Dissertação (Mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências Físicas e Matemáticas. / Made available in DSpace on 2012-10-17T05:08:41Z (GMT). No. of bitstreams: 0Bitstream added on 2016-01-09T00:52:40Z : No. of bitstreams: 1 147511.pdf: 17268276 bytes, checksum: 65debb5f710d27789f5c3a3e1c3f53e7 (MD5)

A proteção anódica de metais se caracteriza pela formação de um filme de óxidos protetores na sua superfície, promovendo assim a passivação e a desaceleração do processo corrosivo. O uso de polímeros intrinsecamente condutores (PIC), como a polianilina (PAni) utilizada neste trabalho, tem-se apresentado como alternativa de revestimento ou componente de revestimentos protetores, devido às suas características peculiares que podem proporcionar e induzir o efeito de proteção anódica em metais passiváveis. Devido à dificuldade de dissolução e de coesão de filmes a base de PAni, foi investigada a possibilidade da obtenção de seus filmes pela mistura de PAni no estado oxidado e desdopada, conhecida como PAni esmeraldina base (PAni EB), com o plastificante não dopante 4-cloro-3-metilfenol (CMF) e solvente conveniente. Os filmes produzidos foram caracterizados química e morfologicamente, apresentando-se como um revestimento coeso e auto-suportado com a preservação das funções e das características desejáveis da PAni para aplicação como revestimento anticorrosivo. Os ensaios eletroquímicos realizados em filme de PAni EB aplicado sobre aço carbono AISI 1006, em diferentes concentrações de H2SO4 aquoso, ofereceram respostas que indicam a formação de par redox polímero-metal na faixa de potencial em que é possível a passivação ou manutenção da passivação do substrato metálico, o que resulta na elevação do potencial de corrosão, fazendo com que o metal se comporte de forma mais nobre. Com isso viabiliza-se a utilização do binder de PAni EB como filme anticorrosivo ou/e resina de tintas que promovam a proteção anódica e o efeito de barreira na proteção do aço carbono AISI 1006 contra a corrosão. / The anodic protection of metals is characterized by the formation of a protective oxide film on its surface, thus promoting the passivation and the slowdown of the corrosion process. The use of intrinsically conductive polymers (PCI) such as polyaniline (PAni) used in this work, has been presented as an alternative coating or component of protective coatings, due to their peculiar characteristics that may induce and provide the protective anodic effect on oxidizable metals. Due to the difficulty of dissolution and cohesion of films based the polyaniline, was investigated the possibility of obtaining of their films by mixing PAni in the oxidized state and undoped, known as PAni base emeraldine (PAni EB), with plasticizer no dopant 4 -chloro-3-methylphenol (CMF) and convenient solvent. The films produced were characterized chemically and morphologically, presenting itself as a coating cohesive and self-supported, with the preservation of the functions and desirable characteristics of the PAni to application as anticorrosive coating. The electrochemical tests performed on PAni EB film applied over carbon steel AISI 1006, at different concentrations of aqueous H2SO4, offer answers that indicate the formation of redox pair polymer-metal in the potential range in which is possible the passivation or maintenance of the passivation of metallic substrate, resulting in the increase potential of corrosion, doing with that metal to behave of more noble form. With that enables the use of binder of PAni EB as film anticorrosive or/and resin of paints that promote the anodic protection and the effect of barrier in the protection the carbon steel AISI 1006 against corrosion.

Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2009 / Bibliografia: f. 78-81 / A utilização de tratamentos térmicos em ligas ferrosas tem por função a modificação da microestrutura do material, a fim de promover propriedades adequadas as solicitações funcionais especificas de uma determinada peça. A tempera de solidos por resfriamen / The use of heat treatments in ferrous alloys has the task of modifying the microstructure of the material in order to promote adequate properties to functional requirements of a specific part. The hardening by cooling of solids in fluids, altering the mic

O comportamento eletroquímico do aço carbono em soluções aquosas contendo KNO3 0,10 mol L-1 e soluções etanólicas contendo cloreto de tetraetilamônio 0,10 mol L-1 foi estudado na ausência e na presença de diferentes concentrações (0,50 mM a 50,0 mM) de acetato de linalila, mentol, limoneno e pulegona. Técnicas eletroquímicas como a potenciometria, varredura potenciodinâmica, cronoamperometria, curvas de Tafel e espectroscopia de impedância eletroquímica foram utilizadas a fim de compreender a interação entre os compostos orgânicos e a superfície do eletrodo. Medidas de perda de massa também foram realizadas, bem como a comprovação visual dos resultados mediante registros fotográficos. O acetato de linalila adsorve na superfície do aço carbono mesmo na presença de grande quantidade de água ou etanol. A energia livre de adsorção de Gibbs para este processo é de -26,0 kJ mol-1 em soluções aquosas e -26,7 kJ mol-1 em soluções etanólicas. Para o mentol, a energia livre de adsorção de Gibbs calculada foi de -26,7 kJ mol-1 em soluções aquosas e -24,2 kJ mol-1 em soluções etanólicas. Para o limoneno, esses valores foram -24,2 kJ mol-1 em meio aquoso e -26,0 kJ mol-1 em meio etanólico, e para a pulegona os valores foram de -25,7 kJ mol-1 e -24,6 kJ mol-1, em meio aquoso e etanólico, respectivamente. Foi detectado que as espécies adsorvidas na superfície do metal diminuíram os valores das densidades de corrente anódicas, bem como a perda de massa do metal. Esses efeitos permitem-nos classificar esses compostos orgânicos como inibidores naturais de corrosão para o aço carbono em soluções aquosas e etanólicas. / The electrochemical behavior of low carbon steel in aqueous solutions containing KNO3 0.10 mol L-1 and ethanolic solutions containing tetraethylammonium chloride 0.10 mol L-1 was studied in the absence and presence of different concentrations (0.50 mM to 50.0 mM) of linalyl acetate, menthol, limonene and pulegone. Electrochemical techniques such as potentiometry, cyclic voltammetry, chronoamperometry, Tafel curves and electrochemical impedance spectroscopy were used to understand the interaction between the organic compound and the electrode surface. Weight loss measurements were also performed, as well as visual confirmation of the results by photographic records. Linalyl acetate adsorbed on low carbon steel surface even in the presence of a large amount of water or ethanol. The Gibbs free energy of adsorption for this process was -26.0 kJ mol-1 in aqueous solutions and -26.7 kJ mol-1 for ethanol solutions. For menthol, the Gibbs free energy of adsorption was calculated -26.7 kJ mol-1 in aqueous solutions and -24.2 kJ mol-1 for ethanol solutions. For limonene, these values were -24.2 kJ mol-1 in aqueous medium and -26.0 kJ mol-1 in ethanolic medium, and for pulegone the values were - 25.7 kJ mol-1 and -24.6 kJ mol-1 in aqueous and ethanolic medium, respectively. It was detected that the species adsorbed on the metal surface decreased the amounts of anodic current densities and the metal mass loss. These effects allow us to classify the organic compounds investigated as natural corrosion inhibitors for low carbon steel in aqueous and ethanolic solutions.

Alumínio Pulverizado Termicamente (TSA) é amplamente utilizado em instalações offshore como revestimento de ânodo de sacrifício em tubulações de aço carbono. O transporte e a instalação desses componentes podem levar a pequenos danos no revestimento, o que pode expor a superfície do aço à água do mar. Sabe-se que o depósito calcário é formado na superfície do aço polarizado catodicamente. Assim, esta pesquisa avaliou o TSA aplicado por sistema de pulverização de arco duplo (TWAS) no aço ao carbono S355J2 + N quando ocorrem danos (holidays) para estudar a formação de depósitos calcários no aço e adquirir dados sobre o desempenho do TSA sob altas temperaturas. A aplicação de diferentes condições também foi considerada: presença de selantes; liga do revestimento (99,5% de Al e Al-5% de Mg) e condições enterradas/não enterradas. Dois tipos de experimentos foram realizados: i) testes em potencial livre sob temperaturas constantes (30, 60 e 90°C) e diferentes tamanhos de holidays (expondo 5, 10 e 20% da superfície do aço) e ii) testes sob gradient térmico onde óleo a ~125°C foi adicionado em uma torre polimérica e água externa a ~10°C ficou em contato com a superfície das amostras (tanto potencial livre como polarização de -950 mVAg/AgCl foram aplicados). Análises incluíram inspeção visual, microscópio eletrônico de varredura e difração de Raio-X. A partir dos testes em temperaturas constante, o TSA atingiu um bom potencial de proteção (-800 a -900 mVAg/AgCl) e pouca diferença nos resultados devido à diferença na composição doTSA e no tamanho do holiday foi observada. As taxas de corrosão foram mantidas entre 0,02 e 0,01 mm/ano. No ensaio sob gradiente térmico e potencial livre, a perda de revestimento e as taxas de corrosão foram de 0,4 a 0,002 mm/ano. Além disso, o potencial alcançado foi de uma faixa menor do que a obtida anteriormente (-745 a -835 mVAg/AgCl). No entanto, quando o TSA foi combinado com proteção catódica externa e gradiente térmico, a espessura do TSA foi satisfatório e as taxas de corrosão obtidas foram inferiores a 0,076 mm/ano. O depósito calcário formado no holiday protegeu o aço contra a corrosão e seu mecanismo de crescimento baseado nesta pesquisa foi construído. / Thermally Sprayed Aluminium (TSA) is widely used in offshore facilities as sacrificial anode coating for carbon-steel risers and pipelines. Transportation and installation of those components can lead to small damages in the coating, which can expose the steel surface to the seawater. It is known that calcareous deposit is formed on the cathodically polarised steel surface. Thus, this research evaluated the TSA applied by twin wire arc spray system (TWAS) on S355J2+N carbon-steel when damage (holidays) is present in order to study the calcareous deposit formation on steel and acquire data regarding the TSA performance at high temperatures. Application of different conditions was also considered: presence of sealing; coating alloy (99.5%Al and Al-5%Mg) and buried/unburied conditions. Generally, two types of experiment were conducted – i) tests at free potential at steady temperatures (30, 60 and 90°C) and different holiday sizes (exposing 5, 10 and 20% of the steel surface) and ii) tests under thermal gradient where oil at ~125°C was added in polymeric tower and external water at ~10°C was in contact with the samples surface (both free potential and polarisation of -950 mVAg/AgCl were applied). Methodology of analyses included visual inspection, scanning electron microscope and X-ray Diffraction. From the tests at steady temperatures, the TSA reached a very good protective potential (-800 to -900 mVAg/AgCl) and little difference in results due to difference in TSA composition and holiday size was observed. Corrosion rates were kept between 0.02 and 0.01 mm/year. From the thermal gradient test under free potential, the coating loss and corrosion rates were 0.4 to 0.002 mm/year. Also, the potential achieved was in a lower range than previously obtained (-745 to -835 mVAg/AgCl). However, when TSA was combined with external cathodic protection and thermal gradient, the thickness of the TSA was satisfactory and corrosion rates obtained were below 0.076 mm/year. The calcareous deposit formed within the holiday protected the steel substrate against corrosion and its growth mechanism based in this research was built.

Em função das novas fronteiras exploratórias de petróleo, principalmente proveniente das reservas do pré-sal, as situações operacionais e condições de serviços estão se tornando cada vez mais severas (pressão, temperatura, composição dos fluidos, etc), exigindo o desenvolvimento de novos materiais e de novas tecnologias para a adequação de materiais tradicionais existentes, como o aço carbono, agregando-lhes novas propriedades e características, por exemplo, com o uso de revestimentos poliméricos. Este trabalho tem por objetivo desenvolver e avaliar um projeto de uma válvula esfera industrial com todas suas partes internas revestidas, incluindo componentes internos, e realizar uma análise do processo de revestimento e validação do projeto final com os testes de desempenho realizados baseados na norma ABNT NBR 15827, com vistas a possibilitar a substituição de ligas metálicas nobres de alto custo (inconel, duplex, superduplex etc.), por aço carbono revestido. Inicialmente, foram realizadas alterações no projeto original da válvula esfera industrial de diâmetro 4‖ CL300 montagem tipo flutuante para tornar o projeto convencional em um projeto com revestimento interno. Na sequência, foram revestidas duas válvulas com o polímero etileno clorotrifluoroetileno (ECTFE), e realizados ensaios de controle de qualidade durante as etapas do revestimento e ao final do processo. Após a montagem e testes iniciais funcionais e de vedação das válvulas, estas foram submetidas a teste de ciclagem e desempenho, com 1000 ciclos de abertura e fechamento com a pressão máxima de trabalho, sendo realizado monitoramento contínuo do torque de acionamento e pressão aplicada. Foram realizadas sete avaliações de integridade das vedações e do revestimento durante a ciclagem. Gráficos de ciclagem, pressão e testes de vedação foram gerados na etapa de avaliação de desempenho dos protótipos. Ao final dos ensaios os protótipos foram desmontados e uma avaliação dos componentes foi realizada, sendo observado apenas desgaste uniforme nas vedações e superfície de vedação da esfera e haste devido ao atrito gerado pela abertura e fechamento da válvula. Este desgaste não comprometeu a vedação das válvulas. Os resultados satisfatórios validaram o projeto e o processo de revestimento desenvolvido. / Due to new exploratory frontiers of oil, mainly from pre-salt reserves, the operational situations and service conditions are becoming increasingly severe (pressure, temperature, composition of fluids, among others), demanding the development of new materials and technologies to the suitability of the traditional materials, as the carbon steel, by adding them new properties and characteristics, for example, with the use of polymeric coatings. This paper has the objective of to develop and evaluate the project of an industrial ball valve, with all the inner parts coated, including internal components, perform an analysis of the coating and validate the final design process with performance tests conducted based on standard ABNT NBR 15827, with the objective of enabling the replacement of noble metal alloys of high cost (inconel, duplex, super duplex, etc.) by coated carbon steel. Initially, there were changes in the original design of industrial ball valve of a diameter 4‖ CL300 floating mounting type to turn the conventional project in a project with internal coating. Following, two valves were coated with the polymer ethylene chlorotrifluoroethylene (ECTFE) and control quality tests performed during the stages of the coating and the end of the process. After the assembly and the initial functional tests and sealing of the valves, they were subjected to cycling and performance tests with 1000 cycles of opening and closing at maximum working pressure, being carried out continuous monitoring of the drive torque and pressure applied. Seven evaluations of the integrity of the sealing and coating were performed during cycling. Charts of cycle number, pressure and sealing tests were generated during the stage of evaluation of the prototype's performance. At the end of the testing, the prototypes were disassembled and a review of the components was conducted, being observed only the uniform wear on the seals and sealing surfaces of the sphere and the stem due to the friction generated by the opening and closing of the valve. This wear did not commit the seal of the valves. Satisfactory results have validated the project and the coating process developed.

Submitted by Elizabete Silva (elizabete.silva@ufes.br) on 2015-01-15T17:45:47Z No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) DISSERTAÇÃO SURYA CANTARINO.pdf: 2381118 bytes, checksum: 11b4cb4af814846458aac4b435f315ae (MD5) / Approved for entry into archive by Elizabete Silva (elizabete.silva@ufes.br) on 2015-01-16T18:42:08Z (GMT) No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) DISSERTAÇÃO SURYA CANTARINO.pdf: 2381118 bytes, checksum: 11b4cb4af814846458aac4b435f315ae (MD5) / Made available in DSpace on 2015-01-16T18:42:08Z (GMT). No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) DISSERTAÇÃO SURYA CANTARINO.pdf: 2381118 bytes, checksum: 11b4cb4af814846458aac4b435f315ae (MD5) Previous issue date: 2014 / A mudança no mercado global do petróleo nos últimos anos, com o declínio das reservas de óleo leve, têm forçado a busca por novos campos petrolíferos em ambientes mais remotos, como nos campos localizados na camada pré-sal, e a exploração de óleos pesados que possuem elevado teor de ácidos naftênicos. Isso acarreta em grandes desafios para a previsão do desempenho de materiais frente às novas condições ambientais em que estão inseridos. No presente trabalho, o comportamento da corrosão do aço carbono AISI 1010 e do aço inoxidável AISI 316L foi estudado em soluções aquosas com elevado teor de cloreto e em solução de ácido naftênico ciclopentanóico a fim de ter melhor entendimento da ação dessas espécies no processo de corrosão e simular a corrosão pela água de produção na indústria petrolífera. Foram aplicadas as técnicas de potencial de circuito aberto, polarização potenciodinâmica, voltametria cíclica, espectroscopia de impedância eletroquímica, espectroscopia Raman, microscopia eletrônica de varredura e microscopia de força atômica, usadas, em cada caso, de acordo com a conveniência. O aumento da [Cl-] na faixa de 1,2–2,8 mol.L-1 não altera os processos catódicos e anódicos perto do Ecorr para os aços AISI 1010 e AISI 316L. Em condições de sobrepotenciais afastados do Ecorr, o aumento de [Cl-] aumenta os processos oxidativos de corrosão, o que é expresso pelas maiores densidades de corrente e carga anódica e aumento da perda de massa sofrida pelos eletrodos de ambos os aços. Portanto, os danos da corrosão são mais intensos quando se aumenta a [Cl-]. O aço AISI 1010 é ativo nas soluções de NaCl e a corrosão se propaga livremente de forma uniforme. Para o aço AISI 316L, uma ampla faixa de passividade pode ser vista nas soluções de NaCl; no Epit ocorre a ruptura do filme passivo e o crescimento de pites estáveis. Após 24 h de imersão em soluções de sulfato de sódio (branco) e de ácido naftênico ciclopentanóico ocorre crescimento de filme de óxido e as fases α-Fe2O3, Fe3O4 e δ-FeO(OH) foram identificadas nos espécimes de aço AISI 1010 e Fe3O4 foi identificado nos defeitos do filme prévio presente na superfície do aço AISI 316L. Os filmes formados em solução de ácido ciclopentanóico possuem menor resistência à polarização, maior rugosidade e maior taxa de corrosão quando comparado aos filmes crescidos na solução branco, para ambos os aços. A presença do ácido naftênico muda a forma como a reação de corrosão se procede e contribui para o aumento da corrosão. A corrosão naftênica foi mais pronunciada no aço carbono porque a presença dos elementos de liga no aço inox reduzem o número de sítios ativos ricos em Fe e tornam menos oportuna a ligação do Fe com o naftenato. / The change in the oil global market in recent years, with declining reserves of light oil, have forced to search for new oil fields in more remote environments, such as in fields located in the pre-salt layer, and to the exploitation of heavy oils that have high content of naphthenic acids. This leads to major challenges for predicting the performance of materials in new environmental conditions in which they are. In the present work, the corrosion behavior of AISI 1010 carbon steel and AISI 316L stainless steel was studied in aqueous solutions with high chloride content and in cyclopentanoic naphthenic acid solution in order to better understanding the action of these species in the corrosion process and simulate corrosion by produced water in the oil industry. The techniques of open circuit potential, potentiodynamic polarization, cyclic voltammetry, electrochemical impedance spectroscopy, Raman spectroscopy, scanning electron microscopy and atomic force microscopy were applied according to convenience in each case. The increase in [Cl-] in the range of 1,2 to 2,8 mol.L-1 does not alter the cathode and anode processes near Ecorr for AISI 1010 and AISI 316L steels. Under conditions of overpotentials far from Ecorr, increasing [Cl-] increases oxidative corrosion processes, which is expressed by higher anodic current densities and anodic charge and increase of mass loss of the electrodes of both steels. Therefore, the damage of corrosion are more intense when increasing the [Cl-]. AISI 1010 steel is active in NaCl solutions and corrosion propagates freely in a generalized manner. For AISI 316L steel, a wide range of passivity can be seen in NaCl solutions; in Epit occurs the rupture of the passive film and growth of stable pitting. After 24 h immersion in sodium sulfate (white) and cyclopentanoic naphthenic acid solutions occurs growth of oxide film and the phase α-Fe2O3, Fe3O4 and δ-FeO(OH) have been identified on AISI 1010 steel specimens and Fe3O4 identified in the defects of the prior oxide film present on AISI 316L steel surface. The films grown in cyclopentanoic acid solution have lower polarization resistance, higher roughness and greater corrosion rate compared to films grown in the blank solution, for both steels. The presence of naphthenic acid changes how the corrosion reaction is carried and contributes to increased corrosion. The naphthenic corrosion was more pronounced in carbon steel because the presence of alloying elements in stainless steel reduce the number of Fe rich active sites and become less opportune connection of Fe with the naphthenate.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Mecânica / Made available in DSpace on 2012-10-20T22:13:29Z (GMT). No. of bitstreams: 1 232853.pdf: 6063764 bytes, checksum: 3ba59f36fb4ffac49818c148c0411b43 (MD5) / A furação por escoamento, processo pelo qual são geradas buchas escoadas em chapas e perfis em diversos materiais, possui como característica principal a obtenção de buchas sem a remoção de material. As buchas são produzidas através do emprego de uma ferramenta rotativa, normalmente de metal-duro, que pressionada contra o material da peça produz calor por atrito e deformação, provocando o amolecimento do material e seu escoamento durante a sua penetração. As buchas escoadas são empregadas em diversas aplicações industriais, sendo a mais comum em uniões removíveis, onde se faz necessária a confecção de rosca pelo processo de rosqueamento por conformação. Este trabalho tem como objetivo relacionar os parâmetros de trabalho do processo de furação por escoamento com as alterações na microestrutura do material-base, e relacionar as alterações na microestrutura com as propriedades mecânicas de buchas escoadas. O estudo foi desenvolvido através da realização de ensaios experimentais de furação por escoamento empregando-se ferramenta de metal-duro e aços de baixo carbono. Foram analisadas as influências das condições de trabalho (rotação e velocidade de avanço) e da variação do teor de carbono e espessura do material sobre as características do processo (força de avanço, momento torçor, potência, temperatura e tempo de processo) e a influência das características do processo sobre os resultados do processo (dimensões principais, microdureza e transformações microestruturais). Além desses, foram determinadas a carga máxima de resistência das buchas escoadas e a classe de resistência da rosca obtida nas buchas através de ensaios de tração, permitindo uma avaliação das relações entre as transformações microestruturais e as propriedades mecânicas. Independente da espessura do material e do teor de carbono, o emprego das condições de trabalho mais severas durante a furação por escoamento promoveram a obtenção de buchas com geometria e alterações microestruturais mais adequadas à elevação da resistência mecânica, além do processo se desenvolver mais rapidamente. Como conclusão pode-se afirmar, para a maioria das análises realizadas, haver um relacionamento termomecânico entre o processo de furação por escoamento, as alterações promovidas na microestrutura do material-base e as propriedades mecânicas resultantes.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Ciência e Engenharia de Materiais / Made available in DSpace on 2012-10-18T05:42:56Z (GMT). No. of bitstreams: 0Bitstream added on 2014-09-25T20:59:07Z : No. of bitstreams: 1 180505.pdf: 28077041 bytes, checksum: d54f24f974183c19616124bfa8a37f34 (MD5) / Este trabalho teve por objetivo estudar o processo de recozimento de esferoidização de um aço SAE 1045 e correlacionar as suas propriedades mecânicas com as respectivas microestruturas apresentadas. As amostras foram laminadas à frio (com 21% de deformação) e também temperadas (austenitizadas em 850ºC, 1000ºC e 1100ºC por 30 minutos e resfriadas em água), de modo a obter diferentes microestruturas, prévias ao recozimento de esferoidização. Para o estudo do efeito das variações dos tratamentos térmicos na esferoidização foram utilizados dois ciclos térmicos: um subcrítico, logo abaixo de Ac1 (710ºC por 18 e 22 horas) e outro pendular, em torno de Ac1 (entre 740ºC e 680ºC) por 22 horas. Estas variações no processo de preparação das amostras, objetivaram ampliar as diferenças entre os parâmetros a serem avaliados, de modo a melhor correlacioná-los com as propriedades mecânicas obtidas. Análises qualitativas e quantitativas foram realizadas via microscopia ótica e eletrônica de varredura. O comportamento mecânico foi avaliado a partir de ensaios de tração e de dureza das amostras esferoidizadas. Variações na distribuição e forma dos carbonetos, bem como, do tamanho de grão ferrítico, influenciaram de forma direta as propriedades do aço esferoidizado, indicando uma maior dependência das propriedades mecânicas sobre os carbonetos, que do tamanho de grão ferrítico. A cinética de esferoidização também foi estudada, visando fornecer informações referente ao comportamento do aço SAE 1045 frente a duas microestruturas prévias, uma deformada e outra temperada. Boas correlações foram obtidas após a análise dos resultados apresentados.

A proteção anódica de metais se caracteriza pela formação de um filme de óxidos protetores na sua superfície, promovendo assim a passivação e a desaceleração do processo corrosivo. O uso de polímeros intrinsecamente condutores (PIC), como a polianilina (PAni) utilizada neste trabalho, tem-se apresentado como alternativa de revestimento ou componente de revestimentos protetores, devido às suas características peculiares que podem proporcionar e induzir o efeito de proteção anódica em metais passiváveis. Devido à dificuldade de dissolução e de coesão de filmes a base de PAni, foi investigada a possibilidade da obtenção de seus filmes pela mistura de PAni no estado oxidado e desdopada, conhecida como PAni esmeraldina base (PAni EB), com o plastificante não dopante 4-cloro-3-metilfenol (CMF) e solvente conveniente. Os filmes produzidos foram caracterizados química e morfologicamente, apresentando-se como um revestimento coeso e auto-suportado com a preservação das funções e das características desejáveis da PAni para aplicação como revestimento anticorrosivo. Os ensaios eletroquímicos realizados em filme de PAni EB aplicado sobre aço carbono AISI 1006, em diferentes concentrações de H2SO4 aquoso, ofereceram respostas que indicam a formação de par redox polímero-metal na faixa de potencial em que é possível a passivação ou manutenção da passivação do substrato metálico, o que resulta na elevação do potencial de corrosão, fazendo com que o metal se comporte de forma mais nobre. Com isso viabiliza-se a utilização do binder de PAni EB como filme anticorrosivo ou/e resina de tintas que promovam a proteção anódica e o efeito de barreira na proteção do aço carbono AISI 1006 contra a corrosão. / The anodic protection of metals is characterized by the formation of a protective oxide film on its surface, thus promoting the passivation and the slowdown of the corrosion process. The use of intrinsically conductive polymers (PCI) such as polyaniline (PAni) used in this work, has been presented as an alternative coating or component of protective coatings, due to their peculiar characteristics that may induce and provide the protective anodic effect on oxidizable metals. Due to the difficulty of dissolution and cohesion of films based the polyaniline, was investigated the possibility of obtaining of their films by mixing PAni in the oxidized state and undoped, known as PAni base emeraldine (PAni EB), with plasticizer no dopant 4 -chloro-3-methylphenol (CMF) and convenient solvent. The films produced were characterized chemically and morphologically, presenting itself as a coating cohesive and self-supported, with the preservation of the functions and desirable characteristics of the PAni to application as anticorrosive coating. The electrochemical tests performed on PAni EB film applied over carbon steel AISI 1006, at different concentrations of aqueous H2SO4, offer answers that indicate the formation of redox pair polymer-metal in the potential range in which is possible the passivation or maintenance of the passivation of metallic substrate, resulting in the increase potential of corrosion, doing with that metal to behave of more noble form. With that enables the use of binder of PAni EB as film anticorrosive or/and resin of paints that promote the anodic protection and the effect of barrier in the protection the carbon steel AISI 1006 against corrosion.