Orientadores: Fernando Galembeck, Mauricio Urban Kleinke / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-01T08:17:11Z (GMT). No. of bitstreams: 1 Gandur_MarceloCatanoce_D.pdf: 5947620 bytes, checksum: c413aa446d8931e4cbb0c12472717d06 (MD5) Previous issue date: 2001 / Doutorado

Orientador : Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T13:58:39Z (GMT). No. of bitstreams: 1 Chaves_Eclerion_D.pdf: 2686935 bytes, checksum: a0aae1903153a990c6baf47e2d25878c (MD5) Previous issue date: 2002 / Resumo: O objetivo deste estudo foi avaliar o efeito do tempo de armazenagem inicial na resistência à tração de três cimentos resinosos unidos à dentina. Foram utilizados 120 dentes bovinos. Os dentes foram embutidos, desgastados com lixas de granulação 220 e 600 e limpos em ultra-som. A seguir foram divididos em 3 grupos contendo 20 amostras: Grupo I foi usado o Cimento Rely X; Grupo II, Cimento Enforce e Grupo III, Cimento Dual Cement. As amostras de cada grupo foram cimentadas com os materiais preparados de acordo com as instruções de cada fabricante. A seguir, os dentes foram embutidos aos pares e posicionados em uma matriz, com as superfícies tratadas em contato entre si para o procedimento de fixação com o cimento resinoso. A resina foi fotopolimerizada por 160 segundos e os corpos-de-prova armazenados a 37° C e 100% de umidade relativa. A seguir, com o auxílio de uma matriz metálica, os corpos-de-prova foram submetidos ao ensaio de tração em uma máquina de ensaio universal INSTRON (modelo 4411) a velocidade de 1 mm/min. Metade das corpos-de-prova foram tracionadas após 30 minutos e a outra metade após 24 horas. Os resultados obtidos foram submetidos à análise de variância e ao teste de Tukey (p<0,05%). As médias obtidas foram as seguintes: Grupo I, 30 minutos = 2,53 (+0,49) MPa; 24 horas = 2,90 (+1, 12) MPa; Grupo II, 30 minutos = 1,65 (+0,46) MPa, 24 horas = 1,94 (+0,43) MPa; Grupo III, 30 minutos = 4,24 (+1,26) MPa; 24 horas = 6,14 (+01,80) MPa. Após o ensaio de resistência à tração, as superfícies fraturadas e representativas dos corpos-de-prova foram analisadas sob microscopia eletrônica de varredura para determinar o predomínio do padrão de fratura na interface. Tendo por base os resultados obtidos e discutidos na pesquisa podemos concluir que Os valores médios de resistência à tração, para os grupos I e II, obtidos a partir de corpos-de-prova tracionados nos períodos de 30 minutos não diferiram estatisticamente (p<0,05) dos tracionados em 24 horas, com exceção do grupo III que apresentou diferença estatística. Os valores médios de resistência á tração obtidos individualmente para os grupos I (Re/y X), grupo II (Enforce) e III (Dua/ Cement) apresentaram diferenças estatísticas significantes entre si (P<0,05). Comparando-se os tempos e os valores obtidos, verifica-se uma proporcionalidade direta entre o tempo e a resistência, o que implica em um tempo maior para que o processo de polimerização ocorra de forma satisfatória / Abstract: The objective of this study was to evaluate the effect of the initial storage time in tensile strength of three resin cements bonded to dentin. Sixty bovine teeth were used. The teeth were embedded, polished with silicon carbide papers of 220 and 600 grit and cleaned on ultra-sonic. They were divided in 3 groups of 20 samples each: Group I was fixed with Rely X cement; Group II, Enforce and Group III, Dual Cement. The samples of each group were lutted with the above materials according to each manufacturer's instructions. Half of the samples were tested after 30 minutes, and the other half, after 24 hours. The teeth were embedded to the pairs and positioned in adie stamp, with the surfaces face-to-face to each other and in contact for the adhesive procedure with the resin cement. The resin was photocured for 160 seconds and each specimen was them stored for 30 minutes or 24 hours at 37° C and 100% of relative humidity. With the aid of a metallic die stamp the samples were submitted to the tensile test in machine of universal test INSTRON I (model 4411) at speed of 1 mm/min. The results were submitted to the variance analysis and to Tukey's test (5%). The obtained averages were the following (SD): Group I, 30 minutes = 2,53 (+0,49) MPa; 24 hours = 2,90 (+1,12) MPa; Group II, 30 minutes = 1,65 (+0,46) MPa, 24 hours = 1,94 (+0,43) MPa; Group III, 30 minutes = 4,24 (+1,26) MPa; 24 hours = 6,14 (+01,80) MPa. After the tensile strength test, the surfaces of one of the tested samples were analyzed under SEM in order to determine the prevalence of the fracture pattern in the interface. Based upon the results obtained and discussed on this study can conclude that the mean values of tensile strength for groups I and groups II Obtained with the samples tested on the period of 30 mino did not differ statistically from those tested 24 h., except for group III that differ statistically. The Mean values of tensile strength of groups I, II e III were statistically different among them. Comparing time and values obtained, it is possible to verify a direct proportionality between time and strength, what means that a longer time is necessary to allow the polymerization process to occur in a satisfactory way / Doutorado / Materiais Dentarios / Doutor em Odontologia

Made available in DSpace on 2014-06-12T22:59:25Z (GMT). No. of bitstreams: 2 arquivo8476_1.pdf: 5038082 bytes, checksum: 0cb3583859984a2f9505d6348cd18d26 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2004 / Verificou-se a influência da remoção do colágeno sobre a adesão dentinária de sistemas restauradores adesivos através de avaliações da resistência adesiva à microtração (RA&#956;T) e da análise morfológica das interfaces adesivas em microscopia eletrômica de varredura (MEV). Molares humanos tiveram a dentina oclusal exposta, sendo distribuídos conforme os grupos: GSB (Single Bond/3M); GPB (Prime & Bond NT/Dentsply); GOC (One Coat Bond/Coltene/Vigodent); GPQ (PQ1/Ultradent); GSE (Clearfil SE Bond/Kuraray); GOU (One Up Bond F/Tokuyama). Cada grupo (n=12 - Ra&#956;T; n=3 - MEV) foi subdividido em 2 subgrupos quanto à forma de tratamento dentinário: 1 protocolo adesivo recomendado pelos fabricantes; 2 remoção do colágeno (H3PO4 15 s + NaOCl 5% por 2 min) + protocolo adesivo. Para os testes de RA&#956;T foram obtidos 9 corpos de prova por dente, com área de interface adesiva de 0,8 mm2 (± 0,2), os quais foram submetidos ao ensaio mecânico de RA&#956;T à velocidade de 0,5 mm/min. Para a MEV, após o preparo e tratamento das interfaces adesivas, realizou-se a metalização das superfícies e análise na linha de união. Os valores médios dos submetidos a ANOVA e teste de Tukey (&#945;=5%) foram em MPa(letras iguais = similaridade estatística): GSB1=60,70 (ab); GSB2=39,08 (de); GPB1=31,73 (e); GPB2=61,53 (a); GOC1=54,30 (abcd); GOC2=51,24 (abcd); GPQ1=39,11 (de); GPQ2=58,18 (abc); GSE1=44,11 (abcde); GSE2=51,00 (abcd); GOU1=42,2 (bcde); GOU2=40,18 (cde). A análise em MEV evidenciou ausência de camada híbrida em todos os grupos submetidos à desproteinização. A remoção das fibras colágenas interferiu positivamente sobre a adesão do sistema adesivo Prime & Bond NT/Dentsply e PQ1/Ultradent e negativamente para o Single Bond/3M ESPE

Orientadores: Luis Alexandre Maffei Sartini Paulillo, Luiz Andre Freire Pimenta / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T14:24:11Z (GMT). No. of bitstreams: 1 Marchi_GiselleMaria_D.pdf: 5365510 bytes, checksum: 46a61daae12bf4219a7bd5f82c5c8439 (MD5) Previous issue date: 1998 / Resumo: A preservação e a restauração de dentes severamente debilitados sem suporte dentinário no terço cervical do canal radicular é um procedimento difícil. A reconstrução dessas rafzes possibilitaria tratamentos mais conservadores. Por isso, o objetivo deste trabalho foi avaliar a resistência à fratura de rafzes hfgidas e debilitadas reconstrufdas internamente com diferentes materiais de preenchimento atuando como IIdentina artificial" associados a pino intra-radicular. Foram selecionadas 75 rafzes de incisivos inferiores bovinos com volumes semelhantes. Dessas, sessenta foram desgastadas internamente até apresentarem dimensões padronizadas, simulando enfraquecimento. As rafzes debilitadas foram preenchidas com diferentes adesivos dentinários e materiais restauradores, sendo que em trinta delas os pinos pré-fabricados eram posicionados junto com o material de preenchimento. As demais rafzes debilitadas reconstrufdas e as hfgidas' foram preparadas para receber os pinos intra-radiculares, posteriormente fixados com o agente cimentante resinoso. Foram obtidos, assim, cinco grupos experimentais: GRUPO 1 - raiz hfgida com pino pré-fabricado fixado com agente cimentante resinoso; GRUPO 2 - raiz debilitada preenchida com agente cimentante resinoso associado ao pino pré-fabricado; GRUPO 3 - raiz debilitada preenchida com cimento de ionômero de vidro modificado por resina associado ao pino pré-fabricado; GRUPO 4 - raiz debilitada preenchida com resina composta mod,ificada por poliácido e com posterior fixação do pino pré-fabricado com agente cimentante resinoso e GRUPO 5 - raiz debilitada preenchida com resina composta e com posterior fixação do pino pré-fabricado com agente cimentante resinoso. Os corpos-de-prova foram submetidos ao teste de resistência à fratura com aplicação de carregamento tangencial de compressão em um ângulo de 1350 em relação ao longo eixo da raiz, a uma velocidade de 0,5mm/min. Os resultados mostraram diferenças estatisticamente significantes em relação à condição da raiz, sendo as hfgidas mais resistentes à fratura que as debilitadas. Avaliando o material de preenchimento, as rafzes restauradas com o agente cimentante ALL BOND C&B apresentaram os menores valores de resistência à fratura, mostrando diferença estatisticamente significante apenas quando comparado ao VITREMER. Já os materiais VITREMER, DYRACT AP e Z100 exibiram o mesmo comportamento, não havendo, entre eles, diferenças estatisticamente significantes / Abstract: The preservation and the restoration of severely weakened teeth, without dentinal support in the cervical zone of the radicular canal is a difficult procedure. The reconstruction of these roots would make possible more conservative treatments. That is why, the purpose of this study was to evaluate the resistance to fracture of whole and weakened root internally reconstructed with different filling materiais acting as an "artificial dentin" associated to the prefabricated post into the root canal. Seventy-five roots were selected of bovine mandibular incisors with similar bulks. From those, sixty roots were internally wore until presente standardized dimensions, simulating weakened roots. Those roots were filled with different dentinal adhesives and restorative materiais, being thirty of them with the prefabricated posts placed with the filling material. The other weakened filled roots and the whole roots were prepared to receive the intraradicular posts, subsequently fixed with resin cement agent. Thus, were obtained five experimental groups: GROUP 1 - whole root with prefabricated post fixed with resin cement agent; GROUP 2 - weakened root filled with resin cement agent; GROUP 3 - vyeakened root filled with resin-modified glass ionomer associated to the prefabricated post; GROUP 4 - weakened root filled with resin modified by polyacid and with posterior fixing of the prefabricateá post with resin cement agent and GROUP 5 - weakened root filled with composite resin and with posterior fixing of the prefabricated post with resin cement agent. The specimens were submitted to resistance test to fracture with compressive load in an angle of 135 degrees in relation to the long axis of the root, in a speed of 0,5 mm/min. The results showed statiscally significant differences in relation to the condition of the root, being the whole roots more resistants to fracture than the weakened roots. Evaluating the filling material, roots restorated with the resin cement agent ALL BONO C&B presented the least values of resistance to fracture, showing statiscally significant difference only when compared with the VITREMER. The materiais VITREMER, OYRACT AP and Z100 had the same behaviour, do not existing statiscally significant differer:tces among them / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T06:31:48Z (GMT). No. of bitstreams: 1 Giannini_Marcelo_D.pdf: 3468860 bytes, checksum: 8e09eea409a499afa63cd91a42e309b7 (MD5) Previous issue date: 1999 / Resumo: O propósito deste estudo foi o avaliar efeito da densidade (DT) e da área ocupada pelos túbulos dentinários (AO) na resistência à tração (RT) de dois sistemas adesivos: Clearfil Liner Bond 2/Kuraray (LB) e Prime & Bond 2.1/Dentsply (PB). Dezenove terceiros molares humanos foram abrasionados a partir da superfície oclusal com lixas de SiC (granulação 600), para exporem uma superfície plana em 3 diferentes níveis de profundidade dentinária: profunda, média e superficial. Os sistemas adesivos foram aplicados de acordo com as recomendações dos fabricantes e coroas de compósito (Z 100/3M) com altura de 10 mm foram confeccionadas nessas superfícies. Após 24 horas de armazenamento em solução salina a 37° C, secções foram realizadas paralelamente ao longo eixo das amostras nos sentidos mésio-distal e vestíbulo-lingual. De cada amostra foram retirados três espécimes, os quais foram submetidos ao teste de microtração com velocidade de 0,5mm/min. Os espécimes que fraturaram na interface de união, tiveram sua superfície em dentina polida ('AL IND.2¿ O IND. 3¿-1000) e condicionada com ácido fosfórico 37% por 15 segundos, para serem observados em MEV em magnificações de 1000X e 4000X. Os valores médios de RT, em MPa, foram: LB:26,04 '+ Ou ¿' 10,25 e PB: 42,64 '+ Ou ¿' 15,20. A análise de regressão linear mostrou, para o adesivo PB, uma significante relação inversa (p<0,05). entre DT e RT ('R POT. 2¿ = 0,6309); e AO e RT (('R POT. 2¿ = 0,6638). Nenhuma correlação estatisticamente significante (p>0,05) foi observada entre os dois parâmetros (TD X RT - ('R POT. 2¿ = 0,0508 e AO X RT - ('R POT. 2¿ = 0,2066) para o adesivo LB. Os resultados sugerem que quanto maior a DT e AO, menor a RT para o adesivo PB. O adesivo PB apresentou valores médios de RT superiores em relação ao adesivo LB / Abstract: The purpose of this study was evaluate the influence of tubule density (TD) and the area they occupy (AO) on tensile bond strength (BS) to dentin of two adhesive system; Prime & Bond 2.1/Dentsply (PB) and Clearfil Liner Bond 2/Kuraray (LB). Nineteen extracted human third molars were abraded with SiC paper discs (600-grit) from the occlusal surface to expose superficial, middle or deep dentin. The adhesive systems were applied to the fIat exposed surfaces according to the manufacturer's instructions and resin build-up "crowns" approximately 10.0 mm high were constructed incrementaly with resin composite (Z-100/3M). After 24 hours storage in physiological saline at 37 °C, the bonded specimens were serially sectioned in both "x"and "y" directions transversally to the bonded interface to obtain three repetitions of bonded sticks, per tooth. Each bonded stick was tested under tension in a DL-500 (Emic) tester aí 0,5mm/min. The specimens which failed adhesively at an interface, had their bonded dentin surface briefly abraded (1000 -grit ('AL IND.2¿ O IND. 3¿) and etched with 37% phosphoric acid for 15 seconds. This was, to permit SEI to be taken at 1000X and 4000X (DSM 940-A/Zeiss) and the DT and AO to be calculated per area (mm2). Mean bond strength of specimens tested were, in MPa LB: 26.04 '+ Ou ¿' 10.25 e PB: 42.64 '+ Ou ¿' 15.20. For PB the linear regression showed a significant (p<0.05) inverse relationship between the DT and BS ('R POT. 2¿ = 0.6309); and AO and BS strength ('R POT. 2¿ = 0.6638). No statistically significant correlation was observed between the two parameters for LB (TD X BS - 'R POT. 2¿ = 0.0508 e TA X BS - 'R POT. 2¿ = 0.2066). Results suggest that the greater the TD and greater the TA, the lower the BS of PB adhesive system to dentin. PB showed significantly high bond strengths than LB / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:34:21Z (GMT). No. of bitstreams: 1 Guimaraes_IsadoraRabelo_D.pdf: 1408417 bytes, checksum: 663b3f486f91d8f3589f07a988f8ba2c (MD5) Previous issue date: 2015 / Resumo: O objetivo deste estudo foi avaliar o efeito da interação de sistemas adesivos multi-mode e cimentos resinosos de polimerização química e dual sobre a superfície da dentina. Quarenta terceiros molares humanos não cariados foram separados em 5 grupos (n=8). Uma superfície plana em dentina foi obtida para cada dente. Blocos de 3,0x12x12 mm de resina composta indireta (Lava Ultimate) foram jateados com partículas óxido de alumínio e cimentados na superfície de dentina, formando os seguintes grupos: I- All Bond Universal fotoativado (AB)/C&B Bond Cement (CB); II- Scotchbond Universal fotoativado (SBU)/RelyXUltimate químico (RXU); III- SBU fotoativado/RXU fotoativado, IV- SBU químico/RXU fotoativado, V- SBU químico /RXU químico. Após a cimentação, os dentes foram mantidos em umidade relativa a 37?C por 24 horas. Os dentes foram seccionados para obter palitos de aproximadamente 0,8 mm². Os espécimes foram posicionados na máquina de ensaio universal EZ-Test para o ensaio de resistência de união com uma velocidade de 0,5 mm/min. Os dados foram estatisticamente analisados por ANOVA um fator e Teste de Fisher's PLSD (?=0,05). Os modos de fratura foram analisados e classificados em microscópio eletrônico de varredura. Para análise das interfaces dentina/adesivo/cimento, cinco espécimes de cada grupo foram corados com Rodamina B a 1% por uma hora e analisados em microscópio confocal de varredura a laser. Nenhuma diferença estatística de resistência da união (MPa) foi observada entre os grupos: I- 59,9 (9,3); II- 57,6 (15,9); III- 63,9 (12,7) e IV- 53,7 (13,9), e todos foram diferentes estatisticamente do grupo V, que apresentou o menor valor de resistência da união 16,2 (6,4). O modo de fratura coesivo foi predominante na interface entre o adesivo e cimento resinoso em todos os grupos. A análise ultraestrutural sugere a interação entre os sistemas adesivos multi-mode e o cimento resinoso na dentina, quando o adesivo ou o cimento resinoso foi fotoativado. A interação adesiva ocorreu entre os adesivos multi-mode e cimentos resinosos, sempre que o adesivo e/ou o cimento resinoso foi fotoativado / Abstract: This study evaluated the dentin surface interaction effect of multi-mode adhesives on bonding to chemical-cured and dual-cured resin cements. Forty non-carious human third molars were divided into five groups (n=8). A flat dentin surface was created for each tooth. Indirect resin composite block 3,0x12x12 mm (Lava Ultimate) were sandblasted with aluminum oxide particles and cemented to the dentin surface following the treatment groups: I- All Bond Universal light-cured/C&B Bond (self-cured cement), II- Scotchbond Universal (SBU) light-cured/RelyX Ultimate (RXU) self-cured, III- SBU light-cured/RXU light-cured, IV - SBU no light-cured/RXU light-cured and V- SBU no light-cured/RXU self-cured. After 24 h, the teeth were sectioned into beans to produce a cross-sectional area of 0.8 mm². Specimens of each group were individually mounted on a jig and placed on a tensile testing universal machine. A tensile force was applied at a 0.5mm/min cross-speed. The bond strength was recorded and failure modes were classified using scanning electron microscopy. In order to observe dentin/adhesive-cement interface, selected beans from each group were stained with 0.1% Rodhamine B for 1 h and analyzed using Confocal Laser Scanning Microscopy. Statistical analysis was performed using ANOVA and Fisher¿s PLSD test (?=0.05). For bond strength (MPa) no statistical difference of was observed among the groups: I - 59.9 (9.3); II- 57.6 (15.9); III - 63.9 (12.7) and IV- 53.7 (13.9). Group V showed statistical lower average value 16.2 (6.4) compared with all others groups. Cohesive failure modes occurred predominately along of adhesive and resin cement to all groups. The ultrastructural observation suggested the dentin surface interaction between multi-mode adhesives and resin cement when the adhesive or resin cement was light-cured. The adhesive interaction occurred between multi-mode adhesive systems and resin cements whenever the adhesive and/or resin cement was light-activated / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários

Orientador: Sergio Eduardo de Paiva Gonçalves / Coorientadora: Paulette Spencer / Banca: Flávia Lucisano Botelho do Amaral / Banca: Taciana Marco Ferraz Caneppele / Banca: Alessandra Cassoni Ferreira / Banca: Renata Marques de Melo Marinho / Resumo: O objetivo desse estudo foi avaliar um adesivo experimental com diferentes concentrações de água, bem como sua degradação morfológica, química, física e mecânica. A primeira etapa envolveu a manipulação do adesivo experimental contendo 45/55% de HEMA e BisGMA, 0.5% de canforoquinona, 0.5% EDMAB e 1% de DPIHP. Foram incorporadas diferentes concentrações de água a partir dessa formulação adesiva (0, 10 e 16%). Os modelos adesivos foram fotopolimerizados e as análises iniciais realizadas: Morfológicas (Estereomicroscopio e Micro-xct); Físicas (Rugosidade-Ru, Sorção-Sor, Solubilidade-Sol); Químicas (Grau de conversão-GC, Mapeamento do espécime com 16% de água e os monômeros liberados pela CLAE); Mecânicas (Resistência flexural-RF, Módulo de elasticidade-ME e Resistência a compressão-RC). Em seguida os espécimes foram divididos conforme a solução de envelhecimento (água, etanol e acetona). Foram realizadas novas análises após o envelhecimento por 2 e 84 dias. Os testes estatísticos ANOVA e Tukey (5%) foram realizados. Os resultados iniciais, sem o envelhecimento, mostraram que as diferentes concentrações de água influenciam as propriedades dos adesivos. Na análise morfológica notou-se a presença de bolhas no espécime com 16% de água. Para a Ru e GC os maiores valores foram encontrados para os espécimes com mais água em sua composição e os menores para 0%. Já nas análises mecânicas, para RF e ME os espécimes com 10% de água foram mais resistentes; e em RC os espécimes com 16% foram... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was evaluated an experimental adhesive with different water content, as well the degradation morphological, physical, chemical and mechanical. Firstly the dental adhesive was manipulated with 45/55% of HEMA and BisGMA, 0.5% of CQ, 0.5% EDMAB e 1% of DPIHP. Was added different water content (0, 10 and 16%). The adhesive model was cured and the analysis was done: Morphological (Stereomicroscope and Micro-xct); Physical (Surface Roughness), Sorption, Solubility); Chemical (Degree of convertion, Map of the pore on 16% water content sample and the released monomers- HPLC); Mechanicals (Flexural strength, Modulus of elasticity and Compressive strength). After the these analyzes, the samples were divided to each evaluation into 3 groups according to solution for performed ageing (water, ethanol and acetone). Further analyzes were performed after aging for 2 and 84 days. Statistical tests of ANOVA and Tukey (5%) were performed. Initial results, without aging, showed that the different water content influence adhesive properties. In the morphological analysis, bubbles were present on the sample with 16% water. For Ru and DC all specimens differed from each other, with the highest values for the specimens with 16% and the lowest to 0%. In the mechanical analyzes, for RF and ME the specimens with 10% water were more resistant; and in RC the specimens with 16% were less resistant. After aging it is possible notice cracks on the border of specimens 0% and 16% in the ... (Complete abstract click electronic access below) / Doutor

O objetivo deste trabalho foi avaliar a resistência adesiva e o padrão de condicionamento do esmalte e da dentina após aplicação do ácido bórico a 2%. Foram utilizados terceiros molares humanos, condicionados com o ácido fosfórico a 35%, em forma de gel, e com diferentes formas de apresentações do ácido bórico a 2%. Para o estudo do padrão de condicioname nto, utilizaram-se discos de dentina e espécimes quadrangulares de esmalte que sofreram o condicionamento com as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% utilizadas por diferentes tempos de aplicações. Após os condicionamentos, os espécimes foram preparados para observação no microscópio eletrônico de varredura. Para a avaliação da resistência adesiva do esmalte e da dentina, através de testes de microtração, foram utilizadas as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% previamente à aplicação de dois sistemas adesivos (Single-Bond e Prime & Bond NT) e de duas resinas composta (Z-250 e TPH). Após os procedimentos adesivos, os dentes sofreram seccionamentos seriados a fim de que fossem obtidos espécimes para os testes de resistência adesiva. Os valores adesivos foram submetidos ao teste de análise de variância (ANOVA) e ao teste de Tukey, para a verificação de possíveis diferenças estatísticas entre os grupos, e em ambos os testes foi adotado um nível de significância de 5% (p< 0,05%). Na dentina e no esmalte, a solução de ácido fosfórico a 35% apresentou um maior poder desmineralizante comparado com as soluções de ácido bórico a 2%. Com relação aos valores de resistência adesiva na dentina, quando se utilizaram as diferentes soluções ácidas com o sistema adesivo Single-Bond e a resina composta Z-250, o grupo condicionado com ácido fosfórico apresentou valores adesivos significantemente maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Porém, quando se utilizou o sistema adesivo Prime & Bond NT e a resina composta TPH, os valores adesivos dos grupos que sofreram os diferentes condicionamentos ácidos não apresentaram diferenças estatísticas entre si. No esmalte, quando se utilizaram as diferentes soluções ácidas em associação com o sistema adesivo Single-Bond e a resina composta Z-250, e também com o sistema adesivo Prime & Bond NT e a resina composta TPH, os grupos que sofreram o condicionamenmto com o ácido fosfórico a 35% apresentaram valores adesivos significantementre maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Assim, pode-se concluir que o tratamento superficial da dentina e do esmalte com as soluções de ácido bórico a 2% não forneceu substratos com características suficientes para proporcionar resistência adesiva semelhante à fornecida pelo ácido fosfórico a 35%. / The aim of this laboratory work was to evaluate the bond strength and etching pattern of dentin and enamel conditioned by 2% boric acid. In this study, human third molars etched with 35% phosphoric acid and different solutions of 2% boric acid were utilized. For the etching pattern determination discs of dentin and square enamel specimens were conditioned (35% phosphoric acid and 2% boric acid solutions) and prepared for scanning electron microscopic observations. For dentin and enamel bond strengths evaluation the microtensile test was used. Phosphoric acid (35%) and boric acid (2%) were utilized in combination with two adhesive systems (Single-Bond and Prime & Bond NT) and two different composite resins (Z-250 and TPH). After bonding procedures, the teeth were sectioned and the obtained specimens submitted for microtensile tests. The results were analyzed by ANOVA followed Tukey’s analysis at a significance level of 5% (p<0,05). The 35% phosphoric acid solution presented higher demineralization power when compared to 2% boric acid solutions either in dentin or enamel. Regarding to the bond strength in dentin, when 35% phosphoric acid solution was used in combination with Single-Bond adhesive system and Z-250 composite resin the values were significantly higher when compared to other acid solutions. Therefore,whem the Prime & Bond NT adhesive system and TPH composite resin were utilized,no statisticaly different values were demonstrated for bond strenght among different acid solutions. In enamel, different acid solutions were also combined with Single-Bond and Prime & Bond adhesive systems and Z-250 and TPH composite resins. Groups etched with 35% phosphoric acid solution presented bond strength values significantly higher than other acid solutions. In conclusion, the utilization of 2% boric acid solution for etching dentin or enamel did not provide characteristics in this substrates and bond strength values similar to 35% phosphoric acid solution.

Tese de mestrado integrado. Engenharia Mecânica. Faculdade de Engenharia. Universidade do Porto. 2010

Tese de mestrado integrado. Engenharia Mecânica. Faculdade de Engenharia. Universidade do Porto. 2010