Biomodificação do colágeno dentinário por Cross-Linkers: efeito na rigidez do colágeno e na longevidade da união resina-dentina produzida pela técnica Dry-BondingBianchi, Luciana [UNESP] 24 November 2015 (has links) (PDF)
Made available in DSpace on 2016-12-09T13:52:20Z (GMT). No. of bitstreams: 0
Previous issue date: 2015-11-24. Added 1 bitstream(s) on 2016-12-09T13:55:24Z : No. of bitstreams: 1
000871154.pdf: 2451026 bytes, checksum: e29c010991d3c7a6ad57c9b8e0e38c24 (MD5) / Os objetivos desse estudo foram investigar o efeito da aplicação de diferentes agentes promotores de ligações cruzadas (cross-linkers) sobre (1) a rigidez do colágeno dentinário e (2) sobre a degradação da união resinadentina produzida pela técnica dry-bonding. Para responder ao primeiro objetivo, 40 discos de dentina com 0,3 mm de espessura foram obtidos de pré-molares hígidos. Após completa desmineralização em ácido fosfórico 10%, os discos foram aleatoriamente divididos em 5 grupos (n=8): água deionizada (controle), carbodiimida (EDC) 0,5 mol/L, proantocianidina (PA) 5% ou glutaraldeído (GA) 5% ou 25%. Os discos permaneceram imersos nas soluções por 60s. A rigidez do colágeno foi indiretamente avaliada com base na contração após desidratação, por meio de transformador linear diferencial variável (LVDT). Para responder ao segundo objetivo, 64 pré-molares humanos hígidos foram desgastados para remoção total do terço coronário, obtendo desta forma superfícies planas de dentina. Estas foram condicionadas com ácido fosfórico a 37% por 15s, seguido do tratamento com as mesmas soluções descritas acima (n=16), exceto para o GA 25%. Após um tempo pré-determinado de tratamento, a dentina foi mantida úmida em metade dos dentes (n=8), e desidratada com jatos de ar nos dentes restantes (n=8). Em seguida, em todos os dentes, foi aplicado o adesivo Prime & Bond 2.1 e foi construído um bloco de resina. Espécimes de 0,81 mm² de área adesiva foram submetidos ao ensaio mecânico de microtração, após 24h ou 6 meses de envelhecimento em saliva artificial. Também foram analisados os tipos de fratura após o teste de microtração e oito espécimes por grupo/período de envelhecimento foram preparados para análise da nanoinfiltração. Para ambos os experimentos, os dados foram submetidos aos testes de ANOVA e Tukey (p<0,05). Na ausência de tratamento...(Resumo completo, clicar acessO letrônico abaixo) / The aims of this study were to investigate the effect of the application of cross-linkers on (1) the stiffness of dentin collagen and (2) the resin-dentin bond degradation produced by the dry-bonding technique. To respond the first objective, forty 0.3 mm-thick dentin disks were obtained from sound premolars. After complete demineralization in 10% phosphoric acid, the discs were randomly divided into 4 groups according to the treatment (n=8): deionized water (control), 0.5 mol/L carbodiimide (EDC), 5% proanthocyanidin (PA) and 5% or 25% glutaraldehyde (GA). The discs were immersed in the solutions for 60s. Collagen stiffness was assessed indirectly based on the shrinkage after dehydration, measured in a linear variable differential transformer (LVDT). For second objective, flat dentin surfaces were produced in 64 sound pre-molars. The dentin was etched with phosphoric acid 37% for 15s, followed by treatment with the same solution described previously (n=16), except for the 25%GA. After the 60s treatment, the dentin was kept moist in half of the teeth (n=8) and dehydrated by air jets in the remaining teeth (n=8). Prime & Bond 2.1 adhesive was applied in all teeth followed by the built up of a composite block. Specimens of 0.81mm² adhesive area were obtained for the microtensile bond strength test, performed after 24h or 6 months of aging in saliva-like solution. After the mechanical test, the failure type was analyzed. Eight specimens by group were prepared for nanoleakage analysis. For both experiments, data were submitted to ANOVA and Tukey tests (p<0.05). In the absence of treatment with cross-linkers (control group), the percentage of shrinkage of the dentin matrix was 60%. Only EDC (23.9%) and glutaraldehyde 25% applied for 10 min (21.7%) were able to significantly reduce dentin shrinkage after dehydration. The highest bond strength values were found for EDC and 10% GA...(Complete abstract eletronic access below)
|
2 |
Biomodificação do colágeno dentinário por Cross-Linkers: efeito na rigidez do colágeno e na longevidade da união resina-dentina produzida pela técnica Dry-Bonding /Bianchi, Luciana. January 2015 (has links)
Orientador: Fernanda Gonçalves Basso / Banca: Elisa Maria Aparecida Giro / Banca: Rita de Cássia Loiola Cordeiro / Banca: Hérica Adad Ricci / Banca: Adriano Fonseca de Lima / Resumo: Os objetivos desse estudo foram investigar o efeito da aplicação de diferentes agentes promotores de ligações cruzadas (cross-linkers) sobre (1) a rigidez do colágeno dentinário e (2) sobre a degradação da união resinadentina produzida pela técnica dry-bonding. Para responder ao primeiro objetivo, 40 discos de dentina com 0,3 mm de espessura foram obtidos de pré-molares hígidos. Após completa desmineralização em ácido fosfórico 10%, os discos foram aleatoriamente divididos em 5 grupos (n=8): água deionizada (controle), carbodiimida (EDC) 0,5 mol/L, proantocianidina (PA) 5% ou glutaraldeído (GA) 5% ou 25%. Os discos permaneceram imersos nas soluções por 60s. A rigidez do colágeno foi indiretamente avaliada com base na contração após desidratação, por meio de transformador linear diferencial variável (LVDT). Para responder ao segundo objetivo, 64 pré-molares humanos hígidos foram desgastados para remoção total do terço coronário, obtendo desta forma superfícies planas de dentina. Estas foram condicionadas com ácido fosfórico a 37% por 15s, seguido do tratamento com as mesmas soluções descritas acima (n=16), exceto para o GA 25%. Após um tempo pré-determinado de tratamento, a dentina foi mantida úmida em metade dos dentes (n=8), e desidratada com jatos de ar nos dentes restantes (n=8). Em seguida, em todos os dentes, foi aplicado o adesivo Prime & Bond 2.1 e foi construído um bloco de resina. Espécimes de 0,81 mm² de área adesiva foram submetidos ao ensaio mecânico de microtração, após 24h ou 6 meses de envelhecimento em saliva artificial. Também foram analisados os tipos de fratura após o teste de microtração e oito espécimes por grupo/período de envelhecimento foram preparados para análise da nanoinfiltração. Para ambos os experimentos, os dados foram submetidos aos testes de ANOVA e Tukey (p<0,05). Na ausência de tratamento...(Resumo completo, clicar acessO letrônico abaixo) / Abstract: The aims of this study were to investigate the effect of the application of cross-linkers on (1) the stiffness of dentin collagen and (2) the resin-dentin bond degradation produced by the dry-bonding technique. To respond the first objective, forty 0.3 mm-thick dentin disks were obtained from sound premolars. After complete demineralization in 10% phosphoric acid, the discs were randomly divided into 4 groups according to the treatment (n=8): deionized water (control), 0.5 mol/L carbodiimide (EDC), 5% proanthocyanidin (PA) and 5% or 25% glutaraldehyde (GA). The discs were immersed in the solutions for 60s. Collagen stiffness was assessed indirectly based on the shrinkage after dehydration, measured in a linear variable differential transformer (LVDT). For second objective, flat dentin surfaces were produced in 64 sound pre-molars. The dentin was etched with phosphoric acid 37% for 15s, followed by treatment with the same solution described previously (n=16), except for the 25%GA. After the 60s treatment, the dentin was kept moist in half of the teeth (n=8) and dehydrated by air jets in the remaining teeth (n=8). Prime & Bond 2.1 adhesive was applied in all teeth followed by the built up of a composite block. Specimens of 0.81mm² adhesive area were obtained for the microtensile bond strength test, performed after 24h or 6 months of aging in saliva-like solution. After the mechanical test, the failure type was analyzed. Eight specimens by group were prepared for nanoleakage analysis. For both experiments, data were submitted to ANOVA and Tukey tests (p<0.05). In the absence of treatment with cross-linkers (control group), the percentage of shrinkage of the dentin matrix was 60%. Only EDC (23.9%) and glutaraldehyde 25% applied for 10 min (21.7%) were able to significantly reduce dentin shrinkage after dehydration. The highest bond strength values were found for EDC and 10% GA...(Complete abstract eletronic access below) / Doutor
|
3 |
Efeito do uso de agentes reticuladores de colágeno em procedimentos adesivos: estudos in vitro e in situHass, Viviane 03 July 2015 (has links)
Made available in DSpace on 2017-07-24T19:21:57Z (GMT). No. of bitstreams: 1
Viviane Hass.pdf: 2803478 bytes, checksum: df63c0c38968187b894f9aa37339ef78 (MD5)
Previous issue date: 2015-07-03 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study evaluated the effect of application of collagen cross-link agents under time and clinically relevant strategy, through two in vitro and one in situ studies. For in vitro experiment 1, 52 third human molars had exposed the dentin surface, acid etched and distributed according the 8 experimental groups: collagen cross-link agent (6.5% pronthocyanidin [PA], 0.1% UVA-light actived riboflavin [RB], 5% glutaraldehyde [GA] and distilled water as control
group [CT], and 2 simplified etch-and-rinse systems (Adper Single Bond Plus [SB] and Tetric N-Bond [TN]. The cross-link agentes were activelly applied for 60 s, bonded and restorated with composite resin. Then, the teeth were sectioned to obtain specimens and tested in immediately [IM] and after 6 months [6M] storage time for microtensile bond strength (μTBS) and
nanoleakage (NL), and IM for degree of conversion (DC) and MMP-activity within the hybrid layer. Additional 24 teeth were used by cytotoxicity assay. For in vitro experiment 2, 2 etchant agentes were tested (2%PA with 10% phosphoric acid [ACPA] and 35% phosphoric acid [CT]). Dentin of 16 teeth was
exposed, etched, bonded using SB adhesive, and restored with composit resin. These teeth were tested by μTBS, NL in IM and 6M; and MMP-activity within the hybrid layer. Additional 10 teeth had flated the enamel surfaces and tested by enamel bond strength in IM and 6M. For the in situ experiment 3, 40 teeth were used, in which 2 cavities prepared. These cavities were etched, treated according the experiment 1, bonded and restored with composite resin. One restoration for each tooth was tested IM and another was included in a palatal
device in cariogenic oral environment [COE] for 10 volunteers during 14 days. The restorations were sectioned and tested by microhardness, μTBS, NL and morphology of the hybrid layer for differential staining technique. All the data were analyzed by 2 way-ANOVA and Tukey’s test (α = 0.05). For experimente
1, all the collagen cross-link agentes were effective to reduce the resin-dentin degradation after 18M e did not exhibit cytotoxic potential, except the GA (p<0.05). For the experiment 2, the PA containing in etchant reduced the resindentin
bond degradation (p<0.05) and did not affect the resin-enamel bond strentgh (p>0.05). However for in situ experiment 3, only the PA and GA reduced the resin-dentin degradation (p<0.05) in COE. The collagen cross-link agentes were effective to reduce the resin-dentin degradation, in time and relevant clinically strategy. The GA exhibited cytotoxic potential and should be
avoided for clinical use. / O objetivo desse trabalho foi verificar o efeito da aplicação de agentes reticuladores de colágeno em tempo e estratégia clinicamente relevantes, através de dois estudos laboratoriais in vitro e um estudo in situ. Para o experimento 1 in vitro, 52 dentes tiveram a superfície dentinária condicionada, e distribuídos entre 8 grupos experimentais pela combinação dos fatores: agente de tratamento (proantocianidina 6,5% [PA], riboflavina 0,1% ativada pela luz ultravioleta [RB], glutaraldeído [GA] e água destilada como grupo controle [CT]; e os sistemas adesivos (Adper Single Bond Plus [SB] e Tetric NBond [TN]. Os agentes foram aplicados com primers aquosos por 60 s, seguido
da aplicação do sistema adesivo e restauração com resina composta. Depois foram seccionados e testados imediatamente (IM) e após 18 meses de armazenamento (18M) para análise da resistência de união à dentina (RU), nanoinfiltração (NI) e em IM para análise do grau de conversão (CG) e atividade de metaloproteinases (MMPs), dentro da camada híbrida. Outros 24
dentes foram utilizados para análise da citotoxicidade. Para o experimento 2 in vitro, foi utilizado 2 condicionadores ácidos (2%PA mais ácido 10% [ACPA] e ácido fosfórico 35% [CT]). Foi exposta a superfície dentinária de 16 dentes, realizado o condicionamento ácido, aplicados o adesivo SB e incrementos de
resina composta. Esses dentes foram destinados para análise da RU, NI em IM e após 6 meses de armazenamento (6M) e atividade de MMPs dentro da camada híbrida IM. Outros 10 dentes tiveram planificadas as faces de esmalte para análise da resistência de união ao esmalte (RE), que também foi testada
em IM e 6M. Para o experimento 3 in situ, foram utilizados 40 dentes, nos quais foram confeccionadas 2 cavidades em cada dente. Essas cavidades foram condicionadas, aplicados os mesmos agentes reticuladores de colágeno como no experimento 1, sistema adesivo SB e restauradas com resina composta. Uma das restaurações de cada dente foi testada IM e a outra foi fixada em um dispositivo palatino, que foi usado por 14 dias em ambiente cariogênico oral [ACO] por 10 voluntários. Esses dentes foram testados para análise da microdureza, RU, NI e análise histológica da morfologia da camada híbrida.
Todos os dados foram submetidos a ANOVA 2 fatores de medidas repetidas e teste de Tukey (α=0,05). Para o experimento 1, todos os agentes foram eficazes para reduzir a degradação da interface de união após 18M e ausentes
de citotoxicidade, exceto o GA (p<0,05). Para o experimento 2, a inclusão da PA no condicionamento ácido foi eficaz para reduzir a degradação em dentina (p<0,05) e não afetou a RE (p>0,05). Já para o experimento 3, in situ, apenas a
PA e o GA foram eficazes para reduzir a degradação da interface de união à dentina em ACO (p<0,05). Os agentes reticuladores foram eficazes para reduzir a degradação da interface de união à dentina, em tempos e estratégia clinicamente relevantes. Contudo o GA foi considerado potencialmente citotóxico e deveria ser evitado para uso clínico.
|