Objetivos: avaliar o efeito de 3 parâmetros de condicionamento da dentina utilizando o laser de Er,Cr;YSGG (2,78m) na resistência de união (RU) de cimento de ionômero de vidro convencional (CIV). Materiais e métodos: Foram utilizados neste estudo 68 terceiros molares humanos, divididos aleatoriamente em 4 grupos (n=17/ grupo): G1 (grupo controle): nenhum tipo de condicionamento; G2: condicionamento com laser de Er,Cr;YSGG 0,5W, 25mJ, 20Hz ou G3: 1,0W, 50mJ, 20Hz e G4: 1,5W, 75mJ, 20Hz. Dois dentes em cada um dos grupos foram observados em microscopia eletrônica de varredura (MEV) para identificar as características morfológicas dos diferentes condicionamentos de superfície realizados. Os outros 15 dentes/grupo, foram preparados para ensaio de RU, obtendo uma superfície plana de dentina onde foram construídos 3 (n=45/grupo) corpos de prova em forma de cilindro (1mm de diâmetro X 0,5mm de altura) utilizando o ionômero de vidro Ketac Molar Easymix- 3M ESPE. Após o armazenamento em água destilada por 24h a 37oC os espécimes foram ensaiados pelo teste de microcisalhamento. Os valores finais de resistência adesiva foram calculados e expressos em Mega Pascal (MPa). Os dados foram coletados e analisados por ANOVA (p<0,001). Resultados: Os espécimes do G2 apresentaram os maiores resultados de RU (10,50MPa ±0,84), seguido pelo G1 (4.77MPa ±0.59), G3 (3.32MPa ±0.39) e G4 (2,94MPa ±0,50) que não apresentaram diferença estatisticamente significante quanto comparados entre si. A análise em MEV do G1 mostrou camada de smear ao longo de toda a superfície de dentina, enquanto nos outros grupos observou-se túbulos dentinários abertos, característicos na irradiação com laser de Er,Cr:YSGG. Os pulsos do laser no G2 eram facilmente distinguidos, o que não acontecia nos grupos G3 e G4, sugerindo que parâmetros de energia maiores podem causar efeitos mais extensos à estrutura da dentina. Na análise do padrão de fratura, todos os grupos apresentaram maior porcentagem de fratura adesiva G1:73,3%, G2:48,9% G3:66,7% e G4:64,4%. O tipo de fratura mista foi proporcional ao aumento da RU (G1:24,4%, G2:46,7%, G3:20,0% e G4:17,8%). Conclusão: O condicionamento da dentina com o laser de Er,Cr:YSGG na potência de 0,5W aumentou significativamente a RU do CIV à dentina, enquanto os demais parâmetros testados reduziram a RU. / Objective: To evaluate the effect of 3 dentin conditioning parameters of Er,Cr:YSGG laser (2,78 m) on the bond strength (BS) of conventional glass ionomer cement (CGIC). Methods: A total of 68 third molars were divided into four groups and was subjected to one of the following pretreatments: G1- the control group, no pretreatment was realized; G2, G3 and G4 were pretreated with Er,Cr:YSGG laser irradiation at 0.5 W, 25 mJ, 9 J/cm2, and 20 Hz (G2); 1.0 W, 50 mJ, 18 J/cm2, and 20 Hz (G3); and at 1.5 W, 75 mJ, 27 J/cm2, and 20 Hz (G4). A scanning electron microscopy (SEM) evaluation (n=2) of pretreated dentine and a microshear bond strength test (n=15) were performed after 24h of water immersion. To build the specimens (each of which was 1 mm in diameter) for the microshear test, CGIC (Ketac Molar Easy Mix) was used. The data were analysed by one-way ANOVA (p<0.001). Results: The G2 specimens presented the highest BS results (10.50 MPa ± 0.84), and G1 had the next highest average BS values (4.77 MPa ± 0.59). G3 (3.32 MPa ± 0.39) and G4 (2.94 MPa ± 0.50) demonstrated the lowest BS values, although the BS difference between these groups was not statistically significant (p>0.001). The SEM analysis of G1 revealed that the smear layer covered the entire dentine surface, whereas in groups G2, G3, and G4, irregular dentine was detected that possessed the open dentinal tubules and protruded peritubular dentine that are the characteristic results of laser irradiation. Laser pulses could easily be distinguished in G2 but not in G3 and G4, suggesting that higher energy parameters can broadly disrupt dentine structure and thereby affect the bonding of dentine to GIC. Conclusion: Dentine pretreatment with an Er,Cr:YSGG laser at a power of 0.5 W increased the BS of conventional GIC.

Com o objetivo de testar a qualidade das restaurações realizadas após a remoção de cárie de raiz com laser de alta potência, realizamos esse trabalho. Lesões de cárie radicular foram induzidas em fragmentos dentais humanos (n=154) através de contaminação com o S. mutans. Obtidas as lesões, essas foram removidas com instrumento cortante rotatório (ICR) em baixa rotação (grupo controle) ou com o laser de Er,Cr:YSGG, (?=2,78 µm, taxa de repetição= 20 Hz, duração de pulso na ordem de 140 a 150 µs, energia por pulso de 0 a 300 mJ) em 13 potências diferentes entre 1 e 4 W, em intervalos de 0,25 W entre cada grupo (n=11 por grupo). Para a remoção de cárie, foi utilizada a peça de mão 2415 e a fibra de safira modelo ?G? (Ø= 600 µm) posicionada a 1 mm das amostras (modo não contato). Após a remoção das lesões de cárie e mensuração do tempo necessário para este passo operatório, uma amostra de cada grupo foi preparada para microscopia eletrônica de varredura (MEV). Em seguida, as demais foram condicionadas com Clearfil SE Bond, restauradas com resina composta de baixa viscosidade e submetidas à termociclagem (1.000 ciclos de 5°C e 55°C) e então imersas em solução de azul de metileno a 2 % para teste de microinfiltração. Depois desta etapa, as amostras foram seccionadas e analisadas em microscopia luz para a obtenção do índice de microinfiltração, assim como de outras características, como a área da interface dente/restauração, a profundidade das cavidades, e a presença de cárie residual sob as restaurações. Os dados foram comparados estatisticamente (p?0,05). Os resultados indicaram que o ICR removeu as lesões de cárie mais rapidamente que o laser (p<0,05). As eletromicrografias de varredura mostraram que o grupo controle apresentou as margens cavitárias sem irregularidades e a superfície dentinária coberta pela camada de esfregaço, obliterando os túbulos dentinários. Todas as cavidades preparadas com o laser apresentaram margens irregulares. Quando parâmetros inferiores a 2,0 W foram utilizados, observou-se a presença de material amorfo sobre a superfície dentinária, com pouca exposição dos túbulos dentinários. Já nos parâmetros acima de 2,0 W, as cavidades apresentaram superfícies com aspecto de escamas, ausência da camada de esfregaço, túbulos dentinários abertos e crateras, distribuídas de forma irregular. Quando analisadas em microscopia de luz, as amostras irradiadas com potências superiores a 3,0 W apresentaram cavidades mais profundas em relação às demais. Graças às irregularidades promovidas pelo laser, as amostras irradiadas com potências maiores que 1,5 W apresentaram maior área de interface dente/restauração do que aquelas do grupo controle ou irradiadas com os parâmetros mais baixos. O índice de infiltração foi semelhante entre todos os grupos irradiados, e significantemente maiores que o do grupo controle. Houve correlação fortemente positiva entre a quantidade de cárie residual presente nas amostras e os índices de microinfiltração. Nas condições deste estudo pôde-se concluir que a remoção de cárie radicular com laser de Er,Cr:YSGG seguida de restauração com resina composta mostrou pobre selamento marginal em função da presença de cárie residual nas paredes das cavidades. / The present study aimed to compare the sealing ability of root caries restoration after caries removal with bur or Er,Cr:YSGG laser. Seventy two extracted human carious-free molars and premolars were used. After the in vitro root caries induction using S. mutans, the carious lesions were removed either by the conventional technique using burs (control), or by the Er,Cr:YSGG laser ((?=2,78 µm, repetition rate= 20 Hz, pulse duration around 150 µs, energy per pulse of 0 to 300 mJ, non-contact mode), using 13 different parameters, between 1 and 4,0 W. For the irradiation procedures, a 600 µm tip was used. During caries removal, preparation time was recorded for all groups. After that, one sample of each group was observed in scanning electron microscopy (MEV), and the others were conditioned with Clearfil SE Bond and restored with a flowable composite. Then, the samples were termocycled (1000 Cycles) and immersed into a 2 % methylene blue solution for microlekage analysis. These samples were sectioned and analyzed under light microscopy for microleakage index calculation. Other characteristics, such as the dentin/composite interface area, the cavity depth and the presence of residual caries under the restorations, were also evaluated. The data were statistically analyzed by either ANOVA complemented by the Tukey?s test or Kruskall-Wallis complemented by the Dunn?s test (p = 0.05). The caries lesions were significantly faster removed by the conventional method (p<0.05). Amongst the lased groups, the caries removal time was inversely proportional to the parameters used. SEM revealed that the surfaces treated by air turbine were smooth, but with debris. When parameters under 2.0 W were used, an amorphous material covering the dentin surface was observed. Using parameters above of 2.0 W, SEM revealed surfaces with smooth undulations, with absence of smear layer, and some irregular-distributed craters. No signs of carbonization were observed. The light microscopy analysis showed that the samples irradiated with power outputs over 3.0 W were deeper than those irradiated with lower parameters and those prepared with bur. The samples irradiated with power outputs higher than 1.5 W presented dentin/composite interface area larger than those of the control group. Finally, the infiltration index was similar in all lased groups, and significantly higher than those of control group (p<0.05). The microleakage index and the presence of residual caries, only detected by light microscopy, at the lateral walls of the cavities obtained by Er, Cr:YSGG laser was significantly higher compared to control cavities. In the conditions of this study, we can conclude that the carious removal by Er, Cr:YSGG laser, independently of the parameters used, creates dentin surfaces characteristics that promotes a poor marginal sealing.

Com o objetivo de testar a qualidade das restaurações realizadas após a remoção de cárie de raiz com laser de alta potência, realizamos esse trabalho. Lesões de cárie radicular foram induzidas em fragmentos dentais humanos (n=154) através de contaminação com o S. mutans. Obtidas as lesões, essas foram removidas com instrumento cortante rotatório (ICR) em baixa rotação (grupo controle) ou com o laser de Er,Cr:YSGG, (?=2,78 µm, taxa de repetição= 20 Hz, duração de pulso na ordem de 140 a 150 µs, energia por pulso de 0 a 300 mJ) em 13 potências diferentes entre 1 e 4 W, em intervalos de 0,25 W entre cada grupo (n=11 por grupo). Para a remoção de cárie, foi utilizada a peça de mão 2415 e a fibra de safira modelo ?G? (Ø= 600 µm) posicionada a 1 mm das amostras (modo não contato). Após a remoção das lesões de cárie e mensuração do tempo necessário para este passo operatório, uma amostra de cada grupo foi preparada para microscopia eletrônica de varredura (MEV). Em seguida, as demais foram condicionadas com Clearfil SE Bond, restauradas com resina composta de baixa viscosidade e submetidas à termociclagem (1.000 ciclos de 5°C e 55°C) e então imersas em solução de azul de metileno a 2 % para teste de microinfiltração. Depois desta etapa, as amostras foram seccionadas e analisadas em microscopia luz para a obtenção do índice de microinfiltração, assim como de outras características, como a área da interface dente/restauração, a profundidade das cavidades, e a presença de cárie residual sob as restaurações. Os dados foram comparados estatisticamente (p?0,05). Os resultados indicaram que o ICR removeu as lesões de cárie mais rapidamente que o laser (p<0,05). As eletromicrografias de varredura mostraram que o grupo controle apresentou as margens cavitárias sem irregularidades e a superfície dentinária coberta pela camada de esfregaço, obliterando os túbulos dentinários. Todas as cavidades preparadas com o laser apresentaram margens irregulares. Quando parâmetros inferiores a 2,0 W foram utilizados, observou-se a presença de material amorfo sobre a superfície dentinária, com pouca exposição dos túbulos dentinários. Já nos parâmetros acima de 2,0 W, as cavidades apresentaram superfícies com aspecto de escamas, ausência da camada de esfregaço, túbulos dentinários abertos e crateras, distribuídas de forma irregular. Quando analisadas em microscopia de luz, as amostras irradiadas com potências superiores a 3,0 W apresentaram cavidades mais profundas em relação às demais. Graças às irregularidades promovidas pelo laser, as amostras irradiadas com potências maiores que 1,5 W apresentaram maior área de interface dente/restauração do que aquelas do grupo controle ou irradiadas com os parâmetros mais baixos. O índice de infiltração foi semelhante entre todos os grupos irradiados, e significantemente maiores que o do grupo controle. Houve correlação fortemente positiva entre a quantidade de cárie residual presente nas amostras e os índices de microinfiltração. Nas condições deste estudo pôde-se concluir que a remoção de cárie radicular com laser de Er,Cr:YSGG seguida de restauração com resina composta mostrou pobre selamento marginal em função da presença de cárie residual nas paredes das cavidades. / The present study aimed to compare the sealing ability of root caries restoration after caries removal with bur or Er,Cr:YSGG laser. Seventy two extracted human carious-free molars and premolars were used. After the in vitro root caries induction using S. mutans, the carious lesions were removed either by the conventional technique using burs (control), or by the Er,Cr:YSGG laser ((?=2,78 µm, repetition rate= 20 Hz, pulse duration around 150 µs, energy per pulse of 0 to 300 mJ, non-contact mode), using 13 different parameters, between 1 and 4,0 W. For the irradiation procedures, a 600 µm tip was used. During caries removal, preparation time was recorded for all groups. After that, one sample of each group was observed in scanning electron microscopy (MEV), and the others were conditioned with Clearfil SE Bond and restored with a flowable composite. Then, the samples were termocycled (1000 Cycles) and immersed into a 2 % methylene blue solution for microlekage analysis. These samples were sectioned and analyzed under light microscopy for microleakage index calculation. Other characteristics, such as the dentin/composite interface area, the cavity depth and the presence of residual caries under the restorations, were also evaluated. The data were statistically analyzed by either ANOVA complemented by the Tukey?s test or Kruskall-Wallis complemented by the Dunn?s test (p = 0.05). The caries lesions were significantly faster removed by the conventional method (p<0.05). Amongst the lased groups, the caries removal time was inversely proportional to the parameters used. SEM revealed that the surfaces treated by air turbine were smooth, but with debris. When parameters under 2.0 W were used, an amorphous material covering the dentin surface was observed. Using parameters above of 2.0 W, SEM revealed surfaces with smooth undulations, with absence of smear layer, and some irregular-distributed craters. No signs of carbonization were observed. The light microscopy analysis showed that the samples irradiated with power outputs over 3.0 W were deeper than those irradiated with lower parameters and those prepared with bur. The samples irradiated with power outputs higher than 1.5 W presented dentin/composite interface area larger than those of the control group. Finally, the infiltration index was similar in all lased groups, and significantly higher than those of control group (p<0.05). The microleakage index and the presence of residual caries, only detected by light microscopy, at the lateral walls of the cavities obtained by Er, Cr:YSGG laser was significantly higher compared to control cavities. In the conditions of this study, we can conclude that the carious removal by Er, Cr:YSGG laser, independently of the parameters used, creates dentin surfaces characteristics that promotes a poor marginal sealing.

Objetivos: avaliar o efeito de 3 parâmetros de condicionamento da dentina utilizando o laser de Er,Cr;YSGG (2,78m) na resistência de união (RU) de cimento de ionômero de vidro convencional (CIV). Materiais e métodos: Foram utilizados neste estudo 68 terceiros molares humanos, divididos aleatoriamente em 4 grupos (n=17/ grupo): G1 (grupo controle): nenhum tipo de condicionamento; G2: condicionamento com laser de Er,Cr;YSGG 0,5W, 25mJ, 20Hz ou G3: 1,0W, 50mJ, 20Hz e G4: 1,5W, 75mJ, 20Hz. Dois dentes em cada um dos grupos foram observados em microscopia eletrônica de varredura (MEV) para identificar as características morfológicas dos diferentes condicionamentos de superfície realizados. Os outros 15 dentes/grupo, foram preparados para ensaio de RU, obtendo uma superfície plana de dentina onde foram construídos 3 (n=45/grupo) corpos de prova em forma de cilindro (1mm de diâmetro X 0,5mm de altura) utilizando o ionômero de vidro Ketac Molar Easymix- 3M ESPE. Após o armazenamento em água destilada por 24h a 37oC os espécimes foram ensaiados pelo teste de microcisalhamento. Os valores finais de resistência adesiva foram calculados e expressos em Mega Pascal (MPa). Os dados foram coletados e analisados por ANOVA (p<0,001). Resultados: Os espécimes do G2 apresentaram os maiores resultados de RU (10,50MPa ±0,84), seguido pelo G1 (4.77MPa ±0.59), G3 (3.32MPa ±0.39) e G4 (2,94MPa ±0,50) que não apresentaram diferença estatisticamente significante quanto comparados entre si. A análise em MEV do G1 mostrou camada de smear ao longo de toda a superfície de dentina, enquanto nos outros grupos observou-se túbulos dentinários abertos, característicos na irradiação com laser de Er,Cr:YSGG. Os pulsos do laser no G2 eram facilmente distinguidos, o que não acontecia nos grupos G3 e G4, sugerindo que parâmetros de energia maiores podem causar efeitos mais extensos à estrutura da dentina. Na análise do padrão de fratura, todos os grupos apresentaram maior porcentagem de fratura adesiva G1:73,3%, G2:48,9% G3:66,7% e G4:64,4%. O tipo de fratura mista foi proporcional ao aumento da RU (G1:24,4%, G2:46,7%, G3:20,0% e G4:17,8%). Conclusão: O condicionamento da dentina com o laser de Er,Cr:YSGG na potência de 0,5W aumentou significativamente a RU do CIV à dentina, enquanto os demais parâmetros testados reduziram a RU. / Objective: To evaluate the effect of 3 dentin conditioning parameters of Er,Cr:YSGG laser (2,78 m) on the bond strength (BS) of conventional glass ionomer cement (CGIC). Methods: A total of 68 third molars were divided into four groups and was subjected to one of the following pretreatments: G1- the control group, no pretreatment was realized; G2, G3 and G4 were pretreated with Er,Cr:YSGG laser irradiation at 0.5 W, 25 mJ, 9 J/cm2, and 20 Hz (G2); 1.0 W, 50 mJ, 18 J/cm2, and 20 Hz (G3); and at 1.5 W, 75 mJ, 27 J/cm2, and 20 Hz (G4). A scanning electron microscopy (SEM) evaluation (n=2) of pretreated dentine and a microshear bond strength test (n=15) were performed after 24h of water immersion. To build the specimens (each of which was 1 mm in diameter) for the microshear test, CGIC (Ketac Molar Easy Mix) was used. The data were analysed by one-way ANOVA (p<0.001). Results: The G2 specimens presented the highest BS results (10.50 MPa ± 0.84), and G1 had the next highest average BS values (4.77 MPa ± 0.59). G3 (3.32 MPa ± 0.39) and G4 (2.94 MPa ± 0.50) demonstrated the lowest BS values, although the BS difference between these groups was not statistically significant (p>0.001). The SEM analysis of G1 revealed that the smear layer covered the entire dentine surface, whereas in groups G2, G3, and G4, irregular dentine was detected that possessed the open dentinal tubules and protruded peritubular dentine that are the characteristic results of laser irradiation. Laser pulses could easily be distinguished in G2 but not in G3 and G4, suggesting that higher energy parameters can broadly disrupt dentine structure and thereby affect the bonding of dentine to GIC. Conclusion: Dentine pretreatment with an Er,Cr:YSGG laser at a power of 0.5 W increased the BS of conventional GIC.

O objetivo deste estudo foi o de avaliar os efeitos da irradiação laser de Er,Cr:YSGG em superfícies dentinárias no tratamento da hipersensibilidade dentinária cervical, em busca de um protocolo para ser aplicado clinicamente. Para o teste de permeabilidade, foram preparados 144 pré-molares, as coroas seccionadas e as raízes impermeabilizadas. Duas áreas de irradiação antagônicas foram delimitadas e livres da impermeabilização (controle e experimental). A seguir, os dentes foram subdivididos em dois sub-grupos, diferindo o condicionamento da superfície irradiada (EDTA 24% e ácido fosfórico 35%) e em grupos diferindo o protocolo:G1)Er:YAG, 60mJ/2Hz; G2)0,25W; G3)0,5W; G4)0,75W; G5)1W, G6)1,25W; G7)1,50W; G8)1,75W G9)2W. Após as irradiações, os espécimes foram imersos em azul de metileno 2% por 4 horas, e incluídos em resina epóxica para a realização dos cortes longitudinais. Estes tiveram suas imagens trabalhadas em computador para mensuração do nível de infiltração. Os dados foram submetidos à análise estatística. O Sub-grupo 1, condicionado com EDTA, apresentou diferenças entre os grupos sendo que as amostras irradiadas com Er:YAG demonstraram menor infiltração, diferindo estatisticamente dos grupos 3, 6 e 9. Os resultados do sub-grupo 2 mostraram que as médias das amostras irradiadas com Er:YAG tenderam a zero entretanto, não houve diferença entre os grupos. Na Fase B, fragmentos de dentina foram obtidos da região cervical de dentes humanos, preparados para análise em microscopia eletrônica de varredura. Morfologicamente, observou-se oclusão parcial dos túbulos dentinários após irradiação com Er:YAG e Er,Cr:YSGG nas condições de 0,25W e 0,50W. A partir de 0.75W, foi observado abertura dos túbulos e à medida que as energias aumentaram, foram observadas carbonização e fendas. De posse dos resultados dos trabalhos in vitro, foram selecionados os parâmetros para a aplicação e o acompanhamento clínico de 1 mês: G1)controle (placebo); G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Após a triagem, foram selecionados voluntários de acordo com critérios de exclusão e inclusão. O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice 1 semana antes (Pré-1), 5 minutos anterior ao tratamento (Pré-2), após 5 minutos (Pós-1), 1 semana (Pós-2) e 1 mês após o tratamento (Pós-3). Os dados foram coletados e submetidos à análise estatística separadamente para os dois estímulos realizados: spray de ar e sonda exploradora. Tanto para o estímulo ar quanto para o estímulo sonda, não foram observadas diferenças estatisticamente significantes nas escalas Pré-1 e Pré-2, concluindo que os pacientes estavam padronizados e não houve efeito da profilaxia nos níveis de dor. Ao estímulo do spray de ar, nota-se uma redução nos níveis de dor na escala Pós-1, porém há uma estabilidade dos valores das escalas seguintes. O grupo 2 (Er:YAG) apresentou o menor nível de dor quando comparado aos outros grupos. Ao estímulo mecânico foi observado que o grupo 4 (Er,Cr:YSGG 0,50W) demonstrou o decréscimo de dor mais acentuado imediatamente após o tratamento, porém ao final do estudo, apresentou os maiores níveis de dor. Os grupos 1, 2 e 3 apresentam redução de dor, porém estatisticamente diferentes do grupo 4. Com base nos resultados apresentados e dentro dos limites e parâmetros estudados, pode-se concluir que nenhuma condição foi capaz de eliminar completamente a microinfiltração e diminuir a permeabilidade dentinária; porém o laser de Er:YAG e o laser de Er,Cr:YSGG 0,25W apresentaram resultados satisfatórios nos três estudos realizados. / The aim of the present study was to determine the correct parameters of the Er,Cr:YSGG laser in the treatment of cervical dentin hypersensitivity. This work was presented in 3 different stages. In the first one, it was evaluated the decrease in dentin permeability of dentinal tubules after Er,Cr:YSGG laser irradiation in radicular surfaces. Ninety premolars were prepared with its crows sectioned, and the roots completely impermeabilized. Two antagonist areas of irradiation were determined as control and experimental. Each surface was conditioned with EDTA 24% (sub-group1) and phosphoric acid 35% (sub-group2) and the selected parameters were: 1)Er:YAG, 60mJ, 2Hz, 4 irradiations of 20sec each, defocused mode; and groups 2 to 9 received irradiation with Er,Cr:YSGG laser, 20Hz, Z6 tip, 600µm diameter, defocus mode, 0% of air and water: 2)Er,Cr:YSGG 0,25W; 3) 0,5W; 4) 0,75W; 5) 1,0W; 6) 1,25W, 7) 1,50W, 8) 2W; 9) 2 W. After irradiation, samples were immersed in a solution of methylene blue for 4 hours, washed for 5 min and included in epoxy resin to allow longitudinal cuts. The images were digitalized and computed worked. Data was statistically analyzed. Although the samples irradiated with Er:YAG showed less microleakage, the sub-group 1 showed differences between the groups, statistically different from groups 3, 6 e 9. The results of the sub-group 2 showed that the mean values of the Er:YAG samples had a tendency to be negative, however, no differences were detected between the groups. In the second stage, cuts from the cervical area were obtained and prepared for scanning electron microscopy to evaluate the superficial morphology. It was observed the partial closure of dentinal tubules after the irradiation with Er:YAG and Er,Cr:YSGG laser in the 0.25 and 0.50W protocols. From the 0.75W until 2W, it was observed the dentinal tubules opened as the energy densities raised. With the results of the in vitro studies, the parameters were selected: G1)control; G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Thirty subjects, who met the entry criteria, were admitted into the study. The assessment method used to quantify sensitivity was the cold air syringe, recorded by the visual analogue scale (VAS), prior to treatment as baseline (Pre-1), immediately before (Pre-2) and immediately after (Post-1) the topical treatment, after 1 week (Post-2) and after 1 month (Post-3). Teeth were assigned to the 4 groups. After the follow-up, data was collected and submitted to statistical analysis for both kinds of stimulus: evaporative (air) and mechanical (probe). For both air and probe it was not observed differences among the Pre-1 and Pre-2 moments, for what it can be concluded that patients were standardized. Analyzing the evaporative stimulus, it can be observed the reduction in the pain level immediately after the treatment; however there was stability in the next values. Group 2 (Er:YAG) showed the least level of pain. Throughout the mechanical stimulus, it was observed that group 4 (Er,Cr:YSGG 0,50W) showed the most pronounced decrease of pain immediately after treatment, however, at the end of the study, the levels of pain increased. Groups 1, 2 e 3 showed reduction of pain, statistically different from the group 4. Based on the results and within the limits of this study, it can be concluded that none of the parameters and lasers studied were capable of eliminate the microleakage and decrease the dentin permeability, however, the Er:YAG and Er,Cr:YSGG 0,25W lasers showed satisfactory results in the three studies performed.

A erosão dental provoca alterações histológicas complexas na dentina e, apesar do aumento da ocorrência desta patologia na última década, a literatura apresenta poucos estudos sobre a adesão na dentina erodida. Com o aprimoramento da tecnologia e o conhecimento de que os lasers de érbio apresentam grande afinidade pela água e hidroxiapatita, sua utilização tem sido considerada um método alternativo para tratamento da superfície dentinária antes dos procedimentos adesivos. Assim, o objetivo deste trabalho in vitro foi avaliar o efeito de diferentes tratamentos de superfície (ponta diamantada, laser de Er:YAG 2,94 m, 60 mJ, 2 Hz, 0,2 W, 19,3 J/cm2 - e laser de Er,Cr:YSGG 2,78 m, 50 mJ, 30 Hz, 1,5 W, 4,5 J/cm2), prévios ao tratamento restaurador, tanto na dentina humana hígida quanto na dentina artificialmente erodida. Metade das amostras foi submetida à ciclagem erosiva, a qual foi realizada durante 5 dias por meio da imersão em solução de ácido cítrico 0,05 M (pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Na fase experimental 1, 32 fragmentos de dentina foram divididos aleatoriamente em 8 grupos (n = 4) e com o auxílio da Microscopia Eletrônica de Varredura (MEV), realizou-se a análise da morfologia da superfície da dentina hígida e da submetida à ciclagem erosiva, após os diferentes tratamentos de superfície. Na fase experimental 2, 192 terceiros molares humanos foram divididos aleatoriamente em 2 grupos (dentina hígida e dentina submetida à ciclagem erosiva) e 8 subgrupos (n = 12) para avaliação da resistência de união entre as superfícies tratadas e 2 sistemas adesivos (01 autocondicionante e 01 com condicionamento ácido prévio), por meio do ensaio de microtração e da análise do padrão de fratura. Para o ensaio de microtração, blocos de resina composta microhíbrida foram confeccionados na superfície de dentina e, após armazenados em água destilada-deionizada por 24h (37oC), palitos foram obtidos para serem tracionados na máquina de ensaio universal (0,5mm/min). A análise do padrão de fratura realizada em microscópio ótico (40x) e as avaliações das eletromicrografias foram feitas de forma descritiva. Os valores obtidos de resistência de união(MPa) foram submetidos aos testes de ANOVA (dois fatores) e de comparações múltiplas de Tukey (p<0,05). A análise morfológica de superfície mostrou alterações significativas da dentina hígida e da dentina artificialmente erodida, submetidas aos diferentes tratamentos de superfície. Quanto à resistência de união, na dentina hígida, o grupo controle, tanto do sistema autocondicionante (54,69 ± 7,80 MPa) quanto do condicionamento ácido total (47,36 ± 9,35 MPa), apresentou valores significativamente maiores que os outros grupos, sendo, porém, diferentes entre si. Na dentina erodida, a maior resistência de união foi alcançada com o grupo tratado com o laser de Er,Cr:YSGG associado ao adesivo autocondicionante (28,26 ± 9,22 MPa), o qual foi significativamente diferente de todos demais grupos. Com base nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que em dentina hígida, os tratamentos de superfície com os lasers de Er:YAG e Er,Cr:YSGG apresentaram resultados de adesão inferiores, mas satisfatórios, em relação ao grupo controle. Já em substrato dentinário erodido, a irradiação com laser de Er,Cr:YSGG, associada ao uso de sistema adesivo autocondicionante, promoveu efeito positivo para a adesão à resina composta. / Dental erosion can cause complex histological changes in dentin and, despite the increase in its incidence during the last decade, limited information is available regarding adhesion to eroded dentin. With improvements in technology and due to the fact that the erbium lasers have high affinity to water and hydroxyapatite, the use of laser can consist on an alternative for the treatment of dentin surface before adhesive procedures. The aim of this in vitro study was to evaluate the effect of different surface treatments (diamond bur, Er:YAG laser 2.94 m, 60 mJ, 2 Hz, 0.2 W, 19.3 J/cm2 - and Er,Cr:YSGG laser 2.78 m, 50 mJ, 30 Hz, 1.5 W, 4.5 J/cm2) prior to restorative treatment, in sound and artificially eroded human dentin. Half of the samples was submitted to the erosive cycling, which was performed by immersion in 0.05 M citric acid (pH 2.3, 10 min, 6x/day) and in supersaturated solution (pH 7.0, 1h, between acid attacks), during 5 days. In phase 1, 32 dentin fragments were randomly divided into 8 groups (n = 4). The analysis of surface morphology of both sound and eroded dentin was performed by Scanning Electron Microscopy (SEM), after the different surface treatments. In phase 2, 192 human third molars were randomly divided into 2 groups (sound and eroded dentin) and 8 subgroups (n=12) to evaluate the bond strength between the treated surfaces and composite resin, with two adhesive systems (self-etching and total-etching) by means of the microtensile bond strength (TBS) test and fracture pattern analysis. For the microtensile bond strength test, blocks of composite resin were bonded to the samples and, after 24 h-storage in distilled/deionized water (37°C), stick-shapped samples were obtained and submitted to TBS test in a universal testing machine (0.5 mm/min). The fracture pattern was performed with an optical microscopy (40x) and the evaluations of the electromicrographs were made under a descriptive mode. The bond strength values (MPa) were analyzed by two-way ANOVA and Tukey tests ( = 0.05). In sound dentin, for the control group, both self-etching (54.69 ± 7.8 MPa) and total-etching adhesive system (47.36 ± 9.3 MPa) showed significantly higher values than all other groups (p<0.05), even though they differ from each other. However, in eroded dentin groups, the self-etching on the samples treated with the Er,Cr:YSGG laser presented the highest mean (28.3 ± 9.2 MPa), which was statistically significant higher than all the other treatments (p<0.05). Based on the irradiation parameters considered for this study, it can be concluded that in healthy dentin, the surface treatment with Er:YAG and Er,Cr:YSGG irradiation showed bonding values lower than the control group, but they presented satisfactory results. However, in eroded dentin, the use of Er,Cr:YSGG laser, associated with the self-etching adhesive system, promoted positive effect on adhesion to composite resin.

O objetivo deste estudo foi o de avaliar os efeitos da irradiação laser de Er,Cr:YSGG em superfícies dentinárias no tratamento da hipersensibilidade dentinária cervical, em busca de um protocolo para ser aplicado clinicamente. Para o teste de permeabilidade, foram preparados 144 pré-molares, as coroas seccionadas e as raízes impermeabilizadas. Duas áreas de irradiação antagônicas foram delimitadas e livres da impermeabilização (controle e experimental). A seguir, os dentes foram subdivididos em dois sub-grupos, diferindo o condicionamento da superfície irradiada (EDTA 24% e ácido fosfórico 35%) e em grupos diferindo o protocolo:G1)Er:YAG, 60mJ/2Hz; G2)0,25W; G3)0,5W; G4)0,75W; G5)1W, G6)1,25W; G7)1,50W; G8)1,75W G9)2W. Após as irradiações, os espécimes foram imersos em azul de metileno 2% por 4 horas, e incluídos em resina epóxica para a realização dos cortes longitudinais. Estes tiveram suas imagens trabalhadas em computador para mensuração do nível de infiltração. Os dados foram submetidos à análise estatística. O Sub-grupo 1, condicionado com EDTA, apresentou diferenças entre os grupos sendo que as amostras irradiadas com Er:YAG demonstraram menor infiltração, diferindo estatisticamente dos grupos 3, 6 e 9. Os resultados do sub-grupo 2 mostraram que as médias das amostras irradiadas com Er:YAG tenderam a zero entretanto, não houve diferença entre os grupos. Na Fase B, fragmentos de dentina foram obtidos da região cervical de dentes humanos, preparados para análise em microscopia eletrônica de varredura. Morfologicamente, observou-se oclusão parcial dos túbulos dentinários após irradiação com Er:YAG e Er,Cr:YSGG nas condições de 0,25W e 0,50W. A partir de 0.75W, foi observado abertura dos túbulos e à medida que as energias aumentaram, foram observadas carbonização e fendas. De posse dos resultados dos trabalhos in vitro, foram selecionados os parâmetros para a aplicação e o acompanhamento clínico de 1 mês: G1)controle (placebo); G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Após a triagem, foram selecionados voluntários de acordo com critérios de exclusão e inclusão. O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice 1 semana antes (Pré-1), 5 minutos anterior ao tratamento (Pré-2), após 5 minutos (Pós-1), 1 semana (Pós-2) e 1 mês após o tratamento (Pós-3). Os dados foram coletados e submetidos à análise estatística separadamente para os dois estímulos realizados: spray de ar e sonda exploradora. Tanto para o estímulo ar quanto para o estímulo sonda, não foram observadas diferenças estatisticamente significantes nas escalas Pré-1 e Pré-2, concluindo que os pacientes estavam padronizados e não houve efeito da profilaxia nos níveis de dor. Ao estímulo do spray de ar, nota-se uma redução nos níveis de dor na escala Pós-1, porém há uma estabilidade dos valores das escalas seguintes. O grupo 2 (Er:YAG) apresentou o menor nível de dor quando comparado aos outros grupos. Ao estímulo mecânico foi observado que o grupo 4 (Er,Cr:YSGG 0,50W) demonstrou o decréscimo de dor mais acentuado imediatamente após o tratamento, porém ao final do estudo, apresentou os maiores níveis de dor. Os grupos 1, 2 e 3 apresentam redução de dor, porém estatisticamente diferentes do grupo 4. Com base nos resultados apresentados e dentro dos limites e parâmetros estudados, pode-se concluir que nenhuma condição foi capaz de eliminar completamente a microinfiltração e diminuir a permeabilidade dentinária; porém o laser de Er:YAG e o laser de Er,Cr:YSGG 0,25W apresentaram resultados satisfatórios nos três estudos realizados. / The aim of the present study was to determine the correct parameters of the Er,Cr:YSGG laser in the treatment of cervical dentin hypersensitivity. This work was presented in 3 different stages. In the first one, it was evaluated the decrease in dentin permeability of dentinal tubules after Er,Cr:YSGG laser irradiation in radicular surfaces. Ninety premolars were prepared with its crows sectioned, and the roots completely impermeabilized. Two antagonist areas of irradiation were determined as control and experimental. Each surface was conditioned with EDTA 24% (sub-group1) and phosphoric acid 35% (sub-group2) and the selected parameters were: 1)Er:YAG, 60mJ, 2Hz, 4 irradiations of 20sec each, defocused mode; and groups 2 to 9 received irradiation with Er,Cr:YSGG laser, 20Hz, Z6 tip, 600µm diameter, defocus mode, 0% of air and water: 2)Er,Cr:YSGG 0,25W; 3) 0,5W; 4) 0,75W; 5) 1,0W; 6) 1,25W, 7) 1,50W, 8) 2W; 9) 2 W. After irradiation, samples were immersed in a solution of methylene blue for 4 hours, washed for 5 min and included in epoxy resin to allow longitudinal cuts. The images were digitalized and computed worked. Data was statistically analyzed. Although the samples irradiated with Er:YAG showed less microleakage, the sub-group 1 showed differences between the groups, statistically different from groups 3, 6 e 9. The results of the sub-group 2 showed that the mean values of the Er:YAG samples had a tendency to be negative, however, no differences were detected between the groups. In the second stage, cuts from the cervical area were obtained and prepared for scanning electron microscopy to evaluate the superficial morphology. It was observed the partial closure of dentinal tubules after the irradiation with Er:YAG and Er,Cr:YSGG laser in the 0.25 and 0.50W protocols. From the 0.75W until 2W, it was observed the dentinal tubules opened as the energy densities raised. With the results of the in vitro studies, the parameters were selected: G1)control; G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Thirty subjects, who met the entry criteria, were admitted into the study. The assessment method used to quantify sensitivity was the cold air syringe, recorded by the visual analogue scale (VAS), prior to treatment as baseline (Pre-1), immediately before (Pre-2) and immediately after (Post-1) the topical treatment, after 1 week (Post-2) and after 1 month (Post-3). Teeth were assigned to the 4 groups. After the follow-up, data was collected and submitted to statistical analysis for both kinds of stimulus: evaporative (air) and mechanical (probe). For both air and probe it was not observed differences among the Pre-1 and Pre-2 moments, for what it can be concluded that patients were standardized. Analyzing the evaporative stimulus, it can be observed the reduction in the pain level immediately after the treatment; however there was stability in the next values. Group 2 (Er:YAG) showed the least level of pain. Throughout the mechanical stimulus, it was observed that group 4 (Er,Cr:YSGG 0,50W) showed the most pronounced decrease of pain immediately after treatment, however, at the end of the study, the levels of pain increased. Groups 1, 2 e 3 showed reduction of pain, statistically different from the group 4. Based on the results and within the limits of this study, it can be concluded that none of the parameters and lasers studied were capable of eliminate the microleakage and decrease the dentin permeability, however, the Er:YAG and Er,Cr:YSGG 0,25W lasers showed satisfactory results in the three studies performed.

A erosão dental provoca alterações histológicas complexas na dentina e, apesar do aumento da ocorrência desta patologia na última década, a literatura apresenta poucos estudos sobre a adesão na dentina erodida. Com o aprimoramento da tecnologia e o conhecimento de que os lasers de érbio apresentam grande afinidade pela água e hidroxiapatita, sua utilização tem sido considerada um método alternativo para tratamento da superfície dentinária antes dos procedimentos adesivos. Assim, o objetivo deste trabalho in vitro foi avaliar o efeito de diferentes tratamentos de superfície (ponta diamantada, laser de Er:YAG 2,94 m, 60 mJ, 2 Hz, 0,2 W, 19,3 J/cm2 - e laser de Er,Cr:YSGG 2,78 m, 50 mJ, 30 Hz, 1,5 W, 4,5 J/cm2), prévios ao tratamento restaurador, tanto na dentina humana hígida quanto na dentina artificialmente erodida. Metade das amostras foi submetida à ciclagem erosiva, a qual foi realizada durante 5 dias por meio da imersão em solução de ácido cítrico 0,05 M (pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Na fase experimental 1, 32 fragmentos de dentina foram divididos aleatoriamente em 8 grupos (n = 4) e com o auxílio da Microscopia Eletrônica de Varredura (MEV), realizou-se a análise da morfologia da superfície da dentina hígida e da submetida à ciclagem erosiva, após os diferentes tratamentos de superfície. Na fase experimental 2, 192 terceiros molares humanos foram divididos aleatoriamente em 2 grupos (dentina hígida e dentina submetida à ciclagem erosiva) e 8 subgrupos (n = 12) para avaliação da resistência de união entre as superfícies tratadas e 2 sistemas adesivos (01 autocondicionante e 01 com condicionamento ácido prévio), por meio do ensaio de microtração e da análise do padrão de fratura. Para o ensaio de microtração, blocos de resina composta microhíbrida foram confeccionados na superfície de dentina e, após armazenados em água destilada-deionizada por 24h (37oC), palitos foram obtidos para serem tracionados na máquina de ensaio universal (0,5mm/min). A análise do padrão de fratura realizada em microscópio ótico (40x) e as avaliações das eletromicrografias foram feitas de forma descritiva. Os valores obtidos de resistência de união(MPa) foram submetidos aos testes de ANOVA (dois fatores) e de comparações múltiplas de Tukey (p<0,05). A análise morfológica de superfície mostrou alterações significativas da dentina hígida e da dentina artificialmente erodida, submetidas aos diferentes tratamentos de superfície. Quanto à resistência de união, na dentina hígida, o grupo controle, tanto do sistema autocondicionante (54,69 ± 7,80 MPa) quanto do condicionamento ácido total (47,36 ± 9,35 MPa), apresentou valores significativamente maiores que os outros grupos, sendo, porém, diferentes entre si. Na dentina erodida, a maior resistência de união foi alcançada com o grupo tratado com o laser de Er,Cr:YSGG associado ao adesivo autocondicionante (28,26 ± 9,22 MPa), o qual foi significativamente diferente de todos demais grupos. Com base nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que em dentina hígida, os tratamentos de superfície com os lasers de Er:YAG e Er,Cr:YSGG apresentaram resultados de adesão inferiores, mas satisfatórios, em relação ao grupo controle. Já em substrato dentinário erodido, a irradiação com laser de Er,Cr:YSGG, associada ao uso de sistema adesivo autocondicionante, promoveu efeito positivo para a adesão à resina composta. / Dental erosion can cause complex histological changes in dentin and, despite the increase in its incidence during the last decade, limited information is available regarding adhesion to eroded dentin. With improvements in technology and due to the fact that the erbium lasers have high affinity to water and hydroxyapatite, the use of laser can consist on an alternative for the treatment of dentin surface before adhesive procedures. The aim of this in vitro study was to evaluate the effect of different surface treatments (diamond bur, Er:YAG laser 2.94 m, 60 mJ, 2 Hz, 0.2 W, 19.3 J/cm2 - and Er,Cr:YSGG laser 2.78 m, 50 mJ, 30 Hz, 1.5 W, 4.5 J/cm2) prior to restorative treatment, in sound and artificially eroded human dentin. Half of the samples was submitted to the erosive cycling, which was performed by immersion in 0.05 M citric acid (pH 2.3, 10 min, 6x/day) and in supersaturated solution (pH 7.0, 1h, between acid attacks), during 5 days. In phase 1, 32 dentin fragments were randomly divided into 8 groups (n = 4). The analysis of surface morphology of both sound and eroded dentin was performed by Scanning Electron Microscopy (SEM), after the different surface treatments. In phase 2, 192 human third molars were randomly divided into 2 groups (sound and eroded dentin) and 8 subgroups (n=12) to evaluate the bond strength between the treated surfaces and composite resin, with two adhesive systems (self-etching and total-etching) by means of the microtensile bond strength (TBS) test and fracture pattern analysis. For the microtensile bond strength test, blocks of composite resin were bonded to the samples and, after 24 h-storage in distilled/deionized water (37°C), stick-shapped samples were obtained and submitted to TBS test in a universal testing machine (0.5 mm/min). The fracture pattern was performed with an optical microscopy (40x) and the evaluations of the electromicrographs were made under a descriptive mode. The bond strength values (MPa) were analyzed by two-way ANOVA and Tukey tests ( = 0.05). In sound dentin, for the control group, both self-etching (54.69 ± 7.8 MPa) and total-etching adhesive system (47.36 ± 9.3 MPa) showed significantly higher values than all other groups (p<0.05), even though they differ from each other. However, in eroded dentin groups, the self-etching on the samples treated with the Er,Cr:YSGG laser presented the highest mean (28.3 ± 9.2 MPa), which was statistically significant higher than all the other treatments (p<0.05). Based on the irradiation parameters considered for this study, it can be concluded that in healthy dentin, the surface treatment with Er:YAG and Er,Cr:YSGG irradiation showed bonding values lower than the control group, but they presented satisfactory results. However, in eroded dentin, the use of Er,Cr:YSGG laser, associated with the self-etching adhesive system, promoted positive effect on adhesion to composite resin.

Objetivos: Este estudo teve como objetivo avaliar a resistência de união entre cimento resinoso e as amostras de zircônia irradiadas como o laser de Er,Cr:YSGG em quatro parâmetros. Foram utilizadas 78 unidades experimentais (12,4 mm x 7,6 mm x 1,6 mm) a partir de blocos de Y-TZP (zircônia tetragonal estabilizada com ítrio) pré-sinterizados. A fim de obter superfícies padronizadas, os espécimes foram lixados com uma sequência decrescente de lixas (600, 1200, 1500). Em seguida, os blocos foram sinterizados em um forno específico, de acordo com as recomendações do fabricante. Os grupos experimentais foram compostos a partir de um fator de variação - tratamento de superfície. Foram formados 6 grupos experimentais (n=13) Controle, sem tratamento de superfície, grupo Rocatec, com tratamento triboquímico (Rocatec System Plus 3M ESPE), e 4 grupos laser (Waterlase Iplus Biolase Inc. Irvine, CA, EUA comprimento de onda 2780nm, 700?s, de 50% de ar e 50% de água, ponta MZ6 600?m): L3W 20Hz (53,57J/cm2), grupo L3W 50Hz (21,43J/cm2), grupo L6W 20Hz (107,14J/cm2), grupo L6W 50Hz (42,68J/cm2). Um espécime de cada grupo foi analisado através de microscopia eletrônica de varredura MEV (10000x). Após dos tratamentos de superfície, em cada bloco de zircônia foram colados 6 cilindros de resina usando cimento dual contendo MDP (Panavia F 2.0). Todas as amostras foram armazenadas em água destilada a 37ºC. O teste de microcisalhamento foi feito na máquina de ensaio universal (Instron 5565 EUA). Três dos 6 tubos colados em cada bloco foram avaliados depois de 24 horas de armazenamento em água a 37ºC e os 3 restantes foram avaliados depois de 2000 ciclos térmicos (5ºC - 30ºC). O tipo de falha foi determinado através de estereomicroscópio. Os dados foram analisados pelos testes de análise de variância (ANOVA) e de Tukey com um nivel de significância de p<0,01. Resultados: O grupo controle positivo (ROCATEC) apresentou diferença significativa (p <0,001) com os demais grupos. Quando foi simulado o envelhecimento térmico (termociclagem), todos os grupos apresentaram diferença significativa (p <0,001) na resistência de união comparada com o protocolo sem termociclagem. O tratamento de superfície convencional ainda é preconizado como uma alternativa válida para melhorar a resistência de união na zircônia. O uso de laser de Er,Cr:YSGG com uma largura de pulso de 700?s dentro dos parâmetros estudados não promoveu mudanças na superfície de zircônia que favorecessem a adesão com cimento resinoso. A termociclagem influenciou negativamente em todos os grupos experimentais. / This study aimed to evaluate the bond strength between resin cement and the irradiated zirconia samples a the Er, Cr: YSGG laser in four parameters. It was used 78 experimental units (12.4mm x 7.6mm x 1.6mm) from pre-sintered Y-TZP (Ytriumstabilized Tetragonal Zirconia) blocks. In order to obtain standardized surfaces the specimens were sanded with a decreasing sanding sequence (600,1200,1500). Then, the blocks form sintered in a specific oven, according to the manufacturer\'s recommendations. The experimental groups were composed of a variation factor - the surface treatment. Thus, 6 experimental groups were formed (n=13). Control, without surface treatment, the Rocatec group, with triboquimic treatment (Rocatec System Plus 3M ESPE), and 4 laser groups (Waterlase Iplus Biolase Inc. Irvine, CA USA wavelength 2780nm, 700?s, 50% air and 50% water, MZ6 600?m tip): L3W 20Hz (53.57J / cm2), L3W 50Hz group (21.43J / cm2), L6W 20Hz group (107.14J / cm2), group L6W 50Hz (42.68J / cm2). One specimen from each group was analyzed by Scanning Electron Microscopy (10000x). After the surface treatments, 6 resin cylinders were bonded to each zirconia block using dual cement containing MDP (Panavia F 2.0). All samples were stored in distilled water at 37 ° C. The micro-shear test was performed on the universal test machine (Instron 5565 USA). 3 of the 6 tubes pasted in each block were evaluated after 24 hours of storage in 37 ° C water and the remaining 3 were evaluated after 2000 thermal cycles (5 ° C - 30 ° C). The type of failure was determined by stereomicroscope. The data were analyzed by a test for analysis of variance (ANOVA) and tukey with a significance level of p <0.01. Results: The positive control group (ROCATEC), evaluated immediately after cementation, showed a better bond strength and there was no significant difference when thermal aging was simulated (thermocycling), nor did it differ significantly from the groups without thermocycling of 3w20Hz or 6w50hz. Conventional surface treatment is still advocated as a valid alternative to improve bond strength in zirconia. The use of Er, Cr: YSGG laser with a pulse width of 700?s within the studied parameters did not promote changes in the zirconia surface that favored adhesion with resin cement. Thermocycling influenced negatively all experimental groups.

No description available.