11 |
Efeito do ultrassom na resistência de união de cimentos resinosos autoadesivos à dentinaSilva, Diego Fabris Ferreira da January 2012 (has links)
Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-05-16T12:10:29Z
No. of bitstreams: 1
438292.pdf: 353384 bytes, checksum: e966b89cb4618df13c2f46329c3c7c3f (MD5) / Made available in DSpace on 2012-05-16T12:10:29Z (GMT). No. of bitstreams: 1
438292.pdf: 353384 bytes, checksum: e966b89cb4618df13c2f46329c3c7c3f (MD5) / O objetivo desse estudo foi avaliar a influência da vibração ultrassônica na resistência de união de cimentos resinosos autoadesivos à dentina. Vinte e quatro dentes terceiros molares foram divididos aleatoriamente em quatro grupos (n=6/grupo): G1 – RelyX Unicem; G2 – Maxcem Elite; G3 – RelyX Unicem com vibração ultrassônica; G4 – Maxcem Elite com vibração ultrassônica. Blocos de resina composta foram cimentados sobre dentina plana com carga de 500 g por 2 min, seguido de fotoativação nos G1 e G2. Em G3 e G4, a vibração ultrassônica foi aplicada por 20 s sobre o bloco de resina composta, seguido de carga de 500 g por 1 min e 40 s e fotoativação. Após armazenagem em água destilada a 37º C por 24 h, seis conjuntos dente/resina foram cortados paralelamente ao longo eixo do dente, nos sentidos x e y, com secção de aproximadamente 0,8 mm2. Foram obtidos 24 corpos de prova para cada grupo, sendo então submetidos ao teste de resistência à microtração (Rμt) em máquina de ensaio universal com velocidade de 0,5 mm/min. De acordo com Análise de Variância Fatorial, as variáveis tipo de cimento resinoso (p=0,000) e tipo de cimentação (p=0,002) foram significativas. A interação das duas varáveis não foi significativa (p=0,676). De acordo com o teste t-student (α=0,05) a média de Rμt com uso da vibração ultrassônica (13,74 MPa) foi estatisticamente superior sem aplicação da vibração ultrassônica (10,57 MPa)). A média de Rμt do RelyX Unicem (13,95 MPa) foi estatisticamente superior ao Maxcem Elite (10,36 MPa). A vibração ultrassônica aumentou a resistência de união dos cimentos resinosos autoadesivos RelyX Unicem e Maxcem Elite à dentina. / The aim of this study was to evaluate the influence of ultrasonic application on bond strength of self-adhesives resin cements to dentin. Twenty-four third molars were randomly divided into 4 groups (n=6/group): G1 - Rely X Unicem; G2 – Maxcem Elite; G3 – RelyX Unicem and ultrasonic application; G4 – Maxcem Elite and ultrasonic application. Composite resin blocks were luted to flat dentin with a load of 500 g for 2 min, followed by light polymerization in G1 and G2. In G3 and G4, the ultrasonic device was applied for 20 s on the composite resin block, followed by 500 g load for 1 min and 40 s, and light polymerization. After storage in distilled water at 37ºC for 24 h, six tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of about 0.8 mm2. Twenty-four specimens were obtained to each group, and submitted to microtensile bond strength (μTBS) test in an universal testing machine at 0,5 mm/min crosshead speed. According to two-way ANOVA, type of cement factor (p=0.000) and type of luting factor (o=0.002) were significant. The interaction was not significant (p=0676). According to student-t test (α=0.05), the μTBS mean with ultrasonic application (13.74 MPa) was statistically higher than without this treatment (10.57 MPa). The μTBS mean of RelyX Unicem (13.95 MPa) was statistically higher than Maxcem Elite (10.36 MPa). The ultrasonic application increased the μTBS of the RelyX Unicem and Maxcem Elite to dentin.
|
12 |
Influência de diferentes cargas de cimentação na resistência de união de cimentos resinosos à dentinaPaludo, Tamara January 2012 (has links)
Submitted by Ginamara Lima (ginaj@pucrs.br) on 2012-05-04T12:15:08Z
No. of bitstreams: 1
438178.pdf: 2149932 bytes, checksum: 72e349d1108a96e32586f332a6db74c4 (MD5) / Made available in DSpace on 2012-05-04T12:15:08Z (GMT). No. of bitstreams: 1
438178.pdf: 2149932 bytes, checksum: 72e349d1108a96e32586f332a6db74c4 (MD5) / Este trabalho avaliou a influência de diferentes cargas de cimentação na resistência de união de cimento resinoso convencional e autoadesivo. Para isso, foram selecionados 42 molares humanos hígidos. Os dentes foram desgastados em politriz até a remoção de esmalte. Os dentes tiveram suas raízes embutidas em resina acrílica autopolimerizável. Foram confeccionadas pastilhas de resina composta (Filtek Z 350 XT, 3M ESPE), conforme as orientações do fabricante. Para cimentação com cimento resinoso convencional Rely X ARC (3M ESPE) – Grupo 1 foi realizado condicionamento ácido da superfície (ácido fosfórico 37%), lavagem, secagem com algodão, aplicação de duas camadas de adesivo (Adper Single Bond 2) e fotoativação através de um fotopolimerizador de luz halógena, seguido da manipulação e da aplicação do cimento, conforme orientações do fabricante. Já a cimentação com o cimento resinoso autoadesivo RelyX U100 (3M ESPE) – Grupo 2 foi feita em dentina úmida, manipulação e aplicação do cimento de acordo com orientações do fabricante. Em ambos os grupos, o bloco de resina composta foi posicionado sobre o cimento com carga de 10 N, 30 N e 60 N pelo tempo de dois minutos e fotoativado pelo tempo de 160 segundos (3M ESPE). As amostras foram armazenadas por 24 horas em 100% de umidade a 37°C. As restaurações foram incluídas com resina acrílica autopolimerizável e submetidas a cortes seriados, obtendo-se o formato de prismas. Os espécimes (n=15 para cada carga) ficaram divididos conforme o cimento e a carga utilizados. Após, foram submetidos ao teste de resistência de união a microtração na máquina de ensaios universal EMIC DL-2000. Além disso, dois conjuntos de cada grupo foram seccionados no sentido mésio-distal, com um disco diamantado de dupla face. As superfícies foram polidas com lixas de carbeto de silício, seguido de polimento com pastas diamantadas. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em microscópio eletrônico de varredura em aumento de 1.000 a 4.000 vezes. Os resultados foram submetidos à Análise de Variância e ao teste de Tukey HSD. A carga de 30N apresentou o maior valor de resistência de união em ambos os grupos, sendo 17,27 ± 5.33 MPa no Grupo 2 (dois) e 15,33 ± 2.75 MPa no Grupo 1 (um). Já a carga de 10 N apresentou valores intermediáriários de resistência de união, sendo (9,47 ± 4.07 MPa) para o Grupo 2 (dois) e (9,36 ± 5.08) para o Grupo 1 (um). A carga de 60 N foi a que apresentou menores valores de resistência de união (9,47 ± 2.64 MPa) para o Grupo 2 (dois) e (9,36 ± 2.49) para o Grupo 1 (um). Houve diferença estatística entre a carga de 30 N do Grupo 2 (dois) e a carga de 60 N do Grupo 1 (um) e também entre a carga de 30 N do Grupo 2(dois) com a carga de 60 N do Grupo 2 (dois). O tipo de fratura foi analisado através de imagens obtidas em MEV e a falha do tipo mista foi predominante em ambos os grupos e cargas. Os resultados sugerem que diferentes cargas de cimentação podem interferir na resistência de união do cimento resinoso RelyX ARC e Rely X U100. / This study evaluated different loads during the cementation on the microtensile bond strength of conventional and self-adhesive resin cement. Fortytwo extracted caries-free molars were selected. Flat coronal dentin surfaces were exposed until the removal of enamel. The selected teeth were embedded in autopolymerized acrylic resin. Composite resin discs (Filtek Z 350 XT, 3M ESPE) were made according to the manufacturer´s instructions. Luting procedures with Rely X ARC - Group 1 (3M ESPE) were made with etched with 37% phosphoric acid gel, rinsed with water and the excess dentin moisture was removed and were applied two consecutive coats of the adhesive (Adper Single Bond 2) and light cured with halogen light (3M ESPE). Immediately the cement was manipulated according to the manufacturer’s instructions and the composite discs were placed under 10N, 30N or 60N static load for 2 minutes. Specimens were light cured for a total of 160 seconds. Luting procedures with Rely X U100 (3M ESPE) - self-adhesive resin cement - Group 2 were made with moist dentin, the cement was manipulated according to the manufacturer’s instructions, following the same protocol of the luting procedures of conventional resin cement. The bonded specimens were stored in water at 37ºC for 24 hours. The restorations were embedded in autopolymerized acrylic resin and then longitudinally sectioned in the “x” and “y” directions perpendicular to the bonded interface to produce rectangular bonded sticks. Specimens (n=15) were divided according to cement and the load. The microtensile bond strength was conducted on a mechanical testing machine EMIC DL-2000. In order to evaluate the hybrid layer, two teeth of each group were cut perpendicular to the bonding interface, exposing the middle of the teeth. The surfaces were flatted and followed by polished and a dehydration process. Specimens were sputter coated with gold and examined with a scanning electron microscope (SEM) at a x1000 to a x4000 magnification. Data were subjected to Analysis of Variance and Tukey’s test (p<0.05). The load of 30 N showed the best mean of the microtensile bond strength of the both groups (17,27 ± 5,33 MPa to group 1 and 15,33 ± 2,75 MPa to group 2). The load of 10 N of group 2 showed intermediary values (9,47 ± 4,07 MPa) followed by load of 10N (9,36 ± 5,08 MPa) and 60N of group 1 (7,84 ± 2,49 MPa). The load of 60N of group 2 resulted in the lowest values (7,34 ± 2,64 MPa). The mode of failure was determined using SEM and the mixed failure werer predominant in all groups. The results suggest that different load during the luting procedures can interfere on the bond strength of resin cements.
|
13 |
Pinos anatômicos cimentados com agentes resinosos em diferentes comprimentos radiculares: estudo da interface e da resistência de união / Anatomic Posts Luted With Resin Gents In Different Lengths Roots: Study Of Interface And Bond StrengthSouza, Niélli Caetano de January 2015 (has links)
Made available in DSpace on 2015-04-30T14:06:25Z (GMT). No. of bitstreams: 1
000467675-Texto+Completo-0.pdf: 1437644 bytes, checksum: dbcd8d581c9d8dc4da7301e5b4e3ac75 (MD5)
Previous issue date: 2015 / The objectives of the study were to evaluate the influence of the depth of cement, the cement type and mechanical cycling through the pullout bond strength of direct anatomical post in fragile bovine roots and assess the thickness of resin cements in different root thirds of direct anatomical post and fiber post in human single-rooted. Eighty bovine roots were obtained for the bond strength by pullout. The canals were endodontically treated and extended with diamond burs. The roots were divided in two groups: G1 - direct anatomical posts cemented with RelyX ARC; G2 - direct anatomical posts cemented with RelyX U200. Both groups were divided in two subgroups, each subgroup (n = 10) cemented with a depth of 5 mm or 10 mm. Half of the specimens of each depth was submitted to mechanical cycling. The specimens were submitted to pullout test in a universal testing machine. The results were analyzed by ANOVA three factors (α=0. 05). To study the thickness of the resin cement, 40 single-rooted human upper anterior teeth were obtained. The teeth were endodontically treated and weakened with drill Largo and diamond burs in a depth of 10 mm. The teeth were randomly divided in four groups (n = 10): Group 1 - fiber post + RelyX ARC; Group 2 - fiber post + RelyX U200 +; Group 3 - anatomical post + RelyX ARC; Group 4 - anatomical post + RelyX U200. The dyes 0. 1% Fluorescein and 0. 1% Rhodamine B isothiocyanate were added to adhesive system and resin cement, respectively. After cementation, the roots were sectioned in slices and observed by confocal laser scanning microscopy. Datas were analyzed by ANOVA followed by Tukey test (α=0. 05). For the pullout test, the resin cement factor (p = 0. 0001) and mechanical loading factor (p = 0. 0001) were significant. The bond strength of RelyX U200 (6. 47 MPa) was statistically superior to RelyX ARC (5. 51 MPa). The depth of cementation factor was not significant (p=0. 328). However, the interaction between depth and mechanical cycling was significant (p=0. 0001). For a depth of 5 mm of cementation, the average bond strength of samples without mechanical cycling (6. 98 MPa) was statistically higher to samples with mechanical cycling (4. 78 MPa). For the depth of cementation of 10 mm, there was no statistical difference between the samples with and without mechanical cycling. For analysis of the resin cement thickness, post, cement and root thirds influenced the thickness of the resin cement (p <0. 001). The thickness of resin cement was significantly lower in anatomical post groups than in fiber post groups, except in the apical third of the canal. There was no significant statistical difference between the cements for the direct anatomical post; for the fiber posts, only the cervical third showed a statistically significant difference between the cements. It was concluded that the direct anatomical posts cemented in the 10 mm depth obtained the best results with RelyX U200, regardless of mechanical cycling. In addition, in weakened roots, the preparation of direct anatomical post allows the better adaptation of post to the channel walls, favoring the formation of a thin and uniform cement film. / Os objetivos do estudo foram avaliar a influência da profundidade de cimentação, do cimento resinoso e da ciclagem mecânica na resistência à tração por pull out de pinos anatômicos diretos em raízes bovinas fragilizadas, assim como avaliar a espessura de cimentos resinosos nos terços radiculares de pinos anatômicos diretos e pinos de fibra de vidro em raízes unirradiculares humanas. Para o ensaio de pull out, 80 remanescentes radiculares bovinos foram tratados endodonticamente e alargados com pontas diamantadas, sendo divididos em dois grupos: G1 - pinos anatômicos diretos cimentados com RelyX ARC; G2 - pinos anatômicos diretos cimentados com RelyX U200. Ambos os grupos foram divididos em dois subgrupos, sendo cada subgrupo (n=10) cimentado com profundidade de 5 mm e 10 mm. Metade dos corpos de prova de cada profundidade recebeu ciclagem mecânica. Os corpos de prova foram submetidos ao ensaio de pull out em máquina de ensaio universal. Os resultados foram analisados pela ANOVA de três fatores (α=0,05). Para o estudo da espessura do cimento resinoso, 40 raízes unirradiculares humanas da região ântero-superior foram tratadas endodonticamente e fragilizadas com broca Largo e pontas diamantadas na profundidade de 10 mm. Os dentes foram divididos aleatoriamente em quatro grupos (n=10): Grupo 1 - pino de fibra de vidro + RelyX ARC; Grupo 2 - pino de fibra de vidro + RelyX U200; Grupo 3 - pino anatômico + RelyX ARC; Grupo 4 - pino anatômico + RelyX U200. Os corantes Fluorosceína 0,1% e Isotiocianato de Rodamina B 0,1% foram adicionados ao sistema adesivo e ao cimento resinoso, respectivamente. Após cimentação, as raízes foram seccionadas em fatias e observadas em microscopia confocal de varredura à laser. Os dados foram analisados pela ANOVA, seguido do teste Tukey (α=0,05). Para o ensaio de pull out, os fatores cimento resinoso (p=0,0001) e ciclagem mecânica (p=0,0001) foram significativos. A resistência de união do RelyX U200 (6,47 MPa) foi estatisticamente superior ao RelyX ARC (5,51 MPa). O fator profundidade de cimentação não foi significativo (p=0,328). No entanto, a interação entre ciclagem mecânica e profundidade foi significativa (p=0,0001). Para a profundidade de 5 mm, a média de resistência de união sem ciclagem mecânica (6,98 MPa) foi estatisticamente superior a com ciclagem mecânica (4,78 MPa). Para a profundidade de 10 mm, não houve diferença estatística entre as amostras sem e com ciclagem mecânica. Para a análise da espessura de cimento resinoso, o pino, o cimento e os terços radiculares influenciaram na espessura do cimento (p<0,001). A espessura de cimento foi significativamente menor nos pinos anatômicos do que nos pinos de fibra de vidro, exceto no terço apical do canal. Não houve diferença estatística significativa entre os cimentos para pinos anatômicos; para os grupos com pinos de fibra de vidro, apenas o terço cervical apresentou diferença estatística significativa entre os cimentos. Concluiu-se que os pinos anatômicos diretos cimentados em profundidade de 10 mm obtiveram os melhores resultados quando utilizado o RelyX U200, independente da ciclagem mecânica, e que, em raízes fragilizadas, a confecção de pinos anatômicos diretos permite uma melhor adaptação dos pinos às paredes do canal, favorecendo a formação de uma película de cimento fina e uniforme.
|
14 |
Influência dos cimentos resinosos na deflexão de cúspides e na carga de fratura de pré-molares tratados endodonticamenteDall Agnol, Rhuy Jacob Cezarotto January 2008 (has links)
Made available in DSpace on 2011-12-27T14:14:19Z (GMT). No. of bitstreams: 2
000415566-0.pdf: 1518608 bytes, checksum: bd39955631082d183040d1bec6aef520 (MD5)
license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this split mouth randomized clinical trial was to evaluate and compare the space closure during the retraction of upper permanent canine with self-ligating"SmartClip" and conventional"Gemini" brackets. Sample complied 13 patients with Class I biprotrusion or Class II 1st division malocclusion, with an average age of 18 years and 4 months, 3 male and 10 female. All were submitted to the therapeutic extraction of two first premolars. The retraction of the upper canines was performed with elastomeric chain with 150g of force. The evaluations were performed at four times (T1 – initial, T2 – 4 weeks, T3 – 8 weeks, T4 – 12 weeks) in stone model casts. The amount of movement and the rotation of the canines as well anchorage loss of upper first molars were evaluated. The space closure measurement was made between canine and second premolar and rotation was assessed by an angle formed by the intersection of the line drawn through the canine’s contact points and the line of the palatal suture. The anchorage loss was measured by a guide adapted at the palatal rugae in stone casts at initial and end. The data obtained were subjected to Student t test considering level of significance of 5%.The results shown that selfligating bracket had an average of 0. 92 mm (+/- 0. 29) of rate movement and 8. 46o (+/- 4. 68) of the rotation of the upper canines and 0. 65 mm (+/- 0. 24) of anchorage loss; the conventional bracket had an average of 0. 84 mm (+/- 0. 22) of rate movement and 11. 77o (+/- 3. 26) of the rotation of and the upper canines and 0. 57 mm (+/- 0. 24) of anchorage loss. There was no difference (p=0. 250) in the rate of movement of the canines between the two types de brackets. The rotational control of the canines was better promoted by self-ligating bracket (p=0. 005). There was anchorage loss for both groups, with no statistical difference between them (p=0. 157). / O objetivo desse trabalho foi avaliar a influência de diferentes cimentos resinosos na deflexão de cúspides e na carga de fratura de dentes com tratamento endodôntico. Quarenta pré-molares superiores foram divididos aleatoriamente em quatro grupos: 1 – hígidos; 2 - RelyX ARC; 3 - RelyX U100; 4 - Maxcem. Os dentes dos grupos 2, 3 e 4 receberam preparos MOD, seguido de moldagem com silicone por adição e vazamento de gesso tipo IV. Sobre cada modelo foi confeccionada uma restauração inlay em resina composta Z250. As restaurações foram cimentadas com os cimentos resinosos, de acordo com cada grupo experimental, seguindo as instruções dos fabricantes. Os corpos-de-prova foram armazenados em água destilada a 37º C por 24 horas. Em máquina de ensaio universal, uma carga de 200 N foi aplicada na região oclusal com esfera de aço de 8 mm de diâmetro e, com o auxílio de um micrômetro posicionado nas faces vestibular e palatina, a deflexão das cúspides foi medida antes e após a carga. Em seguida, os corpos-de-prova foram submetidos à compressão axial com a esfera de aço até ocorrer a fratura. De acordo com ANOVA e teste de Tukey (a = 0,05), o grupo 1 apresentou a menor média de deflexão de cúspide (4μm), não diferindo estatisticamente do grupo 2 (12μm) (p>0,05). O grupo 3 (39μm) e 4 (56μm) apresentaram as maiores médias, diferindo estatisticamente dos grupos 1 e 2 (p<0,05). O grupo 1 teve a maior média de carga de fratura (1982 N), diferindo estatisticamente dos grupos 2 (690 N), 3 (465 N) e 4 (679 N), os quais não diferiram entre si. As inlays fixadas com os cimentos resinosos auto-adesivos RelyX U100 e Maxcem proporcionaram maior deflexão de cúspides. Os valores de carga de fratura para as inlays fixadas com os cimentos resinosos foram semelhantes entre si e não reproduziram a carga de fratura dos dentes hígidos.Houve predominância de falhas consideradas recuperáveis, independente do cimento resinoso empregado.
|
15 |
Avaliação histológica do cimento de fosfato de cálcio (CFC) reforçado por fibras implantado supra-corticalmente em fêmur de ratosOliveira, Taiane Coutinho de January 2009 (has links)
Made available in DSpace on 2011-12-27T14:14:22Z (GMT). No. of bitstreams: 2
000422268-0.pdf: 14833302 bytes, checksum: 1b71642b280aa5b7984729b688fbd92e (MD5)
license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study examines histologically the effect of cement Calcium Phosphate (CFC) reinforced with nylon fibers, polypropylene and carbon used as implant supra-cortical femur of rats. We used 20 male Wistar rats, approximately 300g each. Being prepared plates CFC with fibers, on the size of 2mm thick and 6 mm in diameter, which were tightened in the femur of animals. These were euthanized at 30, 60, 90 and 120 days after the implant. These pieces were removed and subjected to a routine process for preparing slides slides, stained with Hematoxilyn and Eosin. The biocompatibility, the degree material’s resorption anda its ability to osteoconduction were evaluated at the different times. At all diferents times studied, the histological sections showed formation of dense tissue, few cellularized, showing slightly vascularized and discrete mononuclear infiltration. In the area around the implant, there are discrete reabsorption areas, and hyalinization induction of collagen fibers peripheral. The tissue includes the material of the implant. After 120 days, may be observed a formation of osteoid material. The degree of bone reabsorption in the periphery of the implant was less, and without statistical significance. Can be concluded that: The CFC with fiber is biocompatible promotes bone conduction and bone neoformation rounding the cement. CFC with fibers in the form of prefabricated plates is suitable for use as implants and bone substitute, within the parameters of this experiment. / Este estudo analisa histologicamente o efeito do Cimento de Fosfato de Cálcio (CFC) reforçado com fibras de náilon, carbono e polipropileno utilizado como implante supra-cortical em fêmur de ratos. Foram utilizados 20 ratos Wistar, machos, com cerca de 300g cada. Sendo confeccionadas placas de CFC com fibras, no tamanho de 2 mm de espessura por 6 mm de diâmetro, os quais foram aparafusados no fêmur dos animais. E estes foram eutanasiados em 30, 60, 90 e 120 dias após o implante sendo as peças removidas e submetidas ao processo de rotina para confecção de lâminas, coradas com Hematoxilina e Eosina. Foram avaliados nos diferentes tempos a biocompatibilidade, o grau de reabsorção do material e a sua capacidade de osteocondução. Em todos os tempos estudados os cortes histológicos revelam formação de tecido conjuntivo denso, pouco celularizado, apresentando discretamente vascularizado e discreto infiltrado inflamatório mononuclear. No entorno do implante, observam-se discretas áreas de reabsorção, e indução de hialinização das fibras colágenas periféricas. O tecido apresenta inclusão do material do implante. Aos 120 dias chama a atenção a formação de material osteóide, O grau de reabsorção óssea na periferia do implante foi menor não apresentando significância estatística. Podendo-se concluir que: O CFC com fibras é biocompatível, promove a osteocondução e neoformação óssea contornando o cimento. O CFC com fibras, na forma de placas pré-fabricadas é adequado para ser utilizado como implante e substituto ósseo, dentro dos parâmetros deste experimento.
|