No description available.

The test evaluates wear resistance of quenched and tempered steels of 8 grade materials. The steels are low alloyed carbon steels within a hardness range of 120HV to 600HV. The carbon content in the range of 0.3-0.6%. The wear tests were undertaken in a laboratory at SSAB in Oxelösund with a newly designed wear test machine. The wear performance was evaluated by abrasive material clinkers and slag in Room temperature as well as High temperature at 400°C. Eight samples are used for each test, the samples are placed inside the drum with sample holders. The wear test performed by 217mm diameter drum rotate over the two-horizontal bar at 37 RPM, thus creating sliding, rolling and some impact over the surface of the materials. Investigations were performed by weight measurements of the samples, hardness measurements at room temperature, after the 400°C test, and at high temperatures up to 400°C, and light optical microscopy examinations. The results show that wear rate at Room temperature depends on hardness of material and hardness of abrasive material. The wear rate at high temperature 400°C show that wear rate depends on alloying element and the tempering temperature of the material.

Ti and Ti-based alloys are used in many aerospace and automotive components due to their high strength-to-weight ratio and corrosion resistance. However, room and elevated temperature wear resistance remain an issue, thus requiring some form of secondary hard phase, e.g., refractory carbides and oxides, as well as solid lubrication to mitigate wear. In this study, Ti-TiC (14, 24 and 35 vol% TiC) composite coatings were deposited on mild steel substrates using cold spray with comparisons made to baseline cold-sprayed Ti. The dry sliding friction and wear behavior were studied from 25°C to 575°C and during thermal cycling in this temperature range. While the room temperature friction coefficient of all the coatings remained relatively constant at ~0.5, the wear rate continually decreased from ~1x10-3 to ~2x10-5 mm3/N-m with increasing the TiC loading. Raman spectroscopy measurements determined that the same TiO2 tribochemical phases (rutile and anatase) were present on the room temperature sliding wear surfaces, thus responsible for similar friction coefficients. With increasing sliding temperatures to 575°C, the Ti-35%TiC composite coating exhibited the best overall tribological behavior, i.e., the friction coefficient decreased to ~0.3 along with a negative wear rate of -6.6x10-5 mm3/N-m (material gain on the wear track was recorded due to oxidation and transfer from the counterface). These friction and wear reductions were determined to be due to the formation of stable, low interfacial shear strength oxide glaze layers on the wear surfaces, composed of TiO2, WO3, and CoWO4 (transfer from WC-Co counterface). In addition, self-adaptive friction behavior was observed during thermal cycling as a result of the microstructural and tribochemical differences in the tribolayers.

Este trabalho traz contribuições à linha de pesquisa \'Nova Família de Ligas Baseada no Sistema Ni-Al-Cr-C Resistentes ao Desgaste em Elevadas Temperaturas\', estudando o comportamento mecânico, tribológico e a estabilidade superficial destas ligas. Esta família de ligas fundidas, denominada NICRALC - busca conjugar algumas características das superligas à base de níquel e dos ferros fundidos brancos, aliando ao comportamento mecânico anômalo do Ni3Al - aumento da resistência mecânica com a temperatura, até valores da ordem de 800°C - a uma dispersão de carbonetos de cromo de alta dureza. Desta forma, busca-se desenvolver uma alternativa às ligas ferrosas nas temperaturas acima das quais estas ligas perdem significativamente sua resistência mecânica (notadamente 600 °C), assim como uma alternativa mais econômica às ligas a base de cobalto resistentes ao desgaste, em virtude das altas cotações e instabilidades no preço deste elemento. Neste trabalho foram avaliadas as propriedades mecânicas em elevadas temperaturas (compressão e dureza), tenacidade à fratura na temperatura ambiente, comportamento tribológico (cavitação, abrasão, deslizamento e erosão) e a resistência à oxidação ao ar e à carburação em atmosfera redutora, em temperaturas elevadas, de ligas Ni-Al-Cr-C (NICRALC) fundidas. Ligas NICRALC fundidas com diferentes teores de carbono e submetidas a diferentes tratamentos tiveram seu comportamento mecânico e tribológico comparado ao comportamento do STELLITE 6 fundido, a uma liga NICRALC produzida por deposição por \'SPRAY\', a um ferro fundido branco alto cromo fundido convencionalmente e a um ferro fundido branco alto cromo depositado por \'SPRAY\'. Os ensaios de compressão confirmaram o comportamento anômalo da matriz ordenada Ni3Al. As ligas NICRALC apresentaram aumento ou manutenção da resistência ao escoamento com o aumento da temperatura de ensaio. A mesma tendência foi encontrada nos ensaios de dureza a quente. As demais ligas apresentaram tendência de queda da resistência ao escoamento e da dureza com o aumento da temperatura de ensaio. Esta tendência é mais acentuada na liga STELLITE, desta forma, as ligas NICRALC apresentaram em altas temperaturas maior resistência ao escoamento e maior dureza que o STELLITE. Os diferentes ensaios de desgaste mostraram, em geral, uma maior resistência do STELLITE em comparação com as ligas NICRALC na temperatura ambiente. Nestas condições verifica-se que a menor resistência mecânica da matriz ordenada nas ligas NICRALC é determinante para definir uma menor resistência ao desgaste na temperatura ambiente. Nos ensaios de erosão-oxidativa realizados a 600 e 800°C as ligas NICRALC mostraram perdas de massa menores que as experimentadas pelo STELLITE e pelos ferros fundidos. As ligas NICRALC com microestrutura de carbonetos mais homogênea, próxima do eutético, mostraram melhor comportamento sob desgaste abrasivo e erosivo se comparadas às ligas NICRALC 05 e 13. Os ensaios de resistência à oxidação mostraram que as ligas NICRALC são mais resistentes à oxidação que o STELLITE. Além disso, observou-se grande propensão ao destacamento dos filmes de óxidos formados nos STELLITES em temperaturas acima de 800°C. Os ensaios de resistência à carburação mostraram que no caso das ligas NICRALC ocorreu a precipitação de um depósito de grafita e, subjacente a esta, a formação de uma zona de fragmentação microestrutural, na qual se observa empobrecimento ora do Al ora do Cr, que aparentemente impede o avanço do processo. No caso do STELLITE verificou-se a ocorrência do aumento da fração volumétrica de carbonetos, típico dos casos clássicos de carburação. Os procedimentos de simulação termodinâmica utilizados indicam a necessidade de se implementar a descrição da solubilidade do carbono na fase ordenada de forma a permitir o pleno uso do software THERMOCALC no projeto e aprimoramento de ligas NICRALC. / This work contributes to the research line \'New Family of High Temperature Wear Resistant Alloys based on the Ni-Al-Cr-C System\', studying the mechanical and tribological behaviour and the surface stability of these alloys. This family of foundry alloys, called NICRALC, tries to unite some of the characteristics of the Ni based superalloys and the high-chromium-white-cast-irons, associating the anomalous behaviour of the ordered intermetallic phase Ni3Al - which increases its strength with the increase of temperature - with a dispersion of hard chromium carbides. The aim is to develop an alternative to iron-based wear resistant alloys at temperatures where they loose significantly their strength, as well as substituting cobalt based high temperature wear resistant alloys, which suffer from the instability and high cost of the Co metal. The high temperature mechanical properties (hardness and compression), room temperature fracture toughness, tribological behaviour (cavitation, abrasion, sliding and erosion) and resistance to high temperature oxidation and carburization of cast Ni-Al-Cr-C (NICRALC) alloys are studied. Cast NICRALC alloys with different C contents and different heat treatments were compared with a cast STELLITE 6, a conventionally cast high chromium white cast iron, a spray formed high chromium white cast iron and a spray formed NICRALC. Mechanical tests in compression confirmed that NICRALC alloys share the anomalous behaviour of the ordered intermetallic phase Ni3Al, increasing or maintaining their yield strength with increased testing temperature. The same occurred with hot hardness tests. STELLITE and all other alloys showed loss of strength with increased testing temperatures. Thus NICRALC alloys showed higher strength and hardness than STELLITE at high temperatures. All wear tests showed a higher wear resistance of STELLITE in comparison with NICRALC at room temperature. This result can be explained by the higher matrix hardness of STELLITE at room temperature. Oxidative-erosion tests run at 600 and 800° C showed that NICRALC suffered smaller mass loss than STELLITE and the white cast irons. NICRALC alloys with more homogeneous carbide distributions (eutectic alloys) obtained the best results under severe oxidation-erosion conditions. NICRALC alloys were more oxidation resistant than STELLITE alloy, which tended to break and detach the oxide layer formed above 800°C under air. During carburization essays in a reducing atmosphere the NICRALC alloys tended to form a coke-like graphite layer, over a layer with a fragmented microstructure depleted alternatively in chromium and aluminum, which effectively stopped the advance of the process. The STELLITE alloy suffered an increase in carbide volume fraction, a classic carburizing behaviour. The thermodynamic simulation results show that it is still needed to introduce the solubility of carbon on the ordered Ni3Al phase in the model in order to be able to fully calculate the NICRALC phase diagrams.

Este trabalho traz contribuições à linha de pesquisa \'Nova Família de Ligas Baseada no Sistema Ni-Al-Cr-C Resistentes ao Desgaste em Elevadas Temperaturas\', estudando o comportamento mecânico, tribológico e a estabilidade superficial destas ligas. Esta família de ligas fundidas, denominada NICRALC - busca conjugar algumas características das superligas à base de níquel e dos ferros fundidos brancos, aliando ao comportamento mecânico anômalo do Ni3Al - aumento da resistência mecânica com a temperatura, até valores da ordem de 800°C - a uma dispersão de carbonetos de cromo de alta dureza. Desta forma, busca-se desenvolver uma alternativa às ligas ferrosas nas temperaturas acima das quais estas ligas perdem significativamente sua resistência mecânica (notadamente 600 °C), assim como uma alternativa mais econômica às ligas a base de cobalto resistentes ao desgaste, em virtude das altas cotações e instabilidades no preço deste elemento. Neste trabalho foram avaliadas as propriedades mecânicas em elevadas temperaturas (compressão e dureza), tenacidade à fratura na temperatura ambiente, comportamento tribológico (cavitação, abrasão, deslizamento e erosão) e a resistência à oxidação ao ar e à carburação em atmosfera redutora, em temperaturas elevadas, de ligas Ni-Al-Cr-C (NICRALC) fundidas. Ligas NICRALC fundidas com diferentes teores de carbono e submetidas a diferentes tratamentos tiveram seu comportamento mecânico e tribológico comparado ao comportamento do STELLITE 6 fundido, a uma liga NICRALC produzida por deposição por \'SPRAY\', a um ferro fundido branco alto cromo fundido convencionalmente e a um ferro fundido branco alto cromo depositado por \'SPRAY\'. Os ensaios de compressão confirmaram o comportamento anômalo da matriz ordenada Ni3Al. As ligas NICRALC apresentaram aumento ou manutenção da resistência ao escoamento com o aumento da temperatura de ensaio. A mesma tendência foi encontrada nos ensaios de dureza a quente. As demais ligas apresentaram tendência de queda da resistência ao escoamento e da dureza com o aumento da temperatura de ensaio. Esta tendência é mais acentuada na liga STELLITE, desta forma, as ligas NICRALC apresentaram em altas temperaturas maior resistência ao escoamento e maior dureza que o STELLITE. Os diferentes ensaios de desgaste mostraram, em geral, uma maior resistência do STELLITE em comparação com as ligas NICRALC na temperatura ambiente. Nestas condições verifica-se que a menor resistência mecânica da matriz ordenada nas ligas NICRALC é determinante para definir uma menor resistência ao desgaste na temperatura ambiente. Nos ensaios de erosão-oxidativa realizados a 600 e 800°C as ligas NICRALC mostraram perdas de massa menores que as experimentadas pelo STELLITE e pelos ferros fundidos. As ligas NICRALC com microestrutura de carbonetos mais homogênea, próxima do eutético, mostraram melhor comportamento sob desgaste abrasivo e erosivo se comparadas às ligas NICRALC 05 e 13. Os ensaios de resistência à oxidação mostraram que as ligas NICRALC são mais resistentes à oxidação que o STELLITE. Além disso, observou-se grande propensão ao destacamento dos filmes de óxidos formados nos STELLITES em temperaturas acima de 800°C. Os ensaios de resistência à carburação mostraram que no caso das ligas NICRALC ocorreu a precipitação de um depósito de grafita e, subjacente a esta, a formação de uma zona de fragmentação microestrutural, na qual se observa empobrecimento ora do Al ora do Cr, que aparentemente impede o avanço do processo. No caso do STELLITE verificou-se a ocorrência do aumento da fração volumétrica de carbonetos, típico dos casos clássicos de carburação. Os procedimentos de simulação termodinâmica utilizados indicam a necessidade de se implementar a descrição da solubilidade do carbono na fase ordenada de forma a permitir o pleno uso do software THERMOCALC no projeto e aprimoramento de ligas NICRALC. / This work contributes to the research line \'New Family of High Temperature Wear Resistant Alloys based on the Ni-Al-Cr-C System\', studying the mechanical and tribological behaviour and the surface stability of these alloys. This family of foundry alloys, called NICRALC, tries to unite some of the characteristics of the Ni based superalloys and the high-chromium-white-cast-irons, associating the anomalous behaviour of the ordered intermetallic phase Ni3Al - which increases its strength with the increase of temperature - with a dispersion of hard chromium carbides. The aim is to develop an alternative to iron-based wear resistant alloys at temperatures where they loose significantly their strength, as well as substituting cobalt based high temperature wear resistant alloys, which suffer from the instability and high cost of the Co metal. The high temperature mechanical properties (hardness and compression), room temperature fracture toughness, tribological behaviour (cavitation, abrasion, sliding and erosion) and resistance to high temperature oxidation and carburization of cast Ni-Al-Cr-C (NICRALC) alloys are studied. Cast NICRALC alloys with different C contents and different heat treatments were compared with a cast STELLITE 6, a conventionally cast high chromium white cast iron, a spray formed high chromium white cast iron and a spray formed NICRALC. Mechanical tests in compression confirmed that NICRALC alloys share the anomalous behaviour of the ordered intermetallic phase Ni3Al, increasing or maintaining their yield strength with increased testing temperature. The same occurred with hot hardness tests. STELLITE and all other alloys showed loss of strength with increased testing temperatures. Thus NICRALC alloys showed higher strength and hardness than STELLITE at high temperatures. All wear tests showed a higher wear resistance of STELLITE in comparison with NICRALC at room temperature. This result can be explained by the higher matrix hardness of STELLITE at room temperature. Oxidative-erosion tests run at 600 and 800° C showed that NICRALC suffered smaller mass loss than STELLITE and the white cast irons. NICRALC alloys with more homogeneous carbide distributions (eutectic alloys) obtained the best results under severe oxidation-erosion conditions. NICRALC alloys were more oxidation resistant than STELLITE alloy, which tended to break and detach the oxide layer formed above 800°C under air. During carburization essays in a reducing atmosphere the NICRALC alloys tended to form a coke-like graphite layer, over a layer with a fragmented microstructure depleted alternatively in chromium and aluminum, which effectively stopped the advance of the process. The STELLITE alloy suffered an increase in carbide volume fraction, a classic carburizing behaviour. The thermodynamic simulation results show that it is still needed to introduce the solubility of carbon on the ordered Ni3Al phase in the model in order to be able to fully calculate the NICRALC phase diagrams.