82f. / Submitted by Suelen Reis (suziy.ellen@gmail.com) on 2013-04-23T18:03:32Z No. of bitstreams: 1 Dissertacao Gustavo de Freitas.pdf: 4255443 bytes, checksum: e1c6da0abf59a84ad236924bb2db824b (MD5) / Approved for entry into archive by Rodrigo Meirelles(rodrigomei@ufba.br) on 2013-05-08T12:35:27Z (GMT) No. of bitstreams: 1 Dissertacao Gustavo de Freitas.pdf: 4255443 bytes, checksum: e1c6da0abf59a84ad236924bb2db824b (MD5) / Made available in DSpace on 2013-05-08T12:35:27Z (GMT). No. of bitstreams: 1 Dissertacao Gustavo de Freitas.pdf: 4255443 bytes, checksum: e1c6da0abf59a84ad236924bb2db824b (MD5) Previous issue date: 2007 / O objetivo deste trabalho foi avaliar a resistência de união entre um pino de fibra de vidro e um cimento resinoso. Trinta cilindros de resina composta foram confeccionados e pinos de fibra de vidro (ReforPost - Angellus) cimentados em seu interior com um cimento resinoso dual (RELY-X – 3M). A fotoativação do cimento foi feita variando-se as fontes de luz (Halógena e LED). Cada um dos 30 cilindros foi cortado em três partes (terço cervical, médio e apical), resultando 90 discos que foram divididos em 09 grupos (n=10): Grupo 1- Oc: Optlight Plus – GNATUS, terço cervical; Grupo 2-Om: Optlight Plus – GNATUS, médio; Grupo 3-Oa: Optlight Plus – GNATUS, apical; Grupo 4-RC: RADII – SDI, cervical; Grupo 5 Rm: RADII – SDI, médio; Grupo 6-RC: RADII – SDI, apical; Grupo 7- Ec: Elipar Freelight2 – 3M, cervical; Grupo 8-Em: Elipar Freelight2 – 3M, médio; Grupo 9- Ea: Elipar Freelight2 – 3M, apical. Todos os grupos foram submetidos ao ensaio de tração diametral (DTS) em uma máquina de ensaios (EMIC 2000) até a fratura. As médias dos grupos em Mpa foram: G1-Oc: 25,08 (4,20); G2-Om: 23,44 (4,64); G3-Oa: 20,88 (3,62) G4- Rc: 22,86 (5,93); G5-Rm: 22,12 (6,72); G6-Ra: 22,04 (5,61); G7-Ec: 26,01 (3,33); G8-Em: 19,81 (6,09); G9-Ea: 17,74 (4,14). A análise estatística dos dados permitiu concluir que, o grupo G 9–Ea apresentou a menor resistência à tração diametral demonstrando diferença estatisticamente significante quando comparado com os grupos G7-Ec e G1-Oc e não houve influência das diferentes fontes de luz. Com base nestes resultados também podemos afirmar que o aparelho LED (RADII – SDI) apresentou valores de DTS constantes em todos os terços analisados. / Salvador

Dissertação apresentada ao Programa de Pós-Graduação em Ciência e Engenharia de Materiais da Universidade do Extremo Sul Catarinense - UNESC, como requisito à obtenção do título de Mestre em Ciência e Engenharia de Materiais. / In this work were studied the effect of the perceptual of glass fiber and the effect of the injection processing parameters on the mechanical properties of the nanocomposite containing polyamide 6/glass fiber/montmorilonita (PA6/GF/MMT). Were available the influence of the mass temperature, mold temperature, injection pressure and the perceptual of glass fiber on the maximum tension and maximum flexion force. The investigate of the factors effect’s on the mechanical properties were realized with Differential Thermal Analysis (DSC), X-ray Diffraction (XRD), Scanning Electronic Microscopy (SEM) and Fourier Transform Infrared Spectroscopy (FTIR) and the Mechanical Analysis. The results showed the thermal characteristics of the nanocomposite before and after its processing, the deformation type of the nanoparticles, the crystallinity grade’s of the polymeric matrix and the adhesion quality between glass fibers and the polymeric matrix. For both properties the perceptual of fiber, mold temperature and the injection pressure presented the positive effect. The increase of the magnitude of these factors promotes the increase of the maximum flexion force and maximum tension of the nanocomposite, while the mass temperature presented an effect were negative. / Neste trabalho foram estudados os efeitos do percentual de fibra de vidro e dos parâmetros de processo de injeção nas propriedades mecânicas do nanocompósito de poliamida 6/fibra de vidro/montmorilonita (PA6/FV/MMT). Foi avaliada a influência da temperatura de massa,temperatura de molde, pressão de injeção, além do percentual de fibra de vidro, na tensão máxima por tração e tensão máxima por flexão. As investigações dos efeitos dos fatores sobre as propriedades mecânicas foram realizadas com análises de calorimetria exploratória diferencial (DSC), difração de raios X (DRX), microscopia eletrônica de varredura (MEV) e espectroscopia de infravermelho por transformada de Fourier (FTIR), além das técnicas de caracterização mecânica. Estas técnicas permitiram avaliar as características térmicas do compósito antes e após o processamento, o grau de esfoliamento da argila, o grau de cristalinidade e a adesão entre a fibra de vidro e a matriz polimérica. Para a tensão máxima por flexão, o percentual de fibra, a temperatura do molde e a pressão de injeção apresentaram efeitos positivos. Com o aumento destes fatores ocorre o aumento da tensão máxima, enquanto que para a temperatura de massa o efeito foi negativo. Para a tensão máxima por tração, o percentual de fibra, a temperatura do molde e a pressão de injeção, apresentam efeito positivo, enquanto que para a temperatura da massa o efeito foi negativo.

Made available in DSpace on 2016-06-02T19:10:23Z (GMT). No. of bitstreams: 1 6070.pdf: 6999498 bytes, checksum: 9bf7d2ee8c54baf0e933924f3696afe4 (MD5) Previous issue date: 2013-12-06 / Financiadora de Estudos e Projetos / This work presents a study and development of long glass fiber PVC pellet concentrate (LF-PVC) manufactured by extrusion similar wire coating technique to reinforce pelletized rigid PVC compounds to produce injection molding LF-PVC composites. The incorporation of LF-PVC in rigid PVC compound exhibited mechanical benefits mainly in tensile modulus, flexural modulus and notched impact strength. Injection molding LF-PVC composites with 20 wt% of fiberglass presented tensile and flexural modulus 90% higher than unreinforced rigid PVC; Izod and Charpy notched impact strength 13% and 40% higher than unreinforced rigid PVC, respectively. The reinforcement of rigid PVC with LF-PVC presented slight damage in heat distortion and Vicat temperatures. 20wt% fiberglass PVC composites presented around 10% lower than unreinforced rigid PVC because LF-PVC reinforcement presented little quantity of plasticizers and majority of low molecular weight PVC resin. The innovative technique developed by Grizzo in a preliminary work [1; 2] to incorporate long glass fiber in rigid PVC compound was optimized because the LF-PVC pellets produced presented lower quantity of plasticizer, adequate fiberglass roving with suitable coupling agent (sizing) for PVC and a fiberglass roving tex (g/km) with excellent cost. In summary the reinforcement of injection molding rigid PVC compound with LF-PVC compounds produced unsatisfactory mechanical performance of LF-PVC composites, although that allowed them to compete to long glass fiber polypropylene and polyamide composites in injection molding technical parts under room temperature. Also LF-PVC composites allowed improve usual PVC applications such as connections to reduce thickness or rise dimensional, for example diameter and length, which was not possible before. The last, there are potential applications for LF-PVC composites to be used in special pressurized connections to replace internal metallic reinforcement, and in faucets and other bathroom devices for metal replacement. / Neste trabalho é descrito o estudo e o desenvolvido de um composto granulado de PVC reforçado com fibras de vidro longas (LF-PVC), produzidos através de uma técnica de extrusão similar a de recobrimento de fios, para ser utilizado na fabricação de compósitos PVC/fibras de vidro moldados por injeção. A incorporação dos grânulos LF-PVC num composto de PVC rígido apresentou benefícios principalmente quanto à rigidez sob tração e flexão e à resistência ao impacto. O compósito de PVC reforçado com 20% em massa de fibras de vidro longas apresentou aumento de 90% nos valores de módulo de elasticidade sob tração e sob flexão, e um aumento de 13% e 40% na resistência ao impacto Izod e Charpy com entalhes, respectivamente. O reforçamento do composto de PVC rígido com os grânulos LF-PVC apresentou redução moderada nas temperaturas de deflexão térmica (HDT) e de amolecimento Vicat, sendo obtida uma redução de 10% para o compósito reforçado com 20% de fibras de vidro longas, em virtude da presença de uma pequena quantidade de plastificante e do uso de uma resina de baixa massa molar na formulação de PVC utilizada na fabricação do grânulo LF-PVC. A técnica inovadora de incorporação de fibras de vidro longas em compostos de PVC, desenvolvida por Grizzo em trabalho anterior [1; 2], foi aperfeiçoada através da redução da quantidade de plastificante utilizado no composto do grânulo LF-PVC; do uso de um roving de vidro com sizing específico para PVC; e do uso de um roving de vidro com um tex (g/km) de excelente custo. De um modo geral o reforçamento do composto de PVC rígido com os grânulos LFPVC apresentou desempenho mecânico considerado não satisfatório, porém com possibilidade dos compósitos PVC/fibras de vidro de competir com os compósitos de polipropileno e poliamida reforçados com fibras de vidro em peças técnicas moldadas por injeção sob condições normais de temperatura. O reforçamento também possibilita a melhoria de produtos convencionais de PVC, como conexões, através da redução de espessura e da ampliação de dimensionais, como diâmetros e comprimentos, não possíveis até o momento. Por fim, existe a possibilidade de uso dos compósitos PVC/fibras de vidro em conexões especiais, que apresentam alma metálica de reforço para suportarem elevadas pressões, e em torneiras e outros dispositivos sanitários que apresentem partes metálicas.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-06-23T20:06:05Z No. of bitstreams: 1 MaraisaCristianeDeOliveiraLeite_DISSERT.pdf: 2733334 bytes, checksum: d086f67ef0d47e95e151ff9ad376bcd7 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-06-27T20:29:13Z (GMT) No. of bitstreams: 1 MaraisaCristianeDeOliveiraLeite_DISSERT.pdf: 2733334 bytes, checksum: d086f67ef0d47e95e151ff9ad376bcd7 (MD5) / Made available in DSpace on 2016-06-27T20:29:13Z (GMT). No. of bitstreams: 1 MaraisaCristianeDeOliveiraLeite_DISSERT.pdf: 2733334 bytes, checksum: d086f67ef0d47e95e151ff9ad376bcd7 (MD5) Previous issue date: 2015-12-22 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Este trabalho objetiva fabricar e caracterizar um comp?sito hibrido pl?stico, com matriz ? base de resina de poli?ster isoft?lica e tendo como refor?o fibras de vidro e o endocarpo do coco seco (Cocos Nuc?fera Linn) na forma de particulado como carga. O comp?sito foi confeccionado industrialmente na Tecniplas Ind?stria e Com?rcio LTDA. na forma de placa, e o processo de fabrica??o utilizado foi ? lamina??o manual (Hand Lay up). A partir da placa foram preparados corpos de prova para ensaios de densidade volum?trica, absor??o de umidade, tra??o uniaxial nos estados seco e ?mido, e ensaio de flex?o, al?m de estudos sobre o comportamento da fratura gerada nos ensaios mec?nicos por meio do MEV. Todos os ensaios foram feitos de modo a achar as aplica??es mais vi?veis ao comp?sito hibrido fabricado. Nos ensaios de tra??o e flex?o foram analisadas as propriedades de tens?o ?ltima, m?dulo de elasticidade e deforma??o. A partir dos resultados observa-se que o percentual de umidade absorvido foi de 3,03%, um valor razoavelmente alto, dado o intervalo de tempo que ocorreu esta absor??o. A presen?a de umidade no ensaio de tra??o significou uma queda de 19,77% da resist?ncia ?ltima, e 5,26% no m?dulo de elasticidade. Para os ensaios de flex?o obteve-se o valor m?dio de 69,13 MPa de resist?ncia ? flex?o. Os resultados apontam a aplica??o do comp?sito hibrido estudado em estruturas leves, ambientes internos, onde exijam solicita??es de tra??o de baixo/m?dio desempenho, e onde envolvem solicita??es de flex?o. / This work aims to manufacture and characterize a hybrid plastic composite with the matrix isophthalic polyester resin base and having as reinforcing glass fiber and the dry endocarp of coconut (Coco nucifera Linn) in the form of particles as filler. The composite was made industrially in Tecniplas Industry and Trade LTDA. in the form of plate, and was manufactured process made by the manual lamination (Hand Lay Up). From the plate they were prepared test specimens for testing density, water absorption, uniaxial traction in dry and wet states, and testing of bending, as well as studies on the behavior of the generated fractures, macroscopic and microscopic, in mechanical tests through. All tests were performed in order to find the most viable applications the hybrid composite manufactured. The tensile and bending tests were analyzed last tensile properties, elasticity and deformation module. After the studies, it is observed that the percentage moisture absorbed was 3.03%. The presence of moisture in the tensile test meant a decrease of 19.77% from last stand, and 5.26% in the elastic modulus. For bending tests gave an average value of 69.13 MPa flexural strength. The results show the application of hybrid composite studied in lightweight structures, indoors, which require low / medium performance traction demands, and which involve flexural requests.

O uso de pinos de fibra de vidro são cada vez mais comuns em reabilitação oral, dessa forma vários sistemas de adesão são encontrados no mercado. Porém ainda há o desafio de manter assepsia do conduto para cimentação do pino sem contaminação. O objetivo deste trabalho foi avaliar a interação de soluções irrigantes na adesão de cimento auto-adesivo em casos de cimentação de pinos de fibra de vidro. Foram utilizados 75 caninos superiores humanos hígidos seccionados transversalmente, de modo que restaram16mm de comprimento radicular partindo do ápice. Estes dentes foram tratados endodonticamente e receberam preparo com profundidade de 12 mm. Após a inclusão das raízes em resina acrílica receberam irrigação com as soluções: G1 - Soro fisiológico; G2 - Extrato Alcoólico de Neem; G3 - EDTA 17%; G4 Hipoclorito de Sódio 2,5%; G5 - Gluconato de Clorexidina 2%. Após a cimentação dos pinos de fibra de vidro com cimento auto-adesivo estes foram submetidos a teste de tração pull out. Foram obtidos slices das raízes em corte transversal para análise em microscópio confocal a laser e microscopia eletrônica de varredura. Realizou-se teste ANOVA e Tukey para análise estatística. As seguintes médias em Newtons foram observadas: G1 - 334,0; G2 - 265,9; G3 - 281,7; G4 - 205,7; G5 - 303,1.Pela microscopia eletrônica de varredura notou-se que G4 apresentou maior degradação da dentina, G2 mostrou maior deposição de debris. Pela análise confocal observou-se prevalência de falhas adesivas. Após análise dos dados concluiu-se que o gluconato de clorexidina foi a solução que apresentou melhor força de adesão comparada às demais, além de não degradar a dentina e não deixar resíduos. Conclui-se que a Clorexidina ainda é um interessante irrigante prévio a cimentação de pinos de fibra de vidro devido às propriedades apresentadas. / The use of glass fiber posts are increasingly common in oral rehabilitation thus various adhesion systems are found on the market. But there is still the challenge of maintaining the root canal aseptic for luting post without contamination. The objective of this study was to evaluate the interaction between irrigating solutions in the selfadhesive cement in cases of luting glass fiber post. A total of 75 human maxillary canines healthy were sectioned, so that remaining 16 mm of root length from the apex. The roots were endodontic treated and post space preparation were12mm. Then, after inclusion in acrylic resin they were separated in groups according to irrigation protocol: G1 - Saline Solution; G2 - Neem Alcoholic Extract; G3 - EDTA 17%; G4 Sodium Hipocloryte 2,5%; G5 - Chlorhexidine Gel 2%. After luting of glass fiber posts with self adhesive cement these were subjected to tensile test pull out. Slices were obtained in the root cross section for analysis in confocal microscopy and scanning electron microscopy. The statistical analysis was performed by ANOVA and Tukey tests. The following averages in Newtons were observed: G1 - 334,0; G2 - 265,9; G3 - 281,7; G4 - 205,7; G5 - 303,1. By scanning electron microscopy it was noted that G4 showed higher degradation of dentin, G2 showed greater deposition of debris. By confocal analysis showed a prevalence of adhesive failures. After analyzing the data it is concluded that the G5 group showed the best bond strength compared to the others, and does not degrade the dentine and not leaving residue. It follows that the chlorhexidine is still an interesting prior irrigating cementing glass fiber post due to the properties presented.

Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2017-05-03T15:20:09Z No. of bitstreams: 2 Dissertação - Pedro Ivo de Carvalho - 2017.pdf: 4004894 bytes, checksum: 33f2a48487a0eb9767e85161eae677b4 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-05-03T15:20:21Z (GMT) No. of bitstreams: 2 Dissertação - Pedro Ivo de Carvalho - 2017.pdf: 4004894 bytes, checksum: 33f2a48487a0eb9767e85161eae677b4 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-05-03T15:20:22Z (GMT). No. of bitstreams: 2 Dissertação - Pedro Ivo de Carvalho - 2017.pdf: 4004894 bytes, checksum: 33f2a48487a0eb9767e85161eae677b4 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-03-31 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Several researches aim to discover a best development of new glass-fiber-reinforced composite resins for the manufacture of intraradicular posts with better mechanical properties has been the aim of several researches lately. The reinforcement of composite resin with glass fibers can improve the mechanical properties, such as flexural strength, fracture resistance and compressive strength. Considering that the resin matrix monomers, the photoinitiator system and the interaction with the glass fibers interfere in the homogenization of the composite and in the degree of polymer conversion, the present work had as Objective: To evaluate the influence of different proportions of the monomers Bis-EMA / Bis-GMA / TEGDMA and photoactivator systems based on DFI and camphorquinone on the mechanical properties of a experimental fiberglass reinforced composite resin. Methodology: Ten groups were created (n = 10) using an experimental resin based on methacrylate, having as study factors: 1. Different matrices according to the proportions of monomers Bis-GMA (BG), TEGDMA (TE) and Bis-EMA (BE): And 2. The photoinitiator system: without DFI (SD) salt or DFI (CD) salt. The samples were prepared for the flexural strength (RF) and diametral tensile strength (RTD) tests. Statistical analysis showed that for RF (Mpa) there was significance in the interaction between the factors under study (p = 0.047). The highest result occurred for Group 10 (267.815 ± 45.05) c, followed by Group 9 (242.440 ± 44.83) bc; Group 8 (241.05 ± 44.83) b Group 3 (236.152 ± 26.42) abc. The lowest result occurred in Group 9 (192.450 ± 12.60) a, followed by Group 7 (202.35 ± 28.36) ab; Group 6 (207,240 ± 30,07) ab; Group 2 (209.530 ± 23.16) ab; Group 5 (216,760 ± 30,14); And Gruop 1 (218,880 ± 41,49). For RTD only the presence of DFI salt showed statistical significance (p = 0.001). The addition of the DFI salt in the composite significantly increased results for flexural strength and diametral tensile strength, while the increase of Bis-EMA was significant for better flexural strength results. / A busca pelo desenvolvimento de novos compósitos reforçados com fibra de vidro para a confecção de pinos intrarradiculares com melhores propriedades mecânicas tem sido a base de várias pesquisas atuais. O incremento fibras de vidro silanizadas nas resinas promove melhora nos valores de resistência à flexão, resistência à fratura e resistência compressiva. Tendo em vista que os monômeros da matriz resinosa, o sistema fotoiniciador e a interação com as fibras de vidro interferem na qualidade do compósito e no grau de conversão polimérica, o presente trabalho teve como objetivo avaliar as propriedades mecânicas de um compósito experimental reforçado por fibra de vidro composto por 30% de matriz orgânica, 47,5% de partícula de carga e 22,5% de vibras de vidro curta(3mm), variando proporções de monômeros Bis-EMA, Bis-GMA e TEGDMA e o efeito do sal de difenil-iodônio (DFI) em um sistema fotoiniciador à base de canforoquinona. Dez grupos foram criados (n=10) utilizando uma resina experimental a base de metacrilato, tendo como fatores em estudo: 1. Diferentes matrizes de acordo com as proporções dos monômeros Bis-GMA, TEGDMA e Bis-EMA e 2. O sistema fotoiniciador: sem sal DFI (SD) ou com sal DFI (CD). As amostras foram preparadas para os testes resistência flexural (RF) e resistência à tração diametral (RTD). Análise estatística mostrou que para RF (Mpa) houve significância na interação entre os fatores em estudo (p=0,047). Os melhores resultados foram encontrados para os grupos: Grupo 10 (267,815±45,05)c, seguido por Grupo 9 (242,440±44,83)bc. Para RTD somente a presença do sal DFI demonstrou significância estatística (p=0,001). Em MPa foram observados os maiores resultados: Grupo 10, (35,36±2,61b); Grupo 8, (35,07±6,89b). A adição do sal DFI no compósito aumentou significativamente resultados para resistência flexural e resistência à tração diametral, enquanto que a presença de Bis-EMA foi significante para melhores resultados somente em resistência flexural.

Este trabalho tem por objetivo obter propriedades mecânicas de compósitos angle-ply fabricados pelo processo de enrolamento filamentar, na forma de placas com diversas orientações do reforço. As placas foram fabricadas com fibra de carbono e matriz epoxídica e fibra de vidro e matriz epoxídica. Os exemplares para ensaio foram obtidos nas direções de 0°, ±10°, ±20°, ±30°, ±60°, ±70°, ±80° e 90° em relação á direção do equipamento de ensaio, atribuída como sendo 0°. Resultados mostraram que para corpos-de-prova de fibra de cartaono bobinados na direção ±10° a tensão máxima média obtida foi de 855 MPa e o módulo de elasticidade médio de 136 GPa, enquanto que para corpos-de-prova de fibra de carbono bobinados na direção de ±80°, a tensão máxima média foi de 68 MPa e módulo de elasticidade médio de 10 GPa. Os resultados obtidos indicaram que as propriedades mecânicas diminuem acentuadamente a partir da direção de ±10°. Também foram obtidas as frações volumétricas, dureza Barcol e análise térmica das placas fabricadas. / This work aims to obtain some mechanical properties of angle-ply composites manufactured by the filament winding process. The plates were manufactured with different reinforcement orientation. The composites were manufactured with carbon fibers and an epoxy resin system as polymeric matrix and glass fibers and an epoxy resin system as polymeric matrix. The coupons were manufactured in the directions of 0°, ±10°, ±20°, ±30°, ±60°, ±70°, ±80° e 90°, related to the 0° fiber direction. Results show that coupons with cartDon fiber in the direction ±10°, the mean strength was 855 MPa and the mean module of elasticity was 136 GPa, whereas coupons with cartDon fiber in the direction of ±80° the mean strength was 68 MPa and the mean module of elasticity was 10 GPa. The results obtained have indicated that the mechanical strength diminishing acutely from the orientation of ±10° The volumetric fractions, Barcol hardness and thermal analysis are also obtained of all the manufactured plates.

A necessidade de recuperação e reforço em estruturas de madeira, concreto e aço exigiu da construção civil uma procura por métodos mais eficientes que pudessem cumprir esse papel. Com este objetivo vários estudos estão sendo realizados utilizando fibras reforçadas com polímeros (FRP). Dentre estas fibras, as que vêm apresentando melhores resultados como reforço para peças estruturais de madeiras são as fibras de carbono e as fibras de vidro. Dentro deste escopo, este trabalho tem como objetivo estudar o comportamento estrutural de vigas de madeira de espécies nacionais reforçadas com fibras de carbono e com fibras de vidro, verificando a eficiência deste reforço e adequando modelos de cálculo para avaliação da resistência e da rigidez das vigas reforçadas, e também verificar a eficiência de uma formulação de adesivos à base de mamona e do adesivo Cascophen, para fixação das respectivas fibras na madeira, em substituição ao adesivo epóxi, normalmente utilizado. Foram efetuados ensaios de vigas de madeira reforçadas com polímeros, em modelo reduzido, e em protótipos, para diversas configurações de geometria e quantidade de fibras utilizadas. Os resultados obtidos indicam uma boa concordância entre os modelos teóricos para avaliar a resistência e a rigidez das vigas reforçadas, e os resultados experimentais, e a eficiência do reforço. Também foram conduzidos ensaios de tração em corpos-de-prova de fibras laminado com os adesivos, caracterizando a sua resistência e elasticidade e comparando o comportamento dos adesivos estudados. Os resultados indicaram o melhor comportamento do adesivo epóxi. / The necessity of rehabilitation and reinforcement in wood structures, concrete and steel demanded a search for more efficient methods that could to carry this paper. With this objectives several studies are using fibers reinforced polymers (FRP). These fibers which presenting better results in structural reinforcement for structural pieces of wood are the fibers of carbon and the glass fibers. This work has as objective studies the structural behavior of wood beams of national species reinforced with carbon fibers and with glass fibers, verifying the efficiency of this reinforcement and adapting calculation models for evaluation of the strength and stiffness of the reinforced beams, and also to verify the efficiency of a formulation of adhesives to the castor oil and of the adhesive Cascophen, for fixation of the respective fibers in the wood, in substitution the adhesive epoxy, usually used. Experimental work was made with wood beams reinforced with polymeric, in reduced model, and in prototypes, for several geometry configurations and amount of used fibers. The obtained results indicate a good agreement among the theoretical models to evaluate the strength and stiffness of the reinforced beams, and the experimental results, and the efficiency of the reinforcement. Traction rehearsals were also led in body-of-proof of fibers laminated with the adhesives, characterizing your strength and elasticity and comparing the behavior of the studied adhesives. The results indicated the best behavior of the adhesive epoxy.

Este trabalho teve como objetivo avaliar a microdureza de dois cimentos resinosos de polimerização dual (RelyX U100®, 3M-ESPE e Panavia F 2.0®, Kuraray), empregados na cimentação de pinos de fibra de vidro (Fibrekor-Jeneric® Pentron) variando o modo de polimerização em químico, fotoativação imediata ou tardia após 5min através de luz halógena, avaliando também o efeito do armazenamento em água deionizada por três meses. Este trabalho testou as seguintes hipóteses nulas: não há diferença nos valores de microdureza entre os cimentos, modo de polimerização, efeito do armazenamento e entre os terços radiculares. Sessenta raízes de incisivos bovinos, com 16mm de comprimento cérvico-apical, tiveram seus condutos obturados e, posteriormente, preparados para cimentação do pino intracanal. Os espécimes foram divididos em 6 grupos (n = 10), cada um subdividido em 2 subgrupos com 5 espécimes para cada cimento. Os pinos foram cimentados de acordo com o protocolo descrito por cada fabricante. No grupo A1, os espécimes foram mantidos em ambiente à prova de luz para que ocorresse apenas a polimerização química. No grupo B1, os espécimes foram cimentados e submetidos à fotoativação imediata, e, no grupo C1, realizou-se a fotoativação após 5 minutos. As raízes foram seccionadas longitudinalmente, para que a linha de cimento pudesse ser exposta e os testes de microdureza realizados. Após 7 dias, as médias de microdureza (± desvio padrão) foram obtidas, para os terços cervical, médio e apical, respectivamente: A1 (Panavia) - 41,25 ±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. Para os grupos armazenados em água, os valores médios de microdureza (± desvio padrão) obtidos nos 3 grupos, químico (grupo A2), fotoativado imediatamente (grupo B2) e fotoativado tardiamente (grupo C2), nos terços cervical, médio e apical, respectivamente, foram: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. Os resultados foram submetidos ao teste ANOVA a 4 critérios (cimento, modo de polimerização, armazenamento e terços), que detectou diferenças estatísticas entre os grupos, e o teste de Tukey foi aplicado para comparações individuais. Os resultados mostraram que: a fotoativação com luz halógena promoveu um aumento significativo nos valores de microdureza para o cimento Panavia; o armaz namento em água por três meses reduziu os valores de microdureza para a maioria dos grupos, sendo que o cimento o U100 apresentou menor variação de dureza quando comparado ao Panavia; os terços que receberam maior intensidade de luz halógena tiveram maior aumento de microdureza para ambos os cimentos, especialmente para o cimento Panavia. Conclui-se, portanto, que as hipóteses de nulidade propostas foram rejeitadas. / The objective of this study was to evaluate the microhardness of two dual cure resin cements (RelyX - U100®, 3M-ESPE and Panavia F 2.0®, Kuraray), used for fiberglass posts (Fibrekor ® - Jeneric Pentron) cementation. Chemical cure and a halogen immediate and late light cure source were compared, and the effect of storage in deionized water for three months was also evaluated. This study tested the following null hypotheses: there is no difference between the microhardness values for each dual cure resin cement, cure source type, storage time, or root thirds. Sixty bovine incisor roots 16mm long had their roots restored and then prepared for post cementation. The specimens were divided into 6 groups (n = 10), and each group was subdivided into 2 subgroups with 5 specimens for each cement. The posts were cemented according to manufacturers instructions. In group A1, the specimens were kept in a light-proof environment to ensure only a chemical cure. In group B1, the specimens were restored and subjected to immediate light curing, and in group C1, light curing was performed after 5 minutes. The roots were longitudinally sectioned to expose the cement line and perform microhardness tests. After 7 days, the average microhardness (± standard deviation) values were obtained for the cervical, medium and apical thirds, respectively: A1 (Panavia ) - 41,25±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) - 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±1,93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. For the 3 groups stored in deionized water (chemical [group A2], immediate light curing [group B2] and late light curing [group C2]), the average microhardness values (± standard deviation) obtained for the cervical, medium and apical thirds, respectively were: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. ANOVA testing was used to detect statistical differences among the 4 criteria (cements, cure mode, storage and thirds) and the Tukey test was used for individual comparisons. The results showed that the halogen light cure promoted a significant increase in microhardness values for Panavia cement; storage in water for three months reduced microhardness values for most of the groups, although U100 resulted in less microhardness variation compared to Panavia; the thirds that received a higher intensity of halogen light had a higher increase in the average values of microhardness for both cements, especially for Panavia. Therefore, the null hypotheses proposed in this work were rejected.

As fibras de vidro são usadas há alguns anos com a finalidade de melhorar a resistência à tração e ao impacto de compósitos cimentícios. Mas, os álcalis do cimento Portland atacam essas fibras causando a degradação de suas propriedades mecânicas. Para contornar essa degradação, há alguns anos, foram desenvolvidas as fibras álcalis-resistente (AR) que, embora tenham apresentado melhor desempenho que as fibras de vidro convencionais, ainda apresentam perda de desempenho com o tempo. Esse trabalho trata do desenvolvimento de um novo tipo de fibra na forma de telas, a partir das fibras de vidro convencionais, usando uma impregnação de PVC como barreira para impedir o ataque químico dos álcalis do cimento. A análise da eficiência dessas telas em relação à durabilidade foi feita por meio de processo de envelhecimento acelerado e, a seguir, foram estudados os vários tipos de aplicação delas em elementos construtivos à base de matrizes cimentícias concomitantemente como o uso de barras de GFRP. Como resultado final comprovou-se a eficiência da resina desenvolvida na pesquisa para impregnação das fibras em relação à sua durabilidade frente ao meio alcalino do cimento Portland e a adequação do uso das telas impregnadas com essa resina em diversos tipos de produtos de matrizes cimentícias para construção civil. / Glass fibers are used since several years to improve the tensile and impact strengths of cement composites. But, the alkalis from Portland cement attack the glass fibers causing the deterioration of its mechanical properties. For overcome this degradation, some years ago, were developed the fibers alkali-resistant (AR) which, although presented as the best performance fiber glass conventional, still show a loss of performance over time. This work deals with the development of a new type of fiber in the form of mesh, from conventional glass staple fibers, using a PVC impregnation as barrier to hinder the chemical attack alkalis them it cement to these. The analysis of the efficiency of these fibers in relation to the durability was made by means of process accelerated ageing and, next, concomitantly studied some types of application of these fibers in constructive elements to the cements matrix with the use of bars of GFRP. The final result showed tha the resin developed in this work is efficient how coating of conventional fibers to get durability on the alkaline environment and the mesh impregnated with this resin are appropriates of the use in many kinds of products to construction made from cements matrixes.