Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets. In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO2 particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L10 phase. The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L10 order, rapid thermal annealing can lead to the formation of chemically ordered FePt fifilms with (001) texture on amorphous SiO2/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneuosly to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 °C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO2 particle templates with periods down to 50 nm. The addition of Cu improves the (001) texture formation and chemcial ordering for annealing temperatures T < 600 °C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated using e-beam and nanoimprint lithography have been investigated.

Der Einsatz nanostrukturierter Magnetmaterialien als Speicherschichten in Festplatten stellt ein vielversprechendes Konzept zur weiteren Erhöhung der erreichbaren Speicherdichten im Vergleich zu den heute eingesetzten granularen Medien dar. Für die Realisierung dieses Konzeptes ist eine detaillierte Kenntnis der Struktureigenschaften und deren Einfluss auf das magnetische Verhalten der einzusetzenden Schichten erforderlich. Für die vorliegende Arbeit wurden drei verschiedene magnetische Materialien ausgewählt und insbesondere mit elektronenmikroskopischen Methoden in struktureller Hinsicht untersucht. Dazu zählen ferromagnetische (FePt)(100-x)Cu(x) -Schichten, ferromagnetische [Co/Pt]n -Multilagen sowie ferrimagnetische Fe(100-x)Tb(x) -Schichten. Der Schwerpunkt der Untersuchungen lag dabei auf der Korrelation zwischen strukturellen und magnetischen Eigenschaften sowie im Einfluss der Nanostrukturierung auf das magnetische Verhalten der Schichten. In dieser Hinsicht wurden Aspekte der durch die Struktur bedingten magnetischen Anisotropie in Form von magnetokristalliner und Grenzflächenanisotropie betrachtet. Zudem wurde das Kopplungsverhalten zwischen einzelnen Strukturelementen in nanostrukturierten Schichten untersucht. Aufbauend auf die Untersuchung der drei genannten Materialien wurden [Co/Pt]n und Fe(100-x)Tb(x) ausgewählt zum Aufbau eines Systems mit zwei magnetischen Komponenten: Fe(80)Tb(20) / [Co/Pt]10. Die Untersuchungen konzentrierten sich dabei auf die Morphologie der Grenzfläche zwischen den beiden Bestandteilen und deren Einfluss auf den Exchange Bias, der in diesem System vorliegt.

Chemically ordered FePt is one of the most promising materials to reach the ultimate limitations in storage density of future magnetic recording devices due to its high uniaxial magnetocrystalline anisotropy and a corrosion resistance superior to rare-earth based magnets. In this study, FePt and FePt/Cu bilayers have been sputter deposited at room temperature onto thermally oxidized silicon wafers, glass substrates and self-assembled arrays of spherical SiO2 particles with diameters down to 10 nm. Millisecond flash lamp annealing, as well as conventional rapid thermal annealing was employed to induce the phase transformation from the chemically disordered A1 phase into the chemically ordered L10 phase. The influence of the annealing temperature, annealing time and the film thickness on the ordering transformation and (001) texture evolution of FePt films with near equiatomic composition was studied. Whereas flash lamp annealed FePt films exhibit a polycrystalline morphology with high chemical L10 order, rapid thermal annealing can lead to the formation of chemically ordered FePt fifilms with (001) texture on amorphous SiO2/Si substrates. The resultant high perpendicular magnetic anisotropy and large coercivities up to 40 kOe are demonstrated. Simultaneuosly to the ordering transformation, rapid thermal annealing to temperatures exceeding 600 °C leads to a break up of the continuous FePt film into separated islands. This dewetting behavior was utilized to create regular arrays of FePt nanostructures on SiO2 particle templates with periods down to 50 nm. The addition of Cu improves the (001) texture formation and chemcial ordering for annealing temperatures T < 600 °C. In addition, the magnetic anisotropy and the coercivity of the ternary FePtCu alloy can be effectively tailored by adjusting the Cu content. The prospects of FePtCu based exchange spring media, as well as the magnetic properties of FePtCu nanostructures fabricated using e-beam and nanoimprint lithography have been investigated.

Der Einsatz nanostrukturierter Magnetmaterialien als Speicherschichten in Festplatten stellt ein vielversprechendes Konzept zur weiteren Erhöhung der erreichbaren Speicherdichten im Vergleich zu den heute eingesetzten granularen Medien dar. Für die Realisierung dieses Konzeptes ist eine detaillierte Kenntnis der Struktureigenschaften und deren Einfluss auf das magnetische Verhalten der einzusetzenden Schichten erforderlich. Für die vorliegende Arbeit wurden drei verschiedene magnetische Materialien ausgewählt und insbesondere mit elektronenmikroskopischen Methoden in struktureller Hinsicht untersucht. Dazu zählen ferromagnetische (FePt)(100-x)Cu(x) -Schichten, ferromagnetische [Co/Pt]n -Multilagen sowie ferrimagnetische Fe(100-x)Tb(x) -Schichten. Der Schwerpunkt der Untersuchungen lag dabei auf der Korrelation zwischen strukturellen und magnetischen Eigenschaften sowie im Einfluss der Nanostrukturierung auf das magnetische Verhalten der Schichten. In dieser Hinsicht wurden Aspekte der durch die Struktur bedingten magnetischen Anisotropie in Form von magnetokristalliner und Grenzflächenanisotropie betrachtet. Zudem wurde das Kopplungsverhalten zwischen einzelnen Strukturelementen in nanostrukturierten Schichten untersucht. Aufbauend auf die Untersuchung der drei genannten Materialien wurden [Co/Pt]n und Fe(100-x)Tb(x) ausgewählt zum Aufbau eines Systems mit zwei magnetischen Komponenten: Fe(80)Tb(20) / [Co/Pt]10. Die Untersuchungen konzentrierten sich dabei auf die Morphologie der Grenzfläche zwischen den beiden Bestandteilen und deren Einfluss auf den Exchange Bias, der in diesem System vorliegt.