Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia. / Made available in DSpace on 2012-10-23T01:48:19Z (GMT). No. of bitstreams: 1
248356.pdf: 800328 bytes, checksum: 2cbd10e89943f6262ee950f18f7b0fee (MD5) / O objetivo deste estudo foi avaliar a resistência a fratura de 3 compósitos indiretos aplicados diretamente sobre abutments de Ti-6Al-4V, implanto suportados. Quarenta e oito abutments coroas integrados foram alocados aleatoriamente em 3 grupos. Os abutments foram submetidos à abrasão (sandblasting) e em seguida foram deixados em recipiente contendo etanol, por 5min no ultra-som. Depois de secos em condições ambientais, um molde personalizado foi utilizado para confecção de coroas idênticas (n=16 por grupo) deTescera (Bisco, Schaumburg,USA), Ceramage (Shofu, Kyoto ,Japan), e Diamond Crown (DRM Research Laboratories,Braford, CT,USA). As coroas foram fabricadas de acordo com as instruções do fabricante. As coroas foram carregadas mecanicamente até a fratura através de um identador posicionado na ponta de uma das cúspides com uma velocidade avaliada em 1mm/min. Em seguida a análise das fraturas foi realizada através de estereomicroscopia e microscópico eletrônico de varredura. ANOVA, com nível de significância 95% e Tukey`s post-hoc para comparações múltiplas foram utilizados para análise estatística. Os resultados de resistência à fratura com este tipo de carga (single-load) foram: Tescera (1130 ± 105Na), Ceramage (1099 ± 105Na), e Diamond Crown(1155 ± 105Na) (p> 0,85). A análise pela estereomicroscopia mostrou dois modos distintos de fratura das cúspides, com ou sem exposição do abutment. Fraturas sem exposição do abutment ocorreram em aproximadamente 80% das amostras de Tescera, 60% das amostras de Ceramage e 40% das amostras de Diamond. Análise das fraturas através de microscópio eletrônico de varredura (MEV) mostrou múltiplas propagações das trincas em direção a região cervical da coroa, abaixo da região de deformação plástica onde o identador contactava. Uma redução na quantidade de vazios (bolhas) foi observada na microestrutura do Tescera quando comparado com os outros materiais compósitos. Todos os compósitos apresentaram alta resistência à fratura com os valores excedendo a função oclusal normal.
The purpose of this study was to test the strength to failure of three indirect composite materials directly applied onto Ti-6Al-4V implant abutments. 48 locking taper abutments were randomly allocated to three groups and were cleaned in ethanol in an ultrasonic bath for 5 minutes. After drying under ambient conditions, the abutments were grit-blasted and a custom 4-cusp molar crown mold was utilized to produce identical crowns (n=16 per group) of Tescera (Bisco, Schaumburg, USA), Ceramage (Shofu, Kyoto, Japan), and Diamond Crown (DRM Research Laboratories, Bran ford, CT,USA). The crowns were produced according to the manufacturer's instructions. The crowns were loaded to failure by an indenter placed at one of the cusp tips at a 1mm/min rate. Subsequently, fracture analysis was performed by means of stereomicroscopy and scanning electron microscopy. One-way ANOVA at 95% significance level and Tukey's post-hoc multiple comparisons were utilized for statistical analysis. The single load to failure results were: Tescera (1130 ± 105Na), Ceramage (1099 ± 105Na), and Diamond Crown (1155 ± 105Na) (p > 0.85). Stereomicroscopy analysis showed two distinct failure modes, where the loaded cusp failed either with or without abutment exposure. Fractures without abutment exposure comprised ~80% for Tescera, ~60% for Ceramage, and ~40% for Diamond crown samples. SEM analysis of the fractures showed multiple crack propagation towards the cervical region of the crown below a region of plastic deformation at the indenter contact region. A reduced amount of micro structural voids were observed for Tescera compared to the other composite materials. All composite materials presented high strength to failure values which exceeded normal occlusion function.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/89704 |
| Date | January 2007 |
| Creators | Andriani Júnior, Wilson |
| Contributors | Universidade Federal de Santa Catarina, Cardoso, Antonio Carlos, Coelho, Paulo Guilherme |
| Publisher | Florianópolis, SC |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 46 f.| il., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds