• Refine Query
  • Source
  • Publication year
  • to
  • Language
  • 40
  • 2
  • 1
  • Tagged with
  • 43
  • 34
  • 13
  • 13
  • 13
  • 12
  • 10
  • 10
  • 10
  • 9
  • 9
  • 8
  • 8
  • 8
  • 7
  • About
  • The Global ETD Search service is a free service for researchers to find electronic theses and dissertations. This service is provided by the Networked Digital Library of Theses and Dissertations.
    Our metadata is collected from universities around the world. If you manage a university/consortium/country archive and want to be added, details can be found on the NDLTD website.
41

Estudos de síntese e processamento de compósitos de óxido de níquel-céria dopada utilizados como anodo de células a combustível de óxido sólido de temperatura intermediária (IT-SOFC) / Synthesis and processing study of nickel oxide doped ceria composites used as anode of intermediate temperature solid oxide fuel cells (IT-SOFC)

Alexander Rodrigo Arakaki 23 July 2014 (has links)
Este trabalho compreendeu os estudos de síntese química de pós por via úmida, de processamento cerâmico e de redução do óxido de níquel contido nos compósitos de céria dopada com samária e gadolínia, aplicados, principalmente, como anodos de Células a Combustível de Óxido Sólido. A rota adotada para a preparação dos pós com composição Ce0,8(SmGd)0,2O1,9/NiO e proporção em massa de 40 : 60% foi a coprecipitação de hidróxidos associada ao tratamento solvotérmico, utilizando-se como matérias-primas cloretos de cério, níquel, samário e gadolínio. O surfactante aniônico brometo de cetil trimetil amônio (CTAB) também foi utilizado na etapa de precipitação na relação molar Metal / CTAB entre 1 e 3. A influência do solvente orgânico utilizado no tratamento solvotérmico dos pós foi analisada utilizando o etanol, propanol e o butanol, nas condições de temperatura de 150ºC por 16 h, com e sem calcinação a 600ºC por 1h, e moagem em moinho de bolas. As amostras compactadas foram sinterizadas em temperaturas entre 1200 e 1400ºC por 1h. A redução in situ do NiO-SGDC foi estudada na amostra cerâmica preparada nas seguintes condições: síntese por coprecipitação usando ou não o CTAB, tratamento solvotérmico em butanol, calcinação a 600ºC, prensagem e sinterização a 1350ºC por 1h. O processo de redução das amostras sintetizadas em butanol foi avaliado em forno tubular em atmosfera dinâmica de 4%H2/Ar, fixando-se a temperatura a 900°C e variando-se o tempo entre 10 e 120 minutos. A redução também foi relizada nos compósitos sintetizados utilizando o CTAB na proporção Metal/CTAB = 2, tratados termicamente em etanol e butanol, após calcinação, prensagem e sinterização em forno tubular sob atmosfera de H2/Ar em isotermas de 700, 800 e 900°C por períodos entre 2 e 240 minutos. Os pós, as cerâmicas e os compósitos sintetizados em laboratório foram comparados com os materiais compósitos produzidos com pós de origem comercial. A caracterização dos pós foi realizada por difração de raios X (DRX), microscopia eletrônica de varredura (MEV), área de superfície específica por adsorção gasosa de nitrogênio (BET), análise térmica (TG/DTA) e distribuição granulométrica por espalhamento de feixe laser (Cilas). As cerâmicas foram analisadas por microscopia eletrônica de varredura, DRX e medidas de densidade pela técnica de imersão em água (método de Arquimedes). As cerâmicas e os compósitos foram caracterizados eletricamente por medidas de resistência elétrica pelo método de quatro pontas DC. Os resultados mostraram que os pós sem calcinação apresentaram as estruturas cristalinas características da céria e do hidróxido de níquel, e elevada área de superfície específica (80 m2/g). As cerâmicas provenientes dos pós tratados com etanol e propanol apresentaram boa homogeneidade química, estrutural e valores de densidade de 99% em relação a densidade teórica. Verificou-se que 80 a 90% do NiO é reduzido e as porosidades atingidas pelos compósitos são da ordem de 30%. A caracterização elétrica mostrou que a condutividade iônica da fase cerâmica do anodo, sintetizado solvotermicamente em butanol, possui valor de 0,03S.cm-1 na temperatura de 600°C, valor superior aos encontrados na literatura. A caracterização elétrica dos compósitos reduzidos revelou alta condutividade elétrica característica do níquel metálico, indicando percolação adequada da fase de níquel e distribuição homogênea de ambas fases cerâmica e metálica. As rotas de síntese e os materiais estudados são, portanto, adequados para a aplicação como anodo das IT-SOFCs. / This work comprises studies of powder chemical synthesis by wet route, ceramic processing and reduction of nickel oxide added to samaria and gadolinia doped ceria ceramic composite, mainly applied as Solid Oxide Fuel Cells anode. The route adopted for the powders preparation with composition Ce0.8(SmGd)0.2O1.9/NiO and mass ratio of 40:60% was hydroxides coprecipitation and solvothermal treatment, using as start materials the cerium, nickel, samarium and gadolinium chlorides. The anionic surfactant cetyltrimethylammonium bromide (CTAB) was also used in the precipitation stage with the molar ratio Metal/CTAB ranging between 1 and 3. The influence of organic solvent used in the powders solvothermal treatment was analyzed by using ethanol, propanol and butanol at temperature of 150°C for 16h, with and without calcination at 600°C for 1h, and grinding in a ball mill. The compacted samples were sintered at temperatures between 1200 and 1400°C for 1h. The in situ reduction of NiO-SGDC was studied in the samples synthesized by coprecipitation using CTAB and without it, followed by solvothermal treatment in butanol, calcined at 600°C, pressed and sintered at 1350°C for 1h. The reduction procedure was evaluated in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 900°C and time range between 10 and 120 minutes. The composites synthesized using the CTAB in the proportion of Metal/CTAB = 2, followed by solvothermal treatment in ethanol and butanol, after calcining, compaction and sintering, was also reduced in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 700, 800 and 900°C and time range between 2 and 240 minutes. The powders, ceramics and the sinterized cermets syntesized in laboratory were compared to the materials produced with comercial powders. The powders characterization was performed by X-ray diffraction (XRD), scanning electron microscopy (SEM), specific surface area by nitrogen gas adsorption (BET), thermal analysis (TG / DTA) and particle size distribution by scattering beam laser (Cilas). Ceramics were analyzed by scanning electron microscopy (SEM), XRD and density measurements by the technique of immersion in water (Archimedes method). The ceramics and cermets condutivity was characterized by the four probe DC method. The results obtained showed that the powders without calcination presented the crystal structures characteristics of ceria and nickel hydroxide, and high specific surface area (80m2/g) . The ceramic prepared from powders treated with ethanol and propanol had a high chemical and structural homogeneity and density values corresponding to 99% of the theoretical density. It was found that 80 to 90 % of NiO is reduced and the porosity of the composite reached about of 30 %. The anode ceramic phase synthesized solvothermically in butanol presented electrical conductivity of 0.03S.cm-1 at 600°C, higher than found at literature. The reduced cermets electrical characterization showed high electrical conductivity feature of metallic nickel, indicating the nickel phase good percolation and homogeneous distribution of both ceramic and metallic phases. Considering all these results, the synthesis routes and studied materials are suitable for use as the anode IT- SOFCs.
42

Densificação e condutividade elétrica da Zircônia-Escândia-Céria / Densification and electrical conductivity of Zirconia-Scandia-Ceria

Robson Lopes Grosso 22 May 2012 (has links)
Estudos recentes demonstram que o sistema cerâmico zircônia-escândia-céria (ScCeSZ) apresenta-se promissor para aplicações como eletrólito sólido em células a combustível de óxido sólido de temperaturas intermediárias de operação (600 a 800 °C). Neste trabalho, foi realizada a sinterização convencional, de duas etapas e assistida por campo elétrico do ZrO2 contendo 10% em mol de Sc2O3 e 1% em mol de CeO2 comercializado pela Fuel Cell Materials visando melhorar a densificação com reduzido tamanho médio de grãos. A condutividade elétrica de amostras densas de ScCeSZ sinterizadas pelos diferentes métodos foi investigada por espectroscopia de impedância. Diferentes condições de sinterização foram analisadas. A taxa de retração dos compactos é máxima a 1180 °C, determinada pela análise de dilatometria. Foi confirmado por difração de raios X que a adição de céria à zircônia-escândia promove a estabilização da fase cúbica à temperatura ambiente. No entanto, dependendo das condições de sinterização pode haver a formação de fases secundárias, as quais foram detectadas por difração de raios X e espectroscopia Raman. A sinterização assistida por campo elétrico promoveu a formação das fases cúbica e tetragonal. Considerando os métodos convencional e de duas etapas, para a obtenção do material cúbico monofásico é necessária uma seleção cuidadosa das condições de sinterização. Os valores de condutividade elétrica estão de acordo com as condutividades do ScCeSZ reportadas na literatura. / Recent reports show that scandia-and ceria-doped zirconia (ScCeSZ) is a promising material for application as solid electrolyte in solid oxide fuel cells operating at intermediate temperatures (600 - 800 °C). In this work, ZrO2 containing 10 mol% Sc2O3 and 1 mol% CeO2 commercial powder (Fuel Cell Materials) was used to investigate the densification along with the mean grain size in specimens sintered by different methods: conventional, two-step sintering and electric field assisted sintering. The electrical conductivity of dense sintered specimens was studied by impedance spectroscopy. The linear shrinkage was followed by dilatometry. The maximum shrinkage rate of powder compacts was obtained at 1180 ºC. X-ray diffraction experiments revealed that ceria stabilizes the cubic phase of scandia-doped zirconia at room temperature. However, secondary phases (rhombohedric and tetragonal) were detected by both X-ray diffraction and Raman spectroscopy depending on the sintering conditions. The field assisted sintering method resulted in specimens with cubic and tetragonal phases. In the case of conventional and two-step sintering methods, a careful selection of the temperatures and sintering times is essential to obtain a cubic single-phase material. Values of the electrical conductivity of ScCeSZ are in general agreement with those reported in the literature.
43

Densificação e condutividade elétrica da Zircônia-Escândia-Céria / Densification and electrical conductivity of Zirconia-Scandia-Ceria

Grosso, Robson Lopes 22 May 2012 (has links)
Estudos recentes demonstram que o sistema cerâmico zircônia-escândia-céria (ScCeSZ) apresenta-se promissor para aplicações como eletrólito sólido em células a combustível de óxido sólido de temperaturas intermediárias de operação (600 a 800 °C). Neste trabalho, foi realizada a sinterização convencional, de duas etapas e assistida por campo elétrico do ZrO2 contendo 10% em mol de Sc2O3 e 1% em mol de CeO2 comercializado pela Fuel Cell Materials visando melhorar a densificação com reduzido tamanho médio de grãos. A condutividade elétrica de amostras densas de ScCeSZ sinterizadas pelos diferentes métodos foi investigada por espectroscopia de impedância. Diferentes condições de sinterização foram analisadas. A taxa de retração dos compactos é máxima a 1180 °C, determinada pela análise de dilatometria. Foi confirmado por difração de raios X que a adição de céria à zircônia-escândia promove a estabilização da fase cúbica à temperatura ambiente. No entanto, dependendo das condições de sinterização pode haver a formação de fases secundárias, as quais foram detectadas por difração de raios X e espectroscopia Raman. A sinterização assistida por campo elétrico promoveu a formação das fases cúbica e tetragonal. Considerando os métodos convencional e de duas etapas, para a obtenção do material cúbico monofásico é necessária uma seleção cuidadosa das condições de sinterização. Os valores de condutividade elétrica estão de acordo com as condutividades do ScCeSZ reportadas na literatura. / Recent reports show that scandia-and ceria-doped zirconia (ScCeSZ) is a promising material for application as solid electrolyte in solid oxide fuel cells operating at intermediate temperatures (600 - 800 °C). In this work, ZrO2 containing 10 mol% Sc2O3 and 1 mol% CeO2 commercial powder (Fuel Cell Materials) was used to investigate the densification along with the mean grain size in specimens sintered by different methods: conventional, two-step sintering and electric field assisted sintering. The electrical conductivity of dense sintered specimens was studied by impedance spectroscopy. The linear shrinkage was followed by dilatometry. The maximum shrinkage rate of powder compacts was obtained at 1180 ºC. X-ray diffraction experiments revealed that ceria stabilizes the cubic phase of scandia-doped zirconia at room temperature. However, secondary phases (rhombohedric and tetragonal) were detected by both X-ray diffraction and Raman spectroscopy depending on the sintering conditions. The field assisted sintering method resulted in specimens with cubic and tetragonal phases. In the case of conventional and two-step sintering methods, a careful selection of the temperatures and sintering times is essential to obtain a cubic single-phase material. Values of the electrical conductivity of ScCeSZ are in general agreement with those reported in the literature.