La resistivité et le pouvoir thermoélectrique de deux séries d'alliages amorphes ont éte mesurés entre 4 et 300K. Létude a porté sur le MgZn et le CuZr, et dans les deux la plus vaste gamme de concentrations disponible pour ces materiaux amorphes. / The resistivity and thermopower of two series of amorphous alloys have been measured between 4 and 300K. The alloys studied are MgZn and CuZr, both in the largest concentration range available as amorphous materials.

A pesquisa teve como objetivo estudar procedimentos para a condução dos testes de deterioração controlada, envelhecimento acelerado, condutividade elétrica e lixiviação de potássio, procurando-se verificar sua eficiência para identificação de diferentes níveis de vigor de lotes de sementes de melão (Cucumis melo L.). Para tanto, o estudo foi conduzido em duas etapas, utilizando-se cinco lotes de sementes dos híbridos AF-646 e AF-682. Na primeira foram realizados os testes de germinação, primeira contagem de germinação, Método Agroflora, emergência de plântulas em casa de vegetação e estudos específicos para os testes de deterioração controlada (graus de umidade de 18%, 21% e 24%, a 45ºC, durante 24 e 48 horas), de envelhecimento acelerado, com e sem solução salina (períodos 48, 72 e 96 horas, a 38ºC ou 41ºC), de condutividade elétrica (temperaturas de 20ºC, 25ºC e 30ºC, volumes de 50 e 75mL de água, 25 e 50 sementes e períodos de 1, 2, 4, 8, 12, 16, 20 e 24 horas) e de lixiviação de potássio (25 e 50 sementes, 50 e 75mL de água, a 25ºC e 30ºC, durante 30, 60, e 90 minutos, 2h, 2h e 30 minutos, 3, 4 e 5 horas). Os procedimentos considerados mais promissores para cada teste, nesta primeira fase, foram comparados na segunda etapa, que também incluiu os testes de germinação, primeira contagem de germinação, Método Agroflora e emergência de plântulas em casa de vegetação. Diante dos resultados obtidos, concluiu-se que os testes de deterioração controlada (24%/45ºC/24h) e de envelhecimento acelerado (procedimento tradicional e com solução salina), utilizando a combinação 41ºC/72h, apresentam sensibilidade suficiente para avaliação do potencial fisiológico de sementes de melão. O teste de condutividade elétrica não constitui em opção eficiente para avaliação do vigor das sementes, enquanto o teste de lixiviação de potássio necessita de estudos adicionais para adequar sua metodologia e viabilizar a sua utilização para sementes de melão, considerando-se, inclusive, os prováveis efeitos do genótipo. / This research was conducted to study and select procedures for the controlled deterioration, accelerate aging, electrical conductivity and potassium lixiviation tests, to verify their sensitivity to identify different vigor levels of melon (Cucumis melo L.) seed lots. Five seed lots each from the hybrids AF-646 and AF-682 were used. In the first experimental stage, the following tests were performed: germination, germination first count, Agroflora Method and seedling emergence. Specific studies were also conducted to the following tests: controlled deterioration (seed moisture content of 18%, 21% and 24%, at 45ºC, for 24 and 48 hours), traditional accelerated aging, saturated salt accelerated aging (for 48, 72 and 96 hours, at 38 o C or 41 o C), electrical conductivity (25 or 50 seeds imbibed in 50mL or 75mL water, 20 o C, 25 o C and 30 o C, for 1, 2, 4, 8, 12, 16 and 20 hours) and potassium leachate (25 or 50 seeds, imbibed in 50mL and 75mL, at 25 o C and 30 o C, for 30, 60, 90, 120, 150, 180, 240 and 300 minutes). The procedures considered the most promising for each test in the first stage were compared, in the second stage. The later stage also included germination, germination first count, Agroflora Method and seedling emergence tests. From the results, it was concluded that controlled deterioration (24%/45 o C/24h) and accelerate aging (traditional procedure and salt saturated) tests, using the 41 o C/72h combination, showed to be sufficiently sensitive for the evaluation of the physiological potential of melon seeds. The electrical conductivity test does not constitute an efficient option for the vigor evaluation, while the potassium lixiviation test needs further studies in order to adjust its methodology and enable its use for melon seeds, also considering the probable genotype effects.

A correlação entre as medidas de condutividade elétrica e propriedades físico-químicas do solo é uma das linhas de estudo que vem sendo exploradas onde os conceitos de agricultura de precisão estão mais avançados. Este estudo teve como objetivo avaliar a eficiência do monitoramento da condutividade elétrica do solo a partir do desenvolvimento de dois sistemas. O primeiro, denominado de Resistência Elétrica do Solo (RES), consiste em definir a condutividade elétrica de um material através de uma amostra de dimensões conhecidas, para medir a sua resistência elétrica utilizando dois eletrodos. O segundo, denominado de Duas Pontas (DP), consiste em definir a condutividade elétrica de um material aplicando uma corrente elétrica em uma amostra para medir a alteração no potencial elétrico, gerado pelo meio em que a corrente elétrica transitou, utilizando dois eletrodos dispostos linearmente. Para a avaliação dos resultados obtidos pelos sistemas desenvolvidos foi utilizado como referência um sistema comercial de origem norte americana e algumas propriedades do solo. Os equipamentos de condutividade elétrica do solo foram aplicados em duas áreas pertencentes à Escola Superior de Agricultura “Luiz de Queiroz” e em época distintas. Na Área 1, com 4,97 ha, o levantamento dos dados foi feito na primeira quinzena de Agosto de 2003 e na Área 2, com 1,3 ha, o levantamento dos dados foi feito na segunda quinzena de Dezembro de 2003. Após a aquisição dos dados experimentais foram feitas análises estatísticas descritivas e exploratórias, análises geoestatísticas, construção de mapas de superfície, análises de correlação e regressão linear múltipla a fim de avaliar os sistemas. De acordo com a metodologia desenvolvida e análises de funcionamento dos equipamentos, foi possível verificar que os sistemas construídos para a coleta, transformação e armazenagem dos dados foram eficientes no levantamento dos pontos amostrais. No entanto os sistemas de condutividade elétrica do solo não apresentaram a eficiência desejada no monitoramento das propriedades do solo em ambas as áreas experimentais. Quando os sistemas desenvolvidos foram comparados ao sistema comercial, também foi possível observar que não houve correlação no monitoramento, o que sugere a necessidade da continuidade e aprofundamento no desenvolvimento desses sistemas. / The correlation between electrical conductivity and physical-chemical properties of the soil is one of the research areas that have been explored where precision agriculture concepts are more advanced. This study had the objective of evaluating the soil electrical conductivity mapping efficiency of different measuring systems. The first one, known as Electrical Resistance of the Soil consists in defining the electrical conductivity of any given material using a sample of known dimensions, to measure its electrical resistance using two electrodes. The second one, the Two Edges method, consists in defining the electrical conductivity of a material applying an electric current in a sample to measure any change on the electric potential, generated by the environment in which the electric current transited through, using two linearly displaced electrodes. To evaluate the results obtained by the developed systems some soil properties and a commercial soil electrical conductivity measuring system where used as guidelines. The soil electrical conductivity equipments mapped two fields, at the Escola Superior de Agricultura “Luiz de Queiroz”. In Field 1 (4,97 ha) the data collecting process took place in the first fortnight of august 2003, and, in Field 2 (1,3 ha), the sampling process took place in the second fortnight of December 2003. After the acquisition of the experimental data, descriptive and exploratory statistical and geostatistical analysis were made, electrical conductivity surface maps were obtained and correlation and multiple linear regression analysis, in order to evaluate both systems, were made. In accordance to the developed methodology and analysis of the equipment, it was possible to check that the systems developed to acquire, transform and store the data were efficient in mapping the sampling points. However, the soil electrical conductivity systems did not show the desired efficiency in mapping the soil properties in both experimental fields. When the developed systems were compared to a commercial one it was also possible to observe that there was no correlation in the measurements, which suggests the necessity of new developments on these systems.

A solução sólida céria-samária é uma das principais candidatas para aplicação como eletrólito sólido em células a combustível de óxido sólido, devido sua alta condutividade iônica em temperaturas intermediárias (500-750 ºC) de operação. Um dos problemas ainda não solucionados com relação a este material é sua relativamente baixa sinterabilidade. Nesse trabalho foi utilizado o método de sinterização em duas etapas visando melhorar a densificação com reduzido tamanho médio de grãos. Soluções sólidas comercial e obtida por mistura de óxidos de composição Ce0,8Sm0,2O1,9 foram utilizadas. Para fins comparativos também foi utilizado o método denominado sinterização em duas etapas tradicional que visa a obtenção de amostras densas independentemente do tamanho médio de grãos. Resultados de densidade aparente e retração linear revelaram que ambos os tipos de amostras têm comportamento distinto. Para a solução sólida comercial, a retração total até 1400 ºC foi de ~18%. Só foram obtidos resultados de densidade significativos ao utilizar temperaturas elevadas (igual ou superior a 1300 ºC). Para o material obtido por mistura de óxidos não foi possível atingir densidades maiores que 90% da densidade teórica. A sinterização em duas etapas tradicional produziu amostras densas, da mesma forma, que a não-tradicional, mas com tamanhos de grãos consideravelmente maiores. Amostras sinterizadas por ambos os processos foram analisadas por espectroscopia de impedância para a determinação da condutividade elétrica em função da temperatura, e não apresentaram variação significativa nas condutividades intra e intergranular. A sinterização em duas etapas não resultou em melhorias na densificação e nem na condutividade elétrica das amostras. Entretanto, a redução obtida no tamanho médio de grãos pode melhorar as propriedades mecânicas. / Samaria-doped ceria solid solution has been proposed to be used as solid electrolyte in Solid Oxide Fuel Cells due to its high ionic conductivity at intermediate temperatures (500-750 ºC). One of the main problems related to this solid solution is the relatively low sinterability. In this work, sintering of powder compacts was carried out by the two-step sintering method to improve the densification with simultaneous reduction of the mean grain size. Samaria-doped ceria, both commercial and prepared by solid state reactions, with composition Ce0.8Sm0.2O1.9 were investigated. For comparison purposes, the traditional two-step sintering method, by which dense specimens are produced, was also utilized. Apparent density and linear shrinkage results showed distinct features depending on the type of specimen. Total linear shrinkage for commercial solid solution up to ~ 1400 ºC was 18%, but high density values were obtained only for sintering experiments conducted at high temperatures ( 1300 ºC). Specimens prepared by solid state reactions did not attain density values higher than 90% of the theoretical one. The traditional method produced dense specimens as well as the two-step sintering, although the grain size was considerably higher in the former. Specimens sintered by the two methods were used for electrical conductivity measurements. No significant variation in both the grain and the grain boundary conductivities was obtained. The two-step sintering did not allow any improvement in the densification and in the electrical conductivity of samaria-doped ceria. However, the decrease in the mean grain size may contribute to improve the mechanical properties of this solid solution.

Amostras de antimoneto de cobalto, preparadas pela fusão de quantidades estequi- ométricas de Co e Sb, foram submetidas a diferentes condições de pressão, temperatura e tempo com objetivo de maximizar a produção de uma fase de alta pressão previamente ob- servada em experimentos com uma câmara de bigornas de diamantes. A partir dos dados de difração de raios X (convencional e síncrotron), refinamentos Rietveld foram realizados para determinar a composição de fases e os parâmetros estruturais. O maior rendimento foi obtido a 7,7 GPa, 550 ◦C e, ao menos, 5 min de processamento (89(2)% em massa da fase de SbxCoSb3−x).O método de maximização da entropia foi utilizado para obtenção de mapas de densidade eletrônica da fase SbxCoSb3−x à temperatura ambiente e a 155 ◦C. Os resultados revelaram uma distribuição de carga com um conjunto de seis máximos fora do centro da cavidade em condições ambiente, compatível com o sítio 12d do grupo espacial de simetria Im3. A 155 ◦C a distribuição da densidade de carga associada ao átomo inserido na cavidade está uniformemente distribuída por cerca de 0,5 Å a partir do centro da cavidade (sítio 2a), ao longo de seis direções equivalentes. O pico endotérmico observado em resul- tados de calorimetria exploratória de varredura a 145 ◦C foi atribuido à transição reversível da espécie hóspede, do sítio 12d para o sítio 2a. A carga total dentro da cavidade, obtida a partir da análise de Bader, foi de aproximadamente 50,6e. Isto confirma a hipótese original de que são átomos de Sb que se encontram dentro da cavidade do antimoneto de cobalto. Contudo, o mecanismo de formação da fase SbxCoSb3−x em alta pressão e alta temperatura é diferente daquele nos experimentos com a câmara de bigornas de diamantes. Nas amostras processadas a 7,7 GPa e 550 ◦C são encontradas as fases Sb0,20CoSb2,80, CoSb2,79 e CoSb2, sendo que a primeira é formada pela inserção de Sb resultante da decomposição do antimo- neto de cobalto. A condutividade térmica e o coeficiente Seebeck foram medidos para esta amostra e, usando modelos para materiais compósitos, as propriedades termoelétricas foram estimadas para as fases CoSb2,79 e Sb0,20CoSb2,80. A condutividade térmica do CoSb2,79 e Sb0,20CoSb2,80 é igual a 1,5 W·m−1· ◦C−1 e 1,4 W·m−1· ◦C−1, respectivamente, à tempe- ratura ambiente. De acordo com os resultados obtidos para o coeficiente Seebeck, as fases CoSb2,79 e Sb0,20CoSb2,80 apresentam comportamento semicondutor tipo n. A figura de mé- rito termoelétrico do Sb0,20CoSb2,80 é cerca de 33% maior que a do CoSb2,79 à temperatura ambiente. / Cobalt antimonide samples, prepared by melting stoichiometric quantities of Co and Sb, were submitted to different conditions of pressure, temperature and time, aiming to maximize the production of the high pressure phase previously observed in experiments with a diamond anvil cell. From x-ray powder diffraction data (both conventional and syn- chrotron), Rietveld refinements were performed to determine the phase composition and structural parameters. The maximum yield was obtained at 7.7 GPa, 550 ◦C and, at least, 5 min of processing (89(2)wt.% of SbxCoSb3−x phase). The maximum-entropy method was used to obtain electronic charge density maps for SbxCoSb3−x at room temperature and at 155 ◦C. The results revealed a charge distribution with a set of six maxima off the center of the cage at ambient conditions, compatible with 12d site of Im3 space group. At 155 ◦C the charge density distribution associated to the guest atom is evenly spread over about 0.5 Å from the center of the cage (2a site), along six equivalent directions. The endothermic peak previously observed in differential scanning calorimetry analysis at 145 ◦C was thus attribu- ted to the reversible transition guest species, 12d site to 2a site. The total charge inside the cage, obtained from Bader’s analysis, was approximately 50,6e. This confirms the original hypothesis that Sb atoms occupy the cages of the cobalt antimonide. However, the forma- tion mechanism of the SbxCoSb3−x phase at high pressure and high temperature is different from that in the experiments with the diamond anvil cell. Indeed, in samples processed at 7.7 GPa and 550 ◦C we observe the presence of Sb0.20CoSb2.80, CoSb2.79 and CoSb2 phases, end evidences suggest that the former is formed by insertion of Sb resulting from decompo- sition of cobalt antimonide. Thermal conductivity and Seebeck coefficient were measured for this sample and, using models for composite materials, the thermoelectric properties were estimated for CoSb2.79 and Sb0.20CoSb2.80 phases. Thermal conductivity of CoSb2.79 and Sb0.20CoSb2.80 is 1.5 W·m−1· ◦C−1 and 1.4 W·m−1· ◦C−1, respectively, at room tem- perature. According to the results obtained for the Seebeck coefficient, the CoSb2.79 and Sb0.20CoSb2.80 phases exhibit n-type semiconducting behavior. The thermoelectric figure of merit for Sb0.20CoSb2.80 is about 33% greater than that for CoSb2.79 at room temperature.

Esta tese trata-se dos estudos dos mecanismos relacionados com a condução elétrica ac de polietileno de baixa densidade (PEBD), virgem e envelhecido sob radiação UV, carregado com diferentes concentrações de negro de fumo (NF). Medidas experimentais de condutividade ac foram feitas em amostras com diferentes concentrações de NF, em diferentes temperaturas. Análise de calorimetria diferencial (DSC) e medidas de expansão térmica foram realizadas como complementos a esse estudo. Observamos também o efeito do envelhecimento UV sobre as propriedades elétrica das amostras. Baseado na distribuição do NF na matriz polietileno, a condutividade ac foi explicada em termos do mecanismo \"hopping\" considerando o material como um sistema onde as barreiras de energia potencial estão aleatoriamente distribuídas no volume do material. Estudamos a ruptura dielétrica do PEBD/NF com diferentes concentrações de NF, e os resultados foram interpretados usando a distribuição estatística de Weibull, utilizando tanto o métodos gráfico quanto o analítico, para determinar a rigidez dielétrica e os parâmetros de escala e de forma da distribuição / We performed a study of mechanisms related to ac electrical conduction of virgin and aged low-density polyethylene (LDPE) charged with different concentrations of carbon black (CB). Experimental ac conductivity measurements were carried out in samples of different CB concentrations for several temperatures. Measurements of differential scanning calorimetry (DSC) and of thermal expansion were performed as auxiliary methods in this study. We also observed the ultraviolet aging effect on the electrical properties of the samples. Based on the distribution of the CB in the polyethylene matrix, the ac conductivity was explained in t e m of hopping mechanism considering the material as a system where the energy potential barriers are randomly distributed in material bulk. We also performed studies of dielectric breakdown of LDPE/NF with different CB concentrations, and the results are studied by Weibull approach, using both analytical and graphic methods to determine the dielectric strength and the scale and shape parameters

The Precision Agriculture is a management tool that allows you to evaluate, analyze and intervene with actions in the correct location, at the correct time with the correct agricultural input and with the more profitably way, decreasing the spatial variability of the area also allowing increases in productivity with rationalization of resources. In economic terms, the use of this technology allows the prioritization of investments in areas where the potential for production is more effective, ensuring a bigger economic return. The geostatistics has become an important tool because it allows us to study the behavior of the spatial variability, both of chemical and of physical nature, allows to the producer to combine this information with the productivity maps and thus make decisions that can increase production efficiency. The objective of this study was to evaluate through maps of soil compaction and electrical conductivity which of these factors is more correlated with soybean yield in irrigated area. The work was conducted in the municipality of Pejuçara, RS. The first step was the acquisition of productivity map at harvest of the crop soybeans 2013-2014, in a demarcated area of 47 hectares. After was carried the work to yield maps of soil compaction on three layers of soil, collected in 190 points in the area, and the data were interpolated with CR Campeiro 7. For the assessment of soil electrical conductivity, we used the equipment Veris 3100 which made assessments at depths 0-30 and 30-90 cm deep. After the evaluations, it was found that much of the area is compacted. From the analyzes performed, it was not possible to notice the correlation between productivity and the variables studied. These facts lead us to conclude that in irrigated area the soil compaction is not able to affect, so severely in the levels detected, the development of culture. / A Agricultura de Precisão é uma ferramenta de gestão que permite avaliar, analisar e intervir com ações no local correto, na hora correta com o insumo correto e da maneira mais rentável, diminuindo a variabilidade espacial da área permitindo também aumentos na produtividade com racionalização dos recursos.Em termos econômicos, a utilização desta tecnologia possibilita a priorização de investimentos em áreas onde o potencial de produção seja mais efetivo, garantindo maior retorno econômico. A geoestatística se tornou uma importante ferramenta pois permite estudar o comportamento da variabilidade espacial, além de poder também quantificar o seu tamanho. Estudos da variabilidade espacial, tanto de natureza química quanto física, permite ao produtor aliar essas informações aos mapas de produtividade e assim tomar decisões que possam aumentar a eficiência da produção.O objetivo desse trabalho foi avaliar através de mapas de compactação de solo e condutividade elétrica quais desses fatores que mais se correlacionam com a produtividade de soja em área irrigada.O trabalho foi realizado no município de Pejuçara, RS, onde sua primeira etapa foi a aquisição do mapa de produtividade na colheita da soja safra 2013-2014, numa área demarcada de 47 ha. Após realizou-se o trabalho para originar os mapas de compactação de solo em três camadas de solo, coletados em 190 pontos da área, sendo que os dados obtidos foram interpolados com o CRCampeiro7. Para a avaliação da condutividade elétrica do solo, utilizou-se o equipamento Veris 3100 o qual fez avaliações nas camadas de 0-30 e 30-90 cm de profundidade. Após as avaliações feitas, verificou-se que grande parte da área encontra-se compactada, não sendo possível perceber correlação entre produtividade e as variáveis estudadas. Esses fatos nos levam a concluir que em área irrigada a compactação de solo não é capaz de afetar, com tanta severidade, até os níveis detectados, o desenvolvimento da cultura.

O presente estudo apresenta uma investigação experimental sobre as propriedades de magnetotransporte nos compostos Ba(Fe1−xMnx)2As2 com x = 0, 2,57, 5,16, 9,27 e 14,7 at % de Mn. Este sistemas apresentam ordem antiferromagnética do tipo onda de densidade de spin (Spin Density Wave - SDW). Em baixas concentrações de Mn, a transição magnética é acompanhada de uma transição estrutural do estado tetragonal e paramagnético de alta temperatura para um estado ortorrômbico e magneticamente ordenado de baixas temperaturas. Os resultados de magnetorresistência mostram efeitos de condução por duas bandas (elétrons e lacunas). Observa-se também efeitos do mecanismo de supressão da desordem de spin induzida pelo campo magnético aplicado. As medidas de resistividade Hall mostram que a contribuição Hall anômala está presente e domina em todo o regime magneticamente ordenado. O mecanismo de espalhamento por impurezas magnéticas, skew-scattering, é o principal responsável pela contribuição anômala ao efeito Hall. Outro objeto de estudo desta Tese é a família de compostos RCo12B6 (R = Y, Gd e Ho). O ordenamento magnético observado nestes compostos depende do átomo de terra rara presente. No composto YCo12B6 ocorre uma ordem do tipo ferromagnética (TC ≈ 148 K). Entretanto, os compostos GdCo12B6 e HoCo12B6 apresentam um estado do tipo ferrimagnético (TC ≈ 160 K e 144 K, respectivamente), com uma temperatura de compensação em torno de 50 K. Resultados de magnetização, calor específico, efeito magnetocalórico, resistividade, magnetorresistência e efeito Hall são apresentados e discutidos. Os resultados de resistividade e magnetorresistência indicam que a condução elétrica é polarizada em spin. A magnetorresistência é fortemente positiva em baixas temperaturas e revela efeitos de mistura das correntes dependentes de spin. A magnetorresistência é fortemente positiva em baixas temperaturas e revela efeitos de mistura das correntes dependentes de spin. Nas medidas de efeito Hall evidenciou-se a presença de bandas de elétrons e lacunas. O mecanismo de skew-scattering é a contribuição mais importante ao termo anômalo da resistividade Hall destes sistemas. Contudo, uma segunda contribuição ao efeito Hall anômalo deve ser considerada. Essa contribuição é relacionada ao efeito de quiralidade originada por canting na sub-rede de Co. Indícios da presença de frustração também são percebidos nos resultados de magnetização, magnetorresistência, efeito magnetocalórico e impedância elétrica. Neste último, também se observa o efeito Hopking nas vizinhanças da temperatura de ordem magnética. / This work presents an experimental investigation on the magnetotransport properties of the compounds Ba(Fe1−xMnx)2As2, with x = 0, 2,57, 5,16, 9,27 e 14,7 at % Mn. These compounds exhibit Spin DensityWave (SDW) antiferromagnetic ordering. In low Mn concentration, a structural transition from a high-temperature paramagnetic and tetragonal phase to a low-temperature antiferromagnetic and orthorhombic phase is observed. The magnetoresistance results show contributions from the conduction by two bands (electrons and holes) and from the suppression of spin disorder induced by the applied magnetic field. Hall resistivity measurements shows that the anomalous contribution is dominant in the magnetically ordered phase. The asymmetric scattering mechanism by magnetic impurities, known as skew scattering, is responsible for the anomalous contribution to the Hall effect in the Ba(Fe1−xMnx)2As2 system. Magnetotransport studies, as well as magnetization, specific heat and magnetocaloric effect experiments were performed in the compounds RCo12B6 (R = Y, Gd and Ho). The magnetic ordering observed in these systems depends on the rare-earth atom. In the compound YCo12B6, a ferromagnetic type ordering is observed (TC ≈ 148 K). The compounds GdCo12B6 and HoCo12B6 show a magnetic order of ferrimagnetic type (TC ≈ 160 K e 144 K, respectively), with a compensation temperature around 50 K. The resistivity and magnetoresistance results indicate that the current is spin polarized. Hall resistivity measurements are consistent with two-band conduction (electrons and holes). The skew scattering mechanism is the most relevant contribution to the anomalous Hall resistivity in these compounds. However, a second anomalous contribution to the anomalous Hall effect must be considered. This term is due to canting of the Co moments that originates a chiral mechanism. Evidences of frustration are also present in the results of magnetization, magnetoresistance, magnetocaloric effect and electrical impedance. In the last, one also observes the occurrence of the Hopkinson effect around TC.

O presente trabalho consiste da realização de um estudo experimental sobre os efeitos das substituições químicas na irreversibilidade magnética e na magnetocondutividade do supercondutor YBa2Cu3O7-δ. Para tanto, o comportamento da linha de irreversibilidade magnética (LIM) bem como dos regimes de flutuações na magnetocondutividade foram pesquisados em amostras policristalinas e moncristalinas de YBa2-xSrxCu3O7-δ (x = 0, 0.1, 0.25, 0.37 e 0.5) e YBa2Cu2.97D0.03O7-δ (D = Zn ou Mg). Além de reduzir drasticamente o valor da temperatura crítica de transição, Tc, os dopantes introduzem um caráter granular nos monocristais. No monocristal puro, o comportamento da LIM é descrito pela lei de potências prevista pelo modelo de "flux creep" gigante para dinâmica de fluxo de Abrikosov convencional. Por outro lado, o comportamento da LIM para as amostras supercondutoras granulares apresenta características própias bastante relevantes. Os dados do limite de irreversibilidade, Tirr(H) seguem a lei de potência ditada pelas teorias de "flux creep" somente em altos campos magnéticos.Na região de baixos campos magnéticos, dois diferentes regimes de dinâmica de fluxo surgem: Nos campos magnéticos mais baixos que 1 kOe, os dados de Tirr(H) seguem uma lei de potência do tipo de Almeida-Thouleess (AT). Perto de 1 kOe, ocorre um "crossover" e em campos magnéticos intermediários passa a ter seu comportamento descrito por uma lei de potências do tipo Gabay-Toulouse (GT). A ocorrência de um comportamento AT-GT na LIM é a assinatura de um sistema frustrado onde a dinâmica de fluxo intergranular ou de Josephson é dominante. Na ausência de teorias específicas para este comportamento em baixos campos, descrevemos o comportamento da LIM de nossos supercondutores granulares, na região de baixo campo, em analogia aos sistemas vidros de spin. No entanto, o comportamento de Tirr(H) na região de altos campos, ocorre de acordo com a teoria de "flux creep" gigante. Particularmente, para valores acima de 20 kOe, a LIM nos monocristais de YBa2-xSrxCu3O7-δ para H // ab, exibe fortes propriedades direcionais para a orientação de H próximo aos planos de maclas (PMCs). Este comportamento é do tipo "cusp", similar ao observado em supercondutores com defeitos colunares, o qual caracteriza uma fase vidro de Bose. Por outro lado, a magnetoresistividade elétrica revela que a transição resistiva dos supercondutores granulares ocorre em duas etapas. Quando a temperatura é decrescida, inicialmente ocorre a transição de pareamento no interior dos grãos. Em temperaturas inferiores, na proximidade do estado de resistência nula, ocorre a transição de coerência, observada pela primeira vez num monocristal. Na transição de coerência, o parâmetro de ordem adquire ordem de longo alcance. Na região de temperaturas imediatamente acima de Tc, nossos resultados de flutuações na magnetocondutividade revelam a ocorrência de regimes críticos e Gaussianos. Abaixo de Tc, na região paracoerente, que antecede à transição de coerência, observaram-se regimes críticos cujo expoente é consistente com o esperado para o modelo 3D-XY com desordem relevante e dinâmica do tipo vidro de spin.

A resistividade elétrica de ligas CoFe, onde a concen tração de ferro varia de 0 a 10 at%, foi medida no intervalo de temperatura entre 4°K e 300°K. Os resultados permitiram separar as ligas em diluídas e concentradas. Para as ligas diluídas interpretou-se os desvios da regra de Matthiessen em termos de um modelo de condução por duas bandas acopladas. Nas amostras concentradas, os efeitos de transições de fase estruturais tornam a resistividade elétrica em função complicada da temperatura e da concentração. / The electric resistivity measurements on CoFe alloys have been performed as a function of temperature in the interval 4 < T < 300°K, and iron concentration 0 < c < 10 at%. The deviations from Matthiessen's rule for up to 4 at% Fe was possible to interpret in terras of a coupled two band conduction model. The electric resistivity of the high iron concentration alloys (c > 4 at% Fe) has been proved to be an involved function of the temperature and concentration, due to phase transition effects.