Impact of carrier localization on recombination in InGaN quantum wells with nonbasal crystallographic orientations

The modern InGaN technology demonstrates high efficiencies only in the blue spectral region and low current operation modes. The growth of InGaN quantum wells (QWs) on nonbasal crystallographic planes (NBP) has potential to deliver high-power blue and green light emitting diodes and lasers. The emission properties of these QWs are largely determined by the localization of carriers in the minima of spatially inhomogeneous band potential, which affects the recombination dynamics, spectral characteristics of the emission, its optical polarization and carrier transport. Understanding it is crucial for increasing the efficiency of NBP structures to their theoretical limit. In this thesis, the influence of carrier localization on the critical aspects of light emission has been investigated in semipolar  and nonpolar  InGaN QWs. For this purpose, novel multimode scanning near-field optical microscopy configurations have been developed, allowing mapping of the spectrally-, time-, and polarization-resolved emission. In the nonpolar QW structures the sub-micrometer band gap fluctuations could be assigned to the selective incorporation of indium on different slopes of the undulations, while in the smoother semipolar QWs – to the nonuniformity of QW growth. The nanoscale band potential fluctuations and the carrier localization were found to increase with increasing indium percentage in the InGaN alloy. In spite to the large depth of the potential minima, the localized valence band states were found to retain properties of the corresponding bands. The reduced carrier transfer between localization sites has been suggested as a reason for the long recombination times in the green-emitting semipolar QWs. Sharp increase of the radiative lifetimes has been assigned to the effect of nanoscale electric fields resulting from nonplanar QW interfaces. Lastly, the ambipolar carrier diffusion has been measured, revealing ~100 nm diffusion length and high anisotropy. / <p>QC 20170919</p>

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-214599
Date January 2017
CreatorsIvanov, Ruslan
PublisherKTH, Optik och Fotonik, OFO, Stockholm
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationTRITA-FYS, 0280-316X ; 2017:53

Page generated in 0.0028 seconds