Flash vacuum pyrolysis of 2-(2-vinylstyryl)furan derivatives via electrocyclization followed by dehydrogenation will give 2-(2-naphthalen-2-yl)furan analogues, on the other hand, FVP of 2-(2-vinylstyryl)furan derivatives via electrocyclization followed by [1,5]-H shift will give 3-(2-furyl)-1,2-dihydronaphthalene analogues. FVP of 2-[2-(4-methoxyphenyl)vinyl]benzo[b]thiophene gave three products: trans-4-(2-benzo[b]thiophen-2-ylvinyl)phenol, benzo[b]naphtha[1,2-d]thiophen-2-ol and 1H-6-thiacyclopenta[c]fluorene.

No description available.

O óxido de grafeno (OG), nanomaterial sintetizado a partir do grafite, tem atraído atenção como adsorvente com grande capacidade de remoção de cátions e diversos contaminantes de soluções aquosas, devido a presença dos grupos hidroxila, epóxi, carbonila e carboxila em sua superfície. Este trabalho, visa avaliar o potencial do óxido de grafeno bruto (OG) e de sua forma imobilizada em poli(divinilbenzeno) (PDVB-OG) na remoção de íons de césio de uma solução aquosa sintética. Os experimentos foram realizados em batelada, e foi avaliado a influência do tempo de contato e da concentração inicial de íons de césio. Para descrever a isotermas de equilíbrio foram aplicados os modelos de Langmuir e Freundlich, e a cinética do processo de adsorção, foi avaliada utilizando-se os modelos de pseudo-primeira ordem, pseudo-segunda ordem e difusão intrapartícula. Para prever a espontaneidade do processo de adsorção, foi calculado a energia livre de Gibbs. Nos experimentos de adsorção de íons de césio, o OG e o nanocompósito PDVB-OG, após 30 min. de contato, apresentaram taxa de remoção de 80% e 63% respectivamente. O modelo que melhor descreveu o processo de adsorção, para ambos adsorventes, na faixa de concentração de 30 a 130 mg.L-1, foi o de Langmuir e a capacidade máxima de adsorção calculada foi de 17 mg.g-1 para o OG e de 15 mg.g-1 para o PDVB-OG. Tanto para o OG quanto para o PDVB-OG, o modelo cinético que melhor descreveu o processo foi o de pseudo-segunda ordem e o valor da energia livre de Gibbs determinou que a adsorção dos íons de césio foi espontânea. A matriz polimérica não apresentou capacidade de remoção significativa, evidenciando que a adsorção dos íons césio pelo nanocompósito de PDVB-OG se deve a presença do OG imobilizado. Por outro lado, devido a maior densidade, o PDVB-OG foi facilmente separado da solução por decantação após o experimento de adsorção. Os resultados indicam a capacidade do OG e do nanocompósito PDVB-OG em tratar rejeitos líquidos radioativos, a fim de minimiza-los. / Due to the presence of hydroxyl, epoxy, carbonyl and carboxyl groups on its surface, graphene oxide (GO), synthesized from graphite, has attracted attention as a high adsorbent of cation removal and several contaminants from aqueous solutions. This work aims to evaluate the potential of graphene oxide (GO) and its immobilized form as poly(divinylbenzene) (PDVB-GO) in the removal of cesium ions from a synthetic aqueous solution. The experiments were performed in batch, and the influence of the contact time and the initial concentration of cesium ions were studied. Langmuir and Freundlich models as the equilibrium isotherms, and the kinetics of the adsorption process, pseudo-first order, pseudo-second order and intraparticle diffusion models, were evaluated GO and PDVB-GO, removed after 30 min. of contact time 80% and 63% of cesium ion, respectively for both adsorbents. The maximum adsorption capacities were 17 mg.g-1 for the GO and 15 mg.g-1 for the PDVB-GO. For both GO and PDVB-GO, Langmuir model fitted better in the adsorption process, the Gibbs Free Energy showed that this process for were spontaneous and the kinetic models were the pseudo-second order. As the polymer matrix, PDVB, has no significant removal capacity, the adsorption of the cesium ions by the PDVB-GO nanocomposite is due to the presence of the GO. On the other hand, the PDVB-GO was easily separated from the solution by decantation after the adsorption experiment. The results indicate the ability of the GO and the PDVB-GO nanocomposite to treat radioactive liquid wastes in order to minimize them.

Foram realizados experimentos de homopolimerização de estireno e copolimerização de estireno-divinilbenzeno em solução e suspensão aquosa pelos métodos convencional (FRP) e mediado por nitróxido (NMRP). Objetivou-se atingir um maior grau de entendimento sobre estes sistemas em relação ao que se tem na literatura. Para isto, três modelos matemáticos foram avaliados através de validação com os dados obtidos nos experimentos. Os experimentos foram conduzidos em reator de batelada isotérmico. As principais variáveis exploradas neste trabalho foram: temperatura de reação, concentração inicial de divinilbenzeno, diluição inicial da mistura de monômeros e técnicas de polimerização (FRP e NMRP). Os modelos matemáticos foram intitulados: Modelo A, Modelo B e Modelo C. O Modelo A consiste de um balanço de espécies não poliméricas e grupos poliméricos. A determinação das massas moleculares médias e da fração de gel foi feita através de balanços populacionais em termos de função geradora em conjunto com o método das características. Os modelos B e C consistiram de balanços de massa para espécies não poliméricas e método dos momentos para radicais ativos, radicais dormentes e polímero morto. A obtenção das massas moleculares médias e da fração de gel foi feita através do método do fracionamento numérico. Nestes dois modelos, foram consideradas as reações de ciclização através do método dos caminhos. Este método consiste num balanço de segmentos de cadeia que conectam grupos poliméricos. O número máximo de unidades monoméricas, considerado para estes segmentos foi 100 e o valor da constante cinética de ciclização do menor segmento ciclizável (3 unidades monoméricas) foi 450 s-1 para a temperatura de 90°C. O Modelo C leva em conta a redução da reatividade das ligações cruzadas em função do tamanho médio das cadeias em cada geração. Os resultados mostraram que, quando comparado com a FRP, a polimerização NMRP permite somente um controle limitado sobre o processo de reticulação, produzindo distribuições largas de tamanhos de cadeia. Micro e nanoestruturas foram identificadas em produtos obtidos por FRP e NMRP lineares e não lineares. Estas estruturas parecem ser consequência do processo de síntese (ex.: operação em temperatura de reação acima da temperatura de transição vítrea) e do tratamento dos produtos. Massa molecular média mássica e fração de gel foram afetadas consideravelmente pelas reações de ciclização em copolimerizações FRP, porém apresentaram pouca sensibilidade a estas reações em copolimerizações NMRP. A inclusão do mecanismo de ciclização, por si só (no Modelo B), não foi suficiente para produzir bons ajustes modelo/experimentos em termos de massa molecular média mássica (Mw) e fração de gel (Wg). No entanto, o Modelo C é capaz de fornecer boas previsões de Mw e Wg simultaneamente para os experimentos realizados a 90°C. O presente estudo mostrou uma análise na qual os modelos podem se complementar e fornecer subsídios para o desenvolvimento de um modelo unificado. / Homopolymerizations of styrene and copolymerizations of styrene-divinylbenzene were carried out in solution and aqueous suspension through conventional (FRP) and nitroxide-mediated (NMRP) techniques. The aim of the work was to reach a higher level of understanding in comparison to what is found in literature. In order to reach this goal, three mathematical models were assessed through validation using experimental data. The experiments were conducted in isothermal batch reactor. The main variables explored in this work were: reaction temperature, divinylbenzene initial concentration, initial dilution of monomers and polymerization techniques (FRP and NMRP). The mathematical models were named: Model A, Model B and Model C. The Model A consists of a balance of non-polymeric species and polymer groups. The average molecular weights and gel fraction were calculated through population balances in terms of generation function together with the method of characteristics. The models B and C were built using mass balance for non-polymeric species and the method of moments for active radicals, dormant radicals and dead polymer. The average molecular weights and gel fraction were calculated through the numerical fractionation technique. In these two models, cyclization reactions were considered through the method of paths. This method consists of a balance of chain segments which connect polymer groups. The maximum number of monomeric units considered for these segments was 100 and the value of the kinetic constant of cyclization for the smaller cyclizable path (3 monomeric units) was 450 s-1 at 90°C. The Model C takes into account the reduction of reactivity of the crosslink reactions in function of the average size of the chains in each generation. The results showed that, when compared with FRP, NMRP allows only a limited control over the crosslinking process, producing broad chain length distributions. Micro and nanostructures were identified in products obtained by linear and non-linear FRP and NMRP. These structures seem to be consequence of the synthesis process (e.g.: operation in reaction temperatures above the glass transition temperature) and of the products treatment. Weight average molecular weight and gel fraction were affected considerably by the cyclization reactions in FRP, however they presented few sensibility to these reactions in NMRP. The inclusion of the mechanism of cyclization, itself (in Model B), was not enough to obtain good model/experiments fittings in terms of weight average molecular weight (Mw) and weight fraction of gel (Wg). Although, the Model C is capable of providing good predictions of Mw and Wg simultaneously for the experiments carried out at 90°C. The present study showed an analysis in which the models can complement each other, providing subsidies for the development of a unified model.

Foram realizados experimentos de homopolimerização de estireno e copolimerização de estireno-divinilbenzeno em solução e suspensão aquosa pelos métodos convencional (FRP) e mediado por nitróxido (NMRP). Objetivou-se atingir um maior grau de entendimento sobre estes sistemas em relação ao que se tem na literatura. Para isto, três modelos matemáticos foram avaliados através de validação com os dados obtidos nos experimentos. Os experimentos foram conduzidos em reator de batelada isotérmico. As principais variáveis exploradas neste trabalho foram: temperatura de reação, concentração inicial de divinilbenzeno, diluição inicial da mistura de monômeros e técnicas de polimerização (FRP e NMRP). Os modelos matemáticos foram intitulados: Modelo A, Modelo B e Modelo C. O Modelo A consiste de um balanço de espécies não poliméricas e grupos poliméricos. A determinação das massas moleculares médias e da fração de gel foi feita através de balanços populacionais em termos de função geradora em conjunto com o método das características. Os modelos B e C consistiram de balanços de massa para espécies não poliméricas e método dos momentos para radicais ativos, radicais dormentes e polímero morto. A obtenção das massas moleculares médias e da fração de gel foi feita através do método do fracionamento numérico. Nestes dois modelos, foram consideradas as reações de ciclização através do método dos caminhos. Este método consiste num balanço de segmentos de cadeia que conectam grupos poliméricos. O número máximo de unidades monoméricas, considerado para estes segmentos foi 100 e o valor da constante cinética de ciclização do menor segmento ciclizável (3 unidades monoméricas) foi 450 s-1 para a temperatura de 90°C. O Modelo C leva em conta a redução da reatividade das ligações cruzadas em função do tamanho médio das cadeias em cada geração. Os resultados mostraram que, quando comparado com a FRP, a polimerização NMRP permite somente um controle limitado sobre o processo de reticulação, produzindo distribuições largas de tamanhos de cadeia. Micro e nanoestruturas foram identificadas em produtos obtidos por FRP e NMRP lineares e não lineares. Estas estruturas parecem ser consequência do processo de síntese (ex.: operação em temperatura de reação acima da temperatura de transição vítrea) e do tratamento dos produtos. Massa molecular média mássica e fração de gel foram afetadas consideravelmente pelas reações de ciclização em copolimerizações FRP, porém apresentaram pouca sensibilidade a estas reações em copolimerizações NMRP. A inclusão do mecanismo de ciclização, por si só (no Modelo B), não foi suficiente para produzir bons ajustes modelo/experimentos em termos de massa molecular média mássica (Mw) e fração de gel (Wg). No entanto, o Modelo C é capaz de fornecer boas previsões de Mw e Wg simultaneamente para os experimentos realizados a 90°C. O presente estudo mostrou uma análise na qual os modelos podem se complementar e fornecer subsídios para o desenvolvimento de um modelo unificado. / Homopolymerizations of styrene and copolymerizations of styrene-divinylbenzene were carried out in solution and aqueous suspension through conventional (FRP) and nitroxide-mediated (NMRP) techniques. The aim of the work was to reach a higher level of understanding in comparison to what is found in literature. In order to reach this goal, three mathematical models were assessed through validation using experimental data. The experiments were conducted in isothermal batch reactor. The main variables explored in this work were: reaction temperature, divinylbenzene initial concentration, initial dilution of monomers and polymerization techniques (FRP and NMRP). The mathematical models were named: Model A, Model B and Model C. The Model A consists of a balance of non-polymeric species and polymer groups. The average molecular weights and gel fraction were calculated through population balances in terms of generation function together with the method of characteristics. The models B and C were built using mass balance for non-polymeric species and the method of moments for active radicals, dormant radicals and dead polymer. The average molecular weights and gel fraction were calculated through the numerical fractionation technique. In these two models, cyclization reactions were considered through the method of paths. This method consists of a balance of chain segments which connect polymer groups. The maximum number of monomeric units considered for these segments was 100 and the value of the kinetic constant of cyclization for the smaller cyclizable path (3 monomeric units) was 450 s-1 at 90°C. The Model C takes into account the reduction of reactivity of the crosslink reactions in function of the average size of the chains in each generation. The results showed that, when compared with FRP, NMRP allows only a limited control over the crosslinking process, producing broad chain length distributions. Micro and nanostructures were identified in products obtained by linear and non-linear FRP and NMRP. These structures seem to be consequence of the synthesis process (e.g.: operation in reaction temperatures above the glass transition temperature) and of the products treatment. Weight average molecular weight and gel fraction were affected considerably by the cyclization reactions in FRP, however they presented few sensibility to these reactions in NMRP. The inclusion of the mechanism of cyclization, itself (in Model B), was not enough to obtain good model/experiments fittings in terms of weight average molecular weight (Mw) and weight fraction of gel (Wg). Although, the Model C is capable of providing good predictions of Mw and Wg simultaneously for the experiments carried out at 90°C. The present study showed an analysis in which the models can complement each other, providing subsidies for the development of a unified model.

Submitted by Erika Demachki (erikademachki@gmail.com) on 2014-11-03T16:02:19Z No. of bitstreams: 2 Dissertação - Wolney Arruda de Lima - 2013.pdf: 8969401 bytes, checksum: 67628ca83f7e7b88a59b09ef9dcfd500 (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Approved for entry into archive by Erika Demachki (erikademachki@gmail.com) on 2014-11-03T16:03:42Z (GMT) No. of bitstreams: 2 Dissertação - Wolney Arruda de Lima - 2013.pdf: 8969401 bytes, checksum: 67628ca83f7e7b88a59b09ef9dcfd500 (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Made available in DSpace on 2014-11-03T16:03:42Z (GMT). No. of bitstreams: 2 Dissertação - Wolney Arruda de Lima - 2013.pdf: 8969401 bytes, checksum: 67628ca83f7e7b88a59b09ef9dcfd500 (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2013-07-31 / In this work were prepared and characterized polyaniline/poly(styrene-co-divinylbenzene) composites by in situ oxidative polymerization of aniline in the pores of styrene-divinylbenzene copolymers. The aim was to obtain composites with high specific surface areas and total pore volumes for use as adsorbents of complex anions [SnCl4]2-. The copolymers with 29 and 84 % of divinylbenzene (DVB) were called PStyDVB 29 and PStyDVB 84, respectively. They were synthesized by suspension polymerization in the presence of inert diluents like toluene and heptane to obtain mesoporous beads with sizes in the range of 400 to 800 μm. Before the oxidative polymerization, the copolymers were swelled with aniline and ethanol mixture at volumetric ratio 20:80. The oxidative polymerization of aniline in the copolymers was carried out using benzoyl peroxide as an oxidant in the presence of hydrochloric or nitric acid as dopant at 25°C in three polymerization cycles. The materials were characterized by infrared spectroscopy with Fourier transform (FTIR), elemental analysis (CNHS), X ray diffraction, thermogravimetry, nitrogen adsorption (specific surface area and pore volume), Scanning Electron Microscopy and Atomic Absorption spectrophotometry. Elemental analysis indicated that the composite doped with HCl adsorb higher amounts of polyaniline (PANI) than using HNO3. The FTIR spectra and X-ray diffraction patterns of the composites were similar to the ones of the copolymers due the low amounts of PANI incorporated. The copolymers had lower thermal stability than composites, and the copolymer PStyDVB 84 had higher thermal stability due to a higher crosslinking degree. The specific surface areas (SBET) and pore volume (Vp) of the composites showed a decrease compared to the respective copolymers, due to the incorporation of polyaniline by homogeneously distributed inside and outside surfaces. The increasing of DVB content in the composites and copolymers favored the formation of high specific surface areas and pore volumes. The adsorption of anion complex [SnCl4]2- by the composites occurred by ion exchange of ions Cl- or NO3-. The results showed that the complex anions [SnCl4]2- adsorption increased with the increasing of hydrochloric acid and tin ion (II) concentrations. The complex anions [SnCl4]2- adsorbed more on the composite PANI/PStyDVB 84 HNO3, although it showed the lowest PANI content, the highest specific surface area and pore volume compared to the other composites. It can be concluded that the anion complex [SnCl4]2- adsorption depends on the number of binding sites and on the porous structure of the composites. / Neste trabalho, foram preparados e caracterizados compósitos Polianilina/Poli(estireno-co-divinilbenzeno), através da polimerização oxidativa in situ da anilina nos poros dos copolímeros estireno e divinilbenzeno. O objetivo foi obter compósitos com altas áreas superficiais específicas e volume de poros totais, para utilização como adsorventes de ânions complexo [SnCl4]2-. Os copolímeros com 29 e 84 % de divinilbenzeno (DVB) foram denominados PStyDVB 29 e PStyDVB 84, respectivamente, e sintetizados através de polimerização em suspensão, na presença de diluentes inertes tolueno e heptano para obtenção de pérolas com estrutura mesoporosa e tamanhos na faixa de 400 e 800 μm. Antes da polimerização oxidativa, os copolímeros foram intumescidos com mistura de anilina e etanol, na razão volumétrica 20:80. A polimerização oxidativa da anilina nos copolímeros foi realizada com peróxido de benzoíla, como oxidante, na presença de ácido clorídrico ou nítrico como dopante a 25°C, em três ciclos de polimerização. Os materiais foram caracterizados por espectroscopia de Infravermelho com Transformada de Fourier, Análise Elementar (CNHS), Difratometria de Raios X, Termogravimetria, Adsorção Física de Nitrogênio (área específica e volume de poros), Microscopia Eletrônica de Varredura e espectrofotometria de Absorção Atômica. A análise elementar indicou que os compósitos dopados com HCl, adsorveram maiores quantidades de Polianilina (PANI) do que com o uso de HNO3. Os espectros de FTIR e difratogramas de Raios X dos compósitos assemelharam-se aos dos copolímeros, pela baixa quantidade de PANI incorporada. Os copolímeros apresentaram menor estabilidade térmica que os compósitos, sendo que o copolímero PStyDVB 84 apresentou maior estabilidade térmica, devido a um maior número de ligações cruzadas. As medidas de áreas superficiais específicas (SBET) e o volume de poros (Vp) dos compósitos apresentaram diminuição em relação aos respectivos copolímeros, devido à incorporação da Polianilina distribuída homogeneamente pela superfície interna e externa. O copolímero PStyDVB 84 e seus compósitos apresentaram altas áreas superficiais específicas e volumes de poros devido ao maior teor de DVB. A adsorção de ânions complexo de [SnCl4]2- pelos compósitos ocorreu pelo processo de troca iônica de íons Cl- ou NO3-. Os ânions complexo [SnCl4]2- foram mais adsorvidos com a elevação das concentrações do ácido clorídrico e do íon estanho (II) em solução. Os ânions complexos [SnCl4]2- adsorveram mais no compósito PANI/PStyDVB 84 HNO3, sendo que ele apresentou o menor teor de PANI, a maior área superficial específica e o maior volume de poros em comparação com os demais compósitos. Pode ser concluído que a adsorção dos ânios complexo [SnCl4]2- depende do número de sítios ligantes e da estrutura porosa do compósito.

With the aim to develop and characterize a functionalized highly magnetic polymer carrier of micrometer size and of a narrow particle size distribution that will be suitable for biological application, hypercrosslinked microspheres were prepared. Simultaneously, the relation between structure and properties of product was observed. Condition of dispersion polymerization were optimized to obtain starting monodisperse poly(styrene-co-divinylbenzene) [P(St-DVB)] microspheres. The P(St-DVB) microspheres of different degree of crosslinking were prepared and effect of some polymerization parameters such as type of solvent, initiator, concentration and mode of DVB addition on morphology, size and particle size distribution were investigated. The starting microspheres were hypercrosslinked to obtain microporous inner structure. Hyperosslinked particles had very large specific surface area (> 1000 m2/g) and a high content of micropores (ca. 0.6 ml/g). First, P(St-DVB) microspheres were chloromethylated using three different chloromethylation agents to regulate their porous properties. Hypercrosslinking was achieved by the addition of stannic chloride as a catalyst and by increasing a temperature. The hypercrosslinked microspheres were then functionalized with sulfo- or aminogroups. The functional groups captured precipitated iron oxide inside the porous structure of the microspheres and also served as a reactive site for intended immobilization of the protein. A solution of ferrous and ferric chloride was imbibed under vacuum into the porous structure and the iron oxide was precipitated by an aqueous ammonia solution. Finally, the magnetic functionalized hypercrosslinked micropsheres were integrated into a biosensor for qualitative detection of ovalbumin.

Over the last decade, a significant amount of research has been done on sphingosine-1-phosphate (S1P). S1P regulates survival, proliferation and migration of breast cancer cells45, as well as playing an important but still unknown role in ovarian46, prostate, and glioma47 cell carcinomas. S1P plays a significant role in the regulation, proliferation and angiogenesis, and is therefore an area of considerable interest for cancer research. Previous research in our group has shown that two stilbenoid sphingosine analogs (1 & 2) were effective at sphingosine kinase (SphK) inhibition in addition to showing down-regulation of Vascular Endothelial Growth Factor (VEGF), a novel and distinctly different mechanism of action compared to reported sphingosine kinase inhibitors. Both compounds showed novel toxicity toward the parasite Toxoplasma gondii. T. gondii causes toxoplasmosis; a disease carried by up to 1/3rd of the world’s population and one that has been implicated in schizophrenia. Unfortunately, use of 1 & 2 as fluorescent probes is limited; their emission wavelengths fall between 360 and 380 nm, within the range of background fluorescence. The synthesis of five fluorescent sphingosine analogs is described herein, three of which have emission wavelengths above 420 nm. These compounds show single digit µM cytotoxicity towards T. gondii. The second generation synthesis of Fingolimod (FTY720) is also described. The process was optimized for large-scale production. Improvements to the synthesis included increased atom economy, purification and overall reaction efficiency. Yield was increased to 36%, from 33% in the first generation synthesis. Lastly, a synthesis of p-divinylbenzene is described, using “green” solvents and easy sample work-up. The product contains no meta impurities, an issue that arises when p-divinylbenzene is purchased commercially. / Thesis / Candidate in Philosophy

This work focuses on improving the quality of carbon-based core-shell materials for high performance liquid chromatography (HPLC) via the characterization of the core materials, and also the development of chromatographic methods (separations) for them. In the early part of this work, I applied organic synthesis to make uniform, spherical poly(divinylbenzene) (PDVB) microspheres, and then carbonized them to prepare carbon core materials for core-shell particle synthesis. Here, I studied in detail the surface and material properties of these particles with multiple instruments, which allowed me to describe the physical and chemical changes that took place during each treatment. The uniform, spherical carbon core materials greatly improved the efficiency of the previously developed carbon-based core-shell HPLC columns from ca. 70,000 plates per meter (N/m) to ca. 110,000 N/m for various alkyl benzenes. Later, I focused on generating application notes to showcase these mixed-mode HPLC columns. Here, liquid chromatography mass spectrometry (LC-MS) was used for the detection of analytes that lack chromophores for UV detection. In this dissertation, Chapter 1 contains a historical background and theory of HPLC along with a review of the use of carbon-based core-shell materials for elevated pH and temperature applications. Chapter 2 describes the improvement of the efficiency of carbon-based materials for HPLC using carbonized PDVB microspheres as the carbon core material. Chapter 3 is a study on the characterization of carbonized PDVB microspheres with multiple instruments. Chapter 4 describes the separation of cannabinoids using three types of carbon-based mixed-mode HPLC columns. Chapter 5 consists of (i) guidelines for the retention mechanism of the core-shell particles that have been commercialized for chromatography by Diamond Analytics, a US Synthetic Company in Orem, Utah, and (ii) application notes for these columns. Finally, Chapter 6 discusses possible future work.

Este trabalho teve como objetivo sintetizar e caracterizar uma matriz híbrida estável de poli(estireno-co-divinilbenzeno) magnetizado pela adição de magnetita (Fe3O4) e avaliar seu potencial como suporte para a imobilização de lipases. A matriz híbrida foi sintetizado pela técnica de polimerização em suspensão utilizando dos monômeros de estireno e divinilbenzeno e ao qual foram adicionadas partículas de magnetita preparadas por coprecipitação dos íons Fe+2 e Fe+3. A caracterização foi realizada pelas técnicas de microscopia eletrônica de varredura (MEV), espectroscopia na região do infravermelho por transformada de Fourier (FTIR), difratometria de raios-X (DRX) e magnetização de amostra vibrante (VSM), comparando os materiais magnetizados e não magnetizados. Os biocatalisadores foram preparados pela imobilização da lipase de Candida rugosa (LCR) e lipase PS Burkholderia cepacia (LPS) via adsorção física e foram caracterizados em função da influência de pH e temperatura na atividade hidrolítica, parâmetros cinéticos, estabilidade térmica, estabilidade operacional e estabilidade de estocagem. O derivado de LCR foi aplicado em reações de esterificação e o derivado de LPS em reações de transesterificação. Os resultados obtidos pelas análises de FTIR, DRX e VSM confirmaram que a magnetita foi incorporada ao polímero, gerando atração das partículas por um campo magnético externo. A caracterização bioquímica indicou forte influência do pH na atividade hidrolítica, apresentando ponto ótimo próximo a 8,0 tanto para as lipases livres quanto imobilizadas. Os biocatalisadores magnetizados preparados apresentaram bom desempenho em todos os aspectos, o derivado da lipase de Candida rugosa alcançou conversões entre 89-94% nas reações de esterificação, revelando tempo de meia vida de t1/2=52 dias na estabilidade operacional. O derivado de Burkholderia cepacia atingiu rendimentos próximos a 80% nas reações de transesterificação com t1/2=40 dias. A imobilização aumentou a estabilidade térmica das lipases em 50 vezes no caso da LCR e em 2,3 vezes para a LPS. Estes resultados indicam que o material híbrido magnetizado sintetizado possui grande potencial para ser utilizado como suporte na imobilização de enzimas com aplicação em reações de interesse industrial. / This study aimed to synthesize and characterize a stable hybrid matrix of poly (styrene-codivinylbenzene) magnetized by the addition of magnetite (Fe3O4) and evaluate its potential for application in the immobilization of lipases, by characterization of the prepared biocatalysts. The support was synthesized by the suspension polymerization technique by applying styrene and divinylbenzene monomers and adding magnetite particles synthesized by co-precipitation of Fe + 2 and Fe + 3. The characterization of the material was performed by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), vibrating sample magnetization (VSM), by comparison of the magnetized and the not magnetized particles. The biocatalysts were prepared by immobilization of lipase from Candida rugosa (CRL) and lipase from Burkholderia cepacia (Lipase PS) via physical adsorption and they were characterized according to the influence of pH and temperature on the hydrolytic activity, kinetic parameters, thermal stability, operational stability and storage stability. The CRL derivative was applied in esterification reactions and the lipase PS derivative was applied in transesterification reactions. The results obtained by the analysis FTIR, XRD and VSM confirmed the magnetite was successfully incorporated into the polymer and generated the atraction for an external magnetic field. Biochemical characterization indicated a strong influence of pH on the hydrolytic activity, showing better results on pH around 8,0 for free and both immobilized lipases. The magnetized biocatalysts prepared had good performance in all respects, derivative from Candida rugosa lipase reached 89-94% conversion in esterification reactions showing half-life of operational stability t1 / 2 = 52 days. The immobilized lipase from Burkholderia cepacia reached yields close to 80% in transesterification reactions presenting t1/2 = 40 days. Immobilization increased the thermal stability of lipase by 50 times in the case of CRL and 2,3 times for Lipase PS. These results indicate that the magnetized hybrid material synthesized has great potential to be used as a support for the immobilization of enzymes for use in reactions of industrial interest.