Made available in DSpace on 2017-07-24T19:22:28Z (GMT). No. of bitstreams: 1 Vania Aparecida Oliveira Queiroz.pdf: 2334313 bytes, checksum: edfd28d0622cb45ff6c0fde23b982588 (MD5) Previous issue date: 2012-12-06 / Evaluate an alternative sequence for the sandwich technique using the microtensile bond strength testing on glass-ionomer cement (GIC)-dentin and GICcomposite resin (CR) interfaces (in 7 days), and to analyze the mechanical properties (hardness and modulus of elasticity) of GIC-RC interface (in 7 days and 24 months), by the use of nano-indentation. Methods: For that, class I cavities were cut into 60 extracted human molars. The cavities were filled using two diferent sequences of closed sandwich technique with conventional glass-ionomer cement (CGIC) (KetacTM Fil Plus/3M), and resin-modified glass-ionomer cement (RMGIC) (VitrebondTM/3M).The sequences were called, convencional sequence (CS) (etching GICs surface) and alternative sequence (AS) (without etching GICs surface), and they were used in all groups RMGIC-CR, RMGIC-dentin, CGIC-CR, and CGIC-dentin. After storage period, the teeth were horizontally sectioned, along vestibular wall of the class I cavities, for the bond strength of GICs-dentin tests. For analysis of the mechanical properties and bond strength of GICs-CR, the teeth were longitudinally sectioned.The specimens intended for mechanical properties testing have been removed from the sandwich restorations center areas. For the adhesion tests, the beams were aligned, and attached to a jig employing the active gripping method and stressed in tension (MPa). For the mechanical test, the specimens were embedded, and polished, and submitted to nano-indentation (GPa). The data were analyzed by Kruskal-Wallis, Dunn, and Chi-square tests (p<0.05). Results: The GICRM presented better adhesion to dentin and CR, and the CGIC presented better mechanical properties. When was used the RMGIC, both sequences did not present differences in adhesion (dentin and CR), and in mechanical properties (RMGIC,interface, and CR) in 7 days and 24 months. Concerning CGIC-dentin and CGIC-CR,also did not find a significant difference between both sequences, despite the adhesion means difference CGIC-CR between the CS (0.96 MPa) and AS (5.78 MPa). The CS presented a significant number of spontaneously debonded beams at interface with the CR before testing (77.33%) than AS (16%). The mechanical properties analysis of CGIC-interface-CR, in 7 days and 24 months, showed significant differences between techniques. At seven days, no GICC-RC interface data was obtained due to deteriorating condition, while AS showed 0.42 GPa (hardness) and 7.50 GPa (modulus of elasticity) values. After 24 months, AS showed hardness and modulus of elasticity, respectively, 1.24 e 20.96 GPa (CGIC), and 0.40 e 7.05 GPa (interface), while CS showed 0.51 e 8.14 GPa (CGIC) without any interface value. Conclusion: The AS has performed a good option for laminate or sandwich technique when RMGIC was used, and it was the best option when a CGIC was used. / Avaliar uma sequência alternativa para a técnica do sanduíche pela análise da resistência adesiva por microtração nas interfaces cimento de ionômero de vidro (CIV)-dentina e CIV-resina composta (RC) (aos 7 dias) e pela análise das propriedades mecânicas (dureza e módulo de elasticidade) por nanoendentação na interface CIV-RC (aos 7 dias e 24 meses). Material e métodos: Para isto, foram preparadas cavidades de classe I em 60 molares humanos extraídos. As cavidades foram restauradas utilizando duas sequências técnicas diferentes para o sanduíche fechado: com cimento de ionômero de vidro convencional (CIVC) (KetacTM Fil Plus/3M) e com cimento de ionômero de vidro modificado por resina (CIVMR) (VitrebondTM/3M). As técnicas foram denominadas, sequência convencional (SC) (com condicionamento superficial do CIV) e sequência alternativa (SA) (sem condicionamento superficial do CIV), e empregadas em todos os grupos de CIVMRRC, CIVMR-dentina, CIVC-RC e CIVC-dentina. Após períodos de armazenamento, os dentes foram seccionados horizontalmente, ao longo da parede vestibular do preparo de classe I, para o teste de resistência adesiva CIV-dentina. Para análise das propriedades mecânicas e para o teste de resistência adesiva CIV-RC, os dentes foram seccionados longitudinalmente. Os espécimes destinados às análises das propriedades mecânicas foram retirados do centro das restaurações de sanduíche. Para o teste de resistência adesiva, os palitos foram alinhados e colados ao dispositivo da máquina de tração pelo método de fixação ativo e estressados em tensão (MPa). Para análise das propriedades mecânicas, os espécimes foram fixados com parafina no suporte de teste, polidos e submetidos a nanoendentação (GPa). Os testes Kruskal-Wallis, Dunn e Qui-Quadrado foram utilizados para análise dos dados (p<0,05). Resultados: O CIVMR demonstrou maior adesão, à dentina e à RC, e o CIVC demonstrou melhores propriedades mecânicas. Quando foi utilizado o CIVMR, as duas sequências técnicas estudadas não apresentaram diferenças na resistência adesiva (à dentina e à RC) e nas propriedades mecânicas, aos 7 dias e 24 meses. Quanto à resistência adesiva CIVC-dentina e CIVC-RC, também não houve diferenças significantes entre as sequências estudadas, apesar da diferença de médias de adesão CIVC-RC entre a SC (0,96 MPa) e SA (5,78 MPa). A SC também apresentou significante maior número de palitos deslocados espontaneamente na interface com a RC antes do teste (77,33%) que a SA (16%). A análise das propriedades mecânicas, aos 7 dias e 24 meses, demonstrou diferenças significantes entre as técnicas. Aos 7 dias, não foi possível obter valores na interface CIVC-RC na SC devido ao grau de deterioração existente enquanto a SA apresentou valores 0,42 GPa (dureza) e 7,50 GPa (módulo de elasticidade). Após 24 meses, a SA apresentou valores de dureza e módulo de elasticidade, respectivamente, 1,24 e 20,96 GPa (CIVC), e 0,40 e 7,05 GPa (interface), enquanto a SC apresentou 0,51 e 8,14 GPa (CIVC) e nenhum valor para interface.Conclusão: A SA apresentou-se como boa opção para a técnica laminada ou do sanduíche quando foi utilizado o CIVMR, e como a melhor opção quando foi utilizado o CIVC.

Orientador: André Luiz Fraga Briso / Coorientador: Paulo Henrique dos Santos / Banca: Ticiane Cestari Fagundes Tozzi / Banca: Anderson Catelan / Resumo: O objetivo neste estudo foi avaliar o efeito da contaminação do tecido dentinário e dos métodos normalmente empregados na limpeza do substrato sobre a resistência de união obtida na interface cimento de ionômero de vidro modificado por resina (CIVMR)/dentina. Para tanto, os 168 dentes bovinos foram desgastados até o tecido dentinário divididos em doze grupos (n=14), de acordo com o agente contaminante e a técnica de limpeza, sendo: NN - sem contaminação (N) e sem limpeza do substrato (N); NA - sem contaminação (N) e limpeza com spray ar/água (A); NP - sem contaminação (N) e limpeza com ácido poliacrílico 26% (P); SaN - contaminação por saliva (Sa) e sem limpeza do substrato (N); SaA - contaminação por saliva (Sa) e limpeza do substrato com spray ar/água (A); SaP - contaminação por saliva (Sa) e limpeza do substrato com ácido poliacrílico 26% (P); SgN - contaminação por sangue (Sg) e sem limpeza do substrato (N); SgA - contaminação por sangue (Sg) e limpeza do substrato com spray ar/água (A); SgP - contaminação por sangue (Sg) e limpeza do substrato com ácido poliacrílico 26% (P); HN - contaminação por agente hemostático (H) e sem limpeza do substrato (N); HA - contaminação por agente hemostático (H) e limpeza do substrato com spray ar/água (A); HP - contaminação por agente hemostático (H) e limpeza do substrato com ácido poliacrílico 26% (P). Todos os espécimes foram restaurados com o material ionomérico encapsulado Riva Light Cure (SDI) e, posteriormente foram obtidos palito... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate the effect of the contamination of the dentin tissue and the methods normally employed in the cleaning of the substrate on the bond strength obtained at the resin modified glass ionomer cement (RMGIC) / dentin interface. For this purpose, 168 bovine teeth were selected, which were worn to dentin tissue, and were then divided into twelve groups (n = 14), according to the contaminating agent and the cleaning technique: NN - without contamination (N) and without substrate cleaning (N); NW - no contamination (N) and spray / water cleaning (W); NP - without contamination (N) and cleaning with 26% polyacrylic acid (P); SaN - contamination by saliva (Sa) and without substrate cleaning (N); SaW - saliva contamination (Sa) and spray / water substrate cleaning (W); SaP - saliva contamination (Sa) and substrate cleaning with 26% polyacrylic acid (P); BN - blood contamination (B) and no substrate cleaning (N); BW - blood contamination (B) and cleaning the substrate with spray / water (W); BP - blood contamination (B) and substrate cleaning with 26% polyacrylic acid (P); HN - contamination by hemostatic agent (H) and without cleaning of the substrate (N); HW - hemostatic agent contamination (H) and spray / water substrate cleaning (W); HP - hemostatic agent contamination (H) and substrate cleaning with 26% polyacrylic acid (P). All specimens were restored with the Riva Light Cure (SDI) encapsulated ionomeric material and, afterwards, sticks of a... (Complete abstract click electronic access below) / Mestre

Orientador: André Luiz Fraga Briso / Banca: Robson Frederico Cunha / Banca: Mônica Campos Serra / Resumo: O presente trabalho avaliou clinicamente a performance de restaurações Classe I realizadas em molares decíduos pelas técnicas restauradoras atraumáticas convencional (TRA) e modificada (TRA Mod). Foram realizadas 46 restaurações pela técnica do TRA, empregando-se como material restaurador o cimento de ionômero de vidro Ketac Molar Easy Mix (3M, ESPE, Seefelf, Germany) e 57 restaurações pela técnica do TRA Modificado, utilizando-se o ionômero de vidro modificado por resina Fuji II LC (GC Corporation, Tokyo, Japan). As restaurações foram avaliadas após 24 horas, 3, 6 e 12 meses de acordo com a ocorrência de sensibilidade pós-operatória, desempenho clínico e ocorrência de lesões cariosas. Os dados foram analisados transversal e longitudinalmente com a aplicação dos testes de Mann-Whitney e Friedman, respectivamente. A análise transversal mostrou não haver diferença estatisticamente significante entre as técnicas restauradoras em todos os itens avaliados. Da mesma forma, a análise longitudinal revelou semelhança entre os períodos de avaliação para a sensibilidade pós-operatória e ocorrência de lesões cariosas em ambas as técnicas. Todavia, observou-se diferença estatisticamente significante no desempenho clínico das restaurações nos períodos de 3 e 12 meses, assim como aos 6 e 12 meses para técnica do TRA. Nas restaurações realizadas pela técnica do TRA Mod, observou-se diferença entre os períodos de 3 e 12 meses. Concluiu-se que a sensibilidade pós-operatória foi pouco freqüente e semelhante para ambas as técnicas restauradoras e tende a ocorrer nos períodos iniciais pósrestauração. As técnicas restauradoras apresentaram desempenho clínico semelhante em todos os períodos avaliados, destacando-se que as restaurações realizadas pela técnica do TRA mostraram queda em seu desempenho clínico após 6 meses de acompanhamento e para a técnica do TRA Mod aos 12 meses. / Abstract: This study has evaluated clinically the performance of Class I restorations in primary molars by the atraumatic restorative treatment conventional techniques and modified. Forty-six restorations have been done by the ART technique, using as restorative material the GIC Ketac Molar Easy Mix (3M, ESPE, Seefelf, Germany) and 57 restorations by the ART modified technique, using resin-modified glass ionomer (RMGI) Fuji II LC (GC Corporation, Tokyo, Japan.) The restorations have been evaluated after 24 hours, 3, 6 and 12 months according to the post-surgery sensibility occurrence, clinical performance and carious lesions occurrence. Data have been analyzed transversal and longitudinal with Mann-Whitney and Friedman, respectively. The transversal analysis showed no significant difference among the restorative techniques and all other evaluated items. Furthermore, longitudinal analysis showed some similarities between the evaluation periods for post-surgery sensibility and carious lesions occurrences in both techniques. Nevertheless, a significant difference in the clinical performance of restorations in the periods of 3 and 12 months has been noticed, just like 6 and 12 months period for the ART Modified technique, a difference in the period of 3 and 12 months has been noticed. To come to a conclusion the post-surgery sensibility was little frequent and similar for both restorative techniques and that occurs in the first post-surgery periods. Restorative techniques present similar performance in all evaluation periods, highlighting that restorations performed by the ART technique declines after 6 months and for the ART modified in the 12 months. The occurrence of decay lesions on restored teeth was little frenquent and similar for both restoration techniques. / Mestre

O presente estudo in vitro teve o objetivo de avaliar a microdureza e a rugosidade superficial dos materiais restauradores: Resina Composta nanoparticulada (Filtek Z350 XT®), Resina Composta Bulk Fill (Filtek Bulk Fill®) e dois cimentos de ionômero de vidro resino modificados (Vitremer® e Riva®) sob a influência de três bebidas ácidas: Coca Cola®, Suco de laranja natural e Iogurte de morango, controlados por um grupo de saliva artificial. Foi confeccionado um total de 256 corpos de prova, sendo 64 corpos para cada material a ser testado. Estes foram ainda subdivididos nos grupos das bebidas ácidas e da saliva artificial (grupo controle) ficando 16 corpos de cada material imerso nas bebidas durante 1, 24, 72 e 168 horas. Em cada um desses tempos foram realizados os testes de microdureza e rugosidade. Os resultados obtidos foram submetidos a ANOVA com medidas repetidas com 16 repetições. Foram realizadas 1024 parcelas a 5%de significância. Para a análise post hoc foi utilizado o Teste de Tukey. Todos os testes foram realizados utilizando 5% de significância. Os resultados variaram conforme os produtos utilizados, modificadores e tempo. / The objective of this study was to evaluate the microhardness and surface roughness of restorative materials: Filtek Z350 XT® composite resin, Bulk Fill Composite Resin and two modified resin resin ionomer cements Vitremer ® and Riva ®) under the influence of three beverages including: Coca Cola ®, natural orange juice and natural yogurt, controlled by a group of artificial saliva. A total of 256 specimens were prepared, 64 bodies for each material to be tested. These were further subdivided into the artificial acid and saliva beverage groups (control group), leaving 16 bodies of each material immersed in the beverages for 1; 24; 72 and 168 hours. In each case, microhardness and roughness tests were performed. The results were submitted to ANOVA with repeated measurements with 16 replicates. There were 512 plots. For a post hoc examination and the Tukey Test was used. All tests were performed, use 5% significance. The results varied according to the products used, modifiers and time.

O objetivo deste estudo foi avaliar durante 2 anos a efetividade do cimento de ionômero de vidro modificado por resina (Vitremer - 3M) e da resina composta “condensável" (Solitaire - Kulzer) em classe II de molares decíduos. Realizou-se a análise clínica qualitativa, radiográfica, avaliação direta nos molares decíduos esfoliados e microinfiltração marginal da restauração nos mesmos. Este estudo foi composto de 64 restaurações classe II de cimento de ionômero de vidro modificado por resina (Vitremer) e 59 de resina composta “condensável" (Solitaire). O preparo cavitário de classe II foi realizado de acordo com a extensão do processo de cárie, limitando-se apenas ao corte de entrada para o acesso à lesão e a remoção de todo tecido cariado, observando-se os princípios da dentística operatória moderna, sem extensão preventiva, conservando-se a maior quantidade de estrutura dentária sadia possível. Os materiais restauradores foram manipulados e inseridos de acordo com as instruções do fabricante, sendo que o Vitremer foi inserido com seringa Centrix (DFL) e a Solitaire com espátula antiaderente em incrementos. As restaurações foram avaliadas clinicamente no início, aos 6, 12, 18 e 24 meses pelo critério United States Public Health Service modificado RYGE e CVAR. A tomada radiográfica interproximal padronizada foi realizada no início e aos 24 meses. Após a esfoliação os trinta e seis dentes foram armazenados em água destilada com timol a 1% com finalidade de inibir o crescimento bacteriano. Estes foram analisados diretamente para avaliar a presença de cárie recorrente nas restaurações e a microinfiltração marginal. Posteriormente, as raízes foram seladas com resina composta Z 100 (3M) e aplicadas 2 camadas de esmalte de unha a 1mm das margens da restauração, sendo os espécimes imersos em solução de fucsina básica a 0.5%, à temperatura de 37o C por 24 horas. Após esse período, os mesmos sofreram lavagem em água corrente por 24 horas. Para o seccionamento, os espécimes foram incluídos em resina acrílica autopolimerizável para serem levados à máquina de corte. Cada dente sofreu 3 cortes com um disco diamantado, no sentido mésio-distal. O tamanho da recidiva de cárie, a análise indireta do tamanho das restaurações e a microinfiltração marginal na parede cervical de cada restauração dos dentes esfoliados foram avaliadas através de medidas lineares em um programa de computador (Sigma Scan). Utilizou-se o teste de Mann-Whitney para a análise entre materiais, e para a análise no mesmo material restaurador, porém em períodos diferentes de observação, utilizou-se o teste pareado de Wilcoxon. Já para a análise de medidas realizadas nas recidivas de cárie dos dentes esfoliados e da microinfiltração marginal utilizou-se o teste “t". O nível de significância de 5% foi adotado em todos os testes. Os resultados clínicos demonstraram após os 24 meses de avaliação que o Vitremer apresentou melhores resultados quando comparado a Solitaire. Os dados foram, respectivamente, na descoloração marginal de 89.00% e 33.89%; na forma anatômica de 56.25% e 11.86%; na integridade marginal de 46.87% e 15.25% e, na manutenção do contato proximal de 92.18% e 69.49%. Com relação à estabilidade de cor os dados foram de 79.68% e 80.35%, e quanto à textura da superfície foram de 37.50% e 81.35%, sendo que a Solitaire apresentou melhores resultados. Estas porcentagens são relativas ao escore Alpha na avaliação de 24 meses. Verificou-se que não houve influência geral direta, da remoção do teto da câmara pulpar para a terapia pulpar, no comportamento clínico dos materiais restauradores, somente em alguns quesitos de avaliação como descoloração marginal, textura da superfície e contato proximal é que os dentes que sofreram terapia pulpar apresentaram um desempenho um pouco inferior, sendo na maioria praticamente igual, ou até superior como no caso da estabilidade de cor com relação ao Vitremer. Quanto ao desempenho clínico avaliado através de radiografias, verificou-se, com relação à conformidade da restauração com o dente em relação ao contorno proximal, uma semelhança entre os grupos, não apresentando diferenças estatísticas, pois o Vitremer apresentou escore médio aos 24 meses de 1.08 e a Solitaire de 1.29. Já com relação à presença de radiolucidez na parede gengival, os resultados foram estatisticamente significantes, sendo que a resina composta apresentou um número maior de dentes com área radiolúcida em esmalte e dentina em relação ao Vitremer, na avaliação de 24 meses, com média de 0.17 e 1.23, respectivamente. Ao analisar o desempenho clínico com relação ao tamanho da restauração e o dente em que esta se encontra, verifica-se uma conformidade nos resultados, onde o tamanho da restauração tende a não influenciar no resultado do material. A presença de cárie recorrente, qualitativa e quantitativa, avaliada nos dentes esfoliados, foi marcante na face proximal sendo que a resina composta empregada apresentou um número maior de lesões cavitadas, sendo este número estatisticamente significante, pois a média da Solitarie foi de 3.82mm2 e do Vitremer 0.11mm2 de recidiva cavitada. Na face oclusal houve uma diferença estatisticamente significante entre os materiais testados, sendo a média da Solitaire de 1.25mm2 de recidiva e o Vitremer não apresentou recidiva cavitada na oclusal. Ao analisar a microinfiltração marginal nos dentes esfoliados através do uso de corante, verificou-se uma maior penetração do corante na parede gengival nos dentes restaurados com resina composta, apresentando 1.73mm de média na penetração do corante e 0.35mm de média para o Vitremer, sendo a diferença estatisticamente significante. Nas avaliações realizadas neste estudo, verificou-se que o cimento de ionômero de vidro modificado por resina (Vitremer) apresenta condições favoráveis de desempenho clínico, radiográfico e menor microinfiltração marginal em restaurações classe II de molares decíduos, no período avaliado, superando o desempenho da resina composta “condensável" (Solitaire). / The purpose of this study was to evaluate for two years the clinical performance of a resin-modified glass ionomer cement (Vitremer - 3M) and the “condensable" composite resin (Solitaire - Kulzer) in the restoration of class II cavities in primary teeth. Clinical, radiographic, direct following exfoliation in the primary molars and marginal microleakage evaluations were performed. A total of 64 class II cavities in the primary molar was restored with resin modified glass ionomer cement (Vitremer - 3M) and 59 class II cavities in the primary molars with “condensable" composite resin (Solitaire - Kulzer). The preparation was accomplished according to the extension of the decay process. The dentist placed resinmodified glass ionomer cement according to the manufacturer’s recommendations. First, he placed a dentin primer and light-polymerized it. Then, he hand-mixed the fluoroaluminosilicate glass powder base with the poliacrilic acid, placed it in the cavity preparation (Centrix) and then exposed it to visible light for initial polymerization. The composite resin Solitaire was placed in the cavity preparation in increments. Each restoration was directly and clinically evaluated at baseline and at 6, 12, 18, 24 months, based on the modified United Stated Public Health Service methodological technique for evaluations. Standardized bitewing radiograph were accomplished in the baseline and at 24 months. After exfoliation, the teeth were stored in distilled water with timol 1% with purpose of inhibiting the bacterial growth. Visual inspection was carried out in the thirty-six restorations collected after exfoliation, to evaluated recurrent decay and marginal microleakage. The roots were sealed with composite resin Z 100 (3M) and applied two layers of fingernail enamel at 1mm of the margins of the restorations, being the specimens immersed in basic fucsin solution, at 0,5%, at a temperature of 37oC, for 24 hours, and rinsed in running average water for 24 hours, sectioned and evaluated. Each sample was included in auto-cured resin and mesiodistal planes, with a diamond disk had three cuts. Decay size, the indirect analysis of the size restorations and the marginal microleakage in the cervical wall, were measured in a computer program (Sigma Scan). Mann-Whitney’s test was used for the analysis among the materials, and for the analysis in the same restorative material, although in different observation periods; of Wilcoxon paired test used. As to the analysis of measures accomplished in the decay of the teeth after exfoliation and marginal microleakage, the “t" test was used. The significance level of 5% was used in all tests. The clinical results demonstrated, after 24 months of evaluation, that Vitremer presented better results when compared with Solitaire, begin: the marginal discoloration, 89,00% and 33,89%; anatomic form, 56,25% and 11,86%; marginal integrity, 46,87% and 15,25%; maintenance of interproximal contact, 92,18% and 69,49%; except for color stability, 79,68% and 80,35%; and surface texture, 37,50% and 81,35% Solitaire presented better results, being these resulted related to percentages of the score Alpha, in the evaluation of 24 months. This study verified that there is not a direct, general influence when removing the pulpal roof chamber for the pulpal therapy, on the clinical behavior of, restoring materials. Only in some evaluation requirements, as marginal discoloration, surface texture and maintenance of interproximal contact is that the teeth that suffered pulpal therapy presented a little inferior performance, being practically equal in most instances, or even superior, in the case of color stability, in relation to Vitremer. The clinical performance was evaluated through bitewing radiographs, regarding the conformity of the restoration with the tooth in relation to the proximal contour, a similarity among groups, not presenting statistical differences, because Vitremer showed medium score at 24 months of 1,08 and Solitaire 1,29. As to the presence of a radio-lucid area in the gingival wall, the results were statistically significant and Solitaire presented a larger number of teeth with radio-lucid areas in the enamel and dentin, in relation to Vitremer, in the evaluation of 24 months, with an average score of 0,17 and 1,23, respectively. When analyzing the clinical performance in relation to the size of the restoration and the tooth in which localized, a conformity is verified in the results, where the size of the restoration tends to not influence the result of the material. The quantitative and qualitative caries recurrence evaluation in the teeth, after exfoliation, was greater the proximal surface of the composite resin, presenting a larger number of carious lesions, being this number statistically significant, since the average of Solitarie was 3,82mm2 and that of Vitremer 0,11mm2 of recurrent caries. In the oclusal surface, there was a significant statistically difference among the tested materials, being the average of Solitaire 1,25 mm2 of recurrent caries and Vitremer did not present recurrent caries in the oclusal surface. When analyzing the marginal microleakage in the teeth, after exfoliation through the use of dye, a larger penetration of the it was verified in the gingival wall in the teeth restored with composite resin, presenting 1,73 mm in average in the penetration of the dye and 0,35mm in average, for Vitremer, being the differences statistically significant. In the evaluations accomplished in this study, it was verified that the resin-modified glass ionomer cement (Vitremer) presented a favorable clinical and radiographic performance, and smaller marginal microleakage in class II restorations in primary molars, in the assessed period, surpassing the performance of the "condensable" composite resin (Solitaire).

O objetivo deste estudo foi avaliar a rugosidade superficial (&micro;m) e microdureza Vickers (VH) de materiais restauradores temporários: cimento Biodentine&trade; (M1) e o cimento de ionômero de vidro - Fuji IX (M2) submetidos a diferentes enxaguatórios bucais. Foram confeccionados 54 corpos de prova (cps) por meio de uma matriz de teflon (6mm x 2mm), distribuídos aleatoriamente em 6 grupos de acordo com a solução utilizada: água destilada (S1), enxaguatório com álcool - Listerine Cool Mint (S2) e enxaguatório sem álcool - Colgate Plax (S3). Todos os cps foram mantidos em umidade relativa de 100%, em estufa 37±1°C durante todo o experimento, exceto nos períodos de imersão nos enxaguatórios estabelecidos. Os cps foram colocados individualmente em um frasco contendo 8mL do enxaguatório específico para cada grupo, durante 2 minutos, sob vibração, duas vezes ao dia, por um período de 21 dias. As leituras foram realizdas por meio do microdurômetro e rugosímetro nos tempos de 48 horas (T0), 7 dias (T1), 14 dias (T2) e 21 dias (T3). Os dados obtidos foram agrupados em tabelas e submetidos aos testes estatísticos de normalidade, Kolmogorov-Smirnov, Shapiro-Wilk, Anova e Teste de Tukey por meio do Programa Estatístico Assistat Versão 7.7 beta (2016). Resultados: Verificou-se que os fatores Tempo (T), Solução (S) e Material (M) isoladamente e a interação TxM e SxM tiveram efeito estatisticamente significante na rugosidade superficial. Isoladamente, T3 (0,92±0,02) e M1 (0,87±0,01) apresentaram maior média de rugosidade e S3 (0,72±0,02) a menor média de rugosidade. Nas interações MxT e SXM, respectivamente o M1T3 (1,10±0,03) e M1S1 (1,03±0,03) apresentaram maiores médias de rugosidade. Para a microdureza o fator Material isoladamente, e a interação TxS, TxM e SxM tiveram efeito estatisticamente significante. O M1 (61,2±0,87) apresentou maior microdureza, que M2 (54,4±0,87). Para a interação TxS, a condição S2T2 (54,09±2,61) apresentou menor média de microdureza. Para a interação TxM, o M1 comparado com M2 determinou maior microdureza nos tempos T0, T1 e T2. E para a interação SxM, M1S1 (61,59±1,51) e M1S2 (62,86±1,51) apresentaram maior microdureza que M2S1 (51,53±1,51) e M2S2 (54,34±1,51). De acordo com a metodologia pode-se concluir que: a) o M1 apresentou maior rugosidade superficial nos tempos T1, T2 e T3 e maior microdureza nos tempos T0, T1, e T2 do que o M2 b) O material M1 apresentou maior microdureza independente das soluções. / The aim of this study was to evaluate the surface roughness (&micro;m) and Vickers microhardness of provisory restorative materials: BiodentineTM (M1) and Fuji IX - glass ionomer cement (M2) were submitted to different mouthwashes. Fifty-four specimens were prepared using a Teflon mold (6mm x 2mm), randomly distributed into 6 groups according to the solution used: distilled water (S1), mouthwash containing alcohol -Listerine Cool Mint (S2) and alcohol-free mouthwash - Colgate Plax (S3). During the experiment, all specimens were carried out at a relative humidity of 100% in an oven at 37±1°C, except in the soaking periods in the established mouthwashes. The samples were individually placed in a flask containing 8mL of the specific mouthwash for each group for 1 minute, under vibration twice a day for a period of 21 days. The readings of the variables were carried out at the time of 48 hours (T0), 7 days (T1), 14 days (T2) and 21 days (T3). The obtained data were grouped in tables and submitted to the Normality Tests for Statistical Analysis Kolmogorov-Smirnov, Shapiro-Wilk, Anova and Tukey\'s Test provided by the Statistical software Assistat Program Version 7.7 beta (2016). Results: It was found that there was a significant effect on surface roughness when considered alone Time (T), Solution (S), Material (M) and the interaction between TxM and SxM. On the other hand, T3 (0.92±0.02) and M1 (0.87±0.01) presented the higher roughness and S3 (0.72±0.02) the lowest average roughness. For the interactions MxT and SxM, M1T3 (1,10±0,03) and M1S1 (1,03±0,03) presented higher roughness averages. To microhardness analysis, the material as a alone factor and the interaction TxS, TxM and SxM had a statistically significant effect. M1 (61.2±0.87) presented a higher microhardness than the M2 (54.4±0.87). For the TxS interaction, S2T2 (54.09 ± 2.61) had a lower microhardness average. To TxM interaction, the M1 compared to M2 determined a higher microhardness at T0, T1 and T2. In interaction SxM, M1S1 (61.59±1.51) and M1S2 (62.8 ±1.51) had a higher microhardness than M2S1 (51.53±1.51) and M2S2 (54.3 ±1,51). According to the methodology, it can be concluded that: a) M1 presented greater surface roughnes at T1, T2 and T3 and higher microhardness at T0, T1, and T2 than M2 b) M1 presented a higher microhardness than M2 for S1 and S2.

O objetivo deste trabalho foi o de avaliar in vitro o efeito da ação antibacteriana de cimentos de ionômero de vidro (CIVs) convencionais incorporados com diacetato de clorexidina (DCHX) sobre o Streptococcus mutans. Foram testados os CIVs Maxxion R e Vitro Fil R com a incorporação dos percentuais de 0,5%, 1% e 2% de DCHX através de difusão em ágar e pela exaustão do DCHX por até 40 dias, a fim de observar a longevidade de sua ação inibitória. Foi também avaliado o efeito do fluoreto de sódio na ação antibacteriana do DCHX. Para determinar a diferença entre a média dos halos de inibição Os resultados foram analisados por análise de variância e pelo teste Student-Newman-Keuls (SNK). Todos os corpos de prova com DCHX apresentaram halo para os CIVs variando de 2,29mm a 6,82mm para o Maxxion R e de 1,73mm a 8,97mm para o Vitro Fil R. A capacidade de inibição foi proporcional à concentração de DCHX. Através do teste SNK apenas os grupos Vitro Fil R 0,5% e1% não variaram significativamente entre si. O 15o dia foi o de maior atividade antibacteriana para ambos os CIVs. Os grupos Maxxion R 1% e 2% foram os que menos apresentaram diferenças ao longo do tempo. Não houve crescimento de S mutans para os períodos de 7 e 15 dias de exaustão, sendo verificado o crescimento de colônias apenas na superfície do meio após o período de 96hs de incubação. Não foi observado efeito antagônico na capacidade antibacteriana do DCHX na presença de fluoreto de sódio. A incorporação de DCHX aos CIVs Maxxion R e Vitro Fil R, nas concentrações testadas e por um período de até 40 dias, apresentam resultados positivos no controle bacteriano de S mutans. Dentro das limitações deste estudo é lícito concluir que: efeito da inibição ao S mutans é dependente da concentração do DCHX; o fluoreto por si só não é capaz de inibir o crescimento de S mutans; a associação do DCHX com os CIVs não alterou a capacidade da ação antibacteriana da CHX; a ação antibacteriana da CHX incorporada aos CIVs se mantém eficaz por 15 dias, independente do CIV testado. / The purpose of this study was to evaluate (the in vitro the effect) of antibacterial action of conventional glass ionomer cements (GICs glass ionomer cements) incorporated with chlorhexidine diacetate (DCHX) on Streptococcus mutans. We tested the GICs Maxxion Vitro Fil R & R with the incorporation of the percentage of 0.5%, 1% and 2% DCHX by agar diffusion and the depletion of DCHX by up to 15 days to observe the longevity of its inhibitory action. It was also evaluated the effect of sodium fluoride on the antibacterial action of DCHX. To determine the difference between the mean of the inhibition zones, the results were analyzed by analysis of variance and the Student-Newman-Keuls test (SNK). All specimens presented with DCHX halo for GICs ranging from 2.29 mm to 6.82 mm for Maxxion R and 1.73 mm to 8.97 mm for the FIL Vitro R. The inhibition capacity were proportional to the concentration of DCHX. Through the SNK test only groups Vitro Fil R 0.5% e1% did not vary significantly. The 15th day was the one with highest antibacterial activity for both GICs. The R Maxxion 1% and 2% were the groups with less differences over time. No growth was observed of S. mutans for periods of 7 and 15 days of exhaustion, with observed growth of colonies only on the surface of the culture media after 96 hours of incubation period. No antagonistic effect was observed in the ability of the antibacterial DCHX in the presence of sodium fluoride. Incorporating DCHX GICs Maxxion Vitro Fil R & R, in tested concentrations and for a period up to 40 days showed a positive bacterial control of S. mutans. Despite the limitations of this study, we may conclude that: inhibition effect of S. mutans is dependent on the concentration of DCHX; fluoride alone is not able to inhibit growth of S. mutans; the association of DCHX with VSDs did not alter the capacity of the antibacterial action of CHX and the antibacterial action of CHX incorporated into GICs remains effective for 15 days, regardless of the GIC tested.

Orientador: Elisa Maria Aparecida Giro / Resumo: Lesões de cárie secundarias nas margens das restaurações tem sido a principal razão para a sua substituição. Portanto, o desenvolvimento de materiais com propriedades antibacterianas melhoradas e duradouras é desejável. O objetivo deste estudo foi avaliar a influência da incorporação de nanopartículas de hexametafosfato de clorexidina (NPs CLX-HMP) a um cimento de ionômero de vidro (CIV) de alta viscosidade, nas suas propriedades físico-químicas, mecânica e antibacteriana. Após a síntese e caracterização, as nanopartículas foram adicionadas ao CIV nas concentrações de 1%, 2% e 5%. O CIV sem adição de nanopartículas foi utilizado como controle. Espécimes cilíndricos (3mm x 6mm) foram confeccionados com os materiais (n=12/grupo) e mantidos em água deionizada por 30 dias. A liberação de CLX foi avaliada no eluato por espectrofotometria ultravioleta e a dosagem do flúor foi feita com auxílio de um eletrodo específico, nos períodos de 1 h e 1, 7, 15 e 30 dias. No 30º dia, os espécimes receberam uma aplicação tópica de flúor gel neutro 2% e a liberação de flúor foi reavaliada por mais 30 dias. Para avaliar a atividade antibacteriana, biofilmes polimicrobianos cresceram sobre espécimes dos materiais (n=10/grupo), utilizando um modelo de aderência ativa. Em seguida, foram coletados e inoculados em meios de cultura específicos para a quantificação de microrganismos totais, bactérias acidúricas totais e estreptococos do grupo mutans. A atividade metabólica foi analisada pelo ensaio de ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Secondary caries on the margins of restorations have been the main reason for their replacement. Therefore, the development of materials with improved and long-lasting antibacterial properties is desirable. The objective of this study was to evaluate the influence of the incorporation of chlorhexidine hexametaphosphate nanoparticles (CHX-HMP NPs) to a high viscosity glass ionomer cement (GIC) in its physicochemical, mechanical and antibacterial properties. After synthesis and characterization, the nanoparticles were added to the GIC at concentrations of 0%, 1%, 2% and 5%. Cylindrical specimens (3 mm x 6 mm) made with the materials were kept in deionized water for 30 days. The CHX release was evaluated in the eluate by ultraviolet spectrophotometry and the fluoride dosage was done with the help of a specific electrode, in the periods of 1 h and 1, 7, 15 and 30 days. On the 30th day, the specimens received a topical application of neutral fluorine gel 2% and the fluoride release was reevaluated for another 30 days. To evaluate the antibacterial activity, polymicrobial biofilms grew on the specimens of the materials, using an active adherence model. The biofilms formed were collected, inoculated in specific culture media and thereafter, the quantification of total microorganisms, total acid bacteria and streptococci of mutans group was made. The metabolic activity was analyzed by the XTT assay and the biomass by violet crystal staining. Finally, it was evaluated the bond strength of the material to the sound and caries-affected dentin, after 24 h and 6 months of storage of the specimens in artificial saliva, using the microshear test. The fracture patterns were evaluated with the aid of light microscope. Adequate statistical tests were applied according to the distribution of the data and the homogeneity of variances. The level of significance was set at 5%. The synthesized nanoparticles presented ...(complete abstract electronic access below) / Doutor

Proposição: o objetivo deste trabalho foi avaliar, após doze meses, qualitativamente o desempenho clínico e o tempo gasto na execução de 86 restaurações atraumáticas realizadas em pré-escolares de creches comunitárias do município de Porto Alegre, utilizando o cimento de ionômero de vidro de alta viscosidade (Vitro- Molar/DFL). Metodologia: foram selecionadas 42 crianças com necessidades restauradoras, inseridas em um programa educativo-preventivo. As respectivas restaurações foram avaliadas seguindo os critérios USPHS modificado e analisadas estatisticamente pelo teste não paramétrico Mann- Whitney (p<0,05). Resultados: encontrou-se 94,2% de retenção das restaurações envolvendo uma ou mais superfícies em dentes decíduos. O tempo médio despendido para execução da restauração foi de 4,47 minutos segundo análise de variância. Conclusão: concluí-se que as restaurações atraumáticas são indicadas para serem utilizadas em pré-escolares, por apresentarem um bom desempenho clínico e agilidade no atendimento. / Objective: the aim of the present study was to qualitatively assess the clinical performance, after 12 months, of 86 atraumatic restorations bonded with highviscosity glass ionomer cement (Vitro-Molar/DFL), in preschoolers from Porto Alegre-based day care centers, in southern Brazil, and also to assess the length of the treatment. Methods: a total of 42 children who required restorative treatment were selected from a preventive educational program. The restorations were assessed using the modified USPHS criteria and statistically analyzed by the nonparametric Mann-Whitney test (p<0.05). Results: the restorations on one or more surfaces of deciduous teeth had a retention rate of 94.2%. According to the analysis of variance, the length of restorative treatment averaged 4.47 minutes. Conclusion: atraumatic restorations are recommended in preschoolers, since they have a good clinical performance and allow prompt treatment.

Foram avaliadas a resposta periodontal, clínica e histologicamente, a procedimentos restauradores subgengivais com amálgama de prata (Am), cimento de ionômero de vidro (CIV) e sítios controle não restaurados (CT), em um período de 120 dias, em 3 cães suscetíveis à doença periodontal. Após 4 meses de uma raspagem e alisamento supragengival, foram realizados retalhos totais seguidos de raspagem e alisamento radicular em pré-molares apresentando perda de inserção e sinais inflamatórios. Cavidades radiculares experimentais foram restauradas com Am ou CIV. Durante os 3 meses do pós-operatório os quadrantes 2 e 3 receberam controle mecânico de placa (c/ct). Previamente às restaurações e ao final do período experimental, foram anotados os índices de placa visível (IPV), sangramento gengival (ISG), sangramento à sondagem (SS), profundidade de sondagem (PS), perda de inserção (PI) e distância da margem gengival à uma marca referência na coroa (DMM). Nove dentes foram restaurados com Am, 11 com CIV, e 10 serviram como controles. Após processamento, em espécimes representativos, foram avaliados histologicamente o grau de inflamação no conjuntivo, integridade e posição do epitélio em relação à face cervical das restaurações e da crista óssea (epit/co), e a altura da crista óssea em relação ao preparo cavitário (cav/co). Todos os locais apresentavam inicialmente 100% de IPV, ISG e SS. Foram restaurados dez dentes com cada material e outros 10 locais foram utilizados como controle (CT). O IPV apresentou-se reduzido nos quadrantes 2 e 3 enquanto que o ISG apresentou reduções também nos locais sem controle de placa (s/ct). A redução no SS ocorreu somente em um cão. A PS apresentou alterações variadas, com as maiores reduções (-0,5mm) associadas ao CIV c/ct e os maiores aumentos com Am s/ct e CT s/ct (1,00mm). Aumentos da PI foram também variados, sendo os menores associados com áreas CT c/ct (1,00mm) e os maiores com Am s/ct. As diferenças entre DMM final e inicial variaram de –1,00mm (Am c/ct e CT c/ct) a 1,50mm (CIV c/ct). Alterações epiteliais foram mais freqüentemente observadas em sitos Am s/ct e c/ct. As médias das distâncias cav/co variaram de 1,77mm (CIV c/ct) a 2,51mm (CIV s/ct). As médias das distâncias epit/co variaram de 1,49mm (CIV c/ct) a 2,09mm (CT c/ct). Quanto ao infiltrado inflamatório, sítios Am s/ct e c/ct , e CIV s/ct estiveram mais associados a escores Severo. Pode-se concluir que quadros clínicos e histológicos de maior inflamação e destruição periodontal foram associados a locais restaurados em relação a locais não restaurados, sendo que a resposta inflamatória parece estar na dependência do controle da placa bacteriana supragengival.