Orientador: Eunice Teresinha Giampaolo / Banca: Gelson Luis Adabo / Banca: Carlos Eduardo Vergani / Banca: Maria da Glória Chiarello de Mattos / Banca: Ricardo Faria Ribeiro / Resumo: Este estudo teve como objetivo avaliar a efetividade de quatro condicionadores de metal (Metal Photo Primer, MPP; Cesead II Opaque Primer, OP; Targis Link, TL e Siloc, S) aplicados sobre diferentes superfícies das ligas de Ni-Cr, Co-Cr e do metal Ti Cp. Após o polimento metalográfico e jateamento com Al2O3, foram obtidos três grupos experimentais para cada metal : Grupo polimento (P) - controle; Grupo (J50), jateado com Al2O3 de 250 um. A esses grupos foram aplicados os condicionadores e as resinas opaca e de revestimento estético (Artglass). Decorridos 24 horas de armazenamento em água a 37ºC, cada grupo foi dividido em dois grupos e submetidos aos ensaios mecânicos de cisalhamento (0,5 mm/min.), um antes e outro após 500 ciclos térmicos (60ºC e 4ºC). As superfícies fraturadas foram analisadas e o padrão de falhas determinado. Adicionalmente foram feitas análises de MEV e EDS. Seguem os resultados para cada metal: Liga de Ni-Cr: para os Grupos P e J50, não foram observadas diferenças (p>0,05) nos valores médios de tensão de cisalhamento entre os condicionadores OP e TL e entre MPP e S, sendo maiores as médias dos dois primeiros. Não foram encontradas diferenças (p>0,05) entre as médias de tensão para os condicionadores do Grupo J250. No entanto, esses valores foram superiores aos do Grupo J50. Após a termociclagem, as médias para os condicionadores OP, S e TL não apresentaram aumento significante (p>0,05), enquanto a média para o MPP aumentou (p<0,05). Liga de Co-Cr, para o Grupo P, não foram observadas diferenças (p>0,05) nos valores médios de tensão entre os condicionadores OP e TL e entre MPP e S, sendo superiores as médias dos dois primeiros. As médias de tensão para o Grupo J250 foram estatisticamente maiores às do Grupo J50, ...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of the study was to evaluated the effect of three adhesive primers (Metal Photo Primer, MPP; Cesead II Opaque Primer, OP; Targis Link, TL) and a bonding system (Siloc, S) on the shear bond strength between a prosthetic composite material (Artglass) to Ni-Cr alloy (Wiron 99), Co-Cr alloy (Wironit), and CP Ti (Tritan). Disk patterns were cast of the 3 alloys. All the disk surfaces were abraded with No. 80, 320, and 600 SiC paper, respectively and three different surface treatment were applied: No. 600 SiC polishing, P; 50 mm Al2O3 sandblasting, S50; 250 mm Al2O3 sandblasting, S250. The composites (Artglass opaque and dentin) were applied using a cylindrical stainless steel split according to manufacturer's instructions then light polymerized. Specimens without primer and bonding system were also prepared as control. The specimens were stored in water a 37oC for 24 h and then shear bond strengths were determined both before and after immersed alternately in water baths at 4oC and 60oC for 15 seconds each for up to 500 thermal cycles before shear mode testing at a crosshead speed of 0.5 mm/min. Data were statistically analyzed using 3-way ANOVA and 1-way ANOVA, followed by Tukey multiple range intervals calculated at the 0.05 significance level. Fractured interfaces were analyzed by use of light microscopy and SEM. Results: Ni-Cr alloy: The bond strength of the P-OP/J50-OP group and P-TL/J50- TL group were statistically comparable (p>0,05) and exhibited greater strength than the P-MPP/J50-MPP group and P-S/J50-S (p<0,05). No significant differences were found among the four conditioners for J250 group (p>0,05), and these group showed the greater strength than the J50 group (p<0,05). After thermocycling, no significant differences (p>0,05) were found among the three primers (OP, S, TL) and the bond strength of MPP increased...(Complete abstract, click electronic access below) / Doutor

Statement of problem: With the variety of materials and techniques available, the knowledge of which combination provides frameworks with a better biomechanical behavior and greater fit accuracy is essential for a planning aiming prosthesis longevity. Purpose. To analyze which manufacture technique and material provides a better stress/strain and internal fit correlation. Material and methods. The groups were divided according to framework material and fabrication method: Titanium milled (TiCAD), Zirconia milled (ZrCAD), Cobalt-Chromium alloy milled (CoCrCAD), one-piece casting CoCr alloy (CoCrCAS) and cast and welded CoCr alloy (CoCrWEL). Four external hexagon implants and their respective mini-abutments were placed parallel to each other in a polyurethane model. This model was duplicated, scanned, and a single framework design was created to be used for all milled groups. Casting was done from a wax milled pattern following the same framework design used for the other groups. In preload condition, the strains generated by each framework were recorded by strain gauges fixed around the implants. The internal fit was evaluated by micro-CT scanning. Results. Regarding the uniformity of stress distribution, ZrCAD and CoCrCAD groups presented irregular stress distribution, while TiCAD presented the most uniform distribution. Regarding the internal fit, the TiCAD group presented values significantly better than the others, but not statistically different from ZrCAD. The three manufacturing methods associated to CoCr alloy presented no statistical differences among them. The correlation between the method was statistically significant. Conclusion. The physical and mechanical properties of the complete-arch implant-supported frameworks materials influence the stresses distribution and internal fit. TiCAD presented the best framework stress/strain ratio and internal fit. / Afirmação do problema. Diante da variedade de materiais e técnicas disponíveis, ter o conhecimento de qual combinação proporciona infraestruturas com um melhor comportamento biomecânico e maior precisão na adaptação é essencial para um planejamento visando a longevidade da prótese. Finalidade. Analisar qual material e método de confecção das infraestruturas proporciona a melhor relação tensão/deformação e adaptação interna. Material e métodos. Os grupos foram divididos de acordo com o material e forma de confecção das infraestruturas: fresado em Titânio (TiCAD), fresado em Zircônia (ZrCAD), fresado em Cobalto Cromo (CoCrCAD), CoCr fundido em monobloco (CoCrCAS) e CoCr fundido e com ponto de solda (CoCrWEL). Quatro implantes hexágonos externos e seus respectivos mini-abutments foram colocados paralelos entre si em um modelo de poliuretano. Este modelo foi duplicado, digitalizado e um único desenho de infraestrutura foi criado para todos os grupos fresados. Para fundição, foi utilizado um padrão de cera fresado a partir do projeto usado nos outros grupos. Na condição de pré-carga, as tensões geradas por cada infraestrutura foram registradas por strain gauges fixados ao redor dos implantes. A adaptação interna foi avaliada através de escaneamento por micro-CT. Resultados. Quanto a uniformidade na distribuição das tensões, os grupos ZrCAD e CoCrCAD se apresentaram irregulares, sendo que o grupo TiCAD apresentou distribuição mais uniforme. Quanto à adaptação interna, o grupo TiCAD apresentou valores significativamente melhores que os demais, mas sem diferença estatística em relação ao grupo ZrCAD. As três formas de produção da infraestrutura usando a liga de CoCr não apresentaram diferenças estatísticas entre si. A correlação entre os métodos foi estatisticamente significativa. Conclusão. As propriedades físicas e mecânicas dos materiais de confecção das infraestruturas influenciam na distribuição de estresses e na adaptação interna. O grupo que apresentou a melhor relação tensão/deformação e adaptação foi o grupo TiCAD.