11 |
Estudio in vitro de la variación de la conductancia hidráulica en discos de dentina tratados con dos dentífricos con agentes desensibilizantesGonzález Cabezas, Héctor Javier January 2012 (has links)
Trabajo de Investigación
Requisito para optar al Título de
Cirujano Dentista / El objetivo del estudio fue determinar “in vitro” los efectos de agentes desensibilizantes de dentífricos sobre la conductancia hidráulica de la dentina.
Se seleccionaron 60 terceros molares humanos sanos, recientemente extraídos, sin contacto oclusal, de pacientes entre 15-30 años, los cuales fueron limpiados (Cureta Gracey 13-14, HuFriedy, USA), desinfectados (Timol 0,1% por 24 horas) y conservados a Tº ambiente en solución HBSS (Hanks Balanced Salt Solution, SIGMA, UK) durante un máximo de 14 días. Los especímenes fueron incluidos en resina epóxica (Bosh, Corea). Las coronas fueron seccionadas perpendicular al eje dentario mayor (ISOMET 1000BUEHLER LER LAKEBUFF IL, USA, 750 r/min. Presión 250 gr, USA) bajo abundante refrigeración, obteniendo un disco de 1mm +/- 0,1 mm. de espesor por cada corona. Se regularizaron las caras oclusales (papel abrasivo nº 600 Silicon carbide, SIA, Switzerland). Se trataron ambas superficies del disco con ácido ortofosfórico al 35% (Enchant gels 2,5 ml., Coltene Whaledent) por 15 segundos. Los discos se separaron en los siguientes tres grupos de tratamiento, de 20 discos cada uno, los que fueron cepillados (Cepillo Eléctrico Oral-B Pro Salud Power) durante 2 minutos solo por su cara oclusal con; A: Colgate® Sensitive Pro Alivio con tecnología Pro Arginina (Colgate-Palmolive, USA), B: Sensodyne® Rápido Alivio (GlaxoSmitheKline, UK), y C: Agua destilada como control negativo.
Previamente la cámara de difusión fue sometida a dos controles; Control Positivo: Medición sin disco de dentina y Control Negativo: Disco de Resina Epóxica. Los datos fueron analizados estadísticamente por medio de las pruebas de Kruskall Wallis y Mann Whitney.
Los resultados expresados en µl/min/cm2 como medias, separados por grupo fueron; A: 0,00650 (±0,00384), B: 0,00800(±0,00472) y C: 0,03649(±0,03042).
Se pudo concluir con el estudio que los dos agentes desensibilizantes dentinarios presentan significativa disminución de la conductancia hidráulica en dentina. Se encontraron diferencias estadísticamente significativas entre el grupo control y Sensodyne® Rápido Alivio (significancia = 0,000) y entre grupo control y Colgate® Sensitive Pro Alivio (significancia = 0,000). No se observó diferencia entre las dos pastas dentales (significancia = 0,317).
|
12 |
Correlación del aumento de la sensibilidad dentinaria asociada a blanqueamiento y el espesor dentario medido por tomografía ConebeamSepúlveda Galarce, Dania Alejandra January 2013 (has links)
Trabajo de Investigación Requisito para optar al Título de Cirujano Dentista / Introducción: No existe evidencia concluyente sobre la influencia del grosor dentario
en la génesis e intensidad de la sensibilidad dentinaria asociada a blanqueamiento
dental, por lo que el objetivo de este trabajo fue determinar la relación entre el
espesor dentario y la sensibilidad dentinaria luego del blanqueamiento.
Materiales y Método: La muestra fue de 48 pacientes adultos sanos de ambos
sexos, con dientes anteriores sanos y que contaban con una Tomografía Conebeam.
Se confeccionó una ficha y se les pidió su consentimiento informado por escrito.
Previo al blanqueamiento se cuantificó la sensibilidad dentinaria mediante escala
visual análoga (EVA). Los pacientes fueron sometidos a una sesión de
blanqueamiento por 45 minutos (H
2
O
2
35%, White Gold Dentsply ®). Para la
cuantificación del espesor dentario se realizaron, sobre cada Tomografía, tres cortes
en cada pieza dentaria del sector anterior, determinándose un promedio de espesor
dentario por paciente. Posterior al blanqueamiento se registró nuevamente la
sensibilidad dentinaria. Para determinar las diferencias entre la sensibilidad previa y
posterior al blanqueamiento se utilizó la prueba de rangos con signo de Wilcoxon y
se correlacionó el promedio de espesor dentario con el incremento de sensibilidad
dentinaria por medio de la prueba estadística Rho de Spearman (SPSS 14.v1).
Resultados: La muestra estuvo constituida por 31 mujeres y 17 hombres (edad
promedio 23,4 años). El promedio EVA inicial fue de 1,11 (+1,32) y el promedio EVA
posterior fue de 3,00 (+ 2,8). El promedio de incremento de sensibilidad dentinaria
fue de 1,99 (+ 2,46). El promedio de espesor dentario fue de 2,68mm (+ 0.12). El
valor de la prueba de Wilcoxon fue de 4,45 (p=0.00) y el valor de la correlación de
Spearman Rho fue de 0,058 (p=0.698).
Conclusiones: El blanqueamiento dental a base de peróxido de hidrógeno al 35%
produce un aumento de la sensibilidad dentinaria. El espesor dentario tomográfico de
las piezas anterosuperiores en este estudio es uniforme. No existe correlación entre
la sensibilidad dentinaria luego de blanqueamiento dental a base de peróxido de
hidrógeno al 35% y el espesor dentario tomográfico.
|
13 |
Comparación de la hiepersensibilidad dentinaria generada por tres sistemas de blanqueamiento dental para uso en la clínica: Estudio in vivoElphick Andino, Klaus January 2011 (has links)
Trabajo de Investigación Requisito para optar al Título de Cirujano Dentista / Autor no autoriza el acceso a texto completo de su documento / Introducción: La hipersensibilidad dentinaria es el efecto adverso más
frecuente en los procedimientos de blanqueamiento dental. Este fenómeno
depende directamente de la concentración del agente blanqueador y del tiempo de
aplicación, por lo tanto, en productos de uso en clínica altamente concentrados
este es un problema común y una molestia que el paciente deberá asumir. Es por
esto que el presente estudio pretende comparar la hipersensibilidad dentinaria
generada por tres sistemas blanqueadores para uso en clínica, entre ellos un
producto que incluye dióxido de titanio (TiO
) como fotocatalizador del proceso
blanqueador, que es presentado por el fabricante como un agente más seguro,
menos agresivo y, al ser menos concentrado, más cómodo para el paciente en
términos de la hipersensibilidad post-tratamiento generada.
2
Materiales y método: En el presente estudio se consideraron 88 voluntarios
de entre 18 y 37 años de edad, de ambos sexos, distribuidos al azar en tres
grupos de tratamiento. Se comparó la hipersensibilidad dentinaria generada por
tres sistemas blanqueadores basados en peróxido de hidrógeno (H
al
15% con TiO
2
activado por luz (Lase Peroxide Lite, DMC). 2. H
2
O
al 35% (Lase
Peroxide Sensy, DMC). 3. H
2
O
al 35% sin activación por luz (WhiteGold Office,
Dentsply). Los registros de sensibilidad se realizaron con Escala Visual Análoga
(EVA) previo al blanqueamiento, inmediatamente después, y a los 7 y 30 días
post-tratamiento en cada grupo. Los resultados obtenidos se analizaron
estadísticamente mediante test de ANOVA de un factor y test post-hoc de Tukey.
2
2
O
2
Resultados: Los registros EVA previos al tratamiento blanqueador de los
tres grupos de estudio no fueron estadísticamente diferentes entre sí (p=0,593).
Valores menores de hipersensibilidad dentinaria se obtuvieron en el grupo N°1, sin
embargo, al comparar entre grupos la variación de hipersensibilidad posttratamiento
con respecto al registro inicial no se obtuvieron diferencias
estadísticamente significativas en ningún momento de evaluación (p=0,174,
evaluación inmediata; p=0,438, evaluación 7 días; p=0,913, evaluación 30 días).
Conclusiones: Todos los sistemas blanqueadores evaluados generan
hipersensibilidad dentinaria luego del tratamiento. El blanqueador basado en H
al 15% con TiO
activado por luz genera una menor hipersensibilidad posttratamiento
en comparación a los otros sistemas estudiados, pero ésta no es
estadísticamente significativa.
|
14 |
Estudo sobre o potencial imunogênico da dentina: contribuição para a etiopatogenia da reabsorção dentária / Study on the immunogenical dentin potencial: contribution for the etiopathogenesis of dental resorptionHidalgo, Mirian Marubayashi 20 November 2001 (has links)
As reabsorções dentárias são inflamatórias e/ou substitutivas e representam o fenômeno principal que impede o sucesso dos transplantes e reimplantes dentários. Sua ocorrência pode ser conseqüência de traumatismos, periapicopatias e movimentação dentária induzida. Na odontogênese, a dentina fica sempre escondida" do sistema imunológico e posteriormente protegida pelo esmalte, cemento e cementoblastos no lado externo e pela camada de odontoblastos internamente. Duas proteínas não colagênicas são específicas da dentina: a fosfoforina e a sialoproteína dentinária. Construiu-se a seguinte hipótese: a dentina, como antígeno seqüestrado, pode induzir fenômenos auto- imunes e participar da etiopatogenia das reabsorções dentárias. A partir de dentes humanos, obteve-se um extrato dentinário inoculado em coelhos para análise dos soros imunes. O extrato dentinário humano apresentou capacidade de indução à resposta imunológica e reagiu com anticorpos de coelho. Foram selecionados 12 pacientes com reabsorção radicular inflamatória apical ativa, 12 indivíduos saudáveis sem quaisquer evidências de reabsorção radicular e quatro pacientes com reabsorção radicular por substituição. Através da metodologia Western blotting, verificou-se que a maioria das frações do extrato dentinário humano foi reconhecida de forma semelhante por pacientes com reabsorção dentária e controles, mas seis delas foram reconhecidas de forma estatisticamente diferente, não sendo reconhecidas como próprias pelo sistema imunológico. O extrato dentinário humano foi fracionado e os subprodutos coletados por intervalo de tempo com a utilização de HPLC. Resultados de ELISA demonstraram que os soros de pacientes com reabsorção dentária apresentaram quantidades maiores de IgG antiextrato dentinário humano e antifrações que indivíduos controles, sendo possível traçar um perfil sorológico próprio e possivelmente identificador do processo. IgM sérica antiextrato dentinário humano e antifrações dos pacientes com reabsorção inflamatória estavam em quantidades maiores ou iguais aos demais grupos estudados. Os perfis séricos de IgG e IgM permitem identificar especificidades dentro do próprio grupo de reabsorções dentárias, dividindo-as em inflamatória e por substituição. Há heterogeneidade na imunogenicidade das frações do extrato dentinário. As culturas de células provenientes de pacientes com reabsorção dentária mostraram índices de proliferação menores que os controles quando estimulados com o extrato dentinário ou suas frações, mas normais quando estimulados com mitógenos. O extrato dentinário humano e suas frações apresentaram capacidade de induzir à liberação de todas as citocinas relacionadas com a reabsorção dentária em maior ou igual concentração nas células de pacientes com reabsorção inflamatória se comparados com os controles sem reabsorção. Isto não foi observado nas células de pacientes com reabsorção por substituição, permitindo identificar os grupos com reabsorção dentária. Os resultados obtidos confirmam a hipótese que a dentina apresenta imunogenicidade e que o perfil sorológico dos pacientes com reabsorção dentária pode ser identificado por análise bioquímica sangüínea. O seu delineamento preciso pode levar ao diagnóstico precoce da reabsorção dentária antes que se manifeste radiograficamente. / The dental resorptions are inflammatory and/or substitutive and represent the principal phenomenon that prevents the success of transplants and dental reimplants from happening. Its occurrence can be a consequence of traumatism, periapical disease and induced dental movements. During the odontogenesis the dentin is always "hidden" from immune system and later protected by the enamel, cement and cementoblasts on the external side and, by the odontoblasts layer on the internal side. Two non-colagenical proteins phosphophorin and dentinal sialoprotein are specific of dentin. It was constructed the following hypothesis: the dentin, as a "hidden" antigen, can induce auto- immune phenomena and participate in the etiopathogenesis of the dental resorptions. Starting from extracted human teeth, we obtained a human dentinal extract inoculated into rabbits to obtain the immune sera. The huma n dentinal extract was able to react with the antibodies and to induce immune response in the rabbit. It was selected 12 patients with radicular inflammatory active apical resorption, 12 healthy individuals without signs of radicular resorptions evidences, and 4 patients with substitutive radicular resorption. Western blotting analysis showed that most of the fractions of the human dentinal extract were recognized by patients with resorption and controls in a similar way. Nevertheless, six of the fractions studied were not recognized as autologous by the immunological system of the patients. With the use of HPLC the human dentinal extract was fractioned and the subproducts collected by time interval. Results of ELISA demonstrated that the sera of patients with dental resorption presented larger amounts of IgG anti- total human dentinal extract and anti- fractions than control individuals, allowing a characterization of the sorological profile of the process. IgM anti-total human dentinal extract and anti- fractions in serum of patients with inflammatory resorption are in larger or equal amounts as the other studied groups. The seric profile of IgG and IgM allows to identify specificities inside of its own group of dental resorptions, dividing them into inflammatory and by substitution. There is an heterogenecity in the imunogenicity of the fractions of the dentinal extract. The cell cultures of patients with resorption had a smaller proliferation index than the controls when stimulated with total dentin extract or their fractions, but normal when stimulated with mitogens. The total human dentinal extract and its fractions presented capacity to induce a larger or equal concentration release of all the cytocins related to resorption in comparison to the controls without it. This was not observed with patients with dental substitution resorption, allowing the characterization of the groups with inflammatory and substitutive dental resorption. The obtained results reinforces an hypothesis that the dentin presents immunogenicity and the sorological profile of patients with dental resorption can be identified by blood biochemical analysis. Its precise screening can lead us to early diagnosis of dental resorption before it appears clinically and radiographically.
|
15 |
Avaliação da técnica de réplica para análise in vitro e in vivo das alterações da superfície da dentina hiperestésica e tratada com oxalato de potássio. / Evaluation of a Replica Technique for In Vitro and In Vivo Analyses of the Alterations on the Hypersensitive Dentin Surface Treated with Potassium OxalateMartineli, Ana Christina Bonato Figueiredo 15 August 2002 (has links)
O presente trabalho teve como objetivo avaliar in vitro e in vivo, através de uma técnica de réplica associada à microscopia eletrônica de varredura (MEV), as características e modificações da superfície da dentina hiperestésica e tratada com um agente dessensibilizante à base de oxalato de potássio. O estudo in vitro foi realizado utilizando-se discos de dentina, cuja superfície foi condicionada com ácido cítrico a 6%, coberta com smear layer artificial e dividida em 4 quadrantes. A smear layer foi mantida no quadrante 1, considerado o controle para a dentina não exposta. Os quadrantes 2, 3 e 4 de cada disco foram recondicionados com ácido cítrico a 6%, e o oxalato de potássio foi aplicado nos quadrantes 3 e 4. O quadrante 4 foi, então, novamente condicionado com ácido cítrico a 6%. Feita a moldagem com Aquasil ULV, removeu-se o disco do molde após 6 minutos. Decorridas 24 horas, uma resina epóxica de baixa viscosidade foi vazada sobre o molde, e deixada polimerizar por outras 24 horas. Os discos de dentina, moldes e réplicas de resina epóxica foram metalizados para análise no MEV. No estudo in vivo, os pacientes, cujos dentes caninos e pré-molares apresentavam lesões cervicais não cariosas e sensíveis aos estímulos sonda e/ou jato de ar conforme a Escala Visual Analógica (EVA), foram selecionados e divididos em 2 grupos. No baseline, após o registro da sensibilidade em ambos os grupos, a superfície de dentina foi limpa com hipoclorito de sódio a 1%, e 3 moldagens consecutivas foram realizadas, sendo a primeira para remoção de debris, e as outras, para obtenção das réplicas positivas e negativas. Os moldes foram armazenados por um período de 24 horas em local fechado, seco e limpo, e a resina epóxica foi, então, vazada. O Grupo 1 (16 dentes) recebeu 4 aplicações de Oxa-Gel® em intervalos de 7 dias. No Grupo 2 (7 dentes), nenhum agente antihiperestésico foi aplicado. Após 4 semanas, reavaliou-se o grau de sensibilidade, seguindo-se os mesmos procedimentos de moldagem e obtenção das réplicas, exceto a primeira moldagem. Todos os espécimes foram metalizados para análise no MEV. No estudo in vitro, a comparação das fotomicrografias dos discos de dentina e seus respectivos moldes e réplicas mostrou que essa técnica pode reproduzir as características da superfície dentinária tratada com oxalato de potássio. No estudo in vivo, as réplicas positivas não forneceram detalhes como no estudo in vitro. Por outro lado, as réplicas negativas favoreceram a análise das características da superfície da dentina hiperestésica, do efeito do oxalato de potássio, e das modificações que ocorreram na superfície dentinária no Grupo 2. A análise das fotomicrografias possibilitou o estabelecimento de uma correlação entre a presença de túbulos dentinários e o grau de sensibilidade relatado pelos pacientes nas diferentes situações. Os resultados demonstraram que a técnica de réplica negativa pode ser um recurso complementar confiável para a avaliação clínica da hiperestesia dentinária. / The present study was carried out to evaluate, in vitro and in vivo, the characteristics and alterations occurring on the surface of hypersensitive dentin treated with a potassium oxalate-based desensitizing agent using a replica technique associated with the scanning electron microscopy (SEM). The in vitro experiment was performed using dentin discs, their surface having been conditioned with 6% citric acid, covered with artificial smear layer and divided into 4 quadrants. The smear layer was maintained in quadrant 1, which was the control for the non-exposed dentin. Quadrants 2, 3 and 4 of each disc were reconditioned with 6% citric acid, and potassium oxalate was applied to quadrants 3 and 4. Once again, quadrant 4 was then conditioned with 6% citric acid. The impression using Aquasil ULV was made, and, 6 minutes later, the disc was removed. After 24 hours, a low-viscosity epoxy resin was poured into the model, and left to polymerize for another period of 24 hours. The dentin discs, models and epoxy resin replicas were metallized for analysis in the SEM. In the in vivo study, the patients whose canines and pre-molars had caries-free cervical lesions, and were sensitive to probe and/or air jet stimuli according to the Analogical Visual Scale (AVS) were selected and divided into 2 groups. At the baseline, after recording the degree of sensitivity in both groups, the surface was cleaned with 1% sodium hypochlorite, and 3 consecutive impressions were made: the first one to remove the debris, and the other two to obtain positive and negative replicas. The models were stored in a closed, dry and clean environment for 24 hours; then, the epoxy resin was poured into such models. Group 1 (16 teeth) received 4 applications of Oxa-Gel® at 7-day intervals, while in Group 2 (7 teeth) no desensitizing agent was used. After 4 weeks, the degree of sensitivity was assessed following the same procedures used to obtain the impressions and replicas, except the first impression. All the specimens were metallized for analysis in the SEM. As for the in vitro experiment, the comparison between the photomicrographs of the dentin discs and their respective models and replicas showed that this technique can reproduce the characteristics of the dentin surface treated with potassium oxalate. In the in vivo study, the positive replicas did not provide the details as noted in the in vitro investigation. On the other hand, the negative replicas favored an analysis of the hypersensitive dentin surface characteristics, the effect of potassium oxalate on that surface, and the alterations that occurred on the hypersensitive dentin surface of Group 2. The analysis of the photomicrographs made it possible to draw a correlation between the presence of dentinal tubules and the degree of sensitivity reported by the patient in different situations. The results showed that the negative replica technique can be a reliable complementary tool for the clinical evaluation of dentin hypersensitivity.
|
16 |
Influência do ultra-som na resistência adesiva à dentina de cimentos de ionômero de vidro / Tensile Bond Strength of Glass Ionomer Cements After SonicationFagundes, Ticiane Cestari 23 May 2005 (has links)
O objetivo deste trabalho foi avaliar in vitro a influência da irradiação ultra-sônica na resistência adesiva a dentina de cimentos de ionômero de vidro restauradores: convencional (Fuji II, Ketac Fil Plus), modificado por resina (Fuji II LC Improved, Photac Fil Quick Aplicap) e de alta viscosidade (Ketac Molar). Cinqüenta dentes terceiros molares humanos extraídos foram seccionados no sentido mésio-distal de forma a se obter 100 secções. As secções foram incluídas em resina epóxica, com as superfícies vestibular ou lingual expostas, e desgastadas até a obtenção de uma superfície plana em dentina. Sobre as secções foi adaptada uma matriz confeccionada com molar bovino (com orifício central em formato de tronco de cone invertido) onde o ionômero foi inserido. Nos grupos em que o ultrasom foi utilizado, este foi aplicado por 15s sobre a matriz e o material. Após 20 minutos da aplicação do ultra-som, a matriz foi removida e os corpos-de-prova (dentina/tronco de cone de ionômero) foram armazenados em água deionizada por 24 horas a 37° . Em seguida, os corpos-de-prova foram adaptados por meio de dispositivos à máquina de ensaios para a realização dos testes. Os dados foram submetidos a ANOVA a dois critérios e ao teste de Tukey (p<0,05). As médias e desvios-padrão dos resultados (MPa) sem aplicação do ultra-som foram: 2,21 ± 0,53.(Fuji II); 1,85 ± 0,5 (Ketac Fil Plus); 8,65 ± 2,46 (Fuji II LC Improved); 5,93 ± 1,77 (Photac Fil Quick Aplicap) e 2,10 ± 0,57 (Ketac Molar). Com a utilização de excitação ultra-sônica os valores aumentaram para 3,33 ± 0,96 (Fuji II); 2,19 ± 0,64 (Ketac Fil Plus); 9,95 ± 2,79 (Fuji II LC Improved); 6,10 ± 1,41 (Photac Fil Quick Aplicap) e 2,65 ± 0,75 (Ketac Molar). Os resultados com excitação ultra-sônica foram estatisticamente diferentes e superiores aos observados pelos ionômeros sem o emprego do ultra-som. Não houve diferença estatisticamente significante entre os cimentos convencionais e os de alta viscosidade. Entretanto, houve diferença estatisticamente significante entre os modificados por resina e os outros cimentos estudados. O Fuji II LC Improved apresentou resistências maiores que o Photac Fil Quick Aplicap. A excitação ultra-sônica aumentou a resistência adesiva à dentina nos cimentos de ionômero de vidro estudados. / The aim of this study was to evaluate the influence of ultrasonic irradiation on the bond strength to dentin of glass-ionomer cements: conventional (Fuji II-a, Ketac-Fil Plus-b), resin-modified (Fuji II LC Improved-c, Photac-Fil Quick Aplicap-d) and high-viscosity (Ketac Molar-e). Fifty human molars were sectioned, embedded in epoxy resin with buccal or lingual surfaces exposed and grounded to obtain flattened dentin. An inverted truncated cone central orifice matrix was built with bovine tooth and positioned against the dentin. In the control groups materials were just inserted in the matrix. The sonication excitation was applied for 15 seconds on the matrix and on the material (test groups). Specimens were stored in deionized water for 24 hours at 37°C and then submitted to bond strength tests. Data were analyzed by two-way ANOVA and Tukey tests. The mean (SD) bond strengths in MPa for the control groups were: a: 2.21 (0.53); b: 1.85 (0.5); c: 8.65 (2.46); d: 5.93 (1.77) and e: 2.10 (0.57). The results for the test groups were: a: 3.33 (0.96); b: 2.19 (0.64); c: 9.95 (2.79); d: 6.10 (1.41) and e: 2.65 (0.75). Ultrasonic irradiation increased the tensile bond strength of all tested cements. There were no differences statistically significant between conventional and high-viscosity cements. There were differences statistically significant among resin-modified and the other cements. Fuji II LC was statistically better than Photac-Fil. Ultrasonic excitation improved the bond strength of glass ionomer cement to dentin after 24 hours.
|
17 |
Ação de bebidas com teor ácido sobre a permeabilidade dentinária: estudo in vitroMattos, Maria Cecília Ribeiro de 20 June 2005 (has links)
A hiperestesia dentinária não é uma condição de dor incomum na odontologia. Porém, mesmo diante dos inúmeros trabalhos efetuados, sua compreensão ainda não é total. A teoria da Hidrodinâmica, que melhor explica a ocorrência dessa situação clínica, baseia-se no movimento do fluido dentinário através dos túbulos como provável desencadeador da dor, O estudo do consumo de bebidas de alto teor ácido e seus efeitos sobre as estruturas dentárias é também bastante explorado pelas pesquisas em geral . O presente trabalho analisou, in vitro, as alterações da permeabilidade dentinária frente à exposição à Coca Cola regular, Coca Cola light, sucos de laranja natural e artificial e Cerveja. Realizou-se o teste da condutividade hidráulica em 50 discos de dentina, divididos em 5 grupos correspondentes às bebidas analisadas, avaliados após 3 e 5 minutos do contato com cada bebida. Os resultados foram analisados estatisticamente através do teste de variação e teste de Duncan. Os resultados mostraram que: as bebidas de teor ácido estudadas exerceram efeito sobre a condutividade hidráulica de dentina; não houve diferença estatisticamente significante entre os valores condutividade hidráulica obtidos após 3 e 5 minutos; para os dois tempos estudados, os sucos de laranja exerceram efeito significantemente maior na condutividade hidráulica da dentina do que as bebidas do tipo \"Cola\" . Os efeitos destas e da Cerveja foram estatisticamente semelhantes. / Dentine hipersensibility isn\' t an unusual pain condition in dentistry. However, although many researches have been made about the subject, its comprehension is still not clear. Hidrodynamic theory, which better explains the clinical situation, is based on dentinal fluid movement through dentinal tubules as a cause of pain. The study of the acidic drinks and its effects over tooth structures is much explored in the recent researches. The present study analyzed, in vitro, the dentine permeability changes to the exposition to regular Coca Cola, Coca Cola light, natural and artificial oranges juices and beer. Hydraulic conductivity test has been made in 50 dentine discs, divided into 5 groups, during 3 and 5 minutes of contact with each drink. The results were statistically analyzed with the Duncan test. The findings demonstrate that acidic drinks have an effect over the dentine hydraulic conductivity. More over, there isn\' t significance differences between hydraulic conductivity values after 3 and 5 minutes. In both intervals of time, orange juices provided an extremely effect over dentine hydraulic conductibility when compared with like cola drinks. Beer effects and like cola drinks were statistically similar.
|
18 |
Influência dos espessantes na rugosidade da superfície da dentina e resistência ao cisalhamento de três sistemas adesivosCastilio, Daniela 06 April 2005 (has links)
Este estudo teve como objetivo determinar a influência dos espessantes na rugosidade da superfície da dentina e resistência ao cisalhamento de três sistemas adesivos. Foram utilizadas 144 coroas de incisivos bovinos. A rugosidade da superfície da dentina foi avaliada antes e após o condicionamento com três diferentes formulações de ácido fosfórico 37%. Os ácidos experimentais foram espessados com sílica silanizada e polímero, sendo o comercial espessado com sílica coloidal. Três sistemas adesivos foram utilizados em combinação com as três diferentes formulações de ácido fosfórico 37%. O sistema adesivo comercial foi o Prime & Bond 2.1, à base de acetona; os experimentais foram formulados à base de água, sendo adicionado, o tetrahidrofurano, no Gluma B. Metade das restaurações foram realizadas com a resina composta Filtek Z 250TM e a outra metade com a resina composta Beautifil. Os espécimes foram armazenados por 24h em água deionizada à 37°C e então submetidos ao teste de resistência ao cisalhamento na máquina de ensaio Kratos, a uma velocidade de deslocamento de 0,5mm/min. Alguns espécimes foram preparados para análise em MEV da penetração de resina no interior dos túbulos dentinários. Os dados foram analisados através dos testes de ANOVA, a um critério de classificação e Tukey. O ácido espessado com sílica aumentou significantemente a rugosidade superficial da dentina (P<0,05). Os espessantes não influenciaram na resistência ao cisalhamento dos dois materiais restauradores. Para a resina composta Filtek Z 250TM houve diferença entre os sistemas adesivos somente nos grupos condicionados com ácido espessado com polímero. A resistência ao cisalhamento do sistema Gluma B, empregado com a resina Beautifil, apresentou maiores valores quando comparado ao Gluma A, e sem diferença quando comparado ao sistema comercial (C). Houve a formação da camada híbrida e tags de resina em todos os grupos estudados.
|
19 |
Efeito do trimetafosfato de sódio na prevenção de erosão intríseca em dentina : estudo in vitroPereira, Carla Kuroki Kawamoto 03 August 2018 (has links)
Made available in DSpace on 2019-03-30T00:26:41Z (GMT). No. of bitstreams: 0
Previous issue date: 2018-08-03 / Dental erosion is defined as an irreversible loss of dental structure
caused by acidic substances contained in food, beverages, medications and reflux of stomach fluids. The present study proposed to evaluate, in vitro, the effect of a toothpaste containing sodium trimetaphosphate associated with or not to fluoride in low concentration (500 ppm NaF) on the dentin surface subjected to erosion of intrinsic origin. Methodology: Human dentin blocks were selected by surface hardness and randomized in five groups (n = 12): SFST Group (toothpaste 0 ppmF); Group F 500 (toothpaste 500 ppm NaF); Group F 1500 (toothpaste 1500 ppm NaF); TMP Group (toothpaste 1% tmp); and group F + TMP (toothpaste 500 ppm NaF + 1% TMP). All the blocks were subjected to erosive challenge by immersion in hydrochloric acid 0.01 M (pH 1.5) for 30 seconds. Subsequently, specimens were treated with dilution of toothpaste in distilled water (1:3 w/w). The following were immersed in artificial saliva for 2 hours, the complete cycle being repeated three times a day for 3 days. The measurement of dental wear and the percentage of dentin hardness loss were carried out after the last experimental day. The statistical analysis was carried out by the ANOVA test at a level of 5% significance. / A erosão dentária é definida como uma perda irreversível de
estrutura dentária causada por substâncias ácidas contidas em alimentos,
bebidas, medicações e em refluxo de fluidos estomacais. O presente estudo
propôs avaliar in vitro o efeito de um dentifrício contendo trimetafosfato de sódio
associado ou não ao flúor em baixa concentração (500 ppm NaF), na superfície
dentinária submetida a erosão de origem intrínseca. Metodologia: Blocos de
dentina humana foram selecionados pela dureza de superfície e randomizados
em cinco grupos (n=12): Grupo SFST (dentifrício 0 ppmF); Grupo F 500
(dentifrício 500 ppm NaF); Grupo F 1500 (dentifrício 1500 ppm NaF); Grupo TMP
(dentifrício 1% TMP); e Grupo F+TMP (dentifrício 500 ppm NaF + 1% TMP). Todos os blocos foram submetidos a desafio erosivo por imersão em ácido hidroclorídrico 0,01 M (pH 1,5) durante 30 segundos. Posteriormente, os espécimes foram tratados com diluição de dentifrício em água destilada (1:3 p/p). A seguir, foram imersos em saliva artificial por 2 horas, sendo o ciclo completo repetido três vezes ao dia, durante 3 dias. A mensuração do desgaste dentário e a porcentagem de perda de dureza da dentina foram realizadas após o último dia experimental. A análise estatística foi realizada pelo teste ANOVA.
|
20 |
Avaliação de LEDs de alta intensidade quanto à eficiência de polimerização de resina composta e variação de temperatura na dentina bovina /Mollica, Fernanda Brandão. January 2007 (has links)
Orientador: Maria Amélia Maximo de Araújo / Banca: Luzia da Glória Gomês Coelho / Banca: Maria Filomena Rocha Lima Huhatala / Resumo: Este estudo teve por objetivo avaliar a eficiência de polimerização de uma resina composta (RC) e a variação de temperatura na dentina bovina, empregando aparelhos de Diodo Emissor de Luz (LED) de alta intensidade em comparação a um aparelho de Quartzo-Halogênio-Tungstênio (QTH). Os aparelhos utilizados foram: Curing Light XL 3000 (3M, 600 mW/cm2), LED SmartLite PS (Dentsply, 950 mW/cm2) e LED Radii (SDI, 1400 mW/cm2) e a RC, a Esthet X (Dentsply). Para o teste de microdureza Vickers, foram confeccionados 84 corpos-de-prova (2 mm x 5 mm) em matriz de teflon bipartida, variando-se o tempo de exposição em 10, 20 e 40 s, sendo que o aparelho XL 3000 foi utilizado para o grupo controle apenas pelo tempo de 40 s. Após 24 h, realizou-se o teste de microdureza no topo e na base dos corpos-de-prova com carga de 50 g e duração de 15 s. Para a medida da variação de temperatura ocasionada pelos aparelhos, foram utilizadas 45 fatias de dentina bovina de 0,7 mm de espessura e termopar tipo T conectado a um sistema de aquisição de dados ADS 2000 IP (Lynx Tecnologia). As fatias foram divididas em três grupos, sendo a variação de temperatura medida em três etapas: 1) durante a fotopolimerização do adesivo (10 s); 2) durante a fotopolimerização da RC (40 s) e 3) após 24 h (40 s). Os valores de microdureza do topo e da base e os dados de temperatura foram submetidos ao teste ANOVA de medidas repetidas e aos testes de Tukey e Dunnet (p=5%). Os resultados revelaram diferença estatística significante de microdureza no topo e na base quando se utilizaram ambos os LEDs por 10 s em relação ao uso do XL 3000 por 40 s, não havendo diferenças estatísticas entre os grupos com os tempos de 20 s e 40 s. A utilização do LED Radii pelos tempos de 10 e 20 s não foi suficiente... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate the efficiency of polymerization of a resin composite and the temperature variation in bovine dentine, using two curing units of Light Emitting Diode (LED) of high intensity in comparison to a Quartz-Halogen-Tungsten device (QTH). The light curing units used were: Curing Light XL 3000 (3M, 600 mW/cm2), LED SmartLite PS (Dentsply, 950 mW/cm2) and LED Radii (SDI, 1400 mW/cm2) and the resin composite, Esthet X (Dentsply). For the test of Vickers microhardness, 84 specimens (2 mm X 5 mm) were prepared in bipartite matrix of teflon, varying the time of exposition in 10, 20 and 40 s. The curing unit XL 3000 was used for the control group for 40 s. After 24 h, the microhardness test was made on the top and base of the specimens with 50 g of load and 15 s of duration. For the temperature variation measurement caused by the different curing units, 45 slices of bovine dentine of 0.7 mm thickness and a thermocouple type T hardwired to a system of data acquisition ADS 2000 IP (Lynx Technology) were used. The slices were divided in three groups and the temperature variation was measured in three stages: 1) during the adhesive photopolymerization (10 s); 2) during resin composite photopolymerization (40 s) and 3) after 24 h (40 s). The values of microhardness of the top and the base and the data of temperature variation were submitted to ANOVA of repeated measures test and to the tests of Tukey and Dunnet (p=5%). The results showed statistical significant difference of microhardness for the top and base values when both LEDs were used for 10 s in relation to the use of XL 3000 for 40 s, but no statistical differences were found between the groups when the exposition time was 20 s and 40 s. The use of LED Radii for 10 s and 20 s was not enough to equal statistically ... (Complete abstract, click electronic access below) / Mestre
|