Orientador: Sizenando de Toledo Porto Neto / Banca: Marcelo Ferrarezi de Andrade / Banca: Maria Salete Machado Cândido / Banca: Alberto Magno Gonçalves / Banca: Edson Alves de Campos / Resumo: Este trabalho teve como objetivo avaliar in vitro a força de união da resina composta à dentina tratada com quatro adesivos dentinários, sendo dois sistemas universais simplificados (G1- Prime & Bond® NT/ Dentsply, G2- Single Bond/ 3M) e dois auto-condicionantes (G3- AdheSE® / Vivadent, G4- Adper- PromptL-Pop/ 3M). Para a realização deste estudo, foram selecionados 20 terceiros molares humanos íntegros e livres de cárie, que tiveram suas superfícies oclusais cortadas em 3mm. Após o corte, cada grupo de dentes receberam seus respectivos sistemas de tratamento adesivo, pré-selecionados. Todas as amostras de dentes foram restauradas com a resina composta Tetric Ceram® / IvoclarVivadent, termocicladas em 550 ciclos e cortadas. Dessa forma, obtendo-se espécimes de 1,0mm2 l0,1mm2 que foram levados a uma Máquina de Teste Universal onde foi realizado o ensaio de microtração. Os tipos de fraturas foram analisados, mediante microscopia óptica (40X) e as fraturas mais representativas foram levadas à microscopia eletrônica de varredura. Os resultados mostraram que os sistemas universais simplificados (G1 e G2) apresentaram valores de resistência de união mais elevados do que os sistemas auto-condicionantes (G3 e G4). A maioria das fraturas encontradas foram do tipo adesiva para os grupos G3 e G4, enquanto nos grupos G1 e G2 87% dos modos de fraturas foram distribuídas entre adesivas e coesivas da resina. / Abstract: This work had with aim to evaluate "in vitro" the bond strength of composite resin to dentine bonded with four dentin adhesives. In this study, were used two one-step adhesive systems (G1- Prime & Bond® NT/Dentsply, G2-Single Bond/ 3M)and two self-etching adhesive systems (G3- AdheSE® /Vivadent, G4- Adper Prompt L-Pop/3M). For this, were chosen twenty human healthy third molars, that had their oclusal surfaces cut in 3mm. After the cut, each group of teeth received their respectives adhesive systems, even then chosen. All the samples were restored with the composite Tetric Ceram® / IvoclarVivadent, thermocycled 550 times and cut. Then, obtaining specimens of 1,0mm2 l 0,1mm2 that were made a test of micro tensile bond strength in a Universal Test Machine. The fractures were analyzed in a optical microscope (40X), and the more representative fractures were then analyzed at scanning electronic microscope. The results revealed that the one-step adhesive systems (G1 and G2) showed higher values of bond strength compared to the self-etching adhesive systems (G3 and G4). The fractures more commum were the adhesive type in the G3 and G4 groups, while in the G1 and G2 groups, 87% of the fractures were the adhesive and cohesion of resin types. / Doutor

Orientador: José Roberto Rodrigues / Banca: Eduardo Shigueyuki Uemura / Banca: Carlos Henrique Ribeiro Camargo / Banca: George Miguel Spyrides / Banca: Gorgulho Zanet / Resumo: O objetivo do estudo foi avaliar quatro diferentes sistemas adesivos (Multi- Purpose, Single Bond, SE Plus e Easy Bond - 3M ESPE) no que se refere à resistência adesiva ao microcisalhamento na dentina bovina. Além de avaliar a citotoxicidade desses novos sistemas adesivos por meio do teste de barrerira dentinária e ensaio de MTT em fibroblastos pulpares bovinos. Para o teste de microcisalhamento 80 dentes bovinos tiveram suas raízes seccionadas, foram embutidos em resina acrílica e tiveram a superfície vestibular desgastada expondo-se a dentina, sendo que em 40 dentes a espessura de dentina remanescente foi de 500μm e nos outros 40 de 200μm. Os cdp receberam então o procedimento adesivo de acordo com as instruções do fabricante e com auxílio de uma matriz metálica, cilindros de resina (Z 250 - 3M ESPE) de 0,8 mm de diâmetro e 1mm de altura foram construídos. Após 24h os cdp foram então submetidos ao ensaio de microcisalhamento. Para avaliar a citotoxicidade foi usado o teste de barreira dentinária. Células pulpares bovinas transformadas foram cultivadas em redes de nylon por 2 semanas, obtendo-se uma cultura de 3 dimensões. Essas culturas celulares foram separadas dos materiais testados por fatias de dentina de 500 e 200μm em um dispositivo de perfusão celular. Os materiais foram aplicados na porção cavitária do dispositivo de acordo com as instruções do fabricante, e um material de moldagem a base de silicona (President, Coltene) foi usado como controle negativo (100% de viabilidade celular). Após 24 h de periodo de exposição, a viabilidade celular foi mensurada fotometricamente (teste MTT). Por meio de estatística descritiva verificou-se que a melhor eficiência adesiva foi apresentada pelo adesivo auto-condicionante de um passo só, Easy Bond (21,06 MPa - 200μm; 27,01 MPa- 500μm) seguido pelo Single Bond (15,64 MPa - 200μm; 23,45 MPa- 500μm), SE Plus... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate four different adhesive systems (Multi- Purpose, Single Bond, SE Bond Plus and Easy - 3M ESPE) with regard to microshear bond strength to bovine dentin. In addition evaluate the cytotoxicity of these new adhesive systems by means of a dentin barrier test. To test microshear 80 bovine teeth had their roots sectioned and were embedded in acrylic resin. The buccal surface had been worn to expose the dentin, in 40 teeth the remaining dentin thickness was 500μm and 200μm in the other 40. The specimes received the adhesive procedure according to the manufacturer's instructions and with the aid of a metal matrix, cylinders of resin (Z 250 - 3M ESPE) from 0.8 mm in diameter and 1mm in height were built. After 24h the specimes were then subjected to the microshear testing To evaluate the cytotoxicity, a dentin barrier test was used. SV3NeoB transfected bovine pulp derived cells were grown on nylon meshes for 2 weeks achieving a 3-dimensional cell culture as described. These cell cultures were separated from the test materials by dentin slices of 200 or 500μm thickness in a cell cultures perfusion chamber. The materials were applied into the cavity part of the device according to manufacturer's instruction, and a silicon impression material (President, Coltene) served as a negative control material (100% cell viability). After a 24h exposure period, cell viability was measured photometrically (MTT test). Median values (plus 25% and 75% percentiles) of cell viability measurements (n=10) were statistically analyzed (Mann-Whitney test, = 0.05). Descriptive statistics found that the best bonding performance was presented by the single step adhesive Easy Bond (21.06 - 200μm, 27.01 - 500μm) followed by Single Bond (15.64 - 200μm; 23.45 - 500μm), SE Plus (18.23 - 200μm; 20.07 - 500μm) and Multi Purpose (15.24 - 200μm; 17.99 - 500μm). Moreover, it was... (Complete abstract click electronic access below) / Doutor

Resumo: O objetivo deste trabalho foi avaliar a influência que o laser de Er:YAG exerce sobre a resistência de união do material restaurador ao substrato dentinário, associando-se a diferentes sistemas adesivos. Para isto foram avaliados 30 molares humanos livres de cárie divididos em três grupos experimentais, utilizando o laser de Er:YAG com uma energia de 260 mJ/10Hz e três grupos controles, em que foram aplicados os seguintes tratamentos: G1) laser, ácido fosfórico a 37%, Excite/Vivadent; G2) controle, ácido fosfórico a 37%, Excite/Vivadent; G3) laser, sistema adesivo Prompt L-pop/Espe; G4) controle, Prompt L-pop;/Espe; G5) laser, ácido fosfórico a 37%, Single Bond/3M; G6) controle, ácido fosfórico a 37%, Single Bond/3M. Todas as amostras foram restauradas com a resina composta Tetric Ceram/Vivadent, termocicladas em 550 ciclos e cortadas, obtendo-se espécimes de mais ou menos 1mm,2 para serem levados a uma Máquina de Testes Universal onde foi realizado o ensaio de microtração. Os tipos de fraturas ocorridos foram analisados mediante microscopia óptica digital e as fraturas mais representativas foram levadas à microscopia eletrônica de varredura. Os resultados mostraram que o sistema laser de Er:YAG apresentou as menores médias de tensão de ruptura, independente do sistema adesivo utilizado. O sistema adesivo Prompt l-pop mostrou resistência adesiva estatisticamente menor em relação aos outros sistemas adesivos estudados. Não houve diferença estatística entre os sistemas adesivos Single Bond e Excite. A maior parte das fraturas encontradas para todos os grupos foram do tipo adesiva. / Abstract: The aim of this study is to evaluate the influence of the laser Er:YAG to the junction resístance between the tooth surface and the restorative material , using different adhesives . For this study were used 30 human healthy molars, divided in three experimental groups and three control groups. The experimental groups were exposed to a laser of Er:YAG with 260 mJ/10Hz of energy. The six groups were: G1) laser, phosforic acid at 37%, Excite/ Vivadent. G2) control, phosforic acid at 37 % , Excite/ Vivadent. G3) laser, adhesive system Prompt L-pop/ Espe. G4) control, adhesive system Prompt L-pop/ Espe. G5) laser, phosforic acid 37% , Single Bond/ 3M. G6) control, Single Bond/ 3M. All the teeth were restored with the composite Tetric Ceram/ Vivadent. Then thermocycled 550 times and cut in specimens of 1mm2. In these specimens was made a test of micro tensile bond strength in a Universal Test Machine. The fractures were analyzed in a digital optical microscope, and more representative fractures were then analyzed in a electronic microscope. The results revealed that the groups treated with laser Er:YAG presented less tensile bond strengh, independently to the adhesive system used. The adhesive Promp 1-pop presented less tensile bond strengh compared to the other adhesives evaluated. There no was difference between the groups of Single Bond and Excite. The fractures more commun were the adhesive type. / Orientador: Sizenando de Toledo Porto Neto / Coorientador: Vanderlei Salvador Bagnato / Banca: Osmir Batista de Oliveira Júnior / Banca: Alberto Magno Gonçalves / Mestre

Orientador: Josimeri Hebling / Banca: Marcela Rocha de Oliveira Carrilho / Banca: Edson Alves de Campos / Resumo: O objetivo geral desse trabalho, dividido em dois experimentos (capítulos 1 e 2), foi avaliar a citotoxicidade de sistemas adesivos experimentais (SAEs), com diferentes graus de hidrofilia, e do etanol como solução de solvatação da dentina, sobre células odontoblastóides. No capítulo 1, discos de papel filtro esterilizados foram impregnados com 10 μL de cada SAE (n=22): R1, R2, R3, R4 e R5 (em ordem crescente de hidrofilia), seguido de fotoativação. Os discos foram individualmente imersos em meio de cultura DMEM para obtenção de extratos (DMEM + componentes liberados dos SAEs), os quais foram posteriormente aplicados sobre células MDPC-­‐23 em cultura. Discos não impregnados (R0) serviram como controle. Foram avaliados o metabolismo celular (teste de MTT), a expressão de proteína total (PT) e a atividade de fosfatase alcalina (FA), além do tipo de morte celular (citometria de fluxo) e grau de conversão monomérica (FTIR) dos SAEs. Os dados de cada variável resposta do estudo foram analisados por testes de Kruskal-­‐Wallis e Mann-­‐Whitney (α=0,05). Considerando R0 como 100%, foi observada redução do metabolismo celular de 36,4%, 3,1%, 0,2%, 21,5% e 65,7%, respectivamente para R1, R2, R3, R4 e R5. Apenas R1 e R5 diferiram estatisticamente do controle. Para PT, R1, R4 e R5 tiveram expressão estatisticamente inferior ao controle, enquanto que a atividade de FA foi significativamente reduzida por R1 e R5. Esses mesmos SAEs juntamente com R4 induziram as maiores porcentagens de morte... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The overall aim of this study, divided into two experiments, was to evaluate the cytotoxicity of experimental adhesive systems (EAS) with different hydrophilicity, and ethanol as a dentin solvation solution, on odontoblast-­‐like cells. In the first experiment, sterilized filter paper discs were impregnated with 10 μL of each EAS: R1, R2, R3, R4 and R5 (in increasing rank of hydrophilicity), followed by light activation. The paper discs were individually immersed in DMEM culture medium for obtaining the extracts (DMEM + released components of EAS), which were applied on MDPC-­‐23 cells in culture. Non-­‐impregnated paper discs (R0) were used as control. Cell metabolism (MTT assay), total protein expression (TP) and alkaline phosphatase activity (ALP) were assessed, in addition to the type of cell death (flow cytometry) and the degree of monomer conversion (FTIR). Data for each response variable were submitted to Kruskal-­‐Wallis and Mann-­‐Whitney tests (α=0.05). Compared to the control (100%), cell metabolism was decreased by 36.4%, 3.1%, 0.2%, 21.5% and 65.7% for R1, R2, R3, R4 and R5, respectively. However, only R1 and R5 differed from the control. R1, R4 and R5 decreased the expression of TP compared to the control, whereas only R1 and R5 significantly reduced the activity of ALP. The later EAS plus R4 caused the highest percentages of cell death by necrosis. A higher percentage of monomer conversion was detected as a function of the hydrophilicity. According to the experimental conditions, it could be... (Complete abstract click electronic access below) / Mestre

Orientador: Marcelo Ferrarezi de Andrade / Banca: Maria Salete Machado Cândido / Banca: Luís Geraldo Vaz / Banca: Paulo Sérgio Quagliatto / Banca: Marcela Rocha de Oliveira Carrilho / Resumo: Este estudo avaliou, por meio do teste de microtração, a resistência de união da resina composta à dentina, verificando a influência da irradiação do tecido com laser de Nd:YAG, realizada após a aplicação do adesivo, e associada ou não ao pré-tratamento ácido do mesmo. Superfícies dentinárias planas foram criadas em 37 terceiros molares humanos extraídos, dos quais, 36 foram selecionados para teste. Os adesivos Single Bond (SB) e Clearfil SE Bond (CSEB) foram aplicados, com ou sem o condicionamento da dentina (ácido fosfórico para o SB e "primer" auto-condicionante para o CSEB). Após aplicação dos adesivos e antes de sua fotopolimerização, as superfícies foram irradiadas com laser, exceto para os controles, testando-se duas potências, 0,75 e 1W. No total, 12 grupos foram criados, 6 para cada sistema. Coroas de resina composta foram construídas e os dentes armazenados a 37ºC por 24h. Depois, os mesmos foram cortados serialmente, resultando em espécimes com secção transversal de união aproximada de 0,49mm2, que foram, em seguida, testados sob tração. Espécimes fraturados, representativos dos diferentes grupos, tiveram suas superfícies dentinárias observadas ao microscópio eletrônico de varredura (MEV). As interfaces adesivas de 2 espécimes não testados em cada grupo também foram observadas ao MEV. O sistema SB foi aplicado na superfície do dente remanescente (sem ácido e sem laser), a coroa de resina construída e o conjunto seccionado em duas metades, para observação da interface ao MEV. Os resultados mostraram que a aplicação do laser aumentou a resistência à microtração apenas quando o SB foi aplicado sem o condicionamento ácido prévio e em relação ao grupo em que só o adesivo foi aplicado (SB / sem ácido/ sem laser). Entretanto, estes valores foram inferiores aos obtidos quando o SB foi... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This study evaluated if the irradiation of dentin trough the adhesive applied on it affected micro-tensile bond strength of composite to this tissue. Flat dentin surfaces were created in 37 extracted human third molars. Thirty-six teeth were selected and received surface treatments. Single Bond (SB) and Clearfil SE Bond (CSEB) systems were individually applied after dentin had been acid-etched or not, with phosphoric acid for SB or self-etching primer for CSEB. Immediately after adhesives application and before light curing, surfaces were lased, except for controls, using two power settings, 0.75 and 1W. So, 12 groups were designed, 6 for each bonding system. After that, composite crowns were built-up over the treated surfaces and the teeth were stored in distillated water, at 37ºC, for 24h. The teeth were serially sectioned in beams with cross-sectional area of approximately 0,49mm2, and the specimens were stressed to failure under tension using a testing machine. Representative fractured specimens were selected and had their dentin surfaces observed under scanning electron microscopy (SEM). Interfaces of two untested beams were also observed under SEM. Moreover, the dentin surface of one additional tooth received SB application (with neither acid etching nor laser irradiation), a composite crown was built-up on it and the tooth was cut longitudinally in two halves, which had their dentin/resin interfaces observed under SEM. This study showed that laser irradiation increased micro-tensile bond strength only in Groups 5 and 6, where SB was applied without previous dentin acid etching, in comparison to the group where this adhesive was used alone (Group 4 - no etching / no laser). However, these values were lower than those found when dentin was etched. There was not an improvement in bond... (Complete abstract, click electronic address below) / Doutor