Síntese e caracterização de espinélios de lítio e manganês obtidos via rota hidrotermal assistida por microondas / Synthesis and caracterization of lithium and manganese spinels obtained by microwave-assisted hydrothermal routeSilva, Daiane Piva Barbosa da 28 November 2014 (has links)
Made available in DSpace on 2016-06-02T20:34:59Z (GMT). No. of bitstreams: 1
6440.pdf: 13562062 bytes, checksum: 63ddee486c9be2cd2baaae0f61496ced (MD5)
Previous issue date: 2014-11-28 / Universidade Federal de Sao Carlos / Lithium and manganese oxide in spinel phase (LiMn2O4) was obtained by microwave-assisted hydrothermal route starting from completely soluble reagents. For this, a mixture of potassium permanganate and lithium hydroxide monohydrate (Li/Mn = 1.2) aqueous solutions and acetone (acetone/Mn = 1.1) was treated in a microwave reactor (850 W) at 140 °C for different times (10 s - 30 min) and under constant magnetic stirring. The obtained materials were characterized by X-ray diffraction, scanning and transmission electron microscopy, X-ray dispersive energy spectroscopy, electrons diffracton, inductively coupled plasma-atomic emission spectroscopy, cyclic voltammetry, thermogravimetry, structural refinement by Rietveld method and chronopotentiometry. The X-ray diffractogramm for the material synthesized in 5 min could be indexed to the JCPDS card number 35-0782 related to the LiMn2O4 in spinel phase, but the unwanted presence of K+ ions in its structure was verified. Thus, an ionic exchange step was included in the process, in which the newly-synthesized material was treated in an aqueous solution of lithium hydroxide in the same microwave reactor for different times (5 - 40 min) and under constant magnetic stirring. After 10 min, a material with low content of K+ ions and Li/Mn ratio = 0.52 was obtained, but it was electrochemically inactive. The material was submitted to a heat treatments in a conventional microwave oven for distinct times (1 - 5 min), having presented, after 4 min, the characteristic electrochemical profile of the spinel. The images obtained by scanning and transmission electron microscopy for this material showed the predominance of prismatic particles with nearly 10 - 25 nm. The results of charge and discharge tests showed that the specific capacity values are strongly dependent of the composite film thickness that composes the electrode. Thinner films presented a value of initial specific capacity of 100 ± 17 mA h g-1 with charge retention of 93% after 75 charge and discharge cycles at C/1 discharge rate. / O óxido de lítio e manganês na fase espinélio (LiMn2O4) foi obtido via rota hidrotermal assistida por micro-ondas a partir de reagentes completamente solúveis. Para tal, uma mistura das soluções aquosas de permanganato de potássio e hidróxido de lítio monoidratado (Li/Mn = 1,2) e acetona (acetona/Mn = 1,1) foi tratada em um reator de micro-ondas (850 W) a 140 oC por diferentes tempos (10 s 30 min) e sob constante agitação magnética. Os materiais obtidos foram caracterizados por difratometria de raios X, microscopia eletrônica de varredura e transmissão, energia dispersiva de raios X, difração de elétrons, espectroscopia de emissão atômica em plasma indutivamente acoplado, voltametria cíclica, termogravimetria, refinamento estrutural pelo método de Rietveld e cronopotenciometria. O difratograma de raios X do material sintetizado em 5 min pôde ser indexado à ficha cristalográfica JCPDS 35- 0782, referente ao LiMn2O4 na fase espinélio, porém verificou-se a presença indesejada de íons K+ em sua estrutura. Assim, inseriu-se no processo uma etapa de troca iônica, na qual o material recém-sintetizado foi tratado em solução aquosa de hidróxido de lítio no mesmo reator de micro-ondas a 140 oC por diferentes tempos (5 40 min) e sob constante agitação magnética. Após 10 min, foi obtido um material com baixo teor de íons K+ e com uma razão Li/Mn = 0,52, porém eletroquimicamente inativo. O material foi submetido a tratamentos térmicos em forno de micro-ondas convencional por distintos tempos (1 5 min), tendo apresentado, após 4 min, o perfil eletroquímico característico do espinélio. Nas imagens obtidas por microscopia eletrônica de varredura e transmissão para este material observa-se a predominância de partículas com morfologia prismática com cerca de 10 25 nm. Os resultados dos testes de carga e descarga demonstraram que os valores de capacidade específica são fortemente dependentes da espessura do filme compósito que compõe o eletrodo. Filmes menos espessos apresentaram um valor de capacidade específica inicial de 100 ± 17 mA h g-1 com retenção de carga de 93% após 75 ciclos de carga e descarga a uma taxa de descarga C/1.
|
2 |
Propriedades estruturais e eletroquímicas de espinélios de lítio e manganês dopados para uso em baterias de lítio / Structural and electrochemical properties of doped spinels For use in lithium batteriesAmaral, Fábio Augusto do 02 September 2005 (has links)
Made available in DSpace on 2016-06-02T20:34:09Z (GMT). No. of bitstreams: 1
1271.pdf: 3028789 bytes, checksum: 3f5d6ad235e817cd1ee8e5e686a1dd40 (MD5)
Previous issue date: 2005-09-02 / The spinels investigated in the present work were obtained by solid state reaction at 750 ºC for 72 h among the precursors ε-MnO2, LiOH and the respective oxides/salt of the doping ions. In order to control the particles size, all the spinels were milled in a ball milling for 30 min. The mechanical milling, associated or not to further calcination, was also used for obtaining the pure spinel LiMn2O4. The different obtained spinels were characterized by the average manganese valence (n), X ray diffractometry, electronic scanning microscopy, particles size distribution and specific superficial area. From the X ray diffractograms, spinels of single cubic phase belong to the Fd3m space group were identified. The calculated values for the unity cell parameter (a) were lower for the doped spinels (8,221 Å at 8,229 Å) than for the pure one (8,234 Å), decreasing in the following order: a(Li1,05Ga0,02Mn1,98O4) > a(Li1,05Co0,02Mn1,98O4) > a(Li1,05Al0,02Mn1,98O4) > a(Li1,05M0,02Mn1,98O3,98S0,02) > a(Li1,05M0,02Mn1,98O3,98F0,02). The values of n were higher for the doped spinels (3,56 3,50) than for the pure one (3,53 ± 0,01), decreasing in the following order: n(Li1,05Ga0,02Mn1,98O4) > n(Li1,05Co0,02Mn1,98O4) > n(Li1,05Al0,02Mn1,98O4) > n(Li1,05M0,02Mn1,98O3,98F0,02) > n(Li1,05M0,02Mn1,98O3,98S0,02). The mechanical milling after calcination changed the spinel particles in three aspects: formation of nanometer-scale particles, generation of lattice strain and partial oxidation of manganese ions. Before calcination, it allowed obtaining of pure spinel LiMn2O4 with highly disordered lattice structure, nanometer particles and high number of structural defects. A gel polymer electrolyte of the polyacrylonitrile (PAN)/polyvinylacrylate (PVA) was developed with different mixtures of organic solvents and lithium salts. From impedance measurements, the highest value of ionic conductivity (1,47 x 10-3 S cm-1) was obtained, at 25 oC, for the electrolyte prepared from the mixture (1:1) of ethyl (EC) and dimethyl (DMC) carbonates containing 1 mol L-1 of lithium tetrafluoroborate (LiBF4). Cyclic voltammetric measurements showed that this gel electrolyte only oxidizes at potentials close to 5 V vs. Li/Li+. In the charge and discharge tests, the cathodes of the doped spinels presented values of specific discharge capacity decreasing in the following order: C(Li1,05Al0,02Mn1,98S3,02O3,98) > C(Li1,05Al0,02Mn1,98F3,02O3,98) > C(Li1,05Ga0,02Mn1,98S3,02O3,98) > C(Li1,05Ga0,02Mn1,98F3,02O3,98) > C(Li1,05Co0,02Mn1,98S3,02O3,98) > C(Li1,05Co0,02Mn1,98F3,02O3,98). Although the Li1,05Al0,02Mn1,98S3,02O3,98 cathode presented the highest initial capacity value (126 mA h g-1), the Li1,05Ga0,02Mn1,98S3,02O3,98 cathode presented the lowest capacity fading (from 120 mA h g-1 to 115 mA h g-1, that is, only 4%) after three hundred cycles of charge and discharge. / Os espinélios investigados no presente trabalho foram obtidos por reação em estado sólido, a 750 ºC por 72 h, entre os precursores ε-MnO2, LiOH e respectivos óxidos/sal dos íons dopantes. Para controlar o tamanho de partículas, todos os espinélios foram moídos em moinho de bolas por 30 min. A moagem mecânica, associada ou não à posterior calcinação, também foi usada para obter o espinélio puro LiMn2O4. Os diferentes espinélios sintetizados foram caracterizados pela valência média do manganês (n), difratometria de raios X, microscopia eletrônica de varredura, distribuição de tamanho de partículas e área superficial específica. A partir dos difratogramas de raios X, identificou-se espinélios de fase cúbica pertencente ao grupo espacial Fd3m. Os valores calculados de parâmetro de célula unitária (a) para os espinélios dopados (8,221 Å - 8,229 Å) foram menores que para o espinélio puro (8,234 Å), diminuindo na seguinte ordem: a(Li1,05Ga0,02Mn1,98O4) > a(Li1,05Co0,02Mn1,98O4) > a(Li1,05Al0,02Mn1,98O4) > a(Li1,05M0,02Mn1,98O3,98S0,02) > a(Li1,05M0,02Mn1,98O3,98F0,02). Os valores de n dos espinélios dopados (3,56 3,50) foram maiores que o do puro (3,53 ± 0,01), diminuindo na seguinte ordem: n(Li1,05Ga0,02Mn1,98O4) > n(Li1,05Co0,02Mn1,98O4) > n(Li1,05Al0,02Mn1,98O4) > n(Li1,05M0,02Mn1,98O3,98F0,02) > n(Li1,05M0,02Mn1,98O3,98S0,02). A moagem mecânica posterior à calcinação alterou as partículas de espinélio em três aspectos: formação de partículas em escala nanométrica, geração de distorção da rede cristalina e oxidação parcial dos íons manganês. Antes da calcinação, permitiu a obtenção do espinélio puro LiMn2O4 com estrutura cristalina altamente desordenada, partículas nanométricas e grande número de defeitos estruturais. Um eletrólito polimérico gelificado de poliacrilonitrila (PAN)/polivinilacrilato (PVA) foi desenvolvido com diferentes misturas de solventes orgânicos e sais de lítio. A partir de medidas de impedância, o maior valor de condutividade iônica (1,47 x 10- 3 S cm-1) foi obtido, a 25 oC, para o eletrólito preparado a partir da mistura (1:1) dos carbonatos de etileno (EC) e dimetileno (DMC), contendo tetrafluoroborato de lítio (LiBF4) 1 mol L-1. Medidas de voltametria cíclica mostraram que este eletrólito gelificado somente se oxida a potenciais próximos de 5 V vs. Li/Li+. Nos testes de carga e descarga, os catodos de espinélios dopados apresentaram valores de capacidade específica de descarga (C) decrescentes na seguinte ordem: C(Li1,05Al0,02Mn1,98S3,02O3,98) > C(Li1,05Al0,02Mn1,98F3,02O3,98) > C(Li1,05Ga0,02Mn1,98S3,02O3,98) > C(Li1,05Ga0,02Mn1,98F3,02O3,98) > C(Li1,05Co0,02Mn1,98S3,02O3,98) > C(Li1,05Co0,02Mn1,98F3,02O3,98). Embora o catodo de Li1,05Al0,02Mn1,98S3,02O3,98 tenha apresentado o maior valor de capacidade (126 mA h g-1), o catodo de Li1,05Ga0,02Mn1,98S3,02O3,98 apresentou a menor queda de capacidade (de 120 mA h g-1 para 115 mA h g-1, isto é, somente 4%) após trezentos ciclos de carga e descarga.
|
3 |
Compósitos de Polipirrol e Li1,05Mn2O4 : preparação por dip coating ou casting e caracterização eletroquímica / Polypyrrole and Li1.05Mn2O4 composites: preparation by dip coating or casting and electrochemical caracterizationBrocenschi, Ricardo Francisco 21 August 2009 (has links)
Made available in DSpace on 2016-06-02T20:36:23Z (GMT). No. of bitstreams: 1
2656.pdf: 4791047 bytes, checksum: e96032040fa0ff27949ac8acdb653ef4 (MD5)
Previous issue date: 2009-08-21 / Universidade Federal de Sao Carlos / Films of polypyrrole/Li1.05Mn2O4 composites were prepared by chemical synthesis over a carbon-fiber substrate, using the dipcoating and casting techniques, aiming at improving the performance of these materials as cathodes in secondary lithium or lithium-ion batteries. For this the following were investigated: i) electrochemical behavior of both materials (polymer and oxide) over the carbon-fiber surface; ii) electrochemical characteristics and stability of the composites obtained by the different methods; iii) best electrolyte to work at high potentials (> 4 V vs. Li/Li+); iv) electronic conduction of the composites; v) morphology of both components of the composites; vi) behavior of the composites as cathodes of lithium-ion batteries. From the obtained results it could be concluded that neither preparation technique led to films with a good electrical contact between the spinel crystals and the carbon fibers, which is necessary for them to show a high performance for charge storage. For the materials prepared by dip coating, the use of factorial design effectively helped in obtaining a higher specific-capacity value for polypyrrole (118 mA h g-1), but that was not the case for the polypyrrole/Li1.05Mn2O4 composite (only 20 mA h g-1). On the other hand, for the films prepared by casting, the electronic conduction of the spinel was increased due to the polypyrrole and carbon black mixture, while the most appropriate electrolyte for the electrochemical characterizations was 1 mol L-1 LiClO4 in EC:DMC 1:1 (V/V). However, only the predominantly capacitive behavior of the carbon fiber was observed in the charge/discharge tests. Finally, the charge/discharge tests of the polypyrrol/Li1.05Mn2O4 composite compacted over platinum yielded values of ~70 mA h g-1 for the first cycle and a better stability than that presented by the pure spinel. / Filmes de compósitos de polipirrol/Li1,05Mn2O4 foram preparados por síntese química sobre substratos de fibra de carbono, utilizando as técnicas dip coating e casting, visando melhorias no desempenho desses materiais como catodos de baterias secundárias de lítio ou de íons lítio. Para isso, foi necessário investigar: i) o comportamento eletroquímico de ambos os materiais (polímero e óxido) sobre a superfície da fibra de carbono; ii) a estabilidade e características eletroquímicas dos compósitos obtidos pelos diferentes métodos; iii) o melhor eletrólito para operar em altos potenciais (> 4 V vs. Li/Li+); iv) a condutividade eletrônica dos compósitos; v) a morfologia de ambos os constituintes do compósito; vi) o desempenho dos compósitos como catodos numa bateria de íons lítio. Os resultados permitiram concluir que ambas as técnicas de dip coating e casting não resultam em filmes com um bom contato elétrico entre os cristais do espinélio e as fibras de carbono, o qual é necessário para que os eletrodos apresentem alto desempenho para armazenamento de carga. Para os materiais preparados por dip coating, o uso de planejamento fatorial efetivamente ajudou na obtenção de um valor mais alto de capacidade específica para o polipirrol (118 mA h g-1), mas isto não ocorreu para o compósito polipirrol/Li1,05Mn2O4 (20 mA h g-1). Por outro lado, para os filmes preparados por casting, a condutividade eletrônica do espinélio foi aumentada devido à mistura de polipirrol e carbon black, enquanto que o eletrólito mais adequado para as caracterizações eletroquímicas foi LiClO4 1 mol L-1 em EC:DMC 1:1 (v/v). Entretanto, nos testes de carga/descarga observou-se somente o comportamento predominantemente capacitivo da fibra de carbono. Finalmente, testes de carga e descarga do compósito polipirrol/Li1,05Mn2O4 compactado sobre platina resultaram em valores de ~70 mA h g-1 para os primeiros ciclos e melhor estabilidade que a do espinélio puro.
|
4 |
Propriedades estruturais e eletroquímicas de espinélios de lítio e manganês dopados para uso em baterias de lítio. / Structural and electrochemical properties of doped spinels for use in lithium batteries.Amaral, Fábio Augusto do 01 September 2005 (has links)
Made available in DSpace on 2016-06-02T19:55:20Z (GMT). No. of bitstreams: 1
TeseFAA.pdf: 3028789 bytes, checksum: 3f5d6ad235e817cd1ee8e5e686a1dd40 (MD5)
Previous issue date: 2005-09-01 / The spinels investigated in the present work
were obtained by solid state reaction at 750 ºC for 72 h among the precursors
ε-MnO2, LiOH and the respective oxides/salt of the doping ions. In order to control
the particles size, all the spinels were milled in a ball milling for 30 min. The
mechanical milling, associated or not to further calcination, was also used for
obtaining the pure spinel LiMn2O4. The different obtained spinels were
characterized by the average manganese valence (n), X ray diffractometry,
electronic scanning microscopy, particles size distribution and specific superficial
area. From the X ray diffractograms, spinels of single cubic phase belong to the
Fd3m space group were identified. The calculated values for the unity cell
parameter (a) were lower for the doped spinels (8,221 Å at 8,229 Å) than for the
pure one (8,234 Å), decreasing in the following order: a(Li1,05Ga0,02Mn1,98O4) >
a(Li1,05Co0,02Mn1,98O4) > a(Li1,05Al0,02Mn1,98O4) > a(Li1,05M0,02Mn1,98O3,98S0,02) >
a(Li1,05M0,02Mn1,98O3,98F0,02). The values of n were higher for the doped spinels
(3,56 3,50) than for the pure one (3,53 ± 0,01), decreasing in the following order:
n(Li1,05Ga0,02Mn1,98O4) > n(Li1,05Co0,02Mn1,98O4) > n(Li1,05Al0,02Mn1,98O4) >
n(Li1,05M0,02Mn1,98O3,98F0,02) > n(Li1,05M0,02Mn1,98O3,98S0,02). The mechanical milling
after calcination changed the spinel particles in three aspects: formation of
nanometer-scale particles, generation of lattice strain and partial oxidation of
manganese ions. Before calcination, it allowed obtaining of pure spinel LiMn2O4
with highly disordered lattice structure, nanometer particles and high number of
structural defects. A gel polymer electrolyte of the polyacrylonitrile
(PAN)/polyvinylacrylate (PVA) was developed with different mixtures of organic
solvents and lithium salts. From impedance measurements, the highest value of
ionic conductivity (1,47 x 10-3 S cm-1) was obtained, at 25 oC, for the electrolyte
prepared from the mixture (1:1) of ethyl (EC) and dimethyl (DMC) carbonates
containing 1 mol L-1 of lithium tetrafluoroborate (LiBF4). Cyclic voltammetric
measurements showed that this gel electrolyte only oxidizes at potentials close to
5 V vs. Li/Li+. In the charge and discharge tests, the cathodes of the doped spinels
presented values of specific discharge capacity decreasing in the following order:
C(Li1,05Al0,02Mn1,98S3,02O3,98) > C(Li1,05Al0,02Mn1,98F3,02O3,98) >
C(Li1,05Ga0,02Mn1,98S3,02O3,98) > C(Li1,05Ga0,02Mn1,98F3,02O3,98) >
C(Li1,05Co0,02Mn1,98S3,02O3,98) > C(Li1,05Co0,02Mn1,98F3,02O3,98). Although the
Li1,05Al0,02Mn1,98S3,02O3,98 cathode presented the highest initial capacity value (126
mA h g-1), the Li1,05Ga0,02Mn1,98S3,02O3,98 cathode presented the lowest capacity
fading (from 120 mA h g-1 to 115 mA h g-1, that is, only 4%) after three hundred
cycles of charge and discharge. / Os espinélios investigados no
presente trabalho foram obtidos por reação em estado sólido, a 750 ºC por 72 h,
entre os precursores ε-MnO2, LiOH e respectivos óxidos/sal dos íons dopantes.
Para controlar o tamanho de partículas, todos os espinélios foram moídos em
moinho de bolas por 30 min. A moagem mecânica, associada ou não à posterior
calcinação, também foi usada para obter o espinélio puro LiMn2O4. Os diferentes
espinélios sintetizados foram caracterizados pela valência média do manganês
(n), difratometria de raios X, microscopia eletrônica de varredura, distribuição de
tamanho de partículas e área superficial específica. A partir dos difratogramas de
raios X, identificou-se espinélios de fase cúbica pertencente ao grupo espacial
Fd3m. Os valores calculados de parâmetro de célula unitária (a) para os
espinélios dopados (8,221 Å - 8,229 Å) foram menores que para o espinélio puro
(8,234 Å), diminuindo na seguinte ordem: a(Li1,05Ga0,02Mn1,98O4) >
a(Li1,05Co0,02Mn1,98O4) > a(Li1,05Al0,02Mn1,98O4) > a(Li1,05M0,02Mn1,98O3,98S0,02) >
a(Li1,05M0,02Mn1,98O3,98F0,02). Os valores de n dos espinélios dopados (3,56 3,50)
foram maiores que o do puro (3,53 ± 0,01), diminuindo na seguinte ordem:
n(Li1,05Ga0,02Mn1,98O4) > n(Li1,05Co0,02Mn1,98O4) > n(Li1,05Al0,02Mn1,98O4) >
n(Li1,05M0,02Mn1,98O3,98F0,02) > n(Li1,05M0,02Mn1,98O3,98S0,02). A moagem mecânica
posterior à calcinação alterou as partículas de espinélio em três aspectos:
formação de partículas em escala nanométrica, geração de distorção da rede
cristalina e oxidação parcial dos íons manganês. Antes da calcinação, permitiu a
obtenção do espinélio puro LiMn2O4 com estrutura cristalina altamente
desordenada, partículas nanométricas e grande número de defeitos estruturais.
Um eletrólito polimérico gelificado de poliacrilonitrila (PAN)/polivinilacrilato (PVA)
foi desenvolvido com diferentes misturas de solventes orgânicos e sais de lítio. A
partir de medidas de impedância, o maior valor de condutividade iônica (1,47 x 10-
3 S cm-1) foi obtido, a 25 oC, para o eletrólito preparado a partir da mistura (1:1)
dos carbonatos de etileno (EC) e dimetileno (DMC), contendo tetrafluoroborato de
lítio (LiBF4) 1 mol L-1. Medidas de voltametria cíclica mostraram que este eletrólito
gelificado somente se oxida a potenciais próximos de 5 V vs. Li/Li+. Nos testes de
carga e descarga, os catodos de espinélios dopados apresentaram valores de
capacidade específica de descarga (C) decrescentes na seguinte ordem:
C(Li1,05Al0,02Mn1,98S3,02O3,98) > C(Li1,05Al0,02Mn1,98F3,02O3,98) >
C(Li1,05Ga0,02Mn1,98S3,02O3,98) > C(Li1,05Ga0,02Mn1,98F3,02O3,98) >
C(Li1,05Co0,02Mn1,98S3,02O3,98) > C(Li1,05Co0,02Mn1,98F3,02O3,98). Embora o catodo de
Li1,05Al0,02Mn1,98S3,02O3,98 tenha apresentado o maior valor de capacidade
(126 mA h g-1), o catodo de Li1,05Ga0,02Mn1,98S3,02O3,98 apresentou a menor queda
de capacidade (de 120 mA h g-1 para 115 mA h g-1, isto é, somente 4%) após
trezentos ciclos de carga e descarga.
|