Orientador : Jacinta Enzweiler / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Geociencias / Made available in DSpace on 2018-07-28T19:42:19Z (GMT). No. of bitstreams: 1
Vendemiatto_MariaAparecida_M.pdf: 4921255 bytes, checksum: 8fa65f7fb2585244f582f44a3c2a5dba (MD5)
Previous issue date: 2001 / Resumo: Esta dissertação propõe um método simples de controle da qualidade de resultados, na análise de silicatos por espectrometria de fluorescência de raios X, baseado na expressão de Horwitz modificada (Hc = 0,01c0,8495 qual prevê como a precisão analítica Hc varia com a concentração do analitos. A expressão foi utilizada para calcular Hc de cada valor recomendado VR dos materiais de referência utilizados para avaliar a exatidão. O intervalo VR±Hc foi tomado como limite de aceitação dos resultados analíticos. Programas de determinação de elementos maiores (Si02, TiO2, A1203, Fe203, MnO, MgO, CaO, Na20, K2O, P2Os) em discos de vidro e de traços (Ba, Ce, Cr, Cs, Cu, Ga, La, Nb, Nd, Ni, Pb, Rb, Se, Sn, Sr, Th, U, V, Y, Zn e Zr) em pastilhas prensadas foram elaborados e os resultados analíticos de nove materiais de referência foram avaliados. A adoção do intervalo VR±Hc como critério de aceitação dos resultados foi útil para identificar deficiências e erros sistemáticos na calibração do espectrômetro e corrigi-Ios. Observou-se que os resultados dos elementos maiores facilmente atendem ao intervalo VR±Hc, enquanto para os elementos-traços, os resultados nem sempre caem naquele intervalo, especialmente quando a concentração é próxima do limite de detecção. Este efeito foi atribuído aos tempos de leitura (contagens) adotados e, também, às incertezas dos valores recomendados dos materiais de referência. A precisão foi medida com a análise de dez pastilhas prensadas e dez discos de vidro de uma amostra de referência interna (BAC). Os coeficientes de variação da maior parte dos resultados encontram-se entre 0,2 e 2,6%. Adicionalmente, o método de duplicação das amostras foi usado para avaliar a contribuição de cada etapa do processo analítico à precisão total. As etapas avaliadas foram a cominuição da amostra (homogeneização do material britado, quarteamento e moagem), a preparação dos discos de vidro e pastilhas prensadas e a medida instrumental. Para a maioria dos analitos (maiores e muitos traços), a cominuição é a etapa que mais contribui à incerteza analítica total, seguida da preparação dos discos de vidro ou pastilhas prensadas. Na faixa de menor concentração, isto é, para alguns elementos-traços, a precisão instrumental é a etapa cuja contribuição é dominante em relação às demais / Abstract: This dissertation proposes a simple method for quality control of results in silicate analysis by X-ray fluorescence spectrometry, based on the modified Horwitz expression, (Hc = 0,01c0,8495 which allows to foresee the analytical precision Hc according to the analyte concentration c. The expression was used to calculate Hc of each recommended value RV of the reference materials used to evaluate the accuracy. The interval RV±Hc was taken as limits to accept the analytical results. Analytical programs for determination of major elements (SiO2, Ti_, A12O3, F_O3, MnO, MgO, CaO, Na20, K2O, P20S) in glass disks and of traces (8a, Ce, Cr, Cs, Cu, Ga, La, Nb, Nd, Ni, Pb, Rb, Sc, Sn, Sr, Th, U, V, Y, Zn e Zr) in pressed pellets were prepared and analytical results of nine reference materials were evaluated. The interval RV±Hc as criterion for acceptance of results was useful to identify deficiencies and systematic errors of the spectrometer calibration, and to correct them. It was observed that results of major elements easily fall within the interval RV±Hc, while results of trace elements sometimes exceed it, specially when concentration is close to the detection limit. This effect was attributed to the counting times adopted for analysis and, also, to the uncertainties associated to the recommended values of the reference materials. The precision was measured by analysis of ten pressed pellets and ten glass disks of an in-house reference sample (BAC). The coefficients of variation of most results were between 0.2 and 2.6%. Additionally, the method of sample duplication was used to evaluate the contribution of each stage of the analytical process to the whole precision. Sample comminution (homogenisation of crushed material, quartering and grinding), is the step that contributes mostly to the whole analytical uncertainty, followed by glass disks and pressed pellets preparation. At the low level concentration, i.e., for some trace elements, the instrumental measurement represents the dominant contribution, in comparison to the others / Mestrado / Metalogenese / Mestre em Geociências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/286774 |
| Date | 08 February 2001 |
| Creators | Vendemiatto, Maria Aparecida |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Enzweiler, Jacinta, 1955-, Hinrichs, Ruth, Choudhuri, Asit |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Geociências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 75p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds