No description available.

Thesis (M.S.)--Massachusetts Institute of Technology, Dept. of Materials Science and Engineering, 1981. / MICROFICHE COPY AVAILABLE IN ARCHIVES AND SCIENCE. / Includes bibliographical references. / by Carl J. White. / M.S.

Thesis. 1978. Ph.D.--Massachusetts Institute of Technology. Dept. of Materials Science and Engineering. / MICROFICHE COPY AVAILABLE IN ARCHIVES AND SCIENCE. / Vita. / Includes bibliographical references. / Ph.D.

A systematic study of the effect of sulphidizing atmosphere on the High Temperature Low Cycle Fatigue (HTLCF) properties of coated and uncoated unidirectionally solidified MARM002 nickel base superalloy was performed at 870°C. The coating systems investigated were, aluminide coating, three types of platinum modified aluminide coatings, and platinum coating. The creep-plasticity mode of the strain range partitioning method was used for creep-fatigue loading. A constant loading regime (Strain range 6.6 x 10-3 ) was used to test the samples in argon, air and Ar + 5%S02 and a lower strain range of3.8 x 10-3 was used to investigate the creep-fatigue properties in Ar + 5%S02 only. The results were analysed using scanning electron microscopy including spot analyses (SEM-EDS), Auger electron spectroscopy (AES) and X-ray diffraction (XRD) techniques. The synergistic effect of sulphidizing environment and the creep fatigue loading (Strain range - 0.66%) resulted in accelerated failure in all the materials systems tested, except for the TYPE I platinum aluminide coated sample. This coating displayed a "self-healing" mechanism which enhanced its fatigue life under sulphidizing conditions. In general, the coatings had an adverse effect on the fatigue properties of the material systems. This was due to the poor mechanical properties of the coating. The mechanical properties of the coating was influenced by the coating microstructure and the chemical composition. The modification of the NiAI zone with platinum in the platinum aluminide coatings improved the fatigue properties of the coating by altering the crack propagation mechanism in the NiAl zone. The higher the platinum content in this region the more brittle it became. The platinum modified aluminide coating showed an improvement in the corrosion fatigue properties in the S02 containing environment at the higher strain range when compared with the uncoated, aluminide coated and platinum coated samples. However, at the lower strain range all the coating systems performed worse than the uncoated alloy. This was mainly due to the brittle failure of the coating. The platinum modified aluminides performed the worst due to the presence of brittle platinum aluminide phases. The interdiffusion and interaction of platinum with the substrate alloying elements, resulted in this coating being ineffective for corrosion protection. The resultant coating layer produced poor corrosion-fatigue properties. Although the coating systems did show evidence of resistance to sulphidation and oxidation there were relatively ineffective under the combination of sulphidizing environment and fatigue loading due to their poor mechanical properties. The mechanism of sulphidation was consistent for all the material systems tested with oxidation proceeding first and sulphidation proceeding at the corrosion scale/substrate interface. The crack propagation in the coating and substrate was controlled by the sulphidation attack at the crack tip and failure of the oxide scales formed in the cracks. / Thesis(M.Sc.Eng.)- University of Natal, Durban, 1998.

Microstructural features at different scales affect the constitutive stress-strain response and the fatigue crack initiation life in Ni-base superalloys. While numerous efforts have been made in the past to experimentally characterize the effects of these features on the stress-strain response and/or the crack initiation life, there is a significant variability in the data with sometimes contradictory conclusions, in addition to the substantial costs involved in experimental testing. Computational techniques can be useful tools to better understand these effects since they are relatively inexpensive and are not restricted by the limitations in processing techniques. The effect of microstructure on the stress-strain response and the variability in fatigue life were analyzed using two Ni-base superalloys; DS GTD111 which is a directionally solidified Ni-base superalloy, and IN100 which is a polycrystalline Ni-base superalloy. Physically-based constitutive models were formulated and implemented as user material subroutines in ABAQUS using the single crystal plasticity framework which can predict the material stress-strain response with the microstructure-dependence embedded into them. The model parameters were calibrated using experimental cyclic stress-strain histories. A computational exercise was employed to quantify the influence of idealized microstructural variables on the fatigue crack initiation life. Understanding was sought regarding the most significant microstructure features using explicit modeling of the microstructure with the aim to predict the variability in fatigue crack initiation life and to guide material design for fatigue resistant microstructures. Lastly, it is noted that crystal plasticity models are often too computationally intensive if the objective is to model the macroscopic behavior of a textured or randomly oriented 3-D polycrystal in an engineering component. Homogenized constitutive models were formulated and implemented as user material subroutines in ABAQUS, which can capture the macroscale stress-strain response in both DS GTD111 and IN100. Even though the study was conducted on two specific Ni-base superalloys; DS GTD111 and IN100, the objective was to develop generic frameworks which should also be applicable to other alloy systems.

Hot sections of gas engine turbines require specialized materials to withstand extreme conditions present during engine operation. Nickel-base superalloys are typically used as blades and disks in the high pressure turbine section because they possess excellent fatigue strength, creep strength and corrosion resistance at elevated temperatures. Components undergo thermomechanical fatigue conditions as a result of transient engine operation. Sharp geometric features, such as cooling holes in blades or fir-tree connections in disks, act as local stress raisers. The material surrounding these features are potential sites of localized inelastic deformation and crack formation. To reduce customer costs associated with unnecessary overhauls or engine down-time, gas turbine manufacturers require accurate prediction methods to determine component endurances. The influence of stress concentration severity on thermomechanical fatigue crack formation is of particular importance as cracks often initiate in these hot spots. Circumferentially notched specimens were utilized to perform thermomechanical fatigue experiments on blade material CM247LC DS and disk material PM IN100. A parametric study on CM247LC DS was performed utilizing four notched specimens. Experimental results were coupled with finite element simulations utilizing continuum based constitutive models. The effects of applied boundary conditions on crack initiation life was studied in both alloys by performing experiments under remotely applied force and displacement boundary conditions. Finite element results were utilized to develop a life prediction method for notched components under thermomechanical fatigue conditions.

This research establishes a physics-based life determination model for the second generation single crystal superalloy PWA 1484 experiencing out-of-phase thermomechanical fatigue (TMF). The life model was developed as a result of a combination of critical mechanical tests, dominant damage characterization and utilization of well-established literature. The resulting life model improves life prediction over currently employed methods and provides for extrapolation into yet unutilized operating regimes. Particularly, the proposed deformation model accounts for the materials' coupled fatigue-environment-microstructure response to TMF loading. Because the proposed model is be based upon the underlying deformation physics, the model is robust enough to be easily modified for other single crystal superalloys having similar microstructure. Future use of this model for turbine life estimation calculations would be based upon the actual deformation experienced by the turbine blade, thereby enabling turbine maintenance scheduling based upon on a "retirement for a cause" life management scheme rather than the currently employed "safe-life" calculations. This advancement has the ability to greatly reduce maintenance costs to the turbine end-user since turbine blades would be removed from service for practical and justifiable reasons. Additionally this work will enable a rethinking of the warranty period, thereby decreasing warranty related replacements. Finally, this research provides a more thorough understanding of the deformation mechanisms present in loading situations that combine fatigue-environment-microstructure effects.