We study a novel structure employing the woven continuous carbon fiber (CCF) epoxy composite with high electromagnetic (EM) shielding. The influences of wove type, number and angle of overlapped plates upon the shielding effectiveness (SE) of wove CCF epoxy composite are investigated. The minimum SE of the single, double, and triple plain or balanced twill woven CCF composite plates were measured to be as high as 50 dB, 60 dB, and 70 dB, respectively. More than 100 dB of SE was obtained for the triple overlapped plain wove CCF composite at frequency of 0.9 GHz. The weight percentage of single CCF composite plate required for electronic application was 4.8% only, which was less than one quarter of the carbon fiber (CF) content and the performance of SE was 10 dB higher in comparison with long CF filled liquid crystal polymer composites. The SE calculated theoretically is consistent with that measured by the experiment.
We have demonstrated a new woven CCF epoxy composite with high EM shielding. This work may lead to the development of effective shielding for plastic optical transceiver modules to prevent electromagnetic interference (EMI) for use in low cost and lightwave communication systems.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0627103-200602 |
| Date | 27 June 2003 |
| Creators | Hung, Wen-Chi |
| Contributors | Tzong-Lin Wu, Sheng-Lung Huang, Wen-Feng Hsieh, Wern-Shiarng Jou, Wood-Hi Cheng |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0627103-200602 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0024 seconds