira geral, os modelos geraram maiores desajustes marginais em relação ao modelo mestre, independentemente da técnica de união dos transferentes. Porém, só houve diferenças estatísticas quando comparado à técnica de moldagem OM=203,04µm (guia multifuncional com palato aberto e transferentes unidos com metal e resina acrílica) com às técnicas de moldagem PR=151,61µm (guia multifuncional com cobertura de palato e transferentes unidos com resina acrílica) e com o modelo Mestre (MM=142,78µm). Considerando as limitações desse estudo pode-se sugerir que a utilização da técnica de moldagem OM gera os modelos menos precisos. / Abstract:This study analyze "in vitro" the accuracy of different union transfers methods in impressiom using multifunctional guides for prosthetic rehabilitation in a toothless jaw with external hexagon implants installed. For the impression techniques with two types of multifunctional guide (palate coverage and open palate) it was compared different methods of union of the square transfers: metal splinted transfers, acrylic resin splinted transfers and without splinted transfers. A metal structure fabricated on the master model with passive fit was screwed in the models obtained, on A analogue while measurements were made 3 times on analogs C and D and when screwed into analog D measurements were made 3 times in analogues A and B, by a image analysis software (Leica QWin) that received the images from a video camera attached to a Leica magnifier (100X). After verification of distribution and homoscedasticity data, statistical methods (α = 0.05) were used to assess the influence of the independent variables. In general, larger models generated fringe displacement in relation to the master model, irrespective of splint techniques. But only exist statistical differences when compared the impression technique OM = 203,04µm (multifunctional guide with open palate and transfers splinted with metal and acrylic resin) with impression technique PR = 151,61µm (multifunctional guide with coverage palate and transfers splinted with resin acrylic) and the master model (MM = 142,78µm). Considering the limitations of this study may suggest that the use of OM molding technique generates less accurate models. / Mestre

Este estudo in vitro avaliou a microinfiltração marginal de restaurações de classe V em resina composta, preparadas utilizando-se três técnicas de preparo cavitário: Alta-rotação (AR), ultrassom (US) e a associação das duas técnicas (AR+US); e restauradas após a aplicação de 3 sistemas adesivos, sendo um de condicionamento total (Single-Bond (SB)) e dois autocondicionantes (Clearfil SE Bond (CSE) e Prompt L-Pop (POP)). Foram formados nove grupos (n=14) com terceiros molares que tiveram cavidades preparadas em suas faces vestibular e lingual, e foram classificados como: Grupo1- AR/SB; Grupo 2 AR/CSE; Grupo 3 AR/POP; Grupo 4 US/SB; Grupo 5 US/CSE; Grupo 6 US/POP; Grupo 7 AR+US/SB; Grupo 8 - AR+US/CSE; Grupo 9 - AR+US/POP. Após a aplicação do adesivo as cavidades foram preenchidas com resina composta Z250-3M ESPE e armazenadas em água destilada a 37°C durante 24 horas. Posteriormente, as restaurações foram polidas e os espécimes termociclados (1000 ciclos/ 5 e 55°C), impermeabilizados, imersos em solução de nitrato de prata 50% por 8 horas, seccionados em 3 fatias, imersos em solução fotoreveladora por 16 horas e observados em microscópio óptico acoplado à uma câmera de vídeo. As imagens foram digitalizadas e um software foi utilizado para medir a microinfiltração marginal dos lados oclusal e cervical. Foi realizado ANOVA Split-plot que demonstrou não haver diferenças estatisticamente significantes para os lados oclusal e cervical (p<0.05). A média dos lados oclusal e cervical foi realizada e os dados submetidos à ANOVA 2 Fatores (p=0,05), que mostrou haver diferenças estatisticamente significante entre os grupos, sendo necessário a utilização de um Teste de Tukey (p=0,05). Este teste mostrou não haver diferenças estatisticamente significantes entre os grupos restaurados com o sistema adesivo de condicionamento total (SB), no entanto, os grupos restaurados com os adesivos CSE e POP apresentaram menor microinfiltração para os grupos preparados com US e AR+US. O Grupo US/CSE apresentou o menor índice de microinfiltração e o AR/POP o maior. Nas condições deste estudo, podemos concluir que o método de preparo das cavidades pode alterar a microinfiltração marginal para restaurações que utilizem sistema adesivo autocondicionante. / This in vitro study compared the microleakage of class V resin composite restorations placed in cavities prepared with high-speed dental bur (AR), ultrasonic preparation devices (US) and high-speed dental bur plus ultrasonic preparation devices(AR+US), and restored using three different adhesive systems (One all etch Single Bond (SB) , and two Self-etch Clearfil CSE bond (CSE), Prompt L-Pop (POP)). Nine groups (n= 14) of human third molars each were prepared on the bucal and lingual surfaces were formed: Group 1- AR/SB; Group 2 AR/CSE; Group3 AR/POP; Group4 US/SB; Group 5 US/CSE; Group 6 US/POP; Group 7 AR+US/SB; Group 8 - AR+US/CSE; Group 9 - AR+US/POP. Specimens were built up with Z250/3M ESPE composite and stored in distilled water at 37°C for 24 hours. Then, the restorations were polished and the specimens thermocycling (1000 cycles/ 5°- 55°C), put impermeable, immersed in a 50% silver nitrate solution for 8 hours, sectioned, immersed in a photographic developer solution at darkness for 16 hours, and analyzed for leakage at the oclusal and cervical interface using an optical microscope connected to a video camera. The images were digitalized and software was utilized for microleakage assessment. Upon analyzing the results using a Split-plot ANOVA no statistically significant differences (p<0,05) between the cervical and oclusal interfaces for all groups was observed. The average of the interfaces was held and a Two-Way ANOVA revealed differences in microleakage among the tested groups (p=0,05). Tukey Test for Multiple Comparisons (p=0,05) demonstrated no significant difference between the groups restored with total etch adhesive system (SB), the groups restored with CSE and POP showed the least microleakage for the group prepared with the US and AR/US. The group US/CSE had the lowest microleakage and the group AR/POP had the highest. In the conditions of this study, we can conclude that the method of cavity preparation may affect the microleakage when a selfetch adhesive system is used.